WO2009154301A1 - Bloc pour le traitement de prothèses dentaires, et son procédé de fabrication - Google Patents

Bloc pour le traitement de prothèses dentaires, et son procédé de fabrication Download PDF

Info

Publication number
WO2009154301A1
WO2009154301A1 PCT/JP2009/061541 JP2009061541W WO2009154301A1 WO 2009154301 A1 WO2009154301 A1 WO 2009154301A1 JP 2009061541 W JP2009061541 W JP 2009061541W WO 2009154301 A1 WO2009154301 A1 WO 2009154301A1
Authority
WO
WIPO (PCT)
Prior art keywords
block
composite resin
resin material
curing
color
Prior art date
Application number
PCT/JP2009/061541
Other languages
English (en)
Japanese (ja)
Inventor
紺谷和生
江口未来
Original Assignee
株式会社アドバンス
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社アドバンス filed Critical 株式会社アドバンス
Priority to JP2010518045A priority Critical patent/JPWO2009154301A1/ja
Publication of WO2009154301A1 publication Critical patent/WO2009154301A1/fr

Abstract

L'invention porte sur un procédé de fabrication de blocs de traitement de prothèses dentaires qui sont utilisés lors de la fabrication de prothèses dentaires par CAO/FAO. Un moule, dont la surface intérieure a la forme de la forme extérieure d'un bloc, est partiellement rempli d'un matériau de résine qui contient un matériau de remplissage inorganique. Ensuite, on exécute une agitation rotative, suivie par un durcissement de polymère. Par la répétition du processus, on peut également fabriquer non seulement des blocs monochromatiques, mais également des blocs avec des gradients de couleur. Les blocs de traitement obtenus sont robustes même après traitement, d'une excellente esthétique et peuvent être fabriqués par un procédé plus simple.
PCT/JP2009/061541 2008-06-18 2009-06-18 Bloc pour le traitement de prothèses dentaires, et son procédé de fabrication WO2009154301A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2010518045A JPWO2009154301A1 (ja) 2008-06-18 2009-06-18 歯科補綴物加工用ブロック及びその製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2008159573 2008-06-18
JP2008-159573 2008-06-18

Publications (1)

Publication Number Publication Date
WO2009154301A1 true WO2009154301A1 (fr) 2009-12-23

Family

ID=41434210

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2009/061541 WO2009154301A1 (fr) 2008-06-18 2009-06-18 Bloc pour le traitement de prothèses dentaires, et son procédé de fabrication

Country Status (2)

Country Link
JP (1) JPWO2009154301A1 (fr)
WO (1) WO2009154301A1 (fr)

Cited By (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011162286A1 (fr) * 2010-06-25 2011-12-29 パナソニック電工株式会社 Corps moulé pour travail de coupe dentaire, et procédé de fabrication de celui-ci
WO2012042911A1 (fr) * 2010-09-30 2012-04-05 クラレメディカル株式会社 Ébauche dentaire
JP2012078644A (ja) * 2010-10-04 2012-04-19 Jsr Corp 歯牙模型および歯牙模型ブロック、ならびにそれらの製造方法
KR101221026B1 (ko) 2012-09-14 2013-01-10 고찬중 크라운 제조방법 및 이를 이용한 크라운
WO2014021343A1 (fr) 2012-07-31 2014-02-06 クラレノリタケデンタル株式会社 Procédé pour la fabrication de ciment dentaire blanc broyé
WO2015045698A1 (fr) * 2013-09-24 2015-04-02 株式会社ジーシー Procédé pour fabriquer un bloc de résine dentaire
JP5944602B1 (ja) * 2016-01-13 2016-07-05 株式会社松風 透明性が異なる多層構造を有したファイバー材含有の歯科切削加工用ブロック状複合材料。
WO2016148289A1 (fr) * 2015-03-19 2016-09-22 クラレノリタケデンタル株式会社 Unité à façonner, et procédé de fabrication de celle-ci
JP2016174684A (ja) * 2015-03-19 2016-10-06 株式会社ジーシー セラミックスブランク
JP2017006728A (ja) * 2012-06-01 2017-01-12 スリーエム イノベイティブ プロパティズ カンパニー カスタマイズされた歯科用ブランク製造方法及びシステム
WO2017098096A1 (fr) * 2015-12-10 2017-06-15 Societe De Recherches Techniques Dentaires - Rtd Disque usinable par cfao pour la fabrication d'inlay core fibres
JP2017109036A (ja) * 2015-12-18 2017-06-22 クラレノリタケデンタル株式会社 歯科用ミルブランクの製造方法及びその製造方法により得られた歯科用ミルブランク
WO2017154850A1 (fr) * 2016-03-07 2017-09-14 クラレノリタケデンタル株式会社 Ébauche de fraise dentaire et son procédé de production
WO2018002960A1 (fr) * 2016-06-30 2018-01-04 Dws S.R.L. Procédé et système de fabrication de prothèses dentaires
EP3275851A1 (fr) 2016-07-29 2018-01-31 Shofu Inc. Corps dentaire calciné temporairement ayant un intérieur coloré
WO2018049331A1 (fr) * 2016-09-09 2018-03-15 Jensen Industries Inc. Ébauche de zircone ayant un gradient de couleurs et procédés pour la préparer
JP2018042894A (ja) * 2016-09-16 2018-03-22 ローランドディー．ジー．株式会社 歯冠補綴物作製システム、歯冠補綴物作製方法および歯冠補綴物作製のためのプログラム
JP2018042895A (ja) * 2016-09-16 2018-03-22 ローランドディー．ジー．株式会社 歯冠補綴物作製システム、歯冠補綴物作製方法および歯冠補綴物作製のためのプログラム
JP2018126588A (ja) * 2012-05-10 2018-08-16 レニショウ パブリック リミテッド カンパニーＲｅｎｉｓｈａｗ Ｐｕｂｌｉｃ Ｌｉｍｉｔｅｄ Ｃｏｍｐａｎｙ 物品を製造する方法
JPWO2018074583A1 (ja) * 2016-10-20 2018-12-06 Ｙａｍａｋｉｎ株式会社 歯科切削加工用複合レジン材料及びその製造方法
JP2018537230A (ja) * 2015-12-15 2018-12-20 クルツァー ゲゼルシャフト ミット ベシュレンクテル ハフツングＫｕｌｚｅｒ ＧｍｂＨ 重合した大きな歯科材料ブロックを製造する方法
JP2019000683A (ja) * 2018-09-05 2019-01-10 株式会社ジーシー セラミックスブランク
JPWO2018230657A1 (ja) * 2017-06-14 2020-05-21 クラレノリタケデンタル株式会社 歯科用ミルブランク
JP2020099600A (ja) * 2018-12-25 2020-07-02 株式会社トクヤマデンタル 加工用接合構造
WO2020185086A1 (fr) * 2019-03-14 2020-09-17 Identiq Tandtechniek Procédé permettant de fournir une couleur naturelle et une profondeur optique à un objet dentaire
US10898302B2 (en) 2016-04-25 2021-01-26 3M Innovative Properties Company Multi-layered zirconia dental mill blank and process of production
US10905531B2 (en) 2016-07-29 2021-02-02 Shofu Inc. Mill blank for dental CAD/CAM with groove not extending over whole of circumference
US11033369B2 (en) 2015-08-28 2021-06-15 Shofu Inc. Dental mill blank having multiple layers that are visually identifiable
CN113730264A (zh) * 2021-09-01 2021-12-03 爱迪特（秦皇岛）科技股份有限公司 一种牙科用渐变色树脂陶瓷修复材料及其制备方法
JPWO2020166667A1 (ja) * 2019-02-14 2021-12-09 クラレノリタケデンタル株式会社 歯科用ミルブランク
KR20220066478A (ko) * 2020-11-16 2022-05-24 주식회사 바이오덴 치과용 하이브리드 레진 블록 조성물 및 이를 이용한 치과용 하이브리드 레진 블록의 제조 방법
WO2022209951A1 (fr) * 2021-03-29 2022-10-06 キヤノン株式会社 Procédé d'estimation de couleur pour prothèse dentaire, dispositif de traitement d'informations, procédé de production de prothèse dentaire, procédé de traitement d'informations, et programme
WO2022248775A1 (fr) * 2021-05-27 2022-12-01 Societe De Recherches Techniques Dentaires Bloc usinable par cfao pour la fabrication d'élément prothétique dentaire notamment d'inlay-core fibré
EP3943041A4 (fr) * 2019-03-20 2022-12-14 Kuraray Noritake Dental Inc. Dispositif de coloration de prothèse dentaire, dispositif de traitement, et procédé de coloration
WO2023032728A1 (fr) 2021-09-06 2023-03-09 株式会社トクヤマデンタル Procédé de confirmation de couleur d'aspect de couronne, kit d'appareil et appareil de démonstration

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7018257B2 (ja) * 2016-06-28 2022-02-10 株式会社ジーシーデンタルプロダクツ 歯科用レジン硬化体の製造方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1094551A (ja) * 1996-05-17 1998-04-14 Brandestini Marco 歯科用構成物の製作方法および該方法を実施するためのブランク
JPH11104404A (ja) * 1997-10-01 1999-04-20 Eme:Kk 混練脱泡方法とその装置
JPH11290668A (ja) * 1998-04-13 1999-10-26 Shinkii:Kk 攪拌脱泡装置
JP2004035332A (ja) * 2002-07-03 2004-02-05 Advance Co Ltd セラミックスブロック
JP2004516066A (ja) * 2000-12-18 2004-06-03 スリーエム イノベイティブ プロパティズ カンパニー 歯科用ミルブランク組立体およびその作製方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH1094551A (ja) * 1996-05-17 1998-04-14 Brandestini Marco 歯科用構成物の製作方法および該方法を実施するためのブランク
JPH11104404A (ja) * 1997-10-01 1999-04-20 Eme:Kk 混練脱泡方法とその装置
JPH11290668A (ja) * 1998-04-13 1999-10-26 Shinkii:Kk 攪拌脱泡装置
JP2004516066A (ja) * 2000-12-18 2004-06-03 スリーエム イノベイティブ プロパティズ カンパニー 歯科用ミルブランク組立体およびその作製方法
JP2004035332A (ja) * 2002-07-03 2004-02-05 Advance Co Ltd セラミックスブロック

Cited By (76)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPWO2011162286A1 (ja) * 2010-06-25 2013-08-22 パナソニック株式会社 歯科切削加工用成形体及びその製造方法
WO2011162286A1 (fr) * 2010-06-25 2011-12-29 パナソニック電工株式会社 Corps moulé pour travail de coupe dentaire, et procédé de fabrication de celui-ci
US9320579B2 (en) 2010-06-25 2016-04-26 Panasonic Healthcare Holdings Co., Ltd. Dental molded product for milling and manufactual method thereof
JP5868853B2 (ja) * 2010-06-25 2016-02-24 パナソニックヘルスケアホールディングス株式会社 歯科切削加工用成形体及びその製造方法
CN102958466A (zh) * 2010-06-25 2013-03-06 松下电器产业株式会社 牙科磨削用成型制品及其制造方法
EP2586399A4 (fr) * 2010-06-25 2015-09-30 Panasonic Healthcare Holdings Co Ltd Corps moulé pour travail de coupe dentaire, et procédé de fabrication de celui-ci
US9089482B2 (en) 2010-09-30 2015-07-28 Kuraray Noritake Dental Inc. Dental mill blank
JP5613772B2 (ja) * 2010-09-30 2014-10-29 クラレノリタケデンタル株式会社 歯科用ミルブランク
WO2012042911A1 (fr) * 2010-09-30 2012-04-05 クラレメディカル株式会社 Ébauche dentaire
CN103118626B (zh) * 2010-09-30 2015-08-05 可乐丽则武齿科株式会社 牙科用研磨坯料
CN103118626A (zh) * 2010-09-30 2013-05-22 可乐丽则武齿科株式会社 牙科用研磨坯料
JP2012078644A (ja) * 2010-10-04 2012-04-19 Jsr Corp 歯牙模型および歯牙模型ブロック、ならびにそれらの製造方法
JP2018126588A (ja) * 2012-05-10 2018-08-16 レニショウ パブリック リミテッド カンパニーＲｅｎｉｓｈａｗ Ｐｕｂｌｉｃ Ｌｉｍｉｔｅｄ Ｃｏｍｐａｎｙ 物品を製造する方法
JP2017006728A (ja) * 2012-06-01 2017-01-12 スリーエム イノベイティブ プロパティズ カンパニー カスタマイズされた歯科用ブランク製造方法及びシステム
US10172695B2 (en) 2012-07-31 2019-01-08 Kuraray Noritake Dental Inc. Method for manufacturing dental mill blank
WO2014021343A1 (fr) 2012-07-31 2014-02-06 クラレノリタケデンタル株式会社 Procédé pour la fabrication de ciment dentaire blanc broyé
KR101221026B1 (ko) 2012-09-14 2013-01-10 고찬중 크라운 제조방법 및 이를 이용한 크라운
JP5727112B1 (ja) * 2013-09-24 2015-06-03 株式会社ジーシー 歯科用レジンブロックの製造方法
JP2015097854A (ja) * 2013-09-24 2015-05-28 株式会社ジーシー 歯科用レジンブロックの製造方法
WO2015045698A1 (fr) * 2013-09-24 2015-04-02 株式会社ジーシー Procédé pour fabriquer un bloc de résine dentaire
WO2016148289A1 (fr) * 2015-03-19 2016-09-22 クラレノリタケデンタル株式会社 Unité à façonner, et procédé de fabrication de celle-ci
JP2016174684A (ja) * 2015-03-19 2016-10-06 株式会社ジーシー セラミックスブランク
JP7029293B2 (ja) 2015-03-19 2022-03-03 クラレノリタケデンタル株式会社 被加工ユニット及びその製造方法
US11185397B2 (en) 2015-03-19 2021-11-30 Kuraray Noritake Dental Inc. Workpiece unit and method for producing same
JPWO2016148289A1 (ja) * 2015-03-19 2018-01-18 クラレノリタケデンタル株式会社 被加工ユニット及びその製造方法
US11033369B2 (en) 2015-08-28 2021-06-15 Shofu Inc. Dental mill blank having multiple layers that are visually identifiable
JP2019504114A (ja) * 2015-12-10 2019-02-14 ソシエテ ドゥ ルシェルシュ テクニク ダンテール 繊維インレイコアの製造のためのｃａｄ／ｃａｍ機械加工可能なディスク
CN108366847A (zh) * 2015-12-10 2018-08-03 Rtd牙科技术研究公司 用于制造纤维嵌芯的cad/cam可加工圆盘
WO2017098096A1 (fr) * 2015-12-10 2017-06-15 Societe De Recherches Techniques Dentaires - Rtd Disque usinable par cfao pour la fabrication d'inlay core fibres
FR3044890A1 (fr) * 2015-12-10 2017-06-16 Soc De Rech Techniques Dentaires - Rtd Disque usinable par cfao pour la fabrication d'inlay core fibres
US10524887B2 (en) 2015-12-10 2020-01-07 Societe De Recherches Techniques Dentaires—Rtd CAD/CAM-machinable disc for the manufacture of fiber inlay-cores
JP2018537230A (ja) * 2015-12-15 2018-12-20 クルツァー ゲゼルシャフト ミット ベシュレンクテル ハフツングＫｕｌｚｅｒ ＧｍｂＨ 重合した大きな歯科材料ブロックを製造する方法
JP2017109036A (ja) * 2015-12-18 2017-06-22 クラレノリタケデンタル株式会社 歯科用ミルブランクの製造方法及びその製造方法により得られた歯科用ミルブランク
JP5944602B1 (ja) * 2016-01-13 2016-07-05 株式会社松風 透明性が異なる多層構造を有したファイバー材含有の歯科切削加工用ブロック状複合材料。
US11141247B2 (en) 2016-01-13 2021-10-12 Shofu Inc. Block-like composite material for dental cutting and processing having multilayered structure including layers with different transparencies and containing fiber material
JP2017124981A (ja) * 2016-01-13 2017-07-20 株式会社松風 透明性が異なる多層構造を有したファイバー材含有の歯科切削加工用ブロック状複合材料。
CN106963656B (zh) * 2016-01-13 2022-02-22 株式会社松风 具有透明性不同的多层结构的含纤维材料的牙科切削加工用块状复合材料
CN106963656A (zh) * 2016-01-13 2017-07-21 株式会社松风 具有透明性不同的多层结构的含纤维材料的牙科切削加工用块状复合材料
WO2017154850A1 (fr) * 2016-03-07 2017-09-14 クラレノリタケデンタル株式会社 Ébauche de fraise dentaire et son procédé de production
US10898302B2 (en) 2016-04-25 2021-01-26 3M Innovative Properties Company Multi-layered zirconia dental mill blank and process of production
KR20190018500A (ko) * 2016-06-30 2019-02-22 디더블유에스 에스.알.엘. 치과용 보철물을 제조하기 위한 방법 및 시스템
JP2019528805A (ja) * 2016-06-30 2019-10-17 ディーダブリューエス エス．アール．エル． 歯科補綴物を作成するための方法及びシステム
KR102102566B1 (ko) 2016-06-30 2020-04-21 디더블유에스 에스.알.엘. 치과용 보철물을 제조하기 위한 방법 및 시스템
WO2018002960A1 (fr) * 2016-06-30 2018-01-04 Dws S.R.L. Procédé et système de fabrication de prothèses dentaires
US11980512B2 (en) 2016-06-30 2024-05-14 Dws S.R.L. Method and system for making dental prostheses
EP4180406A1 (fr) 2016-07-29 2023-05-17 Shofu Inc. Corps calciné temporaire dentaire ayant une partie intérieure colorée
US10905531B2 (en) 2016-07-29 2021-02-02 Shofu Inc. Mill blank for dental CAD/CAM with groove not extending over whole of circumference
EP3275851A1 (fr) 2016-07-29 2018-01-31 Shofu Inc. Corps dentaire calciné temporairement ayant un intérieur coloré
WO2018049331A1 (fr) * 2016-09-09 2018-03-15 Jensen Industries Inc. Ébauche de zircone ayant un gradient de couleurs et procédés pour la préparer
JP2018042894A (ja) * 2016-09-16 2018-03-22 ローランドディー．ジー．株式会社 歯冠補綴物作製システム、歯冠補綴物作製方法および歯冠補綴物作製のためのプログラム
JP2018042895A (ja) * 2016-09-16 2018-03-22 ローランドディー．ジー．株式会社 歯冠補綴物作製システム、歯冠補綴物作製方法および歯冠補綴物作製のためのプログラム
JPWO2018074583A1 (ja) * 2016-10-20 2018-12-06 Ｙａｍａｋｉｎ株式会社 歯科切削加工用複合レジン材料及びその製造方法
JP7130641B2 (ja) 2017-06-14 2022-09-05 クラレノリタケデンタル株式会社 歯科用ミルブランク
JPWO2018230657A1 (ja) * 2017-06-14 2020-05-21 クラレノリタケデンタル株式会社 歯科用ミルブランク
JP2019000683A (ja) * 2018-09-05 2019-01-10 株式会社ジーシー セラミックスブランク
CN112969429A (zh) * 2018-12-25 2021-06-15 德山齿科株式会社 加工用接合结构
JP2020099600A (ja) * 2018-12-25 2020-07-02 株式会社トクヤマデンタル 加工用接合構造
RU2769884C1 (ru) * 2018-12-25 2022-04-07 Токуяма Дентал Корпорейшн Соединительная конструкция для обработки
CN112969429B (zh) * 2018-12-25 2022-04-26 德山齿科株式会社 加工用接合结构
WO2020137224A1 (fr) * 2018-12-25 2020-07-02 株式会社トクヤマデンタル Structure de jonction pour traitement
JPWO2020166667A1 (ja) * 2019-02-14 2021-12-09 クラレノリタケデンタル株式会社 歯科用ミルブランク
EP3925593A4 (fr) * 2019-02-14 2023-01-11 Kuraray Noritake Dental Inc. Ébauche de fraisage dentaire
NL2022738B1 (en) * 2019-03-14 2020-09-18 Identiq Tandtechniek Method for providing a natural colour and optical depth to a tooth object
US11813129B2 (en) 2019-03-14 2023-11-14 Oralcol Assets Holding B.V. Method for providing a natural colour and optical depth to a dental object
WO2020185086A1 (fr) * 2019-03-14 2020-09-17 Identiq Tandtechniek Procédé permettant de fournir une couleur naturelle et une profondeur optique à un objet dentaire
EP3943041A4 (fr) * 2019-03-20 2022-12-14 Kuraray Noritake Dental Inc. Dispositif de coloration de prothèse dentaire, dispositif de traitement, et procédé de coloration
US11986365B2 (en) 2019-03-20 2024-05-21 Kuraray Noritake Dental Inc. Dental prosthesis coloring device, machining apparatus, and coloring method
KR102466073B1 (ko) * 2020-11-16 2022-11-11 주식회사 바이오덴 치과용 하이브리드 레진 블록 조성물 및 이를 이용한 치과용 하이브리드 레진 블록의 제조 방법
KR20220066478A (ko) * 2020-11-16 2022-05-24 주식회사 바이오덴 치과용 하이브리드 레진 블록 조성물 및 이를 이용한 치과용 하이브리드 레진 블록의 제조 방법
WO2022209951A1 (fr) * 2021-03-29 2022-10-06 キヤノン株式会社 Procédé d'estimation de couleur pour prothèse dentaire, dispositif de traitement d'informations, procédé de production de prothèse dentaire, procédé de traitement d'informations, et programme
WO2022248775A1 (fr) * 2021-05-27 2022-12-01 Societe De Recherches Techniques Dentaires Bloc usinable par cfao pour la fabrication d'élément prothétique dentaire notamment d'inlay-core fibré
EP4144334A1 (fr) 2021-09-01 2023-03-08 Aidite (Qinhuangdao) Technology Co., Ltd. Matériau de restauration céramique en résine à gradient dentaire et son procédé de préparation
JP2023035918A (ja) * 2021-09-01 2023-03-13 愛迪特（秦皇島）科技股分有限公司 歯科用グラデーションカラーレジンセラミック修復材料及びその製造方法
CN113730264B (zh) * 2021-09-01 2024-03-12 爱迪特（秦皇岛）科技股份有限公司 一种牙科用渐变色树脂陶瓷修复材料及其制备方法
CN113730264A (zh) * 2021-09-01 2021-12-03 爱迪特（秦皇岛）科技股份有限公司 一种牙科用渐变色树脂陶瓷修复材料及其制备方法
WO2023032728A1 (fr) 2021-09-06 2023-03-09 株式会社トクヤマデンタル Procédé de confirmation de couleur d'aspect de couronne, kit d'appareil et appareil de démonstration

Also Published As

Publication number Publication date
JPWO2009154301A1 (ja) 2011-12-01

Similar Documents

Publication Publication Date Title
WO2009154301A1 (fr) Bloc pour le traitement de prothèses dentaires, et son procédé de fabrication
JP7036810B2 (ja) 層状歯科用製品を製造するための３次元造形材料系および方法
CN105705112B (zh) 牙科研磨坯料、牙科修复体以及形成牙科研磨坯料的方法
JP7010859B2 (ja) 歯科製品を生産するための高強度三次元製作材料系及び方法
US8509933B2 (en) Fabrication of non-homogeneous articles via additive manufacturing using three-dimensional voxel-based models
RU2680802C2 (ru) Трехмерные системы поделочных материалов для изготовления стоматологических изделий
AU2013206255B2 (en) Production of individual dental prostheses via CAD/CAM and rapid manufacturing / rapid prototyping based on data of the situation in the mouth obtained by digital means
RU2608197C2 (ru) Способ и система для изготовления индивидуализированной стоматологической заготовки
US10617495B2 (en) Dental milling block containing individualized dental article and process of production
US20180042705A1 (en) Formed denture and method of making same
CN110423311A (zh) 可光固化的树脂组合物及其在3d打印中用于制造假牙和义齿基托的使用方法
US20050170315A1 (en) System, method, computer program product and apparatus for producing dental restorations
JP5436723B2 (ja) 象牙質用修復材料キット
JP2010220882A (ja) 歯科用補綴物の製造方法
JP7170536B2 (ja) 歯科用物体をビルドアップするための方法及びシステム
KR20190137079A (ko) 치과용 경화성 조성물 및 그 제조 방법
JP2004344623A (ja) 歯科用構造物自動作製装置
Fahl Jr Single-shaded direct anterior composite restorations: a simplified technique for enhanced results
US20080199826A1 (en) Dental Composite
TWI643602B (zh) 假牙製作系統及假牙製作方法
JP2005112854A (ja) 義歯又は天然歯の色補正のための方法及びカラーキット
WO2023176792A1 (fr) Ébauche de fraise pour appareil de coupe dentaire et son procédé de production
US20050132928A1 (en) Dental composites placement techniques for direct restorations
US20230026132A1 (en) Systems and methods for 3d printed material surface treatments
JP7333998B2 (ja) 歯科加工用ブランクの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 09766749

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2010518045

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 09766749

Country of ref document: EP

Kind code of ref document: A1