WO2010092906A1 - Adhésif thermosensible et bande adhésive thermosensible - Google Patents

Adhésif thermosensible et bande adhésive thermosensible Download PDF

Info

Publication number
WO2010092906A1
WO2010092906A1 PCT/JP2010/051683 JP2010051683W WO2010092906A1 WO 2010092906 A1 WO2010092906 A1 WO 2010092906A1 JP 2010051683 W JP2010051683 W JP 2010051683W WO 2010092906 A1 WO2010092906 A1 WO 2010092906A1
Authority
WO
WIPO (PCT)
Prior art keywords
temperature
sensitive adhesive
crystalline polymer
chain crystalline
side chain
Prior art date
Application number
PCT/JP2010/051683
Other languages
English (en)
Japanese (ja)
Inventor
実 南地
伸一郎 河原
Original Assignee
ニッタ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ニッタ株式会社 filed Critical ニッタ株式会社
Priority to CN201080007840.0A priority Critical patent/CN102317399B/zh
Priority to JP2010550495A priority patent/JP5600604B2/ja
Publication of WO2010092906A1 publication Critical patent/WO2010092906A1/fr

Abstract

La présente invention concerne un adhésif thermosensible comprenant un polymère cristallin à chaîne latérale et présentant une adhésivité à des températures supérieures au point de fusion du polymère cristallin à chaîne latérale. Le polymère cristallin à chaîne latérale est composé d'un polymère réticulé obtenu par ajout d'un chélate métallique au polymère cristallin à chaîne latérale et par conduite d'une réaction de réticulation. Le polymère cristallin à chaîne latérale cristallise à une température inférieure au point de fusion et démontre une fluidité à des températures au-dessus du point de fusion. La bande adhésive thermosensible décrite comprend une couche adhésive composée de l'adhésif thermosensible sur un côté ou sur les deux côtés d'un film support.
PCT/JP2010/051683 2009-02-16 2010-02-05 Adhésif thermosensible et bande adhésive thermosensible WO2010092906A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201080007840.0A CN102317399B (zh) 2009-02-16 2010-02-05 感温性粘合剂及感温性粘合带
JP2010550495A JP5600604B2 (ja) 2009-02-16 2010-02-05 平板表示装置製造用感温性粘着剤および平板表示装置製造用感温性粘着テープ

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2009-033087 2009-02-16
JP2009033087 2009-02-16

Publications (1)

Publication Number Publication Date
WO2010092906A1 true WO2010092906A1 (fr) 2010-08-19

Family

ID=42561748

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2010/051683 WO2010092906A1 (fr) 2009-02-16 2010-02-05 Adhésif thermosensible et bande adhésive thermosensible

Country Status (5)

Country Link
JP (1) JP5600604B2 (fr)
KR (1) KR101639700B1 (fr)
CN (1) CN102317399B (fr)
TW (1) TWI498407B (fr)
WO (1) WO2010092906A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012197387A (ja) * 2011-03-23 2012-10-18 Nitta Corp 耐熱性感温性粘着剤
WO2014077115A1 (fr) * 2012-11-19 2014-05-22 日立オムロンターミナルソリューションズ株式会社 Adhésif doté de propriétés de pelage facile, et matériau adhésif doté de propriétés de pelage facile mettant en œuvre celui-ci
WO2015163115A1 (fr) * 2014-04-22 2015-10-29 日東電工株式会社 Feuille adhésive
JP2015209449A (ja) * 2014-04-24 2015-11-24 ニッタ株式会社 感温性粘着剤組成物
JP2016046312A (ja) * 2014-08-20 2016-04-04 ニッタ株式会社 Ｔｓｖウエハの製造方法
JP2016201465A (ja) * 2015-04-10 2016-12-01 ニッタ株式会社 セラミック電子部品のダイシング用感温性粘着シートおよびセラミック電子部品の製造方法
EP4039719A4 (fr) * 2019-09-30 2023-10-25 Nitta Corporation Additif pour films de régulation de lumière, et film de régulation de lumière thermosensible

Families Citing this family (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014188840A1 (fr) * 2013-05-24 2014-11-27 ニッタ株式会社 Adhésif thermosensible
CN105158957A (zh) 2013-07-03 2015-12-16 京东方科技集团股份有限公司 一种柔性显示器的制备方法和柔性显示器
TWI635591B (zh) * 2013-11-05 2018-09-11 千住金屬工業股份有限公司 焊料轉印薄片
CN106133102B (zh) * 2014-03-25 2019-08-20 霓达株式会社 感温性粘合剂
JP6289960B2 (ja) * 2014-03-27 2018-03-07 ニッタ株式会社 感温性粘着剤
KR20160009839A (ko) 2014-07-17 2016-01-27 동우 화인켐 주식회사 감온성 점착제 조성물 및 이를 포함하는 감온성 점착 테이프
KR20160100122A (ko) 2015-02-13 2016-08-23 동우 화인켐 주식회사 감온성 점착제 조성물 및 이를 포함하는 감온성 점착 테이프
KR20160114399A (ko) 2015-03-24 2016-10-05 동우 화인켐 주식회사 감온성 점착제 조성물 및 이를 포함하는 감온성 점착 테이프
KR102452985B1 (ko) * 2015-04-01 2022-10-11 니타 가부시키가이샤 감온성 점착제 조성물
KR102453521B1 (ko) * 2015-04-03 2022-10-12 니타 가부시키가이샤 감온성 점착 테이프 및 감온성 점착 시트
JP6595216B2 (ja) * 2015-06-04 2019-10-23 ニッタ株式会社 感温性粘着テープ
JP6789001B2 (ja) * 2016-05-17 2020-11-25 ニッタ株式会社 感温性粘着剤
JP6967908B2 (ja) * 2016-09-09 2021-11-17 ニッタ株式会社 感温性粘着シートおよびこれを用いるウエハの製造方法
JP6792509B2 (ja) * 2017-04-21 2020-11-25 ニッタ株式会社 感温性粘着剤
KR102031621B1 (ko) 2017-10-25 2019-10-14 (주)켐베이스 감온성 점착제 조성물
KR102232046B1 (ko) * 2018-12-27 2021-03-25 (주)이녹스첨단소재 감온성 점착제 조성물 및 이를 포함하는 감온성 점착 테이프
CN110041847B (zh) * 2019-04-24 2021-06-25 厦门市豪尔新材料股份有限公司 一种温控性粘离胶及包含其的温控性粘离膜
CN110655883B (zh) * 2019-09-24 2021-07-13 南京清尚新材料科技有限公司 一种冷关型粘合剂及其制备方法和一种粘合带的制备方法

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04507425A (ja) * 1989-05-11 1992-12-24 ランデック コーポレイション 温度活性接着剤アセンブリ
JPH06510548A (ja) * 1991-02-12 1994-11-24 ランデック コーポレイション 温度帯特異性感圧接着剤組成物、および接着アッセンブリ並びにその使用方法
JP2000355684A (ja) * 1999-06-15 2000-12-26 Nitta Ind Corp 部品の仮止め粘着テープ
JP2001127012A (ja) * 1999-10-26 2001-05-11 Rodel Nitta Kk 基板のダイシング方法
JP2003147300A (ja) * 2001-11-12 2003-05-21 Lintec Corp ウエハ裏面研削時の表面保護シートおよび半導体チップの製造方法
JP2005260187A (ja) * 2004-03-15 2005-09-22 Nitta Ind Corp 感温性粘着テープの剥離方法
JP2005336680A (ja) * 2004-05-31 2005-12-08 Nitta Ind Corp カツラ用固定材および固定テープ
JP2008179744A (ja) * 2007-01-26 2008-08-07 Nitta Ind Corp 粘着剤

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3485412B2 (ja) 1996-03-15 2004-01-13 ニッタ株式会社 積層セラミックコンデンサ積層工程用の仮止め粘着テープ及び積層セラミックコンデンサの製造方法
KR20060124940A (ko) 2005-06-01 2006-12-06 삼성전자주식회사 가요성 표시 장치의 제조 방법

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04507425A (ja) * 1989-05-11 1992-12-24 ランデック コーポレイション 温度活性接着剤アセンブリ
JPH06510548A (ja) * 1991-02-12 1994-11-24 ランデック コーポレイション 温度帯特異性感圧接着剤組成物、および接着アッセンブリ並びにその使用方法
JP2000355684A (ja) * 1999-06-15 2000-12-26 Nitta Ind Corp 部品の仮止め粘着テープ
JP2001127012A (ja) * 1999-10-26 2001-05-11 Rodel Nitta Kk 基板のダイシング方法
JP2003147300A (ja) * 2001-11-12 2003-05-21 Lintec Corp ウエハ裏面研削時の表面保護シートおよび半導体チップの製造方法
JP2005260187A (ja) * 2004-03-15 2005-09-22 Nitta Ind Corp 感温性粘着テープの剥離方法
JP2005336680A (ja) * 2004-05-31 2005-12-08 Nitta Ind Corp カツラ用固定材および固定テープ
JP2008179744A (ja) * 2007-01-26 2008-08-07 Nitta Ind Corp 粘着剤

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012197387A (ja) * 2011-03-23 2012-10-18 Nitta Corp 耐熱性感温性粘着剤
WO2014077115A1 (fr) * 2012-11-19 2014-05-22 日立オムロンターミナルソリューションズ株式会社 Adhésif doté de propriétés de pelage facile, et matériau adhésif doté de propriétés de pelage facile mettant en œuvre celui-ci
JP5961700B2 (ja) * 2012-11-19 2016-08-02 日立オムロンターミナルソリューションズ株式会社 易剥離性粘着剤及びそれを用いた易剥離性粘着材料
WO2015163115A1 (fr) * 2014-04-22 2015-10-29 日東電工株式会社 Feuille adhésive
JP5890596B1 (ja) * 2014-04-22 2016-03-22 日東電工株式会社 粘着シート
JP2016135878A (ja) * 2014-04-22 2016-07-28 日東電工株式会社 粘着シート
JP2019123884A (ja) * 2014-04-22 2019-07-25 日東電工株式会社 粘着シート
US10792902B2 (en) 2014-04-22 2020-10-06 Nitto Denko Corporation Pressure-sensitive adhesive sheet
JP2015209449A (ja) * 2014-04-24 2015-11-24 ニッタ株式会社 感温性粘着剤組成物
JP2016046312A (ja) * 2014-08-20 2016-04-04 ニッタ株式会社 Ｔｓｖウエハの製造方法
JP2016201465A (ja) * 2015-04-10 2016-12-01 ニッタ株式会社 セラミック電子部品のダイシング用感温性粘着シートおよびセラミック電子部品の製造方法
EP4039719A4 (fr) * 2019-09-30 2023-10-25 Nitta Corporation Additif pour films de régulation de lumière, et film de régulation de lumière thermosensible

Also Published As

Publication number Publication date
CN102317399B (zh) 2014-08-06
TW201033324A (en) 2010-09-16
JPWO2010092906A1 (ja) 2012-08-16
KR101639700B1 (ko) 2016-07-14
CN102317399A (zh) 2012-01-11
JP5600604B2 (ja) 2014-10-01
TWI498407B (zh) 2015-09-01
KR20110127124A (ko) 2011-11-24

Similar Documents

Publication Publication Date Title
JP5600604B2 (ja) 平板表示装置製造用感温性粘着剤および平板表示装置製造用感温性粘着テープ
JP5118350B2 (ja) 粘着剤
JP5512143B2 (ja) 感温性粘着テープ
JP5231775B2 (ja) 感温性樹脂および感温性粘着剤、並びに感温性粘着テープ
CA2273890C (fr) Adhesif autocollant conducteur thermique, feuille adhesive contenant cet adhesif, et procede de fixation d'une piece electronique a un element emettant un rayonnement thermique aumoyen de cet adhesif
JP5408774B2 (ja) 感温性粘着剤および感温性粘着テープ
JP6754609B2 (ja) 感温性粘着剤
JP7460451B2 (ja) 感温性粘着剤
JP2011037944A (ja) 感温性粘着剤および感温性粘着テープ
JP2012197387A (ja) 耐熱性感温性粘着剤
JP6116368B2 (ja) 感温性粘着剤
JP2018178060A (ja) 感温性粘着剤
JP5554933B2 (ja) 感温性粘着剤
JP2010121090A (ja) 感温性粘着テープおよびこれを用いたチップ型電子部品の製造方法
KR20160100122A (ko) 감온성 점착제 조성물 및 이를 포함하는 감온성 점착 테이프
TWI740022B (zh) 感溫性黏著劑
JP6514551B2 (ja) セラミック電子部品のダイシング用感温性粘着シートおよびセラミック電子部品の製造方法
TW201807147A (zh) 感溫性黏著劑
KR102232046B1 (ko) 감온성 점착제 조성물 및 이를 포함하는 감온성 점착 테이프
JP5379455B2 (ja) 感温性粘着剤
JP2017031331A (ja) タッチセンサ転写用感温性粘着テープ
JP6789001B2 (ja) 感温性粘着剤
JP5433293B2 (ja) 粘着テープ
KR20160009839A (ko) 감온성 점착제 조성물 및 이를 포함하는 감온성 점착 테이프
WO2019163327A1 (fr) Adhésif thermosensible autocollant, feuille adhésive thermosensible autocollante et ruban adhésif thermosensible autocollant

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201080007840.0

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10741183

Country of ref document: EP

Kind code of ref document: A1

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
ENP Entry into the national phase

Ref document number: 20117016511

Country of ref document: KR

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2010550495

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10741183

Country of ref document: EP

Kind code of ref document: A1