KR960701943A - 프로필렌 중합체조성물의 제조방법 및 프로필렌 중합체조성물 - Google Patents
프로필렌 중합체조성물의 제조방법 및 프로필렌 중합체조성물Info
- Publication number
- KR960701943A KR960701943A KR1019950704627A KR19950704627A KR960701943A KR 960701943 A KR960701943 A KR 960701943A KR 1019950704627 A KR1019950704627 A KR 1019950704627A KR 19950704627 A KR19950704627 A KR 19950704627A KR 960701943 A KR960701943 A KR 960701943A
- Authority
- KR
- South Korea
- Prior art keywords
- propylene
- ethylene
- carbon atoms
- polymer composition
- olefin copolymer
- Prior art date
Abstract
시클로펜타디에닐 골격을 갖는 배위자를 포함하는 전이금속화합물(A)과 상기 전이금속화합물(A)을 활성화시키는 활성화 화합물(B)의 존재하에, 프로필렌(공)중합체(a)를 제조하는 공정(a)과, 프로필렌/올레핀공중합체(b)를 제조하는 공정(b) 및 에틸렌/올레핀공중합체(c)를 제조하는 공정(c)을 포함하는 다단중합을 임의의 순서에 따라 행하고, 또 2번째 단계이후의 중합공정은 전단계까지의 중합공정에서 얻은 중합체의 존재하에 행하고, 프로필렌(공)중합체(a)를 20∼90중량% 비율로 함유하고, 프로필렌/올레핀공중합체(b)를 5∼75%중량%의 비율로 함유하고, 에틸렌/올레핀공중합체(c)를 5∼75중량% 비율로 함유하고, 230℃, 하중 2.16kg에서 측정한 멜트플로우레이트가 0.01∼5009/10분인 프로필렌 중합체 조성물을 제조하는 프로필렌 중합체 조성물의 제조방법 및 이 제조방법에 의해서 제조된 프로필렌중합체조성물에 관한 것이다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (16)
- (A) 시클로펜타디에닐 골격을 갖는 배위자를 포함하는 전이금속화합물과, (B) 상기 전이금속화합물(A)을 활성화시키는 화합물의 존재하에서 하기 공정(a)와 (b) 및 (c)를 포함하는 다단중합을 임의의 순서에 따라 행하고, 2번째 단계이후의 중합공정은 전단계까지의 중합공정에 의해서 얻은 중합체의 존재하에 행하고, 공정(a)에서 얻은 프로필렌(공)중합체(a)를 20∼90중량% 함유하고, 공정(b)에서 얻은 프로필렌/올레핀공중합체(b)를 5∼75중량% 함유하고, 공정(c)에서 얻은 에틸렌/올레핀공중합체(c)를 5∼75중량% 함유하고, 온도 230℃, 하중 2.16kg하에서 측정한 멜트플로우레이트가 0.01∼500g/10분인 프로필렌중합체조성물을 제조하는 것이 특징인 프로필렌중합체조성물의 제조방법. 공정(a):(i) 프로필렌을 단독중합시키거나 또는 (ii) 프로필렌과 에틸렌 및 탄소원자수 4∼20의 올레핀으로부터 선택한 적어도 하나의 올레핀을 공중합시켜 프로필렌으로부터 유도된 구성단위를 80몰%이상을 함유하는 프로필렌(공)중합체(a)를 제조하고, 상기 프로필렌(공)중합체(a)는 시차주사열량계로 측정하여, 융점이 100℃ 이상이고 2.16kg 하중하의 230℃에서 측정한 멜트플로우레이트가 0.01∼1000g/10분이다. 공정(b):프로필렌과 에틸렌 및 탄소원자수 4∼20의 올레핀으로부터 선택한 적어도 하나의 올레핀을 공중합시켜 프로필렌으로부터 유도된 구성단위를 50몰%이상 함유하는 프로필렌/올레핀공중합체(b)를 제조하고, 상기 프로필렌/올레핀공중합체(b)는 135℃의 데칼린중에서 측정한 극한 점도(η)]가 0.1∼20dl/g이다. 공정(c):에틸렌과 탄소원자수 3∼20의 올레핀으로부터 선택한 적어도 하나의 올레핀을 공중합시켜 에틸렌으로부티 유도되는 구성단위를 50몰%이상 함유하는 에틸렌/올레핀공중합체(c)를 제조하고, 여기서 상기 에틸렌/올레핀공중합체(c)는 135℃의 데칼린중에서 측정한 극한 점도(η)]가 0.1∼20dl/g이다.
- 제1항에 있어서, 상기 다단중합을 공정(a), 공정(b), 공정(c)의 순서로 행하는 것이 특징인 프로필렌중합체조성물의 제조방법.
- 제1항 또는 제2항에 있어서, 상기 공정(a)에 있어서, 프로필렌을 단독중합시키고, 상기 공정(b)에 있어서 프로필렌을 에틸렌과 공중합시키고, 공정(c)에 있어서, 에틸렌을 올레핀과 공중합시키는 것이 특징인 프로필렌중합체조성물의 제조방법.
- 제1항 또는 제2항에 있어서, 상기 공정(a)에 있어서, 프로필렌을 단독중합시키고, 상기 공정(b)에 있어서 프로필렌을 1-부텐과 공중합시키고, 상기 공정(c)에 있어서, 에틸렌을 올레핀과 공중합시키는 것이 특징인 프로필렌중합체조성물의 제조방법.
- 제1항 내지 제4항중 어느 한 항에 있어서, 시클로펜타디에닐 골격을 갖는 배위자를 포함하는 전이금속화합물(A)이 다음식(Ⅱ)로 표시되는 화합물인 것이 특징인 프로필렌중합체조성물의 제조방법.(여기서 M1은 주기율표 제Ⅳ∼ⅥB족의 전이금속원자를 나타내고, R1, R2, R3및 R4는 각각 수소, 할로겐, 탄소원자수 1∼20의 탄화수소기, 탄화원자수 1∼20의 할로겐화탄화수소기, 실리콘함유기, 산소함유기, 황함유기, 질소함유기 또는 인함유기를 나타내고, 인접하는 기 R1, R2, R3, R4의 일부가 결합하여, 이들 기가 결합된 탄소원자와 함께 환을 형성해도 좋다. 여기서 R1∼R4는 2개소에 표시되어 있으나, 예를들어 R1과 R1은 동일기 또는 다른 기이어도 좋고, 동일한 서픽스(Suffix)를 갖는 R은 결합하여 환을 형성하기 위한 바람직한 조합을 나타낸다. Y1은 탄소원자수 1∼20의 2가 탄화수소기, 탄소원자수 1∼20의 2가 할로겐화 탄화수소기, 2가 실리콘함유기 또는 2가 게르마늄함유기를 나타내고, X1과 X2는 각각 수소, 할로겐, 탄소원자수 1∼20의 탄화수소기, 탄소원자수 1∼20의 할로겐화탄화수소기, 산소함유기 또는 황함유기를 나타낸다.)
- 제1항 내지 제4항 중 어느 한 항에 있어서, 시클로펜타디에닐 골격을 갖는 배위자를 포함하는 전이금속화합물(A)이 다음식(Ⅲ)으로 표시되는 화합물인 것이 특징인 프로필렌중합체조성물의 제조방법.(여기서 M2은 주기율표 제Ⅳ∼ⅥB족의 전이금속원자이고, R5, R6과 R8∼R10은 동일 또는 다를 수 있고 각각 수소, 할로겐, 탄소원자수 1∼20의 탄화수소기, 탄소원자수 1∼20의 할로겐화 탄화수소기, 실리콘함유기, 산소함유기, 황함유기, 질소함유기 또는 인함유기이고, R7은 탄소원자수 6∼16의 아릴기이고, Y2은 탄소원자수1∼20의 2가 탄화수소기, 탄소원자수 1∼20의 2가 할로겐화 탄화수소기, 2가 실리콘함유기 또는 2가 게르마늄함유기이고, X3과 X4는 각각 수소, 할로겐, 탄소원자수 1∼20의 탄화수소기, 탄소원자수 1∼20의 할로겐화탄화수소기, 산소함유기 또는 황함유기이다.)
- 제1항 내지 제6항 중 어느 한 항에 있어서, 상기 전이금속화합물(A)을 활성화시키는 활성화화합물(B)이 (B-1)유기알루미늄화합물, (B-2)유기알루미늄옥시화합물, (B-3)상기 전이금속화합물(A)과 반응하여 이온쌍을 형성하는 화합물로 된 군으로부터 선택한 적어도 하나의 화합물인 것이 특징인 프로필렌중합체조성물의 제조방법.
- 청구범위 제1항 기제의 방법에 의해서 제조된 것이 특징인 프로필렌중합체조성물.
- (A) 시클로펜타디에닐 골격을 갖는 배위자를 포함하는 전이금속화합물과, (B) 전이 금속화합물(A)을 활성화시키는 화합물의 존재하에서 다음 공정(a), (b), (d) 및 (e)를 포함하는 다단중합을 임의의 순서에 따라 행하고, 2번째 단계 이후의 중합공정은 전단계까지의 중합공정에 의하여 얻은 중합체 존재하에 행하고, 공정(a)에서 얻은 프로필렌(공)중합체(a)를 20∼85중량% 비율로 함유하고, 공정(b)에서 얻은 프로필렌/올레핀공중합체(b)를 5∼75중량% 비율로 함유하고, 공정(d)에서 얻은 에틸렌/올레핀공중합체(d)를 5∼75중량% 비율로 함유하고, 공정(e)에서 얻은 에틸렌/올레핀공중합체(e)를 5∼30중량% 비율로 함유하고, 230℃ 하중 2.16kg에서 측정한 멜트플로우레이트가 0.01∼500g/10분인 프로필렌중합체조성물을 제조하는 것이 특징인 프로필렌중합체조성물의 제조방법. 공정(a):(i) 프로필렌을 단독 중합시키거나 또는 (ii) 프로필렌과 에틸렌 및 탄소원자수 4∼20의 올레핀으로부터 선택한 적어도 하나의 올레핀을 공중합시켜 프로필렌으로부터 유도된 구성단위를 80몰% 이상 함유하는 프로필렌(공)중합체(a)를 제조하고, 상기 프로필렌(공)중합체(a)는 시차주사열량계로 측정하여, 융점이 100℃ 이상이고 2.16kg 하중하의 230℃에서 측청한 멜트플로우레이트가 0.01∼1000g/10분이다. 공정(b):프로필렌과 에틸렌 및 탄소원자수 4∼20의 올레핀으로부터 선택한 적어도 하나의 올레핀을 공중합시켜 프로필렌으로부터 유도된 구성단위를 50몰%이상 함유하는 프로필렌/올레핀공중합체(b)를 제조하고, 상기 프로필렌/올레핀공중합(b)는 135℃의 데칼린중에서 측정한 극한 점도[η]가 0.1∼20dl/g이다. 공정(d):에틸렌과 탄소원자수 3∼20의 올레핀으로부터 선택한 적어도 하나의 올레핀을 공중합시키고, 에틸렌으로부터 유도되는 구성단위를 50몰%이상, 90몰%미만의 비율로 함유하는 에틸렌/올레핀공중합체(d)를 제조하고, 상기 에틸렌/올레핀공중합체(d)는 135℃ 데칼린 중에서 측정한 극한 점도[η]가 0.1∼20dl/g이다. 공정(e):에틸렌과 탄소원자수 3∼20의 올레핀으로부터 선택한 적어도 하나의 올레핀을 공중합시키고, 에틸렌으로부터 유도되는 구성단위를 90몰%이상 비율로 함유하는 에틸렌/올레핀공중합체(e)를 제조하고, 상기 에틸렌/올레핀공중합체(e)는 135℃ 데칼린 중에서 측정한 극한점도[η]가 0.1∼20dl/g이다.
- 제9항에 있어서, 상기 다단중합을 공정(a), 공정(b), 공정(d) 및 공정(e)의 순서로 행하는 것이 특징인 프로필렌중합체조성물의 제조방법.
- 제1O항에 있어서, 상기 공정(a)에서 프로필렌을 단독중합시키고, 상기 공정(b)에서, 프로필렌을 1-부텐과 공중합시키고, 상기 공정(d)에서 에틸렌을 프로필렌과 공중합시키고, 상기 공정(e)에서, 에틸렌을 1-부텐과 공중합시키는 것이 특징인 프로필렌중합체조성물의 제조방법.
- 제11항에 있어서, 상기 공정(a)에서 프로필렌을 단독중합시키고, 상기 공정(b)에서, 프로필렌을 에틸렌과 공중합시키고, 상기 공정(d)에서 에틸렌을 프로필렌과 공중합시키고, 상기 공정(e)에서, 에틸렌을 1-부텐과 공중합시키는 것이 특징인 프로필렌중합체조성물의 제조방법.
- 제9항 내지 제12항 중 어느 한 항에 있어서, 시클로펜타디에닐 골격을 갖는 배위자를 포함하는 전이금속화합물(A)이 상기 식(Ⅱ)으로 표시되는 화합물인 것이 특징인 프로필렌중합체조성물의 제조방법.
- 제9항 내지 12항 중 어느 한 항에 있어서, 시클로펜타디에닐 골격을 갖는 배위자를 포함하는 전이금속화합물(A)이 상기 식(Ⅲ)으로 표시되는 화합물인 것이 특징인 프로필렌중합체조성물의 제조방법.
- 제9항 내지 제14항 중 어느 한 항에 있어서, 전이금속화합물(A)을 활성화시키는 활성화화합물(B)이 (B-1) 유기알루미늄화합물, (B-2) 유기알루미늄옥시화합물 및 (B-3) 상기 전이금속화합물(A)과 반응하여 이 온쌍을 형성하는 화합물로 된 군으로부터 선택한 적어도 하나의 화합물인 것이 특징인 프로필렌중합체조성물의 제조방법.
- 청구범위 제9항 기재의 방법에 의해서, 제조된 것이 특징인 프로필렌중합체조성물.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.