US20060142148A1 - Methods for preparing catalysts supported on carbon nanotube networks - Google Patents
Methods for preparing catalysts supported on carbon nanotube networks Download PDFInfo
- Publication number
- US20060142148A1 US20060142148A1 US11/281,811 US28181105A US2006142148A1 US 20060142148 A1 US20060142148 A1 US 20060142148A1 US 28181105 A US28181105 A US 28181105A US 2006142148 A1 US2006142148 A1 US 2006142148A1
- Authority
- US
- United States
- Prior art keywords
- metal
- carbon nanotubes
- carbon nanotube
- catalyst
- nanotubes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 title claims abstract description 208
- 239000002041 carbon nanotube Substances 0.000 title claims abstract description 174
- 229910021393 carbon nanotube Inorganic materials 0.000 title claims abstract description 174
- 239000003054 catalyst Substances 0.000 title claims abstract description 168
- 238000000034 method Methods 0.000 title claims abstract description 33
- 229910052751 metal Inorganic materials 0.000 claims abstract description 124
- 239000002184 metal Substances 0.000 claims abstract description 124
- KDLHZDBZIXYQEI-UHFFFAOYSA-N Palladium Chemical compound [Pd] KDLHZDBZIXYQEI-UHFFFAOYSA-N 0.000 claims description 24
- 238000011068 loading method Methods 0.000 claims description 21
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 claims description 20
- GRYLNZFGIOXLOG-UHFFFAOYSA-N Nitric acid Chemical compound O[N+]([O-])=O GRYLNZFGIOXLOG-UHFFFAOYSA-N 0.000 claims description 18
- 229910017604 nitric acid Inorganic materials 0.000 claims description 18
- BASFCYQUMIYNBI-UHFFFAOYSA-N platinum Chemical compound [Pt] BASFCYQUMIYNBI-UHFFFAOYSA-N 0.000 claims description 16
- 239000003795 chemical substances by application Substances 0.000 claims description 13
- 150000003839 salts Chemical class 0.000 claims description 13
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims description 11
- 239000007800 oxidant agent Substances 0.000 claims description 11
- 239000000126 substance Substances 0.000 claims description 10
- CURLTUGMZLYLDI-UHFFFAOYSA-N Carbon dioxide Chemical compound O=C=O CURLTUGMZLYLDI-UHFFFAOYSA-N 0.000 claims description 9
- 238000005470 impregnation Methods 0.000 claims description 9
- 238000005342 ion exchange Methods 0.000 claims description 9
- 229910052742 iron Inorganic materials 0.000 claims description 9
- MHAJPDPJQMAIIY-UHFFFAOYSA-N Hydrogen peroxide Chemical compound OO MHAJPDPJQMAIIY-UHFFFAOYSA-N 0.000 claims description 8
- KJTLSVCANCCWHF-UHFFFAOYSA-N Ruthenium Chemical compound [Ru] KJTLSVCANCCWHF-UHFFFAOYSA-N 0.000 claims description 8
- 229910044991 metal oxide Inorganic materials 0.000 claims description 8
- 150000004706 metal oxides Chemical class 0.000 claims description 8
- VKJKEPKFPUWCAS-UHFFFAOYSA-M potassium chlorate Chemical compound [K+].[O-]Cl(=O)=O VKJKEPKFPUWCAS-UHFFFAOYSA-M 0.000 claims description 8
- OSVXSBDYLRYLIG-UHFFFAOYSA-N chlorine dioxide Inorganic materials O=Cl=O OSVXSBDYLRYLIG-UHFFFAOYSA-N 0.000 claims description 7
- QBWCMBCROVPCKQ-UHFFFAOYSA-N chlorous acid Chemical compound OCl=O QBWCMBCROVPCKQ-UHFFFAOYSA-N 0.000 claims description 7
- 229910052804 chromium Inorganic materials 0.000 claims description 7
- 229910052802 copper Inorganic materials 0.000 claims description 7
- GKOZUEZYRPOHIO-UHFFFAOYSA-N iridium atom Chemical compound [Ir] GKOZUEZYRPOHIO-UHFFFAOYSA-N 0.000 claims description 7
- 229910052748 manganese Inorganic materials 0.000 claims description 7
- 150000001247 metal acetylides Chemical class 0.000 claims description 7
- 229910001507 metal halide Inorganic materials 0.000 claims description 7
- 150000005309 metal halides Chemical class 0.000 claims description 7
- 229910052976 metal sulfide Inorganic materials 0.000 claims description 7
- 229910052759 nickel Inorganic materials 0.000 claims description 7
- 229910052758 niobium Inorganic materials 0.000 claims description 7
- 150000004767 nitrides Chemical class 0.000 claims description 7
- SYQBFIAQOQZEGI-UHFFFAOYSA-N osmium atom Chemical compound [Os] SYQBFIAQOQZEGI-UHFFFAOYSA-N 0.000 claims description 7
- 239000010948 rhodium Substances 0.000 claims description 7
- MHOVAHRLVXNVSD-UHFFFAOYSA-N rhodium atom Chemical compound [Rh] MHOVAHRLVXNVSD-UHFFFAOYSA-N 0.000 claims description 7
- 238000001179 sorption measurement Methods 0.000 claims description 7
- 229910052719 titanium Inorganic materials 0.000 claims description 7
- 229910052720 vanadium Inorganic materials 0.000 claims description 7
- 229910052727 yttrium Inorganic materials 0.000 claims description 7
- 229910052725 zinc Inorganic materials 0.000 claims description 7
- 229910052726 zirconium Inorganic materials 0.000 claims description 7
- 238000002156 mixing Methods 0.000 claims description 6
- 229910052763 palladium Inorganic materials 0.000 claims description 5
- JRKICGRDRMAZLK-UHFFFAOYSA-L peroxydisulfate Chemical compound [O-]S(=O)(=O)OOS([O-])(=O)=O JRKICGRDRMAZLK-UHFFFAOYSA-L 0.000 claims description 5
- 229910052697 platinum Inorganic materials 0.000 claims description 5
- 238000001556 precipitation Methods 0.000 claims description 5
- 229910052707 ruthenium Inorganic materials 0.000 claims description 5
- 238000000975 co-precipitation Methods 0.000 claims description 4
- 238000001704 evaporation Methods 0.000 claims description 4
- 229910052741 iridium Inorganic materials 0.000 claims description 4
- 229910052762 osmium Inorganic materials 0.000 claims description 4
- 229910052703 rhodium Inorganic materials 0.000 claims description 4
- 229910000457 iridium oxide Inorganic materials 0.000 claims 3
- 229910000487 osmium oxide Inorganic materials 0.000 claims 3
- 229910003445 palladium oxide Inorganic materials 0.000 claims 3
- 229910003446 platinum oxide Inorganic materials 0.000 claims 3
- 229910003450 rhodium oxide Inorganic materials 0.000 claims 3
- 229910001925 ruthenium oxide Inorganic materials 0.000 claims 3
- 125000004427 diamine group Chemical group 0.000 claims 1
- 239000002071 nanotube Substances 0.000 description 62
- 239000011148 porous material Substances 0.000 description 26
- 238000006243 chemical reaction Methods 0.000 description 21
- OKKJLVBELUTLKV-UHFFFAOYSA-N Methanol Chemical compound OC OKKJLVBELUTLKV-UHFFFAOYSA-N 0.000 description 18
- 125000000524 functional group Chemical group 0.000 description 16
- 239000000463 material Substances 0.000 description 14
- 239000000203 mixture Substances 0.000 description 13
- 229910052799 carbon Inorganic materials 0.000 description 12
- 238000009826 distribution Methods 0.000 description 12
- 239000000047 product Substances 0.000 description 11
- 239000000376 reactant Substances 0.000 description 11
- LQNUZADURLCDLV-UHFFFAOYSA-N nitrobenzene Chemical compound [O-][N+](=O)C1=CC=CC=C1 LQNUZADURLCDLV-UHFFFAOYSA-N 0.000 description 10
- 238000007306 functionalization reaction Methods 0.000 description 9
- 230000000704 physical effect Effects 0.000 description 9
- -1 polyethylene Polymers 0.000 description 9
- UIIMBOGNXHQVGW-UHFFFAOYSA-M Sodium bicarbonate Chemical compound [Na+].OC([O-])=O UIIMBOGNXHQVGW-UHFFFAOYSA-M 0.000 description 8
- 230000015572 biosynthetic process Effects 0.000 description 8
- 230000003197 catalytic effect Effects 0.000 description 8
- 230000008569 process Effects 0.000 description 8
- 238000004026 adhesive bonding Methods 0.000 description 7
- 239000003153 chemical reaction reagent Substances 0.000 description 7
- 239000002245 particle Substances 0.000 description 7
- 239000002002 slurry Substances 0.000 description 7
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 7
- XEKOWRVHYACXOJ-UHFFFAOYSA-N Ethyl acetate Chemical compound CCOC(C)=O XEKOWRVHYACXOJ-UHFFFAOYSA-N 0.000 description 6
- 238000000151 deposition Methods 0.000 description 6
- 150000004985 diamines Chemical class 0.000 description 6
- 230000003647 oxidation Effects 0.000 description 6
- 238000007254 oxidation reaction Methods 0.000 description 6
- 239000002243 precursor Substances 0.000 description 6
- KFZMGEQAYNKOFK-UHFFFAOYSA-N Isopropanol Chemical compound CC(C)O KFZMGEQAYNKOFK-UHFFFAOYSA-N 0.000 description 5
- 239000011149 active material Substances 0.000 description 5
- 238000001354 calcination Methods 0.000 description 5
- 230000008021 deposition Effects 0.000 description 5
- 239000012530 fluid Substances 0.000 description 5
- 150000002739 metals Chemical class 0.000 description 5
- 239000002109 single walled nanotube Substances 0.000 description 5
- LMDZBCPBFSXMTL-UHFFFAOYSA-N 1-ethyl-3-(3-dimethylaminopropyl)carbodiimide Chemical compound CCN=C=NCCCN(C)C LMDZBCPBFSXMTL-UHFFFAOYSA-N 0.000 description 4
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 4
- 229920000049 Carbon (fiber) Polymers 0.000 description 4
- PIICEJLVQHRZGT-UHFFFAOYSA-N Ethylenediamine Chemical compound NCCN PIICEJLVQHRZGT-UHFFFAOYSA-N 0.000 description 4
- 239000006229 carbon black Substances 0.000 description 4
- 239000004917 carbon fiber Substances 0.000 description 4
- 125000003178 carboxy group Chemical group [H]OC(*)=O 0.000 description 4
- 238000006555 catalytic reaction Methods 0.000 description 4
- 238000009792 diffusion process Methods 0.000 description 4
- 150000002009 diols Chemical class 0.000 description 4
- 238000001914 filtration Methods 0.000 description 4
- 239000001257 hydrogen Substances 0.000 description 4
- 229910052739 hydrogen Inorganic materials 0.000 description 4
- 238000004519 manufacturing process Methods 0.000 description 4
- 230000004048 modification Effects 0.000 description 4
- 238000012986 modification Methods 0.000 description 4
- 239000002048 multi walled nanotube Substances 0.000 description 4
- 239000012071 phase Substances 0.000 description 4
- 229910000030 sodium bicarbonate Inorganic materials 0.000 description 4
- 239000002904 solvent Substances 0.000 description 4
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 3
- 230000001588 bifunctional effect Effects 0.000 description 3
- 125000004432 carbon atom Chemical group C* 0.000 description 3
- 239000012018 catalyst precursor Substances 0.000 description 3
- 150000001875 compounds Chemical class 0.000 description 3
- 238000011109 contamination Methods 0.000 description 3
- 230000008878 coupling Effects 0.000 description 3
- 238000010168 coupling process Methods 0.000 description 3
- 238000005859 coupling reaction Methods 0.000 description 3
- 239000006185 dispersion Substances 0.000 description 3
- 238000001125 extrusion Methods 0.000 description 3
- 229910021389 graphene Inorganic materials 0.000 description 3
- 229910002804 graphite Inorganic materials 0.000 description 3
- 239000010439 graphite Substances 0.000 description 3
- 238000005984 hydrogenation reaction Methods 0.000 description 3
- 238000005259 measurement Methods 0.000 description 3
- 230000007246 mechanism Effects 0.000 description 3
- 239000002121 nanofiber Substances 0.000 description 3
- 229910052760 oxygen Inorganic materials 0.000 description 3
- 239000001301 oxygen Substances 0.000 description 3
- 230000009467 reduction Effects 0.000 description 3
- 229910052723 transition metal Inorganic materials 0.000 description 3
- 150000003624 transition metals Chemical class 0.000 description 3
- 239000011800 void material Substances 0.000 description 3
- RYHBNJHYFVUHQT-UHFFFAOYSA-N 1,4-Dioxane Chemical compound C1COCCO1 RYHBNJHYFVUHQT-UHFFFAOYSA-N 0.000 description 2
- CSCPPACGZOOCGX-UHFFFAOYSA-N Acetone Chemical compound CC(C)=O CSCPPACGZOOCGX-UHFFFAOYSA-N 0.000 description 2
- QGZKDVFQNNGYKY-UHFFFAOYSA-N Ammonia Chemical compound N QGZKDVFQNNGYKY-UHFFFAOYSA-N 0.000 description 2
- 229920000742 Cotton Polymers 0.000 description 2
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 description 2
- ATUOYWHBWRKTHZ-UHFFFAOYSA-N Propane Chemical compound CCC ATUOYWHBWRKTHZ-UHFFFAOYSA-N 0.000 description 2
- 238000005411 Van der Waals force Methods 0.000 description 2
- 238000010521 absorption reaction Methods 0.000 description 2
- 229910003481 amorphous carbon Inorganic materials 0.000 description 2
- 230000008901 benefit Effects 0.000 description 2
- 235000005770 birds nest Nutrition 0.000 description 2
- 150000001718 carbodiimides Chemical class 0.000 description 2
- JYYOBHFYCIDXHH-UHFFFAOYSA-N carbonic acid;hydrate Chemical compound O.OC(O)=O JYYOBHFYCIDXHH-UHFFFAOYSA-N 0.000 description 2
- 238000003421 catalytic decomposition reaction Methods 0.000 description 2
- 238000001311 chemical methods and process Methods 0.000 description 2
- 235000009508 confectionery Nutrition 0.000 description 2
- 238000007796 conventional method Methods 0.000 description 2
- 238000006352 cycloaddition reaction Methods 0.000 description 2
- 230000000694 effects Effects 0.000 description 2
- 150000002148 esters Chemical group 0.000 description 2
- 239000000835 fiber Substances 0.000 description 2
- 239000012065 filter cake Substances 0.000 description 2
- 239000007789 gas Substances 0.000 description 2
- 230000014509 gene expression Effects 0.000 description 2
- 230000006872 improvement Effects 0.000 description 2
- 238000011065 in-situ storage Methods 0.000 description 2
- 239000007788 liquid Substances 0.000 description 2
- 239000007791 liquid phase Substances 0.000 description 2
- 150000002736 metal compounds Chemical class 0.000 description 2
- 229910052757 nitrogen Inorganic materials 0.000 description 2
- 239000003208 petroleum Substances 0.000 description 2
- 238000002360 preparation method Methods 0.000 description 2
- 239000011541 reaction mixture Substances 0.000 description 2
- 238000010992 reflux Methods 0.000 description 2
- 235000017557 sodium bicarbonate Nutrition 0.000 description 2
- 239000007790 solid phase Substances 0.000 description 2
- 238000003786 synthesis reaction Methods 0.000 description 2
- 238000011282 treatment Methods 0.000 description 2
- 235000005765 wild carrot Nutrition 0.000 description 2
- QTBSBXVTEAMEQO-UHFFFAOYSA-M Acetate Chemical compound CC([O-])=O QTBSBXVTEAMEQO-UHFFFAOYSA-M 0.000 description 1
- 229920002134 Carboxymethyl cellulose Polymers 0.000 description 1
- VEXZGXHMUGYJMC-UHFFFAOYSA-M Chloride anion Chemical compound [Cl-] VEXZGXHMUGYJMC-UHFFFAOYSA-M 0.000 description 1
- 239000004593 Epoxy Substances 0.000 description 1
- OAKJQQAXSVQMHS-UHFFFAOYSA-N Hydrazine Chemical compound NN OAKJQQAXSVQMHS-UHFFFAOYSA-N 0.000 description 1
- VEXZGXHMUGYJMC-UHFFFAOYSA-N Hydrochloric acid Chemical compound Cl VEXZGXHMUGYJMC-UHFFFAOYSA-N 0.000 description 1
- 229920000663 Hydroxyethyl cellulose Polymers 0.000 description 1
- DGAQECJNVWCQMB-PUAWFVPOSA-M Ilexoside XXIX Chemical compound C[C@@H]1CC[C@@]2(CC[C@@]3(C(=CC[C@H]4[C@]3(CC[C@@H]5[C@@]4(CC[C@@H](C5(C)C)OS(=O)(=O)[O-])C)C)[C@@H]2[C@]1(C)O)C)C(=O)O[C@H]6[C@@H]([C@H]([C@@H]([C@H](O6)CO)O)O)O.[Na+] DGAQECJNVWCQMB-PUAWFVPOSA-M 0.000 description 1
- 229910002651 NO3 Inorganic materials 0.000 description 1
- NHNBFGGVMKEFGY-UHFFFAOYSA-N Nitrate Chemical compound [O-][N+]([O-])=O NHNBFGGVMKEFGY-UHFFFAOYSA-N 0.000 description 1
- 239000004677 Nylon Substances 0.000 description 1
- CBENFWSGALASAD-UHFFFAOYSA-N Ozone Chemical compound [O-][O+]=O CBENFWSGALASAD-UHFFFAOYSA-N 0.000 description 1
- 229910002666 PdCl2 Inorganic materials 0.000 description 1
- 239000004952 Polyamide Substances 0.000 description 1
- 239000004698 Polyethylene Substances 0.000 description 1
- 239000004793 Polystyrene Substances 0.000 description 1
- 229910006069 SO3H Inorganic materials 0.000 description 1
- NINIDFKCEFEMDL-UHFFFAOYSA-N Sulfur Chemical compound [S] NINIDFKCEFEMDL-UHFFFAOYSA-N 0.000 description 1
- 239000004809 Teflon Substances 0.000 description 1
- 229920006362 Teflon® Polymers 0.000 description 1
- 239000002250 absorbent Substances 0.000 description 1
- 230000002745 absorbent Effects 0.000 description 1
- 238000002479 acid--base titration Methods 0.000 description 1
- 239000000853 adhesive Substances 0.000 description 1
- 230000001070 adhesive effect Effects 0.000 description 1
- 238000005054 agglomeration Methods 0.000 description 1
- 230000002776 aggregation Effects 0.000 description 1
- 238000013019 agitation Methods 0.000 description 1
- 229910052783 alkali metal Inorganic materials 0.000 description 1
- 230000029936 alkylation Effects 0.000 description 1
- 238000005804 alkylation reaction Methods 0.000 description 1
- 229910021529 ammonia Inorganic materials 0.000 description 1
- 150000008064 anhydrides Chemical group 0.000 description 1
- 125000000129 anionic group Chemical group 0.000 description 1
- 239000012298 atmosphere Substances 0.000 description 1
- 239000011230 binding agent Substances 0.000 description 1
- 230000005587 bubbling Effects 0.000 description 1
- 150000001720 carbohydrates Chemical class 0.000 description 1
- 235000014633 carbohydrates Nutrition 0.000 description 1
- 150000001722 carbon compounds Chemical class 0.000 description 1
- 239000002134 carbon nanofiber Substances 0.000 description 1
- 125000002091 cationic group Chemical group 0.000 description 1
- 229920002678 cellulose Polymers 0.000 description 1
- 239000001913 cellulose Substances 0.000 description 1
- 235000010980 cellulose Nutrition 0.000 description 1
- 229920003174 cellulose-based polymer Polymers 0.000 description 1
- 230000008859 change Effects 0.000 description 1
- 238000012512 characterization method Methods 0.000 description 1
- 239000003610 charcoal Substances 0.000 description 1
- 239000003638 chemical reducing agent Substances 0.000 description 1
- 238000004891 communication Methods 0.000 description 1
- 238000005056 compaction Methods 0.000 description 1
- 239000002131 composite material Substances 0.000 description 1
- 239000012141 concentrate Substances 0.000 description 1
- 239000000356 contaminant Substances 0.000 description 1
- 238000004132 cross linking Methods 0.000 description 1
- 239000013078 crystal Substances 0.000 description 1
- 230000009849 deactivation Effects 0.000 description 1
- 230000020335 dealkylation Effects 0.000 description 1
- 238000006900 dealkylation reaction Methods 0.000 description 1
- 238000006356 dehydrogenation reaction Methods 0.000 description 1
- 239000008367 deionised water Substances 0.000 description 1
- 238000005137 deposition process Methods 0.000 description 1
- 238000003795 desorption Methods 0.000 description 1
- RTZKZFJDLAIYFH-UHFFFAOYSA-N ether Chemical group CCOCC RTZKZFJDLAIYFH-UHFFFAOYSA-N 0.000 description 1
- 230000008020 evaporation Effects 0.000 description 1
- 238000002474 experimental method Methods 0.000 description 1
- 239000000706 filtrate Substances 0.000 description 1
- 239000012467 final product Substances 0.000 description 1
- 238000007667 floating Methods 0.000 description 1
- 239000012634 fragment Substances 0.000 description 1
- 239000003292 glue Substances 0.000 description 1
- 238000010438 heat treatment Methods 0.000 description 1
- 239000001307 helium Substances 0.000 description 1
- 229910052734 helium Inorganic materials 0.000 description 1
- SWQJXJOGLNCZEY-UHFFFAOYSA-N helium atom Chemical compound [He] SWQJXJOGLNCZEY-UHFFFAOYSA-N 0.000 description 1
- 229930195733 hydrocarbon Natural products 0.000 description 1
- 150000002430 hydrocarbons Chemical class 0.000 description 1
- 238000007037 hydroformylation reaction Methods 0.000 description 1
- 238000007327 hydrogenolysis reaction Methods 0.000 description 1
- 150000002500 ions Chemical class 0.000 description 1
- 238000006317 isomerization reaction Methods 0.000 description 1
- 150000002596 lactones Chemical group 0.000 description 1
- 230000001404 mediated effect Effects 0.000 description 1
- 239000012685 metal catalyst precursor Substances 0.000 description 1
- 238000006263 metalation reaction Methods 0.000 description 1
- VNWKTOKETHGBQD-UHFFFAOYSA-N methane Chemical compound C VNWKTOKETHGBQD-UHFFFAOYSA-N 0.000 description 1
- 239000000693 micelle Substances 0.000 description 1
- 150000002825 nitriles Chemical class 0.000 description 1
- 229920001778 nylon Polymers 0.000 description 1
- 230000003287 optical effect Effects 0.000 description 1
- 125000000962 organic group Chemical group 0.000 description 1
- 239000003960 organic solvent Substances 0.000 description 1
- 230000001590 oxidative effect Effects 0.000 description 1
- 238000005949 ozonolysis reaction Methods 0.000 description 1
- PIBWKRNGBLPSSY-UHFFFAOYSA-L palladium(II) chloride Chemical compound Cl[Pd]Cl PIBWKRNGBLPSSY-UHFFFAOYSA-L 0.000 description 1
- GPNDARIEYHPYAY-UHFFFAOYSA-N palladium(II) nitrate Inorganic materials [Pd+2].[O-][N+]([O-])=O.[O-][N+]([O-])=O GPNDARIEYHPYAY-UHFFFAOYSA-N 0.000 description 1
- 238000002161 passivation Methods 0.000 description 1
- 230000037361 pathway Effects 0.000 description 1
- 238000005453 pelletization Methods 0.000 description 1
- 229920001568 phenolic resin Polymers 0.000 description 1
- 239000005011 phenolic resin Substances 0.000 description 1
- 238000004375 physisorption Methods 0.000 description 1
- 239000002574 poison Substances 0.000 description 1
- 231100000614 poison Toxicity 0.000 description 1
- 229920000435 poly(dimethylsiloxane) Polymers 0.000 description 1
- 229920000058 polyacrylate Polymers 0.000 description 1
- 229920002647 polyamide Polymers 0.000 description 1
- 229920000728 polyester Polymers 0.000 description 1
- 229920000573 polyethylene Polymers 0.000 description 1
- 229920000642 polymer Polymers 0.000 description 1
- 229920002223 polystyrene Polymers 0.000 description 1
- 229920002635 polyurethane Polymers 0.000 description 1
- 239000004814 polyurethane Substances 0.000 description 1
- 238000002459 porosimetry Methods 0.000 description 1
- 159000000001 potassium salts Chemical class 0.000 description 1
- 239000000843 powder Substances 0.000 description 1
- 238000002203 pretreatment Methods 0.000 description 1
- 239000001294 propane Substances 0.000 description 1
- 238000007670 refining Methods 0.000 description 1
- 238000011160 research Methods 0.000 description 1
- 229910052708 sodium Inorganic materials 0.000 description 1
- 239000011734 sodium Substances 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- 239000008247 solid mixture Substances 0.000 description 1
- 238000003756 stirring Methods 0.000 description 1
- 238000006467 substitution reaction Methods 0.000 description 1
- 239000011593 sulfur Substances 0.000 description 1
- 229910052717 sulfur Inorganic materials 0.000 description 1
- 239000000725 suspension Substances 0.000 description 1
- 238000007669 thermal treatment Methods 0.000 description 1
- 150000003568 thioethers Chemical class 0.000 description 1
- 238000010555 transalkylation reaction Methods 0.000 description 1
- 238000005406 washing Methods 0.000 description 1
- 238000009736 wetting Methods 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C209/00—Preparation of compounds containing amino groups bound to a carbon skeleton
- C07C209/30—Preparation of compounds containing amino groups bound to a carbon skeleton by reduction of nitrogen-to-oxygen or nitrogen-to-nitrogen bonds
- C07C209/32—Preparation of compounds containing amino groups bound to a carbon skeleton by reduction of nitrogen-to-oxygen or nitrogen-to-nitrogen bonds by reduction of nitro groups
- C07C209/36—Preparation of compounds containing amino groups bound to a carbon skeleton by reduction of nitrogen-to-oxygen or nitrogen-to-nitrogen bonds by reduction of nitro groups by reduction of nitro groups bound to carbon atoms of six-membered aromatic rings in presence of hydrogen-containing gases and a catalyst
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J21/00—Catalysts comprising the elements, oxides, or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium, or hafnium
- B01J21/18—Carbon
- B01J21/185—Carbon nanotubes
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/16—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/24—Chromium, molybdenum or tungsten
- B01J23/26—Chromium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/16—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of arsenic, antimony, bismuth, vanadium, niobium, tantalum, polonium, chromium, molybdenum, tungsten, manganese, technetium or rhenium
- B01J23/24—Chromium, molybdenum or tungsten
- B01J23/28—Molybdenum
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
- B01J23/40—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals of the platinum group metals
- B01J23/42—Platinum
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
- B01J23/40—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals of the platinum group metals
- B01J23/44—Palladium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/50—Catalysts, in general, characterised by their form or physical properties characterised by their shape or configuration
- B01J35/58—Fabrics or filaments
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/0009—Use of binding agents; Moulding; Pressing; Powdering; Granulating; Addition of materials ameliorating the mechanical properties of the product catalyst
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/0201—Impregnation
- B01J37/0207—Pretreatment of the support
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/06—Washing
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/30—Ion-exchange
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y30/00—Nanotechnology for materials or surface science, e.g. nanocomposites
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B82—NANOTECHNOLOGY
- B82Y—SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES; MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES; MANUFACTURE OR TREATMENT OF NANOSTRUCTURES
- B82Y40/00—Manufacture or treatment of nanostructures
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B32/00—Carbon; Compounds thereof
- C01B32/15—Nano-sized carbon materials
- C01B32/158—Carbon nanotubes
- C01B32/168—After-treatment
- C01B32/174—Derivatisation; Solubilisation; Dispersion in solvents
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
- B01J35/391—Physical properties of the active metal ingredient
- B01J35/393—Metal or metal oxide crystallite size
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
- B01J35/391—Physical properties of the active metal ingredient
- B01J35/394—Metal dispersion value, e.g. percentage or fraction
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/20—Sulfiding
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B2202/00—Structure or properties of carbon nanotubes
- C01B2202/02—Single-walled nanotubes
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B2202/00—Structure or properties of carbon nanotubes
- C01B2202/06—Multi-walled nanotubes
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S977/00—Nanotechnology
- Y10S977/70—Nanostructure
- Y10S977/734—Fullerenes, i.e. graphene-based structures, such as nanohorns, nanococoons, nanoscrolls or fullerene-like structures, e.g. WS2 or MoS2 chalcogenide nanotubes, planar C3N4, etc.
- Y10S977/742—Carbon nanotubes, CNTs
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S977/00—Nanotechnology
- Y10S977/70—Nanostructure
- Y10S977/734—Fullerenes, i.e. graphene-based structures, such as nanohorns, nanococoons, nanoscrolls or fullerene-like structures, e.g. WS2 or MoS2 chalcogenide nanotubes, planar C3N4, etc.
- Y10S977/742—Carbon nanotubes, CNTs
- Y10S977/745—Carbon nanotubes, CNTs having a modified surface
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S977/00—Nanotechnology
- Y10S977/70—Nanostructure
- Y10S977/734—Fullerenes, i.e. graphene-based structures, such as nanohorns, nanococoons, nanoscrolls or fullerene-like structures, e.g. WS2 or MoS2 chalcogenide nanotubes, planar C3N4, etc.
- Y10S977/742—Carbon nanotubes, CNTs
- Y10S977/745—Carbon nanotubes, CNTs having a modified surface
- Y10S977/748—Modified with atoms or molecules bonded to the surface
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S977/00—Nanotechnology
- Y10S977/70—Nanostructure
- Y10S977/734—Fullerenes, i.e. graphene-based structures, such as nanohorns, nanococoons, nanoscrolls or fullerene-like structures, e.g. WS2 or MoS2 chalcogenide nanotubes, planar C3N4, etc.
- Y10S977/742—Carbon nanotubes, CNTs
- Y10S977/75—Single-walled
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S977/00—Nanotechnology
- Y10S977/70—Nanostructure
- Y10S977/734—Fullerenes, i.e. graphene-based structures, such as nanohorns, nanococoons, nanoscrolls or fullerene-like structures, e.g. WS2 or MoS2 chalcogenide nanotubes, planar C3N4, etc.
- Y10S977/742—Carbon nanotubes, CNTs
- Y10S977/752—Multi-walled
Definitions
- the invention relates to a composition of supported catalyst comprising networks of carbon nanotubes.
- the catalysts or catalyst precursor may be predeposited onto the carbon nanotube followed by formation of the carbon nanotube network structure with the predeposited or metal loaded carbon nanotube.
- the catalysts or catalyst precursor may be deposited onto the carbon nanotube after the formation of the carbon nanotube network structure.
- the result of the present invention is a supported catalyst comprising a carbon nanotube network structure with metal catalysts more evenly and thoroughly dispersed in the structure.
- the supported catalyst of the present invention contains a higher concentration and better distribution of metal catalysts, leading to more efficient and higher yields of the desired final product.
- Supported catalysts typically comprise an inert support material and a catalytically active material. Because heterogeneous reactions are normally carried out at elevated temperatures (and sometimes at elevated pressures as well) and in a reactive atmosphere, the exact chemical nature of the active catalyst component within the reaction zone can be difficult to determine. Thus, the terms “catalyst” or “supported catalyst” are often used interchangeably in the industry to refer to the composition comprising both the inert support and catalytically active material that is charged into the reaction zone.
- Supported catalysts may be prepared by, for example, initially depositing precursors of the actual catalytically active material onto the inert support and then treating them accordingly (e.g., calcination), before feeding them into the reaction zone. More extensive pre-treatments and passivation steps to stabilize the supported catalyst before feeding to the reaction zone are also common.
- metal salts are deposited onto inert support, converted into metal oxides by calcinations at elevated temperatures and then further reduced in situ to active pure metal catalysts.
- Supported catalysts are widely used in heterogeneous catalytic reactions for chemical processes in the petroleum, petrochemical and chemical industries. Such reactions are commonly performed with the reactant(s) and product(s) in the fluid phase and the catalyst in the solid phase. In heterogeneous catalytic reactions, the reaction occurs at the interface between the phases, i.e., the interface between the fluid phase of the reactant(s) and product(s) and the solid phase of the supported catalyst. Hence, the properties of the surface of a heterogeneous supported catalyst are important factors in the effective use of the catalyst.
- the surface area of the active catalyst, as supported, and the accessibility of that surface area to reactant adsorption and product desorption are important. These factors affect the activity of the catalyst, i.e., the rate of conversion of reactants to products.
- catalytic activity is proportional to catalyst surface area. Therefore, a high specific area is desirable. However, the surface area should be accessible to reactants and products as well as to heat flow.
- the chemisorption of a reactant by a catalyst surface is preceded by the diffusion of that reactant through the internal structure of the catalyst.
- the active catalyst material may be supported on the external and/or internal structure of a support.
- the internal structure of a support in the form of a porous structure can contain a greater surface area than the external surface. Therefore, when an ample amount of active catalysts are located or supported in the internal structure of a support, the accessibility of the internal structure of the support to reactant(s), product(s) and heat flow is important. Accessibility is measured by porosity and pore size distribution.
- Activated carbons and charcoals used as catalyst supports may have surface areas of about a thousand square meters per gram, and porosities of greater than 1 ml/gm.
- micropores i.e., pores with pore diameters of 2 nm or less. These pores can be inaccessible because of diffusion limitations. They are easily plugged and thereby deactivated.
- high porosity materials where the pores are mainly in the mesopore region (i.e., 2-50 nm) or macropore region (i.e., greater than 50 nm) are most desirable.
- the chemical purity of the catalyst and the catalyst support also have important effects on the selectivity of the catalyst, i.e., the degree to which the catalyst produces one product from among several products, and the life of the catalyst.
- a catalyst it is also important that a catalyst, at the very least, minimize its contribution to the chemical contamination of reactant(s) and product(s). In the case of a catalyst support, this is even more important since the support is a potential source of contamination both to the catalyst it supports and to the chemical process. Further, some catalysts are particularly sensitive to contamination that can either promote unwanted competing reactions, i.e., affect its selectivity, or render the catalyst ineffective, i.e., “poison” it. For example, charcoal and commercial graphites or carbons made from petroleum residues usually contain trace amounts of sulfur or nitrogen. Carbons of agricultural origin may contain these contaminants as well as metals common to biological systems and may be undesirable for that reason.
- Supported catalyst which contain more active catalysts in or on the support will generally have better results and catalytic activity than supported catalyst mainly comprised of the support material with few active catalysts.
- supported catalysts which have catalytic materials more evenly dispersed throughout or within the support generally have higher yield and catalytic activity than supported catalysts which have poor distribution of the catalytic material in or on the support.
- Carbon nanotubes have been identified as materials of interest for use as catalysts and catalyst supports. Carbon nanotubes exist in a variety of forms and have been prepared through the catalytic decomposition of various carbon-containing gases at metal surfaces.
- Carbon nanotubes are vermicular carbon deposits having diameters less than 1.0 ⁇ , preferably less than 0.5 ⁇ , and even more preferably less than 0.2 ⁇ .
- Carbon nanotubes can be either multi walled (i.e., have more than one graphene layer more or less parallel to the nanotube axis) or single walled (i.e., have only a single graphene layer parallel to the nanotube axis).
- Other types of carbon nanotubes are also known, such as fishbone fibrils (e.g., wherein the graphene sheets are disposed in a herringbone pattern with respect to the nanotube axis), etc.
- carbon nanotubes may be in the form of discrete nanotubes, aggregates of nanotubes (i.e., dense, microscopic particulate structure comprising entangled carbon nanotubes) or a mixture of both.
- carbon nanotubes The most preferred way of making carbon nanotubes is by catalytic growth from hydrocarbons or other gaseous carbon compounds, such as CO, mediated by supported or free floating catalyst particles.
- Carbon nanotubes may also be formed as aggregates, which are dense microscope particulate structures of entangled carbon nanotubes and may resemble the morphology of bird nest, cotton candy, combed yarn or open net. Aggregates are formed during the production of carbon nanotubes and the morphology of the aggregate is controlled by the choice of catalyst support. Spherical supports grow nanotubes in all directions leading to the formation of bird nest aggregates. Combed yarn and open net aggregates are prepared using supports having one or more readily cleavable planar surfaces, e.g., an iron or iron-containing metal catalyst particle deposited on a support material having one or more readily cleavable surfaces and a surface area of at least 1 square meter per gram.
- Carbon nanotubes are distinguishable from commercially available continuous carbon fibers.
- carbon fibers have aspect ratios (L/D) of at least 10 4 and often 10 6 or more, while carbon nanotubes have desirably large, but unavoidably finite, aspect ratios (e.g., less than or greater than 100).
- L/D aspect ratios
- carbon nanotubes have desirably large, but unavoidably finite, aspect ratios (e.g., less than or greater than 100).
- the diameter of continuous carbon fibers which is always greater than 1.0 ⁇ and typically 5 to 7 ⁇ , is also far larger than that of carbon nanotubes, which is usually less than 1.0 ⁇ .
- Carbon nanotubes also have vastly superior strength and conductivity than carbon fibers.
- Carbon nanotubes also differ physically and chemically from other forms of carbon such as standard graphite and carbon black.
- Standard graphite because of its structure, can undergo oxidation to almost complete saturation.
- carbon black is an amorphous carbon generally in the form of spheroidal particles having a graphene structure, such as carbon layers around a disordered nucleus.
- carbon nanotubes have one or more layers of ordered graphitic carbon atoms disposed substantially concentrically about the cylindrical axis of the nanotube.
- carbon nanotube structures are known to be useful catalyst supports and catalysts.
- Carbon nanotube structures provide certain structural advantages over other known carbon catalyst supports in that more of the internal pore structures are in the form of mesopores (i.e., 2 to 50 nm) and macropores (i.e., greater than 50 nm).
- carbon nanotube structures also have greater structural strength, and thus is less likely to frit or attrit in comparison to other known carbon catalyst supports.
- Carbon nanotube structures include, but are not limited to the following groups: assemblages, networks and rigid porous structures.
- Assemblages are carbon nanotube structures which have relatively uniform properties along one, preferably two and most desirably three dimensional axis of the three dimensional assemblage.
- assemblages including but not limited to mats and plugs
- assemblages are formed by de-aggregating carbon nanotube aggregates, and then reassembling them to form assemblages which have uniform properties over a greater range of distance than the original aggregates.
- Nanotube mats or assemblages have been prepared by dispersing carbon nanotubes in aqueous or organic mediums and then filtering the nanotubes to form a mat or assemblage.
- Mats and plugs have also been prepared by forming a gel or paste of nanotubes in a fluid, e.g. an organic solvent such as propane and then heating the gel or paste to a temperature above the critical temperature of the medium, removing the supercritical fluid and finally removing the resultant porous mat or plug from the vessel in which the process has been carried out.
- a fluid e.g. an organic solvent such as propane
- a gluing agent may be present during the step of mat or plug formation. As the assemblage dries, the glue will concentrate at the nanotube intersections.
- Preferred gluing agents or binders include cellulose-based polymers, hydroxyl ethyl cellulose, carboxyl methyl cellulose, cellulose, carbohydrates, polyethylene, polystyrene, nylon, polyurethane, polyester, polyamides, poly(dimethylsiloxane), acrylic polymers and phenolic resins.
- the polymers are free of alkali metal salts such as sodium or potassium salts.
- Networks are formed by linking individual functionalized carbon nanotubes (i.e., carbon nanotubes which contain functional groups, such as but not limited to oxygen containing moieties, on their surface) together by using a linking molecule between the functionalized groups located on the surface of the carbon nanotubes.
- functionalized carbon nanotubes i.e., carbon nanotubes which contain functional groups, such as but not limited to oxygen containing moieties, on their surface
- the carbon nanotubes are functionalized, for example, by contacting them with an appropriate reagent such as those described in WO 97/32571 or U.S. Pat. No. 6,203,814, all of which are incorporated by reference.
- the carbon nanotubes are functionalized through oxidation with oxidizing agents such as potassium chlorate (KClO 3 ), sulfuric acid (H 2 SO 4 ), nitric acid (HNO 3 ), hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , ClO 2 , etc.
- oxidizing agents such as potassium chlorate (KClO 3 ), sulfuric acid (H 2 SO 4 ), nitric acid (HNO 3 ), hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , ClO 2 , etc.
- Typical linking molecules or linking agents are bifunctional compounds such as diamines, diols, etc.
- Rigid porous structures are formed by either linking the individual functionalized carbon nanotubes together without the use of a linking molecule, or by gluing carbon nanotube aggregates together with a gluing agent.
- U.S. Pat. No. 6,099,965 hereby incorporated by reference, discloses that functionalized nanotubes become self adhesive after an appropriate thermal treatment.
- the carbon nanotubes are functionalized, for example, by contacting them with an appropriate reagent (e.g., WO 97/32571, U.S. Pat. No.
- oxidizing agent such as potassium chlorate (KClO 3 ), sulfuric acid (H 2 SO 4 ), nitric acid (HNO 3 ), persulfate, hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , ClO 2 , etc.
- oxidizing agent such as potassium chlorate (KClO 3 ), sulfuric acid (H 2 SO 4 ), nitric acid (HNO 3 ), persulfate, hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , ClO 2 , etc.
- the oxidized nanotubes are believed to form ester, anhydride, lactone and ether bonds between themselves.
- assemblages and rigid porous structures as defined above are essentially “pure nanotubes” admixed, at most with a minor amount of gluing agent.
- Networks because of the presence of the “linker” and the availability of linker molecules of various molecular weights and structures provide an additional degree of control on the properties of the final structure. In particular, density and porosity can be tailored.
- Rigid porous structures may advantageously be made by extruding a paste like suspension of functionalized nanotubes or a mixture of as made aggregates and gluing agent, (optionally admixed with a liquid vehicle) followed by a calcinations step to drive off conveying liquids and either cross link the functionalized nanotubes or to pyrolize the gluing agent.
- activated charcoals and other materials have been used as catalysts and catalyst supports, none have heretofore had all of the requisite qualities of high surface area, porosity, pore size distribution, resistance to attrition and purity for the conduct of a variety of selected petrochemical and refining processes as compared to carbon nanotube structures. Furthermore, unlike carbon nanotube structures, much of the surface area in activated charcoals and other materials is in the form of inaccessible micropores.
- a supported catalyst comprising a carbon nanotube structure with well or evenly dispersed metal catalysts therein, the supported catalyst consequently having highly accessible surface area, high porosity, and attrition resistance, and which are substantially micropore free, highly active, highly selective and are capable of extended use with no significant deactivation.
- a new method for preparing supported catalysts comprising the steps of loading metal catalyst onto carbon nanotubes to form metal loaded carbon nanotubes; and forming a carbon nanotube network structure from said metal loaded carbon nanotubes.
- Another new method for preparing supported catalysts comprising the steps of forming a carbon nanotube network structure and then loading metal catalyst onto said carbon nanotube network structure.
- the carbon nanotube network structures are prepared by a process comprising the steps of functionalizing carbon nanotubes with a functionalizing agent to form functionalized carbon nanotubes, and adding an appropriate reagent to said functionalized carbon nanotubes to form a carbon nanotube network structure.
- These reagents are linking molecules such as diamines or diols which hold the functionalized carbon nanotubes together.
- the metal catalyst catalysts may be loaded onto the carbon nanotubes prior to forming the carbon nanotube network structure or may be loaded onto the carbon nanotube network structure after it has been formed.
- oxidizing agents include, but is not limited to, potassium chlorate, sulfuric acid, nitric acid (HNO 3 ), persulfate, hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , or ClO 2 .
- Catalysts or catalyst precursors useful in the methods of the present invention include, but are not limited to, metals such as ruthenium, osmium, rhodium, iridium, palladium, platinum or a mixture thereof, as well as metal oxides, metal halides, metal carbides, metal nitrides, metal phosphides and metal sulfides of other transition metals including but not limited to Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Nb, Mo, La, Ce, W or combinations thereof.
- metals such as ruthenium, osmium, rhodium, iridium, palladium, platinum or a mixture thereof, as well as metal oxides, metal halides, metal carbides, metal nitrides, metal phosphides and metal sulfides of other transition metals including but not limited to Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn,
- the metal catalysts or metal catalyst precursors may be loaded onto the nanotubes by any known method, such as ion exchange, impregnation, or incipient wetness, precipitation, physical or chemical adsorption or co-precipitation.
- the metal catalysts are predeposited or loaded onto the functionalized carbon nanotubes by ion exchange, i.e. mixing a solution containing salts of said metal catalysts with the functionalized carbon nanotubes, allowing the salts to react with the functional groups of the functionalized nanotubes and evaporating the remaining solution (e.g., the excess solvent from the solution ).
- the metal catalysts are predeposited or loaded onto carbon nanotubes by impregnation, or incipient wetness, i.e. wetting a mass of carbon nanotubes with a solution of metal salts and evaporating the solvent.
- metal salts may be caused to precipitate from solution in the presence of a mass of carbon nanotubes causing said precipitated metal salts to physically or chemically adsorb on said nanotubes, followed by evaporation of the solvent.
- these same loading or deposition steps may be used to load or deposit the metal catalysts onto the carbon nanotube network structure after it has been formed.
- FIG. 1 is a flow chart illustrating the various embodiments of the present invention.
- nanotube refers to single walled or multiwalled carbon nanotubes.
- Each refers to an elongated structure preferably having a cross section (e.g., angular fibers having edges) or a diameter (e.g., rounded) less than 1 micron (for multiwalled nanotubes) or less than 5 nm (for single walled nanotubes).
- nanotube also includes “buckytubes”, and fishbone fibrils.
- Aggregate refers to a dense, microscopic particulate structures of entangled carbon nanotubes.
- “Assemblage” refers to structures having relatively or substantially uniform physical properties along at least one dimensional axis and desirably having relatively or substantially uniform physical properties in one or more planes within the assemblage, i.e., they have isotropic physical properties in that plane.
- the assemblage may comprise uniformly dispersed individual interconnected nanotubes or a mass of connected aggregates of nanotubes. In other embodiments, the entire assemblage is relatively or substantially isotropic with respect to one or more of its physical properties.
- the physical properties which can be easily measured and by which uniformity or isotropy are determined include resistivity and optical density.
- Graphenic carbon is a form of carbon whose carbon atoms are each linked to three other carbon atoms in an essentially planar layer forming hexagonal fused rings.
- the layers are platelets having only a few rings in their diameter or ribbons having many rings in their length but only a few rings in their width.
- Graphitic carbon consists of layers which are essentially parallel to one another and no more than 3.6 angstroms apart.
- Internal structure refers to the internal structure of a carbon nanotube structure including the relative orientation of the carbon nanotubes, the diversity of and overall average of nanotube orientations, the proximity of the nanotubes to one another, the void space or pores created by the interstices and spaces between the fibers and size, shape, number and orientation of the flow channels or paths formed by the connection of the void spaces and/or pores.
- the structure may also include characteristics relating to the size, spacing and orientation of aggregate particles that form the assemblage.
- relative orientation refers to the orientation of an individual nanotube or aggregate with respect to the others (i.e., aligned versus non-aligned).
- the “diversity of” and “overall average” of nanotube or aggregate orientations refers to the range of nanotube orientations within the structure (alignment and orientation with respect to the external surface of the structure).
- Isotropic means that all measurements of a physical property within a plane or volume of the structure, independent of the direction of the measurement, are of a constant value. It is understood that measurements of such non-solid compositions must be taken on a representative sample of the structure so that the average value of the void spaces is taken into account.
- Micropore refers to a pore which has a diameter of greater than or equal to 50 nm.
- Pore refers to a pore which has a diameter of greater than or equal to 2 nm but less than 50 nm.
- Micropore refers to a pore which has a diameter of less than 2 nm.
- Nonuniform pore structure refers to a pore structure occurring when individual discrete nanotubes are distributed in a substantially nonuniform manner with substantially nonuniform spacings between nanotubes.
- Physical property means an inherent, measurable property of the porous structure, e.g., surface area, resistivity, fluid flow characteristics, density, porosity, etc.
- Pore traditionally refers to an opening or depression in the surface of a catalyst or catalyst support. Catalysts and catalyst supports comprising carbon nanotubes lack such traditional pores. Rather, in these materials, the spaces between individual nanotubes behave as (and are referred to herein as) pores, and the equivalent pore size of nanotube aggregates can be measured by conventional methods (porosimetry) of measuring pore size and pore size distribution. By varying the density and structure of aggregates, the equivalent pore size and pore size distribution can be varied.
- “Relatively” means that 95% of the values of the physical property when measured along an axis of, or within a plane of or within a volume of the structure, as the case may be, will be within plus or minus 20% of a mean value.
- “Substantially” or “predominantly” mean that 95% of the values of the physical property when measured along an axis of, or within a plane of or within a volume of the structure, as the case may be, will be within plus or minus 10% of a mean value.
- “Surface area” refers to the total surface area of a substance measurable by the BET technique as known in the art, a physisorption technique. Nitrogen or helium can be used as absorbents to measure the surface area.
- Uniform pore structure refers to a pore structure occurring when individual discrete nanotubes or nanofibers form the structure. In these cases, the distribution of individual nanotubes in the particles is substantially uniform with substantially regular spacings between the nanotubes. These spacings (analogous to pores in conventional supports) vary according to the densities of the structures.
- the present invention provides a new process for preparing supported catalysts comprising a metal loaded carbon nanotube network structure.
- the supported catalysts prepared in accordance with the preferred embodiment results in a better distribution and better dispersion of the metal catalysts within the carbon nanotube network structure, and consequently can yield better catalytic activity.
- the method comprises loading the metal catalyst onto carbon nanotubes and forming a carbon nanotube network structure from the loaded carbon nanotubes.
- the carbon nanotubes are functionalized before loading the metal catalysts.
- the method comprises loading the metal catalyst onto carbon nanotube network structures after the network structure has been formed.
- metal catalyst includes precursors of such metal catalyst. That is, metal catalyst includes metals such as ruthenium, osmium, rhodium, iridium, palladium, platinum or a mixture thereof, as well as precursors of other transition metals such as metal oxides, metal halides, metal carbides, metal nitrides, metal phosphides and metal sulfides sulfides of metals including but not limited to Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Nb, Mo, La, Ce, W or combinations thereof.
- metal catalyst includes metals such as ruthenium, osmium, rhodium, iridium, palladium, platinum or a mixture thereof, as well as precursors of other transition metals such as metal oxides, metal halides, metal carbides, metal nitrides, metal phosphides and metal sulfides sulfides of metals including but not limited to Ti, V
- the carbon nanotube network structure containing the metal catalysts represent the supported catalyst.
- metal catalysts in the form of precursors of metal catalyst
- various treatments such as calcinations, reduction, carburization, nitridization, phosphurization and sulphurization can be applied to obtain the desired catalyst composition.
- supported catalyst and supported metal catalyst as used in this application may refer to any of the inert support with metal salt (or active material precursor) deposited thereon; the same material after calcination or other pre-reaction treatment; or the inert support with active material thereon having whatever composition it takes on in the reaction zone.
- carbon nanotubes (whether produced in the form of discrete nanotubes or as-made aggregates, or mixture of both) are predeposited or loaded with metal catalysts before the metal loaded carbon nanotubes are made into a carbon nanotube network structure. All types of carbon nanotubes, whether single walled or multi walled, can be
- a preferred method to accomplish the predeposition or loading of the metal catalyst onto the carbon nanotube is to first functionalize the carbon nanotube surface before mixing with the metal catalyst or salt thereof. Functionalizing the carbon nanotubes results in the substitution of functional groups such as oxygen containing moieties onto the surface of the carbon nanotubes, which consequently results in better attachment of the metal catalyst to the carbon nanotube surface (whether by adsorption, hydrogen bond, adhesion, electrostatic attraction, covalent bond, absorption, van der Waals force, or any other mechanism which may occur to secure, support, hold or otherwise keep the metal catalyst onto the carbon nanotube surface).
- a decent survey article on functionalization hereby included in its entirety by reference, discussing single wall and multi walled carbon nanotubes is Hirsch, A. and Vostrowsky, O., “Functionalization of Carbon Nanotubes”, Topics in Current Chemistry, (2005) 245:193-237.
- Functionalization can be accomplished, for example, by contacting the carbon nanotubes with an appropriate reagent (e.g., WO 97/32571, U.S. Pat. No. 6,203,814, all of which are herein incorporated by reference), or preferably by contacting them with an oxidizing agent such as potassium chlorate, sulfuric acid, nitric acid (HNO 3 ), persulfate, hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , ClO 2 , etc. (e.g., U.S. Pat. No. 5,965,470, WO 95/07316, PCT/US00/18670 or WO 01/07694, all of which are herein incorporated by reference).
- an appropriate reagent e.g., WO 97/32571, U.S. Pat. No. 6,203,814, all of which are herein incorporated by reference
- an oxidizing agent such as potassium chlorate, sulfur
- the carbon nanotubes are in the form of aggregates, it is preferred to both break up or de-aggregate the aggregates and functionalize them. Such tasks can be accomplished concurrently by oxidizing the carbon nanotube aggregates, for example, by contacting them with an oxidizing agent such as potassium chlorate, sulfuric acid, nitric acid (HNO 3 ), persulfate, hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , ClO 2 , etc. (e.g., U.S. Pat. No. 5,965,470, WO 95/07316, PCT/US00/18670 or WO 01/07694, all of which are herein incorporated by reference).
- an oxidizing agent such as potassium chlorate, sulfuric acid, nitric acid (HNO 3 ), persulfate, hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3
- Breaking up of the as-produced aggregates into individual carbon nanotubes is preferable (although not necessary) in order to permit a more thorough distribution of functional groups onto the carbon nanotube surfaces, as well as to easier facilitate the creation of the carbon nanotube network structures.
- oxidizing agents when oxidizing agents are used, the terms “functionalized” and “oxidized” may be used interchangably.
- the carbon nanotubes are oxidized by contacting the nanotubes with ozone under conditions suitable to achieve the desired functionalization (and deaggregation in the case of carbon nanotubes which are in the form of aggregates). Further details are provided in U.S. Provisional Application No. 60/621,132, filed Oct. 22, 2004 entitled “OZONOLYSIS OF CARBON NANOTUBES,” herein incorporated by reference.
- a particularly useful functionalization method especially for single wall tubes is cycloaddition. See, for example, Holzinger, M., et al., “[2+1] cycloaddition for cross linking SWCNTs”, Carbon 42 (2004) 941-947, and Georgakilas, V., etal., “Organic Functionalization of Carbon Nanotubes”, JACS Communications, 124 (2002) 760,761, both of which are hereby included by reference.
- single wall tubes can be functionalized as described in U.S. Ser. No. 10/875,435 filed Jun. 23, (2004), hereby incorporated by reference.
- the functional groups which remain after the deposition or loading of the metal catalyst permit the individual carbon nanotubes to form carbon nanotube network structures with a linking molecule between the functionalized groups located on the surface of the carbon nanotubes.
- a linking molecule between the functionalized groups located on the surface of the carbon nanotubes E.g., PCT/US97/03553 or WO 97/32571, hereby incorporated by reference.
- Preferred metal catalysts include ruthenium, osmium, rhodium, iridium, palladium, platinum or a mixture thereof, as well as metal oxides, metal halides, metal carbides, metal nitrides, metal phosphides and metal sulfides of other transition metals including Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Y, Zr, Nb, Mo, La, Ce, W or combination thereof. More preferably, the metal catalyst is palladium, platinum, or a mixture thereof.
- predeposition or loading of the metal catalyst onto the carbon nanotube surface can be accomplished by mixing the metal catalyst material with the carbon nanotubes. Due to the change in carbon nanotube surface chemistry caused by the presence of functional groups, the metal catalyst may be held or supported onto the carbon nanotube surface via adsorption, hydrogen bond, adhesion, electrostatic attraction, covalent bond, absorption, van der Waals force or any other mechanism which may occur to secure, support, hold or otherwise keep the metal catalyst onto the carbon nanotube surface.
- the functional groups are used to subsequently link the individual nanotubes to form carbon nanotube structures, that the amount of metal deposited or loaded onto the carbon nanotube surface not exceed or otherwise “use up” the functional groups needed to hold or support the metal catalyst on the carbon nanotube surface. In other words, it is preferred that there be free functional groups remaining on the carbon nanotube surface after the predeposition or loading of the metal catalyst.
- the metal catalysts can be introduced to the carbon nanotubes in the form of a salt or derivative, or in the form of metal-containing micelles. As discussed earlier, these forms are often referred to as precursors of the metal catalyst, but are included in the term metal catalysts as used in this application.
- the metal can be introduced to the carbon nanotube in the form of a water-soluble salt such as nitrate, acetate or chloride.
- Metal catalysts which have been loaded onto the carbon nanotube as salts are then preferably reduced via a reducing agent to further accomplish the deposition of the metal catalyst onto the carbon nanotube surface.
- any conventional mixing devices or mechanism can be employed. Factors such as mixing speed or time can be adjusted accordingly to facilitate the contact of the carbon nanotube and the metal catalyst, and to spread the metal catalyst thoroughly throughout the mixture so as to create a better distribution of metal catalysts on the carbon nanotubes.
- Additional methods for accomplishing predeposition of the metal catalyst onto the carbon nanotube surface include, but is not limited to, impregnation, incipient wetness, ion exchange, precipitation, physical or chemical adsorption and co-precipitation.
- Carbon nanotubes which have metal catalysts deposited on them will be referred to as “predeposited carbon nanotubes” or “metal loaded carbon nanotubes.”
- these metal loaded carbon nanotubes are then used to form the carbon nanotube network structures using conventional methods as previously described.
- the metal loaded carbon nanotubes are functionalized, for example, by contacting them with an appropriate reagent such as those described in WO 97/32571 or U.S. Pat. No. 6,203,814, all of which are incorporated by reference.
- the metal loaded carbon nanotubes are functionalized through oxidation with oxidizing agents such as potassium chlorate (KClO 3 ), sulfuric acid (H 2 SO 4 ), nitric acid (HNO 3 ), hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , ClO 2 , etc.
- Typical linking molecules are bifunctional compounds such as diamines, diols, etc.
- the metal catalysts have already been deposited, spread and distributed throughout the carbon nanotubes in its discrete form prior to creating the carbon nanotube network structure, the result is that the carbon nanotube network structure itself would also have a greater and/or more even distribution of metal catalyst throughout and within the network structure.
- the porosity characteristics e.g., more meso and macropores
- the accessibility and availability of the metal catalyst for reactions is greater than in other support catalyst structures previously prepared. This availability improvement is especially significant for liquid phase reactions, where larger pores are needed in order for the liquid phase reactants to reach the internal metal catalysts.
- the carbon nanotube structures may be formed first before loading the metal catalyst.
- the carbon nanotubes are functionalized, for example, by contacting them with an appropriate reagent such as those described in WO 97/32571 or U.S. Pat. No. 6,203,814, all of which are incorporated by reference.
- the carbon nanotubes are functionalized through oxidation with oxidizing agents such as potassium chlorate (KClO 3 ), sulfuric acid (H 2 SO 4 ), nitric acid (HNO 3 ), hydrogen peroxide (H 2 O 2 ), CO 2 , O 2 , steam, N 2 O, NO, NO 2 , O 3 , CO 2 , etc. (e.g., U.S. Pat. No.
- Linking molecules such as bifunctional compounds such as diamines, diols, etc. are then added to form the carbon nanotube network structure.
- the metal catalyst are loaded onto the carbon nanotube network structure using any of the loading/deposition processes previously discussed (e.g., ion exchange, impregnation, or incipient wetness, precipitation, physical or chemical adsorption or co-precipitation, etc.)
- catalytic compositions can be used as catalysts to catalyze reactions such as hydrogenation, hydrodesulfurisation, hydrodenitrogenation, hydrodemetallisation, hydrodeoxygenation, hydrodearomatization, dehydrogenation, hydrogenolysis, isomerization, alkylation, dealkylation, transalkylation, hydroformylation, water-gas shift, Fischer-Tropsch, COx-free hydrogen production, ammonia synthesis, electrocatalysis, oxidation, florination, and NO x reduction.
- reactions such as hydrogenation, hydrodesulfurisation, hydrodenitrogenation, hydrodemetallisation, hydrodeoxygenation, hydrodearomatization, dehydrogenation, hydrogenolysis, isomerization, alkylation, dealkylation, transalkylation, hydroformylation, water-gas shift, Fischer-Tropsch, COx-free hydrogen production, ammonia synthesis, electrocatalysis, oxidation, florination, and NO x reduction.
- a covalently linked, carbon nanotube network is prepared by coupling a plurality of nanotubes together with molecules of a polyfunctional linker.
- the linker can have two or more reactive groups that are either the same or different such that at least one functional group on a linker molecule will react with one nanotube and at least a second functional group on the same linker molecule can react with a second nanotube thereby covalently linking the two nanotubes together.
- the functional groups on the polyfunctional linker can be the same or different and can be selected to react directly with an unfunctionalized nanotubes or selected to react with functional groups already present on the nanotubes.
- Carbon nanotubes with carboxyl functional groups are linked using a diamine linker.
- Carbon nanotubes are slurried in 6M nitric acid in a two-necked, round bottom flask.
- the flask is fitted with a condenser with a water jacket in one neck and an overhead stirrer with a Teflon blade in another neck.
- the slurry is set to stirring and heated to reflux for 1-24 hours during which the nanotubes are oxidized forming carboxyl and other oxygen containing functional groups.
- the degree of functionalization is assayed by acid base titration.
- the carboxyl groups may be predominantly on the ends of the nanotubes or, especially in the case of MWNT, at sites on the sidewalls of the nanotubes.
- Carboxylated nanotubes are activated to an N-hydroxysuccinimide (NHS) ester by carbodiimide coupling using 1-ethyl-3(3-dimethylaminopropyl)-carbodiimide.
- NHS N-hydroxysuccinimide
- the nanotubes are then washed with dioxane and methanol then dried under vacuum to yield NHS ester-activated nanotubes.
- NHS ester-activated nanotubes are cross-linked by the diamine, ethylenediamine, by adding ethylenediamine in 0.2M NaHCO 3 to form a concentrated slurry or paste to maintain a large number of nanotube to nanotube contacts where linkage can take place.
- the linking reaction is carried out for 4 hours at room temperature.
- the resulting linked network of nanotubes is washed with water, methanol, ethyl acetate, methanol, water and sodium bicarbonate (0.2 M, pH 8.0).
- the filter cake can form either a mat via filtration or extrudate via extrusion as disclosed elsewhere.
- Functionalized carbon nanotubes contain a variety of diverse functional groups, i.e. anionic (e.g. —SO 3 H, —COOH), cationic (e.g. —N(R 1 , R 2 , R 3 ) + or more or less complex organic groups like amino, amide, ester, nitrile, epoxy or other reactive centers.
- anionic e.g. —SO 3 H, —COOH
- cationic e.g. —N(R 1 , R 2 , R 3 ) + or more or less complex organic groups like amino, amide, ester, nitrile, epoxy or other reactive centers.
- Preparation of a metal loaded carbon nanotube composite can then be carried out by the preparation of functionalized carbon nanotubes, metallation either by ion-exchange or impregnation with a metal compound and the reduction of metal compound to metallic state.
- Metal catalyst can also be pre-deposited on functionalized carbon nanotubes via ion-exchange or impregnation pathways.
- a Pd catalysts supported on carbon nanotubes is prepared by incipient wetness impregnation. First, 10 grams of CC-type carbon nanotubes are placed in a 250-cc round bottom flask and oxidized by 63% nitric acid under reflux condition for four hours. After thorough washing with de-ionized water, the oxidized nanotubes are impregnated with Pd(NO 3 ) 2 /acetone solution to yield a metal loading of 5%.
- Pd-loaded nanotubes are then activated to an N-hydroxysuccinimide (NHS) ester by carbodiimide coupling using 1-ethyl-3(3-dimethylaminopropyl)-carbodiimide.
- NHS N-hydroxysuccinimide
- the product is then washed with dioxane and methanol then dried under vacuum to yield NHS ester-activated nanotubes.
- NHS ester-activated nanotubes are cross-linked by the diamine, ethylenediamine, by adding ethylenediamine in 0.2M NaHCO 3 to form a concentrated slurry or paste to maintain a large number of nanotube to nanotube contacts where linkage can take place.
- the linking reaction is carried out for 4 hours at room temperature.
- the resulting linked network of nanotubes is washed with water, methanol, ethyl acetate, methanol, water and sodium bicarbonate (0.2 M, pH 8.0).
- the filter cake can form either a mat via filtration or extrudate via extrusion as disclosed elsewhere.
- Hydrogenation of nitrobenzene is generally agreed as a strong exothermic reaction and very fast on many metals.
- the process is usually limited by diffusion.
- carbon nanotube network serves as a catalyst support, the diffusion limitation created by micropores of amorphous carbon when activated carbon was used as support is eliminated.
- Such catalyst provides a better performance when compared with a conventional activated carbon or carbon black supported catalyst.
- the reaction is carried out at ambient temperature and pressure in a three-neck round bottom flask with overhead stirrer. 0.050 g of catalyst made from Example 2 is placed in the flask with 50 ml isopropanol. Before adding the reactant, the catalyst is in-situ reduced by bubbling hydrogen for two hours under agitation. 50 ml of 10 vol % nitrobenzene in 2-propanol is added to the slurry. Small amount of sample is taken out every 30 min (every 15 min in the first 45 min) by using a syringe equipped with a filter until nitrobenzene consumed completely, which is determined by a GC equipped with FID and 3% OV-17/Chromosorb W-HP column. The conversion of nitrobenzene is found to reach 100% after 180 minutes.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Organic Chemistry (AREA)
- Materials Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Nanotechnology (AREA)
- Condensed Matter Physics & Semiconductors (AREA)
- Physics & Mathematics (AREA)
- General Physics & Mathematics (AREA)
- Crystallography & Structural Chemistry (AREA)
- Composite Materials (AREA)
- Manufacturing & Machinery (AREA)
- Inorganic Chemistry (AREA)
- Catalysts (AREA)
- Carbon And Carbon Compounds (AREA)
- Low-Molecular Organic Synthesis Reactions Using Catalysts (AREA)
- Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US11/281,811 US20060142148A1 (en) | 2004-11-16 | 2005-11-16 | Methods for preparing catalysts supported on carbon nanotube networks |
US11/841,733 US7923403B2 (en) | 2004-11-16 | 2007-08-20 | Method for preparing catalysts supported on carbon nanotubes networks |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US62846904P | 2004-11-16 | 2004-11-16 | |
US11/281,811 US20060142148A1 (en) | 2004-11-16 | 2005-11-16 | Methods for preparing catalysts supported on carbon nanotube networks |
Related Child Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/841,733 Continuation US7923403B2 (en) | 2004-11-16 | 2007-08-20 | Method for preparing catalysts supported on carbon nanotubes networks |
US11/841,733 Continuation-In-Part US7923403B2 (en) | 2004-11-16 | 2007-08-20 | Method for preparing catalysts supported on carbon nanotubes networks |
Publications (1)
Publication Number | Publication Date |
---|---|
US20060142148A1 true US20060142148A1 (en) | 2006-06-29 |
Family
ID=36407734
Family Applications (3)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/281,811 Abandoned US20060142148A1 (en) | 2004-11-16 | 2005-11-16 | Methods for preparing catalysts supported on carbon nanotube networks |
US11/281,814 Abandoned US20060142149A1 (en) | 2004-11-16 | 2005-11-16 | Method for preparing supported catalysts from metal loaded carbon nanotubes |
US11/841,359 Expired - Fee Related US7968489B2 (en) | 2004-11-16 | 2007-08-20 | Methods of preparing supported catalysts from metal loaded carbon nanotubes |
Family Applications After (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US11/281,814 Abandoned US20060142149A1 (en) | 2004-11-16 | 2005-11-16 | Method for preparing supported catalysts from metal loaded carbon nanotubes |
US11/841,359 Expired - Fee Related US7968489B2 (en) | 2004-11-16 | 2007-08-20 | Methods of preparing supported catalysts from metal loaded carbon nanotubes |
Country Status (10)
Country | Link |
---|---|
US (3) | US20060142148A1 (zh) |
EP (2) | EP1828447B1 (zh) |
JP (2) | JP2008520413A (zh) |
CN (2) | CN101098991B (zh) |
AT (2) | ATE482029T1 (zh) |
CA (2) | CA2588124A1 (zh) |
DE (2) | DE602005023777D1 (zh) |
DK (2) | DK1828447T3 (zh) |
MX (2) | MX2007005797A (zh) |
WO (2) | WO2006060168A2 (zh) |
Cited By (33)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060223243A1 (en) * | 2005-03-30 | 2006-10-05 | Marko Radosavljevic | Carbon nanotube - metal contact with low contact resistance |
US20070274899A1 (en) * | 2006-05-23 | 2007-11-29 | Bayer Material Science Ag | Temperature-stable catalysts for gas phase oxidation, and processes for using the same |
US20080039315A1 (en) * | 2004-11-16 | 2008-02-14 | Jun Ma | Methods of preparing supported catalysts from metal loaded carbon nanotubes |
WO2008127396A2 (en) * | 2006-11-02 | 2008-10-23 | Ohio University | A solution synthesis of carbon nanotube/metal-containing nanoparticle conjugated assemblies |
WO2009078815A1 (en) * | 2007-12-14 | 2009-06-25 | Nanyang Technological University | A nanostructured material loaded with noble metal particles |
WO2009149849A1 (de) * | 2008-06-12 | 2009-12-17 | Bayer Technology Services Gmbh | Katalysator und verfahren zur hydrierung von organischen verbindungen |
US20100124713A1 (en) * | 2008-11-17 | 2010-05-20 | Xerox Corporation | Toners including carbon nanotubes dispersed in a polymer matrix |
US20110229777A1 (en) * | 2008-09-08 | 2011-09-22 | Wai Fatt Mak | Electrode materials for metal-air batteries, fuel cells and supercapacitators |
US20120016167A1 (en) * | 2010-07-15 | 2012-01-19 | Exxonmobil Research And Engineering Company | Hydroprocessing of biocomponent feeds with low pressure hydrogen-containing streams |
WO2012078384A1 (en) | 2010-12-09 | 2012-06-14 | Eastman Chemical Company | Process for the preparation of 2,2,4,4-tetraalkylcyclobutane-1,3-diols |
WO2012078439A1 (en) | 2010-12-09 | 2012-06-14 | Eastman Chemical Company | Process for the isomerization of 2,2,4,4-tetraalkylcyclobutane-1,3-diols |
US20120329640A1 (en) * | 2011-06-23 | 2012-12-27 | Designed Nanotubes, LLC | Nanoplate-nanotube composites, methods for production thereof and products obtained therefrom |
US20140030171A1 (en) * | 2012-07-27 | 2014-01-30 | Ripi | Nanocatalyst and Process for Removing Sulfur Compounds from Hydrocarbons |
JP2014505580A (ja) * | 2010-11-03 | 2014-03-06 | マサチューセッツ インスティテュート オブ テクノロジー | 官能化炭素ベースのナノ構造物を含む組成物および関連する方法 |
US20150041722A1 (en) * | 2012-03-12 | 2015-02-12 | Kunming University Of Science And Technology | Process For Purifying Tail Gas From Ore-Smelting Electrical Furnace by Catalytic Oxidization |
US9142376B2 (en) | 2012-08-22 | 2015-09-22 | National Defense University | Method for fabricating field emission cathode, field emission cathode thereof, and field emission lighting source using the same |
US20150290620A1 (en) * | 2012-11-16 | 2015-10-15 | University Of Bath | Catalyst comprising iron and carbon nanotubes |
US9238603B1 (en) | 2014-12-10 | 2016-01-19 | Eastman Chemical Company | Batch process for the preparation of cis-2,2,4,4-tetramethylcyclobutane-1,3-diol |
US9238602B1 (en) | 2014-12-10 | 2016-01-19 | Eastman Chemical Company | Process for the preparation of cis-2,2,4,4-tetramethylcyclobutane-1,3-diol |
US9267908B2 (en) | 2008-03-04 | 2016-02-23 | Massachusetts Institute Of Technology | Devices and methods for determination of species including chemical warfare agents |
RU2624004C2 (ru) * | 2012-08-22 | 2017-06-30 | Рисерч Инститьют Питроулеум Индастри (Рипи) | Нанокатализатор и способ для удаления соединений серы из углеводородов |
US9997785B2 (en) | 2011-06-23 | 2018-06-12 | Molecular Rebar Design, Llc | Nanoplate-nanotube composites, methods for production thereof and products obtained therefrom |
CN108310969A (zh) * | 2018-02-26 | 2018-07-24 | 江苏中科纳特环境科技有限公司 | 一种室外空气净化模块和净化方法 |
EP3317380A4 (en) * | 2015-06-30 | 2019-03-06 | Hindustan Petroleum Corporation Ltd. | SUPPORTED CATALYST FOR REFINERY RESIN CHILLING PHASE HYDROCRACKING AND PREPARATION METHOD THEREOF |
CN110577208A (zh) * | 2019-08-18 | 2019-12-17 | 复旦大学 | 一种亲钠性导电碳纳米管骨架材料及其制备方法和应用 |
CN110961093A (zh) * | 2018-09-28 | 2020-04-07 | 中国石油化工股份有限公司 | Cr-Zr-O/TiO2-C纳米管催化剂及其制备方法和应用 |
CN112108139A (zh) * | 2020-09-29 | 2020-12-22 | 西安凯立新材料股份有限公司 | 一种硝基苯液相加氢合成苯胺用催化剂及其制备方法 |
CN113101934A (zh) * | 2021-04-19 | 2021-07-13 | 天津大学 | 一种负载原子级分散金属的碳纳米管催化剂的制备方法及应用 |
US11079387B2 (en) * | 2018-04-12 | 2021-08-03 | Zahra Borzooeian | Length-based carbon nanotube ladders |
US11167247B2 (en) | 2017-02-15 | 2021-11-09 | Nanolc-12, Llc | Length-based separation of carbon nanotubes |
US11353424B2 (en) | 2018-04-12 | 2022-06-07 | Nano LC-12, LLC | Length-based carbon nanotube ladders |
CN115254089A (zh) * | 2022-07-21 | 2022-11-01 | 湖北展鹏电子材料有限公司 | 一种碳纳米管基-TiO2复合纳米材料及其制备方法和应用 |
US11505467B2 (en) | 2017-11-06 | 2022-11-22 | Massachusetts Institute Of Technology | High functionalization density graphene |
Families Citing this family (83)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20100021800A1 (en) * | 2008-07-24 | 2010-01-28 | Rachid Yazami | Carbon cathodes for fluoride ion storage |
US8143189B2 (en) * | 2008-03-12 | 2012-03-27 | Uchicago Argonne, Llc | Subnanometer and nanometer catalysts, method for preparing size-selected catalysts |
JP3974646B2 (ja) * | 2004-07-06 | 2007-09-12 | 三菱商事株式会社 | 微細炭素繊維・金属複合材料及びその製造方法 |
JP4019123B2 (ja) * | 2004-09-06 | 2007-12-12 | 三菱商事株式会社 | 炭素繊維Ti−Al複合材料及びその製造方法 |
US7923403B2 (en) * | 2004-11-16 | 2011-04-12 | Hyperion Catalysis International, Inc. | Method for preparing catalysts supported on carbon nanotubes networks |
WO2006065431A2 (en) * | 2004-11-17 | 2006-06-22 | Hyperion Catalysis International, Inc. | Method for preparing catalyst supports and supported catalysts from single walled carbon nanotubes |
WO2008051239A2 (en) * | 2005-11-16 | 2008-05-02 | Hyperion Catalysis International, Inc. | Mixed structures of single walled and multi walled carbon nanotubes |
US20070161501A1 (en) * | 2006-01-10 | 2007-07-12 | Atomic Energy Council - Institute Of Nuclear Energy Research | Method for making carbon nanotube-supported platinum alloy electrocatalysts |
KR20080092983A (ko) * | 2006-02-07 | 2008-10-16 | 프레지던트 앤드 펠로우즈 오브 하바드 칼리지 | 탄소나노튜브의 기상 기능화 |
US8119032B2 (en) | 2006-02-07 | 2012-02-21 | President And Fellows Of Harvard College | Gas-phase functionalization of surfaces including carbon-based surfaces |
US8940332B2 (en) | 2006-05-18 | 2015-01-27 | Nippon Kayaku Kabushiki Kaisha | High-molecular weight conjugate of podophyllotoxins |
US20080020924A1 (en) * | 2006-07-19 | 2008-01-24 | Atomic Energy Council-Institute Of Nuclear Energy Research | Method of fabricating platinum alloy electrocatalysts for membrane fuel cell applications |
CA2664852A1 (en) * | 2006-10-03 | 2008-04-10 | Nippon Kayaku Kabushiki Kaisha | High-molecular weight conjugate of resorcinol derivatives |
US7770646B2 (en) * | 2006-10-09 | 2010-08-10 | World Energy Systems, Inc. | System, method and apparatus for hydrogen-oxygen burner in downhole steam generator |
US7712528B2 (en) * | 2006-10-09 | 2010-05-11 | World Energy Systems, Inc. | Process for dispersing nanocatalysts into petroleum-bearing formations |
JP5194455B2 (ja) * | 2007-01-22 | 2013-05-08 | 三菱化学株式会社 | 気相成長炭素繊維製造用触媒及び気相成長炭素繊維 |
US20080213367A1 (en) * | 2007-03-01 | 2008-09-04 | Cromoz Inc. | Water soluble concentric multi-wall carbon nano tubes |
JP5349318B2 (ja) | 2007-09-28 | 2013-11-20 | 日本化薬株式会社 | ステロイド類の高分子結合体 |
WO2009116509A1 (ja) | 2008-03-18 | 2009-09-24 | 日本化薬株式会社 | 生理活性物質の高分子結合体 |
JP5453732B2 (ja) * | 2008-05-06 | 2014-03-26 | 株式会社豊田自動織機 | 触媒前駆体、触媒材料およびそれらの製造方法 |
WO2009136572A1 (ja) | 2008-05-08 | 2009-11-12 | 日本化薬株式会社 | 葉酸若しくは葉酸誘導体の高分子結合体 |
WO2010005548A2 (en) * | 2008-07-07 | 2010-01-14 | Northwestern University | Functionalization of carbon nanotubes with metallic moieties |
KR20130081294A (ko) * | 2008-08-29 | 2013-07-16 | 엑손모빌 케미칼 패턴츠 인코포레이티드 | 페놀 제조 방법 |
US9099253B2 (en) * | 2008-10-21 | 2015-08-04 | Brookhaven Science Associates, Llc | Electrochemical synthesis of elongated noble metal nanoparticles, such as nanowires and nanorods, on high-surface area carbon supports |
EP2196260A1 (en) * | 2008-12-02 | 2010-06-16 | Research Institute of Petroleum Industry (RIPI) | Hydrodesulphurization nanocatalyst, its use and a process for its production |
CN102421827B (zh) | 2009-05-15 | 2014-07-30 | 日本化药株式会社 | 具有羟基的生理活性物质的高分子结合体 |
KR101038750B1 (ko) * | 2009-05-20 | 2011-06-03 | 한국에너지기술연구원 | 탄소나노튜브의 내부 채널에 금속촉매 나노입자가 담지된 탄소나노튜브 촉매 및 이의 제조방법 |
CN101920195B (zh) * | 2009-06-09 | 2012-09-05 | 中国石油化工股份有限公司 | 一种以纳米碳纤维为载体的对苯二甲酸加氢精制催化剂的制备方法 |
CN102471698A (zh) * | 2009-07-17 | 2012-05-23 | 埃克森美孚研究工程公司 | 用fcc废气加氢处理生物组分原料 |
US8387692B2 (en) * | 2009-07-17 | 2013-03-05 | World Energy Systems Incorporated | Method and apparatus for a downhole gas generator |
CN102039121B (zh) | 2009-10-21 | 2013-06-05 | 中国科学院大连化学物理研究所 | 一种铂/碳纳米管催化剂及制法和应用 |
US8853474B2 (en) * | 2009-12-29 | 2014-10-07 | Exxonmobil Research And Engineering Company | Hydroprocessing of biocomponent feedstocks with low purity hydrogen-containing streams |
US9242227B2 (en) | 2010-02-05 | 2016-01-26 | Exxonmobil Chemical Patents Inc. | Dehydrogenation catalyst and process |
WO2011096999A2 (en) | 2010-02-05 | 2011-08-11 | Exxonmobil Chemical Patents Inc. | Cyclohexanone dehydrogenation catalyst and process |
US20110207972A1 (en) * | 2010-02-23 | 2011-08-25 | Battelle Memorial Institute | Catalysts and processes for the hydrogenolysis of glycerol and other organic compounds for producing polyols and propylene glycol |
CA2792597C (en) | 2010-03-08 | 2015-05-26 | World Energy Systems Incorporated | A downhole steam generator and method of use |
CA2712051A1 (en) * | 2010-08-12 | 2012-02-12 | The Governors Of The University Of Alberta | Method of fabricating a carbon nanotube array |
CN101814345B (zh) * | 2010-05-22 | 2011-09-14 | 西南交通大学 | 一种疏松的三维立体宏观碳纳米管网的制备方法 |
SG10201503888PA (en) | 2010-06-25 | 2015-06-29 | Exxonmobil Chem Patents Inc | Dehydrogenation process |
FR2962140B1 (fr) * | 2010-07-05 | 2012-08-17 | Centre Nat Rech Scient | Procede de formation d'un depot metallique a la surface d'un substrat et applications |
US20120115692A1 (en) * | 2010-11-04 | 2012-05-10 | Daryl Bussen | Stable Exercise Apparatus |
CA2816997A1 (en) | 2010-11-17 | 2012-05-24 | Nippon Kayaku Kabushiki Kaisha | Novel polymer derivative of cytidine metabolic antagonist |
CN102688744A (zh) * | 2011-03-24 | 2012-09-26 | 长江大学 | 一种载铈活性炭的制备方法 |
EP2514524A1 (en) * | 2011-04-21 | 2012-10-24 | Research Institute of Petroleum Industry (RIPI) | Nanocatalyst and process for removing sulfur compounds from hydrocarbons |
JP5765709B2 (ja) * | 2011-07-15 | 2015-08-19 | 国立研究開発法人物質・材料研究機構 | アミン官能化メソ細孔カーボンナノケージおよびその製造方法 |
BR112014005452B1 (pt) | 2011-09-11 | 2021-03-16 | Nippon Kayaku Kabushiki Kaisha | método de produção de copolímero de bloco |
US20150175876A1 (en) * | 2011-10-03 | 2015-06-25 | The Board Of Regents Of The University Of Oklahoma | Method and foam composition for recovering hydrocarbons from a subterranean reservoir |
US8912525B2 (en) | 2011-12-16 | 2014-12-16 | International Business Machines Corporation | Chemical oxidation of graphene and carbon nanotubes using Cerium (IV) ammonium nitrate |
US9663369B2 (en) | 2011-12-16 | 2017-05-30 | International Business Machines Corporation | Cerium (IV) salts as effective dopant for carbon nanotubes and graphene |
EP2634290A1 (en) * | 2012-02-28 | 2013-09-04 | Fritz Haber Institute of the Max Planck Society Department of Inorganic Chemistry | Electrolytic water splitting using a carbon-supported MnOx-composite |
US20130256123A1 (en) | 2012-04-02 | 2013-10-03 | King Abdulaziz City For Science And Technology | Electrocatalyst for electrochemical conversion of carbon dioxide |
WO2013152144A1 (en) | 2012-04-05 | 2013-10-10 | The Research Foundation Of State University Of New York | Three-dimensional carbon structures |
CN102856611B (zh) * | 2012-04-09 | 2015-02-04 | 中南大学 | 一种锂空气电池用微纳结构正极材料 |
DE102012209634A1 (de) * | 2012-06-08 | 2013-12-12 | Leibniz-Institut Für Katalyse E.V. An Der Universität Rostock | Verwendung von thermisch behandelten geträgerten Kobaltkatalysatoren zur Hydrierung von Nitroaromaten |
ES2907515T3 (es) | 2012-10-16 | 2022-04-25 | Martin Bakker | Catálisis por nanopartículas metálicas dispersas en un material de carbono jerárquicamente poroso |
CN103007965B (zh) * | 2013-01-11 | 2014-08-13 | 南京大学 | 一种钛基碳纳米管负载铜钯双金属催化剂及其制备方法 |
JP6135166B2 (ja) * | 2013-02-13 | 2017-05-31 | 日本ゼオン株式会社 | 酸化還元触媒、電極材料、電極、太陽電池、燃料電池、および窒素酸化物除去触媒 |
CN103691428A (zh) * | 2013-12-26 | 2014-04-02 | 大连大学 | 一种炭载贵金属催化剂的制备方法 |
KR101614283B1 (ko) | 2014-07-08 | 2016-04-21 | 전북대학교 산학협력단 | Cnt-pzt 나노입자 복합체, 그를 이용한 압전소자 및 그의 제조방법 |
CN104437358B (zh) * | 2014-10-20 | 2015-09-23 | 深圳市富可森机械设备有限公司 | 一种同时吸附废气中重金属离子和挥发性有机物的复合吸附材料的制备方法 |
CN104258689B (zh) * | 2014-10-20 | 2015-09-16 | 浙江文国重工机械有限公司 | 一种同时吸附废气中重金属离子和挥发性有机物的吸附柱 |
CN104437537A (zh) * | 2014-11-18 | 2015-03-25 | 福州大学 | 抗二氧化硫型低温锰-铁氧化物脱硝催化剂及其制备方法 |
CN105694009A (zh) * | 2014-11-25 | 2016-06-22 | 上海凯众材料科技股份有限公司 | 锆/铈-蒙脱土复合催化剂和聚酯二元醇的制备方法 |
CN104594021A (zh) * | 2015-02-13 | 2015-05-06 | 武汉大学 | 基于软硬酸碱理论的巯基棉后修饰材料及其制备与应用 |
WO2017024421A1 (zh) * | 2015-08-12 | 2017-02-16 | 华北电力大学(保定) | 一种多壁纳米碳管催化剂及其制备方法和应用 |
SG10202005661YA (en) * | 2016-01-14 | 2020-07-29 | Agency Science Tech & Res | Free-standing mof-derived hybrid porous carbon nanofiber mats |
US10195587B2 (en) | 2016-03-04 | 2019-02-05 | The Board Of Trustees Of The University Of Alabama | Synthesis of hierarchically porous monoliths by a co-gelation method |
CN106215949A (zh) * | 2016-08-02 | 2016-12-14 | 上海应用技术学院 | 一种低温选择性催化还原脱硝催化剂及其制备方法 |
CN106423233A (zh) * | 2016-09-12 | 2017-02-22 | 天津大学 | 过渡金属磷化物催化剂及制备方法及在愈创木酚氢解反应中的应用 |
CN109304199B (zh) * | 2017-07-28 | 2022-03-11 | 中国石油化工股份有限公司 | 一种含杂原子纳米碳材料及其制备方法以及一种硫醚氧化方法 |
CN108377638A (zh) * | 2018-03-06 | 2018-08-07 | 南京航空航天大学 | 一种Co/C复合电磁吸波剂及其制备方法 |
CN110586153A (zh) * | 2019-08-27 | 2019-12-20 | 浙江工业大学 | 碳纳米管内嵌金属粒子催化剂在氨分解反应中的应用 |
CN111545219B (zh) * | 2020-05-01 | 2023-04-28 | 陕西元亨医药科技有限责任公司 | 一种催化剂及其制备方法 |
CN111924826B (zh) * | 2020-07-22 | 2022-05-27 | 中国科学院金属研究所 | 一种窄直径分布、高纯度金属性单壁碳纳米管的制备方法 |
EP3988207A1 (en) | 2020-10-22 | 2022-04-27 | Bestrong International Limited | Supported metal structure |
CN113151856B (zh) * | 2021-04-20 | 2023-03-28 | 中国矿业大学 | 一种高熵合金磷化物纳米粒子催化剂的制备及其在电解水制氢中的应用 |
CN113368857B (zh) * | 2021-04-29 | 2022-08-12 | 中国环境科学研究院 | 体相金属间化合物负载催化剂的制备方法 |
WO2023077130A1 (en) * | 2021-11-01 | 2023-05-04 | Cdti Advanced Materials Inc. | Electrocatalyst, method of making the electrocatalyst, and systems including the electrocatalyst |
CN114797826A (zh) * | 2022-04-29 | 2022-07-29 | 西安工业大学 | 一种含碳纳米管双活性脱硫剂的制备方法 |
CN115282959B (zh) * | 2022-07-26 | 2024-02-27 | 万华化学集团股份有限公司 | 一种碳纳米管负载的Ru-Nb-Ce三金属催化剂、方法及其在制备椰子醛中的应用 |
CN116002842B (zh) * | 2022-12-22 | 2024-04-12 | 昆明理工大学 | 碳纳米管负载型催化剂活化过氧乙酸降解卡马西平的方法 |
CN115845840A (zh) * | 2022-12-23 | 2023-03-28 | 辽宁大学 | 一种石墨烯负载原子级分散钯基催化剂及其制备方法和应用 |
CN117107388B (zh) * | 2023-09-27 | 2024-03-26 | 东莞信鸿工程塑料有限公司 | 一种抗菌阻燃聚酰胺纤维材料及其制备方法 |
Citations (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4666230A (en) * | 1984-12-27 | 1987-05-19 | Microwave Systems & Technology, Inc. | Coaxial cable connector assembly |
US5165909A (en) * | 1984-12-06 | 1992-11-24 | Hyperion Catalysis Int'l., Inc. | Carbon fibrils and method for producing same |
US5171560A (en) * | 1984-12-06 | 1992-12-15 | Hyperion Catalysis International | Carbon fibrils, method for producing same, and encapsulated catalyst |
US5456987A (en) * | 1993-10-27 | 1995-10-10 | Xerox Corporation | Intermediate transfer component coatings of titamer and grafted titamer |
US5500200A (en) * | 1984-12-06 | 1996-03-19 | Hyperion Catalysis International, Inc. | Fibrils |
US5569635A (en) * | 1994-05-22 | 1996-10-29 | Hyperion Catalysts, Int'l., Inc. | Catalyst supports, supported catalysts and methods of making and using the same |
US5691054A (en) * | 1993-05-05 | 1997-11-25 | Hyperion Catalysis Int'l., Inc. | Three dimensional macroscopic assemblages of randomly oriented carbon fibrils and composites containing same |
US5707916A (en) * | 1984-12-06 | 1998-01-13 | Hyperion Catalysis International, Inc. | Carbon fibrils |
US5965470A (en) * | 1989-05-15 | 1999-10-12 | Hyperion Catalysis International, Inc. | Composites containing surface treated carbon microfibers |
US6031711A (en) * | 1996-05-15 | 2000-02-29 | Hyperion Catalysis International, Inc. | Graphitic nanofibers in electrochemical capacitors |
US6099965A (en) * | 1996-05-15 | 2000-08-08 | Hyperion Catalysis International, Inc. | Rigid porous carbon structures, methods of making, methods of using and products containing same |
US6143689A (en) * | 1992-05-22 | 2000-11-07 | Hyperion Catalysis Int'l Inc. | Methods and catalysts for the manufacture of carbon fibrils |
US6203814B1 (en) * | 1994-12-08 | 2001-03-20 | Hyperion Catalysis International, Inc. | Method of making functionalized nanotubes |
US6333016B1 (en) * | 1999-06-02 | 2001-12-25 | The Board Of Regents Of The University Of Oklahoma | Method of producing carbon nanotubes |
US20020121460A1 (en) * | 1999-01-12 | 2002-09-05 | David Moy | Method of using carbide and/or oxycarbide containing compositions |
US20030039604A1 (en) * | 2001-05-18 | 2003-02-27 | Chunming Niu | Modification of nanotubes oxidation with peroxygen compounds |
US20030181526A1 (en) * | 2002-03-20 | 2003-09-25 | Bradley Pharmaceuticals, Inc. | Method of treating onychomycosis |
US6761870B1 (en) * | 1998-11-03 | 2004-07-13 | William Marsh Rice University | Gas-phase nucleation and growth of single-wall carbon nanotubes from high pressure CO |
Family Cites Families (28)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4663230A (en) | 1984-12-06 | 1987-05-05 | Hyperion Catalysis International, Inc. | Carbon fibrils, method for producing same and compositions containing same |
AU3182189A (en) | 1988-01-28 | 1989-08-25 | Hyperion Catalysis International | Carbon fibrils |
ZA907803B (en) | 1989-09-28 | 1991-07-31 | Hyperion Catalysis Int | Electrochemical cells and preparing carbon fibrils |
AU653500B2 (en) | 1989-09-28 | 1994-10-06 | Hyperion Catalysis International, Inc. | Battery |
US5424054A (en) | 1993-05-21 | 1995-06-13 | International Business Machines Corporation | Carbon fibers and method for their production |
JPH07102120A (ja) | 1993-09-10 | 1995-04-18 | Hyperion Catalysis Internatl Inc | 炭素フィブリル含有ゴム組成物および空気入りタイヤ |
RU2200562C2 (ru) * | 1996-03-06 | 2003-03-20 | Хайперион Каталайзис Интернэшнл, Инк. | Функционализованные нанотрубки |
US6221330B1 (en) | 1997-08-04 | 2001-04-24 | Hyperion Catalysis International Inc. | Process for producing single wall nanotubes using unsupported metal catalysts |
US6514897B1 (en) * | 1999-01-12 | 2003-02-04 | Hyperion Catalysis International, Inc. | Carbide and oxycarbide based compositions, rigid porous structures including the same, methods of making and using the same |
EP1226294B1 (en) | 1999-07-21 | 2011-06-29 | Hyperion Catalysis International, Inc. | Methods of oxidizing multiwalled carbon nanotubes |
CN100366528C (zh) * | 1999-10-27 | 2008-02-06 | 威廉马歇莱思大学 | 碳质毫微管的宏观有序集合体 |
TW515129B (en) * | 2000-09-29 | 2002-12-21 | Sony Corp | Method for manufacturing gas diffusion electrode and method for manufacturing electrochemical device |
JP2002110178A (ja) * | 2000-09-29 | 2002-04-12 | Sony Corp | ガス拡散電極の製造方法及び電気化学デバイスの製造方法 |
IL142254A0 (en) * | 2001-03-26 | 2002-03-10 | Univ Ben Gurion | Method for the preparation of stable suspensions of single carbon nanotubes |
US6656339B2 (en) * | 2001-08-29 | 2003-12-02 | Motorola, Inc. | Method of forming a nano-supported catalyst on a substrate for nanotube growth |
US6713519B2 (en) * | 2001-12-21 | 2004-03-30 | Battelle Memorial Institute | Carbon nanotube-containing catalysts, methods of making, and reactions catalyzed over nanotube catalysts |
US7148269B2 (en) * | 2002-03-11 | 2006-12-12 | Trustees Of The University Of Pennsylvania | Interfacial polymer incorporation of nanotubes |
TWI237064B (en) * | 2002-03-25 | 2005-08-01 | Ind Tech Res Inst | Supported metal catalyst for synthesizing carbon nanotubes by low-temperature thermal chemical vapor deposition and method of synthesizing nanotubes using the same |
JP2004026623A (ja) * | 2002-05-10 | 2004-01-29 | Sony Corp | 水素吸蔵用複合体材料、その使用方法及びその製造方法、及び水素吸蔵材料及びその使用方法 |
JP4266752B2 (ja) * | 2002-11-01 | 2009-05-20 | 三菱レイヨン株式会社 | カーボンナノチューブ含有組成物及びその調製方法、またそれを用いた複合体及びその製造方法 |
US7345005B2 (en) * | 2003-02-13 | 2008-03-18 | E.I. Du Pont De Nemours And Company | Electrocatalysts and processes for producing |
JP2005125187A (ja) * | 2003-10-22 | 2005-05-19 | Fuji Xerox Co Ltd | ガス分解器、燃料電池用電極およびその製造方法 |
US7122165B2 (en) * | 2003-11-03 | 2006-10-17 | The Research Foundation Of State University Of New York | Sidewall-functionalized carbon nanotubes, and methods for making the same |
EP1817447A4 (en) | 2004-10-22 | 2012-01-25 | Hyperion Catalysis Int | IMPROVED OZONOLYSIS OF CARBON NANOTONES |
CA2588124A1 (en) * | 2004-11-16 | 2006-06-08 | Hyperion Catalysis International, Inc. | Method for preparing supported catalysts from metal loaded carbon nanotubes |
WO2006065431A2 (en) * | 2004-11-17 | 2006-06-22 | Hyperion Catalysis International, Inc. | Method for preparing catalyst supports and supported catalysts from single walled carbon nanotubes |
EP2432058B8 (en) * | 2004-12-09 | 2013-09-11 | Nanosys, Inc. | Nanowire-based membrane electrode assemblies for fuel cells |
WO2008051239A2 (en) * | 2005-11-16 | 2008-05-02 | Hyperion Catalysis International, Inc. | Mixed structures of single walled and multi walled carbon nanotubes |
-
2005
- 2005-11-16 CA CA002588124A patent/CA2588124A1/en not_active Abandoned
- 2005-11-16 US US11/281,811 patent/US20060142148A1/en not_active Abandoned
- 2005-11-16 DE DE602005023777T patent/DE602005023777D1/de active Active
- 2005-11-16 WO PCT/US2005/041603 patent/WO2006060168A2/en active Application Filing
- 2005-11-16 AT AT05849427T patent/ATE482029T1/de not_active IP Right Cessation
- 2005-11-16 CA CA002588109A patent/CA2588109A1/en not_active Abandoned
- 2005-11-16 AT AT05851732T patent/ATE497034T1/de not_active IP Right Cessation
- 2005-11-16 CN CN2005800463036A patent/CN101098991B/zh not_active Expired - Fee Related
- 2005-11-16 MX MX2007005797A patent/MX2007005797A/es active IP Right Grant
- 2005-11-16 EP EP05851732A patent/EP1828447B1/en not_active Not-in-force
- 2005-11-16 WO PCT/US2005/041605 patent/WO2006055670A2/en active Application Filing
- 2005-11-16 CN CN2005800466388A patent/CN101103144B/zh not_active Expired - Fee Related
- 2005-11-16 DK DK05851732.7T patent/DK1828447T3/da active
- 2005-11-16 DK DK05849427.9T patent/DK1831440T3/da active
- 2005-11-16 DE DE602005026167T patent/DE602005026167D1/de active Active
- 2005-11-16 JP JP2007541475A patent/JP2008520413A/ja active Pending
- 2005-11-16 JP JP2007541476A patent/JP4971175B2/ja not_active Expired - Fee Related
- 2005-11-16 MX MX2007005793A patent/MX2007005793A/es active IP Right Grant
- 2005-11-16 US US11/281,814 patent/US20060142149A1/en not_active Abandoned
- 2005-11-16 EP EP05849427A patent/EP1831440B1/en not_active Not-in-force
-
2007
- 2007-08-20 US US11/841,359 patent/US7968489B2/en not_active Expired - Fee Related
Patent Citations (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5707916A (en) * | 1984-12-06 | 1998-01-13 | Hyperion Catalysis International, Inc. | Carbon fibrils |
US5165909A (en) * | 1984-12-06 | 1992-11-24 | Hyperion Catalysis Int'l., Inc. | Carbon fibrils and method for producing same |
US5171560A (en) * | 1984-12-06 | 1992-12-15 | Hyperion Catalysis International | Carbon fibrils, method for producing same, and encapsulated catalyst |
US5500200A (en) * | 1984-12-06 | 1996-03-19 | Hyperion Catalysis International, Inc. | Fibrils |
US4666230A (en) * | 1984-12-27 | 1987-05-19 | Microwave Systems & Technology, Inc. | Coaxial cable connector assembly |
US5965470A (en) * | 1989-05-15 | 1999-10-12 | Hyperion Catalysis International, Inc. | Composites containing surface treated carbon microfibers |
US6143689A (en) * | 1992-05-22 | 2000-11-07 | Hyperion Catalysis Int'l Inc. | Methods and catalysts for the manufacture of carbon fibrils |
US5691054A (en) * | 1993-05-05 | 1997-11-25 | Hyperion Catalysis Int'l., Inc. | Three dimensional macroscopic assemblages of randomly oriented carbon fibrils and composites containing same |
US5456987A (en) * | 1993-10-27 | 1995-10-10 | Xerox Corporation | Intermediate transfer component coatings of titamer and grafted titamer |
US5569635A (en) * | 1994-05-22 | 1996-10-29 | Hyperion Catalysts, Int'l., Inc. | Catalyst supports, supported catalysts and methods of making and using the same |
US6203814B1 (en) * | 1994-12-08 | 2001-03-20 | Hyperion Catalysis International, Inc. | Method of making functionalized nanotubes |
US6031711A (en) * | 1996-05-15 | 2000-02-29 | Hyperion Catalysis International, Inc. | Graphitic nanofibers in electrochemical capacitors |
US6099965A (en) * | 1996-05-15 | 2000-08-08 | Hyperion Catalysis International, Inc. | Rigid porous carbon structures, methods of making, methods of using and products containing same |
US6761870B1 (en) * | 1998-11-03 | 2004-07-13 | William Marsh Rice University | Gas-phase nucleation and growth of single-wall carbon nanotubes from high pressure CO |
US20020121460A1 (en) * | 1999-01-12 | 2002-09-05 | David Moy | Method of using carbide and/or oxycarbide containing compositions |
US6333016B1 (en) * | 1999-06-02 | 2001-12-25 | The Board Of Regents Of The University Of Oklahoma | Method of producing carbon nanotubes |
US20030039604A1 (en) * | 2001-05-18 | 2003-02-27 | Chunming Niu | Modification of nanotubes oxidation with peroxygen compounds |
US20030086858A1 (en) * | 2001-05-18 | 2003-05-08 | Chunming Niu | Modification of nanotubes oxidation with peroxygen compounds |
US20030181526A1 (en) * | 2002-03-20 | 2003-09-25 | Bradley Pharmaceuticals, Inc. | Method of treating onychomycosis |
Cited By (43)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20080039315A1 (en) * | 2004-11-16 | 2008-02-14 | Jun Ma | Methods of preparing supported catalysts from metal loaded carbon nanotubes |
US7968489B2 (en) * | 2004-11-16 | 2011-06-28 | Hyperion Catalysis International, Inc. | Methods of preparing supported catalysts from metal loaded carbon nanotubes |
US20060223243A1 (en) * | 2005-03-30 | 2006-10-05 | Marko Radosavljevic | Carbon nanotube - metal contact with low contact resistance |
US20070274899A1 (en) * | 2006-05-23 | 2007-11-29 | Bayer Material Science Ag | Temperature-stable catalysts for gas phase oxidation, and processes for using the same |
WO2008127396A3 (en) * | 2006-11-02 | 2008-12-18 | Univ Ohio | A solution synthesis of carbon nanotube/metal-containing nanoparticle conjugated assemblies |
WO2008127396A2 (en) * | 2006-11-02 | 2008-10-23 | Ohio University | A solution synthesis of carbon nanotube/metal-containing nanoparticle conjugated assemblies |
WO2009078815A1 (en) * | 2007-12-14 | 2009-06-25 | Nanyang Technological University | A nanostructured material loaded with noble metal particles |
US20110014550A1 (en) * | 2007-12-14 | 2011-01-20 | Nanyang Technological University | Nanostructured material loaded with noble metal particles |
US9267908B2 (en) | 2008-03-04 | 2016-02-23 | Massachusetts Institute Of Technology | Devices and methods for determination of species including chemical warfare agents |
WO2009149849A1 (de) * | 2008-06-12 | 2009-12-17 | Bayer Technology Services Gmbh | Katalysator und verfahren zur hydrierung von organischen verbindungen |
US8614355B2 (en) | 2008-06-12 | 2013-12-24 | Bayer Technology Services Gmbh | Catalyst and process for hydrogenating organic compounds |
US20110130592A1 (en) * | 2008-06-12 | 2011-06-02 | Bayer Technology Services Gmbh | Catalyst and Process for Hydrogenating Organic Compounds |
US20110229777A1 (en) * | 2008-09-08 | 2011-09-22 | Wai Fatt Mak | Electrode materials for metal-air batteries, fuel cells and supercapacitators |
US9660310B2 (en) | 2008-09-08 | 2017-05-23 | Nanyang Technological University | Electrode materials for metal-air batteries, fuel cells and supercapacitors |
US20100124713A1 (en) * | 2008-11-17 | 2010-05-20 | Xerox Corporation | Toners including carbon nanotubes dispersed in a polymer matrix |
US20120016167A1 (en) * | 2010-07-15 | 2012-01-19 | Exxonmobil Research And Engineering Company | Hydroprocessing of biocomponent feeds with low pressure hydrogen-containing streams |
US9770709B2 (en) | 2010-11-03 | 2017-09-26 | Massachusetts Institute Of Technology | Compositions comprising functionalized carbon-based nanostructures and related methods |
JP2014505580A (ja) * | 2010-11-03 | 2014-03-06 | マサチューセッツ インスティテュート オブ テクノロジー | 官能化炭素ベースのナノ構造物を含む組成物および関連する方法 |
WO2012078384A1 (en) | 2010-12-09 | 2012-06-14 | Eastman Chemical Company | Process for the preparation of 2,2,4,4-tetraalkylcyclobutane-1,3-diols |
WO2012078439A1 (en) | 2010-12-09 | 2012-06-14 | Eastman Chemical Company | Process for the isomerization of 2,2,4,4-tetraalkylcyclobutane-1,3-diols |
US9997785B2 (en) | 2011-06-23 | 2018-06-12 | Molecular Rebar Design, Llc | Nanoplate-nanotube composites, methods for production thereof and products obtained therefrom |
US20120329640A1 (en) * | 2011-06-23 | 2012-12-27 | Designed Nanotubes, LLC | Nanoplate-nanotube composites, methods for production thereof and products obtained therefrom |
US20150041722A1 (en) * | 2012-03-12 | 2015-02-12 | Kunming University Of Science And Technology | Process For Purifying Tail Gas From Ore-Smelting Electrical Furnace by Catalytic Oxidization |
US20140030171A1 (en) * | 2012-07-27 | 2014-01-30 | Ripi | Nanocatalyst and Process for Removing Sulfur Compounds from Hydrocarbons |
US9142376B2 (en) | 2012-08-22 | 2015-09-22 | National Defense University | Method for fabricating field emission cathode, field emission cathode thereof, and field emission lighting source using the same |
RU2624004C2 (ru) * | 2012-08-22 | 2017-06-30 | Рисерч Инститьют Питроулеум Индастри (Рипи) | Нанокатализатор и способ для удаления соединений серы из углеводородов |
US20150290620A1 (en) * | 2012-11-16 | 2015-10-15 | University Of Bath | Catalyst comprising iron and carbon nanotubes |
US9238602B1 (en) | 2014-12-10 | 2016-01-19 | Eastman Chemical Company | Process for the preparation of cis-2,2,4,4-tetramethylcyclobutane-1,3-diol |
WO2016094478A1 (en) | 2014-12-10 | 2016-06-16 | Eastman Chemical Company | Process for the preparation of cis-2,2,4,4-tetramethylcyclobutane-1,3-diol |
WO2016094479A1 (en) | 2014-12-10 | 2016-06-16 | Eastman Chemical Company | Batch process for the preparation of cis-2,2,4,4-tetramethylcyclobutane-1,3-diol |
US9238603B1 (en) | 2014-12-10 | 2016-01-19 | Eastman Chemical Company | Batch process for the preparation of cis-2,2,4,4-tetramethylcyclobutane-1,3-diol |
EP3317380A4 (en) * | 2015-06-30 | 2019-03-06 | Hindustan Petroleum Corporation Ltd. | SUPPORTED CATALYST FOR REFINERY RESIN CHILLING PHASE HYDROCRACKING AND PREPARATION METHOD THEREOF |
US11167247B2 (en) | 2017-02-15 | 2021-11-09 | Nanolc-12, Llc | Length-based separation of carbon nanotubes |
US11505467B2 (en) | 2017-11-06 | 2022-11-22 | Massachusetts Institute Of Technology | High functionalization density graphene |
CN108310969A (zh) * | 2018-02-26 | 2018-07-24 | 江苏中科纳特环境科技有限公司 | 一种室外空气净化模块和净化方法 |
CN108310969B (zh) * | 2018-02-26 | 2021-06-01 | 江苏中科纳特环境科技有限公司 | 一种室外空气净化模块和净化方法 |
US11079387B2 (en) * | 2018-04-12 | 2021-08-03 | Zahra Borzooeian | Length-based carbon nanotube ladders |
US11353424B2 (en) | 2018-04-12 | 2022-06-07 | Nano LC-12, LLC | Length-based carbon nanotube ladders |
CN110961093A (zh) * | 2018-09-28 | 2020-04-07 | 中国石油化工股份有限公司 | Cr-Zr-O/TiO2-C纳米管催化剂及其制备方法和应用 |
CN110577208A (zh) * | 2019-08-18 | 2019-12-17 | 复旦大学 | 一种亲钠性导电碳纳米管骨架材料及其制备方法和应用 |
CN112108139A (zh) * | 2020-09-29 | 2020-12-22 | 西安凯立新材料股份有限公司 | 一种硝基苯液相加氢合成苯胺用催化剂及其制备方法 |
CN113101934A (zh) * | 2021-04-19 | 2021-07-13 | 天津大学 | 一种负载原子级分散金属的碳纳米管催化剂的制备方法及应用 |
CN115254089A (zh) * | 2022-07-21 | 2022-11-01 | 湖北展鹏电子材料有限公司 | 一种碳纳米管基-TiO2复合纳米材料及其制备方法和应用 |
Also Published As
Publication number | Publication date |
---|---|
WO2006060168A3 (en) | 2006-12-07 |
EP1831440A4 (en) | 2009-08-26 |
JP2008520413A (ja) | 2008-06-19 |
EP1828447B1 (en) | 2011-01-26 |
ATE497034T1 (de) | 2011-02-15 |
CN101098991B (zh) | 2012-10-10 |
EP1831440A2 (en) | 2007-09-12 |
MX2007005797A (es) | 2007-10-03 |
CA2588109A1 (en) | 2006-05-26 |
DE602005026167D1 (de) | 2011-03-10 |
CN101103144B (zh) | 2013-02-06 |
WO2006060168A2 (en) | 2006-06-08 |
DE602005023777D1 (de) | 2010-11-04 |
EP1828447A4 (en) | 2009-09-02 |
CN101103144A (zh) | 2008-01-09 |
MX2007005793A (es) | 2007-10-04 |
DK1831440T3 (da) | 2010-11-08 |
JP2008520414A (ja) | 2008-06-19 |
JP4971175B2 (ja) | 2012-07-11 |
US20060142149A1 (en) | 2006-06-29 |
EP1828447A2 (en) | 2007-09-05 |
US20080039315A1 (en) | 2008-02-14 |
WO2006055670A2 (en) | 2006-05-26 |
US7968489B2 (en) | 2011-06-28 |
EP1831440B1 (en) | 2010-09-22 |
WO2006055670A3 (en) | 2006-12-07 |
CN101098991A (zh) | 2008-01-02 |
CA2588124A1 (en) | 2006-06-08 |
ATE482029T1 (de) | 2010-10-15 |
DK1828447T3 (da) | 2011-03-21 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US7923403B2 (en) | Method for preparing catalysts supported on carbon nanotubes networks | |
EP1831440B1 (en) | Methods for preparing catalysts supported on carbon nanotube networks | |
US7396798B2 (en) | Method for preparing catalyst supports and supported catalysts from single walled carbon nanotubes | |
AU2005332975B2 (en) | Improved ozonolysis of carbon nanotubes | |
US9126828B2 (en) | Mixed structures of single walled and multi walled carbon nanotubes | |
US8852547B2 (en) | Processes for the recovery of catalytic metal and carbon nanotubes |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: HYPERION CATALYSIS INTERNATIONAL, INC., MASSACHUSE Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MA, JUN;MOY, DAVID;FISCHER, ALAN;AND OTHERS;REEL/FRAME:017459/0094;SIGNING DATES FROM 20060207 TO 20060209 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |