WO2020143532A1 - 正极活性材料及其制备方法、钠离子电池及包含钠离子电池的装置 - Google Patents
正极活性材料及其制备方法、钠离子电池及包含钠离子电池的装置 Download PDFInfo
- Publication number
- WO2020143532A1 WO2020143532A1 PCT/CN2020/070136 CN2020070136W WO2020143532A1 WO 2020143532 A1 WO2020143532 A1 WO 2020143532A1 CN 2020070136 W CN2020070136 W CN 2020070136W WO 2020143532 A1 WO2020143532 A1 WO 2020143532A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- active material
- positive electrode
- electrode active
- sodium
- sodium ion
- Prior art date
Abstract
Description
Claims (12)
- 根据权利要求1所述的正极活性材料,其中,所述正极活性材料满足1≤z/y≤12,优选3≤z/y≤9。
- 根据权利要求1或2所述的正极活性材料,其中,所述正极活性材料的晶胞参数满足3.8510≤c/a≤4.9000,优选3.8602≤c/a≤3.8800。
- 根据权利要求1-3任一项所述的正极活性材料,其中,所述正极活性材料的平均粒径D v50为3μm~20μm,优选为5μm~12μm。
- 根据权利要求1-4任一项所述的正极活性材料,其中,所述正极活性材料的比表面积为0.01m 2/g~6m 2/g,优选为0.5m 2/g~4m 2/g。
- 根据权利要求1-5任一项所述的正极活性材料,其中,所述正极活性材料具有六方相晶体结构。
- 根据权利要求1-6任一项所述的正极活性材料,其中,所述正极活性材料在12MPa压力下的粉体电阻率为20Ω·cm~10000Ω·cm,优选为20Ω·cm~1000Ω·cm。
- 根据权利要求1-7任一项所述的正极活性材料,其中,所述正极活性材料的振实密度≥1.5g/cm 3,优选为1.5g/cm 3~3.0g/cm 3;和/或,所述正极活性材料在8吨压力下的压实密度≥3g/cm 3,优选为3.5g/cm 3~5g/cm 3。
- 根据权利要求1-8任一项所述的正极活性材料,其中,所述正极活性材料的形貌为多边形片状结构,优选为六边形片状结构。
- 一种钠离子电池,包括正极片,所述正极片包括权利要求1-9任一项所述的正极活性材料。
- 一种装置,包括权利要求11所述的钠离子电池。