WO2021243749A1 - Matériau composite intégré au cuir à double face et procédé de préparation associé - Google Patents

Matériau composite intégré au cuir à double face et procédé de préparation associé Download PDF

Info

Publication number
WO2021243749A1
WO2021243749A1 PCT/CN2020/096050 CN2020096050W WO2021243749A1 WO 2021243749 A1 WO2021243749 A1 WO 2021243749A1 CN 2020096050 W CN2020096050 W CN 2020096050W WO 2021243749 A1 WO2021243749 A1 WO 2021243749A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
leather
hair
integrated
composite material
Prior art date
Application number
PCT/CN2020/096050
Other languages
English (en)
Chinese (zh)
Inventor
杨乐
王永刚
周晓辉
张新平
李海林
Original Assignee
焦作隆丰皮草企业有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 焦作隆丰皮草企业有限公司 filed Critical 焦作隆丰皮草企业有限公司
Publication of WO2021243749A1 publication Critical patent/WO2021243749A1/fr

Abstract

Un matériau composite intégré au cuir à double face est divulgué, comprenant un film de revêtement ; une couche d'apprêt composée sur le film de revêtement ; un matériau de base composé sur la couche d'apprêt ; une couche adhésive composée sur le matériau de base ; une couche tressée qui a une couche de nappage et qui est composée sur la couche adhésive, la couche adhésive étant composée sur une surface tressée de la couche tressée qui a la couche de nappage ; ou une couche intégrée au cuir authentique à double face composée sur la couche adhésive, la couche adhésive étant composée sur une couche de peau de la couche intégrée au cuir authentique à double face. Le matériau composite intégré au cuir à double face selon la présente invention présente une épaisseur de revêtement qui peut être contrôlée au niveau du micron, et le style de surface de carte peut atteindre n'importe quelle texture ou n'importe quel effet visuel. En même temps, le produit présente de bonnes propriétés physiques, une bonne stabilité et une bonne consistance, un procédé de production simple et une efficacité de protection environnementale élevée, et est écologique et durable, et approprié pour la production, la promotion et l'application à grande échelle.
PCT/CN2020/096050 2020-06-04 2020-06-15 Matériau composite intégré au cuir à double face et procédé de préparation associé WO2021243749A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN202010500898.4 2020-06-04
CN202010500898.4A CN111519446A (zh) 2020-06-04 2020-06-04 一种毛革一体复合材料及其制备方法

Publications (1)

Publication Number Publication Date
WO2021243749A1 true WO2021243749A1 (fr) 2021-12-09

Family

ID=71913095

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2020/096050 WO2021243749A1 (fr) 2020-06-04 2020-06-15 Matériau composite intégré au cuir à double face et procédé de préparation associé

Country Status (2)

Country Link
CN (1) CN111519446A (fr)
WO (1) WO2021243749A1 (fr)

Citations (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1288317A (fr) * 1970-04-07 1972-09-06
CN1709694A (zh) * 2004-06-17 2005-12-21 金技五 粘合有织物或人造革的天然毛皮
CN202222551U (zh) * 2011-08-26 2012-05-23 泉州宝马鞋业有限公司 一种防水保暖鞋邦面
CN202463025U (zh) * 2011-12-20 2012-10-03 朱晓华 一种牛皮合成革
CN202592841U (zh) * 2012-03-16 2012-12-12 朱晓华 仿皮皮革
CN202727422U (zh) * 2012-07-25 2013-02-13 龙之族（中国）有限公司 一种防水透湿面料
CN202862733U (zh) * 2012-11-02 2013-04-10 李安飞 一种新型皮革
CN203174416U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 一种高装饰性复合仿真皮
CN203174414U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 胶原纤维麂皮绒复合仿真皮
CN203174417U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 仿棉绒复合仿真皮
CN203174412U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 复合仿真皮
CN203174415U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 胶原纤维仿棉绒复合仿真皮
CN203174413U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 一种胶原纤维针织布复合仿真皮
CN203174418U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 高装饰性胶原纤维麂皮绒复合仿真皮
CN104328676A (zh) * 2013-07-22 2015-02-04 江阴友利特金属制品有限公司 保暖且带有幻彩效果的尺寸稳定性较好人造革
CN205975161U (zh) * 2016-08-29 2017-02-22 温州金裕植绒鞋材有限公司 一种新型合成革
CN206436590U (zh) * 2016-12-06 2017-08-25 东莞市利通皮革制品有限公司 高保暖羊皮革
CN207159667U (zh) * 2017-05-26 2018-03-30 天守(福建)超纤科技股份有限公司 一种胶原纤维超细纤维仿真皮

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103085402B (zh) * 2013-02-04 2015-07-08 苏春 高仿真皮毛一体面料及其制备方法
AT518103A2 (de) * 2015-12-18 2017-07-15 Schaefer Philipp Verfahren zur Herstellung einer Beschichtungsfolie und eines Verbundmaterials
CN111206129A (zh) * 2020-03-25 2020-05-29 焦作隆丰皮草企业有限公司 高档沙发革水性涂饰工艺

Patent Citations (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1288317A (fr) * 1970-04-07 1972-09-06
CN1709694A (zh) * 2004-06-17 2005-12-21 金技五 粘合有织物或人造革的天然毛皮
CN202222551U (zh) * 2011-08-26 2012-05-23 泉州宝马鞋业有限公司 一种防水保暖鞋邦面
CN202463025U (zh) * 2011-12-20 2012-10-03 朱晓华 一种牛皮合成革
CN202592841U (zh) * 2012-03-16 2012-12-12 朱晓华 仿皮皮革
CN202727422U (zh) * 2012-07-25 2013-02-13 龙之族（中国）有限公司 一种防水透湿面料
CN202862733U (zh) * 2012-11-02 2013-04-10 李安飞 一种新型皮革
CN203174416U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 一种高装饰性复合仿真皮
CN203174414U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 胶原纤维麂皮绒复合仿真皮
CN203174417U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 仿棉绒复合仿真皮
CN203174412U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 复合仿真皮
CN203174415U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 胶原纤维仿棉绒复合仿真皮
CN203174413U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 一种胶原纤维针织布复合仿真皮
CN203174418U (zh) * 2013-03-25 2013-09-04 江阴骏华纺织科技有限公司 高装饰性胶原纤维麂皮绒复合仿真皮
CN104328676A (zh) * 2013-07-22 2015-02-04 江阴友利特金属制品有限公司 保暖且带有幻彩效果的尺寸稳定性较好人造革
CN205975161U (zh) * 2016-08-29 2017-02-22 温州金裕植绒鞋材有限公司 一种新型合成革
CN206436590U (zh) * 2016-12-06 2017-08-25 东莞市利通皮革制品有限公司 高保暖羊皮革
CN207159667U (zh) * 2017-05-26 2018-03-30 天守(福建)超纤科技股份有限公司 一种胶原纤维超细纤维仿真皮

Also Published As

Publication number Publication date
CN111519446A (zh) 2020-08-11

Similar Documents

Publication Publication Date Title
CN103255640B (zh) 一种环保阻燃聚氨酯合成革、制备方法及其制品
CN100560855C (zh) 一种具有高耐磨和阻燃性能沙发革的制备方法
CN201881594U (zh) 一种皮质保暖面料
CN101247949B (zh) 处理过的织物
CN102359023B (zh) 超纤环保阻燃合成革及其制备方法
CN107385940B (zh) 一种无溶剂高光漆面超细纤维聚氨酯合成革及其制备方法
CN113119556B (zh) 一种适用于喷胶包覆的汽车内饰pu皮革及其制备方法
CN112824591B (zh) 一种耐磨转移涂层伞面织物的生产工艺
CN103526562B (zh) 一种无纺布聚氨酯运动休闲鞋革及其制备方法
CN105821670A (zh) 一种纺织品新型防绒工艺
CN109624422B (zh) 一种tpu高低温膜复合网布及其制备方法
CN1228500C (zh) 一种超细纤维合成革的后整饰方法
CN102690904A (zh) 一种皮革表面涂饰工艺
CN109322158B (zh) 一种单面防水织物及其制备方法
CN101956329B (zh) 一种亮光印花涂层涤纶布的制备工艺
CN107287917A (zh) 一种仿厚牛皮高档沙发装饰面料生产工艺
CN115612756A (zh) 一种白色运动鞋面革的涂饰工艺
WO2021243749A1 (fr) Matériau composite intégré au cuir à double face et procédé de préparation associé
CN104233843A (zh) 一种pu贴膜革的生产工艺
CN102133804A (zh) 一种皮质保暖面料
CN113123142B (zh) 一种可压花、高物性水性pu无溶剂鞋里革及其制备方法
CN108824010A (zh) 一种按摩椅用环保超纤革及其制备方法
CN212505582U (zh) 一种毛革一体复合材料及真毛革一体复合材料
CN203807860U (zh) 一种防水透湿格栅印花织物
CN108914620A (zh) 一种足球用环保超纤革及其制备方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20939384

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20939384

Country of ref document: EP

Kind code of ref document: A1