RU96116894A - Корпус режущего инструмента и способ нанесения на него оксидного покрытия - Google Patents
Корпус режущего инструмента и способ нанесения на него оксидного покрытияInfo
- Publication number
- RU96116894A RU96116894A RU96116894/02A RU96116894A RU96116894A RU 96116894 A RU96116894 A RU 96116894A RU 96116894/02 A RU96116894/02 A RU 96116894/02A RU 96116894 A RU96116894 A RU 96116894A RU 96116894 A RU96116894 A RU 96116894A
- Authority
- RU
- Russia
- Prior art keywords
- hkl
- layer
- cutting tool
- coating
- exceeding
- Prior art date
Links
- 239000011248 coating agent Substances 0.000 title claims 4
- 238000000576 coating method Methods 0.000 title claims 4
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims 7
- 229910034327 TiC Inorganic materials 0.000 claims 2
- 239000007789 gas Substances 0.000 claims 2
- 238000010899 nucleation Methods 0.000 claims 2
- 230000003647 oxidation Effects 0.000 claims 2
- 238000007254 oxidation reaction Methods 0.000 claims 2
- 239000000654 additive Substances 0.000 claims 1
- 230000000996 additive Effects 0.000 claims 1
- PNEYBMLMFCGWSK-UHFFFAOYSA-N al2o3 Chemical compound [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 claims 1
- 229910052782 aluminium Inorganic materials 0.000 claims 1
- -1 aluminum halides Chemical class 0.000 claims 1
- 230000015572 biosynthetic process Effects 0.000 claims 1
- 239000000919 ceramic Substances 0.000 claims 1
- 239000003795 chemical substances by application Substances 0.000 claims 1
- 229910052739 hydrogen Inorganic materials 0.000 claims 1
- 239000001257 hydrogen Substances 0.000 claims 1
- UFHFLCQGNIYNRP-UHFFFAOYSA-N hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 claims 1
- 230000003301 hydrolyzing Effects 0.000 claims 1
- 230000001590 oxidative Effects 0.000 claims 1
- 239000000843 powder Substances 0.000 claims 1
- 239000000126 substance Substances 0.000 claims 1
- NINIDFKCEFEMDL-UHFFFAOYSA-N sulfur Chemical compound [S] NINIDFKCEFEMDL-UHFFFAOYSA-N 0.000 claims 1
- 229910052717 sulfur Inorganic materials 0.000 claims 1
- 239000011593 sulfur Substances 0.000 claims 1
- RTAQQCXQSZGOHL-UHFFFAOYSA-N titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 claims 1
- 229910052719 titanium Inorganic materials 0.000 claims 1
- 239000010936 titanium Substances 0.000 claims 1
Claims (6)
1. Корпус режущего инструмента, имеющий покрытие по меньшей мере частичное, образованное одним или несколькими тугоплавкими слоями, одним из которых является слой оксида алюминия, отличающийся тем, что указанный слой Al2O3 имеет толщину d = 0,5 - 25 мкм, со средним размером зерна (s), который составляет 0,5 мкм < s < 1 мкм, для d: 0,5 мкм < d < 2,5 мкм и 0,5 мкм < s < 4 мкм, для d: 2,5 мкм < d < 25 мкм и состоит из единственной фазы α - -структуры, текстурированной в направлении (104), причем коэффициент текстуры превышает 1,5, преимущественно превышает 2,5, предпочтительно превышает 3,0, при этом коэффициент текстуры определен следующим образом:
TC(hkl)=I(hkl)/Io(hkl) {1/n Σ I(hkl)/Io(hkl)}-1
где I(hkl) - измеренная интенсивность (hkl) отражения;
Io(hkl) - стандартная интенсивность данных отражения от стандартной порошковой картины ASTM;
n - число отражений, использованных при вычислениях, причем использованными (hkl) отражениями являются: (012), (104), (110), (113), (024), (116).
TC(hkl)=I(hkl)/Io(hkl) {1/n Σ I(hkl)/Io(hkl)}-1
где I(hkl) - измеренная интенсивность (hkl) отражения;
Io(hkl) - стандартная интенсивность данных отражения от стандартной порошковой картины ASTM;
n - число отражений, использованных при вычислениях, причем использованными (hkl) отражениями являются: (012), (104), (110), (113), (024), (116).
2. Корпус режущего инструмента по п.1, отличающийся тем, что слой Al2O3 представляет собой самый верхний обнаженный слой.
3. Корпус режущего инструмента по пп. 1 и 2, отличающийся тем, что слой Al2O3 находится в контакте со слоем TiCxNyOz.
4. Корпус режущего инструмента по п. 3, отличающийся тем, что слой TiCx NyOz является самым нижним слоем покрытия.
5. Корпус режущего инструмента по одному из пп. 1-4, отличающийся тем, что он представляет собой режущую пластину из цементированного карбида, карбонитрида на базе титана или керамики.
6. Способ нанесения на корпус режущего инструмента покрытия α-Al2O3, при котором корпус вводят в контакт с транспортирующим газом водородом, содержащим один или несколько галидов алюминия и агент гидролизации или оксидации при высокой температуре, отличающийся тем, что потенциал оксидации атмосферы реактора CVD ранее образования центров кристаллизации Al2O3 поддерживается на низком уровне, с использованием полной концентрации H2O или других окисляющих веществ, преимущественно составляющем менее 5 млн-1, причем образование центров кристаллизации Al2O3, начинается с контролируемой последовательности подачи реагирующих газов, при которой вначале в реактор вводят CO2 и CO в атмосфере N2 и/или Ar, вслед за чем вводят H2 и AlCl3 при этом температура в ходе образования центров кристаллизации преимущественно составляет 950-1000oC, причем во время роста Al2O3 добавляют сернистую присадку, преимущественно H2S.