WO2016039157A1 - 電極材料およびそれを用いた電極層、電池並びにエレクトロクロミック素子 - Google Patents
電極材料およびそれを用いた電極層、電池並びにエレクトロクロミック素子 Download PDFInfo
- Publication number
- WO2016039157A1 WO2016039157A1 PCT/JP2015/074197 JP2015074197W WO2016039157A1 WO 2016039157 A1 WO2016039157 A1 WO 2016039157A1 JP 2015074197 W JP2015074197 W JP 2015074197W WO 2016039157 A1 WO2016039157 A1 WO 2016039157A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- powder
- electrode material
- tungsten oxide
- electrode
- less
- Prior art date
Abstract
Description
(1)酸化タングステン:WO3-x、0≦x≦1。
(2)酸化モリブデン:MoO3-x、0≦x≦1。
(3)酸化チタン:TiO2-x、0≦x≦1。
(4)MoxWyOz、0<x≦1、0<y≦1、x+y=1としたとき2≦z≦3。
(5)WxTiyOz、0<x≦1、0<y≦1、x+y=1としたとき2≦z≦3。
(6)MoxTiyOz、0<x≦1、0<y≦1、x+y=1としたとき2≦z≦3。
(7)MoxWyOzTiα、0<x≦1、0<y≦1、0<α≦1、x+y+α=1としたとき2≦z≦3。
(8)タングステン酸リチウム:LixWyO3-z、0<x≦1、0<y≦1、0≦z≦1。
(9)モリブデン酸リチウム:LixMoyO3-z、0<x≦1、0<y≦1、0≦z≦1。
(10)チタン酸リチウム:LixTiyO3-z、0<x≦1、0<y≦1、0≦z≦1。
(11)硫化モリブデン:MoS2-x、0<x≦1。
(実施例1~3および比較例1~2)
原料粉末として平均粒径が1.5μmの酸化タングステン粉末を用意した。この原料粉末を、空気をキャリアガスとして誘導結合プラズマ炎に平均流速が1.5m/sとなるように噴霧し、原料粉末を昇華させながら酸化反応を行う昇華工程により酸化タングステン(WO3)粉末を得た。得られた酸化タングステン(WO3)粉末の平均粒径は8.2nm(0.008μm)であった。
原料粉末として平均粒径が2.0μmの酸化タングステン粉末を用意した。この原料粉末を、空気をキャリアガスとして誘導結合プラズマ炎に平均流速1.2m/sとなるように噴霧し、原料粉末を昇華させながら酸化反応を行う昇華工程により酸化タングステン(WO3)粉末を得た。得られた酸化タングステン(WO3)粉末の平均粒径は12.1nm(0.0012μm)であった。
実施例1~3および比較例1~2に係る酸化タングステン粉末を使用してキャパシタを作製した。キャパシタの構成は図8に示す。図8中、符号20はキャパシタであり、21は負極側電極層であり、22は負極層であり、23はセパレータ層であり、24は正極層であり、25は正極側電極層である。負極側電極層21および正極側電極層25は厚さ15μmのアルミ箔から成る。
平均粒径が1 μmである酸化モリブデン(MoO3)粉末を用意した。この酸化モリブデン粉末に対し、大気中で60分間の熱処理を実施した。
電極材料を実施例5~6および比較例3に代えた以外は実施例1と同様に処理して実施例5A~6Aおよび比較例3Aに係るキャパシタを作製した。各キャパシタについて、実施例1Aと同様の方法で初期の電気容量、サイクル試験後の容量維持率、内部抵抗値を測定した。その測定結果を下記表10に示す。
実施例2の酸化タングステン粉末の窒素中での熱処理条件を、窒素と水素との混合ガスに変えたものを実施例7とした。なお、窒素と水素の混合ガスは水素を3vol%、残部が窒素からなるものである。また、熱処理条件は700℃×5分とした。
実施例2Aのキャパシタの電極材料を実施例7の酸化タングステン粉末に代えたキャパシタを作成し実施例7Aとした。実施例2Aと同様の測定方法で、初期の電気容量およびサイクル試験後の容量維持率を測定した。その測定結果を下記表13に示す。
2 …測定用試料
3 …n-Si層
4 …SiO2層
5 …実施例(または比較例)の酸化タングステン粉末からなる電極層
6 …金属電極
20…キャパシタ
21…負極側電極層
22…負極層
23…セパレータ層
24…正極層
25…正極側電極層
Claims (12)
- 金属化合物粉末および炭素粉末の少なくとも1種の粉末から成る電極材料であり、上記粉末の平均粒径が50μm以下であり、活性化エネルギーEαが0.05eV以下であることを特徴とする電極材料。
- 前記粉末が常温(25℃)でホッピング伝導特性を有することを特徴とする請求項1記載の電極材料。
- 前記粉末の酸素欠損量が1×1018cm-3以上であることを特徴とする請求項1ないし請求項2のいずれか1項に記載の電極材料。
- 前記粉末のキャリア密度が1×1018cm-3以上であることを特徴とする請求項1ないし請求項3のいずれか1項に記載の電極材料。
- 前記金属化合物粉末は、酸化タングステン、酸化モリブデン、酸化チタン、タングステン酸リチウム、モリブデン酸リチウム、チタン酸リチウムおよび硫化モリブデンから選択される少なくとも1種であることを特徴とする請求項5記載の電極材料。
- 測定温度をT(°K)とした場合に、1000/T値が2.8~4.0の範囲で前記粉末がホッピング伝導特性を有することを特徴とする請求項1ないし請求項5のいずれか1項に記載の電極材料。
- 前記粉末の常温(25℃)での抵抗率が10Ωcm以下であることを特徴とする請求項1ないし請求項7のいずれか1項に記載の電極材料。
- 前記粉末の平均粒径が10μm以下であることを特徴とする請求項1ないし請求項7のいずれか1項に記載の電極材料。
- 請求項1ないし請求項8のいずれか1項に記載の電極材料を50質量%以上100質量%以下含有することを特徴とする電極層。
- 請求項9記載の電極層を具備したことを特徴とする電池。
- 請求項9記載の電極層を負極として具備したことを特徴とする請求項10記載の電池。
- 請求項1ないし請求項8のいずれか1項に記載の電極材料を具備したことを特徴とするエレクトロクロミック素子。