RU2018137905A - Тонкие волокна, полученные путем сшивания при комнатной температуре - Google Patents

Тонкие волокна, полученные путем сшивания при комнатной температуре Download PDF

Info

Publication number
RU2018137905A
RU2018137905A RU2018137905A RU2018137905A RU2018137905A RU 2018137905 A RU2018137905 A RU 2018137905A RU 2018137905 A RU2018137905 A RU 2018137905A RU 2018137905 A RU2018137905 A RU 2018137905A RU 2018137905 A RU2018137905 A RU 2018137905A
Authority
RU
Russia
Prior art keywords
epoxide
composition
solvent
polymer component
fiber
Prior art date
Application number
RU2018137905A
Other languages
English (en)
Other versions
RU2018137905A3 (ru
RU2749977C2 (ru
Inventor
Суреш Лаксман ШЕНОЙ
Original Assignee
Дональдсон Компани, Инк.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Дональдсон Компани, Инк. filed Critical Дональдсон Компани, Инк.
Publication of RU2018137905A publication Critical patent/RU2018137905A/ru
Publication of RU2018137905A3 publication Critical patent/RU2018137905A3/ru
Application granted granted Critical
Publication of RU2749977C2 publication Critical patent/RU2749977C2/ru

Links

Classifications

    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/44—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from mixtures of polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds as major constituent with other polymers or low-molecular-weight compounds
    • D01F6/56—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from mixtures of polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds as major constituent with other polymers or low-molecular-weight compounds of polymers of cyclic compounds with one carbon-to-carbon double bond in the side chain
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D39/00—Filtering material for liquid or gaseous fluids
    • B01D39/14—Other self-supporting filtering material ; Other filtering material
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01D—MECHANICAL METHODS OR APPARATUS IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS
    • D01D5/00—Formation of filaments, threads, or the like
    • D01D5/0007—Electro-spinning
    • D01D5/0015—Electro-spinning characterised by the initial state of the material
    • D01D5/003—Electro-spinning characterised by the initial state of the material the material being a polymer solution or dispersion
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D39/00—Filtering material for liquid or gaseous fluids
    • B01D39/14—Other self-supporting filtering material ; Other filtering material
    • B01D39/16—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres
    • B01D39/1607—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres the material being fibrous
    • B01D39/1623—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres the material being fibrous of synthetic origin
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D39/00—Filtering material for liquid or gaseous fluids
    • B01D39/14—Other self-supporting filtering material ; Other filtering material
    • B01D39/16—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres
    • B01D39/18—Other self-supporting filtering material ; Other filtering material of organic material, e.g. synthetic fibres the material being cellulose or derivatives thereof
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J7/00—Chemical treatment or coating of shaped articles made of macromolecular substances
    • C08J7/04—Coating
    • C08J7/0427—Coating with only one layer of a composition containing a polymer binder
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L39/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a single or double bond to nitrogen or by a heterocyclic ring containing nitrogen; Compositions of derivatives of such polymers
    • C08L39/04—Homopolymers or copolymers of monomers containing heterocyclic rings having nitrogen as ring member
    • C08L39/08—Homopolymers or copolymers of vinyl-pyridine
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F1/00—General methods for the manufacture of artificial filaments or the like
    • D01F1/02—Addition of substances to the spinning solution or to the melt
    • D01F1/10—Other agents for modifying properties
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F8/00—Conjugated, i.e. bi- or multicomponent, artificial filaments or the like; Manufacture thereof
    • D01F8/04—Conjugated, i.e. bi- or multicomponent, artificial filaments or the like; Manufacture thereof from synthetic polymers
    • D01F8/10—Conjugated, i.e. bi- or multicomponent, artificial filaments or the like; Manufacture thereof from synthetic polymers with at least one other macromolecular compound obtained by reactions only involving carbon-to-carbon unsaturated bonds as constituent
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F8/00—Conjugated, i.e. bi- or multicomponent, artificial filaments or the like; Manufacture thereof
    • D01F8/04—Conjugated, i.e. bi- or multicomponent, artificial filaments or the like; Manufacture thereof from synthetic polymers
    • D01F8/12—Conjugated, i.e. bi- or multicomponent, artificial filaments or the like; Manufacture thereof from synthetic polymers with at least one polyamide as constituent
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F8/00—Conjugated, i.e. bi- or multicomponent, artificial filaments or the like; Manufacture thereof
    • D01F8/04—Conjugated, i.e. bi- or multicomponent, artificial filaments or the like; Manufacture thereof from synthetic polymers
    • D01F8/16—Conjugated, i.e. bi- or multicomponent, artificial filaments or the like; Manufacture thereof from synthetic polymers with at least one other macromolecular compound obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds as constituent
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M13/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment
    • D06M13/10—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with non-macromolecular organic compounds; Such treatment combined with mechanical treatment with compounds containing oxygen
    • D06M13/11—Compounds containing epoxy groups or precursors thereof
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M15/00—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment
    • D06M15/19—Treating fibres, threads, yarns, fabrics, or fibrous goods made from such materials, with macromolecular compounds; Such treatment combined with mechanical treatment with synthetic macromolecular compounds
    • D06M15/21—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D06M15/356—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds of other unsaturated compounds containing nitrogen, sulfur, silicon or phosphorus atoms
    • D06M15/3562—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds of other unsaturated compounds containing nitrogen, sulfur, silicon or phosphorus atoms containing nitrogen
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/02—Types of fibres, filaments or particles, self-supporting or supported materials
    • B01D2239/0208—Single-component fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/02—Types of fibres, filaments or particles, self-supporting or supported materials
    • B01D2239/0216—Bicomponent or multicomponent fibres
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/06—Filter cloth, e.g. knitted, woven non-woven; self-supported material
    • B01D2239/0604—Arrangement of the fibres in the filtering material
    • B01D2239/0618—Non-woven
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/06—Filter cloth, e.g. knitted, woven non-woven; self-supported material
    • B01D2239/0604—Arrangement of the fibres in the filtering material
    • B01D2239/0627—Spun-bonded
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/06—Filter cloth, e.g. knitted, woven non-woven; self-supported material
    • B01D2239/0604—Arrangement of the fibres in the filtering material
    • B01D2239/0631—Electro-spun
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2239/00—Aspects relating to filtering material for liquid or gaseous fluids
    • B01D2239/10—Filtering material manufacturing
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2339/00—Characterised by the use of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by a single or double bond to nitrogen or by a heterocyclic ring containing nitrogen; Derivatives of such polymers
    • C08J2339/04—Homopolymers or copolymers of monomers containing heterocyclic rings having nitrogen as ring member
    • C08J2339/08—Homopolymers or copolymers of vinyl-pyridine
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
    • C08J2463/00—Characterised by the use of epoxy resins; Derivatives of epoxy resins
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2205/00—Polymer mixtures characterised by other features
    • C08L2205/14—Polymer mixtures characterised by other features containing polymeric additives characterised by shape
    • C08L2205/16—Fibres; Fibrils
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F6/00—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof
    • D01F6/88—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from mixtures of polycondensation products as major constituent with other polymers or low-molecular-weight compounds
    • D01F6/90—Monocomponent artificial filaments or the like of synthetic polymers; Manufacture thereof from mixtures of polycondensation products as major constituent with other polymers or low-molecular-weight compounds of polyamides

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Textile Engineering (AREA)
  • General Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Health & Medical Sciences (AREA)
  • Medicinal Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Dispersion Chemistry (AREA)
  • Mechanical Engineering (AREA)
  • Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
  • Artificial Filaments (AREA)
  • Nonwoven Fabrics (AREA)
  • Filtering Materials (AREA)
  • Epoxy Resins (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Spinning Methods And Devices For Manufacturing Artificial Fibers (AREA)

Claims (42)

1. Способ получения тонкого волокна, причем способ включает:
обеспечение полимерного компонента, где полимерный компонент содержит полимер, содержащий 4-винилпиридин;
обеспечение растворителя, который не образует комплекс с 4-винилпиридином; обеспечение эпоксида, где эпоксид является по меньшей мере дифункциональным; и
объединение полимерного компонента, растворителя и эпоксида с образованием композиции и образование множества волокон из композиции таким образом, чтобы полный объем каждого волокна был получен из композиции.
2. Способ получения тонкого волокна, причем способ включает:
обеспечение полимерного компонента, где полимерный компонент содержит полимер, содержащий 4-винилпиридин; обеспечение растворителя;
обеспечение эпоксида, где эпоксид является по меньшей мере дифункциональным; и
объединение полимерного компонента, растворителя и эпоксида с образованием композиции и образование множества волокон из композиции таким образом, чтобы полный объем каждого волокна был получен из композиции без повышения температуры композиции выше 80°С.
3. Способ по п. 2, где полимерный компонент, растворитель и эпоксид объединяют при комнатной температуре и образуют множество волокон без повышения температуры композиции выше комнатной температуры.
4. Способ по любому из пп. 1-3, где объединение полимерного компонента, растворителя и эпоксида с образованием композиции и образование множества волокон из композиции осуществляют одновременно.
5. Способ по любому из пп. 1-4, где объединение полимерного компонента, растворителя и эпоксида с образованием композиции и образование множества волокон из композиции включают:
смешивание полимерного компонента, растворителя и эпоксида;
обеспечение протекания реакции полимера, содержащего 4-винилпиридин, и эпоксида и
удаление по меньшей мере части растворителя.
6. Способ получения покрытого тонкого волокна, причем способ включает:
обеспечение полимерного компонента, где полимерный компонент содержит полимер, содержащий 4-винилпиридин;
обеспечение растворителя, который не образует комплекс с 4-винилпиридином;
обеспечение эпоксида, где эпоксид является по меньшей мере дифункциональным;
обеспечение волокна и
объединение полимерного компонента, растворителя и эпоксида с образованием композиции и покрытие волокна с помощью композиции.
7. Способ получения покрытого тонкого волокна, причем способ включает:
обеспечение полимерного компонента, где полимерный компонент содержит полимер, содержащий 4-винилпиридин;
обеспечение растворителя;
обеспечение эпоксида, где эпоксид является по меньшей мере дифункциональным;
обеспечение волокна и
объединение полимерного компонента, растворителя и эпоксида с образованием композиции и покрытие волокна с помощью композиции без повышения температуры композиции или температуры волокна выше 80°С.
8. Способ по п. 7, где полимерный компонент, растворитель и эпоксид объединяют при комнатной температуре и волокно покрывают без повышения температуры композиции или температуры волокна выше комнатной температуры.
9. Способ по любому из пп. 6-8, где объединение полимерного компонента, растворителя и эпоксида с образованием композиции и покрытие волокна с помощью композиции осуществляют одновременно.
10. Способ по любому из пп. 6-9, где объединение полимерного компонента, растворителя и эпоксида с образованием композиции и покрытие волокна с помощью композиции включают:
смешивание полимерного компонента, растворителя и эпоксида;
обеспечение протекания реакции полимера, содержащего 4-винилпиридин, и эпоксида и
удаление по меньшей мере части растворителя.
11. Способ по любому из пп. 1-10, где растворитель предусматривает этанол.
12. Способ по любому из пп. 1-11, где растворитель предусматривает апротонный растворитель.
13. Способ по любому из пп. 1-12, где полимер, содержащий 4-винилпиридин, предусматривает гомополимер поли(4-винилпиридин), сополимер на основе 4-винилпиридина или их смесь.
14. Способ по любому из пп. 1-13, где полимерный компонент дополнительно содержит нейлон, полиамидный терполимер, поливинилбутираль (PVB), поливиниловый спирт (PVA) или полиуретан, или их комбинацию.
15. Способ по любому из пп. 1-14, где эпоксид предусматривает диглицидиловый эфир 1,4-бутандиола, диглицидиловый эфир бисфенола А, эпоксидную смолу на основе бисфенола F, эпоксидную смолу на основе бисфенола A/F, эпоксидную смолу на основе модифицированного бисфенола А, бромированную эпоксидную смолу, новолачную эпоксидную смолу, фенольную новолачную эпоксидную смолу, крезольную новолачную эпоксидную смолу, дифункциональную циклоалифатическую эпоксидную смолу или мультифункциональную эпоксидную смолу глицидиламинового типа или их комбинацию.
16. Способ по любому из пп. 1-15, где полимерный компонент содержит по меньшей мере 20 вес. % полимера, содержащего 4-винилпиридин, в пересчете на полимерные твердые вещества.
17. Тонкое волокно, где полный объем волокна содержит композицию, при этом композиция содержит продукт реакции полимерного компонента и эпоксида, где полимерный компонент содержит полимер, содержащий 4-винилпиридин, и при этом дополнительно эпоксид является по меньшей мере дифункциональным.
18. Тонкое волокно по п. 17, где полимер, содержащий 4-винилпиридин, предусматривает гомополимер поли(4-винилпиридин), сополимер на основе 4-винилпиридина или их смесь.
19. Фильтрующая среда, содержащая множество волокон по любому из пп. 17 или 18.
20. Фильтрующая среда по п. 19, дополнительно содержащая подложку для фильтрации, где множество волокон расположено на подложке с образованием тонковолоконного слоя.
RU2018137905A 2016-04-06 2017-04-06 Тонкие волокна, полученные путем сшивания при комнатной температуре RU2749977C2 (ru)