KR102082627B1 - 전이 금속 박막의 원자층 증착 - Google Patents
전이 금속 박막의 원자층 증착 Download PDFInfo
- Publication number
- KR102082627B1 KR102082627B1 KR1020147002941A KR20147002941A KR102082627B1 KR 102082627 B1 KR102082627 B1 KR 102082627B1 KR 1020147002941 A KR1020147002941 A KR 1020147002941A KR 20147002941 A KR20147002941 A KR 20147002941A KR 102082627 B1 KR102082627 B1 KR 102082627B1
- Authority
- KR
- South Korea
- Prior art keywords
- alkyl
- modified surface
- acid
- substrate
- pulse time
- Prior art date
Abstract
기판 상에 금속막을 형성하기 위한 원자층 증착 방법은, a) 제1의 사전 결정된 펄스 시간 동안 기판을 화학식 1에 의해 기술되는 금속 함유 화합물의 증기와 접촉시켜 제1의 개질된 표면을 형성하는 단계(화학식 1: MLn; n은 1 내지 8이고; M은 전이금속이며; L은 리간드임); b) 제2의 사전 결정된 펄스 시간 동안 제1의 개질된 표면을 산과 접촉시켜 제2의 개질된 표면을 형성하는 단계; 및 c) 제3의 사전 결정된 펄스 시간 동안 제2의 개질된 표면을 환원제와 접촉시켜 금속층을 형성하는 단계를 포함하는 증착 주기를 포함한다.
Description
관련 출원과의 상호 참조
본 출원은 2011년 7월 6일 출원된 미국 가출원 제61/504,859호의 이익을 주장한다.
본 발명의 기술분야
적어도 일 양태에서, 본 발명은 저온에서 원자층 증착에 의해 금속 층을 형성하는 방법에 관한 것이다.
현재 전이금속 박막, 특히 구리, 니켈, 코발트 및 망간에 대한 원자층 증착 박막 성장 공정은 거의 없다. 구리는 마이크로전자 소자에서 배선 재료로서 사용된다. 장래의 마이크로전자 소자의 코팅 필요를 충족시키기 위해, 원자층 증착은 막 성장 기술로서 사용되어야 한다. 추가로, 성장 온도는 가능한한 낮아야 한다(예를 들어, 100℃).
따라서, 원자층 증착에 의해 금속 박막을 증착시키기 위한 개선된 공정에 대한 필요성이 있다.
본 발명은 전이 금속 박막의 원자층 증착을 제공하는 것을 목적으로 한다.
본 발명은 적어도 일 실시형태에서 기판 상에 금속막을 형성하기 위한 원자층 증착(atomic layer deposition: ALD) 방법을 제공함으로써 선행기술의 하나 이상의 문제를 해결한다. 해당 방법은
a) 제1의 사전 결정된 펄스 시간 동안 기판을 화학식 1에 의해 기술되는 금속 함유 화합물의 증기와 접촉시켜 제1의 개질된 표면을 형성하는 단계:
[화학식 1]
MLn
(n은 1 내지 8이고;
M은 전이금속이며;
L은 리간드임);
b) 제2의 사전 결정된 펄스 시간 동안 제1의 개질된 표면을 산과 접촉시켜 제2의 개질된 표면을 형성하는 단계; 및
c) 제3의 사전 결정된 펄스 시간 동안 제2의 개질된 표면을 환원제와 접촉시켜 금속층을 형성하는 단계를 포함하는 증착 주기를 포함한다. M은 화학식 1을 갖는 화합물이 300℃까지의 온도에서 적어도 0.01토르(torr)의 수증기압을 가지게 한다. L에 대한 컨쥬게이트 산의 pKa는 단계 b)에서 사용되는 산의 pKa보다 크다.
다른 실시형태에서, 기판 상에 금속막을 형성하는 방법이 제공된다. 해당 방법은
a) 제1의 사전 결정된 펄스 시간 동안 기판을 화학식 1에 의해 기술되는 금속 함유 화합물의 증기와 접촉시켜 제1의 개질된 표면을 형성하는 단계:
[화학식 1]
MLn
(상기 식에서
n은 1 내지 8이고;
M은 전이금속이며;
L은 리간드임);
b) 제2의 사전 결정된 펄스 시간 동안 제1의 개질된 표면을 산과 접촉시켜 제2의 개질된 표면을 형성하는 단계(L에 대한 컨쥬게이트 산의 pKa는 이 단계에서 사용되는 산의 pKa보다 큼); 및
c) 제3의 사전 결정된 펄스 시간 동안 제2의 개질된 표면을 환원제와 접촉시켜 금속층을 형성하는 단계(증착 주기는 다수회 반복되어 두께가 약 5나노미터 내지 약 300나노미터인 금속막을 형성함)
를 포함하는 증착 주기를 포함한다.
도 1은 원자층 증착 시스템을 개략적으로 예시한 것이다.
도 2는 금속을 함유하는 ALD 전구체에 대해 적합한 리간드의 예를 제공한다.
도 3은 금속을 함유하는 ALD 전구체에 대해 적합한 리간드의 예를 제공한다.
도 4는 ALD 공정의 실시형태에서 유용한 산의 예를 제공한다.
도 5는 Cu(dmap)2 펄스 길이의 함수로서 성장 속도의 플롯을 제공한다.
도 6은 증착 온도의 함수로서 성장 속도의 플롯을 제공한다.
도 7은 증착 주기의 수에 대한 막 두께의 의존도를 나타내는 플롯을 제공한다.
도 2는 금속을 함유하는 ALD 전구체에 대해 적합한 리간드의 예를 제공한다.
도 3은 금속을 함유하는 ALD 전구체에 대해 적합한 리간드의 예를 제공한다.
도 4는 ALD 공정의 실시형태에서 유용한 산의 예를 제공한다.
도 5는 Cu(dmap)2 펄스 길이의 함수로서 성장 속도의 플롯을 제공한다.
도 6은 증착 온도의 함수로서 성장 속도의 플롯을 제공한다.
도 7은 증착 주기의 수에 대한 막 두께의 의존도를 나타내는 플롯을 제공한다.
발명자들에 대해 현재 공지된 본 발명을 실행하는 최상의 방식을 구성하는 본 발명의 현재 바람직한 조성물, 실시형태 및 방법에 대해 상세하게 언급될 것이다. 도면은 반드시 일정한 비율인 것은 아니다. 그러나, 개시된 실시형태는 단지 다양한 그리고 대안의 형태로 구현될 수 있는 본 발명의 예시인 것이 이해되어야 한다. 그러므로, 본 명세서에 개시된 구체적인 상세 내용은 제한으로서 해석되어서는 안되며, 단지 본 발명의 어떤 양태에 대한 대표적인 기초로서 및/또는 본 발명을 다양하게 이용하기 위해 당업자를 교시하기 위한 대표적인 기초로서 해석되어야 한다.
실시예 또는 달리 명백하게 표시된 경우를 제외하고, 반응 및/또는 사용의 재료 또는 조건의 양을 나타내는 본 설명의 모든 수치적 양은 본 발명의 가장 넓은 범주를 설명하는 단어 “약”에 의해 변형되는 바와 같이 이해되어야 한다. 언급되는 수치적 한계 내의 실행이 일반적으로 바람직하다. 또한, 반대로 명확하게 언급되지 않는다면, 백분율, “부(part of)” 및 비(ratio) 값은 중량에 의한 것이며, 본 발명과 관련되어 주어진 목적을 위해 적합하거나 또는 바람직하다면, 물질의 그룹 또는 분류의 설명은 그룹 또는 분류의 구성원 중 임의의 2 이상의 혼합물이 동일하게 적합하거나 또는 바람직하다는 것을 나타내고, 화학적 용어에서 구성요소의 설명은 본 설명에서 구체화된 임의의 조합에 대한 추가 시간에서의 구성요소를 지칭하며, 일단 혼합되면 혼합물의 구성요소 간의 화학적 상호작용을 반드시 불가능하게 하는 것은 아니고, 두문자어 또는 기타 다른 약어의 처음의 정의는 동일한 약어의 본 명세서에서 모든 후속적 사용에 적용되며, 처음에 정의된 약어의 보통의 문법적 변형에 대해 필요한 부분만 수정하여 적용되고, 달리 반대로 명백하게 언급되지 않는다면, 특성의 측정은 동일한 특성에 대하여 이전에 언급되거나 또는 이후에 언급되는 바와 같은 동일한 기술에 의해 결정된다.
또한 구체적 성분 및/또는 병태가 물론 다를 수 있기 때문에, 본 발명은 이하에 기술는 구체적 실시형태 및 방법으로 제한되지 않는다는 것이 이해되어야 한다. 더 나아가, 본 명세서에 사용되는 전문용어는 단지 본 발명의 특정 실시형태를 설명하는 목적을 위해 사용되며, 어떤 방법으로 제한하는 것으로 의도되지 않는다.
또한 본 명세서 및 첨부되는 특허청구범위에서 사용되는 바와 같은 단수 형태(“a”, “an” 및 “the”)는 달리 명확하게 표시되지 않는다면, 복수의 대상을 포함한다는 것이 주목되어야 한다. 예를 들어, 단수 부품에 대한 언급은 복수의 부품을 포함하는 것으로 의도된다.
본 실시형태의 실시형태에서, 기판의 표면 상에 박막을 증착하기 위한 방법이 제공된다. 도 1에 대해서, 증착 시스템(10)은 반응 챔버(12), 기판 홀더(14) 및 진공 펌프(16)를 포함한다. 통상적으로, 기판은 히터(18)를 통해 가열된다. 해당 방법은 기판(20) 상의 금속막의 두께를 구성하기 위해 다회 반복되는 증착 주기를 가진다. 각각의 증착 주기 동안, 기판 온도는 통상적으로 100℃ 내지 200℃에서 유지된다. 각 증착 주기는 기판(20)을 화학식 1에 의해 기술되는 금속 함유 화합물의 증기와 접촉시키는 단계를 포함하며,
[화학식 1]
MLn
(상기 식에서
n은 1 내지 8이고;
M은 전이금속이며;
L은 리간드임);
다양한 상이한 리간드가 L에 대해 사용될 수 있다. 예를 들어, L은 2개의 전자 리간드, 여러자리 리간드(예를 들어, 이좌배위자 리간드), 하전된 리간드(예를 들어, -1 하전), 중성 리간드 및 이들의 조합일 수 있다. n이 리간드의 수로 제공되지만, 리간드는 2 초과의 n값에 대해 동일할 필요는 없다. 적합한 리간드의 구체적 예는 도 2 및 도 3에 제시된다. 도 2 및 도 3에서, R, R1, R2는 각각 독립적으로 수소, C1-8 알킬, C6-12 아릴, Si(R3)3 또는 비닐이고, R4는 C1-8 알킬이다. 개량에서, R, R1, R2는 각각 독립적으로 수소, C1-4 알킬, C6-10 아릴, Si(R3)3 또는 비닐이고, R3은 C1-8 알킬이다. 유용한 알킬기의 예는 메틸, 에틸, n-프로필, 이소프로필, n-부틸, t-부틸, 이소-부틸, sec-부틸 등을 포함하지만, 이들로 제한되지 않는다. 유용한 아릴기의 예는 페닐, 톨릴, 나프틸 등을 포함하지만, 이들로 제한되지 않는다. 또한 R, R1, R2는 선택적으로 할로겐화물과 같은 기로 치환될 수 있다는 것이 인식되어야 한다. 특히 유용한 리간드는 디메틸아미노-2-프로폭시드이다. 개량에서, L에 대한 컨쥬게이트 산의 pKa는 단계 b)에서 사용되는 산의 pKa보다 크다. 다른 개량에서, M은 화학식 1을 갖는 화합물이 300℃까지의 온도에서 적어도 0.01토르의 수증기압을 가지게 한다.
바람직한 실시형태의 개량에서, M은 0 내지 +6 산화 상태의 전이금속이다. 추가적인 개량에서, M은 +1 내지 +6 산화 상태의 전이금속이다. 또한 추가 개량에서, M은 +2 산화 상태의 전이금속이다. M에 대해 유용한 금속의 예는, 은, 팔라듐, 백금, 로듐, 이리듐, 코발트, 루테늄, 망간, 니켈 및 구리를 포함하지만, 이들로 제한되지 않는다.
또한 도 1에 대해서, 제1의 사전 결정된 펄스 시간 동안 증기가 전구체 공급원(22)으로부터 반응 챔버(12) 내로 도입된다. 변형에서, 전구체 공급원(22)으로부터의 화합물은 직접 액체 주입에 의해 챔버(12) 내로 도입된다. 제1의 사전 결정된 펄스 시간은 기판 표면(금속층으로 코팅 또는 비코팅) 상에서 이용가능한 결합 부위가 포화되도록(즉, 부착된 금속 함유 화합물) 충분히 길어야 한다. 통상적으로, 제1의 사전 결정된 펄스 시간은 1초 내지 20초이다. 제1의 사전 결정된 펄스 시간은 제어 밸브(24)를 통해 제어된다. 금속 함유 화합물 증기의 적어도 일부는 기판 표면(26)을 변형시켜(예를 들어, 흡착되거나 반응됨) 제1의 개질된 표면을 형성한다. 그 다음에 반응 챔버(12)는 제1의 퍼지 시간 동안 비활성 기체를 이용하여 퍼지된다. 제1의 퍼지 시간은 반응 챔버(12)로부터 금속 함유 화합물을 제거하기에 충분하며, 통상적으로 0.5초 내지 2분이다.
증착 주기의 다음 반응 단계에서, 그 다음에 제2의 사전 결정된 펄스 시간 동안 포름산과 같은 산이 산 공급원(30)으로부터 반응 챔버(12) 내로 도입된다. 기타 다른 적합한 산의 예는 도 4에 제공되어 있다. 도 4에서, R4는 H(즉, 수소화물), C1-8 알킬, C6-12 아릴 또는 C1-8 플루오로알킬이고, X는 N3 -, N03 -, 할로겐화물(예를 들어, Cl, F, Br)이며, n은 1 내지 6의 정수이다. 개량에서, R4는 수소화물, C1-4 알킬, C6-10 아릴 또는 C1-4 플루오로알킬이며, X는 N3 -, N03 -, 할로겐화물(예를 들어, Cl, F, Br)이고, n은 1 내지 6의 정수이다. 유용한 알킬 기의 예는, 메틸, 에틸, n-프로필, 이소프로필, n-부틸, t-부틸, 이소-부틸, sec-부틸 등을 포함하지만, 이들로 제한되지 않는다. 유용한 아릴 기의 예는, 페닐, 톨릴, 나프틸 등을 포함하지만, 이들로 제한되지 않는다. 또한 R, R1, R2는 할로겐화물과 같은 기로 선택적으로 치환될 수 있다는 것이 인식되어야 한다. 제2의 사전 결정된 펄스 시간은 제1의 개질된 기판 표면 상의 이용가능한 결합 부위가 포화되고, 제2의 개질된 표면이 형성되도록 충분히 길어야 한다. 통상적으로, 제2의 사전 결정된 펄스 시간은 0.1초 내지 20초이다. 제2의 사전 결정된 펄스 시간은 제어 밸브(32)를 통해 제어된다. 그 다음에 반응 챔버(12)는 제2의 퍼지 시간(통상적으로 상기 제시된 바와 같이 0.5초 내지 2분) 동안 비활성 기체를 이용하여 퍼지된다.
증착 주기의 최종 반응 단계에서, 그 다음에 환원제는 제3의 사전 결정된 시간 동안 환원제 공급원(34)으로부터 반응 챔버(12) 내로 도입된다. 적합한 환원제의 예는, 하이드라진, 하이드라진 수화물, 알킬 하이드라진, 1,1-디알킬하이드라진, 1,2-디알킬하이드라진, H2, H2 플라스마, 암모니아, 암모니아 플라스마, 실란, 디실란, 트리실란, 게르만, 디보란, 포르말린, 아민 보란, 디알킬 아연, 알킬 알루미늄, 알킬 갈륨, 알킬 인듐 복합체 및 기타 다른 플라스마계 가스, 및 이들의 조합물을 포함하지만, 이들로 제한되지 않는다. 제3의 사전 결정된 펄스 시간은 제2의 개질된 기판 표면 상에서 이용가능한 결합 부위가 그 위에 형성된 금속층으로 포화되도록 충분히 길어야 한다. 통상적으로, 제3의 사전 결정된 펄스 시간은 0.1초 내지 20초이다. 그 다음에 반응 챔버(12)는 제3의 퍼지 시간(통상적으로 상기 제시된 바와 같이 0.5초 내지 2분) 동안 비활성 기체를 이용하여 퍼지된다.
펄스 시간 및 퍼지 시간은 또한 화학적 전구체 및 기판의 기하학적 형상의 특성에 의존한다는 것이 인식되어야 한다. 편평한 기판 상의 박막 성장은 짧은 펄스 및 퍼지 시간을 사용하지만, 3차원 기판 상에서 ALD 성장의 펄스 및 퍼지 시간은 매우 길 수 있다. 그러므로, 일 개량에서, 펄스 시간 및 퍼지 시간은 각각 독립적으로 약 0.0001초 내지 200초이다. 다른 개량에서, 펄스 및 퍼지 시간은 각각 독립적으로 약 0.1초 내지 약 10초이다.
원하는 금속막 두께는 증착 주기의 수에 좌우된다. 예를 들어, Cu(dmap)2(dmap = 디메틸아미노-2-프로폭시드)로부터 증착된 구리 막에 대해, 1000 주기는 통상적으로 약 500 옹스트롬의 두께를 생성한다. 그러므로, 개량에서, 증착 주기는 다수회 반복되어 사전 결정된 금속막의 두께를 형성한다. 추가 개량에서, 증착 주기는 다수회 반복되어 두께가 약 5 나노미터 내지 약 200 나노미터인 금속막을 형성한다. 또 다른 개량에서, 증착 주기는 다수회 반복되어 두께가 약 5나노미터 내지 약 300 나노미터인 금속막을 형성한다. 또 다른 개량에서, 증착 주기는 다수회 반복되어 두께가 약 5 나노미터 내지 약 100 나노미터인 금속막을 형성한다.
본 실시형태의 방법에 의한 막 형성 동안, 기판 온도는 화학물질 전구체(들) 및 형성되는 막의 특성에 적합한 온도에 있을 것이다. 방법의 개량에서, 기판은 약 0℃ 내지 1000℃의 온도로 설정된다. 방법의 다른 개량에서, 기판은 온도가 약 50℃ 내지 450℃이다. 방법의 다른 개량에서, 기판은 온도가 약 100℃ 내지 250℃이다. 방법의 추가 다른 개량에서, 기판은 온도가 약 150℃ 내지 400℃이다. 방법의 다른 개량에서, 기판은 온도가 약 200℃ 내지 300℃이다.
유사하게, 막 형성 동안 압력은 화학물질 전구체 및 형성되는 막의 특성에 적합한 값으로 설정된다. 일 개량에서, 압력은 약 10-6토르 내지 약 760토르이다. 다른 개량에서, 압력은 약 0.1 밀리토르 내지 약 10토르이다. 또 다른 개량에서, 압력은 약 1밀리토르 내지 약 100밀리토르이다. 또 다른 개량에서, 압력은 약 1밀리토르 내지 20밀리토르이다.
다음의 실시예는 본 발명의 다양한 실시형태를 예시한다. 당업자는 본 발명의 사상과 특허청구범위의 범주 내에 있는 다양한 변형을 인식할 것이다.
ALD에 의한 Cu 막의 성장을 Cu(dmap)2(dmap = 디메틸아미노-2-프로폭시드), 포름산 및 무수 하이드라진을 사용하여 수행하였다. 성장 거동을 평가하기 위해, 전구체 펄스 길이, 기판 온도 및 주기의 수를 변화시켰다. 성장 속도를 120℃에서 Cu(dmap)2 펄스 길이의 함수로서 조사하였다. 증착 주기의 수, Cu(dmap)2의 길이, 포름산, 및 무수 하이드라진 펄스, 및 비활성 기체 퍼지 시간을 각각 1000, 3.0s, 0.2s, 0.2 s 및 5.0s에서 일정하게 유지시켰다. 도 5에 나타낸 바와 같이, ≥ 3s의 Cu(dmap)2 펄스 길이로 주기 당 약 0.50Å의 일정한 성장 속도를 제공하였다. 주기 당 0.45Å 및 0.35Å의 더 낮은 성장 속도를 각각 1.0s 및 0.5s의 Cu(dmap)2 펄스 길이에서 관찰하였다. ALD 성장의 중요한 필요조건은 모든 이용가능한 표면 부위가 각각의 전구체 펄스 동안 기체 전구체와 반응하는 것이다. 일단 이 조건이 충족되면, 전구체가 열 분해를 겪지 않는다는 조건 하에서, 과량의 전구체 흐름이 있을 때조차도 일정한 성장 속도가 관찰된다. 도 5의 조사는 ≥ 3.0s의 Cu(dmap)2 펄스 길이 및 더 짧은 펄스 시간에서 일어나는 자기 제한적 막 성장이 거의 포화된(sub-saturative) 성장으로 이어질 수 있다는 것을 나타낸다. 본 명세서의 연구를 위해, 3.0s의 Cu(dmap)2 펄스를 이용하여 자기 제한적 성장을 보장하였다. 성장 속도 대 포름산 펄스 길이 및 성장 속도 대 무수 하이드라진 펄스 길이의 유사한 플롯은 시약 둘 다에 대해 ≥ 0.2s의 펄스를 지니는 포화된 거동을 나타내었다. 이들 실험은 120℃에서 막 성장이 자기 제한적 ALD 메커니즘에 의해 진행한다는 것을 입증한다. 최적화된 증착 조건(3.0s Cu(dmap)2, 5.0s 퍼지, 0.2s 포름산, 5.0s 퍼지 0.2s 무수 하이드라진, 5.0s 퍼지)하에서, 1000 주기 증착은 상업적으로 입수가능한 ALD 반응기 상에서 약 5.0h을 필요로 하였다.
증착 온도의 함수로서 성장 속도를 또한 조사하였다(도 6). 110℃ 내지 160℃의 ALD 창을 관찰한다. 이들 증착의 조건은 Cu(dmap)2, 포름산 및 하이드라진 각각에 대해 3.0s, 0.2s 및 0.2s의 펄스 길이, 펄스 간에 5.0s의 퍼지 길이 및 1000 증착 주기로 이루어졌다. 0.47Å/주기 내지 0.50Å/주기의 일정한 성장 속도를 100℃ 내지 170℃에서 관찰하였다(ALD 창). 더 낮은 성장 속도가 80℃, 180℃ 및 200℃에서 일어났다.
증착 주기의 수에 대한 막 두께의 의존도를 다음에 조사하였다(도 7). 이들 실험에서, Cu(dmap)2, 포름산 및 하이드라진의 펄스 길이는 각각 3.0s, 0.2s 및 0.2s였고, 펄스 간에 5.0s의 펄스 길이를 지녔다. 증착 온도는 120℃였다. 필름 두께는 주기의 수에 의해 선형으로 변화하였고, 선의 기울기(0.50Å/주기)는 도 5에서 확립된 포화 성장 곡선과 동일하였다. 최고로 적합한 선은 1.46nm의 y절편을 나타내는데, 이는 실험오차 0 내에 있으며, 효율적인 핵 생성을 시사한다.
비행 시간-탄성 반동 검출 분석(Time of flight-elastic recoil detection analysis: TOF-ERDA)을 100℃, 120℃, 140℃, 160℃ 및 180℃에서 성장시킨 45nm 내지 50nm 두께의 필름 상에서 수행하여 원소 조성을 규명하였다(표 1). 막의 원자 조성은 95.9% 내지 98.8% 구리, 0.1% 내지 1.2% 탄소, 0.5% 내지 1.0% 산소, ≤ 0.4% 질소 및 ≤ 2.0% 수소의 범위에 있다. 일반적으로, 막은 100℃에서 가장 높은 순도를 가지며, 180℃에서 가장 낮은 순도를 가진다. 그러나 180℃ 온도에서 성장은 일부 전구체 자기 증착을 포함할 수 있지만, 조성물 내의 불확실한 것은 더 확정적인 결과를 불가능하게 한다. 시뮬레이션은 대다수의 불순물이 막 표면에 그리고 구리와 규소 기판 사이의 계면에 존재한다는 것을 입증한다. 탄소, 산소 및 수소 불순물은 주위 대기에 대한 증착 후 노출로부터 또는 막 내에 남아있는 미량의 포름산염으로부터 생길 수 있다.
X선 광전자 분광법(X-ray photoelectron spectroscopy: XPS)을 140℃에서 증착된 50nm 두께의 구리 필름 상에서 수행하여 막의 조성을 평가하였다. 증착할때 필름의 표면은 금속 구리로부터 생기는 예상된 이온화뿐만 아니라 산소 및 탄소로부터의 적은 이온화를 나타내었다. 질소 농도는 검출 한계 이하였다(< 1%). 아르곤 이온 스퍼터링 후, 구리 95.1원자%, 탄소 1.2원자%, 산소 3.1원자% 및 질소 < 1원자%의 일정한 조성을 관찰하였다. Cu2p1/2 및 Cu2p3/2 이온화는 952.2eV 및 932.4eV에서 나타났는데, 이는 구리 금속에 대해 정확하게 일치한다.
100℃에서 증착시킨 45nm 두께의 막 및 120℃, 140℃, 160℃ 및 180℃에서 성장시킨 50nm 두께의 막 상에서 분말 X선 회절 실험을 수행하였다. 증착될 때 모든 필름은 결정질이었고, 구리 금속의 (111), (200) 및 (220) 면으로부터 생기는 반사를 나타내었다(JCPDS 제출 번호 04-0836). 120℃에서 성장시킨 50nm 두께 막의 AFM 영상은 3.5nm의 rms 표면 거칠기를 가졌다. 동일 조건 하에 증착된 막의 SEM 영상은 균열이나 핀홀(pinhole)을 나타내지 않았고, 매우 균일한 표면을 나타내었다. 구리의 벌크 저항률(bulk resistivity)이 20℃에서 1.72μΩ인 것에 비하여, 100℃, 120℃ 및 140℃에서 증착된 45nm 내지 50nm 두께 구리 필름의 저항률은 20℃에서 9.6μΩ cm 내지 16.4μΩ cm였다. 비교를 위해 Si02 기판 상의 스퍼터링된 40nm 내지 50nm 두께의 구리 필름은 저항률이 6μΩ cm 내지 8μΩ cm였다. 따라서 본 발명자의 저항률 값은 고순도 구리 금속을 나타낸다. 모든 온도에서 성장시킨 막은 스카치 테이프 시험을 통과하였고, 이는 양호한 접착력을 입증한다.
본 발명의 실시형태를 예시하고, 설명하였지만, 이들 실시형태가 본 발명의 모든 가능한 형태를 예시하고 설명하는 것으로 의도하지는 않는다. 오히려, 본 명세서에 사용된 단어는 제한보다는 설명하는 단어이고, 본 발명의 사상과 범주로부터 벗어나지 않으면서 다양한 변화가 이루어질 수 있다는 것이 이해된다.
Claims (20)
- a) 기판은 원자층 증착이 발생하는 온도에 있고, 제1의 사전 결정된 펄스 시간 동안 상기 기판을 화학식 1에 의해 기술되는 금속 함유 화합물의 증기와 접촉시켜 제1의 개질된 표면을 형성하는 단계;
[화학식 1]
MLn
(상기 식에서
n은 1 내지 8이고;
M은 전이금속이며;
L은 리간드임);
b) 제2의 사전 결정된 펄스 시간 동안 제1의 개질된 표면을 산과 접촉시켜 제2의 개질된 표면을 형성하는 단계; 및
c) 제3의 사전 결정된 펄스 시간 동안 제2의 개질된 표면을 환원제와 접촉시켜 금속층을 형성하는 단계
를 포함하는 증착 주기를 포함하고,
상기 산은, HX, H3PO4, H3PO2, 포름산, 로 이루어진 군으로부터 선택되고, X는 N3 -, NO3 - 및 할로겐화물이고, R은 수소, C1-4 알킬, C6-12 아릴, Si(R3)3 또는 비닐이고; R3은 C1-8 알킬이며; n은 1 내지 6인, 기판 상에 금속막을 형성하는 방법. - 제1항에 있어서, M은 +2 산화 상태의 전이금속인 방법.
- 제1항에 있어서, M은 은, 팔라듐, 백금, 로듐, 이리듐, 코발트, 루테늄, 망간, 니켈 또는 구리인 방법.
- 제1항에 있어서, M은 구리인 방법.
- 삭제
- 삭제
- 제1항에 있어서, L에 대한 컨쥬게이트 산의 pKa는 단계 b)에서 사용되는 산의 pKa보다 큰 방법.
- 삭제
- 제1항에 있어서, 환원제는 하이드라진, 하이드라진 수화물, 알킬 하이드라진, 1,1-디알킬하이드라진, 1,2-디알킬하이드라진, H2, H2 플라스마, 암모니아, 암모니아 플라스마, 실란, 디실란, 트리실란, 게르만, 디보란, 포르말린, 아민 보란, 디알킬 아연, 알킬 알루미늄, 알킬 갈륨, 알킬 인듐 복합체 및 기타 다른 플라스마계 가스 및 이들의 조합물로 이루어진 군으로부터 선택되는 방법.
- 제1항에 있어서, 각각의 L은 독립적으로 2개의 전자 리간드, 여러자리 리간드, 하전된 리간드, 중성 리간드 및 이들의 조합으로 이루어진 군으로부터 선택되는 성분을 포함하는 방법.
- 제1항에 있어서, 2개의 L 리간드는 이좌배위자 리간드의 부분으로서 함께 조합되는 방법.
- 제11항에 있어서, 이좌배위자 리간드는 디메틸아미노-2-프로폭시드인 방법.
- 제1항에 있어서, 증착 주기는 다수회 반복되어 사전 결정된 두께의 금속막을 형성하는 방법.
- 제1항에 있어서, 증착 주기는 다수회 반복되어 두께가 5나노미터 내지 300나노미터인 금속막을 형성하는 방법.
- a) 제1의 사전 결정된 펄스 시간 동안 기판을 화학식 1에 의해 기술되는 금속 함유 화합물의 증기와 접촉시켜 제1의 개질된 표면을 형성하는 단계:
[화학식 1]
MLn
(상기 식에서:
n은 1 내지 8이고;
M은 전이금속이며;
L은 리간드임);
b) 제2의 사전 결정된 펄스 시간 동안 제1의 개질된 표면을 산과 접촉시켜 제2의 개질된 표면을 형성하는 단계(L에 대한 컨쥬게이트 산의 pKa는 이 단계에서 사용되는 산의 pKa보다 큼); 및
c) 제3의 사전 결정된 펄스 시간 동안 제2의 개질된 표면을 환원제와 접촉시켜 금속층을 형성하는 단계(증착 주기는 다수회 반복되어 두께가 5나노미터 내지 300나노미터인 금속막을 형성함)
를 포함하는 증착 주기를 포함하는, 기판 상에 금속막을 형성하는 방법. - 제19항에 있어서, L은 디메틸아미노-2-프로폭시드,
로 이루어진 군으로부터 선택되고(R, R1, R2는 각각 독립적으로 수소, C1-4 알킬, C6-12 아릴, Si(R3)3 또는 비닐이고; R3은 C1-8 알킬임);
단계 b)의 산은 포름산,
HX, H3PO4 및 H3P02로 이루어진 군으로부터 선택되며;
(X는 N3-, N03- 및 할로겐화물이고; R은 수소, C1-4 알킬, C6-12 아릴, Si(R3)3 또는 비닐이며; R3은 C1-8 알킬이고, n은 1 내지 6의 정수임);
환원제는 하이드라진, 하이드라진 수화물, 알킬 하이드라진, 1,1-디알킬하이드라진, 1,2-디알킬하이드라진, H2, H2 플라스마, 암모니아, 암모니아 플라스마, 실란, 디실란, 트리실란, 게르만, 디보란, 포르말린, 아민 보란, 디알킬 아연, 알킬 알루미늄, 알킬 갈륨, 알킬 인듐 복합체 및 기타 다른 플라스마계 가스, 및 이들의 조합물로 이루어진 군으로부터 선택되는 방법.