WO1992004413A1 - Matieres thermoplastiques de conditionnement obtenues a partir d'acide lactique - Google Patents

Matieres thermoplastiques de conditionnement obtenues a partir d'acide lactique Download PDF

Info

Publication number
WO1992004413A1
WO1992004413A1 PCT/US1991/006327 US9106327W WO9204413A1 WO 1992004413 A1 WO1992004413 A1 WO 1992004413A1 US 9106327 W US9106327 W US 9106327W WO 9204413 A1 WO9204413 A1 WO 9204413A1
Authority
WO
WIPO (PCT)
Prior art keywords
lactide
lactic acid
plasticizer
composition
poly
Prior art date
Application number
PCT/US1991/006327
Other languages
English (en)
Inventor
Richard G. Sinclair
Joseph R. Preston
Original Assignee
Biopak Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US07/579,000 external-priority patent/US5216050A/en
Priority claimed from US07/579,460 external-priority patent/US5252642A/en
Priority claimed from US07/579,005 external-priority patent/US5180765A/en
Application filed by Biopak Technology Ltd filed Critical Biopak Technology Ltd
Priority to KR1019930700677A priority Critical patent/KR930703399A/ko
Priority to JP3516685A priority patent/JPH06504799A/ja
Priority to BR919106821A priority patent/BR9106821A/pt
Publication of WO1992004413A1 publication Critical patent/WO1992004413A1/fr
Priority to FI930992A priority patent/FI930992A/fi

Abstract

Un premier mode de réalisation général comprend des compositions d'acide polylactique biodégradables dans l'environnement intimement plastifiées avec des dérivés d'oligomères d'acide lactique, ainsi que des mélanges tels que l'acide lactique. Un second mode de réalisation général comprend un polymère biodégradable comportant de l'acide lactique polymérisé dans lequel le nombre d'unités n d'acide lactique à répétition est un nombre entier compris entre 450 et 10 000, et le carbone alpha est un mélange de configurations L et D avec une prépondérance d'unités soit D soit L. Un troisième mode de réalisation général comprend une composition dégradable dans l'environnement de mélanges d'un mélange physique d'acide polylactique, d'un polymère sélectionné dans le groupe constitué de polyéthylène térephtalate, d'un polymère ou d'un copolymère de styrène, d'éthylène, de propylène, de chlorure vinylique, d'acétate vinylique, de méthacrylate d'alkyle, d'acrylate d'alkyle et de mélanges physiques de ces derniers. Un quatrième mode de réalisation général comprend une composition dégradable dans l'environnement comportant des mélanges d'un mélange physique d'un acide polylactique, représentant environ 1 à 99 pourcent en poids de la composition, et d'un polymère compatible avec un mélange élastomère.
PCT/US1991/006327 1990-09-06 1991-09-04 Matieres thermoplastiques de conditionnement obtenues a partir d'acide lactique WO1992004413A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
KR1019930700677A KR930703399A (ko) 1990-09-06 1991-09-04 락트산으로부터 제조한 포장용 열가소성 수지
JP3516685A JPH06504799A (ja) 1990-09-06 1991-09-04 乳酸からの包装用熱可塑性プラスチック
BR919106821A BR9106821A (pt) 1990-09-06 1991-09-04 Termoplasticos para embalagem provenientes de acido latico
FI930992A FI930992A (fi) 1990-09-06 1993-03-05 Ur mjoelksyra framstaellda termoplastiska foerpackningsplaster

Applications Claiming Priority (8)

Application Number Priority Date Filing Date Title
US57946590A 1990-09-06 1990-09-06
US07/579,000 US5216050A (en) 1988-08-08 1990-09-06 Blends of polyactic acid
US579,465 1990-09-06
US07/579,460 US5252642A (en) 1989-03-01 1990-09-06 Degradable impact modified polyactic acid
US579,005 1990-09-06
US579,460 1990-09-06
US07/579,005 US5180765A (en) 1988-08-08 1990-09-06 Biodegradable packaging thermoplastics from lactides
US579,000 1990-09-06

Publications (1)

Publication Number Publication Date
WO1992004413A1 true WO1992004413A1 (fr) 1992-03-19

Family

ID=27504934

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1991/006327 WO1992004413A1 (fr) 1990-09-06 1991-09-04 Matieres thermoplastiques de conditionnement obtenues a partir d'acide lactique

Country Status (9)

Country Link
EP (1) EP0548284A1 (fr)
JP (1) JPH06504799A (fr)
KR (1) KR930703399A (fr)
CN (1) CN1061421A (fr)
AU (1) AU8660191A (fr)
BR (1) BR9106821A (fr)
CA (1) CA2091185A1 (fr)
FI (1) FI930992A (fr)
WO (1) WO1992004413A1 (fr)

Cited By (56)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0544701A1 (fr) * 1990-07-16 1993-06-09 E.I. Du Pont De Nemours And Company Films d'acide polyhydroxy
EP0515203A3 (en) * 1991-05-24 1993-08-11 Novacor Chemicals (International) S.A. Polylactide blends
US5247058A (en) * 1992-01-24 1993-09-21 Cargill, Incorporated Continuous process for manufacture of lactide polymers with controlled optical purity
US5247059A (en) * 1992-01-24 1993-09-21 Cargill, Incorporated Continuous process for the manufacture of a purified lactide from esters of lactic acid
EP0562528A1 (fr) * 1992-03-27 1993-09-29 MITSUI TOATSU CHEMICALS, Inc. Récipient biodégradable en polymères d'acide lactique
US5258488A (en) * 1992-01-24 1993-11-02 Cargill, Incorporated Continuous process for manufacture of lactide polymers with controlled optical purity
US5274073A (en) * 1992-01-24 1993-12-28 Cargill, Incorporated Continuous process for manufacture of a purified lactide
WO1994011445A1 (fr) * 1992-11-06 1994-05-26 Zeneca Limited Composition en polyester
US5338822A (en) * 1992-10-02 1994-08-16 Cargill, Incorporated Melt-stable lactide polymer composition and process for manufacture thereof
EP0662107A1 (fr) * 1992-09-22 1995-07-12 BioPak Technology, Ltd. Regulation de degradation de materiaux jetables, degradables par l'environnement
JPH07207041A (ja) * 1994-01-11 1995-08-08 Mitsubishi Plastics Ind Ltd ポリ乳酸系フイルム
JPH07205278A (ja) * 1994-01-11 1995-08-08 Mitsubishi Plastics Ind Ltd ポリ乳酸系重合体延伸フイルムの製造方法
EP0683207A3 (fr) * 1994-05-19 1996-02-21 Mitsui Toatsu Chemicals Composition de polymère de L-acide lactique, produit moulé et feuille.
US5525706A (en) * 1992-10-02 1996-06-11 Cargill, Incorporated Melt-stable lactide polymer nonwoven fabric and process for manufacture thereof
GB2296013A (en) * 1994-12-13 1996-06-19 Moelnlycke Ab A lactic acid excreting ploylactide sheet for use in absorbent articles
WO1996040031A2 (fr) * 1995-06-07 1996-12-19 Kimberly-Clark Worldwide, Inc. Appareil et procede de formation d'un applicateur en papier a revetement compostable, et article obtenu
US5594095A (en) * 1993-07-30 1997-01-14 Cargill, Incorporated Viscosity-modified lactide polymer composition and process for manufacture thereof
EP0765913A1 (fr) * 1995-09-29 1997-04-02 Dainippon Ink And Chemicals, Inc. Procédé de préparation des compositions de polyesters à base d'acide lactique
US5665474A (en) * 1992-10-02 1997-09-09 Cargill, Incorporated Paper having a melt-stable lactide polymer coating and process for manufacture thereof
US5714573A (en) * 1995-01-19 1998-02-03 Cargill, Incorporated Impact modified melt-stable lactide polymer compositions and processes for manufacture thereof
US5795320A (en) * 1995-06-07 1998-08-18 Kimberly-Clark Worldwide, Inc. Paper applicator containing a compostable coating
US5849401A (en) * 1995-09-28 1998-12-15 Cargill, Incorporated Compostable multilayer structures, methods for manufacture, and articles prepared therefrom
US5849374A (en) * 1995-09-28 1998-12-15 Cargill, Incorporated Compostable multilayer structures, methods for manufacture, and articles prepared therefrom
EP0934976A2 (fr) * 1998-02-06 1999-08-11 KABUSHIKI KAISHA KOBE SEIKO SHO also known as Kobe Steel Ltd. Matière à mouler biodégradable
US5984888A (en) * 1995-06-07 1999-11-16 Kimberly-Clark Worldwide, Inc. Applicator and coating
US6005068A (en) * 1992-10-02 1999-12-21 Cargill Incorporated Melt-stable amorphous lactide polymer film and process for manufacture thereof
US6005067A (en) * 1992-01-24 1999-12-21 Cargill Incorporated Continuous process for manufacture of lactide polymers with controlled optical purity
US6114495A (en) * 1998-04-01 2000-09-05 Cargill Incorporated Lactic acid residue containing polymer composition and product having improved stability, and method for preparation and use thereof
US6183814B1 (en) 1997-05-23 2001-02-06 Cargill, Incorporated Coating grade polylactide and coated paper, preparation and uses thereof, and articles prepared therefrom
US6323307B1 (en) 1988-08-08 2001-11-27 Cargill Dow Polymers, Llc Degradation control of environmentally degradable disposable materials
US6326458B1 (en) 1992-01-24 2001-12-04 Cargill, Inc. Continuous process for the manufacture of lactide and lactide polymers
EP0585747B2 (fr) † 1992-08-24 2002-10-30 MITSUI TOATSU CHEMICALS, Inc. Produit formé à partir de polymère à base d'acide L-lactique et son procédé de préparation
DE10127314A1 (de) * 2001-06-06 2002-12-19 Trespaphan Gmbh Biologisch abbaubare biaxial verstreckte Folie mit kontrolliertem Weiterreißverhalten
JP2003002984A (ja) * 2002-06-14 2003-01-08 Mitsubishi Plastics Ind Ltd ポリ乳酸系フィルム
US6506873B1 (en) 1997-05-02 2003-01-14 Cargill, Incorporated Degradable polymer fibers; preparation product; and, methods of use
EP1473324A1 (fr) * 2002-02-05 2004-11-03 Mitsui Chemicals, Inc. Composition de resine biodegradable et objet moule a base de cette composition
EP1609819A1 (fr) * 2003-03-28 2005-12-28 Toray Industries, Inc. Composition de resine d'acide polylactique, procede de production de celle-ci, film d'acide polylactique etire de maniere biaxiale et articles moules associes
WO2006080560A1 (fr) * 2005-01-27 2006-08-03 Dow Corning Toray Co., Ltd. Composition elastomere thermoplastique pour moulage de fenetre de vehicule
WO2006109872A1 (fr) * 2005-04-08 2006-10-19 Dow Corning Toray Co., Ltd. Composition d’elastomere thermoplastique et ensemble de panneaux de verre moules pour un vehicule
EP1975201A1 (fr) * 2007-03-30 2008-10-01 Total Petrochemicals France Composition de polymère monovinylaromatique comprenant un polymère fabriqué à partir de ressources renouvelables en tant que phase dispersée
WO2009092825A1 (fr) * 2008-01-25 2009-07-30 Paolo Ara Procédé de plastification de polymères d'acide lactique
EP2147934A1 (fr) 2008-07-25 2010-01-27 Total Petrochemicals France Procédé de fabrication d'une composition comportant un polymère mono-vinyl-aromatique et polymère fabriqué à partir de ressources renouvelables
CN101362853B (zh) * 2008-09-12 2011-03-30 浙江海正生物材料股份有限公司 一种低成本全生物降解聚乳酸片材及其制备方法
US7919566B2 (en) 2007-01-22 2011-04-05 Tate & Lyle Public Limited Company Lactic acid polymers
US8851084B2 (en) 2011-07-19 2014-10-07 British American Tobacco (Investments) Limited Cellulose acetate compositions
US9085660B2 (en) 2011-03-31 2015-07-21 British American Tobacco (Investments) Limited Blends of a polylactic acid and a water soluble polymer
US20150218358A1 (en) * 2011-06-29 2015-08-06 Fina Technology, Inc. Epoxy Functional Polystyrene for Enhanced PLA Miscibility
US9381693B2 (en) 2012-12-24 2016-07-05 Innovia Films Limited Packaging and labelling films
WO2017200756A1 (fr) * 2016-05-20 2017-11-23 3M Innovative Properties Company Film orienté à base d'un polymère d'acide lactique
RU2637022C2 (ru) * 2012-03-07 2017-11-29 Хухтамяки Оюй Термоформуемая композиция в основном на основе биологического сырья и формованные из нее контейнеры
CN109312147A (zh) * 2016-06-21 2019-02-05 3M创新有限公司 包括半结晶聚乳酸基膜的图形制品
EP3581608A1 (fr) * 2018-06-14 2019-12-18 Stichting Wageningen Research Produits polymères
US10577494B2 (en) 2014-12-22 2020-03-03 3M Innovative Properties Company Compositions and films comprising polylactic acid polymer, polyvinyl acetate polymer and plasticizer
WO2020236467A1 (fr) * 2019-05-17 2020-11-26 Northern Technologies International Corporation Mélange maître à base de polylactide pour processus de moulage par injection de recuit en moule en une seule étape commercialement viable
US11098191B2 (en) 2014-06-05 2021-08-24 Omya International Ag Polymer composition filled with an inorganic filler material mixture
US11407872B2 (en) 2016-06-21 2022-08-09 3M Innovative Properties Company Foam compositions comprising polylactic acid polymer, polyvinyl acetate polymer and plasticizer, articles, and methods of making and using same

Families Citing this family (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
AU667048B2 (en) * 1992-09-07 1996-03-07 Guidor Ab Bioresorbable material and an article of manufacture made of such material for medical use
JPH06330001A (ja) * 1992-09-28 1994-11-29 Mitsui Toatsu Chem Inc 分解性粘着フィルム
JP3301506B2 (ja) * 1993-09-20 2002-07-15 大日本インキ化学工業株式会社 ラクタイド系共重合体の製造方法
JP3330273B2 (ja) * 1996-01-11 2002-09-30 三菱樹脂株式会社 熱収縮性ポリ乳酸系フィルムおよびその製造方法
JP2001294737A (ja) * 2000-04-12 2001-10-23 Musashino Chemical Laboratory Ltd 改善された物性を有する生分解性ポリエステル樹脂組成物
CN1320044C (zh) 2003-04-25 2007-06-06 株式会社艾迪科 聚乳酸类树脂组合物、成型品及其制备方法
JP2005226056A (ja) * 2004-02-16 2005-08-25 Asahi Kasei Chemicals Corp 脂肪族ポリエステル樹脂の成形体
JP2005226055A (ja) * 2004-02-16 2005-08-25 Asahi Kasei Chemicals Corp 脂肪族ポリエステル樹脂成形体
CN100443541C (zh) * 2004-02-16 2008-12-17 三井化学株式会社 含有共聚物的脂肪族聚酯树脂组合物
JP4640765B2 (ja) 2004-09-03 2011-03-02 株式会社Ａｄｅｋａ ポリ乳酸系樹脂組成物、成形品及びその製造方法
JP4622397B2 (ja) * 2004-09-06 2011-02-02 住友ベークライト株式会社 カレンダー成形用ポリ乳酸系樹脂組成物およびシート
CN101838425B (zh) 2005-08-04 2012-07-18 东丽株式会社 树脂组合物和由该树脂组合物形成的成型品
JP5223076B2 (ja) * 2006-03-24 2013-06-26 和歌山県 樹脂組成物の物理的性質制御方法
JP5583912B2 (ja) * 2008-04-28 2014-09-03 花王株式会社 ポリ乳酸樹脂組成物の製造法
JP4574701B2 (ja) * 2008-08-25 2010-11-04 富士通株式会社 生分解性樹脂組成物とそれを用いた樹脂筐体
AU2009311593B2 (en) * 2008-11-07 2012-09-13 Colgate-Palmolive Company Blends of polylactic acid and thermo-plastic polymers for packaging applications
CN102079852A (zh) * 2010-12-16 2011-06-01 昆明学院 环保型茶具及其制备方法
EP2787040B1 (fr) * 2013-04-04 2016-02-03 Instituto Tecnológico Del Embalaje, Transporte Y Logistica Itene Composition pour la préparation d'un matériau polymère biodégradable nanostructuré, le matériau ainsi obtenu et ses utilisations
MX2017014225A (es) * 2015-05-07 2018-04-20 Fina Technology Polietileno para un rendimiento superior de termoformacon de extrusion de lamina.
CN105061478B (zh) * 2015-08-07 2017-05-10 常州大学 一种热稳定锌金属有机骨架材料及其制备方法和应用
FR3083544B1 (fr) * 2018-07-06 2020-09-11 Carbiolice Matiere plastique à haute teneur en pla comprenant des oligomeres d’acide lactique
CN109777053B (zh) * 2019-01-11 2021-10-29 海南三碳科技有限公司 一种含乳酸钙可控生物降解速率的材料
JP2022536064A (ja) * 2019-06-13 2022-08-12 ネイチャーワークス・エル・エル・シー 急速加水分解ポリラクチド樹脂組成物

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0202065A2 (fr) * 1985-05-07 1986-11-20 Takeda Chemical Industries, Ltd. Polymère, sa préparation et son utilisation
WO1990001521A1 (fr) * 1988-08-08 1990-02-22 Battelle Memorial Institute Thermoplastique degradable derive de lactides

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0202065A2 (fr) * 1985-05-07 1986-11-20 Takeda Chemical Industries, Ltd. Polymère, sa préparation et son utilisation
WO1990001521A1 (fr) * 1988-08-08 1990-02-22 Battelle Memorial Institute Thermoplastique degradable derive de lactides

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
CHEMICAL ABSTRACTS, vol. 108, no. 18, 2 May 1988, Columbus, Ohio, US; abstract no. 156432B, T. NAKAMURA: 'surgical application of biodegradable films prepared from lactide-"epsilon"-caprolactone copolymers' page 391 ;column 2 ; & Adv. Biomater. 1987, 7(Biomater. Clin. Appl.), 759-64 SA 52077 030see abstract *
CHEMICAL ABSTRACTS, vol. 110, no. 24, 12 June 1989, Columbus, Ohio, US; abstract no. 219007F, R. BODMEIER: 'the effect of the addition of low-molecular weight poly(dl-lactide) on drug release from biodegradable poly(DL-lactide) drug delivery systems' page 409 ;column 2 ; & Int. J. Pharm. 1989, 51(1), 1-8 SA 52077 030see abstract *

Cited By (117)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6323307B1 (en) 1988-08-08 2001-11-27 Cargill Dow Polymers, Llc Degradation control of environmentally degradable disposable materials
EP0544701A4 (en) * 1990-07-16 1993-07-14 E.I. Du Pont De Nemours And Company Polyhydroxy acid films
EP0544701A1 (fr) * 1990-07-16 1993-06-09 E.I. Du Pont De Nemours And Company Films d'acide polyhydroxy
EP0748846A2 (fr) * 1991-05-24 1996-12-18 Camelot Technologies Inc. Compositions de polylactides
EP0515203A3 (en) * 1991-05-24 1993-08-11 Novacor Chemicals (International) S.A. Polylactide blends
EP0748846A3 (fr) * 1991-05-24 1997-02-12 Camelot Technologies Inc Compositions de polylactides
US6005067A (en) * 1992-01-24 1999-12-21 Cargill Incorporated Continuous process for manufacture of lactide polymers with controlled optical purity
US5274073A (en) * 1992-01-24 1993-12-28 Cargill, Incorporated Continuous process for manufacture of a purified lactide
US5258488A (en) * 1992-01-24 1993-11-02 Cargill, Incorporated Continuous process for manufacture of lactide polymers with controlled optical purity
US6277951B1 (en) 1992-01-24 2001-08-21 Cargill, Incorporated Continuous process for manufacture of lactide polymers with controlled optical purity
US5357035A (en) * 1992-01-24 1994-10-18 Cargill, Incorporated Continuous process for manufacture of lactide polymers with purification by distillation
US6326458B1 (en) 1992-01-24 2001-12-04 Cargill, Inc. Continuous process for the manufacture of lactide and lactide polymers
US5247059A (en) * 1992-01-24 1993-09-21 Cargill, Incorporated Continuous process for the manufacture of a purified lactide from esters of lactic acid
US5247058A (en) * 1992-01-24 1993-09-21 Cargill, Incorporated Continuous process for manufacture of lactide polymers with controlled optical purity
US5409751A (en) * 1992-03-27 1995-04-25 Mitsui Toatsu Chemicals, Incorporated Degradable container
EP0562528A1 (fr) * 1992-03-27 1993-09-29 MITSUI TOATSU CHEMICALS, Inc. Récipient biodégradable en polymères d'acide lactique
EP0585747B2 (fr) † 1992-08-24 2002-10-30 MITSUI TOATSU CHEMICALS, Inc. Produit formé à partir de polymère à base d'acide L-lactique et son procédé de préparation
EP0662107A1 (fr) * 1992-09-22 1995-07-12 BioPak Technology, Ltd. Regulation de degradation de materiaux jetables, degradables par l'environnement
EP0662107A4 (fr) * 1992-09-22 1995-09-27 Biopak Technology Ltd Regulation de degradation de materiaux jetables, degradables par l'environnement.
US5852166A (en) * 1992-10-02 1998-12-22 Cargill, Incorporated Paper having a melt-stable lactide polymer coating and process for manufacture thereof
US5981694A (en) * 1992-10-02 1999-11-09 Cargill, Incorporated Melt-stable lactide polymer composition and process for manufacture thereof
US5536807A (en) * 1992-10-02 1996-07-16 Cargill, Incorporated Melt-stable semi-crystalline lactide polymer film and process for manufacture thereof
US5539081A (en) * 1992-10-02 1996-07-23 Cargill, Incorporated Melt-stable lactide polymer composition and process for manufacture thereof
US6093791A (en) * 1992-10-02 2000-07-25 Cargill, Incorporated Melt-stable semi-crystalline lactide polymer film and process for manufacture thereof
US5585191A (en) * 1992-10-02 1996-12-17 Cargill, Incorporated Melt-stable amorphous lactide polymer film and process for manufacture thereof
US5525706A (en) * 1992-10-02 1996-06-11 Cargill, Incorporated Melt-stable lactide polymer nonwoven fabric and process for manufacture thereof
US6143863A (en) * 1992-10-02 2000-11-07 Cargill, Incorporated Melt-stable lactide polymer composition and process for manufacture thereof
US6005068A (en) * 1992-10-02 1999-12-21 Cargill Incorporated Melt-stable amorphous lactide polymer film and process for manufacture thereof
US6207792B1 (en) 1992-10-02 2001-03-27 Cargill, Incorporated Melt-stable amorphous lactide polymer film and process for manufacture thereof
US5484881A (en) * 1992-10-02 1996-01-16 Cargill, Inc. Melt-stable amorphous lactide polymer film and process for manufacturing thereof
US5475080A (en) * 1992-10-02 1995-12-12 Cargill, Incorporated Paper having a melt-stable lactide polymer coating and process for manufacture thereof
US5665474A (en) * 1992-10-02 1997-09-09 Cargill, Incorporated Paper having a melt-stable lactide polymer coating and process for manufacture thereof
US6355772B1 (en) 1992-10-02 2002-03-12 Cargill, Incorporated Melt-stable lactide polymer nonwoven fabric and process for manufacture thereof
US5338822A (en) * 1992-10-02 1994-08-16 Cargill, Incorporated Melt-stable lactide polymer composition and process for manufacture thereof
US6121410A (en) * 1992-10-02 2000-09-19 Cargill, Incorporated Melt-stable semi-crystalline lactide polymer film and process for manufacture thereof
US5798436A (en) * 1992-10-02 1998-08-25 Cargill, Incorporated Melt-stable amorphous lactide polymer film and process for manufacture thereof
US5763564A (en) * 1992-10-02 1998-06-09 Cargill, Incorporated Melt-stable lactide polymer composition and process for manufacture thereof
US5773562A (en) * 1992-10-02 1998-06-30 Cargill, Incorporated Melt-stable semi-crystalline lactide polymer film and process for manufacture thereof
AU684499B2 (en) * 1992-11-06 1997-12-18 Monsanto Company Polyester composition
US5550173A (en) * 1992-11-06 1996-08-27 Zeneca Limited Polyester composition
WO1994011445A1 (fr) * 1992-11-06 1994-05-26 Zeneca Limited Composition en polyester
US6291597B1 (en) 1993-07-30 2001-09-18 Cargill, Incorporated Viscosity-modified lactide polymer composition and process for manufacture thereof
US5798435A (en) * 1993-07-30 1998-08-25 Cargill, Incorporated Viscosity-modified lactide polymer composition and process for manufacture thereof
US5594095A (en) * 1993-07-30 1997-01-14 Cargill, Incorporated Viscosity-modified lactide polymer composition and process for manufacture thereof
US5998552A (en) * 1993-07-30 1999-12-07 Cargill, Incorporated Viscosity-modified lactide polymer composition and process for manufacture thereof
JPH07205278A (ja) * 1994-01-11 1995-08-08 Mitsubishi Plastics Ind Ltd ポリ乳酸系重合体延伸フイルムの製造方法
JPH07207041A (ja) * 1994-01-11 1995-08-08 Mitsubishi Plastics Ind Ltd ポリ乳酸系フイルム
EP0683207A3 (fr) * 1994-05-19 1996-02-21 Mitsui Toatsu Chemicals Composition de polymère de L-acide lactique, produit moulé et feuille.
US5763513A (en) * 1994-05-19 1998-06-09 Mitsui Toatsu Chemicals, Inc. L-lactic acid polymer composition, molded product and film
US6136905A (en) * 1994-05-19 2000-10-24 Mitsui Chemicals, Inc. L-lactic acid polymer composition, molded product and film
GB2296013A (en) * 1994-12-13 1996-06-19 Moelnlycke Ab A lactic acid excreting ploylactide sheet for use in absorbent articles
GB2296013B (en) * 1994-12-13 1999-05-12 Moelnlycke Ab A lactic acid excreting polyactide sheet for use in absorbant articles
US6020453A (en) * 1994-12-13 2000-02-01 Sca Molnlycke Products Ab Lactic acid excreting polylactide sheet for use in absorbent articles
US5922832A (en) * 1995-01-19 1999-07-13 Cargill, Incorporated Impact modified melt-stable lactide polymer compositions and processes for manufacture thereof
US5714573A (en) * 1995-01-19 1998-02-03 Cargill, Incorporated Impact modified melt-stable lactide polymer compositions and processes for manufacture thereof
US6495631B1 (en) 1995-01-19 2002-12-17 Cargill, Incorporated Impact modified melt-stable lactide polymer compositions and processes for manufacture thereof
WO1996040031A3 (fr) * 1995-06-07 1997-02-20 Kimberly Clark Co Appareil et procede de formation d'un applicateur en papier a revetement compostable, et article obtenu
US5984888A (en) * 1995-06-07 1999-11-16 Kimberly-Clark Worldwide, Inc. Applicator and coating
WO1996040031A2 (fr) * 1995-06-07 1996-12-19 Kimberly-Clark Worldwide, Inc. Appareil et procede de formation d'un applicateur en papier a revetement compostable, et article obtenu
US5795320A (en) * 1995-06-07 1998-08-18 Kimberly-Clark Worldwide, Inc. Paper applicator containing a compostable coating
US6312823B1 (en) 1995-09-28 2001-11-06 Cargrill, Incorporated Compostable multilayer structures, methods for manufacture and articles prepared therefrom
US5849401A (en) * 1995-09-28 1998-12-15 Cargill, Incorporated Compostable multilayer structures, methods for manufacture, and articles prepared therefrom
US5849374A (en) * 1995-09-28 1998-12-15 Cargill, Incorporated Compostable multilayer structures, methods for manufacture, and articles prepared therefrom
US5686540A (en) * 1995-09-29 1997-11-11 Dainippon Ink And Chemicals, Inc. Process for the preparation of lactic acid-based polyester
EP0765913A1 (fr) * 1995-09-29 1997-04-02 Dainippon Ink And Chemicals, Inc. Procédé de préparation des compositions de polyesters à base d'acide lactique
US6506873B1 (en) 1997-05-02 2003-01-14 Cargill, Incorporated Degradable polymer fibers; preparation product; and, methods of use
US6183814B1 (en) 1997-05-23 2001-02-06 Cargill, Incorporated Coating grade polylactide and coated paper, preparation and uses thereof, and articles prepared therefrom
EP0934976A3 (fr) * 1998-02-06 2000-02-02 KABUSHIKI KAISHA KOBE SEIKO SHO also known as Kobe Steel Ltd. Matière à mouler biodégradable
EP0934976A2 (fr) * 1998-02-06 1999-08-11 KABUSHIKI KAISHA KOBE SEIKO SHO also known as Kobe Steel Ltd. Matière à mouler biodégradable
US6114495A (en) * 1998-04-01 2000-09-05 Cargill Incorporated Lactic acid residue containing polymer composition and product having improved stability, and method for preparation and use thereof
US6353086B1 (en) 1998-04-01 2002-03-05 Cargill, Incorporated Lactic acid residue containing polymer composition and product having improved stability, and method for preparation and use thereof
DE10127314A1 (de) * 2001-06-06 2002-12-19 Trespaphan Gmbh Biologisch abbaubare biaxial verstreckte Folie mit kontrolliertem Weiterreißverhalten
EP1473324A4 (fr) * 2002-02-05 2005-07-06 Mitsui Chemicals Inc Composition de resine biodegradable et objet moule a base de cette composition
EP1473324A1 (fr) * 2002-02-05 2004-11-03 Mitsui Chemicals, Inc. Composition de resine biodegradable et objet moule a base de cette composition
JP2003002984A (ja) * 2002-06-14 2003-01-08 Mitsubishi Plastics Ind Ltd ポリ乳酸系フィルム
EP1609819A1 (fr) * 2003-03-28 2005-12-28 Toray Industries, Inc. Composition de resine d'acide polylactique, procede de production de celle-ci, film d'acide polylactique etire de maniere biaxiale et articles moules associes
EP1609819A4 (fr) * 2003-03-28 2006-04-12 Toray Industries Composition de resine d'acide polylactique, procede de production de celle-ci, film d'acide polylactique etire de maniere biaxiale et articles moules associes
US7718718B2 (en) 2003-03-28 2010-05-18 Toray Industries, Inc. Polylactic acid resin composition, process for producing the same, biaxially stretched polylactic acid film, and molded articles thereof
WO2006080560A1 (fr) * 2005-01-27 2006-08-03 Dow Corning Toray Co., Ltd. Composition elastomere thermoplastique pour moulage de fenetre de vehicule
WO2006109872A1 (fr) * 2005-04-08 2006-10-19 Dow Corning Toray Co., Ltd. Composition d’elastomere thermoplastique et ensemble de panneaux de verre moules pour un vehicule
US8067495B2 (en) 2005-04-08 2011-11-29 Dow Corning Toray Company, Ltd. Thermoplastic elastomer composition and glass panel molding assembly for a vehicle
US7919566B2 (en) 2007-01-22 2011-04-05 Tate & Lyle Public Limited Company Lactic acid polymers
KR101207819B1 (ko) 2007-03-30 2012-12-05 토탈 페트로케미컬스 프랑스 재생산가능한 자원으로부터 분산상으로서 제조된 중합체를 함유하는 모노비닐방향족 중합체 조성물
US8575271B2 (en) 2007-03-30 2013-11-05 Total Petrochemicals France Monovinylaromatic polymer composition comprising a polymer made from renewable resources as a dispersed phase
EP1975201A1 (fr) * 2007-03-30 2008-10-01 Total Petrochemicals France Composition de polymère monovinylaromatique comprenant un polymère fabriqué à partir de ressources renouvelables en tant que phase dispersée
WO2008119668A1 (fr) * 2007-03-30 2008-10-09 Total Petrochemicals France Composition de polymère monovinylaromatique comprenant un polymère obtenu à partir de ressources renouvelables comme phase dispersée
WO2009092825A1 (fr) * 2008-01-25 2009-07-30 Paolo Ara Procédé de plastification de polymères d'acide lactique
US8084551B2 (en) 2008-01-25 2011-12-27 Marco Paolo Ara Method for plasticizing lactic acid polymers
US9527993B2 (en) 2008-07-25 2016-12-27 Total Research & Technology Feluy Process to make a composition comprising a monovinylaromatic polymer and a polymer made from renewable resources
EP2147934A1 (fr) 2008-07-25 2010-01-27 Total Petrochemicals France Procédé de fabrication d'une composition comportant un polymère mono-vinyl-aromatique et polymère fabriqué à partir de ressources renouvelables
CN101362853B (zh) * 2008-09-12 2011-03-30 浙江海正生物材料股份有限公司 一种低成本全生物降解聚乳酸片材及其制备方法
US9085660B2 (en) 2011-03-31 2015-07-21 British American Tobacco (Investments) Limited Blends of a polylactic acid and a water soluble polymer
US20150218358A1 (en) * 2011-06-29 2015-08-06 Fina Technology, Inc. Epoxy Functional Polystyrene for Enhanced PLA Miscibility
US9796842B2 (en) * 2011-06-29 2017-10-24 Fina Technology, Inc. Epoxy functional polystyrene for enhanced PLA miscibility
US8851084B2 (en) 2011-07-19 2014-10-07 British American Tobacco (Investments) Limited Cellulose acetate compositions
RU2637022C2 (ru) * 2012-03-07 2017-11-29 Хухтамяки Оюй Термоформуемая композиция в основном на основе биологического сырья и формованные из нее контейнеры
US10626271B2 (en) 2012-03-07 2020-04-21 Huhtamäki Oyj Essentially biobased, thermoformable composition and containers formed thereof
US9381693B2 (en) 2012-12-24 2016-07-05 Innovia Films Limited Packaging and labelling films
US11098191B2 (en) 2014-06-05 2021-08-24 Omya International Ag Polymer composition filled with an inorganic filler material mixture
US11787929B2 (en) 2014-12-22 2023-10-17 3M Innovative Properties Company Compositions and films comprising polylactic acid polymer, polyvinyl acetate polymer and plasticizer
US11254812B2 (en) 2014-12-22 2022-02-22 3M Innovative Properties Company Compositions and films comprising polylactic acid polymer, polyvinyl acetate polymer and plasticizer
US10577494B2 (en) 2014-12-22 2020-03-03 3M Innovative Properties Company Compositions and films comprising polylactic acid polymer, polyvinyl acetate polymer and plasticizer
CN109153799A (zh) * 2016-05-20 2019-01-04 3M创新有限公司 取向聚乳酸聚合物基膜
WO2017200756A1 (fr) * 2016-05-20 2017-11-23 3M Innovative Properties Company Film orienté à base d'un polymère d'acide lactique
CN109153799B (zh) * 2016-05-20 2022-03-08 3M创新有限公司 取向聚乳酸聚合物基膜
US11066551B2 (en) 2016-05-20 2021-07-20 3M Innovative Properties Company Oriented polylactic acid polymer based film
CN109312147A (zh) * 2016-06-21 2019-02-05 3M创新有限公司 包括半结晶聚乳酸基膜的图形制品
US10982090B2 (en) 2016-06-21 2021-04-20 3M Innovative Properties Company Graphic articles comprising polylactic acid polymer based film
CN109312147B (zh) * 2016-06-21 2021-04-16 3M创新有限公司 包括半结晶聚乳酸基膜的图形制品
US11407872B2 (en) 2016-06-21 2022-08-09 3M Innovative Properties Company Foam compositions comprising polylactic acid polymer, polyvinyl acetate polymer and plasticizer, articles, and methods of making and using same
US20190185662A1 (en) * 2016-06-21 2019-06-20 3M Innovative Properties Company Graphic articles comprising polylactic acid polymer based film
WO2019240583A1 (fr) * 2018-06-14 2019-12-19 Stichting Wageningen Research Produits polymères
EP3581608A1 (fr) * 2018-06-14 2019-12-18 Stichting Wageningen Research Produits polymères
WO2020236467A1 (fr) * 2019-05-17 2020-11-26 Northern Technologies International Corporation Mélange maître à base de polylactide pour processus de moulage par injection de recuit en moule en une seule étape commercialement viable
CN113748157A (zh) * 2019-05-17 2021-12-03 北方技术国际公司 用于商业可行的一步式模内退火注塑工艺的聚乳酸基母料
CN113748157B (zh) * 2019-05-17 2022-08-19 北方技术国际公司 用于商业可行的一步式模内退火注塑工艺的聚乳酸基母料
US11905407B2 (en) 2019-05-17 2024-02-20 Northern Technologies International Corporation Polylactide-based masterbatch, for a commercially viable single-step in-mold annealing injection molding process

Also Published As

Publication number Publication date
FI930992A0 (fi) 1993-03-05
BR9106821A (pt) 1993-07-13
KR930703399A (ko) 1993-11-30
CN1061421A (zh) 1992-05-27
EP0548284A1 (fr) 1993-06-30
JPH06504799A (ja) 1994-06-02
AU8660191A (en) 1992-03-30
CA2091185A1 (fr) 1992-03-07
FI930992A (fi) 1993-03-05

Similar Documents

Publication Publication Date Title
EP0428620B1 (fr) Méthode pour la plastification de polymères de lactide.
US5180765A (en) Biodegradable packaging thermoplastics from lactides
WO1992004413A1 (fr) Matieres thermoplastiques de conditionnement obtenues a partir d'acide lactique
US5424346A (en) Biodegradable replacement of crystal polystyrene
JP3037431B2 (ja) 分解性ポリマー組成物
CA1339026C (fr) Thermoplastique biodegradable a base de lactides
US6323307B1 (en) Degradation control of environmentally degradable disposable materials
JP3436368B2 (ja) 溶融安定性ラクチド・ポリマーフィルムとその製造方法
US5216050A (en) Blends of polyactic acid
US5550173A (en) Polyester composition
AU752603B2 (en) Condensation copolymers having surpressed crystallinity
EP1322345B1 (fr) Articles absorbants contenant des compositions a base de melanges de polyesters biodegradables
US7265188B2 (en) Biodegradable polyester blend compositions and methods of making the same
AU634723B2 (en) Degradable thermoplastic from lactides
EP1360237B1 (fr) Compositions a base de melanges de polyesters biodegradables et leurs procedes de preparation
JP3431042B2 (ja) 微生物分解性樹脂組成物
KR20000059820A (ko) 고용융점도를 갖는 생분해성 수지 조성물
PT91598B (pt) Processo para a preparacao de termoplasticos degradaveis de lactideos
DD299530A5 (de) Zerzetzbare thermoplaste aus lactiden

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU BB BG BR CA CS FI HU JP KP KR LK MC MG MN MW NO PL RO SD SU

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IT LU NL SE

WWE Wipo information: entry into national phase

Ref document number: 2091185

Country of ref document: CA

Ref document number: 930992

Country of ref document: FI

WWE Wipo information: entry into national phase

Ref document number: 1991919263

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1991919263

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1991919263

Country of ref document: EP