WO2011022879A1 - 发光元件、其制造方法及其发光方法 - Google Patents
发光元件、其制造方法及其发光方法 Download PDFInfo
- Publication number
- WO2011022879A1 WO2011022879A1 PCT/CN2009/073518 CN2009073518W WO2011022879A1 WO 2011022879 A1 WO2011022879 A1 WO 2011022879A1 CN 2009073518 W CN2009073518 W CN 2009073518W WO 2011022879 A1 WO2011022879 A1 WO 2011022879A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- light
- substrate
- emitting
- luminescent
- metal layer
- Prior art date
Description
Claims