WO2015141808A1 - Cellule secondaire et solution d'électrolyte pour cellule secondaire - Google Patents

Cellule secondaire et solution d'électrolyte pour cellule secondaire Download PDF

Info

Publication number
WO2015141808A1
WO2015141808A1 PCT/JP2015/058371 JP2015058371W WO2015141808A1 WO 2015141808 A1 WO2015141808 A1 WO 2015141808A1 JP 2015058371 W JP2015058371 W JP 2015058371W WO 2015141808 A1 WO2015141808 A1 WO 2015141808A1
Authority
WO
WIPO (PCT)
Prior art keywords
electrolyte
metal
secondary battery
negative electrode
positive electrode
Prior art date
Application number
PCT/JP2015/058371
Other languages
English (en)
Japanese (ja)
Inventor
裕之 小堀
千紘 中村
Original Assignee
大日本印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大日本印刷株式会社 filed Critical 大日本印刷株式会社
Priority to JP2015554375A priority Critical patent/JP5892434B2/ja
Publication of WO2015141808A1 publication Critical patent/WO2015141808A1/fr

Abstract

[Problème] Fournir : une nouvelle cellule secondaire pour laquelle le coût est faible, l'énergie est conservée, et avec laquelle le CO2 est réduit ; et une solution d'électrolyte pour une cellule secondaire. [Solution] Le problème est résolu par une cellule secondaire (10) selon l'invention ayant une électrode positive (1) contenant un métal en tant que substance active d'électrode positive, une électrode négative (2) et une solution d'électrolyte (3). La solution d'électrolyte (3) contient un électrolyte et un solvant, et l'électrolyte contient un composé ionique MX (où M est une substance ionique métallique et X est une substance anionique). Dans ce cas, l'électrolyte peut être configuré de manière à être dissous dans la solution d'électrolyte ou à être utilisé comme un solide, et l'électrode négative (2) peut être configurée de manière à contenir une substance active d'électrode négative pour métallisation, par réduction de la substance ionique métallique M ou stockage de la substance ionique métallique M.
PCT/JP2015/058371 2014-03-20 2015-03-19 Cellule secondaire et solution d'électrolyte pour cellule secondaire WO2015141808A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2015554375A JP5892434B2 (ja) 2014-03-20 2015-03-19 二次電池

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2014059152 2014-03-20
JP2014-059152 2014-03-20
JP2014-233215 2014-11-18
JP2014233215 2014-11-18

Publications (1)

Publication Number Publication Date
WO2015141808A1 true WO2015141808A1 (fr) 2015-09-24

Family

ID=54144770

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/058371 WO2015141808A1 (fr) 2014-03-20 2015-03-19 Cellule secondaire et solution d'électrolyte pour cellule secondaire

Country Status (3)

Country Link
JP (2) JP5892434B2 (fr)
TW (1) TW201543734A (fr)
WO (1) WO2015141808A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017126687A1 (fr) * 2016-01-22 2017-07-27 旭化成株式会社 Précurseur d'électrode positive
JP7343116B1 (ja) 2022-03-24 2023-09-12 恒 高橋 二次電池

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10826051B2 (en) 2016-12-19 2020-11-03 National Chung Shan Institute Of Science And Technology Method for producing anode material of lithium ion battery from flexible graphite powder
JP6873767B2 (ja) 2017-03-17 2021-05-19 株式会社東芝 二次電池、電池パック及び車両
FI129959B (en) * 2018-09-17 2022-11-30 Broadbit Batteries Oy A re-chargeable electrochemical cell, which comprises metallic electrodes, assembled in the disassembly mode

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04212269A (ja) * 1990-03-23 1992-08-03 Sanyo Electric Co Ltd アルカリ蓄電池
JP2000156242A (ja) * 1998-11-20 2000-06-06 Mitsubishi Chemicals Corp リチウム二次電池
JP2001118597A (ja) * 1999-10-14 2001-04-27 Toshiba Battery Co Ltd アルカリ二次電池
JP2003100347A (ja) * 2001-09-26 2003-04-04 Toshiba Corp 非水電解液電池および非水電解液
JP2004047416A (ja) * 2002-05-23 2004-02-12 Sanyo Electric Co Ltd 非水電解質電池
JP2004047406A (ja) * 2002-05-23 2004-02-12 Sanyo Electric Co Ltd 非水電解質二次電池
JP2007200616A (ja) * 2006-01-24 2007-08-09 Kri Inc エネルギー変換システム
JP2013525993A (ja) * 2010-04-27 2013-06-20 トヨタ モーター エンジニアリング アンド マニュファクチャリング ノース アメリカ マグネシウムアノード及び硫黄と適合性がある安定で安全な電解質を含む電気化学デバイス

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04212269A (ja) * 1990-03-23 1992-08-03 Sanyo Electric Co Ltd アルカリ蓄電池
JP2000156242A (ja) * 1998-11-20 2000-06-06 Mitsubishi Chemicals Corp リチウム二次電池
JP2001118597A (ja) * 1999-10-14 2001-04-27 Toshiba Battery Co Ltd アルカリ二次電池
JP2003100347A (ja) * 2001-09-26 2003-04-04 Toshiba Corp 非水電解液電池および非水電解液
JP2004047416A (ja) * 2002-05-23 2004-02-12 Sanyo Electric Co Ltd 非水電解質電池
JP2004047406A (ja) * 2002-05-23 2004-02-12 Sanyo Electric Co Ltd 非水電解質二次電池
JP2007200616A (ja) * 2006-01-24 2007-08-09 Kri Inc エネルギー変換システム
JP2013525993A (ja) * 2010-04-27 2013-06-20 トヨタ モーター エンジニアリング アンド マニュファクチャリング ノース アメリカ マグネシウムアノード及び硫黄と適合性がある安定で安全な電解質を含む電気化学デバイス

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017126687A1 (fr) * 2016-01-22 2017-07-27 旭化成株式会社 Précurseur d'électrode positive
JP6227840B1 (ja) * 2016-01-22 2017-11-08 旭化成株式会社 正極前駆体
CN108028138A (zh) * 2016-01-22 2018-05-11 旭化成株式会社 正极前体
CN108028138B (zh) * 2016-01-22 2019-05-03 旭化成株式会社 正极前体
US11107639B2 (en) 2016-01-22 2021-08-31 Asahi Kasei Kabushiki Kaisha Positive electrode precursor
JP7343116B1 (ja) 2022-03-24 2023-09-12 恒 高橋 二次電池
JP2023141529A (ja) * 2022-03-24 2023-10-05 恒 高橋 二次電池

Also Published As

Publication number Publication date
JPWO2015141808A1 (ja) 2017-04-13
TW201543734A (zh) 2015-11-16
JP2016103492A (ja) 2016-06-02
JP5892434B2 (ja) 2016-03-23

Similar Documents

Publication Publication Date Title
JP6246361B2 (ja) リチウム−硫黄電池用の正極およびその製造方法
JP5892434B2 (ja) 二次電池
US9614251B2 (en) High-performance rechargeable batteries with nanoparticle active materials, photochemically regenerable active materials, and fast solid-state ion conductors
JP2017059367A (ja) 二次電池、二次電池用電解液
CN108630988B (zh) 复合电解质、二次电池、电池包及车辆
JP2002110237A (ja) リチウム−硫黄電池用正極活物質組成物、その製造方法及びリチウム−硫黄電池
JP2015002168A (ja) 二次電池
JP5191931B2 (ja) イオン液体を用いたリチウム二次電池
JP2015109214A (ja) 集電体およびリチウムイオン二次電池
JP2015503187A (ja) 電気化学セル
CN108695542A (zh) 锂离子二次电池和其制造方法
JP2006252917A (ja) リチウムイオン二次電池
US20140315084A1 (en) Method and apparatus for energy storage
JP4569126B2 (ja) 非水電解液二次電池の充電方法及び非水電解液二次電池
JP2010086813A (ja) 非水電解質二次電池
JP2017059370A (ja) 二次電池
JP4433021B2 (ja) 非水電解質電池
JP2008300179A (ja) 非水二次電池
JP2008077847A (ja) 非水二次電池用負極材料及びそれを用いた非水二次電池
JPH10208748A (ja) 非水電解質二次電池
JP2011142040A (ja) 固体電池モジュール
JP2017059366A (ja) 二次電池、二次電池用電解液
KR20240027734A (ko) 저가의 고 출력 밀도 리튬-이온 배터리
JP2022039816A (ja) 固体電解質、固体電解質の製造方法および複合体
JP2022039124A (ja) 固体電解質、固体電解質の製造方法および複合体

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2015554375

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15764264

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15764264

Country of ref document: EP

Kind code of ref document: A1