WO2021258662A1 - 一种正极材料、其制备方法和锂离子电池 - Google Patents
一种正极材料、其制备方法和锂离子电池 Download PDFInfo
- Publication number
- WO2021258662A1 WO2021258662A1 PCT/CN2020/135523 CN2020135523W WO2021258662A1 WO 2021258662 A1 WO2021258662 A1 WO 2021258662A1 CN 2020135523 W CN2020135523 W CN 2020135523W WO 2021258662 A1 WO2021258662 A1 WO 2021258662A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- positive electrode
- cobalt
- active material
- single crystal
- free single
- Prior art date
Abstract
Description
首周充电比容量(mAh/g) | 首周效率(%) | 50周循环性能(%) | |
实施例1 | 224.3 | 88.1 | 99.1 |
实施例2 | 222.5 | 87.9 | 99.8 |
实施例3 | 228.9 | 87.5 | 97.9 |
实施例4 | 225.3 | 87.2 | 98.6 |
实施例5 | 223.4 | 87.4 | 98.2 |
实施例6 | 221.8 | 87.1 | 97.2 |
实施例7 | 220.9 | 86.9 | 97.3 |
实施例8 | 219.8 | 86.7 | 97.1 |
实施例9 | 229.7 | 88.0 | 96.8 |
实施例10 | 218.5 | 86.5 | 100.2 |
对比例1 | 219.2 | 86.3 | 94.0 |
对比例2 | 221.6 | 87.1 | 95.4 |
对比例3 | 222.3 | 87.5 | 96.2 |
Claims (26)
- 一种正极材料,所述正极材料为核壳结构,核层包括无钴单晶正极活性物质,壳层包括LiAlO 2和LiFePO 4。
- 根据权利要求1所述的正极材料,其中,所述无钴单晶正极活性物质的含量为98.5~99.9wt%。
- 根据权利要求1或2所述的正极材料,其中,所述LiAlO 2的含量为0.05~0.5wt%。
- 根据权利要求1-3任一项所述的正极材料,其中,所述LiFePO 4的含量为0.05~1wt%。
- 如权利要求1-4任一项所述的正极材料,其中,所述无钴单晶正极活性物质为LiNi xMn yO 2,0.45≤x≤0.95,0.05≤y≤0.55。
- 一种如权利要求1-5任一项所述正极材料的制备方法,所述方法包括如下步骤:将无钴单晶正极活性物质、锂盐、含铝材料和FePO 4混合,煅烧,得到正极材料。
- 如权利要求6所述的方法,其中,所述无钴单晶正极活性物质的制备方法包括:将锂盐和无钴正极活性物质前驱体混合,烧结,得到无钴单晶正极活性物质。
- 如权利要求7所述的方法,其中,所述无钴正极活性物质前驱体的化学式为Ni xMn y(OH) 2,0.45≤x≤0.95,0.05≤y≤0.55。
- 如权利要求6-8任一项所述的方法,其中,所述锂盐包括LiOH和/或Li2CO3。
- 如权利要求7-9任一项所述的方法,其中,所述烧结的温度为800~1000℃。
- 如权利要求7-10任一项所述的方法,其中,所述烧结的时间为10~20h。
- 如权利要求7-11任一项所述的方法,其中,所述烧结的气氛为空气气氛或O2气氛。
- 如权利要求7-12任一项所述的方法,其中,所述烧结之后,还包括将得到的产物进行破碎。
- 如权利要求13所述的方法,其中,破碎后的物料过300~400目筛。
- 如权利要求6-14任一项所述的方法,其中,所述无钴单晶正极活性物 质的残碱含量≤0.5wt%。
- 如权利要求6-15任一项所述的方法,其中,所述无钴单晶正极活性物质的pH值≤12。
- 如权利要求6-16任一项所述的方法,其中,所述无钴单晶正极活性物质的比表面积≤2m 2/g。
- 如权利要求6-17任一项所述的方法,其中,所述含铝材料为Al 2O 3和/或Al(OH) 3。
- 如权利要求6-18任一项所述的方法,其中,所述混合为搅拌混合。
- 如权利要求19所述的方法,其中,搅拌的速率为900~1000rpm。
- 如权利要求6-20任一项所述的方法,其中,所述混合的时间为5~20min。
- 如权利要求6-21任一项所述的方法,其中,所述煅烧的温度为400~700℃。
- 如权利要求6-22任一项所述的方法,其中,所述煅烧的时间为5~8h。
- 如权利要求6-23任一项所述的方法,其中,所述煅烧之后,还包括将产物进行300~400目筛分的过程。
- 如权利要求6-24任一项所述的方法,其中,所述方法包括如下步骤:(1)将锂盐和无钴正极活性物质前驱体进行搅拌混合5~15min,搅拌的转速为800~900rpm;(2)在空气或O 2气氛下,将步骤(1)得到的产物在800~1000℃烧结10~20h,将烧结得到的产物通过对辊破碎和气流粉碎,将粉碎后的物料过300~400目筛,得到无钴单晶正极活性物质;(3)将所述无钴单晶正极活性物质、锂盐、含铝材料和FePO 4进行搅拌混合5~20min,搅拌的速率为900~1000rpm,然后进行400~700℃煅烧5~8h,300~400目筛分,得到正极材料;所述正极材料中,所述无钴单晶正极活性物质的含量为98.5~99.9wt%,所述LiAlO 2的含量为0.05~0.5wt%,所述LiFePO 4的含量为0.05~1wt%。
- 一种锂离子电池,所述锂离子电池包括权利要求1-5任一项所述的正极材料。