US20200190705A1 - Carbon fiber bundle and method of manufacturing same - Google Patents

Carbon fiber bundle and method of manufacturing same Download PDF

Info

Publication number
US20200190705A1
US20200190705A1 US16/623,479 US201816623479A US2020190705A1 US 20200190705 A1 US20200190705 A1 US 20200190705A1 US 201816623479 A US201816623479 A US 201816623479A US 2020190705 A1 US2020190705 A1 US 2020190705A1
Authority
US
United States
Prior art keywords
fiber bundle
carbon fiber
strands
heat
tensile strength
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/623,479
Other languages
English (en)
Inventor
Naohiro MATSUMOTO
Haruki Okuda
Fumihiko Tanaka
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Industries Inc
Original Assignee
Toray Industries Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Industries Inc filed Critical Toray Industries Inc
Assigned to TORAY INDUSTRIES, INC. reassignment TORAY INDUSTRIES, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: MATSUMOTO, NAOHIRO, OKUDA, HARUKI, TANAKA, FUMIHIKO
Publication of US20200190705A1 publication Critical patent/US20200190705A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
    • D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
    • D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
    • D01F9/14—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments
    • D01F9/20—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products
    • D01F9/21—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products from macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D01F9/22—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products from macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds from polyacrylonitriles
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F9/00—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments
    • D01F9/08—Artificial filaments or the like of other substances; Manufacture thereof; Apparatus specially adapted for the manufacture of carbon filaments of inorganic material
    • D01F9/12—Carbon filaments; Apparatus specially adapted for the manufacture thereof
    • D01F9/14—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments
    • D01F9/20—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products
    • D01F9/21—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products from macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D01F9/22—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products from macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds from polyacrylonitriles
    • D01F9/225—Carbon filaments; Apparatus specially adapted for the manufacture thereof by decomposition of organic filaments from polyaddition, polycondensation or polymerisation products from macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds from polyacrylonitriles from stabilised polyacrylonitriles
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D1/00—Treatment of filament-forming or like material
    • D01D1/10—Filtering or de-aerating the spinning solution or melt
    • D01D1/106—Filtering
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D10/00—Physical treatment of artificial filaments or the like during manufacture, i.e. during a continuous production process before the filaments have been collected
    • D01D10/02—Heat treatment
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/02—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D01F6/18—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from homopolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds from polymers of unsaturated nitriles, e.g. polyacrylonitrile, polyvinylidene cyanide
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/28—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from copolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D01F6/38—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from copolymers obtained by reactions only involving carbon-to-carbon unsaturated bonds comprising unsaturated nitriles as the major constituent
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/29—Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
    • Y10T428/2913—Rod, strand, filament or fiber
    • Y10T428/2918—Rod, strand, filament or fiber including free carbon or carbide or therewith [not as steel]

Definitions

  • This disclosure relates to a carbon fiber bundle and a method of manufacturing the same.
  • Carbon fiber bundles have been widely used as reinforcing fibers for composite materials, and there is a strong demand for more performance.
  • it is required to improve mechanical properties such as the tensile strength of resin-impregnated strands and elastic modulus of resin-impregnated strands of the carbon fiber bundle (hereinafter tensile strength of strands and elastic modulus of strands) in a well-balanced manner.
  • tensile strength of strands and elastic modulus of strands the environmental load in the manufacture of carbon fiber bundles.
  • a polyacrylonitrile-based carbon fiber bundle is obtained through a process in which a precursor fiber bundle for carbon fiber is heat-treated in an oxidizing atmosphere of 200 to 300° C.
  • carbonization yield the yield of the carbon fiber bundles (hereinafter carbonization yield) is about half. It is necessary to increase the yield of carbon fiber bundles with the same manufacturing energy from the viewpoint of reducing the manufacturing energy per production amount, that is, environmental load.
  • JP '541 studies have been made to improve the tensile strength of strands of the carbon fiber bundle by minimizing the amount of heat (J ⁇ h/g) given by high-temperature treatment in the oxidation process.
  • JP '729 it was proposed to set the oxidation temperature to a high temperature according to the amount of oxygen added in the middle of the oxidation process and, in JP '020, it was proposed to oxidize at a temperature as high as possible by repeating heating and cooling so that the precursor fiber bundle for carbon fiber does not thermally run away to shorten the oxidation process.
  • JP '778 and JP '242 proposed attempts to increase the carbonization yield by increasing the density of oxidized fiber bundle in a short time by heating the precursor fiber bundle for carbon fiber in an oxidizing atmosphere in an initial stage of oxidation, and then bringing it into contact with a high-temperature heating roller at 250 to 300° C.
  • WO 2013/157613 A and Japanese Patent Laid-open Publication No. 2015-096664 have proposed carbon fiber bundles with high knot strength that reflect mechanical properties in a direction other than a fiber axis direction and exhibit sufficient mechanical properties in pseudo-isotropic materials.
  • Japanese Patent Laid-open Publication No. 2017-66580 has proposed a carbon fiber bundle exhibiting a high carbonization yield, excellent tensile strength of strands and elastic modulus of strands in a well-balanced manner, and further satisfies excellent knot strength at the same time since an oxidized fiber bundle having a specific density can be obtained by performing high-temperature heat treatment in the latter half at an appropriate temperature profile in the oxidation process when obtaining an oxidized fiber bundle having a specific density to satisfy a high carbonization yield.
  • carbon fiber is a brittle material, and since a slight surface flaw and an internal flaw cause a decrease in tensile strength of strands, delicate attention has been paid to the generation of flaws.
  • Japanese Examined Patent Publication No. H8-6210 has proposed to reduce flaws on the surface of the carbon fiber to obtain a carbon fiber bundle having a high tensile strength of strands by densification of the precursor fiber bundle for carbon fiber, reduction of dust during the manufacturing process, and removal of flaw by electrochemical treatment.
  • JP '541 an attempt has been made to reduce the integrated value of the amount of heat given in the oxidation process, which is not sufficient to achieve both the tensile strength of strands and the carbonization yield.
  • JP '729 and JP '020 since the oxidation temperature has been increased and the oxidation time has been shortened, the oxidation temperature control that can satisfy the required tensile strength of strands is not performed, and suppression of stress concentration on a difference between skin-core structure has been a problem.
  • JP '778 and JP '242 while heat treatment has been performed at a high temperature using a heating roller with high heat transfer efficiency to perform heat treatment at a high temperature in a short time in the latter half of the oxidation process, sufficient tensile strength of strands has not been obtained due to too short heat treatment time at a high temperature, and generation of flaws due to adhesion between single fibers when passing through the roller.
  • WO '613 states that the knot strength is increased by adjusting the oxidation process even when the single fiber diameter is large, the effect is limited due to the structure distribution in the single fiber at the time of oxidation, and the level of knot strength has been insufficient.
  • JP '664 states that the knot strength is increased by mainly adjusting the surface treatment of the carbon fiber bundle and the sizing agent, it is limited to those having a low single fiber diameter, and in having a low single fiber diameter, the fracture tension of the single fiber is lowered during the manufacturing process so that there is a problem that the quality of the manufacturing process is lowered due to fiber fracture.
  • JP '580 the tensile strength of strands and knot strength have been increased by high-temperature heat treatment in the latter half at an appropriate temperature profile in the oxidation process, but the control of flaws affecting these characteristics has been not sufficient, and there has been room for improvement.
  • JP '210 although the flaws on the carbon fiber surface can be effectively removed by electrochemical treatment, strong electrochemical treatment is required to remove the flaws, and a long electrochemical treatment bath is required so that there has been a problem that it is difficult to implement industrially. In addition, there has been also a problem that a brittle layer that may lead to deterioration of mechanical properties of a composite is formed on the surface of the carbon fiber by strong electrochemical treatment. Furthermore, as a flaw, characteristics of flaws in the fracture surface collected when the single fiber tensile test was performed with a gauge length of 50 mm are defined.
  • the gauge length that affects the tensile strength of strands and the tensile strength of the composite material is shorter than 10 mm so that there has been also an essential problem that the carbon fiber bundles that increase the tensile strength of the composite material are not necessarily obtained simply by defining the characteristics of flaws observed at a gauge length of 50 mm.
  • the carbon fiber bundle has an elastic modulus of strands of 240 to 280 GPa, a tensile strength of strands of 5.8 GPa or more, a knot strength K [MPa] of ⁇ 88d+1390 ⁇ K (d: average single fiber diameter [ ⁇ m]), and an average single fiber diameter of 6.5 to 8.0 ⁇ m, wherein a probability that a flaw with a size of 50 nm or more exists on a fracture surface, which is collected when a single fiber tensile test is performed with a gauge length of 10 mm, is 35% or less.
  • an oxidized fiber bundle having a specific density can be obtained by heat-treating at an appropriate temperature profile in the oxidation process, whereby flaws governing the tensile strength of strands and the knot strength are controlled to be very small, and thus a carbon fiber bundle exhibiting the tensile strength of strands and the elastic modulus of strands in a well-balanced manner and has excellent knot strength can be manufactured without impairing productivity. Moreover, the carbon fiber bundle satisfies productivity at the time of manufacturing a composite material.
  • FIG. 1 is a scanning electron microscope (SEM) image of a fracture surface of a carbon fiber. Radial streaks converging to one point are confirmed.
  • FIG. 2 is an enlarged image of the vicinity of a fracture origin in FIG. 1 . Flaws like attached substances are confirmed.
  • FIG. 3 is an enlarged image of the vicinity of a fracture origin of another fracture surface. Flaws like dents are confirmed.
  • FIG. 4 is an enlarged image of the vicinity of a fracture origin of another fracture surface. No noticeable morphological features of 50 nm or more are confirmed.
  • the carbon fiber bundle has a tensile strength of strands of 5.8 GPa or more, and preferably 6.0 GPa or more.
  • a tensile strength of strands of 5.8 GPa or more when a composite material is manufactured using the carbon fiber bundle, the composite material exhibits good tensile strength. The higher tensile strength of strands of the carbon fiber bundle is better. However, even when the tensile strength of strands is 7.0 GPa or less, a sufficient tensile strength of the composite material can be obtained.
  • the tensile strength of strands can be determined by a method described in the strand tensile test of the carbon fiber bundle described later. In addition, this tensile strength of strands can be controlled by using the method of manufacturing a carbon fiber bundle described below.
  • the carbon fiber bundle has an elastic modulus of strands of 240 to 280 GPa, preferably 245 to 275 GPa, and more preferably 250 to 270 GPa.
  • An elastic modulus of strands of 240 to 280 GPa is preferable because of excellent balance between the elastic modulus of strands and the tensile strength of strands.
  • the elastic modulus of strands can be determined by a method described in the strand tensile test of the carbon fiber bundle described below. At this time, the strain range is set to 0.1 to 0.6%.
  • the elastic modulus of strands of the carbon fiber bundle can be controlled mainly by applying tension to the fiber bundle in any of the heat treatment processes in the manufacturing process of the carbon fiber bundle, improving the difference between skin-core structure that is the structure distribution within the single fiber, or changing the carbonization temperature.
  • a knot strength K obtained by forming a knot part at the midpoint portion of the carbon fiber bundle and performing a fiber bundle tensile test is preferably 700 MPa or more, more preferably 740 MPa or more, and further preferably 770 MPa or more.
  • the knot strength can be obtained by a method described in the knot strength of the carbon fiber bundle described below.
  • the knot strength is an index that reflects mechanical properties of the fiber bundle in a direction other than a fiber axis direction.
  • knot strength when having a knot strength of 700 MPa or more, even in conditions where the running speed of the fiber bundle is high, a composite material with high quality can be obtained.
  • the carbon fiber bundle preferably has the number of filaments of 10,000 to 60,000.
  • the number of filaments is 10,000 or more, a composite material can be manufactured with high productivity.
  • the number of filaments is 60,000 or less, the generation of fuzz at the time of manufacturing a composite material can be suppressed, and the running speed of the fiber bundle is increased so that the productivity is easily increased.
  • the knot strength K satisfies ⁇ 88d+1390 ⁇ K, during a filament winding molding process, even in a carbon fiber bundle with a large average single fiber diameter which is prone to fuzz due to abrasion with guide parts or rollers, it is possible to suppress the generation of fuzz and mold by increasing the running speed of the fiber bundle.
  • the probability that a flaw with a size of 50 nm or more exists on the fracture surface, which is collected when a single fiber tensile test is performed with a gauge length of 10 mm is preferably 35% or less, more preferably 30% or less, and further preferably 25% or less. It is known that the tensile fracture of carbon fiber starts from flaws. It is known that there are various types of flaws to be fracture origins of carbon fibers such as voids, damage on the fiber surface, dents, attached substances, or adhesion marks that remain after single fibers adhere to each other by the heat of heat treatment.
  • the probability that a flaw with a size of 50 nm or more exists on the fracture surface, which is collected when a single fiber tensile test is performed with a gauge length of 10 mm, is set to 35% or less, whereby flaws affecting the tensile strength of strands of the carbon fiber bundle and the tensile strength of the composite material are effectively reduced, as a result, the tensile strength of strands and the tensile strength of the composite material reach high levels.
  • the probability that a flaw with a size of 50 nm or more exists on the fracture surface which is collected when a single fiber tensile test is performed with a gauge length of 10 mm” is reduced by controlling filtration conditions of a spinning dope solution, that are filtration speed, particle retention, and filter basis weight, according to the methods described below, and effectively removing foreign substances in the spinning dope solution.
  • the average single fiber diameter is 6.5 to 8.0 ⁇ m, preferably 6.7 to 8.0 ⁇ m, more preferably 7.0 to 8.0 ⁇ m, further preferably 7.3 to 8.0 ⁇ m, and most preferably 7.5 to 8.0 ⁇ m.
  • the average single fiber diameter is smaller, the difference between skin-core structure tends to decrease.
  • it may cause insufficient impregnation due to a high matrix resin viscosity, which may lower the tensile strength of the composite material.
  • An average single fiber diameter of 6.5 to 8.0 ⁇ m is preferred because insufficient impregnation of a matrix resin is unlikely to occur and a high carbonization yield and tensile strength of strands are stably exhibited.
  • the average single fiber diameter can be calculated from the mass and density per unit length of the carbon fiber bundle and the number of filaments.
  • the average single fiber diameter of the carbon fiber bundle is increased by increasing the average single fiber diameter of the precursor fiber bundle for carbon fiber, increasing the carbonization yield in the carbonization process by controlling the oxidizing conditions, and lowering the pre-carbonization stretch ratio.
  • the carbon fiber bundle preferably has a mean surface roughness Ra of a single fiber surface measured by an atomic force microscope (AFM) of 1.8 nm or less. Details of the measurement method will be described later.
  • the mean surface roughness of the precursor fiber bundle for carbon fiber is substantially maintained even in the carbon fiber bundle.
  • the mean surface roughness is preferably 1.0 to 1.8 nm, and further preferably 1.6 nm or less. When the mean surface roughness exceeds 1.8 nm, it tends to be a stress concentration point during tension, and the tensile strength of strands may decrease. The lower mean surface roughness is better. However, when the mean surface roughness is less than 1.0 nm, the effect is often almost saturated.
  • the mean surface roughness of the carbon fiber bundle can be controlled by appropriately controlling spinning conditions of the precursor fiber bundle for carbon fiber (spinning method and coagulation bath conditions) and reducing the surface flaws of the carbon fiber bundle.
  • the carbon fiber bundle has an area ratio (hereinafter the skin layer ratio) in a cross section of a blackened thickness of an outer peripheral portion of the cross section perpendicular to the fiber axis direction of the single fiber of the carbon fiber of preferably 90% by area or more, more preferably 90 to 95% by area, and further preferably 90 to 93% by area.
  • the skin layer ratio is an area ratio (%) obtained by dividing an area occupied by the blackened thickness seen in the outer peripheral portion when observing a cross section perpendicular to the fiber axis direction of the single fiber of the carbon fiber with an optical microscope, by an entire cross-sectional area.
  • the higher the skin layer ratio the more the surface layer stress concentration can be suppressed so that high tensile strength of strands can be exhibited.
  • the skin layer ratio is low, a high carbonization yield and a high tensile strength of strands are hardly exhibited.
  • the skin layer ratio is 90% by area or more, the ratio of stress-bearing part on the outer peripheral portion is sufficiently large so that stress concentration on the surface layer is suppressed.
  • the blackened thickness can be measured by embedding a carbon fiber bundle in a resin, polishing a cross section perpendicular to the fiber axis direction, and observing the cross section with an optical microscope. Details will be described later.
  • Our method of manufacturing a carbon fiber bundle is based on the fact that we found that a carbon fiber bundle in which the number of flaws governing the tensile strength of strands and the knot strength is controlled to be extremely small, and a high carbonization yield and excellent tensile strength of strands and knot strength are exhibited is obtained by performing high-temperature heat treatment in the latter half at an appropriate temperature profile in the oxidation process so that the oxidized fiber bundle has a specific density.
  • a preferred example will be described in detail below.
  • the precursor fiber bundle for carbon fiber can be obtained by spinning a spinning dope solution in which a polyacrylonitrile copolymer is dissolved in a solvent. At this time, the spinning dope solution is filtered under specific conditions to effectively remove foreign substances in the spinning dope solution, and then the filtered spinning dope solution is spun to obtain a precursor fiber bundle for carbon fiber.
  • the obtained precursor fiber bundle for carbon fiber is subjected to at least an oxidation process, a pre-carbonization process and a carbonization process so that a carbon fiber bundle having a high tensile strength of strands with few flaws can be obtained.
  • the polyacrylonitrile copolymer it is preferable to use a polyacrylonitrile copolymer containing other monomers in addition to acrylonitrile as a main component.
  • the polyacrylonitrile copolymer preferably contains 90 to 100% by mass of acrylonitrile and less than 10% by mass of a copolymerizable monomer.
  • the polyacrylonitrile copolymer preferably contains a copolymer component such as itaconic acid, acrylamide and methacrylic acid, from the viewpoint of improving the stability of the spinning process, the viewpoint of efficiently performing the oxidation treatment, and the like.
  • the method of manufacturing the polyacrylonitrile copolymer can be selected from known polymerization methods.
  • the spinning dope solution is a solution prepared by dissolving the polyacrylonitrile copolymer in a solvent in which polyacrylonitrile such as dimethyl sulfoxide, dimethylformamide, dimethylacetamide or nitric acid/zinc chloride/aqueous sodium rhodanide solution is soluble.
  • the filter device means a facility that filters and removes foreign substances present in the spinning dope solution, composed of an inflow path that introduces the spinning dope solution to be subjected to filtration into the filter device, a filter medium that filters the spinning dope solution, an outflow path that guides the filtered spinning dope solution to outside the filter device, and a storage container.
  • the filter medium is a means for filtering a spinning dope solution stored in the filter device.
  • the filter medium As the form of the filter medium, a leaf disc type filter, a candle type filter, a pleated candle type filter or the like is used.
  • the filter medium of the candle type filter or pleated candle type filter has constant curvature, whereas the leaf disc type filter can use the filter medium in a substantially planar form so that this is preferable because it has an advantage that the pore diameter distribution hardly spreads and the cleaning property is easily maintained.
  • the filter medium is a member that plays a direct role in removing foreign substances present in the spinning dope solution.
  • the filter medium is required to hold the determined opening diameters with narrow variations and, additionally, chemical stability to a substance to be treated, heat resistance and pressure resistance are required.
  • a wire gauze prepared by weaving metal fibers, glass nonwoven fabric, filter medium made of a sintered metal fiber tissue and the like are preferably used.
  • the material of the filter medium is not particularly limited as long as it is inert to the spinning dope solution and contains no elutable component into the solvent, but metals are more preferable from the viewpoint of durability and cost.
  • metal fibers in addition to stainless steel (SUS304, SUS304L, SUS316, SUS316L and the like), “INCONEL” (registered trademark) and “HASTELLOY” (registered trademark), various alloys based on nickel, titanium and cobalt are selected.
  • Methods of manufacturing metal fibers include so-called bundle drawing in which a large number of wires are collected as a bundle and the diameter is reduced by drawing, then individual wires are separated to reduce the diameter, coiled sheet shaving, chatter vibration shaving and the like.
  • the filter medium is wire gauze, because the metal fibers are necessary to be of not fiber bundles but single fibers, it is manufactured by a method including repeating wire drawing and heat treatment or the like.
  • the particle retention is a particle diameter (diameter) of spherical particles, 95% or more of which are collected when the particles pass through the filter medium.
  • the particle retention can be measured according to a method of JIS standard (JIS-B8356-8: 2002). The fact that the particle retention is low and the fact that the particle retention is excellent are synonymous.
  • the spinning dope solution is filtered under conditions where a relationship of the filtration speed A (cm/hour), a particle retention B ( ⁇ m), a filter medium basis weight D (g/m 2 ) satisfies equations (1) to (3), then the filtered spinning dope solution is spun to obtain a precursor fiber bundle for carbon fiber:
  • the filter basis weight D (g/m 2 ) is a total basis weight of a filter medium main body excluding a mesh layer that may be laminated for the purpose of protecting the filter medium main body.
  • the filter basis weight D can be calculated by measuring the mass of the filter medium cut out into an arbitrary area and dividing this mass by the area.
  • minimum filter basis weight As the filter basis weight D is larger, the trapping rate of foreign substances is higher. Conversely, as the filter basis weight D is smaller, foreign substances cannot be easily trapped but tend to slip through. Therefore, when the effect of the filter basis weight D on improvement of the quality of the precursor fiber bundle for carbon fiber and suppression of clogging of the filter was measured while changing the filtration speed A and particle retention B, we confirmed that there was a minimum filter basis weight that could achieve both improvement of the quality of the precursor fiber bundle for carbon fiber and suppression of clogging of the filter at an arbitrary filtration speed and particle retention (hereinafter “minimum filter basis weight”).
  • the minimum filter basis weight can be expressed using ⁇ , a product of mutually independent parameters ⁇ and ⁇ , as shown in the second term on the left side of equation (1).
  • ⁇ is defined as a function of the filtration speed A shown in equation (2)
  • ⁇ is defined as a function of the particle retention B shown in equation (3).
  • a filter medium with the particle retention B ( ⁇ m) satisfying equation (4) is preferably used:
  • a method of manufacturing a precursor fiber bundle for carbon fiber suitable for obtaining a carbon fiber bundle will be described.
  • a method of manufacturing a precursor fiber bundle for carbon fiber includes a spinning process that extrudes a spinning dope solution from a spinneret into a coagulation bath by a dry-jet wet spinning method and spinning fibers, a water washing process that cleans the fibers obtained in the spinning process in a water bath, a water bath stretching process that stretches the fibers obtained in the water washing process in a water bath, and a dry-heat treatment process that dries and heat treats the fibers obtained in the water bath stretching process, and may include a steam stretching process of steam stretching the fibers obtained in the dry-heat treatment process may be included, as necessary.
  • the coagulation bath preferably contains a coagulant and a solvent used as a solvent for the spinning dope solution.
  • a coagulant a component that does not dissolve a polyacrylonitrile copolymer and is compatible with the solvent used in the spinning dope solution can be used.
  • water it is preferable to use water as the coagulant.
  • the water bath temperature in the water washing process is preferably 30 to 98° C., and is preferably washed using a water washing bath having a plurality of stages.
  • the stretch ratio in the water bath stretching process is preferably 2 to 6 times.
  • an oil agent made of silicone or the like to the fiber bundle for the purpose of preventing adhesion between single fibers.
  • a silicone oil agent it is preferable to use a modified silicone, and it is preferable to use one containing an amino-modified silicone having high heat resistance.
  • a known method for the dry-heat treatment process can be used for the dry-heat treatment process.
  • the drying temperature is 100 to 200° C.
  • a precursor fiber bundle for carbon fiber more suitably used for the manufacture of a carbon fiber bundle is obtained by further performing the steam stretching process, after the water washing process, water bath stretching process, oil agent application process, and dry-heat treatment process described above.
  • the steam stretching process it is preferable to stretch 2 to 6 times in pressurized steam.
  • the mean fineness of single fibers contained in the precursor fiber bundle for carbon fiber thus obtained is preferably 0.7 to 1.5 dtex, and more preferably 0.9 to 1.2 dtex.
  • the single-fiber fineness By setting the single-fiber fineness to 0.7 dtex or more, the occurrence of fiber bundle fracture due to the accumulation of single fiber fracture due to contact with rollers and guide parts is suppressed, and the process stability of each of the spinning process, oxidation process, precarbonization process and carbonization process can be maintained.
  • the single-fiber fineness to 1.5 dtex or less the skin layer ratio in each single fiber after the oxidation process is reduced, the process stability in the subsequent carbonization process and the tensile strength of strands and elastic modulus of strands of the resulting carbon fiber bundle can be improved.
  • the resulting precursor fiber bundle for carbon fiber is usually continuous fibers. Also, the number of filaments per one fiber bundle is preferably 10,000 to 60,000.
  • the method of manufacturing a carbon fiber bundle is such that the precursor fiber bundle for carbon fiber is heat-treated in an oxidizing atmosphere until the density reaches 1.32 to 1.35 g/cm 3 , and then heat-treated at 275° C. or more and 295° C. or less in an oxidizing atmosphere until the density reaches 1.46 to 1.50 g/cm 3 . That is, the precursor fiber bundle for carbon fiber is heat-treated until reaching a predetermined density in the former half of the oxidation process, and then heat-treated at a high temperature of 275° C. or more and 295° C. or less in the latter half of the oxidation process.
  • the oxidizing atmosphere is an atmosphere containing 10% by mass or more of a known oxidizing substance such as oxygen and nitrogen dioxide, and an air atmosphere is preferable from the viewpoint of simplicity.
  • the density of the oxidized fiber bundle is generally used as an index indicating the progress of the oxidation reaction.
  • the density is 1.32 g/cm 3 or more
  • the oxidized fiber bundle has a high heat resistant structure so that it is difficult to be decomposed when heat-treated at a high temperature, and the tensile strength of strands of the resulting carbon fiber bundle is improved.
  • the density is 1.35 g/cm 3 or less, a long heat treatment time at a high temperature can be secured in the subsequent process so that the tensile strength of strands of the carbon fiber bundle can be improved.
  • the density of the oxidized fiber bundle can be adjusted by raising the temperature or prolonging the oxidation time in the former half of the oxidation process.
  • the precursor fiber bundle for carbon fiber is heat-treated in an oxidizing atmosphere, at preferably 210° C. or more and less than 245° C., more preferably 220° C. or more and less than 245° C., and further preferably 225° C. or more and less than 240° C., thereby obtaining an oxidized fiber bundle with a density of preferably 1.22 to 1.24 g/cm 3 , and more preferably a density of 1.23 to 1.24 g/cm 3 .
  • the density of the oxidized fiber bundle is 1.22 g/cm 3 or more
  • the chemical structure of the single fiber in the oxidation process is stabilized by heat treatment, and the difference between skin-core structure of the single fiber does not deteriorate even when the subsequent heat treatment is performed at a high temperature so that the tensile strength of strands is often improved.
  • the density is 1.24 g/cm 3 or less
  • the total amount and time of heat treatment including the subsequent heat treatment is reduced, which is often superior in terms of tensile strength of strands and productivity.
  • a temperature of 210° C. or more is preferable because the difference between skin-core structure can be sufficiently suppressed.
  • At a temperature of less than 245° C. is preferable because it is an oxidation initial temperature sufficiently low to suppress the difference between skin-core structure regarding the single fiber diameter of the precursor fiber bundle for carbon fiber, the tensile strength of strands is often increased.
  • the oxidized fiber bundle is heat-treated until the density reaches 1.22 to 1.24 g/cm 3 and then heat-treated in an oxidizing atmosphere to obtain an oxidized fiber bundle with a density of 1.32 to 1.35 g/cm 3 , and more preferably 1.33 to 1.34 g/cm 3 .
  • This heat treatment process is performed in an oxidizing atmosphere at preferably 245° C. or more and less than 275° C., and more preferably 250° C. or more and less than 270° C.
  • the density is 1.32 g/cm 3 or more
  • the chemical structure of the single fiber in the oxidation process is further stabilized by heat treatment, and the difference between skin-core structure does not deteriorate even when the subsequent heat treatment is performed at a higher temperature so that the tensile strength of strands is often improved.
  • the density is 1.35 g/cm 3 or less
  • the total amount and time of heat treatment including the subsequent heat treatment are reduced, and the tensile strength of strands and productivity are superior.
  • the heat treatment temperature is 245° C. or more, the total amount and time of heat treatment are reduced, and the tensile strength of strands and productivity are often superior.
  • the heat treatment temperature is less than 275° C., even when heat-treating an oxidized fiber bundle with a density of 1.22 to 1.24 g/cm 3 , the difference between skin-core structure can be suppressed, and high tensile strength of strands is often exhibited.
  • the obtained oxidized fiber bundle is heat-treated in an oxidizing atmosphere at a temperature of 275° C. or more to 295° C. or less, and preferably 280° C. or more to 290° C. or less to obtain an oxidized fiber bundle with a density of 1.46 to 1.50 g/cm 3 .
  • the heat treatment temperature is 275° C. or more, the amount of heat applied when increasing the density can be reduced, whereby the tensile strength of strands is improved.
  • the heat treatment temperature is 295° C. or less, it is possible to proceed the oxidation reaction without decomposing the structure of the single fiber, and maintain the tensile strength of strands.
  • thermometer such as a thermocouple
  • the simple average temperature is calculated.
  • the final density of the oxidized fiber bundle is 1.46 to 1.50 g/cm 3 , preferably 1.46 to 1.49 g/cm 3 , and further preferably 1.47 to 1.49 g/cm 3 . Since the density of the oxidized fiber bundle correlates with the carbonization yield, the higher density is better, from the viewpoint of reducing manufacturing energy. When the density is 1.46 g/cm 3 or more, the carbonization yield can be sufficiently increased. When the density is 1.50 g/cm 3 or less, the effect of increasing the carbonization yield is not saturated, which is effective from the viewpoint of productivity. To complete the heat treatment at the specified density, it is only necessary to adjust the oxidation temperature and time.
  • the tension applied to the oxidized fiber bundle is preferably 1.6 to 4.0 mN/dtex, more preferably 2.5 to 4.0 mN/dtex, and further preferably 3.0 to 4.0 mN/dtex.
  • the oxidation tension is represented by a value obtained by dividing the tension (mN) measured on an exit side of the oxidation oven by the fineness (dtex) of the precursor fiber bundle for carbon fiber in complete dryness.
  • the tension When the tension is 1.6 mN/dtex or more, the orientation of the carbon fiber bundle is sufficiently increased, and the tensile strength of strands is often improved. When the tension is 4.0 mN/dtex or less, quality deterioration due to fuzz tends to be small.
  • the density of the oxidized fiber bundle is increased to obtain a high carbonization yield
  • the tensile strength of strands of the carbon fiber bundle tends to decrease.
  • the difference between skin-core structure of the single fiber is greatly suppressed, and the structure is stabilized so that both high carbonization yield and high tensile strength of strands can be achieved.
  • a known method of manufacturing a carbon fiber bundle may be basically followed.
  • the pre-carbonization process it is preferable to obtain a carbonized fiber bundle by heat-treating the oxidized fiber obtained in the oxidation process in an inert atmosphere at a maximum temperature of 500 to 1000° C. until the density reaches 1.5 to 1.8 g/cm 3 .
  • a carbonization process is performed, following pre-carbonization.
  • the carbonization process it is preferable to obtain a carbon fiber bundle by heat-treating the pre-carbonized fiber bundle in an inert atmosphere at a maximum temperature of 1200 to 1800° C., and preferably 1200 to 1600° C.
  • the maximum temperature is 1200° C. or more, the nitrogen content in the carbon fiber bundle is reduced, and the tensile strength of strands is stably exhibited.
  • the maximum temperature is 1800° C. or less, a satisfactory carbonization yield can be obtained.
  • the carbon fiber bundle obtained as described above is preferably subjected to an oxidation treatment so that an oxygen containing functional group is introduced to improve adhesion to a matrix resin.
  • an oxidation treatment method gas phase oxidation, liquid phase oxidation, liquid phase electrolytic oxidation and the like are used. From the viewpoint that high productivity and uniform treatment can be achieved, liquid phase electrolytic oxidation is preferably used.
  • the method of liquid phase electrolytic oxidation is not particularly specified, and may be performed by a known method.
  • a sizing treatment can also be performed to impart convergency to the obtained carbon fiber bundle.
  • a sizing agent having good compatibility with the matrix resin can be appropriately selected according to the type of the matrix resin used for a composite material.
  • the tensile strength of strands and elastic modulus of strands of the carbon fiber bundle are determined in accordance with a resin-impregnated strand test method of JIS-R-7608 (2004), according to the following procedure. Ten resin-impregnated strands of the carbon fiber bundle are measured, and the average value thereof is defined as the tensile strength of strands. Strain is evaluated using an extensometer. The strain was evaluated at a strain range of 0.1 to 0.6%.
  • 1.0 to 3.0 g of the oxidized fiber bundle is collected and completely dried at 120° C. for 2 hours.
  • ⁇ is a specific gravity of ethanol at the measurement temperature.
  • a carbon fiber bundle to be measured is embedded in a resin, a cross section perpendicular to the fiber axis direction is polished, and the cross section is observed using a 100 times objective lens of an optical microscope at a total magnification of 1000.
  • the blackened thickness of the outer peripheral portion is measured from the cross-sectional microscopic image of the polished surface. Analysis is performed using image analysis software Image J.
  • black and white area division is performed by binarization. For the luminance distribution in the single fiber cross section, the average value of the distribution is set as a threshold value, and binarization is performed. In the obtained binarized image, the shortest distance from a point on the surface layer to a lined region from black to white is measured in the fiber diameter direction.
  • the skin layer ratio is calculated from the area ratio (%) of the blackened thickness portion with respect to the entire cross section perpendicular to the fiber axis direction of the single fiber of the carbon fiber. The same evaluation is performed on 30 single fibers in the carbon fiber bundle, and the average value thereof is used.
  • a mass A f (g/m) and a density B f (g/cm 3 ) per unit length are determined for a carbon fiber bundle composed of a large number of carbon filaments to be measured.
  • the number of filaments of the carbon fiber bundle to be measured is defined as C f
  • the average single fiber diameter ( ⁇ m) of the carbon fibers is calculated by the equation below:
  • a grip part having a length of 25 mm is attached to both ends of a carbon fiber bundle with a length of 150 mm to prepare a test specimen.
  • a load of 9.0 ⁇ 10 ⁇ 5 N/dtex is applied to the carbon fiber bundle for alignment.
  • One knot is made at the midpoint of the test specimen, and the test specimen is subjected to a fiber bundle tensile test at a crosshead speed at tension of 100 mm/min.
  • a total of 12 fiber bundles are subjected to the measurement.
  • the average value of 10 fiber bundles excluding the maximum value and the minimum value is used as the measured value.
  • the knot strength a value obtained by dividing the maximum load value obtained in the fiber bundle tensile test by the average cross-sectional area value of the carbon fiber bundles is used.
  • a single fiber tensile test of the single fibers of the carbon fibers is performed in accordance with JIS R7606 (2000), and a sample of the single fibers of the carbon fibers after fracture including a fracture surface (hereinafter “fracture surface”) is collected.
  • the number of single fibers to be tested is one set of 50 fibers, and when it is not possible to collect 30 or more pairs of fracture surfaces on both sides, another set of 50 fibers is subjected to a single fiber tensile test to collect 30 or more pairs of fracture surfaces on both sides.
  • the strain rate during the tensile test is set to 0.4 mm/min.
  • traces of the fracture radially progressing from the fracture origin (i) remained as radial streaks on the original fracture surface caused by tensile fracture of the carbon fiber, a portion on which the streaks present on an SEM observation image converged to one point when traced is identified as a fracture origin (i).
  • the streaks cannot be recognized or when the streaks can be recognized, but stain is adhered near the fracture origin (i) so that the streaks are hardly observed on at least one side of the fracture surfaces on both sides, the pair of such fracture surfaces is excluded from evaluation.
  • the fracture surface reduced by the exclusion is replenished as appropriate so that 30 pairs of fracture surfaces will eventually be observed.
  • the fracture origin (i) is examined whether there are any morphological features.
  • morphological features such as dents, attached substances, traces of the fiber surface being partially peeled, damages and adhesion marks.
  • the morphological features to be fracture origins that can be observed by SEM are collectively referred to as “flaws.” Lengths measured along the circumferential direction of the fiber, that is, those with a size of 50 nm or more, are uniformly classified as a “fracture surface in which a flaw with a size of 50 nm or more exists” regardless of differences in appearance.
  • the single fiber tensile test was performed by TENSILON “RTC-1210A” manufactured by A&D Company, Limited, with a gauge length of 10 mm, using a commercially available cyanoacrylate instant adhesive to fix the carbon fiber to a test piece mount, and use a special test jig designed to perform in water. Further, a scanning electron microscope (SEM) “5-4800” manufactured by Hitachi High-Technologies Corporation was used to observe the collected fracture surfaces.
  • SEM scanning electron microscope
  • Measurement mode tapping mode Scanning speed: 1.0 Hz Scanning range: 600 nm ⁇ 600 nm Resolution: 512 pixels ⁇ 512 pixels Measurement environment: room temperature, in air.
  • a three-dimensional surface shape image is measured under the above conditions, and the obtained measurement image is subjected to image processing using, “flat treatment” for removing undulation of data derived from the device using the attached software (NanoScope Analysis), taking a curvature of a fiber cross section into account, “median 8 treatment” which is a filter treatment that replaces a central value of a matrix from a median value of Z data in the 3 ⁇ 3 matrix, and “three-dimensional tilt correction” for carrying out fitting of a cubic curved surface by a least square method from all image data and correcting in-plane tilt, then surface roughness analysis is performed with the attached software to calculate mean surface roughness.
  • the mean surface roughness (Ra) is a three-dimensional extension of a centerline roughness Ra defined in JIS B0601 (2001) so that it can be applied to surface measurement and is defined as a mean value of absolute values of deviations from a reference surface to a designated surface.
  • Ra centerline roughness
  • the quality of the carbon fiber bundle affecting productivity during manufacture of the composite material is evaluated by a method of directly counting the number of fuzzes by the following method.
  • a method of directly counting the number of fuzzes by the following method.
  • the number of fractures single fibers protruding 5 mm or more from the surface of the carbon fiber bundle is counted at a length of the carbon fiber bundle of 20 m to evaluate the number of fuzzes per 1 m (fuzzes/m).
  • a copolymer composed of 99% by mass of acrylonitrile and 1% by mass of itaconic acid was polymerized by solution polymerization using dimethyl sulfoxide as a solvent to produce a polyacrylonitrile copolymer to obtain a spinning dope solution.
  • the spinning dope solution was allowed to flow into a filter device and filtered.
  • the filter medium used was a sintered metal filter having a particle retention B of 1 ⁇ m, a filter medium thickness C of 800 ⁇ m, and a filter basis weight D of 2500 g/m 2 , and filtration was performed under a filtration condition with a filtration speed A of 3 cm/hour.
  • Fibers were spun by a dry-jet wet spinning method in which the filtered spinning dope solution was once extruded through a spinneret into the air and introduced into a coagulation bath composed of an aqueous solution of 35% dimethyl sulfoxide controlled at 3° C.
  • the spun fiber bundle was washed with water at 30 to 98° C., and 3.5 times water bath stretching was performed at that time.
  • an amino-modified silicone-based silicone oil agent was applied to the fiber bundle after the water bath stretching in the water bath and dried using a roller heated to a temperature of 160° C. to obtain a fiber bundle with a number of single fibers of 12,000.
  • the fiber bundle was stretched 3.7 times in pressurized steam to make the total stretch ratio of the yarn 13 times. Then, the fiber bundle was subjected to entangling treatment by air having a fluid extrusion pressure of 0.35 MPa with a tension of 2 mN/dtex being applied to the fiber bundle to obtain a precursor fiber bundle for carbon fiber with a single-fiber fineness of 1.1 dtex and a number of single fibers of 12,000. Next, using the oxidizing conditions described in Condition 1 in Table 1, the precursor fiber bundle for carbon fiber was heat-treated in an oven in an air atmosphere at a stretch ratio of 1.0 to obtain an oxidized fiber bundle.
  • the obtained oxidized fiber bundle was subjected to a pre-carbonization treatment at a stretch ratio of 0.95 in a nitrogen atmosphere at a temperature of 300 to 800° C. to obtain a pre-carbonized fiber bundle.
  • the obtained pre-carbonized fiber bundle was subjected to a carbonization treatment at a maximum temperature of 1350° C. in a nitrogen atmosphere.
  • the obtained carbon fiber bundle was subjected to surface treatment and sizing agent coating treatment to obtain a final carbon fiber bundle.
  • the number of fuzzes of the carbon fiber bundle at this time was less than 0.1/m, and almost no fuzz was confirmed and the quality was good.
  • Table 2 shows the tensile strength of strands, elastic modulus of strands, skin layer ratio of the single fibers of the carbon fibers, and average single fiber diameter of the obtained carbon fiber bundle.
  • a precursor fiber bundle for carbon fiber and a carbon fiber bundle were obtained in the same manner as in Example 1, except that the filter medium was changed to a sintered metal filter having a particle retention B of 9 ⁇ m, a filter medium thickness C of 3200 ⁇ m, and a filter basis weight D of 6400 g/m 2 .
  • a precursor fiber bundle for carbon fiber and a carbon fiber bundle were obtained in the same manner as in Example 1 except that the filtration speed A was changed to 6 cm/hour under the filtration conditions.
  • a precursor fiber for carbon fiber and a carbon fiber bundle were obtained in the same manner as in Example 3, except that the stretch ratio during pre-carbonization was 1.05 times in Example 4 and 1.10 times in Example 5.
  • a precursor fiber bundle for carbon fiber and a carbon fiber bundle were obtained in the same manner as in Example 2, except that the filter medium was changed to a sintered metal filter having a filter medium thickness C of 1600 ⁇ m and a filter basis weight D of 3200 g/m 2 .
  • the number of fuzzes of the carbon fiber bundle was 0.2/m, and the quality deteriorated.
  • a precursor fiber bundle for carbon fiber and a carbon fiber bundle were obtained in the same manner as in Comparative Example 1 except that the filtration speed A was changed to 6 cm/hour under the filtration conditions.
  • a precursor fiber bundle for carbon fiber and a carbon fiber bundle were obtained in the same manner as in Example 2 except that the filtration speed A was changed to 6 cm/hour under the filtration conditions.
  • a precursor fiber bundle for carbon fiber and a carbon fiber bundle were obtained in the same manner as in Example 3 except that the filtration speed A was changed to 8 cm/hour under the filtration conditions.
  • a precursor fiber bundle for carbon fiber and a carbon fiber bundle were obtained in the same manner as in Example 3 except that the filtration speed A was changed to 12 cm/hour under the filtration conditions.
  • a carbon fiber bundle was obtained in the same manner as in Example 1 except that Condition 2 in Table 1 was used as the oxidizing condition.
  • the skin layer ratio of the carbon fibers was 97%, and the tensile strength of strands decreased as compared to that in Example 1.
  • a carbon fiber bundle was obtained in the same manner as in Example 1 except that Condition 3 in Table 1 was used as the oxidizing condition.
  • the skin layer ratio of the carbon fibers was 85%, and the tensile strength of strands decreased as compared to that in Example 1.
  • the carbon fiber bundle to be obtained is suitably used for general industrial uses such as aircraft, automobile and ship members, sports uses such as golf shafts and fishing rods, and pressure vessels, taking advantage of such characteristics.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Mechanical Engineering (AREA)
  • Health & Medical Sciences (AREA)
  • Toxicology (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Inorganic Fibers (AREA)
  • Artificial Filaments (AREA)
US16/623,479 2017-07-10 2018-06-28 Carbon fiber bundle and method of manufacturing same Abandoned US20200190705A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2017134359 2017-07-10
JP2017-134359 2017-07-10
PCT/JP2018/024513 WO2019012999A1 (fr) 2017-07-10 2018-06-28 Faisceau de fibres de carbone et leur procédé de fabrication

Publications (1)

Publication Number Publication Date
US20200190705A1 true US20200190705A1 (en) 2020-06-18

Family

ID=65002559

Family Applications (1)

Application Number Title Priority Date Filing Date
US16/623,479 Abandoned US20200190705A1 (en) 2017-07-10 2018-06-28 Carbon fiber bundle and method of manufacturing same

Country Status (7)

Country Link
US (1) US20200190705A1 (fr)
EP (1) EP3653768B1 (fr)
JP (1) JP6460284B1 (fr)
KR (1) KR102603178B1 (fr)
CN (1) CN110832127B (fr)
TW (1) TW201908553A (fr)
WO (1) WO2019012999A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114457449A (zh) * 2020-11-10 2022-05-10 中国石油化工股份有限公司 高性能聚丙烯腈前驱体纤维及其制备方法和应用

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20210139092A (ko) 2020-05-13 2021-11-22 현대모비스 주식회사 차량용 시트 에어백장치
CN113402278B (zh) * 2021-06-10 2024-09-13 福建立亚新材有限公司 一种用于高温试验的陶瓷纤维制备方法

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS58163729A (ja) 1982-03-16 1983-09-28 Toray Ind Inc アクリル系繊維束の多段耐炎化方法
JPS58163729U (ja) 1982-04-27 1983-10-31 株式会社小松製作所 ピストンモ−タの軸ブレ−キ装置
JPH086210B2 (ja) 1988-05-30 1996-01-24 東レ株式会社 高強度高弾性率炭素繊維およびその製造方法
JPH06294020A (ja) 1993-04-05 1994-10-21 Asahi Chem Ind Co Ltd 炭素繊維を製造する方法
JP2004027396A (ja) * 2002-06-24 2004-01-29 Toray Ind Inc 炭素繊維用アクリル系前駆体の製造方法
JP4924484B2 (ja) * 2008-03-05 2012-04-25 東レ株式会社 炭素繊維前駆体繊維の製造方法
JP5141598B2 (ja) * 2008-03-05 2013-02-13 東レ株式会社 炭素繊維前駆体繊維の製造方法
JP4957632B2 (ja) * 2008-04-11 2012-06-20 東レ株式会社 炭素繊維前駆体繊維の製造方法
JP5691366B2 (ja) 2010-10-08 2015-04-01 東レ株式会社 炭素繊維の製造方法
JP2013023778A (ja) 2011-07-19 2013-02-04 Mitsubishi Rayon Co Ltd 炭素繊維束の製造方法
KR20130023778A (ko) 2011-08-30 2013-03-08 강원대학교산학협력단 녹차로부터 분리된 클로로필류를 포함하는 항암 조성물
HUE044063T2 (hu) 2012-04-18 2019-09-30 Mitsubishi Chem Corp Szénszál-matring
JP6119168B2 (ja) 2012-10-03 2017-04-26 三菱ケミカル株式会社 耐炎化繊維束の製造方法、及び、炭素繊維束の製造方法
US9500429B2 (en) 2012-12-07 2016-11-22 The Otis Patent Trust Unified bolt and bolt carrier cleaning tool
KR20210054070A (ko) 2012-12-19 2021-05-12 다우 글로벌 테크놀로지스 엘엘씨 무정형 실리카 충전제를 갖는 엘라스토머-기재 중합체 조성물
JP6232897B2 (ja) * 2013-10-04 2017-11-22 三菱ケミカル株式会社 炭素繊維前駆体アクリロニトリル系繊維の製造方法
JP6889106B2 (ja) 2014-10-07 2021-06-18 コーニング インコーポレイテッド 決定された応力プロファイルを有するガラス物品、およびその製造方法
JP5963063B2 (ja) 2014-12-15 2016-08-03 三菱レイヨン株式会社 炭素繊維束
JP6888260B2 (ja) * 2015-09-29 2021-06-16 東レ株式会社 炭素繊維束およびその製造方法
JP6338023B2 (ja) * 2016-06-30 2018-06-06 東レ株式会社 炭素繊維束およびその製造方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114457449A (zh) * 2020-11-10 2022-05-10 中国石油化工股份有限公司 高性能聚丙烯腈前驱体纤维及其制备方法和应用

Also Published As

Publication number Publication date
KR102603178B1 (ko) 2023-11-16
CN110832127A (zh) 2020-02-21
JPWO2019012999A1 (ja) 2019-07-11
JP6460284B1 (ja) 2019-01-30
EP3653768B1 (fr) 2024-11-06
EP3653768A4 (fr) 2021-03-31
WO2019012999A1 (fr) 2019-01-17
EP3653768A1 (fr) 2020-05-20
CN110832127B (zh) 2022-06-14
KR20200028334A (ko) 2020-03-16
TW201908553A (zh) 2019-03-01

Similar Documents

Publication Publication Date Title
EP2208813B1 (fr) Brin de fibre de carbone et son procédé de fabrication
EP3480346B1 (fr) Faisceau de fibres de carbone
EP3653768B1 (fr) Faisceau de fibres de carbone et leur procédé de fabrication
JP6888260B2 (ja) 炭素繊維束およびその製造方法
JP5708896B1 (ja) 炭素繊維束および耐炎化繊維束
CN110300819B (zh) 碳纤维前体丙烯腈系纤维、碳纤维及它们的制造方法
JP7322327B2 (ja) 炭素繊維束およびその製造方法
JP2018141251A (ja) 炭素繊維束およびその製造方法
JP2016128623A (ja) 機械的特性発現に優れた炭素繊維
EP4379100A1 (fr) Faisceau de fibres de carbone et procédé de production pour celui-ci
JP2019023378A (ja) 炭素繊維用アクリロニトリル前駆体繊維束及びその製造方法
JP6881090B2 (ja) 炭素繊維束
WO2023140212A1 (fr) Faisceau de fibres de carbone
JP5842343B2 (ja) 炭素繊維前駆体アクリル繊維束の製造方法
JP2015161056A (ja) 炭素繊維用アクリロニトリル前駆体繊維束及びその製造方法
JP2023037536A (ja) サイジング剤付着繊維束及びその製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: TORAY INDUSTRIES, INC., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MATSUMOTO, NAOHIRO;OKUDA, HARUKI;TANAKA, FUMIHIKO;SIGNING DATES FROM 20191126 TO 20191203;REEL/FRAME:051303/0137

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION