WO2002041081A1 - Procede de formation de motif et agent de traitement a utiliser dans ce dernier - Google Patents
Procede de formation de motif et agent de traitement a utiliser dans ce dernier Download PDFInfo
- Publication number
- WO2002041081A1 WO2002041081A1 PCT/JP2001/009320 JP0109320W WO0241081A1 WO 2002041081 A1 WO2002041081 A1 WO 2002041081A1 JP 0109320 W JP0109320 W JP 0109320W WO 0241081 A1 WO0241081 A1 WO 0241081A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- chemically amplified
- photoresist film
- treating agent
- forming
- amplified photoresist
- Prior art date
Description
Claims