MX2015003967A - Metodo para manufacturar lamina de acero chapada con aleacion de zinc sumergida en caliente. - Google Patents
Metodo para manufacturar lamina de acero chapada con aleacion de zinc sumergida en caliente.Info
- Publication number
- MX2015003967A MX2015003967A MX2015003967A MX2015003967A MX2015003967A MX 2015003967 A MX2015003967 A MX 2015003967A MX 2015003967 A MX2015003967 A MX 2015003967A MX 2015003967 A MX2015003967 A MX 2015003967A MX 2015003967 A MX2015003967 A MX 2015003967A
- Authority
- MX
- Mexico
- Prior art keywords
- dip
- steel sheet
- alloy
- hot
- polyatomic ion
- Prior art date
Abstract
Una capa de chapado de aleación de Zn sumergida en caliente se forma sobre una superficie de una lámina de acero base al sumergir la lámina de acero base en un baño de chapado de aleación de Zn sumergida en caliente que contiene Al y Mg. Una solución acuosa que contiene uno de o dos o más de los iones poliatómicos seleccionados del grupo que consiste de un ión poliatómico que incluye V5+, un ión poliatómico que incluye Si4+ y un ión poliatómico que incluye Cr6+ entonces se pone en contacto con una superficie de la capa de chapado de aleación de Zn sumergida en caliente. La solución acuosa contiene el ión poliatómico en una concentración de 0.01 g/L o más en términos de uno de o dos o más de los átomos seleccionados del grupo que consiste en V, Si y Cr.
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2012258582 | 2012-11-27 | ||
JP2013019275A JP5356616B1 (ja) | 2012-11-27 | 2013-02-04 | 溶融Zn合金めっき鋼板の製造方法 |
PCT/JP2013/001312 WO2014083713A1 (ja) | 2012-11-27 | 2013-03-04 | 溶融Zn合金めっき鋼板の製造方法 |
Publications (2)
Publication Number | Publication Date |
---|---|
MX2015003967A true MX2015003967A (es) | 2015-11-16 |
MX344320B MX344320B (es) | 2016-12-13 |
Family
ID=49850235
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2015003967A MX344320B (es) | 2012-11-27 | 2013-03-04 | Método para manufacturar lámina de acero chapada con aleación de zinc sumergida en caliente. |
Country Status (15)
Country | Link |
---|---|
US (2) | US10167542B2 (es) |
EP (1) | EP2927344B1 (es) |
JP (2) | JP5356616B1 (es) |
KR (1) | KR101572673B1 (es) |
CN (1) | CN104838036B (es) |
AU (1) | AU2013350682B2 (es) |
BR (1) | BR112015010935B1 (es) |
CA (1) | CA2886690C (es) |
ES (1) | ES2663957T3 (es) |
IN (1) | IN2015DN02452A (es) |
MX (1) | MX344320B (es) |
MY (1) | MY170543A (es) |
PL (1) | PL2927344T3 (es) |
RU (1) | RU2590443C1 (es) |
WO (1) | WO2014083713A1 (es) |
Families Citing this family (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
TWI653362B (zh) * | 2012-10-17 | 2019-03-11 | 澳大利亞商布魯史寇普鋼鐵有限公司 | 金屬被覆鋼帶的製造方法 |
JP5356616B1 (ja) | 2012-11-27 | 2013-12-04 | 日新製鋼株式会社 | 溶融Zn合金めっき鋼板の製造方法 |
JP6022433B2 (ja) * | 2013-12-03 | 2016-11-09 | 日新製鋼株式会社 | 溶融Zn合金めっき鋼板の製造方法 |
JP5748829B2 (ja) * | 2013-12-03 | 2015-07-15 | 日新製鋼株式会社 | 溶融Zn合金めっき鋼板およびその製造方法 |
EP3156512B1 (en) * | 2014-07-24 | 2022-01-12 | Nippon Steel Corporation | Method for cooling steel strip and cooling installation |
ES2769960T3 (es) * | 2015-03-31 | 2020-06-29 | Nippon Steel Nisshin Co Ltd | Uso de una lámina de acero chapada como lámina de acero absorbente y radiante de calor |
JP5989274B1 (ja) * | 2015-03-31 | 2016-09-07 | 日新製鋼株式会社 | 吸放熱鋼板および吸放熱部材 |
JP6760002B2 (ja) * | 2016-11-16 | 2020-09-23 | Jfeスチール株式会社 | 鋼板の冷却方法 |
KR102240878B1 (ko) * | 2017-01-27 | 2021-04-15 | 닛폰세이테츠 가부시키가이샤 | 도금 강재 |
KR102031466B1 (ko) | 2017-12-26 | 2019-10-11 | 주식회사 포스코 | 표면품질 및 내식성이 우수한 아연합금도금강재 및 그 제조방법 |
CN110004389B (zh) * | 2019-03-20 | 2021-06-15 | 首钢集团有限公司 | 一种抗黑变锌铝镁镀层钢及其制备方法 |
US11384419B2 (en) * | 2019-08-30 | 2022-07-12 | Micromaierials Llc | Apparatus and methods for depositing molten metal onto a foil substrate |
CN113621852B (zh) * | 2021-07-13 | 2023-02-17 | 株洲冶炼集团股份有限公司 | 一种锌铝镁涂镀材料及其制备方法 |
CN113846256A (zh) * | 2021-08-16 | 2021-12-28 | 株洲冶炼集团股份有限公司 | 一种高铝热镀锌多元合金 |
WO2023145822A1 (ja) * | 2022-01-31 | 2023-08-03 | 日本製鉄株式会社 | めっき鋼板 |
Family Cites Families (30)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3125471A (en) * | 1964-03-17 | Commercially available sheet finishes | ||
US2312066A (en) * | 1939-11-30 | 1943-02-23 | Batcheller Clements | Method of coloring stainless steel |
FR2043646A1 (es) | 1969-05-24 | 1971-02-19 | Parker Ste Continentale | |
BE762838A (fr) | 1971-02-11 | 1971-08-11 | Centre Rech Metallurgique | Procede et dispositif pour la fabrication de ronds a beton, |
JPS5319974B2 (es) * | 1972-10-04 | 1978-06-23 | ||
US4270317A (en) * | 1978-10-10 | 1981-06-02 | Midland-Ross Corporation | Apparatus used in the treatment of a continuous strip of metal and method of use thereof |
US4282073A (en) * | 1979-08-22 | 1981-08-04 | Thomas Steel Strip Corporation | Electro-co-deposition of corrosion resistant nickel/zinc alloys onto steel substrates |
JPS602186B2 (ja) * | 1980-12-24 | 1985-01-19 | 日本鋼管株式会社 | 塗装下地用表面処理鋼板 |
JPS5848657A (ja) * | 1981-09-16 | 1983-03-22 | Hitachi Ltd | 溶融亜鉛メツキ鋼板のスパングル制御法 |
JPS6372887A (ja) * | 1986-09-12 | 1988-04-02 | Nisshin Steel Co Ltd | 耐食性、耐加工性に優れた溶融めつき鋼板の製造方法 |
JPS63297576A (ja) * | 1987-05-29 | 1988-12-05 | Nisshin Steel Co Ltd | 耐黒変性に優れた溶融めっき鋼板の製造方法 |
JPS6411983A (en) * | 1987-07-03 | 1989-01-17 | Nisshin Steel Co Ltd | Hot dipped steel sheet having superior blackening resistance |
JP2754126B2 (ja) * | 1992-11-26 | 1998-05-20 | 新日本製鐵株式会社 | 外観、耐経時黒変性、耐食性に優れる溶融Zn−Alめっき鋼板 |
JPH06336664A (ja) * | 1993-05-27 | 1994-12-06 | Kobe Steel Ltd | スポット溶接性に優れた亜鉛−アルミニウム系めっき 鋼板の製造方法 |
JP3729233B2 (ja) * | 1998-03-31 | 2005-12-21 | 日新製鋼株式会社 | 黒変抵抗をもつ溶融亜鉛基めっき鋼板 |
JP4555491B2 (ja) * | 2000-03-16 | 2010-09-29 | 新日本製鐵株式会社 | 化成処理性に優れた溶融亜鉛−アルミニウム合金めっき鋼板とその製造方法 |
US20030209293A1 (en) * | 2000-05-11 | 2003-11-13 | Ryousuke Sako | Metal surface treatment agent |
JP4064634B2 (ja) | 2001-02-02 | 2008-03-19 | 日新製鋼株式会社 | 光沢保持性の良好な溶融Zn基めっき鋼板およびその製造法 |
DE10110833B4 (de) * | 2001-03-06 | 2005-03-24 | Chemetall Gmbh | Verfahren zum Aufbringen eines Phosphatüberzuges und Verwendung der derart phosphatierten Metallteile |
JP4078044B2 (ja) * | 2001-06-26 | 2008-04-23 | 日本パーカライジング株式会社 | 金属表面処理剤、金属材料の表面処理方法及び表面処理金属材料 |
BE1014525A3 (fr) * | 2001-12-04 | 2003-12-02 | Ct Rech Metallurgiques Asbl | Procede de revetement de surface metallique. |
JP2004176092A (ja) * | 2002-11-25 | 2004-06-24 | Kobe Steel Ltd | 溶接性および耐食性に優れた樹脂被覆溶融亜鉛系めっき鋼板並びにその製造方法 |
JP2005139518A (ja) | 2003-11-07 | 2005-06-02 | Jfe Steel Kk | 化成処理金属帯の製造設備および製造方法 |
JP4804996B2 (ja) * | 2006-04-07 | 2011-11-02 | 新日本製鐵株式会社 | 加工性、パウダリング性、摺動性の良好な合金化溶融亜鉛メッキ鋼板の製造方法 |
JP5088095B2 (ja) * | 2006-12-13 | 2012-12-05 | Jfeスチール株式会社 | 平板部耐食性、耐黒変性およびプレス成形後の外観と耐食性に優れた表面処理亜鉛系めっき鋼板、並びに亜鉛系めっき鋼板用水系表面処理液 |
JP5196916B2 (ja) * | 2007-08-30 | 2013-05-15 | 日本パーカライジング株式会社 | 溶融めっき鋼材の表面改質処理方法、及び表面改質された溶融金属めっき鋼材 |
JP2009102688A (ja) * | 2007-10-22 | 2009-05-14 | Nisshin Steel Co Ltd | 化成処理鋼板 |
JP4226063B1 (ja) * | 2008-02-25 | 2009-02-18 | シーケー金属株式会社 | 溶融亜鉛めっき処理品の生産方法 |
US20110146516A1 (en) * | 2008-08-22 | 2011-06-23 | Fujifilm Corporation | Method of preparing lithographic printing plate |
JP5356616B1 (ja) * | 2012-11-27 | 2013-12-04 | 日新製鋼株式会社 | 溶融Zn合金めっき鋼板の製造方法 |
-
2013
- 2013-02-04 JP JP2013019275A patent/JP5356616B1/ja active Active
- 2013-03-04 ES ES13859545.9T patent/ES2663957T3/es active Active
- 2013-03-04 EP EP13859545.9A patent/EP2927344B1/en active Active
- 2013-03-04 IN IN2452DEN2015 patent/IN2015DN02452A/en unknown
- 2013-03-04 WO PCT/JP2013/001312 patent/WO2014083713A1/ja active Application Filing
- 2013-03-04 CA CA2886690A patent/CA2886690C/en active Active
- 2013-03-04 CN CN201380061100.9A patent/CN104838036B/zh active Active
- 2013-03-04 MY MYPI2015701690A patent/MY170543A/en unknown
- 2013-03-04 RU RU2015119973/02A patent/RU2590443C1/ru active
- 2013-03-04 KR KR1020157012632A patent/KR101572673B1/ko active IP Right Grant
- 2013-03-04 MX MX2015003967A patent/MX344320B/es active IP Right Grant
- 2013-03-04 AU AU2013350682A patent/AU2013350682B2/en active Active
- 2013-03-04 BR BR112015010935-7A patent/BR112015010935B1/pt active IP Right Grant
- 2013-03-04 PL PL13859545T patent/PL2927344T3/pl unknown
- 2013-03-04 US US14/349,334 patent/US10167542B2/en active Active
- 2013-08-28 JP JP2013176827A patent/JP5450874B1/ja active Active
-
2015
- 2015-06-24 US US14/748,279 patent/US10202676B2/en active Active
Also Published As
Publication number | Publication date |
---|---|
AU2013350682A1 (en) | 2015-04-30 |
JP5356616B1 (ja) | 2013-12-04 |
ES2663957T3 (es) | 2018-04-17 |
MY170543A (en) | 2019-08-16 |
CN104838036A (zh) | 2015-08-12 |
JP2014129589A (ja) | 2014-07-10 |
CA2886690C (en) | 2015-08-25 |
KR101572673B1 (ko) | 2015-11-27 |
BR112015010935B1 (pt) | 2020-12-22 |
CN104838036B (zh) | 2016-08-24 |
EP2927344A4 (en) | 2016-10-26 |
EP2927344A1 (en) | 2015-10-07 |
EP2927344B1 (en) | 2018-02-21 |
US10167542B2 (en) | 2019-01-01 |
JP2014129588A (ja) | 2014-07-10 |
BR112015010935A2 (pt) | 2017-07-11 |
JP5450874B1 (ja) | 2014-03-26 |
US20150292073A1 (en) | 2015-10-15 |
US20150259776A1 (en) | 2015-09-17 |
RU2590443C1 (ru) | 2016-07-10 |
CA2886690A1 (en) | 2014-06-05 |
PL2927344T3 (pl) | 2018-08-31 |
US10202676B2 (en) | 2019-02-12 |
IN2015DN02452A (es) | 2015-09-04 |
MX344320B (es) | 2016-12-13 |
KR20150061011A (ko) | 2015-06-03 |
WO2014083713A1 (ja) | 2014-06-05 |
AU2013350682B2 (en) | 2015-06-04 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX344320B (es) | Método para manufacturar lámina de acero chapada con aleación de zinc sumergida en caliente. | |
MY161119A (en) | Steel sheet for container and method of manufacturing the same | |
PH12017501577A1 (en) | HOT-DIP Al-Zn-Mg-Si COATED STEEL SHEET AND METHOD OF PRODUCING SAME | |
MX2015014795A (es) | Lamina de acero galvanizada por inmersion de caliente para estampado en caliente y metodo para fabricar piezas de acero. | |
MY172822A (en) | Composition for metal electroplating comprising leveling agent | |
MY166781A (en) | High-corrosion-resistance hot-dip galvanized steel sheet having excellent appearance uniformity and manufacturing method thereof | |
IN2014MN02124A (es) | ||
TW200736415A (en) | Electroform, methods of making electroforms, and products made from electroforms | |
MY162565A (en) | Steel sheet for containers and manufacturing method for same | |
HK1143194A1 (en) | Method to electrodeposit metals using ionic liquids in the presence of an additive | |
MX2016012502A (es) | Hoja de acero chapado que contiene cuasicristal. | |
WO2010127094A3 (en) | High speed copper plating bath | |
MY162540A (en) | Steel sheet for containers and manufacturing method for same | |
MY172243A (en) | Hot-dip zinc alloy coated steel sheet excellent in coating adhesion, and method for producing the same | |
MX2015013517A (es) | Lamina de acero recubierta de aleacion de ai-zn por inmersion en caliente y metodo para la produccion de la misma. | |
MX2015014999A (es) | Lamina de acero galvanizada y recocida y metodo para fabricar la misma. | |
GB201100447D0 (en) | Improvements in coating technology | |
MX354008B (es) | Tubo de metal para tuberia de vehiculo y metodo de tratamiento de superficie para tubo. | |
WO2016124921A3 (en) | Electrolyte for electroplating | |
MX2016001902A (es) | Metodo para la produccion de lamina de acero galvanizada por inmersion en caliente de alta resistencia y metodo para la produccion de lamina de acero recocida despues de galvanizada de alta resistencia. | |
MX2016001657A (es) | Lamina de acero recubierta con ai que tiene excelentes caracteristicas de reflexion total y resistencia a la corrosion, y metodo para fabricar la misma. | |
MY152832A (en) | Tin-plated steel sheet and method for manufacturing the same | |
MY161932A (en) | Hot-dip zinc-aluminium alloy coated steel sheet having high corrosion resistance and formability and method for producing the same | |
IN2015DN02512A (es) | ||
MX2015013578A (es) | Lamina de acero recubierta de aluminio-zinc. |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
FG | Grant or registration |