WO2007029351A1 - 映写黒板およびその製造方法 - Google Patents

映写黒板およびその製造方法 Download PDF

Info

Publication number
WO2007029351A1
WO2007029351A1 PCT/JP2005/021772 JP2005021772W WO2007029351A1 WO 2007029351 A1 WO2007029351 A1 WO 2007029351A1 JP 2005021772 W JP2005021772 W JP 2005021772W WO 2007029351 A1 WO2007029351 A1 WO 2007029351A1
Authority
WO
WIPO (PCT)
Prior art keywords
glaze
blackboard
layer
titanium
projection
Prior art date
Application number
PCT/JP2005/021772
Other languages
English (en)
French (fr)
Inventor
Kazuhiro Hayashi
Original Assignee
Jfe Metal Products & Engineering Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Metal Products & Engineering Inc. filed Critical Jfe Metal Products & Engineering Inc.
Priority to US12/065,510 priority Critical patent/US8470451B2/en
Priority to EP05809636.3A priority patent/EP1930177B1/en
Publication of WO2007029351A1 publication Critical patent/WO2007029351A1/ja
Priority to US13/849,986 priority patent/US9168566B2/en

Abstract

 課題  優れた黒板機能および優れたスクリーン機能とを兼備する映写黒板およびその製造方法を提供する。  解決手段  金属基板上に形成される琺瑯層のうち、最外層の表面琺瑯層を、透明マット釉薬に少なくとも酸化チタン被覆粒子を、あるいはさらに酸化チタン釉薬を、配合した琺瑯上釉薬を用いて形成し、所定の色調と、Rzが5~25μmである表面特性と、ピークゲインが0.28以上である反射特性と、あるいはさらに光沢度Gs(75°)が1~30%である琺瑯層とする。これにより、優れた黒板機能とスクリーン機能を兼備する黒板とすることができる。なお、酸化チタン被覆粒子は、雲母粒子の表面に酸化チタンを被覆してなる粒子とすることが好ましい。また、金属基板は、冷延鋼板あるいはアルミニウムめっき鋼板またはZn-Al合金めっき鋼板とすることが好ましい。

Description

明 細 書
映写黒板およびその製造方法
技術分野
[0001] 本発明は、表面に琺瑯層を形成してなる黒板 (チョークボードともいう)に係り、とく に、優れた黒板機能と優れたスクリーン機能とを兼備する琺瑯製黒板に関する。なお 、本発明でいう「優れた黒板機能」とは、チョークで文字、画像等を書き易ぐ見やすく 、また書いた文字、画像等を消去しやすい機能を有することを意味する。また、「優れ たスクリーン機能」とは、プロジェクタ、 OHP等で文字等の映像を投影した際に、文字 等の映像が鮮明に映写できる機能を有することを意味する。
背景技術
[0002] 従来から、黒板 (チョークボード)は、表面に文字、画像等をチョークで消去可能に 描ける機能を有し、種々の説明、講義、講演等の補助として利用されてきた。そのた め、従来の黒板 (チョークボード)は、 JIS S 6007にも規定されているように、チョーク( 白墨)で文字、画像等を書き易ぐ消去しやすくするために表面を適正に粗くし、かつ チョーク(白墨)で書かれた文字,画像等を見やすくするため暗色系の材料を使用し てきた。
[0003] しかし、近年では、スライド、 OHP等の各種プロジェクタを利用して、予め用意した 資料をスクリーンに映写し、指示棒等で指しながら説明等を行う場合が一般的となつ てきた。各種プロジェクタを利用して、説明等を行う場合には、映写用のスクリーンと 補足説明のためチョーク(白墨)で文字等を描書および消去ができる黒板とを両方、 用意する必要があり、準備 '後始末にかなりの手間を要していた。というのは、従来の 黒板に各種プロジェクタで映像を投影すると画質が暗く不鮮明となるため、従来の黒 板をスクリーンとして利用することはな力つた。
[0004] 一方、各種プロジェクタで映像を投影することを主たる目的とする反射スクリーンは 、反射特性を向上させるために白色系、あるいは高明度色系の材料を使用している 。このため、スクリーンにチョーク(白墨)で描書すると、コントラストが低ぐ文字、画像 等の認識特性が低下することになるうえ、ビーズ、ホワイトマット等の一般的なスクリー ンは表面硬さが低ぐチョーク(白墨)で描書 ·消去すると、スクリーンが摩耗するという 問題があった。このため、例えば特開平 02— 153080号公報、特開平 04— 229299号 公報に示されるように、スクリーンは、マーカーで描書し消去するマーカーボードとし て用いられる場合はあっても、チョークボードとして用いられることはな力つた。
[0005] このような問題に対し、例えば、実開昭 57— 183190号公報には、釉薬中にブルー 系統の染料を混入して鋼板上に明度 8乃至 4の粗面ホーロー層を形成してなる映写 幕兼用ホーロー黒板が提案されている。
発明の開示
発明が解決しょうとする課題
[0006] しかし、実開昭 57— 183190号公報に記載された技術で製造された黒板では、反射 輝度が低ぐ映像が不鮮明となる傾向が強ぐとくに輝度の低いプロジェクタを用いた 場合には鮮明な映像が得られにくいなど、スクリーンとしての最近の要求特性を十分 満足できないという問題があった。本発明は、上記した従来技術の問題を有利に解 決し、チョーク(白墨)で文字、画像等を描書し易くかつ見やすくチョーク文字認識性 に優れ、またチョーク(白墨)で書いた文字、画像等を容易に消去でき、チョーク文字 認識性、チョーク文字描書 ·消去性に共に優れ、かつ投影された映像を鮮映に映写 でき映像認識性に優れる、優れた黒板機能および優れたスクリーン機能とを兼備す る映写黒板およびその製造方法を提供することを目的とする。なお、本発明が目的と する映写黒板は、金属基板の外表面に少なくとも 1層の琺瑯層を有する琺瑯製黒板 とする。
課題を解決するための手段
[0007] 本発明者らは、上記した課題を達成するために、琺瑯製黒板のチョーク文字認識 性、チョーク描書 ·消去性および映像認識性に影響する要因につ!、て鋭意検討した 。その結果、従来の黒板と同等以上のチョーク文字認識性、チョーク文字描書'消去 性を確保するために、黒板の表面琺瑯層が、所定範囲の明度と、所定の範囲の表面 粗さを有するとともに、さらに映像認識性向上のために、所定値以上のピークゲイン を有する反射特性となるように表面琺瑯層を調整することが肝要であることに想到し [0008] そして、そのような表面琺瑯層は、使用する釉薬を、通常のチョークボード釉薬であ る透明マット釉薬に、少なくとも適正量の酸ィ匕チタン被覆粒子と、あるいはさらに酸ィ匕 チタン釉薬を配合した釉薬とし、焼成条件を適正範囲に調整することにより生成可能 であることを新規に見出した。これにより、黒板に、優れた黒板機能と優れたスクリー ン機能とを兼備させることができることを知見した。
[0009] 本発明は、上記した知見に基づいて、さらに検討をカ卩えて完成されたものである。
すなわち、本発明の要旨はつぎのとおりである。
(1)金属基板上に、少なくとも 1層の琺瑯層を有する黒板であって、前記琺瑯層のう ち最外層の表面琺瑯層が、 JIS Z 8721— 1993に規定される明度 V力 ¾.0〜7.0である 色調と、 JIS B 0601— 2001に規定される表面粗さ Rzが 5〜25 μ mである表面特性と、 ピークゲインが 0.28以上である反射特性と、を有することを特徴とする映写黒板。
[0010] (2) (1)において、前記表面琺瑯層が、透明マット釉薬に少なくとも酸ィ匕チタン被覆 粒子を、あるいはさらに酸ィ匕チタン釉薬、あるいはさらに透明ダロス釉薬を配合した琺 瑯上釉薬を用いて形成された琺瑯層であることを特徴とする映写黒板。
(3) (1)または(2)において、前記表面琺瑯層が、黒色系、緑色系、茶色系のうち の!、ずれかの色を有することを特徴とする映写黒板。
[0011] (4) (1)な!、し(3)の!、ずれかにお 、て、前記表面琺瑯層が、 JIS Z 8741 1997に 規定される 75度鏡面光沢度 Gs (75° )が 1〜30%であることを特徴とする映写黒板。
(5) (1)ないし (4)のいずれか〖こおいて、前記酸化チタン被覆粒子が、雲母粒子の 表面に酸ィ匕チタンを被覆してなる粒子であることを特徴とする映写黒板。
(6)金属基板の表面に、琺瑯下釉薬を塗布し、焼成して下地琺瑯層を形成したの ち、あるいは下地琺瑯層を形成することなぐついで透明マット釉薬に少なくとも酸ィ匕 チタン被覆粒子を、あるいはさらに酸ィ匕チタン釉薬をあるいはさらに透明ダロス釉薬 を配合した琺瑯上釉薬を塗布し、 400〜800°Cで焼成し表面琺瑯層を形成することを 特徴とする映写黒板の製造方法。
[0012] (7) (6)において、前記金属基板が、冷延鋼板、あるいはアルミめつき鋼板または Z n—Al合金めつき鋼板であることを特徴とする映写黒板の製造方法。
(8) (6)または(7)において、前記酸化チタン被覆粒子が、雲母粒子の表面に酸ィ匕 チタンを被覆してなる粒子であることを特徴とする映写黒板の製造方法。 発明の効果
[0013] 本発明によれば、チョーク文字認識性、およびチョーク文字消去性に優れるとともに 、映像認識性にも優れ、取り扱いが容易で、施工性にも優れた映写黒板を、安価に 製造でき、産業上格段の効果を奏する。
図面の簡単な説明
[0014] [図 1]反射特性曲線の一例を示すグラフである。
[図 2]反射輝度の測定方法を示す概略説明図である。
符号の説明
[0015] 1入射光
2 反射光
3s 被測定黒板 (サンプル)
10 光源
11 輝度計
発明を実施するための最良の形態
[0016] 本発明になる映写黒板は、金属基板上に少なくとも 1層の琺瑯層を有する黒板であ る。本発明では、使用する金属基板の種類は、とくに限定されるものではないが、冷 延鋼板とすることが好ましい。金属基板として使用する冷延鋼板には、金属基板と釉 薬との密着性を向上させるために、 Niめっきを施すことが好ましい。なお、冷延鋼板と しては低炭素鋼板、ステンレス鋼板等が例示できる。低炭素鋼板の C含有量は、 mas s%で 0.0200%以下とすることが好ましぐより好ましくは 0.0100%以下、さらに好ましく は 0.0050%以下である。
[0017] また、金属基板としては、アルミニウムめっき鋼板または Zn—Al合金めつき鋼板とし てもよい。 Zn—Al合金めつき鋼板としては、 A1含有量が 4〜70mass%、残部 Znおよび 不可避的不純物からなるめっき層を有するめっき鋼板が例示できる。なお、めっき層 には、めっき皮膜特性向上のための添加物質を含有してもよいことは言うまでもない 上記した金属基板上に形成される琺瑯層のうち、最外層の表面琺瑯層は、 JIS Z 87 21— 1993に規定される明度 V力 ¾.0〜7.0である色調と、 JIS B 0601— 2001に規定され る表面粗さ Rzが 5〜25 μ mである表面特性と、ピークゲインが 0.28以上である反射特 性と、を有する。なお、本発明でいう明度 Vは、 JIS Z 8722— 2000に規定される色の測 定方法に準拠して測定し、 JIS Z 8721— 1993に規定される色の表示方法に準拠して 表示される値を用いるものとする。
[0018] 本発明の映写黒板は、まず、従来の黒板と同等以上のチョーク文字認識性、チョー ク文字消去性を維持し、優れた黒板機能を保持することを必要とする。
そのために、まずチョークで描書された文字、画像等が見えやすくなる、すなわち、 チョーク文字認識性を確保するため、本発明では、表面琺瑯層を、 JIS Z 8721 - 1993 に規定される明度 V力 ¾.0〜7.0である、好ましくは黒色系、緑色系、茶色系、紺色系 のうちのいずれか、さらに好ましくは黒色系、緑色系、茶色系のいずれかの暗色系色 調の琺瑯層とする。明度 Vが上記した範囲を下方に外れると、暗くなりすぎて映像を 投影したときに映像認識性が低下し、一方、明度 Vが上記した範囲を上方に外れると 、明るくなりすぎてチョーク文字認識性が低下する。なお、琺瑯層の色調、明度は、 添加顔料の種類、添加量により調整することができる。明度 Vを 3.0〜7.0に調整する には、顔料として、 Co、 Cr、 Tiの金属またはそれらの酸ィ匕物を単独あるいは複合して 添加することが好ましい。なお、明度 Vは 4.0〜6.0とすることが好ましい。
[0019] また、本発明の映写黒板では、チョークで文字、画像等を書き易くかつ消去し易く なる、チョーク文字描書'消去性を確保するために、表面琺瑯層の表面特性を、 JIS B 0601— 2001に規定される表面粗さ Rzが 5〜25 μ mとなるように調整する。なお、好ま しくは 10〜22 μ m、さらに好ましくは 14〜18 μ mである。
表面琺瑯層の表面粗さ Rzが上記した範囲を外れ、平坦に近づくと、チョークがすべ り、チョーク描書性が低下するとともに、映像認識性が低下する。一方、上記した範囲 を外れ凹凸が大きくなリすぎると、チョーク文字消去性が低下するとともに、映像認識 性が低下する。なお、上記した表面琺瑯層の表面特性は、後記するように、金属基 板に塗布する釉薬の組成と、釉薬塗布後の焼成条件の組み合わせを適正範囲とす ること〖こより、達成できる。 [0020] 本発明の映写黒板においては、表面琺瑯層が上記した色調と表面特性を有し、優 れた黒板機能を維持するとともに、さらにピークゲインが 0.28以上で、好ましくはハー フゲインが 15以上である反射特性を有する。
被測定板の反射特性は、例えば、図 2に示すように、被測定板 Sの中心に垂直方 向に光源 10力も入射光 1を照射し、中心点から同一円弧上を左右に各 75 ° の範囲 で 5° ずつ移動したポイントでの反射光 2の大きさ(反射輝度)を輝度計 11で測定して 得られた反射特性曲線(図 1参照)により求めるものとする。本発明でいう「ピークゲイ ン」とは、標準白板 (完全拡散板:硫酸バリウムを焼き付けた純白板)に光を当てたと きの反射輝度に対する、同一条件で測定した被測定黒板の反射輝度の比率を 、う 力 この場合、通常、視野角 5° での反射輝度を用いる。また、本発明でいう「ハーフ ゲイン」は、反射特性曲線における反射輝度がピークの 1/2となった場合の視野角幅 (度)をいう。
[0021] ピークゲインが 0.28未満では、投影した映像が暗ぐ映像認識性に劣ることになり、 映写黒板としての要求を満足することができなくなるため、 0.28をピークゲインの下限 値とした。なお、ピークゲインは好ましくは、 0.5〜1.0である。また、広い視野角を得る ために、ハーフゲインを 15以上とすることが好ましい。このため、本発明では、 0.28以 上のピークゲインと、好ましくは 15以上のハーフゲインを有する反射特性の表面琺瑯 層とする。
[0022] 上記した表面琺瑯層の反射特性は、後記するように、金属基板に塗布する釉薬に 、適正粒径分布を有する酸化チタン被覆粒子、好ましくは酸ィ匕チタンを被覆した雲母 粒子、を適正量添加し、焼成温度を適正範囲に調整することにより達成できる。 上記した特性を有する表面琺瑯層は、 JIS Z 8741— 1997に規定され 75度鏡面光沢 度 Gs (75° )が 1〜30%の表面光沢を有することが好ましい。 Gs (75° )が 1%未満で は、チョーク文字消去性が劣化するとともに、反射輝度が小さくなり、映像が不鮮明と なる。一方、 Gs (75° )が 30%を超えると、チョーク文字描書性が劣化するとともに、ハ レーシヨンを起こし易く視野角が狭くなる。なお、より好ましくは Gs (75° )が 15〜25% である。
[0023] 表面琺瑯層には、酸化チタン被覆粒子が含有される。表面琺瑯層に酸ィ匕チタン被 覆粒子を含有させることにより、鮮映性が向上するとともに、表面に凹凸が形成され 拡散反射性が向上し、ハレーションが抑制され、反射特性が向上する。本発明では、 表面琺瑯層には、酸ィ匕チタン被覆粒子を表面琺瑯層全量に対する質量%で 2〜40 %、さらに好ましくは 3〜20%含有させることが好ましい。酸ィ匕チタン被覆粒子が 2質 量%未満では反射特性向上効果が少な!/ヽ。酸化チタン被覆粒子が 40質量%を超え て含有させると、表面粗さ Rzが過剰に大きくなりすぎて、チヨ—ク文字消去性が悪ィ匕 すると共に、明度が大きくなりすぎて、チヨ—ク文字認識性が低下する。
[0024] また、酸ィ匕チタン被覆粒子は、 100 μ m以下の平均粒径を有することが好ま 、。さ らに好ましくは 5〜80 μ mである。酸化チタン被覆粒子の平均粒径が 5 μ m未満では 拡散反射性が低下し、一方、酸ィ匕チタン被覆粒子の平均粒径が 100 /z mを超えると、 表面琺瑯層の表面粗さが過剰に大きくなり、チョーク文字消去性が低下する。なお、 ここでいう粒子の平均粒径とは、レーザ回折式粒度分布測定装置を利用して測定し た、 50%累積粒子径を言うものとする。また、酸ィ匕チタン被覆粒子は、雲母粒子の表 面に酸ィ匕チタンを被覆した粒子とすることが好ましぐ雲母粒子は薄板状雲母粒子と することがより好まし!/、。
[0025] 上記した特性を有する表面琺瑯層は、透明マット釉薬に、少なくとも酸ィ匕チタン被 覆粒子を、あるいはさらに酸ィ匕チタン釉薬を、あるいはさらには透明ダロス釉薬を配 合した琺瑯上釉薬を用いて形成された琺瑯層とすることが好ましい。なお、表面琺瑯 層の厚さは、剥離性の観点から 200 m以下とすることが好ましい。なお、より好ましく は 150 m以下である。
[0026] 上記した琺瑯上釉薬を用いて形成された表面琺瑯層は、質量%で、酸化チタン被 覆粒子の酸化チタンを含む酸化チタンの合計量を TiOとして、 TiO : 0.5〜15%、より
2 2
好ましくは 0.5〜10%未満、さらに好ましくは 2〜5%を含み、さらに、 SiO : 15〜45%、
2
A1 0 : 5〜30%、 Na 0、 K 0、 Li 0から選ばれた 1種または 2種以上を合計: 2〜20%
2 3 2 2 2
、 B 0 : 2〜20%を含む、琺瑯層とすることが好ましい。なお、本発明では、黒板の表
2 3
面琺瑯層には、所望の色を得るために、黒色系顔料、緑色系顔料、黄色系顔料のう ちから選ばれた顔料を合計で 20質量%以下含むことは言うまでもない。
[0027] 次に、本発明映写黒板の好ましい製造方法について、説明する。 本発明の映写黒板は、金属基板の表面に、琺瑯下釉薬を塗布し、焼成して下地琺 瑯層を形成したのち、あるいは下地琺瑯層を形成することなぐついで透明マット釉 薬に少なくとも酸ィ匕チタン被覆粒子を、あるいはさらに酸ィ匕チタン釉薬を、あるいはさ らに透明ダロス釉薬を、配合した琺瑯上釉薬を塗布し、 400〜850°Cで焼成し表面琺 瑯層を形成する製造方法で製造することが好ましい。なお、金属基板は、冷延鋼板、 あるいはアルミめつき鋼板または Zn—Al合金めつき鋼板とすることが好ましい。
[0028] 金属基板として冷延鋼板を用いる場合には、好ましくは冷延鋼板に Niめっきを施し たのち、冷延鋼板 (金属基板)表面に琺瑯下釉薬を塗布し、焼成して下地琺瑯層を 形成する。琺瑯下釉薬としては、とくに限定されるものではなぐ従来の琺瑯製黒板 で使用される琺瑯下釉薬がいずれも好適である。琺瑯下釉薬の塗布は、スプレー、 ロールコータ等の公知の塗布方法がいずれも適用できる。
[0029] 琺瑯下釉薬としては、なかでも、例えば、固形分全量に対する質量%で、 SiO : 20
2
〜80%含有し、残部として、 TiO : 0〜: L5%、ZrO : 0〜20%、B O : 0〜25%、A1〇:
2 2 2 3 2 3
0〜25%、 Na O : 0〜20%、 Li O : 0〜20%、 K O : 0〜20%、 PbO : 0〜40%、 ZnO : 0〜
2 2 2
50%、 BaO : 0〜15%、 CaO : 0〜15%、 CaF : 0〜: 10%、 CoO : 0〜20%、 Ni〇:0〜20%
2
、 MnO : 0〜20%などを含有する SiO系釉薬とすることが好ましい。
2
[0030] 得られた下地琺瑯層の表面に、琺瑯上釉薬を塗布し、その後、 600〜850°Cで焼成 し表面琺瑯層を形成する。琺瑯上釉薬の塗布は、スプレー、ロールコータ等の公知 の塗布方法が 、ずれも適用できる。
琺瑯上釉薬は、透明マット釉薬 (フリット)に、あるいは、透明マット釉薬 (フリット) 100 重量部に対し、酸化チタン釉薬 (フリット)を 100〜20重量部、あるいはさらに透明グロ ス釉薬 (フリット) 20重量部以下を添加した釉薬に、適正量の酸化チタン被覆粒子を 添加した釉薬とすることが好ましい。また、酸ィ匕チタン被覆粒子の添加量は、透明マ ット釉薬または混合した釉薬 (スリップ): 100重量部 (焼成後の重量換算)に対し、 1〜 25重量部とすることが好ま 、。
[0031] 琺瑯上釉薬は、透明マット釉薬のフリットと、あるいは、透明マット釉薬、酸化チタン 釉薬、あるいはさらに透明ダロス釉薬のフリットと、必要に応じて各種添加物および顔 料と、水との混合物の粉砕で得られた泥状物 (スリップ)に、適正量の酸化チタン被覆 粒子粉末を添加、混合して得られる。なお、顔料として、黒板の所望の色調に合わせ て、黒色系顔料、緑色系顔料、黄色系顔料のいずれか単独あるいは複合して添カロ する必要がある。顔料の添加量としては、スリップ: 100重量部(焼成後の重量換算) に対し合計で 20重量部以下とすることが好ま 、。添加量が 20重量部を超えて多くな ると、スリップの流動性が低下する。
[0032] なお、透明マット釉薬 (フリット)としては、固形分全量に対する質量%で、 SiO : 30
2
〜45%、A10 :20〜35%、B O :5〜: 15%、 K 0:5〜15%、 Na 0: 10〜25%、を含み
2 3 2 3 2 2
、残部として、 Ba〇:0〜: 15%、 Ca〇:0〜: 15%、 F :0〜: L0%、Ti〇:0〜: 10%などを含
2 2
む釉薬とすることが好ましい。
酸ィ匕チタン釉薬 (フリット)としては、固形分全量に対する質量%で、 TiOを 10〜30
2
%含有し、残部として、 SiO :0〜80%、 A10 :0〜20%、 B 0 :0〜25%、 Na O:0〜2
2 2 3 2 3 2
0%、 K O:0〜20%、 Li O:0〜20%、 P O :0〜: 10%、 ZrO :0〜20%、 BaO:0〜15%
2 2 2 5 2
、 Ca〇:0〜15%、 Mg〇:0〜5%、 Pb〇:0〜40%、 Zn〇:0〜50%、 CaF :0〜: 10%など
2
を含む釉薬とすることが好ましい。なお、酸ィ匕チタン釉薬の顔料である酸ィ匕チタンに 代えて、酸ィ匕ジルコニウム、酸ィ匕アンチモン、酸ィ匕亜鉛のうちの 1種または 2種以上の 顔料としてもよい。
[0033] 透明ダロス釉薬 (フリット)としては、固形分全量に対する質量%で、 SiO :40〜65%
2 を含み、残部として、 B 0 :5〜20%、 Na〇、 K〇、 Li 0のいずれか 1種以上を合計で
2 3 2 2 2
5〜40%、F :0〜10%、Α1 Ο :0〜: 10%、 CaO :0〜10%、 TiO :0〜10%、ZnO:0〜10
2 2 3 2
%、 MgO:0〜5%などを含む釉薬とすることが好ましい。なお、酸化チタン釉薬の顔 料である酸化チタンに代えて、酸化ジルコニウム、酸化アンチモン、酸化亜鉛のうち の 1種または 2種以上の顔料としてもよ 、。
[0034] 焼成温度が、 600°C未満では、表面粗さが粗くなりすぎて、反射特性が劣化する。
一方、 850°Cを超えると、表面が平滑になりすぎて、チョーク文字認識性、チョーク文 字描書'消去性が低下する。
また、金属基板としてアルミニウムめっき鋼板または Zn—Al合金めつき鋼板を用いる 場合には、金属基板表面に、琺瑯上釉薬を塗布し、 400〜600°Cで焼成し表面琺瑯 層を形成することが好ましい。 [0035] なお、この場合には、めっき層の溶融防止の観点から、低融点の琺瑯上釉薬を用 いる必要がある。このため、上記した透明マット釉薬に代えてリン酸を配合した釉薬に 、酸ィ匕チタン被覆粒子を、あるいはさらに酸ィ匕チタン釉薬を、配合してなる琺瑯上釉 薬とすることが好ましい。リン酸を配合した釉薬中のリン酸の含有量は、 40質量%以 上、好ましくは 80質量%以下、さらに好ましくは 70%以下とすることが好ましい。
[0036] リン酸を配合した釉薬 (フリット)としては、固形分全量に対する質量%で、 P 0 :40
2 5
〜80%を含有し、残部として、 SiO : 0〜40%、 A1 0 : 0〜50%、 B 0 : 0〜25%、 Na 0
2 2 3 2 3 2
: 0〜20%、 K O : 0〜20%、 Li O : 0〜20%、 TiO : 0〜30%、 Sb O : 0〜25%、 ZnO : 0
2 2 2 2 3
〜20%、 BaO : 0〜15%、 CaO : 0〜15%、 MgO : 0〜5%、 PbO : 0〜10%、 SrO : 0〜20 %などを含む釉薬とすることが好ま 、。
[0037] なお、金属基板としてアルミニウムめっき鋼板または Zn—Al合金めつき鋼板を用い る場合には、めっき層の溶融防止の観点から、低融点の琺瑯上釉薬を用いるため、 密着性が向上し、琺瑯下釉薬の塗布は必ずしも必要ではない。
また、金属基板としてアルミニウムめっき鋼板または Zn—Al合金めつき鋼板を用いる 場合、焼成温度が、 400°C未満では、琺瑯層の密着性が低下する。一方、 600°Cを超 えると、めっき層が溶融するという問題が生じる。
実施例
[0038] (実施例 1)
金属基板として冷延鋼板 (C : 0.0050質量%の極低炭素鋼板)を用いた。冷延鋼板 表面には、硫酸ニッケル浴中でニッケルめっき層を形成した。ついで、ニッケルめつ きされた冷延鋼板の両表面に、琺瑯下釉薬をロールコータ法で塗布したのち、 800°C で焼成し 30 mの下地琺瑯層を形成した。なお、琺瑯下釉薬は、 SiO系釉薬 (フリット
2
) : 100重量部に、粘土: 6重量部、炭酸マグネシウム: 0.15重量部、硼砂: 0.4重量部、 シリカ: 1重量部、水:70重量部を添加した配合原料をボールミルに投入し、混合、粉 砕してスリップとしたものを使用した。
[0039] っ 、で、得られた下地琺瑯層の一方の表面に、琺瑯上釉薬をスプレー法で塗布し たのち、 750°Cで焼成し 70 mの表面琺瑯層を形成し、サンプル黒板とした。一部の 黒板では、焼成温度を 700〜780°Cの範囲で変化させた。 なお、表 1に示す組成の透明マット釉薬 (フリット): 100重量部に、粘土: 5.5重量部、 亜硝酸ソーダ : 0.15重量部、シリカ: 0.5重量部、水: 70重量部を添加し、さらに顔料と して、 TiO、 Sb 0、 NiOを合計: 1重量部、 Cr 0 : 8.2重量部、 Co、 Crを合計: 10.0重
2 2 5 2 3
量部、 Fe 0、 CuO、 CoO、 MnO等を合計: 0.1重量部を添カ卩し、ボールミルで、混合、
2 3
粉砕して得たスリップ Aを作製し、また、表 2に示す酸ィ匕チタン釉薬 (フリット): 100重 量部に、粘土: 5.5重量部、塩化カリ: 0.2重量部、アルミン酸ソーダ : 0.3重量部、水: 5 4重量部を添加し、ボールミルで、混合、粉砕してスリップ Bを得た後、該スリップ B : 10 0重量部に、(焼成後の重量換算)酸化チタン被覆粒子粉末: 20重量部を水: 45重量 部とともに添加し、混合してスリップ Cを作製し、これらスリップ Aとスリップ Cとを、 3 : 1 の比率で配合し、混合して本発明で使用する琺瑯上釉薬とした。なお、一部では、ス リップ Aとスリップ Cとの混合比を変化した。酸化チタン被覆粒子粉末は、薄板状雲母 粒子の表面に酸ィ匕チタンを被覆した粒子で、平均粒径は 20 m、酸化チタン被覆率 は 30%である。なお、平均粒径は、レーザ回折式粒度分布測定装置を利用して測定 した、 50%累積粒子径を示す。
[0040] 従来例として、表 1に示す組成の透明マット釉薬 (フリット): 100重量部に、粘土: 5.5 重量部、亜硝酸ソーダ : 0.15重量部、シリカ: 0.5重量部、水: 70重量部を添加し、さら に顔料として、 TiO、 Sb 0、 NiOを合計: 0.5重量部、 Cr 0 :4.1重量部、 Co、 Crを合
2 2 5 2 3
計: 5.0重量部、 Fe 0、 CuO、 CoO、 MnO等を合計: 0.05重量部を添カ卩し、ボールミル
2 3
で、混合、粉砕して得たスリップ Dを琺瑯上釉薬として使用し、焼成温度: 700°Cで焼 成した。
[0041] 得られたサンプル黒板の表面琺瑯層につ ヽて、組成と、表面粗さ、色調、光沢度、 反射特性を調査した。
(1)表面粗さ
表面粗さの測定は、接触式表面粗度計を用い、 JIS B 0601— 2001の規定に準拠し て、算術平均粗さ Raと最大高さ Rzを求めた。
(2)色調
色調は、 JIS Z 8722— 2000の規定に準拠して測定し、 JIS Z 8721— 1993の規定に準 拠して、各サンプル黒板の色調を表示した。 (3)光沢度
光沢度は、 JIS Z 8741 1997に準拠して 75度鏡面光沢度 Gs (75° )を求めた。
(4)反射特性
反射特性は、図 2に示すように、被測定板 Sの中心に垂直方向に光源 10力 入射 光 1を照射し、中心点から同一円弧上を左右に各 75 ° の範囲で 5° ずつ移動したポ イントでの反射光 2の大きさ (反射輝度)を輝度計 11で測定し、ピークゲイン、ハーフ ゲインを求めた。ピークゲインとは、標準白板 (完全拡散板:硫酸バリウムを焼き付け た純白板)に光を当てたときの反射輝度に対する、同一条件で測定したサンプル黒 板の反射輝度の比率を、ピークゲインとした。なお反射輝度は、視野角 5° での反射 輝度を用いた。
[0042] 本発明の黒板 (本発明品)と従来の黒板 (従来品)の反射特性の一例を図 1に示す 。なお、縦軸は被測定黒板の反射輝度を標準白板の反射輝度 (ピーク)を 100%とし たときの比率で示した。
(5)黒板機能
さらに、得られたサンプル黒板に、 JIS B 6007の規定に準拠して、チョーク(白墨)で 文字を描書し、白墨の着きやすさ、および落ち易さを判定した。白墨の着きやすさは 、黒板面から lm離れた位置力 見て、線にムラがないか、さらに 8m離れた位置で見 て、線が鮮明であるか、を判定した。線のムラがなくかつ鮮明である場合を◎とし、や や鮮明度が低下する場合を〇とし、線のムラがある力あるいは鮮明でない場合を Xと し、チョーク文字認識性を評価した。また、白墨の落ち易さは、黒板の描書した文字 を、イレーザー (フェルト製)で擦ったのち、黒板から lm離れた位置で見て、黒板面 に筆跡跡、消しムラがない場合を◎、やや筆跡跡が残る場合を〇、それ以外の場合 を Xとして、チョーク文字消去性を評価した。
[0043] 得られた結果を、表 3、表 4に示す。
[0044] [表 1]
Figure imgf000014_0001
[0045] [表 2] 組 成 (質量! ¾)
Si02 A1203 Na20+K20+Li20 B203 Ti02 P205 F3 残部 酸化チタン釉薬 35 3 18 13 22 2.5 4 2.5
[0046] [表 3]
Figure imgf000015_0001
[0047] [表 4]
Figure imgf000015_0002
[0048] 本発明例はいずれも、従来黒板と同等のチョーク文字認識性、チョーク文字消去性 を維持し、優れた黒板機能を保持するとともに、 0.28以上のピークゲインが得られ、反 射特性に優れた黒板となり、映像を投影した場合に、映像認識性に優れ、映写用と して好適な黒板となっている。本発明の範囲を外れる比較例は、チョーク文字認識性 、チョーク文字消去性の黒板機能が低下している力 あるいは反射特性が劣り、映像 認識性が低下している。

Claims

請求の範囲
[1] 金属基板上に、少なくとも 1層の琺瑯層を有する黒板であって、前記琺瑯層のうち 最外層の表面琺瑯層が、 JIS Z 8721— 1993に規定される明度 V力 ¾.0〜7.0である色 調と、 JIS B 0601— 2001に規定される表面粗さ Rzが 5〜25 μ mである表面特性と、ピ ークゲインが 0.28以上である反射特性と、を有することを特徴とする映写黒板。
[2] 前記表面琺瑯層が、透明マット釉薬に少なくとも酸ィ匕チタン被覆粒子を配合した琺 瑯上釉薬を用いて形成された琺瑯層であることを特徴とする請求の範囲第 1項に記 載の映写黒板。
[3] 前記琺瑯上釉薬がさらに酸ィ匕チタン釉薬を、あるいはさらに透明ダロス釉薬を配合 したものであることを特徴とする請求の範囲第 2項に記載の映写黒板。
[4] 前記表面琺瑯層が、黒色系、緑色系、茶色系のうちのいずれかの色を有することを 特徴とする請求の範囲第 1項ないし請求の範囲第 3項のいずれかに記載の映写黒 板。
[5] 前記表面琺瑯層が、 JIS Z 8741— 1997に規定される 75度鏡面光沢度 Gs (75° )が 1 〜30%であることを特徴とする請求の範囲第 1項な 、し請求の範囲第 4項の 、ずれ かに記載の映写黒板。
[6] 前記酸ィ匕チタン被覆粒子が、雲母粒子の表面に酸ィ匕チタンを被覆してなる粒子で あることを特徴とする請求の範囲第 2項な 、し請求の範囲第 5項の 、ずれかに記載 の映写黒板。
[7] 前記金属基板が、冷延鋼板、あるいはアルミめつき鋼板または Zn—Al合金めつき鋼 板であることを特徴とする請求の範囲第 1項ないし請求の範囲第 6項のいずれかに 記載の映写黒板。
[8] 金属基板の表面に、琺瑯下釉薬を塗布し、焼成して下地琺瑯層を形成したのち、 あるいは下地琺瑯層を形成することなぐついで透明マット釉薬に少なくとも酸ィ匕チタ ン被覆粒子を配合した琺瑯上釉薬を塗布し、 400〜850°Cで焼成し表面琺瑯層を形 成することを特徴とする映写黒板の製造方法。
[9] 前記琺瑯上釉薬が、さらに酸ィ匕チタン釉薬を、あるいはさらに透明ダロス釉薬を配 合したものであることを特徴とする請求の範囲第 8項に記載の映写黒板の製造方法。
[10] 前記酸ィ匕チタン被覆粒子が、雲母粒子の表面に酸ィ匕チタンを被覆してなる粒子で あることを特徴とする請求の範囲第 8項または請求の範囲第 9項に記載の映写黒板 の製造方法。
[11] 前記金属基板が、冷延鋼板、あるいはアルミめつき鋼板または Zn—Al合金めつき鋼 板であることを特徴とする請求の範囲第 8項ないし請求の範囲第 10項のいずれかに 記載の映写黒板の製造方法。
PCT/JP2005/021772 2005-09-02 2005-11-28 映写黒板およびその製造方法 WO2007029351A1 (ja)