RU99111752A - Жесткие полиуретановые пенопласты - Google Patents
Жесткие полиуретановые пенопластыInfo
- Publication number
- RU99111752A RU99111752A RU99111752/04A RU99111752A RU99111752A RU 99111752 A RU99111752 A RU 99111752A RU 99111752/04 A RU99111752/04 A RU 99111752/04A RU 99111752 A RU99111752 A RU 99111752A RU 99111752 A RU99111752 A RU 99111752A
- Authority
- RU
- Russia
- Prior art keywords
- isocyanate
- weight
- composition
- reactive
- amine catalyst
- Prior art date
Links
- 229920005830 Polyurethane Foam Polymers 0.000 title 1
- 239000011496 polyurethane foam Substances 0.000 title 1
- 239000003054 catalyst Substances 0.000 claims 9
- 239000000203 mixture Substances 0.000 claims 9
- KRKNYBCHXYNGOX-UHFFFAOYSA-N citric acid Chemical group OC(=O)CC(O)(C(O)=O)CC(O)=O KRKNYBCHXYNGOX-UHFFFAOYSA-N 0.000 claims 6
- 125000002887 hydroxy group Chemical group [H]O* 0.000 claims 6
- 150000001412 amines Chemical class 0.000 claims 5
- 150000001735 carboxylic acids Chemical class 0.000 claims 5
- KWYUFKZDYYNOTN-UHFFFAOYSA-M potassium hydroxide Inorganic materials [OH-].[K+] KWYUFKZDYYNOTN-UHFFFAOYSA-M 0.000 claims 4
- IQPQWNKOIGAROB-UHFFFAOYSA-N [N-]=C=O Chemical compound [N-]=C=O IQPQWNKOIGAROB-UHFFFAOYSA-N 0.000 claims 3
- 229920005906 polyester polyol Polymers 0.000 claims 3
- VHYFNPMBLIVWCW-UHFFFAOYSA-N 4-Dimethylaminopyridine Chemical compound CN(C)C1=CC=NC=C1 VHYFNPMBLIVWCW-UHFFFAOYSA-N 0.000 claims 2
- BJEPYKJPYRNKOW-UHFFFAOYSA-N Malic acid Chemical group OC(=O)C(O)CC(O)=O BJEPYKJPYRNKOW-UHFFFAOYSA-N 0.000 claims 2
- 229920000582 Polyisocyanurate Polymers 0.000 claims 2
- RTZKZFJDLAIYFH-UHFFFAOYSA-N diethyl ether Chemical compound CCOCC RTZKZFJDLAIYFH-UHFFFAOYSA-N 0.000 claims 2
- 239000006260 foam Substances 0.000 claims 2
- 125000000524 functional group Chemical group 0.000 claims 2
- AEMRFAOFKBGASW-UHFFFAOYSA-N glycolic acid Chemical group OCC(O)=O AEMRFAOFKBGASW-UHFFFAOYSA-N 0.000 claims 2
- 239000001630 malic acid Chemical group 0.000 claims 2
- 229940099690 malic acid Drugs 0.000 claims 2
- 235000011090 malic acid Nutrition 0.000 claims 2
- 239000011495 polyisocyanurate Substances 0.000 claims 2
- 229920002635 polyurethane Polymers 0.000 claims 2
- 239000004814 polyurethane Substances 0.000 claims 2
- MCTWTZJPVLRJOU-UHFFFAOYSA-N 1-Methylimidazole Chemical compound CN1C=CN=C1 MCTWTZJPVLRJOU-UHFFFAOYSA-N 0.000 claims 1
- RGUKYNXWOWSRET-UHFFFAOYSA-N 4-pyrrolidin-1-ylpyridine Chemical compound C1CCCN1C1=CC=NC=C1 RGUKYNXWOWSRET-UHFFFAOYSA-N 0.000 claims 1
- UKODFQOELJFMII-UHFFFAOYSA-N PMDTA Chemical group CN(C)CCN(C)CCN(C)C UKODFQOELJFMII-UHFFFAOYSA-N 0.000 claims 1
- 229920001228 Polyisocyanate Polymers 0.000 claims 1
- 150000001875 compounds Chemical class 0.000 claims 1
- JVTAAEKCZFNVCJ-UHFFFAOYSA-N lactic acid Chemical group CC(O)C(O)=O JVTAAEKCZFNVCJ-UHFFFAOYSA-N 0.000 claims 1
- 239000004310 lactic acid Substances 0.000 claims 1
- 235000014655 lactic acid Nutrition 0.000 claims 1
- 239000005056 polyisocyanate Substances 0.000 claims 1
Claims (13)
1. Способ получения жестких пенополиуретанов или пенополиизоциануратов, модифицированных уретаном, включающий стадию взаимодействия состава на основе органического полиизоцианата с реакционно-способным по отношению к изоцианату составом, включающим в себя сложный полиэфирполиол, имеющий среднее количество функциональных групп от 1,8 до 8, гидроксильное число от 15 до 750 мг КОН/г и молекулярный вес от 400 до 10000, в присутствии аминового катализатора, отличающийся тем, что упомянутый аминовый катализатор выбран из группы, состоящей из 2,2'-диморфолинодиэтилового эфира, 1-метилимидазола, 4-диметиламинопиридина и 4-пирролидинопиридина.
2. Способ согласно п. 1, где упомянутый аминовый катализатор используют в количестве между 0,05 и 5 вес.% от веса реакционно-способного по отношению к изоцианату состава.
3. Способ согласно одному из предшествующих пунктов, где используют дополнительный трет-аминовый катализатор.
4. Способ согласно п. 3, где упомянутый дополнительный катализатор представляет собой пентаметилдиэтилентриамин.
5. Способ согласно п. 3 или 4, где упомянутый дополнительный катализатор используют в количестве между 0,01 и 5 вес.% от веса реакционно-способного по отношению к изоцианату состава.
6. Способ согласно одному из предшествующих пунктов, где сложный полиэфирполиол составляет по крайней мере 10 вес.% от веса соединений, реакционно-способных по отношению к изоцианату.
7. Способ согласно одному из предшествующих пунктов, где упомянутую реакцию проводят в присутствии органической карбоновой кислоты, содержащей гидроксильные группы.
8. Способ согласно п. 7, где упомянутая карбоновая кислота, содержащая гидроксильные функциональные группы, выбрана из группы, состоящей из молочной кислоты, гликолевой кислоты, яблочной кислоты, лимонной кислоты.
9. Способ согласно п. 8, где в качестве карбоновой кислоты используют смесь лимонной кислоты и яблочной кислоты в весовом отношении примерно 1:1.
10. Способ согласно пп. 7, 8 или 9, где упомянутую карбоновую кислоту, содержащую гидроксильные функциональные группы, используют в количестве, находящемся в диапазоне от 0,1 до 5 вес.% от веса реакционно-способного по отношению к изоцианату состава.
11. Жесткие пенополиуретаны или пенополиизоцианураты модифицированные уретаном, получаемые по способу, как определено в любом из предшествующих пунктов.
12. Реакционно-способный по отношению к изоцианату состав, включающий сложный полиэфирполиол, имеющий среднее количество функциональных групп от 1,8 до 8, гидроксильное число от 15 до 750 мг КОН/г и молекулярный вес от 400 до 10000 и аминовый катализатор, отличающийся тем, что упомянутый аминовый катализатор представляет собой такой катализатор, как определено в п. 1 или 2.
13. Реакционно-способный по отношению к изоцианату состав согласно п. 12, где упомянутый состав дополнительно включает карбоновую кислоту, содержащую гидроксильные функциональные группы, как определено в любом из пп. 7 - 10.