WO2010058820A1 - Semi-conducteur au nitrure - Google Patents

Semi-conducteur au nitrure Download PDF

Info

Publication number
WO2010058820A1
WO2010058820A1 PCT/JP2009/069646 JP2009069646W WO2010058820A1 WO 2010058820 A1 WO2010058820 A1 WO 2010058820A1 JP 2009069646 W JP2009069646 W JP 2009069646W WO 2010058820 A1 WO2010058820 A1 WO 2010058820A1
Authority
WO
WIPO (PCT)
Prior art keywords
nitride semiconductor
gas
substrate
layer
quantum well
Prior art date
Application number
PCT/JP2009/069646
Other languages
English (en)
Japanese (ja)
Inventor
秀善 堀江
香 栗原
Original Assignee
三菱化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱化学株式会社 filed Critical 三菱化学株式会社
Publication of WO2010058820A1 publication Critical patent/WO2010058820A1/fr
Priority to US13/112,564 priority Critical patent/US8624220B2/en
Priority to US14/087,855 priority patent/US20140073118A1/en
Priority to US14/921,570 priority patent/US9711681B2/en

Abstract

L'invention porte sur un semi-conducteur au nitrure de haute qualité qui, lorsqu'il est produit en tant qu'élément électroluminescent, possède un rendement de luminescence élevé. Le semi-conducteur au nitrure comprend, superposées dans l'ordre suivant, une partie semi-conductrice au nitrure d'un premier type de conduction, une partie à structure de couche active à puits quantique, et une partie semi-conductrice au nitrure d'un autre type de conduction, qui est opposé au premier type de conduction. Lorsque ce semi-conducteur au nitrure est obtenu, des cristaux sont développés sur un substrat ayant une surface principale constituée d'un nitrure non polaire. La partie semi-conductrice au nitrure du premier type de conduction est formée par superposition d'une première couche semi-conductrice au nitrure et d'une seconde couche semi-conductrice au nitrure dans cet ordre, et la seconde couche semi-conductrice au nitrure est déposée en une épaisseur de 400 nm à 20 µm de façon à avoir une surface extérieure non polaire. Par sélection du substrat pour une croissance cristalline, on empêche les électrons et trous qui contribuent à la luminescence basée sur l'effet Stark de confinement quantique (QCSE) d'être spatialement séparés, et un rayonnement efficace est rendu possible. Par régulation de la seconde couche semi-conductrice au nitrure de façon à avoir l'épaisseur appropriée, on empêche le semi-conducteur au nitrure d'avoir une surface considérablement rugueuse.
PCT/JP2009/069646 2008-11-20 2009-11-19 Semi-conducteur au nitrure WO2010058820A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
US13/112,564 US8624220B2 (en) 2008-11-20 2011-05-20 Nitride semiconductor
US14/087,855 US20140073118A1 (en) 2008-11-20 2013-11-22 Nitride semiconductor
US14/921,570 US9711681B2 (en) 2008-11-20 2015-10-23 Nitride semiconductor

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2008297177A JP5453780B2 (ja) 2008-11-20 2008-11-20 窒化物半導体
JP2008-297177 2008-11-20

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US13/112,564 Continuation US8624220B2 (en) 2008-11-20 2011-05-20 Nitride semiconductor

Publications (1)

Publication Number Publication Date
WO2010058820A1 true WO2010058820A1 (fr) 2010-05-27

Family

ID=42198259

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2009/069646 WO2010058820A1 (fr) 2008-11-20 2009-11-19 Semi-conducteur au nitrure

Country Status (3)

Country Link
US (3) US8624220B2 (fr)
JP (1) JP5453780B2 (fr)
WO (1) WO2010058820A1 (fr)

Families Citing this family (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5090396B2 (ja) * 2009-03-27 2012-12-05 シャープ株式会社 窒化物半導体発光素子及びその製造方法、並びに、半導体光学装置
JP5004989B2 (ja) 2009-03-27 2012-08-22 シャープ株式会社 窒化物半導体発光素子及びその製造方法、並びに、半導体光学装置
JP4927121B2 (ja) 2009-05-29 2012-05-09 シャープ株式会社 窒化物半導体ウェハ、窒化物半導体素子および窒化物半導体素子の製造方法
JP2011146650A (ja) * 2010-01-18 2011-07-28 Sumitomo Electric Ind Ltd ＧａＮ系半導体発光素子およびその製造方法
JP5919703B2 (ja) * 2011-06-24 2016-05-18 サンケン電気株式会社 半導体装置
CN102368525A (zh) * 2011-10-27 2012-03-07 华灿光电股份有限公司 提高载流子复合效率的复合量子阱结构及其制备方法
US10177273B2 (en) 2012-03-29 2019-01-08 Seoul Viosys Co., Ltd. UV light emitting device
US10164150B2 (en) 2012-03-29 2018-12-25 Seoul Viosys Co., Ltd. Near UV light emitting device
US9224913B2 (en) * 2012-03-29 2015-12-29 Seoul Viosys Co., Ltd. Near UV light emitting device
KR101997020B1 (ko) * 2012-03-29 2019-07-08 서울바이오시스 주식회사 근자외선 발광 소자
US9312447B2 (en) 2012-03-29 2016-04-12 Seoul Viosys Co., Ltd. Near UV light emitting device
JP5934575B2 (ja) * 2012-05-16 2016-06-15 サンケン電気株式会社 窒化物半導体装置の製造方法
JP2012178609A (ja) * 2012-05-22 2012-09-13 Sharp Corp 窒化物半導体発光素子及びその製造方法、並びに、半導体光学装置
WO2014042054A1 (fr) * 2012-09-11 2014-03-20 株式会社トクヤマ Substrat en nitrure d'aluminium et stratifié en nitrure du groupe iii
CN108281378B (zh) * 2012-10-12 2022-06-24 住友电气工业株式会社 Iii族氮化物复合衬底、半导体器件及它们的制造方法
JP2014143255A (ja) * 2013-01-23 2014-08-07 Mitsubishi Chemicals Corp 窒化物系発光ダイオードの製造方法
KR102098250B1 (ko) 2013-10-21 2020-04-08 삼성전자 주식회사 반도체 버퍼 구조체, 이를 포함하는 반도체 소자 및 반도체 버퍼 구조체를 이용한 반도체 소자 제조방법
WO2015115685A1 (fr) * 2014-01-29 2015-08-06 광전자 주식회사 Diode électroluminescente à base d'aluminium-gallium-indium-phosphore ayant une couche de nitrure de gallium de type irrégulière et son procédé de production
KR102197080B1 (ko) * 2014-02-04 2020-12-31 엘지이노텍 주식회사 반도체 소자
JP6582736B2 (ja) * 2015-08-25 2019-10-02 富士電機株式会社 窒化物半導体装置の製造方法
JP6498635B2 (ja) * 2016-06-23 2019-04-10 信越半導体株式会社 貼り合わせｓｏｉウェーハの製造方法
JP6859084B2 (ja) * 2016-11-30 2021-04-14 住友化学株式会社 半導体基板
EP3340279A1 (fr) 2016-12-21 2018-06-27 IMEC vzw Procédé de croissance épitaxiale sélective d'une couche de nitrure du groupe iii
JP6906205B2 (ja) * 2017-08-01 2021-07-21 株式会社サイオクス 半導体積層物の製造方法および窒化物結晶基板の製造方法
JP7264343B2 (ja) * 2019-02-20 2023-04-25 パナソニックホールディングス株式会社 Ｉｉｉ族窒化物結晶の製造方法および種基板

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04273492A (ja) * 1991-02-28 1992-09-29 Toshiba Corp 半導体レーザ装置
JP2007201019A (ja) * 2006-01-24 2007-08-09 Sharp Corp 窒化物半導体発光素子とその製造方法
JP2008078613A (ja) * 2006-08-24 2008-04-03 Rohm Co Ltd 窒化物半導体の製造方法及び窒化物半導体素子
WO2008047907A1 (fr) * 2006-10-20 2008-04-24 Panasonic Electric Works Co., Ltd. Substrat de saphir, élément luminescent à semi-conducteur nitrure utilisant le substrat de saphir, et procédé destiné à fabriquer l'élément luminescent à semi-conducteur nitrure
JP2008235803A (ja) * 2007-03-23 2008-10-02 Rohm Co Ltd 窒化物半導体発光素子
WO2008126695A1 (fr) * 2007-04-06 2008-10-23 Sumitomo Electric Industries, Ltd. Dispositif électroluminescent à semi-conducteur de nitrure et son procédé de production

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5253262A (en) 1990-10-31 1993-10-12 Kabushiki Kaisha Toshiba Semiconductor laser device with multi-directional reflector arranged therein
JP3374737B2 (ja) 1997-01-09 2003-02-10 日亜化学工業株式会社 窒化物半導体素子
JP3929008B2 (ja) * 2000-01-14 2007-06-13 シャープ株式会社 窒化物系化合物半導体発光素子およびその製造方法
US7208393B2 (en) 2002-04-15 2007-04-24 The Regents Of The University Of California Growth of planar reduced dislocation density m-plane gallium nitride by hydride vapor phase epitaxy
JP2005311072A (ja) 2004-04-21 2005-11-04 Matsushita Electric Ind Co Ltd 発光素子および照明装置
JP4513422B2 (ja) 2004-06-02 2010-07-28 住友電気工業株式会社 半導体装置を製造する方法
JP5135686B2 (ja) * 2005-03-23 2013-02-06 住友電気工業株式会社 Ｉｉｉ族窒化物半導体素子
WO2009066466A1 (fr) 2007-11-21 2009-05-28 Mitsubishi Chemical Corporation Semi-conducteur au nitrure, procédé de croissance de cristal de semi-conducteur au nitrure, et élément luminescent à semi-conducteur au nitrure
US9048100B2 (en) 2007-11-21 2015-06-02 Mitsubishi Chemical Corporation Nitride semiconductor and nitride semiconductor crystal growth method

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH04273492A (ja) * 1991-02-28 1992-09-29 Toshiba Corp 半導体レーザ装置
JP2007201019A (ja) * 2006-01-24 2007-08-09 Sharp Corp 窒化物半導体発光素子とその製造方法
JP2008078613A (ja) * 2006-08-24 2008-04-03 Rohm Co Ltd 窒化物半導体の製造方法及び窒化物半導体素子
WO2008047907A1 (fr) * 2006-10-20 2008-04-24 Panasonic Electric Works Co., Ltd. Substrat de saphir, élément luminescent à semi-conducteur nitrure utilisant le substrat de saphir, et procédé destiné à fabriquer l'élément luminescent à semi-conducteur nitrure
JP2008235803A (ja) * 2007-03-23 2008-10-02 Rohm Co Ltd 窒化物半導体発光素子
WO2008126695A1 (fr) * 2007-04-06 2008-10-23 Sumitomo Electric Industries, Ltd. Dispositif électroluminescent à semi-conducteur de nitrure et son procédé de production

Also Published As

Publication number Publication date
US20110253974A1 (en) 2011-10-20
US20160043273A1 (en) 2016-02-11
US9711681B2 (en) 2017-07-18
US20140073118A1 (en) 2014-03-13
JP5453780B2 (ja) 2014-03-26
US8624220B2 (en) 2014-01-07
JP2010123803A (ja) 2010-06-03

Similar Documents

Publication Publication Date Title
JP5812166B2 (ja) 窒化物半導体の結晶成長方法
JP5453780B2 (ja) 窒化物半導体
JP6179624B2 (ja) 結晶成長方法および発光素子の製造方法
US6165812A (en) Gallium nitride compound semiconductor light emitting device and process for producing gallium nitride compound semiconductor
US20120248457A1 (en) Group iii nitride semiconductor multilayer structure and production method thereof
US10665753B2 (en) Vertical-type ultraviolet light-emitting diode
WO2009142311A1 (fr) Structure stratifiée de semi-conducteur au nitrure du groupe iii et procédé de fabrication de la structure stratifiée de semi-conducteur au nitrure du groupe iii
WO2013042297A1 (fr) Elément électroluminescent renfermant un composé de nitrure de gallium semi-conducteur et dispositif source de lumière l'utilisant
EP2071053B1 (fr) Procédé de dépôt en film pour une structure stratifiée de semi-conducteur de nitrure de groupe iii
JP5682716B2 (ja) 窒化物半導体
Zhou et al. Epitaxial Growth of III-Nitride LEDs
JP2980379B2 (ja) 窒化ガリウム系化合物半導体発光素子及び窒化ガリウム系化合物半導体の製造方法
Zhang Micro-structural and optical investigation of semi-polar (11-22) III-nitrides overgrown on regularly arrayed micro-rods
NAKARMI Al-RICH AlGaN ALLOYS AND AlN EPILAYERS

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09827601

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09827601

Country of ref document: EP

Kind code of ref document: A1