US20060099497A1 - Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly - Google Patents

Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly Download PDF

Info

Publication number
US20060099497A1
US20060099497A1 US11/267,404 US26740405A US2006099497A1 US 20060099497 A1 US20060099497 A1 US 20060099497A1 US 26740405 A US26740405 A US 26740405A US 2006099497 A1 US2006099497 A1 US 2006099497A1
Authority
US
United States
Prior art keywords
porous film
group
polymer
reactive polymer
reactive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/267,404
Other languages
English (en)
Inventor
Yoshihiro Uetani
Keisuke Kii
Tomoaki Ichikawa
Michio Satsuma
Satoshi Nishikawa
Shinji Bessho
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nitto Denko Corp
Original Assignee
Nitto Denko Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corp filed Critical Nitto Denko Corp
Assigned to NITTO DENKO CORPORATION reassignment NITTO DENKO CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BESSHO, SHINJI, ICHIKAWA, TOMOAKI, KII, KEISUKE, NISHIKAWA, SATOSHI, SATSUMA, MICHIO, UETANI, YOSHIHIRO
Publication of US20060099497A1 publication Critical patent/US20060099497A1/en
Priority to US13/612,021 priority Critical patent/US8911648B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/28—Layered products comprising a layer of synthetic resin comprising synthetic resins not wholly covered by any one of the sub-groups B32B27/30 - B32B27/42
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B27/065—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of foam
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/06—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material
    • B32B27/08—Layered products comprising a layer of synthetic resin as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/38—Layered products comprising a layer of synthetic resin comprising epoxy resins
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B5/00—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts
    • B32B5/18—Layered products characterised by the non- homogeneity or physical structure, i.e. comprising a fibrous, filamentary, particulate or foam layer; Layered products characterised by having a layer differing constitutionally or physically in different parts characterised by features of a layer of foamed material
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/056—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes
    • H01M10/0561—Accumulators with non-aqueous electrolyte characterised by the materials used as electrolytes, e.g. mixed inorganic/organic electrolytes the electrolyte being constituted of inorganic materials only
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/403—Manufacturing processes of separators, membranes or diaphragms
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/411—Organic material
    • H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/411—Organic material
    • H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
    • H01M50/417—Polyolefins
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/411—Organic material
    • H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
    • H01M50/42—Acrylic resins
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/449—Separators, membranes or diaphragms characterised by the material having a layered structure
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/46—Separators, membranes or diaphragms characterised by their combination with electrodes
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/489—Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/489—Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties
    • H01M50/491—Porosity
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2250/00—Layers arrangement
    • B32B2250/02—2 layers
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2250/00—Layers arrangement
    • B32B2250/24—All layers being polymeric
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2266/00—Composition of foam
    • B32B2266/02—Organic
    • B32B2266/0214—Materials belonging to B32B27/00
    • B32B2266/0271—Epoxy resin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/20—Properties of the layers or laminate having particular electrical or magnetic properties, e.g. piezoelectric
    • B32B2307/202—Conductive
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2307/00—Properties of the layers or laminate
    • B32B2307/20—Properties of the layers or laminate having particular electrical or magnetic properties, e.g. piezoelectric
    • B32B2307/206—Insulating
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2457/00—Electrical equipment
    • B32B2457/10—Batteries
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M2300/00—Electrolytes
    • H01M2300/0085—Immobilising or gelification of electrolyte
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
    • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T29/00—Metal working
    • Y10T29/49—Method of mechanical manufacture
    • Y10T29/49002—Electrical device making
    • Y10T29/49108—Electric battery cell making
    • Y10T29/49115—Electric battery cell making including coating or impregnating

Definitions

  • the present invention relates to a reactive polymer-supported porous film for battery separator, comprising a porous film substrate having supported thereon a reactive polymer comprising a partially crosslinked polymer, a method for producing the reactive polymer-supported porous film, a method for producing a battery by adhering electrodes to a separator using the reactive polymer-supported porous film, and an electrode/porous film assembly.
  • lithium ion secondary batteries with high energy density have been widely used as a power source of small-type hand-held electronic devices such as cell phone and laptop personal computer.
  • Such lithium ion secondary batteries are produced by a process including a step of laminating or winding, for example, a polyolefin resin-porous film on or around positive and negative electrodes in a sheet form to place the resulting laminate in a battery container made of, for example, a metal can, a step of pouring an electrolyte solution in the battery container, and a step of sealing the battery container or sealing the opening of the battery container.
  • such battery containers of laminate seal type have the following disadvantages. Because face pressure for maintaining the electric connection between the separator and the electrodes cannot sufficiently be applied to the face of the electrodes, the distance between the electrodes partially gets longer over time due to the expansion and shrinkage of electrode active substances during the charge or discharge of the battery. Thus, the internal resistance of the battery increases, involving deterioration of the battery performance. Additionally, the occurrence of resistance variation inside the battery also disadvantageously deteriorates the battery performance.
  • a battery comprising electrodes adhered to a separator, by joining a separator impregnated with an electrolyte solution to positive and negative electrodes through a porous adhesive resin layer for closely contacting those, and holding the electrolyte solution in the through holes (for example, JP-A-10-172606).
  • thickness of the adhesive resin layer must increase in order to obtain sufficient adhesive force between the separators and the electrodes. Further, because the amount of the electrolyte solution relative to the adhesive resin cannot increase, the internal resistance of the resulting batteries is high, so that satisfactory cycle performance and high-rate discharge performance cannot be obtained, which is disadvantageous.
  • a porous film for battery separator various production methods have conventionally been known to produce a porous film for battery separator.
  • One of the methods is a method of producing a sheet comprising a polyolefin resin, and stretching the sheet at high stretching ratio (for example, JP-A-9-12756).
  • a battery separator comprising such a porous film obtained by stretching at high stretching ratio gives rise to the problem that a battery remarkably shrinks under high temperature environment such as a case that temperature abnormally elevates by, for example, internal short circuit, and in some cases, the separator does not function as a partition wall between electrodes.
  • an adhesive resin layer between a separator and an electrode for example, JP-A-10-177865, JP-A-10-189054 and JP-A-10-172606.
  • an electrode and a separator are adhered through the adhesive resin layer.
  • strength of a resin forming the adhesive resin layer deteriorates under high temperature environment, and as a result, heat shrinkage of the separator cannot sufficiently be suppressed.
  • the present invention has been made to overcome the problems in the production of batteries by adhering electrodes to separators.
  • one object of the present invention is to provide a reactive polymer-supported porous film for battery separator, which can suitably be used for the production of a battery having sufficient adhesiveness between electrodes and a separator, low internal resistance and high-rate discharge performance.
  • Another object of the present invention is to provide a method for producing the reactive polymer-supported porous film.
  • Still another object of the present invention is to provide a method for producing a battery using the reactive polymer-supported porous film.
  • Further object of the present invention is to provide an electrode/porous film assembly.
  • a reactive polymer-supported porous film for battery separator comprising a porous film substrate having supported thereon a reactive polymer obtained by reacting a crosslinkable polymer having at least one reactive group selected from the group consisting of 3-oxetanyl group and epoxy group in the molecule, with an acid anhydride, thereby partially crosslinking the polymer.
  • a method for producing a reactive polymer-supported porous film for battery separator comprising:
  • a method for producing a battery comprising:
  • an electrolyte solution containing a cationic polymerization catalyst in the battery container to swell at least a part of the reactive polymer in the electrolyte solution or dissolve at least a part of the reactive polymer into the electrolyte solution in at least the vicinity of an interface of the porous film and the electrodes, thereby inducing cationic polymerization of residual reactive groups in the reactive polymer to further crosslink the reactive group, and gelling at least a part of the electrolyte solution to adhere the porous film and the electrodes.
  • an electrode/porous film assembly obtained by laminating electrodes on above-described reactive polymer-supported porous film to prepare a laminate of reactive polymer-supported porous film/electrodes, and adhering electrodes to the laminate.
  • the attached Figure is a cross-sectional view showing a separator (porous film)/electrode assembly and an apparatus for measuring coefficient of area heat shrinkage of the assembly.
  • the reactive polymer-supported porous film for battery separator in accordance with the present invention comprises a porous film substrate having supported thereon a reactive polymer obtained by reacting a crosslinkable polymer having at least one reactive group selected from the group consisting of 3-oxetanyl group and epoxy group in the molecule, with an acid anhydride, thereby partially crosslinking the polymer.
  • the porous film substrate has a thickness of preferably 3-50 ⁇ m.
  • the porous film has a thickness less than 3 ⁇ m, the film strength is insufficient, and when such a porous film is used as the battery separator, the electrodes may cause internal short circuit.
  • the porous film has a thickness exceeding 50 ⁇ m, the battery using such a porous film as the separator has too large distance between the electrodes, so that the internal resistance of the battery is excessive.
  • the porous film substrate used has pores having a mean pore diameter of 0.01-5 ⁇ m and a porosity of 20-95%, preferably 30-90%, and more preferably 35-85%. Where the porosity ratio is too low, such a porous film when used as a battery separator causes reduction in ionic conduction paths so that sufficient battery performance cannot be obtained. On the other hand, where the porosity is too high, the strength of the film when used as a battery separator is insufficient. In such a case, a porous film substrate having further large thickness has to be used in order to obtain the required strength. This results in unfavorable increase in the internal resistance of the battery.
  • the porous film has an air permeability of 1,500 seconds/100 cc or smaller, and preferably 1,000 seconds/100 cc or smaller. Where the permeability is too high, such a film when used as a battery separator has low ionic conductivity, so that sufficient battery performance cannot be obtained. Further, the porous film substrate preferably has a puncture strength of 1N or more. Where the puncture strength is less than 1N, the substrate breaks when the face pressure is applied to between the electrodes, which may cause internal short circuit.
  • the porous film substrate is not particularly limited so long as it has the above-described properties.
  • a porous film comprising polyolefin resins such as polyethylene and polypropylene is preferably used.
  • polyethylene resin film is particularly preferably used as the porous film for the reason that the film has a property such that when heated, the resin melts and clogs the pores, thereby giving a so-called shutdown function to the battery.
  • the polyethylene resin used herein includes not only ethylene homopolymer but also copolymers of ethylene with ⁇ -olefins such as propylene, butene and hexene.
  • laminate films of porous films such as polytetrafluoroethylene and polyimide with the polyolefin resin porous film have excellent heat resistance. Therefore, such laminate films are also preferably used as the porous film substrate in the present invention.
  • the crosslinkable polymer used in the present invention means polymers having at least one reactive group selected from the group consisting of 3-oxetanyl group and epoxy group in the molecule.
  • the crosslinkable polymer is preferably radical copolymers of at least one radically polymerizable monomer selected from the group consisting of a radically polymerizable monomer having 3-oxetanyl group and a radically polymerizable monomer having epoxy group, and other radically polymerizable monomer.
  • the crosslinkable polymer particularly preferably used is a polymer having 3-oxetanyl group and epoxy group in the molecule or a polymer having epoxy group in the molecule.
  • Such a crosslinkable polymer can preferably be obtained by radical polymerization of a radically polymerizable monomer having 3-oxetanyl group, a radically polymerizable monomer having epoxy group, and other radically polymerizable monomer, or radical polymerization of a radically polymerizable monomer having epoxy group and other radically polymerizable monomer.
  • 3-oxetasnyl group or epoxy group is capable of reacting with acid anhydride group, and also capable of undergoing cationic polymerization.
  • a crosslinkable polymer having at least one reactive group selected from the group consisting of 3-oxetanyl group and epoxy group in the molecule is first reacted with an acid anhydride by means of those reactive groups to form a partially crosslinked reactive polymer, and the reactive polymer is then supported on a porous film substrate to form a reactive polymer-supported porous film for battery separator.
  • electrodes are laminated on such a reactive polymer-supported porous film to form a laminate of electrodes/porous film.
  • This laminate is dipped in an electrolyte solution containing a cationic polymerization catalyst, preferably an electrolyte solution containing an electrolyte which also functions as a cationic polymerization catalyst, to swell a partially crosslinked crosslinkable polymer on the porous film substrate, i.e., at least a part of the reactive polymer, in the electrolyte solution, or dissolve or disperse the polymer in the electrolyte solution.
  • the reactive polymer is further crosslinked by cationic polymerization of residual reactive groups of the reactive polymer to gel the electrolyte solution in the vicinity of an interface of the porous film and the electrodes, thereby adhering the electrodes and the porous film.
  • the 3-oxetanyl group-containing radically polymerizable monomer and/or epoxy group-containing radically polymerizable monomer are used in an amount of 5-50% by weight, preferably 10-30% by weight, in terms of its total amount, based on the weight of the entire monomers. Therefore, in the case of obtaining a crosslinkable polymer containing 3-oxetanyl group, the 3-oxetanyl group-containing radically polymerizable monomer is used in an amount of 5-50% by weight, preferably 10-30% by weight, based on the weight of the entire monomers.
  • the epoxy group-containing radically polymerizable monomer is used in an amount of 5-50% by weight, preferably 10-30% by weight, based on the weight of the entire monomers.
  • the total amount of the 3-oxetanyl group-containing radically polymerizable monomer and the epoxy group-containing radically polymerizable monomer used is also in a range of 5-50% by weight, preferably 10-30% by weight, based on the weight of the entire monomers used.
  • the epoxy group-containing radically polymerizable monomer is used in an amount of 90% by weight or less based on the weight of the sum of those monomers.
  • the total amount of the 3-oxetanyl group-containing radically polymerizable monomer and the epoxy group-containing radically polymerizable monomer is less than 5% by weight based on the weight of the entire monomers used, this results in increasing the amount of the crosslinkable polymer required for gelling the electrolyte solution, and as a result, performance of the battery obtained deteriorates.
  • the total amount exceeds 50% by weight, the property to maintain the electrolyte solution in a form of a gel deteriorates. As a result, the adhesiveness between the electrodes and the separator in the resulting battery deteriorates.
  • the 3-oxetanyl group-containing radically polymerizable monomer preferably used is 3-oxetanyl group-containing (meth)acrylate represented by the following formula (I): wherein R 1 represents hydrogen atom or methyl group, and R 2 represents hydrogen atom or an alkyl group having 1-6 carbon atoms.
  • Examples of the 2-oxetanyl group-containing (meth)acrylate include 3-oxetanylmethyl (meth)acrylate, 3-methyl-3-oxetanylmethyl (meth)acrylate, 3-ethyl-3-oxetanylmethyl (meth)acrylate, 3-butyl-3-oxetanylmethyl (meth)acrylate, and 3-hexyl-3-oxetanylmethyl (meth)acrylate.
  • These (meth) acrylates can be used alone or as mixtures of two or more thereof.
  • the term “(meth)acrylate” used herein means acrylate or methacrylate.
  • the epoxy group-containing radically polymerizable monomer preferably used is an epoxy group-containing (meth)acrylate represented by the following formula (II); wherein R 3 represents hydrogen atom or methyl group; and R 4 represents an epoxy group-containing group represented by the following formula (1) or (2):
  • epoxy group-containing (meth)acrylate examples include 3,4-epoxycyclohexylmethyl (meth)acrylate, and glycidyl (meth)acrylate. These (meth)acrylates can be used alone or as mixtures of two or more thereof.
  • the other radically polymerizable monomer to be copolymerized with such 3-oxetanyl group-containing radically polymerizable monomer or epoxy group-containing radically polymerizable monomer is preferably at least one selected from (meth)acrylates represented by the following formula (II): wherein R 5 represents hydrogen atom or methyl group; A represents an oxyalkylene group having 2 or 3 carbon atoms (preferably, oxyethylene group or oxypropylene group): R 6 represents an alkyl group having 1-6 carbon atoms or a fluorinated alkyl group having 1-6 carbon atoms; and n is an integer of 0-3, and vinyl ester represented by the following formula (IV); wherein R 7 represents methyl group or ethyl group; and R 8 represents hydrogen atom or methyl group.
  • Examples of the (meth)acrylate represented by the formula (III) include methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, butyl (meth)acrylate, 2,2,2-trifluoroethyl (meth)acrylate, and 2,2,3,3-tetrafluoropropyl (meth)acrylate.
  • n is an integer of 0-3.
  • examples of the other radically polymerizable monomer that can adjust glass transition point of the reactive polymer to 70° C. or lower include ethyl acrylate, butyl acrylate, propyl acrylate, isooctyl acrylate, 2-ethylhexyl acrylate and dodecyl acrylate.
  • Examples of the vinyl ester represented by the formula (IV) include vinyl acetate and vinyl propionate.
  • the crosslinkable polymer containing at least one reactive group selected from the group consisting of 3-oxetanyl group and epoxy group in the molecule can preferably be obtained as radical copolymers via radical copolymerization of the at least one radically polymerizable monomer selected from the group consisting of 3-oxetanyl group-containing radically polymerizable monomer and the epoxy group-containing radically polymerizable monomer with other radically polymerizable monomer using radical polymerization initiators as described above.
  • the radical copolymerization may be conducted by any polymerization processes such as solution polymerization, bulk polymerization, suspension polymerization or emulsion polymerization. From the standpoints of ease of polymerization, molecular weight adjustment and post-treatment, the radical copolymerization is preferably conducted by solution polymerization or suspension polymerization.
  • the radical polymerization initiators are not particularly limited, and examples thereof include N,N′-azobisisobutyronitrile, dimethyl N,N′-azobis(2-methylpropionate), benzoyl peroxide, and lauroyl peroxide. If required and necessary, molecular weight regulators such as mercaptan can be used in this radical copolymerization.
  • the crosslinkable polymer preferably has a weight average molecular weight of 10,000 or more. Where the weight average molecular weight is smaller than 10,000, a larger amount of the crosslinking polymers is required for the gelation of the electrolyte solution, resulting in deterioration of the performance of the battery obtained.
  • the upper limit of the weight average molecular weight is not particularly limited. However, the upper limit is about 3,000,000, and preferably 2,500,000, so as to maintain the electrolyte solution in the gel form.
  • the crosslinkable polymer further preferably has a weight average molecular weight of 100,000-2,000,000.
  • crosslinkable polymer containing at least one reactive group selected from the group consisting of 3-oxetanyl group and epoxy group in the molecule is conventionally known as disclosed in, for example, JP-A-2001-176555 and JP-A-2002-110245.
  • the reactive polymer-supported porous film for battery separator is obtained by reacting the crosslinkable polymer with an acid anhydride to partially crosslink the reactive polymer, and supporting the partially crosslinked reactive polymer on a porous film substrate.
  • Crosslinking the crosslinkable polymer with an acid anhydride is due to the reaction between 3-oxetanyl group or epoxy group of the crosslinkable polymer and an acid anhydride, as disclosed in, for example, JP-A-11-43540 and JP-A-11-116663.
  • the crosslinkable polymer and acid anhydride are reacted utilizing the reactivity of 3-oxetanyl group or epoxy group to partially crosslink the polymer, thereby forming a reactive polymer.
  • the acid anhydride used to partially crosslink the crosslinkable polymer is represented by the following formula (V) wherein R is 2n valent hydrocarbon group, and n is an integer of 1-3.
  • the “acid anhydride group” used herein means a divalent group in the bracket in the acid anhydride represented by the above formula (V).
  • the hydrocarbon group may have optional substituents so long as it does not adversely affect the reaction between the acid anhydride and the reactive group of the crosslinkable polymer, and further does not adversely affect the battery finally obtained according to the present invention.
  • the optional substituent include halogen atom, nitro group, alkoxyl group, and aryloxyl group.
  • the hydrocarbon group is that a part of carbon atoms constituting the group may be substituted with hetero atoms such as oxygen atom or nitrogen atom. Further, the hydrocarbon group may have carboxyl group.
  • examples of bifunctional acid anhydride include pyromellitic anhydride, 3,3′,4,4′-benzophenonetetracarboxylic dianhydride, ethyleneglycolbis(anhydrotrimate), and 5-(2,5-dioxotetrahydro-3-furanyl)-3-methyl-cyclohexene-1,2-dicarboxylic anhydride.
  • examples of trifunctional acid anhydride include hexahydromellitic anhydride and mellitic anhydride.
  • anhydride having free carboxyl group examples include ⁇ , ⁇ -aconitic anhydride, glycolic anhydride and trimellitic anhydride and polyazelaic anhydride.
  • the reactive polymer-supported porous film for battery separator according to the present invention is that the crosslinkable polymer is reacted with an acid anhydride to partially crosslink the polymer, thereby forming a reactive polymer, and the reactive polymer is supported on the porous film.
  • a method of supporting the reactive polymer on the porous film is not particularly limited.
  • the crosslinkable polymer is dissolved in an appropriate organic solvent such as acetone, ethyl acetate or butyl acetate together with an acid anhydride to prepare a solution of a mixture of the crosslinkable polymer and the acid anhydride, this solution is applied to the surface of a porous film by casting or spray coating, or a porous film is dipped in the solution, and the porous film thus treated is dried to remove the organic solvent.
  • the porous film having supported thereon the crosslinkable polymer/acid anhydride mixture is heated to an appropriate temperature to react the crosslinkable polymer with the acid anhydride, thereby partially crosslinking the crosslinkable polymer.
  • the reactive polymer-supported porous film for battery separator according to the present invention is obtained.
  • onium salt as a catalyst may be supported on the porous film together with the crosslinkable polymer and acid anhydride.
  • the onium salts that can be used are described hereinafter.
  • the method of supporting the reactive polymer obtained by partially crosslinking the crosslinkable polymer with an acid anhydride, on the porous film substrate is not limited to the above-described method. Besides the above method, for example, the following method can be employed.
  • a solution of the crosslinkable polymer is applied to the porous film and dried.
  • a solution of the acid anhydride is applied to the porous film, or the porous film is dipped in the solution of the acid anhydride, and the porous film thus treated is heated to an appropriate temperature.
  • Another method is that the crosslinkable polymer is previously reacted with the acid anhydride in a solvent to partially crosslink the polymer, thereby forming a reactive polymer, and a solution containing the reactive polymer is applied to the porous film, and dried.
  • crosslinkable polymer is previously reacted with the acid anhydride in a solvent to partially crosslink the polymer, thereby forming a reactive polymer; a solution containing the reactive polymer is applied to an appropriate release sheet and dried; and the resulting coating film is transferred to the porous film substrate.
  • the particularly preferable method according to the present invention is that a solution containing the crosslinkable polymer and the acid anhydride is applied to a release sheet, and dried to form a crosslinkable polymer/acid anhydride layer on the release sheet; the release sheet is laminated on the porous film substrate under heating and pressure to transfer the crosslinkable polymer/acid anhydride layer to the porous film substrate; the crosslinkable polymer/acid anhydride layer is heated to an appropriate temperature to form a reactive polymer on the porous film.
  • glass transition temperature of the crosslinkable polymer obtained can be lowered to preferably 70° C. or lower.
  • the crosslinkable polymer/acid anhydride layer when the crosslinkable polymer/acid anhydride layer is formed on the release sheet using such a crosslinkable polymer, and this layer is press bonded to the porous film substrate while heating to a temperature of from a glass transition temperature of the crosslinkable polymer to 100° C., the crosslinkable polymer/acid anhydride layer can be transferred to the porous film substrate without adversely affecting the porous film substrate.
  • the crosslinkable polymer/acid anhydride layer thus transferred is heated to an appropriate temperature, the reactive polymer layer can easily be formed on the porous film.
  • the heating temperature is preferably 100° C. or lower such that deformation or melting of the porous film substrate does not cause by heating. Accordingly, the crosslinkable polymer preferably has the glass transition temperature in a range of 20-60° C.
  • the representative release sheet preferably used is a polypropylene resin sheet, but is not limited thereto.
  • sheets of polyethylene phthalate, polyethylene, vinyl chloride, engineering plastics or the like, papers (particularly, resin-impregnated papers), synthetic papers, or laminates of those can also be used. If required and necessary, those sheets may be back surface-treated with silicone-based or long chain alkyl-based compounds.
  • the crosslinkable polymer/acid anhydride layer when the crosslinkable polymer/acid anhydride layer is transferred to the porous film substrate to form the crosslinkable polymer/acid anhydride layer on the porous film substrate, the crosslinkable polymer/acid anhydride layer can securely be formed on the surface of the porous film substrate without invading the crosslinkable polymer or the crosslinkable polymer/acid anhydride into pores inside the porous film, as a result, without clogging pores of the porous film, as being different from the case of for example, applying a solution of the crosslinkable polymer or the crosslinkable polymer/acid anhydride to the porous film substrate.
  • the reactive polymer obtained by partially crosslinking the crosslinkable polymer has an insoluble content of generally 1-90%, preferably 3-75%, and more preferably 10-65%.
  • insoluble content means a proportion of the residual reactive polymer on the porous film when the porous film having supported thereon the partially crosslinked reactive polymer is dipped in an ethylene carbonate/diethyl carbonate (1/1 volume ratio) mixed solvent at room temperature for 2 hours under stirring, and then further dipped in ethyl methyl carbonate.
  • the acid anhydride is used in an amount such that acid anhydride groups of the acid anhydride are 0.005-0.5 part by mol, preferably 0.025-0.4 part by mol, and more preferably 0.05-0.35 part by mol, per mol of the reactive groups of the crosslinkable polymer, and heating reaction conditions between the crosslinkable polymer and the acid anhydride are adjusted.
  • the reactive polymer having the desired insoluble content can be obtained.
  • One example for obtaining such a reactive polymer is that the acid anhydride is used in an amount such that the acid anhydride groups are 0.25-0.5 part by mol per mol of the reactive groups of the crosslinkable polymer, and the crosslinkable polymer and the acid anhydride are reacted under heating at 50° C. for 10-500 hours, thereby obtaining the reactive polymer having the insoluble content of 1-90%.
  • the reactive polymer has the insoluble content lower than 1%
  • the reactive polymer is further subjected to cationic polymerization to crosslink, effective adhesion cannot be obtained between the electrodes and the porous film.
  • the reactive polymer has the insoluble content higher than 90%
  • swelling property of the reactive polymer is low.
  • the reactive polymer having the above insoluble content by reacting the crosslinkable polymer with the acid anhydride to react and crosslink a part of the polymer according to the present invention suppresses dissolution and dispersion into the electrolyte solution even when dipped in the electrolyte solution.
  • electrodes are laminated on the porous film to prepare a laminate of electrodes/porous film, the laminate is placed in a battery container, and an electrolyte solution containing an electrolyte containing a cationic polymerization catalyst is poured into the battery container, only a part of the reactive polymer in the electrodes/porous laminate swells or dissolves in the electrolyte solution in the vicinity of an interface between the porous film and the electrodes, and due to residual reactive groups which are not used in the partial crosslinking with the acid anhydride, the reactive polymer undergoes cationic polymerization by a cationic polymerization catalyst in the electrolyte solution, preferably by an electrolyte also serving as a cationic polymerization catalyst to further crosslink, thereby gelling the electrolyte solution and strongly adhering the electrodes to the porous film.
  • an electrode/porous film assembly i.e., a separator
  • the partially crosslinked reactive polymer has the above-described insoluble content. Therefore, even if the polymer is dipped in the electrolyte solution, dissolution or diffusion of the reactive polymer into the electrolyte solution is prevented or minimized, and the reactive polymer is effectively used to adhere the electrodes to the porous film. As a result, by the use of a relatively small amount of the reactive polymer, the electrodes and the porous film can be adhered stably and also further strongly.
  • the reactive polymer-supported porous film according to the present invention has excellent wettability to the electrolyte solution. Therefore, when a laminate comprising a positive electrode material, a negative electrode material, and a separator interposed therebetween, or a cylindrically wound roll of such a laminate is placed in a battery container, and an electrolyte solution is poured into the battery container, the electrolyte solution rapidly permeates in and spreads over the entire separator. As a result, the productivity can be increased in the battery production.
  • the porous film has a small coefficient of heat shrinkage of generally 20% or lower, and preferably 15% or lower, even if the porous film is placed under high temperature environment such as 150° C.
  • the reactive polymer-supported porous film according to the present invention can suitably be used for the production of a battery.
  • the method for producing a battery using the reactive polymer-supported porous film according to the present invention is described below.
  • Electrodes are laminated on or are wound around the reactive polymer-supported porous film to obtain a laminate of electrodes/reactive polymer-supported porous film.
  • the laminate is placed in a battery container comprising a metal can or a laminate film. If required and necessary, terminals are welded.
  • a given amount of an electrolyte solution having a cationic polymerization catalyst dissolved therein is poured in the battery container.
  • the battery container is sealed or the opening of the battery container is sealed.
  • At least a part of the reactive polymer supported on the porous film is swollen at least in the vicinity of the interface between the porous film and the electrodes in the electrolyte solution or dissolves or disperses in the electrolyte solution.
  • the reactive polymer is crosslinked by cationic polymerization to gel at least a part of the electrolyte solution, thereby adhering the electrodes and the porous film.
  • a battery in which the electrodes are strongly adhered to the porous film as a separator can be obtained.
  • the reactive polymer functions to adhere the electrodes to the porous film by the crosslinking thereof via cationic polymerization of reactive groups of the reactive polymer, thereby gelling the electrolyte solution at least in the vicinity of the interface between the porous film and the electrodes.
  • the reactive polymer can be cationically polymerized at ordinary temperature for crosslinking, although depending on the structure thereof, the amount of the reactive polymer supported on the porous film, and the type and amount of the cationic polymerization catalyst.
  • the cationic polymerization can be promoted by heating. In this case, heating is generally conducted at a temperature of about 40-100° C. for about 0.5-24 hours, although depending on the thermal resistance of materials constituting the battery and productivity of the battery.
  • the battery container may be allowed to stand at ordinary temperature for about several hours after pouring the electrolyte solution in the battery container.
  • the laminate of the electrodes/reactive polymer-supported porous film is satisfactory as long as the electrodes are simply laminated on the reactive polymer-supported porous film. Therefore, for example, negative electrode/porous film/positive electrode, negative electrode/porous film/positive electrode/porous film, and the like can be used as the laminate of the electrodes/reactive polymer-supported porous film according to the structure and form of the battery.
  • the electrolyte solution is a solution prepared by dissolving an electrolyte salt in an appropriate organic solvent.
  • the electrolyte salt that can be used is, for example, salts comprising a cation component and an anion component.
  • the cation component is derived from, for example, hydrogen, alkali metals (such as lithium, sodium or potassium), alkaline earth metals (such as calcium or strontium), or tertiary or quaternary ammonium ions.
  • the anion component is derived from, for example, inorganic acids (such as hydrochloric acid, nitric acid, phosphoric acid, sulfuric acid, fluoroboric acid, hydrofluoric acid, hexafluorophosphoric acid or perchloric acid), or organic acids (such as carboxylic acid, organic sulfonic acid or fluorine-substituted organic sulfonic acid).
  • inorganic acids such as hydrochloric acid, nitric acid, phosphoric acid, sulfuric acid, fluoroboric acid, hydrofluoric acid, hexafluorophosphoric acid or perchloric acid
  • organic acids such as carboxylic acid, organic sulfonic acid or fluorine-substituted organic sulfonic acid.
  • electrolyte salts containing alkali metal ions as cation components are particularly preferably used.
  • Examples of the electrolyte salts containing alkali metal salts as cation components include alkali metal perchlorates, such as lithium perchlorate, sodium perchlorate or potassium perchlorate; alkali metal tetrafluoroborates, such as lithium tetrafluoroborate, sodium tetrafluoroborate or potassium tetrafluoroborate; alkali metal hexafluorophosphatets, such as lithium hexafluorophosphate or potassium hexafluorophosphate; alkali metal trifluoroacetates, such as lithium trifluoroacetate; and alkali metal trifluoromethanesulfonates, such as lithium trifluoromethanesulfonate.
  • alkali metal perchlorates such as lithium perchlorate, sodium perchlorate or potassium perchlorate
  • alkali metal tetrafluoroborates such as lithium tetrafluoroborate, sodium tetraflu
  • lithium hexafluorophosphate, lithium tetrafluoroborate, lithium perchlorate or the like is suitably used as the electrolyte salt.
  • the solvent used for the above electrolyte salts can be any solvent so long as it can dissolve the electrolyte salt.
  • Representative example of the solvent is a non-aqueous solvent, and examples thereof include cyclic esters such as ethylene carbonate, propylene carbonate, butylene carbonate or ⁇ -butyrolactone; ethers such as tetrahydrofuran or dimethoxyethane; and chain esters such as dimethyl carbonate, diethyl carbonate or ethyl methyl carbonate. Those can be used alone or as mixtures of two or more thereof.
  • the amount of the electrolyte salts used is appropriately determined depending on the type and amount of a solvent used.
  • the electrolyte salts are generally used in an amount such that the resulting gel electrolyte has the electrolyte salt concentration of 1-50% by weight.
  • Onium salts are preferably used as the cationic polymerization catalyst.
  • the onium salt includes onium salts comprising cation components such as ammonium ion, phosphonium ion, arsonium ion, stibonium ion or iodonium ion, and anion components such as tetrafluoroborate, hexafluorophosphate, trifluoromethanesulfonate or perchlorate.
  • lithium tetrafluoroborate and lithium hexafluorophosphate per se function as a cation polymerization catalyst. Therefore, those are particularly preferably used as an electrolyte salt functioning as both electrolyte salt and cationic polymerization initiator. In this case, lithium tetrafluoroborate and lithium hexafluorophosphate may be used alone or as a mixture thereof.
  • the thickness of a porous film was determined by measurement with a 1/10,000 mm thickness gauge and based on a scanning type electron micrograph (magnification: 10,000) of a cross section of a porous film.
  • the permeability was determined according to JIS P 8117.
  • Puncture test was conducted with a compression tester KES-G5 manufactured by Kato Tech K.K. The maximum load was read from a load-deformation curve obtained from the measurement and was defined as puncture strength.
  • a needle used had a diameter of 1.0 mm and a radius of curvature at the tip of 0.5 mm, and the needle was penetrated at a rate of 2 cm/second.
  • a porous film having supported thereon a given amount of a reactive polymer was weighed to measure its weight B.
  • the reactive polymer-supported porous film was dipped in a mixed solvent of ethylene carbonate/diethyl carbonate (1:1 by volume) at room temperature for 2 hours, washed and dried.
  • the reactive polymer-supported porous film thus treated was weighed to measure its weight C.
  • a reactive polymer-supported porous film was dipped in an electrolyte solution comprising an ethylene carbonate/diethyl carbonate (1:1 by weight ratio) mixed solvent having dissolved therein lithium hexafluorophosphate in a concentration of 1.0 mol/l.
  • the porous film was taken out of the mixed solvent, and was immediately interposed between two platinum electrodes, and 1 kHz alternating current resistance was measured.
  • the 1 kHz alternating current resistances were measured by varying the dipping time, and the dipping time when the resistance is the lower limit was determined, thereby evaluating wettability by electrolyte solution.
  • Glass transition temperature of a crosslinkable polymer was measured as follows. A solution of the crosslinkable polymer was cast on a release paper, and dried to obtain a sheet having a thickness of 0.2-0.5 mm and a width of 5 mm. Glass transition temperature of this sheet was measured using DMS 120 manufactured by Seiko Instruments Inc. with a chuck distance of 10 mm in a bending mode at 10 kHz. Temperature rising rate was 5° C./min and temperature range was 20-200° C. The glass transition temperature was determined from a peak temperature of tan ⁇ .
  • Positive electrode/porous film/negative electrode laminates obtained in the Examples and the Comparative Examples were punched into a predetermined size, and each piece was impregnated with an electrolyte solution composed of an ethylene carbonate/diethyl carbonate (1:1 by weight ratio) mixed solvent having dissolved therein lithium hexafluorophosphate in a concentration of 1.0 mol/l to prepare a sample.
  • O ring 3 is fitted in a cyclic upper edge surface 2 of a circumferential wall of a circular container 1 made of SUS as shown in the Figure.
  • the sample 4 obtained above was placed on the bottom of the container, and a weight 5 was placed on the sample.
  • the container was covered with a lid 6 to seal the container.
  • the container containing the sample was placed in a drier at 150° C. for 1 hour and then gradually cooled.
  • the sample was taken out of the container.
  • a separator (porous film) of the sample was peeled from the positive and negative electrodes. Area of the separator (porous film) was read by scanner, and was compared with area of the original porous film to determine a coefficient of area heat shrinkage.
  • a laminate seal type battery was disintegrated to measure adhesive force as follows.
  • the laminate seal type battery was disintegrated to take out a positive electrode sheet/separator/negative electrode sheet laminate.
  • the interface of the electrode sheets/separator was peeled 5 mm from the edge, and the edge of the electrode sheet and the edge of the separator were alternatively peeled in 180° direction at a rate of 1 mm/sec. Load at this peeling was measured. This load was divided by width of electrode sheet/separator to obtain adhesive force between the electrode sheet and the separator.
  • lithium cobalt oxide as a positive electrode active material Cell Seed C-10 manufactured by Nippon Chemical Industrial Co., Ltd.
  • 10 parts of acetylene black as a conductive auxiliary agent Diska Black manufactured by Denki Kagaku Kogyo Kabushiki Kaisha
  • 5 parts of a vinylidene fluoride resin as a binder KF polymer L #1120 manufactured by Kureha Chemical Industry, Co., Ltd.
  • N-methyl-2-pyrrolidone a slurry of the resulting mixture was prepared so as to have a solid concentration of 15% by weight.
  • the slurry was applied to one side of a 20 ⁇ m thick aluminum foil (current collector) at a build-up of 200 ⁇ m, dried at 80° C. for 1 hour and then at 120° C. for 2 hours, and pressed with a roll press, to prepare a positive electrode sheet having an active material layer thickness of 100 ⁇ m.
  • mesocarbon microbeads as a negative electrode active material MCMB 6-28 manufactured by Osaka Gas Chemical Co., Ltd.
  • 10 parts of acetylene black as a conductive auxiliary agent Denka Black manufactured by Denki Kagaku Kogyo Kabushiki Kaisha
  • 10 parts of a vinylidene fluoride resin as a binder KF polymer L #1120 manufactured by Kureha Chemical Industry, Co., Ltd.
  • the slurry was applied to one side of a 20 ⁇ m thick copper foil (current collector) at a build-up of 200 ⁇ m, dried at 80° C. for 1 hour and then at 120° C. for 2 hours, and pressed with a roll press, to prepare a negative electrode sheet having an active material layer thickness of 100 ⁇ m.
  • a polyethylene resin-made porous film (separator) having a thickness of 16 ⁇ m a porosity of 40%, an air permeability of 300 second/100 cc and a puncture strength of 3.0N was provided.
  • the negative sheet obtained in Reference Example 1, the porous film provided above and the positive electrode sheet obtained in Reference Example 1 were laminated in this order to obtain a positive electrode/porous film/negative electrode laminate.
  • the resulting laminate was placed in an aluminum laminate package.
  • An electrolyte solution containing an ethylene carbonate/diethyl carbonate (1:1 in weight ratio) mixed solvent dissolving lithium hexafluorophosphate therein at a concentration of 1.0 mol/liter was poured into the package.
  • the package was sealed to assemble a lithium ion secondary battery.
  • the battery was charged and discharged at a rate of 0.1 CmA three times. Subsequently, the battery was further charged at 0.1 CmA and then discharged at 1 CmA, to determine the 1 CmA-discharge capacity A.
  • wetting time by the electrolyte solution measured by the above-described method was 5 seconds. Further, coefficient of area heat shrinkage of the separator in the positive electrode/porous film/negative electrode laminate was 72%.
  • Laminate seal-type lithium ion secondary batteries obtained in the following Examples and Comparative Examples were charged and discharged at a rate of 0.1 CmA three times. Subsequently, the batteries were further charged at 0.1 CmA and then discharged at 1 CmA, to determine the 1 CmA-discharge capacity B. Battery characteristics were evaluated on the basis of the percentage (%) of the discharge capacity B to the discharge capacity A of the reference battery.
  • the crosslinkable polymer A had slight yellow, and was viscous and transparent.
  • the crosslinkable polymer A had a weight average molecular weight of 317,000 and a number average molecular weight of 98,800. Further, the crosslinkable polymer A had a glass transition temperature of 51° C.
  • Crosslinkable Polymer B (3,4-epoxycyclohexylmethyl Acrylate Monomer Component: 5% by Weight, 3-oxetanyl Group-Containing Monomer Component: 20% by Weight and Methyl Methacrylate Monomer Component; 75% by Weight)
  • the crosslinkable polymer B thus obtained was a white powder.
  • the crosslinkable polymer B had a weight average molecular weight of 344,400 and a number average molecular weight of 174,500. Further, the crosslinkable polymer B had a glass transition temperature of 116° C.
  • An ethyl acetate solution of the crosslinkable polymer A obtained in Production Example 1 was diluted with ethyl acetate to obtain a crosslinkable polymer solution of 10 wt % concentration Separately, an ethyl acetate solution of phthalic anhydride of 5 wt % concentration was prepared.
  • the phthalic anhydride solution was gradually added dropwise to the solution of the crosslinkable polymer A while stirring to prepare a mixed solution of the crosslinkable polymer A and phthalic anhydride.
  • the ratio of mol number of acid anhydride groups of phthalic anhydride to mol number of reactive groups of the crosslinkable polymer was 0.025.
  • the mixed solution of the crosslinkable polymer A and phthalic anhydride was applied to a release paper with No. 8 wire bar, and heated to 50° C. to form a crosslinkable polymer A/phthalic anhydride layer composed of a mixture of the crosslinkable polymer A and phthalic anhydride on the release paper.
  • the release paper was laminated on a polyethylene resin porous film substrate (film thickness: 16 ⁇ m; porosity: 40%; air permeability: 300 sec/100 cc; puncture strength of 3.0N) so as to face the crosslinkable polymer A/phthalic anhydride layer with the porous film substrate.
  • the resulting laminate was passed through hot rolls at 70° C., and the release paper was removed to obtain a crosslinkable polymer-supported porous film having the crosslinkable polymer supported thereon at a coating density of 1.1 g/m 2 per one side.
  • the crosslinkable polymer-supported porous film was placed in a thermostat chamber at 50° C. for 48 hours to react the crosslinkable polymer supported on the porous film with phthalic anhydride, thereby partially crosslinking the crosslinkable polymer.
  • a reactive polymer-supported porous film was obtained.
  • Insoluble content of the reactive polymer in the reactive polymer-supported porous film was 40%.
  • the electrolyte solution dipping time of this reactive polymer-supported porous film was 15 seconds.
  • the negative electrode sheet obtained in Reference Example 1, the reactive polymer-supported porous film obtained above and the positive electrode sheet obtained in Reference Example 1 were laminated in this order to prepare a laminate of separator/electrodes.
  • This laminate was placed in an aluminum laminate package, and an electrolyte solution of an ethylene carbonate/diethyl carbonate (1:1 in weight ratio) mixed solvent dissolving lithium hexafluorophosphate at a concentration of 1.0 mol/liter was poured in the package. The package was sealed. The package was heated at 70° C. for 7 hours to perform cationic polymerization and crosslink the reactive polymer, thereby adhering the electrode sheets to the porous film (separator) and at the same time, partially gelling the electrolyte solution. Thus, a laminate seal-type battery was obtained.
  • Adhesive force between electrode sheets and separator in this battery was 0.16 N/cm in the positive electrode and 0.20 N/cm in the negative electrode.
  • the 1 CmA discharge capacity of this battery was 99% of the discharge capacity of the reference battery.
  • Coefficient of area heat shrinkage of the separator in the separator/electrode assembly obtained using the reactive polymer-supported porous film was 1.0%.
  • a reactive polymer-supported porous film was obtained in the same manner as in Example 1, except that the ratio of mol number of acid anhydride groups of phthalic anhydride to mol number of reactive groups of the crosslinkable polymer A was 0.25, and the time placed in the 50° C. thermostat chamber was changed to 12 hours. Insoluble content of the reactive polymer in the reactive polymer-supported porous film was 85%. Further, the electrolyte solution dipping time of this reactive polymer-supported porous film was 30 seconds.
  • a laminate seal-type battery was obtained in the same manner as in Example 1 except for using the reactive polymer-supported porous film obtained above.
  • Adhesive force between electrode sheets and separator in this battery was 0.10 N/cm in the positive electrode and 0.10 N/cm in the negative electrode.
  • the 1 CmA discharge capacity of this battery was 92% of the discharge capacity of the reference battery.
  • Coefficient of area heat shrinkage of the separator in the separator/electrode assembly obtained using the reactive polymer-supported porous film was 5.0%.
  • a reactive polymer-supported porous film was obtained in the same manner as in Example 1, except that succinic anhydride was used in place of phthalic anhydride, and the time placed in the 50° C. thermostat chamber was changed to 300 hours.
  • the ratio of mol number of acid anhydride groups of succinic anhydride to mol number of reactive groups of the crosslinkable polymer A was 0.25.
  • Insoluble content of the reactive polymer in the reactive polymer-supported porous film was 50%.
  • the electrolyte solution dipping time of this reactive polymer-supported porous film was 20 seconds.
  • a laminate seal-type battery was obtained in the same manner as in Example 1 except for using the reactive polymer-supported porous film obtained above.
  • Adhesive force between electrode sheets and separator in this battery was 0.20 N/cm in the positive electrode and 0.10 N/cm in the negative electrode.
  • the 1 CmA discharge capacity of this battery was 93% of the discharge capacity of the reference battery.
  • Coefficient of area heat shrinkage of the separator in the separator/electrode assembly obtained using the reactive polymer-supported porous film was 1.3%.
  • a reactive polymer-supported porous film was obtained in the same manner as in Example 3, except that the ratio of mol number of acid anhydride groups of succinic anhydride to mol number of reactive groups of the crosslinkable polymer A was 0.05, and the time placed in the 50° C. thermostat chamber was changed to 96 hours. Insoluble content of the reactive polymer in the reactive polymer-supported porous film was 5%. Further, the electrolyte solution dipping time of this reactive polymer-supported porous film was 10 seconds.
  • a laminate seal-type battery was obtained in the same manner as in Example 1 except for using the reactive polymer-supported porous film obtained above.
  • Adhesive force between electrode sheets and separator in this battery was 0.13 N/cm in the positive electrode and 0.10 N/cm in the negative electrode.
  • the 1 CmA discharge capacity of this battery was 99% of the discharge capacity of the reference battery.
  • Coefficient of area heat shrinkage of the separator in the separator/electrode assembly obtained using the reactive polymer-supported porous film was 50%.
  • a reactive polymer-supported porous film was obtained in the same manner as in Example 1, except that 2,4-diethylglutaric anhydride was used in place of phthalic anhydride, and the time placed in the 50° C. thermostat chamber was changed to 120 hours.
  • the ratio of mol number of acid anhydride groups of 2,4-diethylglutaric anhydride to mol number of reactive groups of the crosslinkable polymer A was 0.25.
  • Insoluble content of the reactive polymer in the reactive polymer-supported porous film was 35%.
  • the electrolyte solution dipping time of this reactive polymer-supported porous film was 15 seconds.
  • a laminate seal-type battery was obtained in the same manner as in Example 1 except for using the reactive polymer-supported porous film obtained above.
  • Adhesive force between electrode sheets and separator in this battery was 0.30 N/cm in the positive electrode and 0.24 N/cm in the negative electrode.
  • the 1 CmA discharge capacity of this battery was 92% of the discharge capacity of the reference battery.
  • Coefficient of area heat shrinkage of the separator in the separator/electrode assembly obtained using the reactive polymer-supported porous film was 0.9%.
  • a reactive polymer-supported porous film having supported thereon the reactive polymer having the insoluble content of 40%, obtained in the same manner as in Example 1 was prepared.
  • the electrolyte solution dipping time of this reactive polymer-supported porous film was 15 seconds.
  • the negative electrode sheet obtained in Reference Example 1, the reactive polymer-supported porous film obtained above and the positive electrode sheet obtained in Reference Example 1 were laminated in this order to prepare a laminate of separator/electrodes.
  • This laminate was press adhered at a temperature of 80° C. under pressure of 5 kgf/cm 2 for 2 minutes.
  • This laminate was placed in an aluminum laminate package, and an electrolyte solution of an ethylene carbonate/diethyl carbonate (1:1 in weight ratio) mixed solvent dissolving lithium hexafluorophosphate at a concentration of 1.0 mol/liter was poured in the package. The package was sealed. The package was heated at 70° C.
  • Adhesive force between electrode sheets and separator in this battery was 0.30 N/cm in the positive electrode and 0.35 N/cm in the negative electrode.
  • the 1 CmA discharge capacity of this battery was 88% of the discharge capacity of the reference battery.
  • Coefficient of area heat shrinkage of the separator in the separator/electrode assembly obtained using the reactive polymer-supported porous film was 0.3%.
  • the crosslinkable polymer B obtained in Production Example 2 was dissolved in ethyl acetate at room temperature to obtain a crosslinkable polymer solution of 10 wt % concentration. Separately, an ethyl acetate solution of phthalic anhydride of 5 wt % concentration was prepared. The phthalic anhydride solution was gradually added dropwise to the solution of the crosslinkable polymer A while stirring to prepare a mixed solution of the crosslinkable polymer B and phthalic anhydride. The ratio of mol number of acid anhydride groups of phthalic anhydride to mol number of reactive groups of the crosslinkable polymer was 0.025.
  • the mixed solution of the crosslinkable polymer B and phthalic anhydride was applied to one side of a polyethylene resin porous film substrate (film thickness: 16 ⁇ m; porosity: 40%; air permeability: 300 sec/100 cc; puncture strength of 3.0N) with No. 8 wire bar, and heated to 50° C. to evaporate ethyl acetate.
  • the mixed solution was also applied to another side of the substrate, and heated to evaporate ethyl acetate, thereby obtaining a crosslinkable polymer-supported porous film having the crosslinkable polymer supported thereon at a coating density of 2.0 g/m 2 per one side.
  • the crosslinkable polymer-supported porous film was placed in a thermostat chamber at 50° C. for 60 hours to react the crosslinkable polymer supported on the porous film with phthalic anhydride, thereby partially crosslinking the crosslinkable polymer.
  • a reactive polymer-supported porous film was obtained.
  • Insoluble content of the reactive polymer in the reactive polymer-supported porous film was 45%.
  • the electrolyte solution dipping time of this reactive polymer-supported porous film was 650 seconds.
  • the negative electrode sheet obtained in Reference Example 1, the reactive polymer-supported porous film obtained above and the positive electrode sheet obtained in Reference Example 1 were laminated in this order to prepare a laminate of separator/electrodes.
  • This laminate was placed in an aluminum laminate package, and an electrolyte solution of an ethylene carbonate/diethyl carbonate (1:1 in weight ratio) mixed solvent dissolving lithium hexafluorophosphate at a concentration of 1.0 mol/liter was poured in the package. The package was sealed. The package was heated at 70° C. for 7 hours to perform cationic polymerization and crosslink the reactive polymer, thereby adhering the electrode sheets to the porous film (separator) and at the same time, partially gelling the electrolyte solution. Thus, a laminate seal-type battery was obtained.
  • Adhesive force between electrode sheets and separator in this battery was 0.20 N/cm in the positive electrode and 0.10 N/cm in the negative electrode.
  • the 1 CmA discharge capacity of this battery was 98% of the discharge capacity of the reference battery.
  • Coefficient of area heat shrinkage of the separator in the separator/electrode assembly obtained using the reactive polymer-supported porous film was 1.5%.
  • Poly(vinylidene fluoride/hexafluoropropylene) copolymer (Kynar 2801 manufactured by Atofina Chemicals, Inc.) was dissolved in N-methyl-2-pyrrolidone to prepare a polymer solution having a concentration of 10% by weight.
  • the polymer solution was applied to both sides of a polyethylene resin porous film (film thickness: 16 ⁇ m, porosity: 40%, air permeability: 30 seconds/100 cc and puncture strength; 3.0 N) with a wire bar (#20), and heat dried at 60° C. to volatilize N-methyl-2-pyrrolidone.
  • the negative electrode sheet obtained in the Reference Example 1, the poly (vinylidene fluoride/hexafluoropropylene) copolymer-supported porous film obtained above and the positive electrode sheet obtained in the Reference Example 1 were laminated in this order, and press bonded at a temperature of 80° C. under a pressure of 5 kg/cm 2 for 1 minute, to obtain a laminate of the separator/electrodes.
  • the laminate of the separator/electrodes was placed in an aluminum laminate package, and an electrolyte solution of an ethylene carbonate/diethyl carbonate (1:1 in weight ratio) mixed solvent dissolving lithium hexafluorophosphate at a concentration of 1.0 mol/liter was poured in the package. The package was sealed to obtain a laminate seal-type battery.
  • Adhesive force between electrode sheets and separator in this battery was 0.20 N/cm in the positive electrode and 0.09 N/cm in the negative electrode.
  • the 1 CmA discharge capacity of this battery was 85% of the discharge capacity of the reference battery.
  • Coefficient of area heat shrinkage of the separator in the separator/electrode assembly obtained using the poly (vinylidene fluoride/hexafluoropropylene) copolymer-supported porous film was 30%.
  • a laminate seal-type battery was obtained in the same manner as in Comparative Example 1 except for changing the concentration of the poly (vinylidene fluoride/hexafluoropropylene) copolymer solution to 5% by weight.
  • Adhesive force between electrode sheets and separator in this battery was 0.05 N/cm in the positive electrode and 0.0 N/cm in the negative electrode.
  • the 1 CmA discharge capacity of the battery was 96% of the discharge capacity of the reference battery.
  • the electrolyte solution dipping time of this poly(vinylidene fluoride/hexafluoropropylene) copolymer-supported porous film was 30 seconds.
  • Coefficient of area heat shrinkage of the separator in the separator/electrode assembly obtained using the poly (vinylidene fluoride/hexafluoropropylene) copolymer-supported porous film was 60%.
  • the reactive polymer-supported porous film for battery separator comprises a porous film substrate having supported thereon a reactive polymer obtained by reacting a crosslinkable polymer having at least one reactive group selected from the group consisting of 3-oxetanyl group and epoxy group in the molecule, with an acid anhydride, thereby partially crosslinking the polymer.
  • the electrode/porous film assembly can be obtained by laminating electrodes on such a reactive polymer-supported porous film to prepare a laminate of reactive polymer-supported porous film/electrodes, placing the laminate in a battery container, and pouring an electrolyte solution containing a cationic polymerization catalyst in the battery container to swell at least a part of the reactive polymer in the electrolyte solution or dissolve at least a part of the reactive polymer into the electrolyte solution in at least the vicinity of an interface of the porous film and the electrodes, thereby inducing cationic polymerization of residual reactive groups in the reactive polymer to further crosslink the reactive group, and gelling at least a part of the electrolyte solution to strongly adhere the porous film and the electrodes.
  • the reactive polymer-supported porous film the reactive polymer is previously partially crosslinked. Therefore, when the laminate of reactive polymer-supported porous film/electrodes is dipped in the electrolyte solution, the reactive polymer is suppressed to dissolve and disperse in the electrolyte solution from the laminate, and at the same time, the reactive polymer swells. As a result, the electrodes can be adhered to the porous film (separator) by using a small amount of the reactive polymer.
  • the porous film has excellent ion permeability, and well functions as a separator. Further, the reactive polymer does not excessively dissolve and disperse in the electrolyte solution, thereby not adversely affecting the electrolyte solution.
  • the crosslinkable polymer layer can be transferred to the porous film substrate at relatively low temperature to support thereon, where the crosslinkable polymer is partially crosslinked.
  • the reactive polymer-supported porous film securely having the reactive polymer on the surface thereof can be obtained.
  • the reactive polymer-supported porous film has excellent electrolyte solution dipping property, and this enables productivity of battery production to increase.
  • a battery having low internal resistance and high rate performance can easily be obtained with good productivity while forming the electrode/separator assembly having strong adhesion between electrodes and separator in the production step of battery in situ.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Manufacturing & Machinery (AREA)
  • Inorganic Chemistry (AREA)
  • Secondary Cells (AREA)
  • Cell Separators (AREA)
  • Manufacture Of Porous Articles, And Recovery And Treatment Of Waste Products (AREA)
  • Epoxy Resins (AREA)
  • Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
US11/267,404 2004-11-08 2005-11-07 Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly Abandoned US20060099497A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US13/612,021 US8911648B2 (en) 2004-11-08 2012-09-12 Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JPP.2004-324258 2004-11-08
JP2004324258A JP4526352B2 (ja) 2004-11-08 2004-11-08 電池用セパレータのための反応性ポリマー担持多孔質フィルムとそれを用いた電池の製造方法

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US13/612,021 Division US8911648B2 (en) 2004-11-08 2012-09-12 Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly

Publications (1)

Publication Number Publication Date
US20060099497A1 true US20060099497A1 (en) 2006-05-11

Family

ID=35482242

Family Applications (2)

Application Number Title Priority Date Filing Date
US11/267,404 Abandoned US20060099497A1 (en) 2004-11-08 2005-11-07 Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly
US13/612,021 Expired - Fee Related US8911648B2 (en) 2004-11-08 2012-09-12 Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly

Family Applications After (1)

Application Number Title Priority Date Filing Date
US13/612,021 Expired - Fee Related US8911648B2 (en) 2004-11-08 2012-09-12 Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly

Country Status (7)

Country Link
US (2) US20060099497A1 (ko)
EP (1) EP1657766B1 (ko)
JP (1) JP4526352B2 (ko)
KR (2) KR100982822B1 (ko)
CN (1) CN1783543B (ko)
AT (1) ATE504093T1 (ko)
DE (1) DE602005027158D1 (ko)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090098464A1 (en) * 2005-01-11 2009-04-16 Nitto Denko Corporation Reactive polymer-supporting porous film for battery separator and use thereof
US20090202898A1 (en) * 2004-09-30 2009-08-13 Nitto Denko Corporation Reactive polymer-carrying porous film and processing for producing the same
US20100136410A1 (en) * 2006-11-14 2010-06-03 Shinya Kawasoe Separator for lithium ion secondary battery and method for manufacturing the same
CN102751461A (zh) * 2012-07-05 2012-10-24 中国科学院化学研究所 一种复合多孔隔膜及其制备方法与应用
US20130004654A1 (en) * 2004-11-08 2013-01-03 Nitto Denko Corporation Reactive polymer-supported porous film for for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly
US20130177817A1 (en) * 2011-06-13 2013-07-11 Nitto Denko Corporation Separator for nonaqueous electrolyte electricity storage devices, nonaqueous electrolyte electricity storage device, and production methods thereof
EP2720295A1 (en) * 2011-06-13 2014-04-16 Nitto Denko Corporation Production method for separator for nonaqueous electrolytic electricity storage device and production method for nonaqueous electrolytic electricity storage device
US20150263324A1 (en) * 2013-09-30 2015-09-17 Lg Chem, Ltd. Method of preparing separator for lithium secondary battery, separator prepared therefrom, and lithium secondary battery comprising the same
US11597874B2 (en) * 2018-03-23 2023-03-07 Tokuyama Corporation Photochromic curable composition

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5401756B2 (ja) * 2006-11-28 2014-01-29 日産自動車株式会社 二次電池
KR100727248B1 (ko) * 2007-02-05 2007-06-11 주식회사 엘지화학 다공성 활성층이 코팅된 유기/무기 복합 분리막 및 이를구비한 전기화학소자
JP5312751B2 (ja) * 2007-03-28 2013-10-09 パナソニック株式会社 非水電解液二次電池の製造方法
JP5124178B2 (ja) * 2007-06-15 2013-01-23 日東電工株式会社 電池用セパレータのための架橋性ポリマー担持多孔質フィルムとその利用
JP2017500688A (ja) * 2013-10-25 2017-01-05 エルジー・ケム・リミテッド 分離膜に粘着性バインダーを塗布する方法
CN111430783B (zh) * 2020-05-08 2021-11-16 衡阳力赛储能有限公司 一种锂离子电池隔膜
CN114221036B (zh) * 2021-12-14 2023-11-28 珠海冠宇电池股份有限公司 一种电解液及包括该电解液的电化学装置
WO2023248698A1 (ja) * 2022-06-23 2023-12-28 日本ゼオン株式会社 全固体二次電池用バインダー組成物、全固体二次電池用スラリー組成物、全固体二次電池用機能層、及び全固体二次電池

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5244944A (en) * 1991-06-05 1993-09-14 Eastman Kodak Company Thermosetting powder coating compositions
US5821305A (en) * 1994-09-08 1998-10-13 Akzo Nobel Nv Allyl-containing epoxy resin composition comprising a copolymer of an ethylenically unsaturated anhydride and a vinyl compound
US6686095B2 (en) * 1999-12-28 2004-02-03 Kabushiki Kaisha Toshiba Gel electrolyte precursor and chemical battery
US7449111B2 (en) * 2003-07-30 2008-11-11 Arkema Inc. Resins containing ionic or ionizable groups with small domain sizes and improved conductivity

Family Cites Families (31)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3892665A (en) * 1973-10-15 1975-07-01 Standard Oil Co Membrane method and product
JPS54151570A (en) * 1978-05-22 1979-11-28 Teijin Ltd Selectively permeable composite membrane and its manufacture
JPH05310989A (ja) 1992-04-30 1993-11-22 Mitsubishi Kasei Corp ポリエチレン多孔膜
JP3549290B2 (ja) 1995-06-29 2004-08-04 東燃化学株式会社 ポリオレフィン微多孔膜及びその製造方法
JP3225864B2 (ja) 1996-12-04 2001-11-05 三菱電機株式会社 リチウムイオン二次電池及びその製造方法
JP3303694B2 (ja) 1996-12-17 2002-07-22 三菱電機株式会社 リチウムイオン二次電池及びその製造方法
JP3225867B2 (ja) 1996-12-18 2001-11-05 三菱電機株式会社 リチウムイオン二次電池及びその製造方法
JP3225871B2 (ja) 1996-12-26 2001-11-05 三菱電機株式会社 リチウムイオン二次電池の製造方法
JP3629907B2 (ja) 1997-07-29 2005-03-16 宇部興産株式会社 熱硬化性オキセタン組成物
JP3575245B2 (ja) 1997-10-17 2004-10-13 宇部興産株式会社 熱硬化性組成物およびそれから得られる硬化物ならびにその製造方法
US6322923B1 (en) 1998-01-30 2001-11-27 Celgard Inc. Separator for gel electrolyte battery
JP3866458B2 (ja) 1998-09-17 2007-01-10 株式会社東芝 非水電解液二次電池及び非水電解液二次電池の製造方法
JP2000268875A (ja) 1999-03-15 2000-09-29 Toshiba Corp 非水電解液二次電池及びその製造方法
JP3447610B2 (ja) 1999-04-23 2003-09-16 日本電気株式会社 電極セパレータ積層体、その製造方法およびそれを用いた電池
JP4911813B2 (ja) 2000-10-03 2012-04-04 サンスター技研株式会社 固体電解質用架橋性組成物、ポリマー固体電解質リチウムイオン２次電池及びポリマー固体電解質リチウムイオン２次電池の製造法
JP4597294B2 (ja) 1999-12-20 2010-12-15 サンスター技研株式会社 ポリマー固体電解質リチウムイオン２次電池
JP3745593B2 (ja) 2000-06-29 2006-02-15 三菱電機株式会社 電池およびその製造方法
JP2002151042A (ja) 2000-11-15 2002-05-24 Yuasa Corp セパレータ及びその製造方法並びにそれを用いた電池及びその製造方法
JP2002305032A (ja) 2001-04-04 2002-10-18 Japan Storage Battery Co Ltd 電 池
JP2003096232A (ja) * 2001-09-26 2003-04-03 Nitto Denko Corp 接着性多孔質膜、それより得られる高分子ゲル電解質とそれらの応用
JP2003109663A (ja) 2001-09-28 2003-04-11 Sanyo Electric Co Ltd ポリマー電池
JP2003142158A (ja) 2001-11-01 2003-05-16 Hitachi Maxell Ltd リチウムイオン二次電池の製造方法
JP4381054B2 (ja) * 2002-11-13 2009-12-09 日東電工株式会社 電池用セパレータのための部分架橋接着剤担持多孔質フィルムとその利用
JP4549621B2 (ja) * 2002-12-02 2010-09-22 日東電工株式会社 電池用セパレータのための架橋性ポリマー担持多孔質フィルムとそれを用いた電池の製造方法
US20040175625A1 (en) * 2003-03-06 2004-09-09 Lotfi Hedhli Non-perfluorinated resins containing ionic or ionizable groups and products containing the same
US7947790B2 (en) * 2003-04-16 2011-05-24 Kureha Corporation Porous film of vinylidene fluoride resin and method for producing same
JP3996089B2 (ja) 2003-04-28 2007-10-24 株式会社Ｉｈｉ 土砂掘削吸引装置
JP4718800B2 (ja) * 2004-06-30 2011-07-06 日東電工株式会社 電池用セパレータのための反応性ポリマー担持多孔質フィルムとこれを用いる電池の製造方法
JP4526352B2 (ja) * 2004-11-08 2010-08-18 日東電工株式会社 電池用セパレータのための反応性ポリマー担持多孔質フィルムとそれを用いた電池の製造方法
WO2008123122A1 (ja) * 2007-03-23 2008-10-16 Chisso Corporation 重合体および重合体を含む表面処理剤
JP2010250109A (ja) * 2009-04-16 2010-11-04 Fujifilm Corp ポジ型感光性組成物、並びに透明導電膜、表示素子及び集積型太陽電池

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5244944A (en) * 1991-06-05 1993-09-14 Eastman Kodak Company Thermosetting powder coating compositions
US5821305A (en) * 1994-09-08 1998-10-13 Akzo Nobel Nv Allyl-containing epoxy resin composition comprising a copolymer of an ethylenically unsaturated anhydride and a vinyl compound
US6686095B2 (en) * 1999-12-28 2004-02-03 Kabushiki Kaisha Toshiba Gel electrolyte precursor and chemical battery
US7267910B2 (en) * 1999-12-28 2007-09-11 Kabushiki Kaisha Toshiba Chemical battery containing gel electrolyte based on crosslinked epoxy compound having an alicyclic structure
US7449111B2 (en) * 2003-07-30 2008-11-11 Arkema Inc. Resins containing ionic or ionizable groups with small domain sizes and improved conductivity

Cited By (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8092935B2 (en) 2004-09-30 2012-01-10 Nitto Denko Corporation Reactive polymer-carrying porous film and process for producing the same
US20090202898A1 (en) * 2004-09-30 2009-08-13 Nitto Denko Corporation Reactive polymer-carrying porous film and processing for producing the same
US20130004654A1 (en) * 2004-11-08 2013-01-03 Nitto Denko Corporation Reactive polymer-supported porous film for for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly
US8911648B2 (en) * 2004-11-08 2014-12-16 Nitto Denko Corporation Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly
US8277968B2 (en) * 2005-01-11 2012-10-02 Nitto Denko Corporation Reactive polymer-supporting porous film for battery separator and use thereof
US20090098464A1 (en) * 2005-01-11 2009-04-16 Nitto Denko Corporation Reactive polymer-supporting porous film for battery separator and use thereof
US20100136410A1 (en) * 2006-11-14 2010-06-03 Shinya Kawasoe Separator for lithium ion secondary battery and method for manufacturing the same
US8628873B2 (en) * 2006-11-14 2014-01-14 Asahi Kasei Chemicals Corporation Separator for lithium ion secondary battery and method for manufacturing the same
US20130177817A1 (en) * 2011-06-13 2013-07-11 Nitto Denko Corporation Separator for nonaqueous electrolyte electricity storage devices, nonaqueous electrolyte electricity storage device, and production methods thereof
EP2720295A1 (en) * 2011-06-13 2014-04-16 Nitto Denko Corporation Production method for separator for nonaqueous electrolytic electricity storage device and production method for nonaqueous electrolytic electricity storage device
EP2720295A4 (en) * 2011-06-13 2015-02-18 Nitto Denko Corp METHOD FOR PRODUCING SEPARATOR FOR NONAQUEOUS ELECTROLYTIC ELECTRICITY STORAGE DEVICE, AND METHOD FOR PRODUCING NONAQUEOUS ELECTROLYTIC ELECTRICITY STORAGE DEVICE
CN102751461A (zh) * 2012-07-05 2012-10-24 中国科学院化学研究所 一种复合多孔隔膜及其制备方法与应用
US20150263324A1 (en) * 2013-09-30 2015-09-17 Lg Chem, Ltd. Method of preparing separator for lithium secondary battery, separator prepared therefrom, and lithium secondary battery comprising the same
US10115950B2 (en) * 2013-09-30 2018-10-30 Lg Chem, Ltd. Method of preparing separator for lithium secondary battery, separator prepared therefrom, and lithium secondary battery comprising the same
US11597874B2 (en) * 2018-03-23 2023-03-07 Tokuyama Corporation Photochromic curable composition

Also Published As

Publication number Publication date
CN1783543B (zh) 2010-09-08
EP1657766A1 (en) 2006-05-17
US8911648B2 (en) 2014-12-16
DE602005027158D1 (de) 2011-05-12
KR100982822B1 (ko) 2010-09-16
CN1783543A (zh) 2006-06-07
KR20100083107A (ko) 2010-07-21
EP1657766B1 (en) 2011-03-30
ATE504093T1 (de) 2011-04-15
JP4526352B2 (ja) 2010-08-18
KR20060052538A (ko) 2006-05-19
KR100984925B1 (ko) 2010-10-01
JP2006131808A (ja) 2006-05-25
US20130004654A1 (en) 2013-01-03

Similar Documents

Publication Publication Date Title
US8911648B2 (en) Reactive polymer-supported porous film for battery separator, method for producing the porous film, method for producing battery using the porous film, and electrode/porous film assembly
US9533475B2 (en) Crosslinking polymer-supported porous film for battery separator and method for producing battery using the same
US8277897B2 (en) Reactive polymer-supporting porous film for battery separator and use thereof
US8277968B2 (en) Reactive polymer-supporting porous film for battery separator and use thereof
JP2007123254A (ja) 電池用セパレータのための反応性ポリマー担持多孔質フィルムとそれを用いた電池の製造方法
JP2007157570A (ja) 電池用セパレータのためのポリマー担持多孔質フィルムとそれを用いる電池の製造方法
JP2009110683A (ja) 電池用セパレータのための反応性ポリマー層担持多孔質フィルムとその利用
JP5260075B2 (ja) 電池用セパレータ用反応性ポリマー担持多孔質フィルムとそれより得られる電極／セパレータ接合体
JP5124178B2 (ja) 電池用セパレータのための架橋性ポリマー担持多孔質フィルムとその利用
JP2007157569A (ja) 電池用セパレータのための反応性ポリマー担持多孔質フィルムとそれを用いる電池の製造方法
JP5260074B2 (ja) 電池用セパレータとそれより得られる電極／セパレータ接合体
JP2006012562A (ja) 電池用正極／反応性ポリマー担持多孔質フィルム／負極積層体

Legal Events

Date Code Title Description
AS Assignment

Owner name: NITTO DENKO CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:UETANI, YOSHIHIRO;KII, KEISUKE;ICHIKAWA, TOMOAKI;AND OTHERS;REEL/FRAME:017607/0900

Effective date: 20051213

STCB Information on status: application discontinuation

Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION