KR102673620B1 - 가연가공기용 히터 도포제 - Google Patents
가연가공기용 히터 도포제 Download PDFInfo
- Publication number
- KR102673620B1 KR102673620B1 KR1020217039890A KR20217039890A KR102673620B1 KR 102673620 B1 KR102673620 B1 KR 102673620B1 KR 1020217039890 A KR1020217039890 A KR 1020217039890A KR 20217039890 A KR20217039890 A KR 20217039890A KR 102673620 B1 KR102673620 B1 KR 102673620B1
- Authority
- KR
- South Korea
- Prior art keywords
- heater
- false
- coating agent
- fatty acid
- mineral oil
- Prior art date
Abstract
본 발명은 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 것을 억제할 수 있는, 가연가공기용 히터 도포제의 제공을 과제로 한다.
상기 과제의 해결수단으로서, 본 발명은 지방산에스테르(A) 및 광물유(B)로부터 선택되는 하나 이상을 함유하는 것을 특징으로 하는 가연가공기용 히터 도포제를 제공한다.
상기 과제의 해결수단으로서, 본 발명은 지방산에스테르(A) 및 광물유(B)로부터 선택되는 하나 이상을 함유하는 것을 특징으로 하는 가연가공기용 히터 도포제를 제공한다.
Description
본 발명은 가연가공기에 있어서 실이 히터로부터 빠지는 것을 억제하는 것을 목적으로 하여, 히터에 도포하는 가연가공기용 히터 도포제에 관한 것이다.
최근 들어, 의류의 다양화, 패션화의 경향은 점점 진행되고, 그 중에서도, 적당한 신축성이나 볼륨감이 있고, 양호한 감촉에 의해 신체에 기분좋게 잘 맞는 스포츠용 의류나 부인용 파운데이션 의류 등 기능성 웨어에 대한 요망이 높아지고 있다. 이 기능성 웨어의 제조에는, 가연가공사는 불가결한 것이다.
일반적으로, 가연가공사(Draw Textured Yarn；이하, DTY라고 하는 경우가 있다.)는, 합성섬유용 처리제를 부여하여 부분연신사(Partially Oriented Yarn；이하, POY라고 하는 경우가 있다.)인 합성섬유 필라멘트사조를 생산한 후, 가연장치의 가열장치(히터)에 의해 합성섬유 필라멘트사조를 가열하고, 동시에 필라멘트사조에 꼬임을 주면서 연신함으로써 얻어진다. 부분연신사(POY)에 부여되는 합성섬유용 처리제는, 특히 유화제나 제전제 등에 고안이 이루어져, 히터 오염, 보풀 실잘림, 정전기 발생을 억제하는 설계가 이루어져 왔다(예를 들면, 특허문헌 1, 2 등).
그러나, 이러한 합성섬유용 처리제가 부여된 부분연신사(POY)의 경우에도, 가열장치(히터)로부터 합성섬유 필라멘트사조가 빠지거나 어긋나 버려, 보풀 실잘림이 발생하는 외에, 가열 부족 및 사도(絲道)의 어긋남에 의해 충분한 꼬임이나 연신이 불가능하다고 하는 문제가 있었다.
본 발명은 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 것을 억제할 수 있는, 가연가공기용 히터 도포제를 제공하는 것을 과제로 하고 있다.
본 발명자들은 상기 과제를 해결하기 위해 예의 연구를 거듭한 결과, 가연가공기의 히터 부분에 특정 성분을 도포함으로써, 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 것을 억제할 수 있는 것을 발견하고, 상기 과제를 해결하는 것에 도달한 것이다.
본 발명은 구체적으로는 다음의 사항을 요지로 한다.
1. 지방산에스테르(A) 및 광물유(B)로부터 선택되는 하나 이상을 함유하는 것을 특징으로 하는 가연가공기용 히터 도포제.
2. 상기 가연가공기용 히터 도포제의 전체 질량에 대해, 상기 지방산에스테르(A) 및 상기 광물유(B)로부터 선택되는 하나 이상을 적어도 50 질량% 이상 함유하는 1.에 기재된 가연가공기용 히터 도포제.
3. 상기 지방산에스테르(A)로서, 질량 평균 분자량이 300∼1000인 지방산에스테르(a1)을 함유하는 1. 또는 2.에 기재된 가연가공기용 히터 도포제.
4. 상기 광물유(B)로서, 60∼600 레드우드 초의 광물유(b1)을 함유하는 1. 또는 2.에 기재된 가연가공기용 히터 도포제.
5. 상기 지방산에스테르(A)로서, 질량 평균 분자량이 300∼1000인 지방산에스테르(a1)을 함유하고, 또한, 상기 광물유(B)로서, 60∼600 레드우드 초의 광물유(b1)을 함유하는 1. 또는 2.에 기재된 가연가공기용 히터 도포제.
6. 추가로, 계면활성제(C)를 함유하는 1. 내지 5. 중 어느 한 항에 기재된 가연가공기용 히터 도포제.
7. 1. 내지 6. 중 어느 한 항에 기재된 가연가공기용 히터 도포제를, 가연가공기의 히터에 도포하는 것을 특징으로 하는 가연가공사의 제조방법.
8. 상기 히터가 접촉형 히터인 7.에 기재된 가연가공사의 제조방법.
본 발명의 가연가공기용 히터 도포제나, 이 가연가공기용 히터 도포제를 가연가공기의 히터에 도포하는 가연가공사의 제조방법은, 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는, 즉 「실빠짐」을 억제하고, 「실빠짐」에 의한 보풀 실잘림이나 합성섬유 필라멘트사조의 가열 부족을 방지하여, 양호하게 꼬임 연신된 가연가공사가 얻어진다고 하는 효과를 발휘한다.
또한, 본 발명의 가연가공기용 히터 도포제는, 단시간에 가연가공기의 히터 상에 퍼지는 확전성도 우수하기 때문에, 급유작업이 단시간에 완료되는 외에, 급유 직후에도 가연가공기를 가동시키는 것이 가능하며, 또한, 본 발명의 가연가공기용 히터 도포제를 가연가공기의 히터 상에 균일하게 부착시켜서 「실빠짐」을 억제하는 효과를 높일 수 있기 때문에, 유용하다.
본 발명은 지방산에스테르(A) 및 광물유(B)로부터 선택되는 하나 이상을 함유하는 가연가공기용 히터 도포제나, 이 가연가공기용 히터 도포제를 가연가공기의 히터에 도포하는 가연가공사의 제조방법에 관한 것이다.
아래에 본 발명에 대해서 상세하게 설명한다.
＜지방산에스테르(A)＞
본 발명의 가연가공기용 히터 도포제는, 그 일태양으로서, 지방산에스테르(A)를 필수성분으로서 함유하는 것이다.
본 발명에 있어서의 지방산에스테르(A)는 지방족 탄화수소의 1가 또는 다가 알코올과, 지방족 탄화수소의 1가 또는 다가 카르복실산인 지방산의 카르복실기가, 에스테르 결합한 화합물이면 어느 것이어도 된다. 구체적으로는, (1) 부틸라우레이트, 부틸스테아레이트, 옥틸팔미테이트, 옥틸스테아레이트, 올레일라우레이트, 올레일올레에이트, 이소트리데실스테아레이트, 이소펜타코사닐이소스테아레이트 등의 지방족 1가 알코올과 지방족 모노카르복실산의 에스테르, (2) 1,6－헥산디올디데카노에이트, 트리메틸올프로판모노올레에이트모노라우레이트, 트리메틸올프로판트리라우레이트, 트리메틸올프로판트리올레에이트, 펜타에리스리톨테트라올레에이트, 피마자유 등의 천연유지 등의, 지방족 다가 알코올과 지방족 모노카르복실산의 에스테르, (3) 아디프산 디라우릴, 아젤라산 디올레일 등의, 지방족 1가 알코올과 지방족 다가 카르복실산의 에스테르 등을 들 수 있다. 이들을 1종 또는 2종 이상 병용해도 된다.
그 중에서도, 본 발명에 있어서의 지방산에스테르(A)로서, 질량 평균 분자량이 300∼1000인 지방산에스테르(a1)을 함유함으로써, 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 「실빠짐」을 보다 억제할 수 있다.
＜광물유(B)＞
본 발명의 가연가공기용 히터 도포제는 그 일태양으로서, 지하자원 유래의 탄화수소 화합물인 광물유(B)를 필수성분으로서 함유하는 것이다. 구체적으로는, 방향족계 탄화수소, 파라핀계 탄화수소, 나프텐계 탄화수소 등을 들 수 있다. 보다 구체적으로는, 예를 들면 스핀들유, 유동 파라핀 등을 들 수 있다. 이들 광물유는 시판품을 적당히 채용할 수 있다. 이들을 1종 또는 2종 이상 병용해도 된다.
그 중에서도, 본 발명에 있어서의 광물유(B)로서, 60∼600 레드우드 초의 광물유(b1)을 함유함으로써, 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 「실빠짐」을 보다 억제할 수 있다. 여기서, 레드우드 초는 광물유의 점도를 나타내고, 용기의 바닥부에 있는 세공을 막고 용기 내의 일정 높이까지 시료를 넣어, 시험온도인 30℃에 도달한 지점에서 구멍을 뚫고 시료를 낙하시켜, 50 ㎤의 시료가 떨어지는 데 소요되는 시간(초)을 의미한다.
본 발명의 가연가공기용 히터 도포제는, 지방산에스테르(A) 및 광물유(B)로부터 선택되는 하나 이상을 함유하면 되고, 지방산에스테르(A)를 함유하는 태양, 광물유(B)를 함유하는 태양, 지방산에스테르(A) 및 광물유(B)를 함유하는 태양 중 어느 태양이어도 된다.
본 발명의 가연가공기용 히터 도포제는, 당해 히터 도포제의 전체 질량에 대해, 지방산에스테르(A) 및 광물유(B)로부터 선택되는 하나 이상을 적어도 50 질량% 이상 함유하는 것이, 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 「실빠짐」을 억제하는 점에 있어서 바람직하고, 60 질량% 이상 함유하는 것이 보다 바람직하며, 70 질량% 이상 함유하는 것이 더욱 바람직하다.
＜계면활성제(C)＞
본 발명의 가연가공기용 히터 도포제는, 추가로 계면활성제(C)를 함유해도 된다. 함유 가능한 계면활성제(C)로서는, 비이온성 계면활성제(c1), 음이온성 계면활성제(c2), 양이온성 계면활성제(c3), 양성 계면활성제(c4) 중 어느 것이어도 되지만, 비이온성 계면활성제(c1)과 음이온성 계면활성제(c2)로부터 선택되는 1종 이상을 함유하는 것이 바람직하고, 그 중에서도, 비이온성 계면활성제(c1)과 음이온성 계면활성제(c2) 양쪽을 함유하는 것이 더욱 바람직하다.
본 발명의 가연가공기용 히터 도포제에 있어서의 계면활성제(C)의 함유량은 특별히 제한은 없으나, 당해 히터 도포제의 전체 질량에 대해 50 질량% 미만의 범위에서 함유해도 되고, 40 질량% 미만의 범위에서 함유하는 것이 바람직하며, 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 「실빠짐」을 억제하는 점에 있어서, 30 질량% 미만의 범위에서 함유하는 것이 더욱 바람직하다.
＜비이온성 계면활성제(c1)＞
본 발명의 가연가공기용 히터 도포제에 배합 가능한, 비이온성 계면활성제(c1)의 구체적인 예로서는, 특별히 제한은 없고, 예를 들면, (폴리)옥시알킬렌알킬에테르, (폴리)옥시알킬렌알킬페닐에테르, (폴리)옥시알킬렌알릴페닐에테르, (폴리)옥시알킬렌스티릴페닐에테르, (폴리)옥시알킬렌알킬페닐에테르포름알데히드 축합물, (폴리)옥시에틸렌－(폴리)옥시프로필렌 블록 폴리머, (폴리)옥시에틸렌－(폴리)옥시프로필렌 랜덤 폴리머, (폴리)옥시에틸렌－(폴리)옥시프로필렌 블록 폴리머 알킬페닐에테르, (폴리)옥시알킬렌 지방산에스테르, (폴리)옥시알킬렌 소르비탄 지방산에스테르, (폴리)옥시알킬렌 경화 피마자유, (폴리)알킬렌글리콜 지방산에스테르, (폴리)알킬렌글리콜 지방산에테르 등을 들 수 있다. 이들은 1종류를 단독으로 사용해도 되고, 2종류 이상을 조합해서 사용해도 된다.
＜음이온성 계면활성제(c2)＞
본 발명의 가연가공기용 히터 도포제에 배합 가능한, 음이온성 계면활성제(c2)의 구체적인 예로서는, 특별히 제한은 없고, 예를 들면, (1) 알킬인산에스테르나트륨염, 알킬인산에스테르칼륨염, 알킬인산에스테르디에탄올아민염, 알킬인산에스테르트리에탄올아민염 등의 알킬기의 탄소수가 4∼18인 알킬인산에스테르염, (2) 알킬설폰산나트륨염, 알킬설폰산칼륨염, 디알킬설폭숙신산나트륨염, 디알킬설포숙신산칼륨염 등의 탄소수 5∼30의 설폰산염, (3) 알킬황산나트륨염, 알킬황산칼륨염 등의 탄소수 5∼30의 황산염, (4) 카르복실산나트륨염, 카르복실산칼륨염 등의 카르복실산염 등을 들 수 있다. 이들은 1종류를 단독으로 사용해도 되고, 2종류 이상을 조합해서 사용해도 된다.
＜양이온성 계면활성제(c3)＞
본 발명의 가연가공기용 히터 도포제에 배합 가능한, 양이온성 계면활성제(c3)의 구체적인 예로서는, 특별히 제한은 없고, 예를 들면 아민염, 암모늄염, 포스포늄염, 이미다졸린염, 이미다졸리늄염 등을 들 수 있다. 이들은 1종류를 단독으로 사용해도 되고, 2종류 이상을 조합해서 사용해도 된다.
＜양성 계면활성제(c4)＞
본 발명의 가연가공기용 히터 도포제에 배합 가능한, 양성 계면활성제(c4)의 구체적인 예로서는, 특별히 제한은 없고, 예를 들면 베타인 등의 양성 계면활성제 등을 들 수 있다. 이들 성분은 1종을 단독으로 사용해도 되고, 2종 이상을 조합해서 사용해도 된다.
＜기타 성분＞
본 발명의 가연가공기용 히터 도포제는, 기타 성분으로서, 실리콘 오일, 산화방지제, 방청제, 방부제 외에, 「실빠짐」 억제효과를 기대하여 불소 화합물 등을 배합할 수 있다. 기타 성분의 배합량은 본 발명의 효과를 손상시키지 않는 범위 내에 있어서 규정할 수 있지만, 가연가공기용 히터 도포제의 전체 질량에 대해 20 질량% 미만의 배합량으로 하는 것이 바람직하다.
실리콘 오일로서는, 예를 들면, 디메틸실리콘, 페닐 변성 실리콘, 아미노 변성 실리콘, 아미드 변성 실리콘, 폴리에테르 변성 실리콘, 아미노폴리에테르 변성 실리콘, 알킬 변성 실리콘, 알킬아랄킬 변성 실리콘, 알킬폴리에테르 변성 실리콘, 에스테르 변성 실리콘, 에폭시 변성 실리콘, 카르비놀 변성 실리콘, 메르캅토 변성 실리콘, 폴리옥시알킬렌 변성 실리콘 등을 들 수 있다. 이들 실리콘 오일은 시판품을 적당히 채용할 수 있다.
산화방지제로서는, (1) 1,3,5－트리스(3',5'－디－t－부틸－4－히드록시벤질)이소시아누르산, 1,3,5－트리스(4－tert－부틸－3－히드록시－2,6－디메틸벤질)이소시아누르산, 1,3,5－트리메틸－2,4,6－트리스(3,5－디－t－부틸－4－히드록시벤질)벤젠, 2,2'－메틸렌－비스(4－메틸－6－t－부틸페놀), 1,1,3－트리스(2－메틸－4－하이드록시－5－t－부틸페닐)부탄, 테트라키스［메틸렌－3－(3',5'－디－t－부틸－4'－히드록시페닐)프로피오네이트］메탄 등의 페놀계 산화방지제, (2) 옥틸디페닐포스파이트, 트리스노닐페닐포스파이트, 테트라트리데실－4,4'－부틸리덴－비스－(2－t－부틸－5－메틸페놀)디포스파이트 등의 포스파이트계 산화방지제, (3) 4,4'－티오비스－(6－t－부틸－3－메틸페놀), 디라우릴－3,3'－티오디프로피오네이트 등의 티오에테르계 산화방지제 등을 들 수 있다.
＜가연가공기용 히터 도포제의 조제방법＞
본 발명의 가연가공기용 히터 도포제의 조제방법으로서는, 특별히 한정은 없고, 구성하는 상기 각 성분을 임의의 순서로 첨가 혼합함으로써 조제할 수 있다.
본 발명의 가연가공기용 히터 도포제를 사용하는 가연가공기로서는, (1) 히터온도 150∼230℃, 히터길이 150∼250 ㎝의 히터를 장착하여, 합성섬유 필라멘트사조가 히터 플레이트 상을 접촉하면서 주행하는 접촉형 히터의 가연가공기, (2) 히터온도 300∼600℃, 히터길이 20∼150 ㎝의 히터를 장착하여, 합성섬유 필라멘트사조가 히터 플레이트 상을 비접촉으로 주행하는 비접촉형 히터의 가연가공기 등을 들 수 있다.
그 중에서도, 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 「실빠짐」을 억제하는 효과를 발휘하는 점에 있어서, 본 발명의 가연가공기용 히터 도포제는 접촉형 히터의 가연가공기에 적용하는 것이 바람직하다.
본 발명의 가연가공기용 히터 도포제를 히터에 도포하는 방법으로서는, 브러시 도포, 플로우 도포, 스프레이 도포, 롤러 도포 또는 침지 도포 등의 방법을 채용할 수 있는데, 가연가공기용 히터 상에 형성되는 도포제층의 평활성, 균일성, 히터면과의 밀착성, 간편성 등의 점에서, 브러시, 롤러, 천 등의 도포구에, 본 발명의 가연가공기용 히터 도포제를 함침시켜서 도포하는 방법이 바람직하다.
실시예
아래에 실시예를 들어 본 발명을 설명하지만, 본 발명의 기술범위는 이들에 의해 한정되는 것은 아니다. 또한, 아래의 실시예 및 비교예에 있어서, 부는 질량부를, 또한 %는 질량%를 의미한다.
＜가연가공기용 히터 도포제의 조제＞
·실시예 1
실시예 1은 옥틸팔미테이트(질량 평균 분자량 369)(A－1)만을 함유하는 가연가공기용 히터 도포제이다.
·실시예 19
옥틸팔미테이트(질량 평균 분자량 369)(A－1)를 30부, 광물유(레드우드 초：800)(B－4)를 60부, 폴리옥시에틸렌(5 몰)도데실에테르(c1－1)을 9부, 이소옥틸인산에스테르칼륨염(c2－1)을 1부 및 디메틸폴리실록산(F－1)을 1부, 이들 전부를 균일하게 혼합하여 실시예 19의 가연가공기용 히터 도포제를 조제하였다.
·실시예 2∼18 및 비교예 1
실시예 2∼18의 가연가공기용 히터 도포제는 아래 표 1에 나타낸 배합으로, 상기 실시예 1 또는 실시예 19의 조제방법과 동일하게 하여 조제하였다. 비교예 1은 가연가공기용 히터 도포제를 히터에 도포하지 않는 예이다.
실시예 1∼19의 가연가공기용 히터 도포제의 각 배합을 아래 표 1에 정리하여 나타낸다.
또한, 표 1 중 기타 성분의 「배합량＊」은, 지방산에스테르(A), 광물유(B), 계면활성제(C)의 합계 100 질량부에 대한 질량부를 의미한다.
표 1 중 각 기호는 아래 성분을 나타낸다.
＜지방산에스테르(A)＞
A－1：옥틸팔미테이트(질량 평균 분자량 369)
A－2：디라우릴아디페이트(질량 평균 분자량 483)
A－3：트리메틸올프로판트리올레에이트(질량 평균 분자량 928)
A－4：부틸라우레이트(질량 평균 분자량 256)
A－5：펜타에리스리톨테트라올레에이트(질량 평균 분자량 1194)
상기 A－1∼A－3는 본 발명에 있어서의 질량 평균 분자량이 300∼1000인 지방산에스테르(a1)에 상당하는 성분이다.
＜광물유(B)＞
B－1：광물유(레드우드 초：80)
B－2：광물유(레드우드 초：500)
B－3：광물유(레드우드 초：40)
B－4：광물유(레드우드 초：800)
상기 B－1, B－2는 본 발명에 있어서의 60∼600 레드우드 초의 광물유(b1)에 상당하는 성분이다.
＜계면활성제(C)＞
·비이온성 계면활성제
c1－1：폴리옥시에틸렌(5 몰)도데실에테르
·음이온성 계면활성제
c2－1：이소옥틸인산에스테르칼륨염
c2－2：2－헥사데실인산에스테르트리에탄올아민염
c2－3：올레산칼륨염
c2－4：디옥틸설포숙신산나트륨염
＜기타 성분＞
F－1：디메틸폴리실록산
G－1：1,1,3－트리스(2－메틸－4－히드록시－5－t－부틸페닐)부탄(산화방지제)
＜가연가공 시험＞
접촉형 히터 가연가공기(TMT 머시너리사 제조의 상품명 ATF－21)를 사용하여, 아래의 합성섬유용 처리제 A(유제 부여량(OPU)：0.4%)를 부여한 산화티탄 함유량 0.2%의 폴리에틸렌테레프탈레이트의 128 데시텍스 36 필라멘트의 부분연신사(POY)에 대해, 가공속도＝650 m／분, 연신배율＝1.70, 시연(施撚)방식＝3축 디스크 외접식 마찰방식(입측(入側) 가이드 디스크 1장, 출측(出側) 가이드 디스크 1장, 경질 폴리우레탄 디스크 4장), 디스크속도／실속도(D／Y)＝1.7, 가연(加撚) 측 히터＝길이 2 m로 표면온도 180℃, 해연(解撚) 측 히터＝없음의 조건에서 가연가공을 행하였다.
또한, 가연가공 전에 상기 접촉형 히터 가연가공기의 히터에, 실시예 1∼19의 각 가연가공기용 히터 도포제를 함침시킨 천을 사용하여, 히터 전면을 도포 가능한 최저한량을 사용해서 도포하였다.
＜합성섬유용 처리제 A＞
부틸알코올에 에틸렌옥사이드(EO)와 프로필렌옥사이드(PO)를 EO／PO＝50／50(질량비)의 비율로 랜덤상으로 부가한 질량 평균 분자량 2000의 폴리에테르모노올을 45부, 라우릴알코올에 에틸렌옥사이드(EO)와 프로필렌옥사이드(PO)를 EO／PO＝70／30(질량비)의 비율로 랜덤상으로 부가한 질량 평균 분자량 1500의 폴리에테르모노올을 42부, 라우릴알코올에 에틸렌옥사이드(EO)를 10 몰 부가한 폴리에테르모노올을 12부, 데칸설폰산나트륨염을 0.5부, 라우릴인산에스테르칼륨염을 0.5부, 이들을 균일하게 혼합하여 합성섬유용 처리제 A를 조제하였다.
＜실빠짐 방지성의 평가＞
상기 조건에서 12추(가연가공기 1 장치에서의 동시 가연가공 수：12)로 10분간의 가연가공을 행하여, 발생한 실빠짐의 추 수를 계측하였다.
［평가기준］
◎：발생 추 수가 0∼1회
○：발생 추 수가 2∼4회
×：발생 추 수가 5회 이상
＜확전성 평가＞
실시예 1∼19의 각 샘플 0.15 g을 45°의 각도로 경사진 표면온도 180℃의 가연가공기의 히터에 늘어뜨리고, 10초간 샘플이 나아간 거리를 측정하였다.
［평가기준］
◎：30 ㎝ 이상
○：30 ㎝ 미만
실시예 1∼19의 가연가공기용 히터 도포제와, 비교예 1에 관한 「실빠짐 방지성의 평가」와 「확전성 평가」 결과를 표 2에 정리하여 나타내었다.
표 2에 나타내는 바와 같이, 본 발명의 가연가공기용 히터 도포제의 구체적인 예인 실시예 1∼19는, 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 「실빠짐」을 양호하게 억제하는 것이, 또한, 「실빠짐」에 의한 보풀 실잘림이나 합성섬유 필라멘트사조의 가열 부족을 방지하여, 양호하게 꼬임 연신된 가연가공사가 얻어지는 것도 확인되었다.
또한, 실시예 1∼19의 가연가공기용 히터 도포제는, 단시간에 가연가공기의 히터 상에 퍼지는 확전성도 우수한 것도 명확해졌다.
이에 대해, 본 발명의 가연가공기용 히터 도포제를 가연가공기의 히터에 도포하지 않고, 합성섬유용 처리제를 부착한 부분연신사(POY)를 사용한 경우에는, 「실빠짐」을 억제하는 것이 불가능하고, 「실빠짐」에 의한 보풀 실잘림이 발생하는 것도 명확해졌다.
산업상 이용가능성
본 발명의 가연가공기용 히터 도포제나, 이 가연가공기용 히터 도포제를 가연가공기의 히터에 도포하는 가연가공사의 제조방법은, 가연가공기에 있어서 합성섬유 필라멘트사조가 히터로부터 빠지는 「실빠짐」을 억제하고, 「실빠짐」에 의한 보풀 실잘림이나 합성섬유 필라멘트사조의 가열 부족을 방지하여, 양호하게 꼬임 연신된 가연가공사가 얻어지기 때문에 매우 유용하다.
Claims (8)
- 지방산에스테르(A)(단, 불소 화합물을 제외한다.) 및 광물유(B)(단, 미네랄 스피릿을 제외한다.)로부터 선택되는 하나 이상을 함유하는 것을 특징으로 하는 가연가공기용 히터 도포제.
- 제1항에 있어서,
상기 가연가공기용 히터 도포제의 전체 질량에 대해, 상기 지방산에스테르(A) 및 상기 광물유(B)로부터 선택되는 하나 이상을 적어도 50 질량% 이상 함유하는 가연가공기용 히터 도포제. - 제1항 또는 제2항에 있어서,
상기 지방산에스테르(A)로서, 질량 평균 분자량이 300∼1000인 지방산에스테르(a1)을 함유하는 가연가공기용 히터 도포제. - 제1항 또는 제2항에 있어서,
상기 광물유(B)로서, 60∼600 레드우드 초의 광물유(b1)을 함유하는 가연가공기용 히터 도포제. - 제1항 또는 제2항에 있어서,
상기 지방산에스테르(A)로서, 질량 평균 분자량이 300∼1000인 지방산에스테르(a1)을 함유하고, 또한, 상기 광물유(B)로서, 60∼600 레드우드 초의 광물유(b1)을 함유하는 가연가공기용 히터 도포제. - 제1항 또는 제2항에 있어서,
추가로, 계면활성제(C)를 함유하는 가연가공기용 히터 도포제. - 제1항 또는 제2항에 기재된 가연가공기용 히터 도포제를, 가연가공기의 히터에 도포하는 것을 특징으로 하는 가연가공사의 제조방법.
- 제7항에 있어서,
상기 히터가 접촉형 히터인 가연가공사의 제조방법.