WO2016121801A1 - Encre absorbant les infrarouges - Google Patents

Encre absorbant les infrarouges Download PDF

Info

Publication number
WO2016121801A1
WO2016121801A1 PCT/JP2016/052288 JP2016052288W WO2016121801A1 WO 2016121801 A1 WO2016121801 A1 WO 2016121801A1 JP 2016052288 W JP2016052288 W JP 2016052288W WO 2016121801 A1 WO2016121801 A1 WO 2016121801A1
Authority
WO
WIPO (PCT)
Prior art keywords
infrared absorbing
infrared
ink
solvent
mass
Prior art date
Application number
PCT/JP2016/052288
Other languages
English (en)
Japanese (ja)
Inventor
文人 小林
渉 吉住
正太 川▲崎▼
芝岡　良昭
優徳 秋元
博昭 島根
Original Assignee
共同印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 共同印刷株式会社 filed Critical 共同印刷株式会社
Priority to JP2016572093A priority Critical patent/JP6403806B2/ja
Publication of WO2016121801A1 publication Critical patent/WO2016121801A1/fr

Abstract

La présente invention vise à procurer une encre absorbant les infrarouges qui présente d'excellentes propriétés d'absorption des infrarouges et de sécurité et peut être utilisée en tant qu'encre d'imprimerie pour la prévention des falsifications. L'encre absorbant les infrarouges selon la présente invention comprend : 1,0 % en masse à 25 % en masse de fines particules d'au un ou plusieurs types de matériau absorbant les infrarouges choisis parmi les oxydes de tungstène composites représentés par la formule générale MxWyOz (M, W, O, x, y et z dans la formule étant tels que définis dans la description) ou les oxydes de tungstène ayant une phase Magneli représentés par la formule générale WyOz (W, O, y et z dans la formule étant tels que définis dans la description) ; et un vecteur. Le vecteur comprend un premier solvant choisi parmi des huiles végétales ou des composés dérivés d'huile végétale, un deuxième solvant choisi parmi des alcools et ayant un point d'ébullition de 180 °C ou moins, et une résine. La teneur du deuxième solvant est de 2 % en masse ou moins par rapport à la masse de l'encre absorbant les infrarouges.
PCT/JP2016/052288 2015-01-27 2016-01-27 Encre absorbant les infrarouges WO2016121801A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2016572093A JP6403806B2 (ja) 2015-01-27 2016-01-27 赤外線吸収性インキ

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015-013572 2015-01-27
JP2015013572 2015-01-27

Publications (1)

Publication Number Publication Date
WO2016121801A1 true WO2016121801A1 (fr) 2016-08-04

Family

ID=56543411

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/052288 WO2016121801A1 (fr) 2015-01-27 2016-01-27 Encre absorbant les infrarouges

Country Status (3)

Country Link
JP (1) JP6403806B2 (fr)
TW (1) TW201700641A (fr)
WO (1) WO2016121801A1 (fr)

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017104855A1 (fr) * 2015-12-18 2017-06-22 住友金属鉱山株式会社 Composition pour encre anti-contrefaçon, encre anti-contrefaçon, article imprimé pour la prévention de la contrefaçon, et procédé de production de composition pour encre anti-contrefaçon
WO2018235820A1 (fr) * 2017-06-19 2018-12-27 住友金属鉱山株式会社 Composition d'encre anti-contrefaçon, encre anti-contrefaçon, article imprimé pour prévention de contrefaçon, et procédé de production de composition d'encre anti-contrefaçon
WO2019021992A1 (fr) * 2017-07-24 2019-01-31 住友金属鉱山株式会社 Dispersion en poudre de microparticules absorbantes dans l'infrarouge, dispersion liquide comprenant cette dispersion en poudre de microparticules absorbantes dans l'infrarouge, encre comprenant cette dispersion en poudre de microparticules absorbantes dans l'infrarouge, encre prévenant la falsification, et objet imprimé pour prévention de la falsification
JP2019077797A (ja) * 2017-10-25 2019-05-23 ゼネラル株式会社 インクジェットインクとそれを用いた半立体画像の形成方法
CN110753730A (zh) * 2017-06-19 2020-02-04 住友金属矿山株式会社 近红外线固化型油墨组合物及其制造方法、近红外线固化膜以及光造型法
WO2020061629A1 (fr) * 2018-09-25 2020-04-02 Ccl Secure Pty Ltd Encre destinée à l'impression d'un document de sécurité et élément de sécurité sur un substrat destiné à un document de sécurité
WO2020061631A1 (fr) * 2018-09-25 2020-04-02 Ccl Secure Pty Ltd Documents de sécurité et dispositifs de sécurité comprenant des compositions absorbant les infrarouges
JP2020050690A (ja) * 2018-09-21 2020-04-02 共同印刷株式会社 赤外線吸収性ｕｖインキ及びその製造方法
WO2021049381A1 (fr) * 2019-09-13 2021-03-18 共同印刷株式会社 Objet imprimé
WO2021161430A1 (fr) * 2020-02-12 2021-08-19 共同印刷株式会社 Encre uv absorbant le rayonnement infrarouge, et procédé de fabrication de celle-ci
CN113755058A (zh) * 2021-09-24 2021-12-07 中钞印制技术研究院有限公司 油墨和印制品
EP3981604A4 (fr) * 2019-06-05 2022-08-10 Sumitomo Metal Mining Co., Ltd. Composition d'encre anti-contrefaçon, encre anti-contrefaçon et matière imprimée anti-contrefaçon
WO2023120513A1 (fr) * 2021-12-22 2023-06-29 共同印刷株式会社 Tissu imprimé permettant d'évaluer l'authenticité, et son procédé de production
CN117467310A (zh) * 2023-10-31 2024-01-30 珠海市铠信科技有限公司 防伪色浆、紫外光固化防伪喷墨墨水及其制备方法和应用

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7371376B2 (ja) * 2019-07-23 2023-10-31 住友金属鉱山株式会社 赤外線吸収微粒子含有組成物およびその製造方法
JP2022010821A (ja) * 2020-06-29 2022-01-17 共同印刷株式会社 赤外線吸収性紫外線硬化型インク及び赤外線吸収性印刷物

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005037932A1 (fr) * 2003-10-20 2005-04-28 Sumitomo Metal Mining Co., Ltd. Microparticules de matiere ecran anti-infrarouge, dispersion de telles microparticules, leur procede de production, et ecran ainsi realise
JP2006143778A (ja) * 2004-11-16 2006-06-08 Sun Bijutsu Insatsu Kk 情報担持シート及びそのための印刷インキ
JP2008291167A (ja) * 2007-05-28 2008-12-04 Toyo Ink Mfg Co Ltd 平版インキ組成物
WO2012128332A1 (fr) * 2011-03-24 2012-09-27 旭硝子株式会社 Composition liquide, son procédé de production, et article en verre
JP2012229388A (ja) * 2011-04-14 2012-11-22 Sumitomo Metal Mining Co Ltd 熱線遮蔽微粒子含有組成物の製造方法および熱線遮蔽微粒子含有組成物、当該熱線遮蔽微粒子含有組成物を用いた熱線遮蔽膜および当該熱線遮蔽膜を用いた熱線遮蔽合わせ透明基材
JP2012532822A (ja) * 2009-07-07 2012-12-20 ビーエーエスエフ ソシエタス・ヨーロピア カリウム・セシウム・タングステンブロンズ粒子
JP2013112791A (ja) * 2011-11-30 2013-06-10 Sumitomo Metal Mining Co Ltd 赤外線遮蔽材料微粒子分散液とその製造方法および熱線遮蔽膜と熱線遮蔽合わせ透明基材
JP2013526625A (ja) * 2010-05-10 2013-06-24 バイエル・インテレクチュアル・プロパティ・ゲゼルシャフト・ミット・ベシュレンクテル・ハフツング 熱吸収特性と高い安定性を有するポリマー組成物
JP2015117353A (ja) * 2013-12-20 2015-06-25 住友金属鉱山株式会社 偽造防止インク及び偽造防止印刷物

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2005037932A1 (fr) * 2003-10-20 2005-04-28 Sumitomo Metal Mining Co., Ltd. Microparticules de matiere ecran anti-infrarouge, dispersion de telles microparticules, leur procede de production, et ecran ainsi realise
JP2006143778A (ja) * 2004-11-16 2006-06-08 Sun Bijutsu Insatsu Kk 情報担持シート及びそのための印刷インキ
JP2008291167A (ja) * 2007-05-28 2008-12-04 Toyo Ink Mfg Co Ltd 平版インキ組成物
JP2012532822A (ja) * 2009-07-07 2012-12-20 ビーエーエスエフ ソシエタス・ヨーロピア カリウム・セシウム・タングステンブロンズ粒子
JP2013526625A (ja) * 2010-05-10 2013-06-24 バイエル・インテレクチュアル・プロパティ・ゲゼルシャフト・ミット・ベシュレンクテル・ハフツング 熱吸収特性と高い安定性を有するポリマー組成物
WO2012128332A1 (fr) * 2011-03-24 2012-09-27 旭硝子株式会社 Composition liquide, son procédé de production, et article en verre
JP2012229388A (ja) * 2011-04-14 2012-11-22 Sumitomo Metal Mining Co Ltd 熱線遮蔽微粒子含有組成物の製造方法および熱線遮蔽微粒子含有組成物、当該熱線遮蔽微粒子含有組成物を用いた熱線遮蔽膜および当該熱線遮蔽膜を用いた熱線遮蔽合わせ透明基材
JP2013112791A (ja) * 2011-11-30 2013-06-10 Sumitomo Metal Mining Co Ltd 赤外線遮蔽材料微粒子分散液とその製造方法および熱線遮蔽膜と熱線遮蔽合わせ透明基材
JP2015117353A (ja) * 2013-12-20 2015-06-25 住友金属鉱山株式会社 偽造防止インク及び偽造防止印刷物

Cited By (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017104855A1 (fr) * 2015-12-18 2017-06-22 住友金属鉱山株式会社 Composition pour encre anti-contrefaçon, encre anti-contrefaçon, article imprimé pour la prévention de la contrefaçon, et procédé de production de composition pour encre anti-contrefaçon
US11008476B2 (en) * 2015-12-18 2021-05-18 Sumitomo Metal Mining Co., Ltd. Anti-counterfeit ink composition, anti-counterfeit ink, anti-counterfeit printed matter, and method for producing the anti-counterfeit ink composition
US20190002712A1 (en) * 2015-12-18 2019-01-03 Sumitomo Metal Mining Co., Ltd. Anti-counterfeit ink composition, anti-counterfeit ink, anti-counterfeit printed matter, and method for producing the anti-counterfeit ink composition
EP3643757A4 (fr) * 2017-06-19 2021-03-24 Sumitomo Metal Mining Co., Ltd. Composition d'encre anti-contrefaçon, encre anti-contrefaçon, article imprimé pour prévention de contrefaçon, et procédé de production de composition d'encre anti-contrefaçon
WO2018235820A1 (fr) * 2017-06-19 2018-12-27 住友金属鉱山株式会社 Composition d'encre anti-contrefaçon, encre anti-contrefaçon, article imprimé pour prévention de contrefaçon, et procédé de production de composition d'encre anti-contrefaçon
CN110753730A (zh) * 2017-06-19 2020-02-04 住友金属矿山株式会社 近红外线固化型油墨组合物及其制造方法、近红外线固化膜以及光造型法
CN110770310A (zh) * 2017-06-19 2020-02-07 住友金属矿山株式会社 防伪油墨用组合物、防伪油墨、防伪用印刷物以及防伪油墨用组合物的制造方法
KR20200019870A (ko) * 2017-06-19 2020-02-25 스미토모 긴조쿠 고잔 가부시키가이샤 위조 방지 잉크용 조성물, 위조 방지 잉크, 및 위조 방지용 인쇄물, 및 위조 방지 잉크용 조성물의 제조 방법
JP7140117B2 (ja) 2017-06-19 2022-09-21 住友金属鉱山株式会社 偽造防止インク用組成物、偽造防止インク、および偽造防止用印刷物、並びに偽造防止インク用組成物の製造方法
US11807766B2 (en) 2017-06-19 2023-11-07 Sumitomo Metal Mining Co., Ltd. Anti-counterfeit ink composition, anti-counterfeit ink, anti-counterfeit printed matter, and method for producing the anti-counterfeit ink composition
KR102522325B1 (ko) * 2017-06-19 2023-04-18 스미토모 긴조쿠 고잔 가부시키가이샤 위조 방지 잉크용 조성물, 위조 방지 잉크, 및 위조 방지용 인쇄물, 및 위조 방지 잉크용 조성물의 제조 방법
JPWO2018235820A1 (ja) * 2017-06-19 2020-04-23 住友金属鉱山株式会社 偽造防止インク用組成物、偽造防止インク、および偽造防止用印刷物、並びに偽造防止インク用組成物の製造方法
AU2018289672B2 (en) * 2017-06-19 2023-08-10 Sumitomo Metal Mining Co., Ltd. Counterfeit-preventing ink composition, counterfeit-preventing ink, printed article for counterfeit prevention, and method for producing counterfeit-preventing ink composition
WO2019021992A1 (fr) * 2017-07-24 2019-01-31 住友金属鉱山株式会社 Dispersion en poudre de microparticules absorbantes dans l'infrarouge, dispersion liquide comprenant cette dispersion en poudre de microparticules absorbantes dans l'infrarouge, encre comprenant cette dispersion en poudre de microparticules absorbantes dans l'infrarouge, encre prévenant la falsification, et objet imprimé pour prévention de la falsification
IL272223B1 (en) * 2017-07-24 2023-09-01 Sumitomo Metal Mining Co Dispersion powder containing INFA red absorbent particles, dispersion liquid containing dispersion powder containing INFA red absorbent particles, ink containing dispersion powder containing INFA red absorbent particles, anti-counterfeiting ink, and anti-counterfeiting printed material
US11787949B2 (en) 2017-07-24 2023-10-17 Sumitomo Metal Mining Co., Ltd. Infrared absorbing fine particle dispersed powder, dispersion liquid containing infrared absorbing fine particle dispersed powder, ink containing infrared absorbing fine particle dispersed powder, and anti-counterfeit ink, and anti-counterfeit printed matter
JPWO2019021992A1 (ja) * 2017-07-24 2020-05-28 住友金属鉱山株式会社 赤外線吸収微粒子分散粉、赤外線吸収微粒子分散粉含有分散液、赤外線吸収微粒子分散粉含有インク、および偽造防止インク、並びに偽造防止用印刷物
JP7259748B2 (ja) 2017-07-24 2023-04-18 住友金属鉱山株式会社 赤外線吸収微粒子分散粉、赤外線吸収微粒子分散粉含有分散液、赤外線吸収微粒子分散粉含有インク、および偽造防止インク、並びに偽造防止用印刷物
JP2019077797A (ja) * 2017-10-25 2019-05-23 ゼネラル株式会社 インクジェットインクとそれを用いた半立体画像の形成方法
JP7122920B2 (ja) 2018-09-21 2022-08-22 共同印刷株式会社 赤外線吸収性ｕｖインキ及びその製造方法
JP2020050690A (ja) * 2018-09-21 2020-04-02 共同印刷株式会社 赤外線吸収性ｕｖインキ及びその製造方法
WO2020061629A1 (fr) * 2018-09-25 2020-04-02 Ccl Secure Pty Ltd Encre destinée à l'impression d'un document de sécurité et élément de sécurité sur un substrat destiné à un document de sécurité
GB2592151A (en) * 2018-09-25 2021-08-18 Ccl Secure Pty Ltd Security documents and security devices comprising infrared-absorbent compositions
WO2020061631A1 (fr) * 2018-09-25 2020-04-02 Ccl Secure Pty Ltd Documents de sécurité et dispositifs de sécurité comprenant des compositions absorbant les infrarouges
EP3981604A4 (fr) * 2019-06-05 2022-08-10 Sumitomo Metal Mining Co., Ltd. Composition d'encre anti-contrefaçon, encre anti-contrefaçon et matière imprimée anti-contrefaçon
WO2021049381A1 (fr) * 2019-09-13 2021-03-18 共同印刷株式会社 Objet imprimé
JPWO2021049381A1 (fr) * 2019-09-13 2021-03-18
EP4030344A4 (fr) * 2019-09-13 2023-10-11 Kyodo Printing Co., Ltd. Objet imprimé
US20220348034A1 (en) * 2019-09-13 2022-11-03 Kyodo Printing Co., Ltd. Printed object
CN114341284A (zh) * 2019-09-13 2022-04-12 共同印刷株式会社 印刷物
JP7433329B2 (ja) 2019-09-13 2024-02-19 共同印刷株式会社 印刷物
WO2021161430A1 (fr) * 2020-02-12 2021-08-19 共同印刷株式会社 Encre uv absorbant le rayonnement infrarouge, et procédé de fabrication de celle-ci
CN113755058A (zh) * 2021-09-24 2021-12-07 中钞印制技术研究院有限公司 油墨和印制品
WO2023120513A1 (fr) * 2021-12-22 2023-06-29 共同印刷株式会社 Tissu imprimé permettant d'évaluer l'authenticité, et son procédé de production
CN117467310A (zh) * 2023-10-31 2024-01-30 珠海市铠信科技有限公司 防伪色浆、紫外光固化防伪喷墨墨水及其制备方法和应用

Also Published As

Publication number Publication date
JPWO2016121801A1 (ja) 2017-10-05
JP6403806B2 (ja) 2018-10-10
TW201700641A (zh) 2017-01-01

Similar Documents

Publication Publication Date Title
JP6403806B2 (ja) 赤外線吸収性インキ
AU2016213105B2 (en) Near-infrared ray absorbing microparticle dispersion solution and production method thereof
JP6541400B2 (ja) 偽造防止用インキ及びその印刷物
US11084949B2 (en) Near infrared absorbing fine particle dispersion liquid and method for producing the same, anti-counterfeit ink composition using near infrared absorbing fine particle dispersion liquid, and anti-counterfeit printed matter using near infrared absorbing fine particles
JP2014514367A (ja) 印刷用インクの凝固特性および耐摩擦性を改善するための組成物および方法
KR20220016039A (ko) 위조 방지 잉크용 조성물, 위조 방지 잉크, 위조 방지용 인쇄물
CN104629524A (zh) 红外线吸收性的油性胶印油墨
WO2015068290A1 (fr) Encre pour impression en creux absorbant les infrarouges
WO2015068289A1 (fr) Encre pour impression typographique absorbant les infrarouges
WO2015068283A1 (fr) Encre pour impression offset absorbant dans l'infrarouge
KR102313716B1 (ko) 인쇄적성과 작업적성 개선을 위한 요판잉크 및 이의 제조방법
WO2015068281A1 (fr) Encre pour sérigraphie à absorption dans l'infrarouge
TW201518446A (zh) 紅外線吸收性平凸印刷墨
WO2015068280A1 (fr) Encre d'héliogravure absorbant les infrarouges
WO2015068291A1 (fr) Article imprimé
TW201518426A (zh) 紅外線吸收性凹版印刷墨
TW201518427A (zh) 紅外線吸收性柔版印刷墨
TW201908420A (zh) 分散著紅外線吸收微粒子之粉末、含有分散著紅外線吸收微粒子之粉末的分散液、含有分散著紅外線吸收微粒子之粉末的油墨、及防偽油墨暨防偽用印刷物
TW201518428A (zh) 紅外線吸收性照相凹版印刷墨
TW201518429A (zh) 紅外線吸收性網版印刷墨
TW201518430A (zh) 印刷物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16743404

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2016572093

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16743404

Country of ref document: EP

Kind code of ref document: A1