TW202019859A - 熱設置用定形接縫料 - Google Patents

熱設置用定形接縫料 Download PDF

Info

Publication number
TW202019859A
TW202019859A TW108135451A TW108135451A TW202019859A TW 202019859 A TW202019859 A TW 202019859A TW 108135451 A TW108135451 A TW 108135451A TW 108135451 A TW108135451 A TW 108135451A TW 202019859 A TW202019859 A TW 202019859A
Authority
TW
Taiwan
Prior art keywords
mass
joint material
less
raw materials
shaped joint
Prior art date
Application number
TW108135451A
Other languages
English (en)
Other versions
TWI721581B (zh
Inventor
大內龍哉
山本正樹
Original Assignee
日商黑崎播磨股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日商黑崎播磨股份有限公司 filed Critical 日商黑崎播磨股份有限公司
Publication of TW202019859A publication Critical patent/TW202019859A/zh
Application granted granted Critical
Publication of TWI721581B publication Critical patent/TWI721581B/zh

Abstract

本發明係以維持定形接縫料的熱封性,且抑制定形接縫料中之可燃物的燃燒所引起的起火及冒煙為目的。亦即,本發明之熱設置用定形接縫料係對包含50質量%以上90質量%以下的三水鋁石之氫氧化鋁原料、1質量%以上9質量%以下的黏土、9質量%以上23質量%以下的石墨,其餘部分主要由其他耐火原料所構成的摻合物100質量%,額外添加26質量%以上50質量%以下之有機質添加劑的合計量進行混煉、成形及乾燥而得。

Description

熱設置用定形接縫料
本發明係有關於一種在熔融金屬之連續鑄造或精煉等用之設備中供接合2個噴嘴之間、設備之接合部分等的定形接縫料,尤其係有關於一種在約200℃~約1000℃左右的熱環境下設置者。
例如在鋼的連續鑄造用設備中,下部噴嘴與長噴嘴間或下部噴嘴與浸漬噴嘴間的接合面,為了防止空氣的侵入或熔鋼的漏出等,而使用墊片或定形接縫料等的接縫料。
墊片係氧化鋁-二氧化矽質無機纖維之成形體,主要係使用於需按連續鑄造的每一批次更換噴嘴的長噴嘴接合用。這是因為,墊片在熱環境下設置時不會起火,可確實地設置,且使用中不會與長噴嘴熔接,使用後的剝離性良好之故。 然而,墊片為氣孔率80%以上的多孔性材質,無法獲得充分在熱環境下的密封性(下稱「熱封性」),因此,對於鋼的品級或於噴嘴接合部的保護,噴嘴的耐用性等存有問題。
定形接縫料係對主要包含各種無機原料的摻合物添加主要為有機質(樹脂系)之黏合劑、塑化劑、溶劑等進行混煉,並進行成形及乾燥而成者。此種定形接縫料係預先加工成接近待接合之對象部分的形狀之形態的耐火性接縫料,對於前述墊片熱封性特別高,而廣泛應用於噴嘴間的接合部。
作為此種定形接縫料,例如專利文獻1中揭示一種定形接縫料,其係對由耐火原料所構成的原料混合物100質量%額外添加20~40質量%之作為黏合劑的丙烯系乳液,並進一步額外添加1~3質量%之作為塑化劑的酯醇,進行混煉,成形後經乾燥而得。 [先前技術文獻] [專利文獻]
[專利文獻1]日本特開2009-227538號公報
[發明所欲解決之課題]
設置於連續鑄造用之噴嘴間的定形接縫料有時設置在連續熔鋼排出的途中(例如更換鍋爐時等之連續鑄造的批次間),或設置在預熱後開始鑄造前等的約200℃~1000℃左右的高溫狀態下。 此時,由於定形接縫料所含之主要為樹脂系黏合劑、塑化劑等的有機質添加劑為可燃性,在熱環境下設置,劇烈地升溫至高溫時,有機質添加劑會氣化燃燒,而發生起火及冒煙。一發生起火及冒煙,接合部分或定形接縫料的辨視性會變差。辨視性一旦變差,便無法將定形接縫料設置於適確的位置而於噴嘴間產生間隙,因大氣的吸引而導致密封性降低,或由此導致噴嘴接合部附近或內孔部的氧化,而容易發生熔鋼的氧化等,或發生漏鋼的危險性提高。
因此,本發明所欲解決之課題在於維持定形接縫料的熱封性,且抑制定形接縫料中之可燃物的燃燒所引起的起火及冒煙。 [解決課題之手段]
本發明為以下1~9所記載之定形接縫料。 1.一種熱設置用定形接縫料,其係對包含: 50質量%以上90質量%以下的三水鋁石之氫氧化鋁原料、 1質量%以上9質量%以下的黏土、 9質量%以上23質量%以下的石墨, 且其餘部分主要由其他耐火原料所構成的摻合物100質量%, 額外添加26質量%以上50質量%以下之有機質添加劑的合計量進行混煉、成形及乾燥而得。 2.如前述1之熱設置用定形接縫料,其中前述氫氧化鋁原料的粒徑為1μm以上0.25mm以下。 3.如前述1或前述2之熱設置用定形接縫料,其中前述摻合物中之其餘部分的耐火原料係選自氧化鋁原料、尖晶石原料、鋯石原料、氧化鋯原料、氧化鎂原料及二氧化矽原料的1種或多種。 4.如前述1至前述3中任一項之熱設置用定形接縫料,其中前述石墨為粒徑0.2mm以上的鱗片狀石墨。 5.如前述1至前述4中任一項之熱設置用定形接縫料,其中前述外加之有機質添加劑係包含黏合劑及塑化劑,黏合劑的添加量為25質量%以上45質量%以下,塑化劑的添加量為1質量%以上5質量%以下。 6.如前述5之熱設置用定形接縫料,其中前述黏合劑為乙烯/乙酸乙烯酯共聚物系乳液,其樹脂濃度為40質量%以上60質量%以下。 7.如前述5或前述6之熱設置用定形接縫料,其中前述塑化劑為酯醇(Texanol)單異丁酸酯或酯醇二異丁酸酯。 8.如前述1至前述7中任一項之熱設置用定形接縫料,其中前述乾燥之溫度為60℃以上100℃以下。 9.如前述1至前述8中任一項之熱設置用定形接縫料,其係設置於至少一者為200℃以上之溫度的2種鋼之連續鑄造用的噴嘴間。
以下說明本發明之特徵。 屬金屬氫氧化物的一種之氫氧化鋁,加熱至高溫時會顯著吸熱並同時釋放出水分子等的非可燃性氣體。由此時的吸熱及分解而產生水蒸氣所產生的冷卻效應,與同時形成於周圍之水蒸氣層所產生之阻絕空氣,亦即氧氣的效果,而對包含有機質添加劑之定形接縫料賦予阻燃性。
定形接縫料的燃燒係大致行經:供給熱→產生可燃性氣體→與空氣中的氧氣結合而起火→擴大燃燒→滅火程序。由此,抑制燃燒或起火及冒煙,便有助於(a)抑制可燃性氣體的釋放;(b)稀釋可燃性氣體;(c)抑制空氣,即氧氣的供給或使氧氣濃度降低;(d)抑制溫度上升或冷卻;(e)抑制導熱等。 而且,重要的是與由燃燒而產生氣體之有機質添加劑與氫氧化鋁所釋放出的水蒸氣的量的平衡、或產生前述氣體與釋放出水蒸氣的時間點。亦即,為使前述之賦予阻燃性的程序更有效地作用,以下3項為必要者。 (1)氫氧化鋁的熱分解行為應配合溫度、時間點等有機質添加劑的熱分解行為。 (2)在前述(1)之條件下釋放出相對於可燃性氣體產生量為足量的水蒸氣。 (3)具備安全性,廉價且可穩定地於產業上取得。
本發明中,作為金屬氫氧化物係使用氫氧化鋁。而且,係使用氫氧化鋁當中的三水鋁石(Al(OH)3 )。 此三水鋁石富含水蒸氣化成分,即(OH)成分,且伴隨脫水反應所產生的總吸熱量為2000J/g,在金屬氫氧化物當中為最大者。而且,其脫水起始溫度為約200℃,在金屬氫氧化物當中為低溫,具有在約200℃以下不會變化而呈穩定,且脫水後可形成具備超越熔鋼溫度之耐熱性的α氧化鋁等性質。
就此三水鋁石進一步敘述其性質與阻燃機制。 由三水鋁石的熱分解特性,其吸熱峰有3處,係分別相當於以下脫水反應的波峰。 245℃: 2Al(OH)3 →Al2 O3 ・H2 O+2H2 O(一部分水鋁石轉移) 320℃: 2Al(OH)3 →Al2 O3 +3H2 O(三水鋁石的脫水反應) 550℃: Al2 O3 ・H2 O→Al2 O3 +H2 O(水鋁石的脫水反應)
此種三水鋁石之脫水的水蒸氣放出溫度,由於接近定形接縫料中之有機質添加劑(黏合劑、塑化劑等)的乾燥後殘留成分的燃燒(熱分解)起始溫度200℃,故可時間點良好地抑制由此等定形接縫料中之有機質添加劑所產生之可燃性氣體的燃燒。 再者,放出之水蒸氣亦具有降低定形接縫料之溫度的機能。 而且,三水鋁石之氫氧化鋁可於產業上以較低的價格穩定地取得。
此外,除三水鋁石以外於產業上較容易取得的氫氧化鋁,有硬水鋁石(AlO(OH), diaspore)。然而,硬水鋁石所產生的水蒸氣量為三水鋁石的1/2以下而較少,其分解溫度,即釋放出水蒸氣之溫度為約500℃,係高於由定形接縫料產生可燃性氣體的溫度區域,而無法獲得充分的起火及冒煙抑制效果。 又,雖亦可使用氫氧化鎂,惟其分解溫度為約350℃,略高於三水鋁石,吸熱量為380cal/g而小於三水鋁石,因此起火及冒煙抑制效果較三水鋁石為差。 由以上所述,為了獲得充分的起火及冒煙抑制效果,宜適用三水鋁石。
此外,例如日本特開平6-272191號公報所揭示之阻燃性薄片材料等,週知在建材相關領域中作為阻燃化材或不燃化材,係使用氫氧化鋁;但其中無如設置於高溫狀態之對象部位的條件,且未考量氣體產生或燃燒成分與由氫氧化鋁釋放出之水蒸氣的量的平衡或產生前述氣體與釋放出水蒸氣的時間點等。 [發明之效果]
根據本發明之定形接縫料,可維持熱封性,且在熱環境下設置時可大幅減少起火及冒煙。 而且,在設置於高溫狀態之長噴嘴等的連續鑄造用噴嘴時,也不會因起火及冒煙而導致辨視性變差,可確實地設置於既定的位置。其結果,在作業(使用定形接縫料之鑄造)中可維持良好的熱封性,可抑制連續鑄造用噴嘴之內孔或接合部附近的氧化所造成的損傷或鐵氧化物所造成的熔損,且亦可防止漏鋼,甚而亦可防止熔鋼的品級劣化。
[實施發明之形態]
三水鋁石之氫氧化鋁(以下簡稱為「氫氧化鋁」)的脫水反應會隨其大小而變化,粒徑小於1μm時,不易發生遵循前述要件的反應,且為了確保作為定形接縫料之具備特性當中尤其是用來賦予密封性的填充性,甚而基於確保可燃性氣體與產生之水蒸氣的透氣性之觀點,粒徑較佳為1μm以上0.25mm以下。
有機質添加劑除外之摻合物(以下簡稱為「摻合物」)中的氫氧化鋁的含有比例係於50質量%以上90質量%以下的範圍內選擇。 氫氧化鋁的含有比例若未達50質量%、阻燃性會變差,於熱設置時無法解決前述課題。氫氧化鋁的含有比例若超過90質量%、因黏土的量相對減少而導致保形性或可撓性等變差,而且因石墨量亦相對減少而導致去除定形接縫料時的剝離性變差。 惟,此氫氧化鋁的含有比例係由與為了獲得定形接縫料的可撓性、可塑性、保存性(歷時變化小)等具備特性而需要的有機質添加劑(黏合劑或塑化劑等)的量之平衡來決定。亦即,氫氧化鋁的具體含有比例,只要依據個別的作業條件,具體而言為設置定形接縫料時之噴嘴的溫度等,或作為依據在個別的作業條件中所要求之可撓性等而調整之結果的有機質添加劑,即可燃物的量來適宜決定即可。
黏土係為了賦予可塑性而使用,亦可使用包含膨潤土等蒙脫石而具有可塑性者。 黏土在摻合物中的含有比例係取1質量%以上9質量%以下。黏土的含有比例若未達1質量%、混煉物的可塑性不足而導致成形性變差。另一方面,黏土的含有比例若超過9質量%則混煉物會變硬,不易成形,同時為了緩和此缺點,有機質添加劑的所需添加量亦增加,結果導致屬可燃物之成分增加,熱設置時更容易或更常發生起火及冒煙。
石墨係以防止與噴嘴等設置面的熔接及提升使用後從設置面的剝離性為目的,而於摻合物中,以9質量%以上23質量%以下的含有比例使用。 石墨的含有比例若未達9質量%、會發生對接合對象物,尤為耐火物製噴嘴的熔接傾向,導致剝離性變差而在拆卸噴嘴、定形接縫料的更換作業等時發生問題。石墨的含有比例若超過23質量%、剝離性雖無問題,但混煉物的可塑性消失而不易成形。又,使用中的接縫料強度降低而導致熱封性變差,或容易發生在熔鋼中的熔出或摩耗,且接合部的保護機能亦發生問題。 所用石墨較佳為粒徑0.2mm以上的鱗片狀石墨。此粒徑0.2mm以上的鱗片狀石墨,由於作為連續體之表面積較大而對於防止摻合物中的構成物彼此或彼等與黏合劑的熔接有其效果。鱗片狀石墨的粒徑的上限不特別限制,產業上可取得者約為0.5mm以下。
摻合物的其餘部分係主要由其他耐火原料所構成。就此耐火原料,較佳選自氧化鋁原料、尖晶石原料、鋯石原料、氧化鋯原料及氧化鎂原料。 定形接縫料中,此等耐火原料在與氫氧化鋁變化而生成的α氧化鋁之間不易發生低熔化等反應,可維持定形接縫料的穩定性。作為此等其餘部分的耐火原料,只要是接縫厚度以下的大小(粒徑),且只要是不會妨礙該定形接縫料的填充性之程度的量,則亦可包含粒徑超過0.25mm之大小的耐火原料。
此處所稱氧化鋁原料,係指以剛玉、矽線石族、莫來石等的氧化鋁為主者;尖晶石原料係指氧化鋁與氧化鎂之正尖晶石;氧化鋯原料係指不拘安定化劑的種類且不拘穩定化度,可為穩定化或未穩定化任一種;氧化鎂原料則指以方鎂石為主體,約略含有80質量%以上的MgO成分者。
就二氧化矽原料,只要為高純度品,在與α氧化鋁之間亦會生成莫來石,可作為構成摻合物的其餘部分的耐火原料使用。 惟,在外來熔渣成分或二氧化矽原料中雜質較多時,有可能生成低熔點物質而引起熔損或摩耗等,因此,只要依據例如使用時間、溫度等作業條件來適宜選擇原料的種類等即可。又,將二氧化矽原料與其他的耐火原料併用時,在與氧化鎂原料之間有可能生成低熔點物質,因此較佳與氧化鎂原料以外的原料併用。
此外,構成此等摻合物之其餘部分的耐火原料不拘人造或天然,且不拘製法。
本發明之定形接縫料中,係對前述摻合物100質量%額外添加26質量%以上50質量%以下之有機質添加劑的合計量。此有機質添加劑係主要由黏合劑及塑化劑所構成。
黏合劑可使用乙烯/乙酸乙烯酯共聚物系乳液。作為此乙烯/乙酸乙烯酯共聚物系乳液,可使用樹脂濃度為40質量%以上60質量%以下(樹脂成分以外主要為水)的市售品。此樹脂成分為可燃物。此樹脂濃度若未達40質量%、乾燥時的成膜機構不充分而不易使接縫料定形。樹脂濃度若超過60質量%、則使用時會劇烈起火及冒煙,也會引起爆裂而不佳。 又,乙烯/乙酸乙烯酯共聚物系乳液的黏度在25℃下較佳為100~500cps。黏度若未達100cps,混煉物的可塑性不足,於成形時發生破損而不易成形。黏度若超過500cps則黏性過高而不易均勻地進行混煉。 再者,乙烯/乙酸乙烯酯共聚物系乳液的pH約較佳為4~8。pH若未達約4,由於為強酸性,對人體的有害性提高,在作業時的取用處理時需加留意。pH若超過約8則為高鹼性,對人體的有害性仍會提高,在作業時的取用處理時需加留意,同時更有可能與耐火原料反應導致混煉物隨時間經過而變化(硬化現象)。從而,較佳為屬穩定區域的pH約4~8者。
乙烯/乙酸乙烯酯共聚物系乳液的添加量,以將前述摻合物設為100質量%的外加比例計,係定為25質量%以上45質量%以下。乙烯/乙酸乙烯酯共聚物系乳液的添加量若未達25質量%、且超過45質量%的話,雖可獲得混煉物,但不易獲得可塑性或保形性等。乙烯/乙酸乙烯酯共聚物系乳液的添加量若為25質量%以上45質量%以下,則可獲得具備具保形性之良好的成形性的混煉物。
塑化劑係賦予可塑性者,在定形接縫料的用途上主要是為了賦予可撓性而使用。於本發明中,較佳使用鄰苯二甲酸系以外者。此係因鄰苯二甲酸系塑化劑在安全方面、環境方面存有問題之故。 作為鄰苯二甲酸系以外的塑化劑,丁基系酯醇單異丁酸酯或酯醇二異丁酸酯(以下總稱為「酯醇」),由與前述黏合劑的相溶性而言係較佳者。又,酯醇其起火點高達390℃,未抵觸PRTR法或VOC規範,且無環境激素物質之虞。因此,可提供環保的定形接縫料。
塑化劑的添加量,以將摻合物設為100質量%的外加比例計,係定為1質量%以上5質量%以下。塑化劑的添加量若未達1質量%、無法獲得充分的可塑性;若超過5質量%、則過量的塑化劑殘留於接縫料中而隨著時間發生變質,因此在成形品乾燥後或至使用前的期間接縫料產生龜裂而缺乏密封性。
本發明之定形接縫料係對前述摻合物添加前述有機質添加劑進行混煉,並進行成形及乾燥而得;混煉可使用一般使用於耐火物的混煉之混合機,例如刀片形螺旋混合機、行星式混合機或調理混合機、艾氏混合機等。於混煉時,只要是破壞摻合物的粒子且不會大幅破壞各原料的粒度或形態之程度,則亦可加壓。 此外,前述摻合物中,除有機質添加劑外,為了便於混煉,亦可適宜添加水以外的溶劑。此時,較佳為乾燥時會氣化而消失者。
成形可使用一般使用於耐火物的成形之例如單軸油壓成形機等。成形壓力只要依據製品的形狀、壓接構造或對應強度之密度等按個別作業的具備條件等任意設定即可。
以乾燥而言,由操作方式可分類為批次式與連續式,由加熱方式可分類為直接與間接,而由熱源則可分類為熱風乾燥,熱風與濕潤體直接通電併用、藉由電熱或輻射管之紅外線乾燥、微波乾燥等。 本發明中之成形體的乾燥較佳利用以下方式來進行:使用此等當中可較容易地利用之藉由電熱乾燥爐的直熱加熱式熱風乾燥爐,其中為批次式電熱乾燥爐(箱型或棚板式)。 乾燥溫度較佳為60℃以上100℃以下。這是因為,可更確實地獲得前述有機質添加劑乾燥後之成膜所產生之接縫料的柔軟性之故。 乾燥溫度未達60℃時,此成膜不充分而導致成膜在整個定形接縫料容易變得不完全,其結果在操作處理時產生龜裂等柔軟性較差。另一方面,乾燥溫度超過100℃則成膜過於強固,導致定形接縫料硬化而有柔軟性較差的傾向。 此外,此等定形接縫料的性質狀態亦會受到在此等乾燥溫度下的保持時間等的影響。
本發明之定形接縫料若設置於例如經預熱之耐火物製噴嘴上,則因耐火物的保有熱,首先使黏合劑(乙烯/乙酸乙烯酯系樹脂)熔融軟化,由此定形接縫料本身會變軟。在維持此狀態的期間,藉由在約1分鐘以內接合的2個噴嘴之間加壓予以壓接,可提高內部組織的填充度而確保充分的熱封性。而且,由於包含石墨,作業中不會與和噴嘴之接合面熔接,使用後的接縫料亦容易剝離,而且不易發生與熔鋼或熔渣等的反應或熔損等。 [實施例]
將本發明之實施例及比較例中所使用之摻合物A~M的各組成示於表1、表2。各原料的純度均為95%以上。又,將使用此等摻合物A~M所製作之定形接縫料的摻合組成及評定結果示於表3及表4。此外,作為黏合劑之乙烯/乙酸乙烯酯共聚物系乳液,係使用樹脂濃度58質量%、黏度200cps、pH5者。又,作為塑化劑之酯醇,係使用2,2,4-三甲基-1,3-戊二醇單異丁酸酯之酯醇單異丁酸酯。
表3、4所示各評定係依以下方法進行。 混煉物的成形性係由混煉物的可塑性或加壓成形後,是否可獲得期望形狀來進行評定。 常溫下的保形性係使用JIS-K6301硫化橡膠物理試驗方法記載之彈簧式硬度試驗,以0~100之指數標示來評定壓針距接縫料表面的侵入程度。此指數標示的數值愈大表示接縫料愈硬,愈小則表示接縫料愈柔軟。 阻燃性的評定係在加熱至800℃的耐火磚上設置定形接縫料並觀察有無燃燒或起火及冒煙。 熱封性係在加熱至600℃的耐火磚間設置定形接縫料,藉由測定由減壓至0.5氣壓之狀態至回復至1氣壓之大氣壓的時間作為復原時間來評定。此復原時間愈長表示熱封性愈高。 使用後之剝離性的評定係在加熱至800℃的耐火磚(下稱「800℃加熱磚」)上載置定形接縫料,1分鐘後覆蓋另一個800℃加熱磚而包夾定形接縫料,置入1100℃的爐內並施加5kg/cm2 的負載15分鐘後取出,以磚塊的剝離難易度來評定。 基於以上各評定,就作為定形接縫料之綜合評定,依◎(良好)、○(尚可)、×(差)此3等級進行評定,以◎、○為合格。
Figure 02_image001
Figure 02_image003
Figure 02_image005
Figure 02_image007
首先,就表3所示本發明之實施例加以說明。
就實施例1,係對由氫氧化鋁90質量%、黏土1質量%、石墨9質量%所構成的摻合物A額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)25質量%、酯醇(塑化劑)1質量%,使用桌上型混合機進行混煉,加壓成形為厚度3mm的片狀並以約80℃加以乾燥,藉由水分的蒸發使乳液成膜而製作定形接縫料,並進行評定。 就阻燃性之評定,無起火而良好,且根據JIS-K6301硫化橡膠物理試驗方法記載之彈簧式硬度試驗機的測定值亦為50~60,具有常溫下的保形性,且熱封性或使用後的剝離性亦良好。
就實施例2,係對由氫氧化鋁82質量%、黏土9質量%、石墨9質量%所構成的摻合物B額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)35質量%、酯醇(塑化劑)3質量%,與實施例1同樣地製作定形接縫料,並進行評定。 就阻燃性之評定,無起火而良好,常溫下的保形性、熱封性或使用後的剝離性亦良好。
就實施例3,係對與實施例2相同之摻合物B額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)40質量%、酯醇(塑化劑)4質量%,與實施例1同樣地製作定形接縫料,並進行評定。 就阻燃性之評定,無起火而良好,常溫下的保形性、熱封性或使用後的剝離性亦良好。
就實施例4,係對由氫氧化鋁79質量%、黏土4質量%、石墨17質量%所構成的摻合物C額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)30質量%、酯醇(塑化劑)2質量%,與實施例1同樣地製作定形接縫料,並進行評定。 就阻燃性之評定,無起火而良好,常溫下的保形性、熱封性或使用後的剝離性亦良好。
就實施例5,係對與實施例4相同之摻合物C額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)35質量%、酯醇(塑化劑)3質量%,與實施例1同樣地製作定形接縫料,並進行評定。 就阻燃性之評定,無起火而良好,常溫下的保形性、熱封性或使用後的剝離性亦良好。
就實施例6,係對由氫氧化鋁76質量%、黏土1質量%、石墨23質量%所構成的摻合物D額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)40質量%、酯醇(塑化劑)2質量%,與實施例1同樣地製作定形接縫料,並進行評定。 就阻燃性之評定,無起火而良好,常溫下的保形性、熱封性或使用後的剝離性亦良好。
就實施例7,係對由氫氧化鋁68質量%、黏土9質量%、石墨23質量%所構成的摻合物E額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)45質量%、酯醇(塑化劑)5質量%,與實施例1同樣地製作定形接縫料,並進行評定。 就阻燃性之評定,無起火而良好,常溫下的保形性、熱封性或使用後的剝離性亦良好。
就實施例8,係對由氫氧化鋁50質量%、氧化鋁(aluminum oxide)原料40質量%、黏土1質量%、石墨9質量%所構成的摻合物F額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)30質量%、酯醇(塑化劑)1質量%,與實施例1同樣地製作定形接縫料,並進行評定。 就阻燃性之評定,無起火而良好,常溫下的保形性、熱封性或使用後的剝離性亦良好。
就實施例9,係對由氫氧化鋁50質量%、氧化鋁(aluminum oxide)原料18質量%、黏土9質量%、石墨23質量%所構成的摻合物G額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)45質量%、酯醇(塑化劑)5質量%,與實施例1同樣地製作定形接縫料,並進行評定。 就阻燃性之評定,無起火而良好,常溫下的保形性、熱封性或使用後的剝離性亦良好。
其次,就表4所示比較例加以說明。
比較例1係對氫氧化鋁的含有比例為46質量%而低於本發明之下限值的摻合物H額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)45質量%、酯醇(塑化劑)4質量%,與實施例1同樣地使用桌上型混合機進行混煉而成者。混煉物的成形性良好,且乾燥後於常溫下的保形性亦良好,但因氫氧化鋁的含有比例過低而可看出起火。因此,熱封性的評定、使用後的剝離性評定皆無法進行,綜合評定為×。
比較例2係對氫氧化鋁的含有比例為92質量%而高於本發明之上限值,且石墨的含量為7質量%而低於本發明之下限值的摻合物I額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)38質量%、酯醇(塑化劑)4質量%,與實施例1同樣地使用桌上型混合機進行混煉而成者。混煉物的成形性良好,且乾燥後於常溫下的保形性亦良好。然而,因氫氧化鋁的含有比例過高,石墨的含有比例相對過低而發生對耐火磚的燒黏,導致使用後的剝離性變差。
比較例3係對不含黏土的摻合物J額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)25質量%、酯醇(塑化劑)2質量%,與實施例1同樣地進行混煉,但由於不存在黏土,致混煉物無可塑性而無法成形。因此,熱封性的評定、使用後的剝離性評定皆無法進行,綜合評定為×。
比較例4係對黏土的含有比例為10質量%而高於本發明之上限值的摻合物K額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)45質量%、酯醇(塑化劑)5質量%,與實施例1同樣地進行混煉而成者,但因黏土的含有比例過高,混煉物偏硬而無法成形。因此,熱封性的評定、使用後的剝離性評定皆無法進行,綜合評定為×。
比較例5係對石墨的含有比例為7質量%而低於本發明之下限值的摻合物L額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)35質量%、酯醇(塑化劑)3質量%,與實施例1同樣地進行混煉而成者。混煉物的成形性良好,乾燥後於常溫下的保形性亦良好,且無起火,熱封性亦良好,但因石墨的含有比例過低而發生對耐火磚的燒黏,導致使用後的剝離性變差。
比較例6係對石墨的含有比例為26質量%而高於本發明之上限值的摻合物M額外添加乙烯/乙酸乙烯酯共聚物系乳液(黏合劑)45質量%、酯醇(塑化劑)5質量%,與實施例1同樣地進行混煉,但因石墨的含有比例過高,致混煉物無可塑性,而無法成形。因此,熱封性的評定、使用後的剝離性評定皆無法進行,綜合評定為×。
比較例7係針對目前作為下部噴嘴與長噴嘴間之接縫料而使用的市售墊片進行同樣的評定者。 結果係如表4所示,雖未燒黏於耐火磚,但熱封性差,因而判定為非適合作為接縫料。此係與實爐相同之結果。
如以上所述,就處於本發明範圍內的實施例1~9,可維持熱封性,且無起火及冒煙,也不會與待接合之噴嘴熔接,而得以容易且確實地實施噴嘴或定形接縫料的更換作業。而且,由於可維持在熱環境下的密封性或接合部的保護,而於作業中無大氣(空氣)的捲入,可獲得高品級的鋼。

Claims (9)

  1. 一種熱設置用定形接縫料,其係對包含: 50質量%以上90質量%以下的三水鋁石之氫氧化鋁原料、 1質量%以上9質量%以下的黏土、 9質量%以上23質量%以下的石墨, 且其餘部分主要由其他耐火原料所構成的摻合物100質量%, 額外添加26質量%以上50質量%以下之有機質添加劑的合計量進行混煉、成形及乾燥而得。
  2. 如請求項1之熱設置用定形接縫料,其中前述氫氧化鋁原料的粒徑為1μm以上0.25mm以下。
  3. 如請求項1或請求項2之熱設置用定形接縫料,其中前述摻合物中之其餘部分的耐火原料係選自氧化鋁原料、尖晶石原料、鋯石原料、氧化鋯原料、氧化鎂原料及二氧化矽原料的1種或多種。
  4. 如請求項1至請求項3中任一項之熱設置用定形接縫料,其中前述石墨為粒徑0.2mm以上的鱗片狀石墨。
  5. 如請求項1至請求項4中任一項之熱設置用定形接縫料,其中前述額外之有機質添加劑係包含黏合劑及塑化劑,黏合劑的添加量為25質量%以上45質量%以下,塑化劑的添加量為1質量%以上5質量%以下。
  6. 如請求項5之熱設置用定形接縫料,其中前述黏合劑為乙烯/乙酸乙烯酯共聚物系乳液,其樹脂濃度為40質量%以上60質量%以下。
  7. 如請求項5或請求項6之熱設置用定形接縫料,其中前述塑化劑為酯醇(Texanol)單異丁酸酯或酯醇二異丁酸酯。
  8. 如請求項1至請求項7中任一項之熱設置用定形接縫料,其中前述乾燥之溫度為60℃以上100℃以下。
  9. 如請求項1至請求項8中任一項之熱設置用定形接縫料,其係設置於至少一者為200℃以上之溫度的2種鋼之連續鑄造用的噴嘴間。
TW108135451A 2018-10-05 2019-10-01 熱設置用定形接縫料 TWI721581B (zh)