KR101168562B1 - 보호 필름이 부착된 다이싱 필름 - Google Patents

보호 필름이 부착된 다이싱 필름 Download PDF

Info

Publication number
KR101168562B1
KR101168562B1 KR1020120024293A KR20120024293A KR101168562B1 KR 101168562 B1 KR101168562 B1 KR 101168562B1 KR 1020120024293 A KR1020120024293 A KR 1020120024293A KR 20120024293 A KR20120024293 A KR 20120024293A KR 101168562 B1 KR101168562 B1 KR 101168562B1
Authority
KR
South Korea
Prior art keywords
film
east
dicing
transmittance
protective film
Prior art date
Application number
KR1020120024293A
Other languages
English (en)
Inventor
유이찌로 시시도
다께시 마쯔무라
Original Assignee
닛토덴코 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 닛토덴코 가부시키가이샤 filed Critical 닛토덴코 가부시키가이샤
Application granted granted Critical
Publication of KR101168562B1 publication Critical patent/KR101168562B1/ko

Abstract

본 발명은 다운 타임을 단축함과 함께, 다이싱 필름을 반도체 웨이퍼에 위치 어긋남을 일으키지 않고 부착하는 것을 가능하게 하는 보호 필름이 부착된 다이싱 필름을 제공한다.
또한 본 발명은 다이싱 필름과 보호 필름이 적층된 보호 필름이 부착된 다이싱 필름이며, 파장 600 내지 700nm에 있어서의 보호 필름의 투과율과, 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분에 있어서의 보호 필름이 부착된 다이싱 필름의 투과율과의 차가 20％ 이상인 것을 특징으로 하는 보호 필름이 부착된 다이싱 필름을 제공한다.

Description

보호 필름이 부착된 다이싱 필름 {DICING FILM HAVING PROTECTION FILM}
본 발명은 보호 필름이 부착된 다이싱 필름에 관한 것이다.
종래 반도체 웨이퍼는 미리 대면적으로 만들어진 후, 칩 형상으로 다이싱(절단 분리)되고, 익스팬드 공정으로 옮겨진다. 다이싱 필름은, 이 다이싱시에 반도체 웨이퍼를 고정하기 위해서 사용된다.
다이싱 필름에 고정된 반도체 웨이퍼는 칩 형상으로 다이싱되고, 각 칩끼리를 분리하기 위해서 익스팬드 링 위에서 면 방향으로 균일하게 익스팬드된 후, 픽업된다.
또한, 종래 다이싱 공정에서 반도체 웨이퍼를 접착 유지함과 함께, 마운트 공정에 필요한 칩 고착용 다이본드 필름도 부여하는 다이싱 필름이 제안되어 있다(예를 들어, 특허문헌 1 참조).
상술한 바와 같은 다이싱 필름은 반도체 웨이퍼의 크기에 맞춰서 원형 등으로 펀칭되고, 긴 보호 필름 위에 소정의 간격을 두고 배치되어 있으며, 웨이퍼 마운트 장치 등을 사용해서 보호 필름으로부터 다이싱 필름이 박리됨과 함께, 반도체 웨이퍼에 부착된다. 이때, 웨이퍼 마운트 장치는, 필름 검출용 광의 투과율이 변화하였을 때, 즉 광의 투과율이 보호 필름만의 투과율로부터 보호 필름과 다이싱 필름과의 합계의 투과율로 변화하였을 때에, 다이싱 필름을 검출하였다고 판단하고, 이 위치를 다이싱 필름 위치의 기준으로 하여, 다이싱 필름에 반도체 웨이퍼를 위치 어긋남을 일으키지 않도록 부착한다.
일본 특허 공개 소 60-57642호 공보
그러나, 종래 웨이퍼 마운트 장치에 있어서, 보호 필름 위의 다이싱 필름을 검출할 수 없으며, 검출 불가능한 다이싱 필름에 대해서는, 그대로 필름이 이송되어버려 사용되지 않고, 그 사이 다운 타임이 발생한다는 문제가 있었다. 또한, 검출의 지연에 의해, 다이싱 필름에 위치 어긋남이 발생한 상태에서 반도체 웨이퍼가 부착되어 버린다는 문제가 있었다.
본 발명은 상기 문제점을 감안하여 이루어진 것으로, 그의 목적은 다운 타임을 단축함과 함께, 다이싱 필름을 반도체 웨이퍼에 위치 어긋남을 일으키지 않고 부착하는 것을 가능하게 하는 보호 필름이 부착된 다이싱 필름을 제공하는 것에 있다.
본원 발명자들은, 상기 종래의 문제점을 해결하기 위해 보호 필름이 부착된 다이싱 필름에 대해서 검토하였다. 그 결과, 하기의 구성을 채용함으로써, 다운 타임을 단축함과 함께, 다이싱 필름을 반도체 웨이퍼에 위치 어긋남을 일으키지 않고 부착하는 것이 가능하다는 것을 발견해서 본 발명을 완성시키기에 이르렀다.
즉, 본 발명에 따른 보호 필름이 부착된 다이싱 필름은, 다이싱 필름과 보호 필름이 적층된 보호 필름이 부착된 다이싱 필름이며, 파장 600 내지 700nm에서의 상기 보호 필름의 투과율과, 상기 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분에 있어서의 상기 보호 필름이 부착된 다이싱 필름의 투과율과의 차가 20％ 이상인 것을 특징으로 한다.
상기 구성에 의하면, 파장 600 내지 700nm에 있어서의 상기 보호 필름의 투과율과, 상기 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분에 있어서의 상기 보호 필름이 부착된 다이싱 필름의 투과율과의 차가 20％ 이상이기 때문에, 필름 검출용 광을 검출하는 센서는, 보호 필름만의 투과율로부터, 다이싱 필름을 포함하는 보호 필름이 부착된 다이싱 필름의 투과율로 변화한 것을 확실하게 검출할 수 있다. 그 결과, 검출 불가능한 다이싱 필름이 이송되어버려 사용되지 않는 것 등을 방지할 수 있고, 그 사이의 다운 타임을 삭감할 수 있다. 또한, 검출의 지연에 의해, 다이싱 필름에 위치 어긋남이 발생한 상태에서 반도체 웨이퍼가 부착되어 버리는 것 등을 방지할 수 있고, 다이싱 필름을 반도체 웨이퍼에 위치 어긋남을 일으키지 않고 부착하는 것이 가능해진다.
상기 구성에 있어서, 상기 다이싱 필름은 기재와 상기 기재 위에 적층된 점착제층을 갖고 있으며, 상기 기재에는 엠보싱 처리가 실시되어 있는 것이 바람직하다. 상기 기재에 엠보싱 처리가 실시되어 있으면, 보호 필름만의 투과율과, 다이싱 필름을 포함하는 보호 필름이 부착된 다이싱 필름의 투과율과의 차를 보다 확실하게 20％ 이상으로 할 수 있다.
상기 구성에 있어서, 상기 다이싱 필름은 기재와 상기 기재 위에 적층된 점착제층을 갖고 있으며, 상기 기재가 착색되어 있는 것이 바람직하다. 상기 기재가 착색되어 있으면, 보호 필름만의 투과율과, 다이싱 필름을 포함하는 보호 필름이 부착된 다이싱 필름의 투과율과의 차를 보다 확실하게 20％ 이상으로 할 수 있다.
상기 구성에 있어서, 상기 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분에 있어서의 상기 보호 필름이 부착된 다이싱 필름의 투과율은 0 내지 70％인 것이 바람직하다. 상기 투과율이 0 내지 70％이면 상기 투과율의 차를 20％ 이상으로 하기 쉬워진다.
상기 구성에 있어서, 상기 보호 필름의 투과율은 75 내지 100％인 것이 바람직하다. 상기 투과율이 75 내지 100％이면 상기 투과율의 차를 20％ 이상으로 하기 쉬워진다.
상기 구성에 있어서, 상기 다이싱 필름의 상기 점착제층 위에 다이본드 필름이 적층되어 있는 것이 바람직하다. 다이싱 필름의 점착제층 위에 다이본드 필름이 적층되어 있으면, 다이본드 필름을 부착하는 공정을 생략할 수 있어, 제조 효율을 향상시킬 수 있다.
도 1의 (a)는 본 발명의 한 실시 형태에 따른 보호 필름이 부착된 다이싱 필름을 도시하는 단면 모식도이고, (b)는 그의 평면도이다.
도 2는 도 1의 (a) 및 도 1의 (b)에 나타낸 보호 필름이 부착된 다이싱 필름의 일부를 도시하는 단면 모식도이다.
도 3은 다른 실시 형태에 따른 보호 필름이 부착된 다이싱 필름을 도시하는 단면 모식도이다.
도 4의 (a), (b)는 본 실시 형태에 따른 반도체 장치의 제조 방법을 설명하기 위한 단면 모식도이다.
도 5는 도 1 및 도 2에 도시한 보호 필름이 부착된 다이싱 필름에 있어서의 접착제층을 개재시켜 반도체 칩을 실장한 예를 도시하는 단면 모식도이다.
(보호 필름이 부착된 다이싱 필름)
본 발명의 한 실시 형태에 따른 보호 필름이 부착된 다이싱 필름에 대해서, 이하에 설명한다. 도 1의 (a)는, 본 발명의 한 실시 형태에 따른 보호 필름이 부착된 다이싱 필름을 나타내는 단면 모식도이며, 도 1의 (b)는 그의 평면도이다. 도 2는, 도 1의 (a) 및 도 1의 (b)에 나타낸 보호 필름이 부착된 다이싱 필름의 일부를 도시하는 단면 모식도이다.
도 1의 (a), 도 1의 (b)에 도시한 바와 같이, 보호 필름이 부착된 다이싱 필름(10)은, 긴 보호 필름(14) 위에 평면에서 볼 때 원 형상인 다이싱 필름(11)이 적층된 구성을 갖는다. 다이싱 필름(11)은 기재(1) 위에 점착제층(2)을 적층해서 구성되어 있고, 점착제층(2)에는 다이싱 필름(11)보다도 직경이 작은 다이본드 필름(3)이 적층되어 있다. 다이싱 필름(11)은, 점착제층(2) 및 다이본드 필름(3)과 대향시키도록 보호 필름(14)에 적층되어 있다. 또한, 본 발명에 있어서는 다이본드 필름이 적층되어 있지 않아도 좋다.
보호 필름이 부착된 다이싱 필름(10)은, 반도체 장치의 제조 공정에 있어서, 일정 방향(도 1의 (b)에서는 좌측 방향)으로 풀어지게 됨과 함께, 보호 필름(14)의 폭 방향 중앙 부분(16)에 필름 검출용 광 L이 조사된다. 이때, 파장 600 내지 700nm에 있어서의 보호 필름(14)의 투과율 T1(도 1의 (a) 참조)과, 다이싱 필름(11)의 광 L이 최초로 투과하는 부분(17)에 있어서의 보호 필름이 부착된 다이싱 필름(10)(본 실시 형태에서는, 보호 필름(14)과 다이싱 필름(11)과의 적층 부분)의 투과율 T2(도 1의 (a) 참조)와의 차는 20％ 이상이다. 상기 투과율의 차는 20％ 이상 40％ 이하인 것이 바람직하고, 30％ 이상 40％ 이하인 것이 보다 바람직하다. 상기 투과율의 차가 20％ 이상이기 때문에, 필름 검출용 광을 검출하는 센서는, 보호 필름(14)만의 투과율 T1로부터 보호 필름(14)과 다이싱 필름(11)과의 적층 부분의 투과율 T2로 변화한 것을 확실하게 인식할 수 있다. 그 결과, 검출 불가능한 다이싱 필름이 이송되어버려져 사용되지 않는 것 등을 방지할 수 있고, 그 사이의 다운 타임을 삭감할 수 있다. 또한, 다이싱 필름을 반도체 웨이퍼에 위치 어긋남을 일으키지 않고 부착하는 것이 가능해진다.
투과율 T1은 75 내지 100％인 것이 바람직하고, 80 내지 100％인 것이 보다 바람직하며, 85 내지 100％인 것이 더욱 바람직하다. 투과율 T1이 75 내지 100％이면 상기 투과율의 차를 20％ 이상으로 하기 쉬워진다.
투과율 T2는 0 내지 70％인 것이 바람직하고, 0 내지 65％인 것이 보다 바람직하며, 0 내지 65％인 것이 더욱 바람직하다. 투과율 T2가 0 내지 70％이면 상기 투과율의 차를 20％ 이상으로 하기 쉬워진다.
상기 기재(1)는 자외선 투과성을 갖는 것이 바람직하고, 다이싱 필름(11)의 강도 모체가 되는 것이다. 예를 들어, 저밀도 폴리에틸렌, 직쇄상 폴리에틸렌, 중밀도 폴리에틸렌, 고밀도 폴리에틸렌, 초저밀도 폴리에틸렌, 랜덤 공중합 폴리프로필렌, 블록 공중합 폴리프로필렌, 호모 폴리프로필렌, 폴리부텐, 폴리메틸펜텐 등의 폴리올레핀, 에틸렌-아세트산 비닐 공중합체, 아이오노머 수지, 에틸렌-(메트)아크릴산 공중합체, 에틸렌-(메트)아크릴산에스테르(랜덤, 교대) 공중합체, 에틸렌-부텐 공중합체, 에틸렌-헥센 공중합체, 폴리우레탄, 폴리에틸렌테레프탈레이트, 폴리에틸렌나프탈레이트 등의 폴리에스테르, 폴리카르보네이트, 폴리이미드, 폴리에테르에테르케톤, 폴리이미드, 폴리에테르이미드, 폴리아미드, 전체 방향족 폴리아미드, 폴리페닐술피드, 아라미드(종이), 유리, 유리 섬유, 불소 수지, 폴리염화비닐, 폴리염화비닐리덴, 셀룰로오스계 수지, 실리콘 수지, 금속(박), 종이 등을 들 수 있다.
또한 기재(1)의 재료로는 상기 수지의 가교체 등의 중합체를 들 수 있다. 상기 플라스틱 필름은 비연신으로 사용해도 좋고, 필요에 따라 1축 또는 2축의 연신 처리를 실시한 것을 사용해도 좋다. 연신 처리 등에 의해 열수축성을 부여한 수지 시트에 의하면, 다이싱 후에 그의 기재(1)를 열수축시킴으로써 점착제층(2)과 다이본드 필름(3)과의 접착 면적을 저하시켜, 반도체 칩(반도체 소자) 회수의 용이화를 도모할 수 있다.
기재(1)는 착색되어 있는 것이 바람직하다. 기재(1)가 착색되어 있으면, 보호 필름(14)만의 투과율 T1과, 보호 필름(14) 및 다이싱 필름의 적층 부분(11)의 투과율 T2와의 차를 보다 확실하게 20％ 이상으로 할 수 있다. 기재(1)를 착색할 때에는, 목적으로 하는 광의 투과율에 따라 색재(착색제)를 사용할 수 있다. 이러한 색재로는 흑색계 색재, 청색계 색재, 적색계 색재 등의 각종 농색계 색재를 적절하게 사용할 수 있고, 특히 흑색계 색재가 적합하다. 색재로는 안료, 염료 등 중 어느 것이어도 좋다. 색재는 단독으로 또는 2종 이상을 조합해서 사용할 수 있다. 또한, 염료로는 산성 염료, 반응 염료, 직접 염료, 분산 염료, 양이온 염료 등 중 어느 형태의 염료여도 사용하는 것이 가능하다. 또한, 안료도 그의 형태는 특별히 제한되지 않으며, 공지된 안료로부터 적절히 선택해서 사용할 수 있다.
특히 색재로서 염료를 사용하면, 기재(1) 중에는 염료가 용해에 의해 균일하거나 또는 거의 균일하게 분산된 상태가 되기 때문에, 착색 농도가 균일한 기재(1)를 용이하게 제조할 수 있다.
흑색계 색재로는 특별히 제한되지 않지만, 예를 들어 무기의 흑색계 안료, 흑색계 염료로부터 적절히 선택할 수 있다. 또한, 흑색계 색재로는 시안계 색재(청록색계 색재), 마젠타계 색재(적보라색계 색재) 및 옐로우계 색재(황색계 색재)가 혼합된 색재 혼합물이어도 좋다. 흑색계 색재는 단독으로 또는 2종 이상을 조합해서 사용할 수 있다. 물론, 흑색계 색재는 흑색 이외의 색의 색재와 병용할 수도 있다.
구체적으로는 흑색계 색재로는, 예를 들어 카본 블랙(퍼니스 블랙, 채널 블랙, 아세틸렌 블랙, 서멀 블랙, 램프 블랙 등), 그래파이트(흑연), 산화구리, 이산화망간, 아조계 안료(아조메틴아조 블랙 등), 아닐린 블랙, 페릴렌 블랙, 티타늄 블랙, 시아닌 블랙, 활성탄, 페라이트(비자성 페라이트, 자성 페라이트 등), 마그네타이트, 산화크롬, 산화철, 이황화몰리브덴, 크롬 착체, 복합 산화물계 흑색 색소, 안트라퀴논계 유기 흑색 색소 등을 들 수 있다.
본 발명에서는, 흑색계 색재로는 C.I. 솔벤트 블랙 3, 동 7, 동 22, 동 27, 동 29, 동 34, 동 43, 동 70, C.I. 다이렉트 블랙 17, 동 19, 동 22, 동 32, 동 38, 동 51, 동 71, C.I. 애시드 블랙 1, 동 2, 동 24, 동 26, 동 31, 동 48, 동 52, 동 107, 동 109, 동 110, 동 119, 동 154, C.I. 디스퍼스 블랙 1, 동 3, 동 10, 동 24 등의 블랙계 염료; C.I. 피그먼트 블랙 1, 동 7 등의 블랙계 안료 등도 이용할 수 있다.
이러한 흑색계 색재로는, 예를 들어 상품명 "Oil Black BY", 상품명 "Oil Black BS", 상품명 "Oil Black HBB", 상품명 "Oil Black 803", 상품명 "Oil Black 860", 상품명 "Oil Black 5970", 상품명 "Oil Black 5906", 상품명 "Oil Black 5905"(오리엔트 가가꾸 고교 가부시끼가이샤제) 등이 시판되고 있다.
흑색계 색재 이외의 색재로는, 예를 들어 시안계 색재, 마젠타계 색재, 옐로우계 색재 등을 들 수 있다. 시안계 색재로는, 예를 들어 C.I. 솔벤트 블루 25, 동 36, 동 60, 동 70, 동 93, 동 95; C.I. 애시드 블루 6, 동 45 등의 시안계 염료; C.I. 피그먼트 블루 1, 동 2, 동 3, 동 15, 동 15:1, 동 15:2, 동 15:3, 동 15:4, 동 15:5, 동 15:6, 동 16, 동 17, 동 17:1, 동 18, 동 22, 동 25, 동 56, 동 60, 동 63, 동 65, 동 66; C.I. 배트 블루 4; 동 60, C.I. 피그먼트 그린 7 등의 시안계 안료 등을 들 수 있다.
또한, 마젠타계 색재에 있어서, 마젠타계 염료로는, 예를 들어 C.I. 솔벤트 레드 1, 동 3, 동 8, 동 23, 동 24, 동 25, 동 27, 동 30, 동 49, 동 52, 동 58, 동 63, 동 81, 동 82, 동 83, 동 84, 동 100, 동 109, 동 111, 동 121, 동 122; C.I. 디스퍼스 레드 9; C.I. 솔벤트 바이올렛 8, 동 13, 동 14, 동 21, 동 27; C.I. 디스퍼스 바이올렛 1; C.I. 베이직 레드 1, 동 2, 동 9, 동 12, 동 13, 동 14, 동 15, 동 17, 동 18, 동 22, 동 23, 동 24, 동 27, 동 29, 동 32, 동 34, 동 35, 동 36, 동 37, 동 38, 동 39, 동 40; C.I. 베이직 바이올렛 1, 동 3, 동 7, 동 10, 동 14, 동 15, 동 21, 동 25, 동 26, 동 27, 동 28 등을 들 수 있다.
마젠타계 색재에 있어서, 마젠타계 안료로는, 예를 들어 C.I. 피그먼트 레드 1, 동 2, 동 3, 동 4, 동 5, 동 6, 동 7, 동 8, 동 9, 동 10, 동 11, 동 12, 동 13, 동 14, 동 15, 동 16, 동 17, 동 18, 동 19, 동 21, 동 22, 동 23, 동 30, 동 31, 동 32, 동 37, 동 38, 동 39, 동 40, 동 41, 동 42, 동 48:1, 동 48:2, 동 48:3, 동 48:4, 동 49, 동 49:1, 동 50, 동 51, 동 52, 동 52:2, 동 53:1, 동 54, 동 55, 동 56, 동 57:1, 동 58, 동 60, 동 60:1, 동 63, 동 63:1, 동 63:2, 동 64, 동 64:1, 동 67, 동 68, 동 81, 동 83, 동 87, 동 88, 동 89, 동 90, 동 92, 동 101, 동 104, 동 105, 동 106, 동 108, 동 112, 동 114, 동 122, 동 123, 동 139, 동 144, 동 146, 동 147, 동 149, 동 150, 동 151, 동 163, 동 166, 동 168, 동 170, 동 171, 동 172, 동 175, 동 176, 동 177, 동 178, 동 179, 동 184, 동 185, 동 187, 동 190, 동 193, 동 202, 동 206, 동 207, 동 209, 동 219, 동 222, 동 224, 동 238, 동 245; C.I. 피그먼트 바이올렛 3, 동 9, 동 19, 동 23, 동 31, 동 32, 동 33, 동 36, 동 38, 동 43, 동 50; C.I. 배트 레드 1, 동 2, 동 10, 동 13, 동 15, 동 23, 동 29, 동 35 등을 들 수 있다.
또한, 옐로우계 색재로는, 예를 들어 C.I. 솔벤트 옐로우 19, 동 44, 동 77, 동 79, 동 81, 동 82, 동 93, 동 98, 동 103, 동 104, 동 112, 동 162 등의 옐로우계 염료; C.I. 피그먼트 오렌지 31, 동 43; C.I. 피그먼트 옐로우 1, 동 2, 동 3, 동 4, 동 5, 동 6, 동 7, 동 10, 동 11, 동 12, 동 13, 동 14, 동 15, 동 16, 동 17, 동 23, 동 24, 동 34, 동 35, 동 37, 동 42, 동 53, 동 55, 동 65, 동 73, 동 74, 동 75, 동 81, 동 83, 동 93, 동 94, 동 95, 동 97, 동 98, 동 100, 동 101, 동 104, 동 108, 동 109, 동 110, 동 113, 동 114, 동 116, 동 117, 동 120, 동 128, 동 129, 동 133, 동 138, 동 139, 동 147, 동 150, 동 151, 동 153, 동 154, 동 155, 동 156, 동 167, 동 172, 동 173, 동 180, 동 185, 동 195; C.I.배트 옐로우 1, 동 3, 동 20 등의 옐로우계 안료 등을 들 수 있다.
시안계 색재, 마젠타계 색재, 옐로우계 색재 등의 각종 색재는 각각 단독으로 또는 2종 이상을 조합해서 사용할 수 있다. 또한, 시안계 색재, 마젠타계 색재, 옐로우계 색재 등의 각종 색재를 2종 이상 사용하는 경우, 이들 색재의 혼합 비율(또는 배합 비율)로는 특별히 제한되지 않고, 각 색재의 종류나 목적으로 하는 광의 투과율 등에 따라 적절히 선택할 수 있다.
기재(1)의 표면은 엠보싱 처리가 실시되어 있는 것이 바람직하다. 기재(1)에 엠보싱 처리가 실시되어 있으면, 보호 필름(14)만의 투과율 T1과, 보호 필름(14) 및 다이싱 필름(11)의 적층 부분의 투과율 T2와의 차를 더욱 확실하게 20％ 이상으로 할 수 있다. 엠보싱 처리의 방법으로는, 예를 들어 필름을 엠보싱 롤에 첨가시키는 방법, 샌드 매트 처리에 의한 방법, 에칭 등의 화학적으로 처리하는 방법 등을 들 수 있다. 엠보싱 처리의 기준으로는, 예를 들어 헤이즈값을 들 수 있다. 기재(1)의 표면의 헤이즈값은 10 내지 100％인 것이 바람직하고, 보다 바람직하게는 20 내지 100％, 더욱 바람직하게는 30 내지 100％이다. 기재(1)의 표면의 헤이즈값을 10 내지 100％로 함으로써, 투과율 T1과 투과율 T2와의 차를 확실하게 20％ 이상으로 할 수 있다.
또한, 기재(1)의 표면은 인접하는 층과의 밀착성, 유지성 등을 높이기 위해, 관용의 표면 처리, 예를 들어 크롬산 처리, 오존 폭로, 화염 폭로, 고압 전격 폭로, 이온화 방사선 처리 등의 화학적 또는 물리적 처리, 하도제(예를 들어, 후술하는 점착 물질)에 의한 코팅 처리를 실시할 수 있다. 상기 기재(1)는 동종 또는 이종의 것을 적절하게 선택해서 사용할 수 있고, 필요에 따라 수종을 블렌드한 것을 사용할 수 있다.
기재(1)의 두께는 특별히 제한되지 않고 적절하게 결정할 수 있지만, 일반적으로는 5 내지 200㎛ 정도이다.
점착제층(2)의 형성에 사용하는 점착제로는 특별히 제한되지 않으며, 예를 들어 아크릴계 점착제, 고무계 점착제 등의 일반적인 감압성 점착제를 사용할 수 있다. 상기 감압성 점착제로는, 반도체 웨이퍼나 유리 등의 오염을 싫어하는 전자 부품의 초순수나 알코올 등의 유기 용제에 의한 청정 세정성 등의 관점에서, 아크릴계 중합체를 베이스 중합체로 하는 아크릴계 점착제가 바람직하다.
상기 아크릴계 중합체로는, 예를 들어 (메트)아크릴산알킬에스테르(예를 들어, 메틸에스테르, 에틸에스테르, 프로필에스테르, 이소프로필에스테르, 부틸에스테르, 이소부틸에스테르, s-부틸에스테르, t-부틸에스테르, 펜틸에스테르, 이소펜틸에스테르, 헥실에스테르, 헵틸에스테르, 옥틸에스테르, 2-에틸헥실에스테르, 이소옥틸에스테르, 노닐에스테르, 데실에스테르, 이소데실에스테르, 운데실에스테르, 도데실에스테르, 트리데실에스테르, 테트라데실에스테르, 헥사데실에스테르, 옥타데실에스테르, 에이코실에스테르 등의 알킬기의 탄소수 1 내지 30, 특히 탄소수 4 내지 18의 직쇄상 또는 분지쇄상의 알킬에스테르 등) 및 (메트)아크릴산시클로알킬에스테르(예를 들어, 시클로펜틸에스테르, 시클로헥실에스테르 등)의 1종 또는 2종 이상을 단량체 성분으로서 사용한 아크릴계 중합체 등을 들 수 있다. 또한, (메트)아크릴산에스테르란 아크릴산에스테르 및/또는 메타크릴산에스테르를 말하며, 본 발명의 (메트)란 모두 마찬가지의 의미이다.
상기 아크릴계 중합체는 응집력, 내열성 등의 개질을 목적으로, 필요에 따라 상기 (메트)아크릴산알킬에스테르 또는 시클로알킬에스테르와 공중합 가능한 다른 단량체 성분에 대응하는 단위를 포함할 수도 있다. 이러한 단량체 성분으로서, 예를 들어 아크릴산, 메타크릴산, 카르복시에틸(메트)아크릴레이트, 카르복시펜틸(메트)아크릴레이트, 이타콘산, 말레산, 푸마르산, 크로톤산 등의 카르복실기 함유 단량체; 무수 말레산, 무수 이타콘산 등의 산 무수물 단량체; (메트)아크릴산 2-히드록시에틸, (메트)아크릴산 2-히드록시프로필, (메트)아크릴산 4-히드록시부틸, (메트)아크릴산 6-히드록시헥실, (메트)아크릴산 8-히드록시옥틸, (메트)아크릴산 10-히드록시데실, (메트)아크릴산 12-히드록시라우릴, (4-히드록시메틸시클로헥실)메틸(메트)아크릴레이트 등의 히드록실기 함유 단량체; 스티렌술폰산, 알릴술폰산, 2-(메트)아크릴아미드-2-메틸프로판술폰산, (메트)아크릴아미드프로판술폰산, 술포프로필(메트)아크릴레이트, (메트)아크릴로일옥시나프탈렌술폰산 등의 술폰산기 함유 단량체; 2-히드록시에틸아크릴로일포스페이트 등의 인산기 함유 단량체; 아크릴아미드, 아크릴로니트릴 등을 들 수 있다. 이들 공중합 가능한 단량체 성분은 1종 또는 2종 이상 사용할 수 있다. 이들 공중합 가능한 단량체의 사용량은 전체 단량체 성분의 40중량％ 이하가 바람직하다.
또한, 상기 아크릴계 중합체는 가교시키기 위해, 다관능성 단량체 등도 필요에 따라 공중합용 단량체 성분으로서 포함할 수 있다. 이러한 다관능성 단량체로서, 예를 들어 헥산디올디(메트)아크릴레이트, (폴리)에틸렌글리콜디(메트)아크릴레이트, (폴리)프로필렌글리콜디(메트)아크릴레이트, 네오펜틸글리콜디(메트)아크릴레이트, 펜타에리트리톨디(메트)아크릴레이트, 트리메틸올프로판트리(메트)아크릴레이트, 펜타에리트리톨트리(메트)아크릴레이트, 디펜타에리트리톨헥사(메트)아크릴레이트, 에폭시(메트)아크릴레이트, 폴리에스테르(메트)아크릴레이트, 우레탄(메트)아크릴레이트 등을 들 수 있다. 이들의 다관능성 단량체도 1종 또는 2종 이상 사용할 수 있다. 다관능성 단량체의 사용량은 점착 특성 등의 관점에서, 전체 단량체 성분의 30중량％ 이하가 바람직하다.
상기 아크릴계 중합체는 단일 단량체 또는 2종 이상의 단량체 혼합물을 중합에 가함으로써 얻어진다. 중합은 용액 중합, 유화 중합, 괴상 중합, 현탁 중합 등 중 어느 방식으로 행할 수도 있다. 청정한 피착체에 대한 오염 방지 등의 관점에서, 저분자량 물질의 함유량이 작은 것이 바람직하다. 이 점으로부터, 아크릴계 중합체의 수 평균 분자량은, 바람직하게는 30만 이상, 더욱 바람직하게는 40만 내지 300만 정도이다.
또한, 상기 점착제에는 베이스 중합체인 아크릴계 중합체 등의 수 평균 분자량을 높이기 위해, 외부 가교제를 적절하게 채용할 수도 있다. 외부 가교 방법의 구체적 수단으로는, 폴리이소시아네이트 화합물, 에폭시 화합물, 아질리딘 화합물, 멜라민계 가교제 등의 소위 가교제를 첨가하여 반응시키는 방법을 들 수 있다. 외부 가교제를 사용하는 경우, 그의 사용량은 가교해야 하는 베이스 중합체와의 밸런스에 따라, 나아가 점착제로서의 사용 용도에 따라 적절히 결정된다. 일반적으로는, 상기 베이스 중합체 100중량부에 대하여 5중량부 정도 이하, 또한 0.1 내지 5중량부 배합하는 것이 바람직하다. 또한, 점착제에는 필요에 따라 상기 성분 이외에, 종래 공지된 각종 점착 부여제, 노화 방지제 등의 첨가제를 사용해도 좋다.
점착제층(2)은 방사선 경화형 점착제에 의해 형성할 수 있다. 방사선 경화형 점착제는, 자외선 등의 방사선의 조사에 의해 가교도를 증대시켜서 그의 점착력을 용이하게 저하시킬 수 있고, 도 2에 도시하는 점착제층(2)의 워크 부착 부분에 대응하는 부분(2a)만을 방사선 조사함으로써 다른 부분(2b)과의 점착력의 차를 만들 수 있다.
또한, 도 2에 도시하는 다이본드 필름(3)에 맞춰서 방사선 경화형의 점착제층(2)을 경화시킴으로써, 점착력이 현저하게 저하된 상기 부분(2a)을 용이하게 형성할 수 있다. 경화하고, 점착력이 저하된 상기 부분(2a)에 다이본드 필름(3)이 부착되기 때문에, 점착제층(2)의 상기 부분(2a)과 다이본드 필름(3)과의 계면은, 픽업시에 용이하게 박리되는 성질을 갖는다. 한편, 방사선을 조사하지 않은 부분은 충분한 점착력을 갖고 있으며, 상기 부분(2b)을 형성한다. 상기 부분(2b)에는, 웨이퍼 링을 고정할 수 있다.
방사선 경화형 점착제는, 탄소-탄소 이중 결합 등의 방사선 경화성의 관능기를 가지며, 점착성을 나타내는 것을 특별히 제한없이 사용할 수 있다. 방사선 경화형 점착제로는, 예를 들어 상기 아크릴계 점착제, 고무계 점착제 등의 일반적인 감압성 점착제에, 방사선 경화성의 단량체 성분이나 올리고머 성분을 배합한 첨가형의 방사선 경화형 점착제를 예시할 수 있다.
배합하는 방사선 경화성의 단량체 성분으로는, 예를 들어 우레탄 올리고머, 우레탄(메트)아크릴레이트, 트리메틸올프로판트리(메트)아크릴레이트, 테트라메틸올메탄테트라(메트)아크릴레이트, 펜타에리트리톨트리(메트)아크릴레이트, 펜타에리트리톨테트라(메트)아크릴레이트, 디펜타에리트리톨모노히드록시펜타(메트)아크릴레이트, 디펜타에리트리톨헥사(메트)아크릴레이트, 1,4-부탄디올디(메트)아크릴레이트 등을 들 수 있다. 또한 방사선 경화성의 올리고머 성분은 우레탄계, 폴리에테르계, 폴리에스테르계, 폴리카르보네이트계, 폴리부타디엔계 등 다양한 올리고머를 들 수 있고, 그의 분자량이 100 내지 30000 정도의 범위인 것이 적당하다. 방사선 경화성의 단량체 성분이나 올리고머 성분의 배합량은, 상기 점착제층의 종류에 따라 점착제층의 점착력을 저하시킬 수 있는 양을 적절하게 결정할 수 있다. 일반적으로는, 점착제를 구성하는 아크릴계 중합체 등의 베이스 중합체 100중량부에 대하여, 예를 들어 5 내지 500중량부, 바람직하게는 40 내지 150중량부 정도이다.
또한, 방사선 경화형 점착제로는, 상기 설명한 첨가형의 방사선 경화형 점착제 이외에, 베이스 중합체로서, 탄소-탄소 이중 결합을 중합체 측쇄 또는 주쇄 중 혹은 주쇄 말단에 갖는 것을 사용한 내재형의 방사선 경화형 점착제를 들 수 있다. 내재형의 방사선 경화형 점착제는, 저분자 성분인 올리고머 성분 등을 함유할 필요가 없거나, 또는 대부분은 포함하지 않기 때문에, 경시적으로 올리고머 성분 등이 점착제재 중을 이동하지 않고, 안정된 층 구조의 점착제층을 형성할 수 있기 때문에 바람직하다.
상기 탄소-탄소 이중 결합을 갖는 베이스 중합체는 탄소-탄소 이중 결합을 가지며, 점착성을 갖는 것을 특별히 제한없이 사용할 수 있다. 이러한 베이스 중합체로는, 아크릴계 중합체를 기본 골격으로 하는 것이 바람직하다. 아크릴계 중합체의 기본 골격으로는, 상기 예시한 아크릴계 중합체를 들 수 있다.
상기 아크릴계 중합체에 대한 탄소-탄소 이중 결합의 도입법은 특별히 제한되지 않고, 다양한 방법을 채용할 수 있지만, 탄소-탄소 이중 결합은 중합체 측쇄에 도입하는 것이 분자 설계가 용이하다. 예를 들어, 미리 아크릴계 중합체에 관능기를 갖는 단량체를 공중합한 후, 이 관능기와 반응할 수 있는 관능기 및 탄소-탄소 이중 결합을 갖는 화합물을, 탄소-탄소 이중 결합의 방사선 경화성을 유지한 상태에서 축합 또는 부가 반응시키는 방법을 들 수 있다.
이들 관능기 조합의 예로는, 카르복실산기와 에폭시기, 카르복실산기와 아질리딜기, 히드록실기와 이소시아네이트기 등을 들 수 있다. 이들 관능기의 조합 중에서도 반응 추적의 용이함 때문에, 히드록실기와 이소시아네이트기와의 조합이 적합하다. 또한, 이들 관능기의 조합에 의해, 상기 탄소-탄소 이중 결합을 갖는 아크릴계 중합체를 생성하는 조합이면, 관능기는 아크릴계 중합체와 상기 화합물 중 어느측에 있어도 좋지만, 상기한 바람직한 조합에서는, 아크릴계 중합체가 히드록실기를 갖고, 상기 화합물이 이소시아네이트기를 갖는 경우가 적합하다. 이 경우, 탄소-탄소 이중 결합을 갖는 이소시아네이트 화합물로는, 예를 들어 메타크릴로일이소시아네이트, 2-메타크릴로일옥시에틸이소시아네이트, m-이소프로페닐-α,α-디메틸벤질이소시아네이트 등을 들 수 있다. 또한, 아크릴계 중합체로는 상기 예시한 히드록시기 함유 단량체나 2-히드록시에틸비닐에테르, 4-히드록시부틸비닐에테르, 디에틸렌글리콜모노비닐에테르의 에테르계 화합물 등을 공중합한 것이 사용된다.
상기 내재형의 방사선 경화형 점착제는 상기 탄소-탄소 이중 결합을 갖는 베이스 중합체(특히 아크릴계 중합체)를 단독으로 사용할 수 있지만, 특성을 악화시키지 않을 정도로 상기 방사선 경화성의 단량체 성분이나 올리고머 성분을 배합할 수도 있다. 방사선 경화성의 올리고머 성분 등은, 통상 베이스 중합체 100중량부에 대하여 3.0중량부의 범위 내이며, 바람직하게는 0 내지 10중량부의 범위이다.
상기 방사선 경화형 점착제에는, 자외선 등에 의해 경화시킨 경우에는 광중합 개시제를 함유시킨다. 광중합 개시제로는, 예를 들어 4-(2-히드록시에톡시)페닐(2-히드록시-2-프로필)케톤, α-히드록시-α,α'-디메틸아세토페논, 2-메틸-2-히드록시프로피오페논, 1-히드록시시클로헥실페닐케톤 등의 α-케톨계 화합물; 메톡시아세토페논, 2,2-디메톡시-2-페닐아세토페논, 2,2-디에톡시아세토페논, 2-메틸-1-[4-(메틸티오)-페닐]-2-모르폴리노프로판-1 등의 아세토페논계 화합물; 벤조인에틸에테르, 벤조인이소프로필에테르, 아니소인메틸에테르 등의 벤조인에테르계 화합물; 벤질디메틸케탈 등의 케탈계 화합물; 2-나프탈렌술포닐클로라이드 등의 방향족 술포닐클로라이드계 화합물; 1-페논-1,1-프로판디온-2-(o-에톡시카르보닐)옥심 등의 광 활성 옥심계 화합물; 벤조페논, 벤조일벤조산, 3,3'-디메틸-4-메톡시벤조페논 등의 벤조페논계 화합물; 티오크산톤, 2-클로로티오크산톤, 2-메틸티오크산톤, 2,4-디메틸티오크산톤, 이소프로필티오크산톤, 2,4-디클로로티오크산톤, 2,4-디에틸티오크산톤, 2,4-디이소프로필티오크산톤 등의 티오크산톤계 화합물; 캄포퀴논; 할로겐화케톤; 아실포스핀옥시드; 아실포스포네이트 등을 들 수 있다. 광중합 개시제의 배합량은, 점착제를 구성하는 아크릴계 중합체 등의 베이스 중합체 100중량부에 대하여, 예를 들어 0.05 내지 20중량부 정도이다.
또한 방사선 경화형 점착제로는, 예를 들어 일본 특허 공개 소 60-196956호 공보에 개시되어 있는, 불포화 결합을 2개 이상 갖는 부가 중합성 화합물, 에폭시기를 갖는 알콕시실란 등의 광중합성 화합물과, 카르보닐 화합물, 유기 황 화합물, 과산화물, 아민, 오늄염계 화합물 등의 광중합 개시제를 함유하는 고무계 점착제나 아크릴계 점착제 등을 들 수 있다.
점착제층(2) 중에는, 기재(1)에 색재를 첨가하는 것 대신에, 또는 기재(1)에 색재를 첨가하는 것 이외에 색재를 첨가할 수 있다. 점착제층(2)에 첨가하는 색재로는, 상술한 기재(1)에 첨가하는 색재와 마찬가지의 것을 사용할 수 있다. 색재의 첨가 방법으로는, 예를 들어 점착제 조성물 용액에 색재를 용해 또는 분산시키는 방법을 들 수 있다.
점착제층(2)을 방사선 경화형 점착제에 의해 형성하는 경우에는, 점착제층(2)에 있어서의 상기 부분(2a)의 점착력<기타 부분 부분(2b)의 점착력이 되도록 점착제층(2)의 일부를 방사선 조사해도 좋다.
상기 점착제층(2)에 상기 부분(2a)을 형성하는 방법으로는, 지지 기재(1)에 방사선 경화형의 점착제층(2)을 형성한 후, 상기 부분(2a)에 부분적으로 방사선을 조사하여 경화시키는 방법을 들 수 있다. 부분적인 방사선 조사는, 상기 부분(2a) 이외에 대응하는 패턴을 형성한 포토마스크를 통해 행할 수 있다. 또한, 스폿적으로 자외선을 조사하여 경화시키는 방법 등을 들 수 있다. 방사선 경화형의 점착제층(2)의 형성은, 세퍼레이터 위에 설치한 것을 지지 기재(1) 위에 전사함으로써 행할 수 있다. 부분적인 방사선 경화는 세퍼레이터 위에 설치한 방사선 경화형의 점착제층(2)에 행할 수도 있다.
또한, 점착제층(2)을 방사선 경화형 점착제에 의해 형성하는 경우에는, 지지 기재(1)의 적어도 한쪽면의, 상기 부분(2a)에 대응하는 부분 이외의 부분의 전부 또는 일부가 차광된 것을 사용하고, 이것에 방사선 경화형의 점착제층(2)을 형성한 후에 방사선 조사하여 상기 부분(2a)을 경화시키고, 점착력을 저하시킨 상기 부분(2a)을 형성할 수 있다. 차광 재료로는 지지 필름 위에서 포토마스크가 될 수 있는 것을 인쇄나 증착 등으로 제조할 수 있다. 이러한 제조 방법에 의하면, 효율적으로 반도체 장치용 필름(10)이 제조 가능하다.
또한, 방사선 조사시에 산소에 의한 경화 저해가 일어나는 경우에는, 방사선 경화형의 점착제층(2)의 표면으로부터 어떠한 방법으로든 산소(공기)를 차단하는 것이 바람직하다. 예를 들어, 상기 점착제층(2)의 표면을 세퍼레이터로 피복하는 방법이나, 질소 가스 분위기 중에서 자외선 등의 방사선의 조사를 행하는 방법 등을 들 수 있다.
점착제층(2)의 두께는 특별히 한정되지 않지만, 칩 절단면의 절결 방지나 접착층의 고정 유지의 양립성 등의 점으로부터는 1 내지 50㎛ 정도인 것이 바람직하다. 보다 바람직하게는 2 내지 30㎛, 더욱 바람직하게는 5 내지 25㎛이다.
다이본드 필름(3)의 적층 구조는, 본 실시 형태와 같이 접착제층의 단층만으로 이루어지는 것이나, 코어 재료의 한쪽면 또는 양면에 접착제층을 형성한 다층 구조 등을 들 수 있다. 상기 코어 재료로는 필름(예를 들어 폴리이미드 필름, 폴리에스테르 필름, 폴리에틸렌테레프탈레이트 필름, 폴리에틸렌나프탈레이트 필름, 폴리카르보네이트 필름 등), 유리 섬유나 플라스틱제 부직 섬유로 강화된 수지 기판, 실리콘 기판 또는 유리 기판 등을 들 수 있다.
다이본드 필름(3)을 구성하는 접착제 조성물로는, 열가소성 수지와 열경화성 수지를 병용한 것을 들 수 있다.
상기 열경화성 수지로는 페놀 수지, 아미노 수지, 불포화 폴리에스테르 수지, 에폭시 수지, 폴리우레탄 수지, 실리콘 수지 또는 열경화성 폴리이미드 수지 등을 들 수 있다. 이들의 수지는 단독으로 또는 2종 이상을 병용해서 사용할 수 있다. 특히, 반도체 소자를 부식시키는 이온성 불순물 등의 함유가 적은 에폭시 수지가 바람직하다. 또한, 에폭시 수지의 경화제로는 페놀 수지가 바람직하다.
상기 에폭시 수지는 접착제 조성물로서 일반적으로 사용되는 것이면 특별히 한정은 없고, 예를 들어 비스페놀 A형, 비스페놀 F형, 비스페놀 S형, 브롬화 비스페놀 A형, 수소 첨가 비스페놀 A형, 비스페놀 AF형, 비페닐형, 나프탈렌형, 플루올렌형, 페놀노볼락형, 오르토크레졸노볼락형, 트리스히드록시페닐메탄형, 테트라페닐올에탄형 등의 2관능 에폭시 수지나 다관능 에폭시 수지, 또는 히단토인형, 트리스글리시딜이소시아누레이트형 혹은 글리시딜아민형 등의 에폭시 수지가 사용된다. 이들은 단독으로 또는 2종 이상을 병용해서 사용할 수 있다. 이들의 에폭시 수지 중 노볼락형 에폭시 수지, 비페닐형 에폭시 수지, 트리스히드록시페닐메탄형 수지 또는 테트라페닐올에탄형 에폭시 수지가 특히 바람직하다. 이들의 에폭시 수지는 경화제로서의 페놀 수지와의 반응성이 풍부하고, 내열성 등이 우수하기 때문이다.
상기 페놀 수지는, 상기 에폭시 수지의 경화제로서 작용하는 것이며, 예를 들어 페놀노볼락 수지, 페놀아랄킬 수지, 크레졸노볼락 수지, tert-부틸페놀노볼락 수지, 페놀비페닐 수지, 노닐페놀노볼락 수지 등의 노볼락형 페놀 수지, 레졸형 페놀 수지, 폴리파라옥시스티렌 등의 폴리옥시스티렌 등을 들 수 있다. 이들은 단독으로 또는 2종 이상을 병용해서 사용할 수 있다. 이들의 페놀 수지 중 페놀노볼락 수지, 페놀아랄킬 수지가 특히 바람직하다. 반도체 장치의 접속 신뢰성을 향상시킬 수 있기 때문이다.
상기 에폭시 수지와 페놀 수지와의 배합 비율은, 예를 들어 상기 에폭시 수지 성분 중 에폭시기 1당량당 페놀 수지 중 수산기가 0.5 내지 2.0당량이 되도록 배합하는 것이 적합하다. 보다 적합한 것은 0.8 내지 1.2당량이다. 즉, 양자의 배합 비율이 상기 범위를 벗어나면 충분한 경화 반응이 진행되지 않아, 에폭시 수지 경화물의 특성이 열화되기 쉬워지기 때문이다.
상기 열가소성 수지로는 천연 고무, 부틸 고무, 이소프렌 고무, 클로로프렌 고무, 에틸렌-아세트산비닐 공중합체, 에틸렌-아크릴산 공중합체, 에틸렌-아크릴산에스테르 공중합체, 폴리부타디엔 수지, 폴리카르보네이트 수지, 열가소성 폴리이미드 수지, 6-나일론이나 6,6-나일론 등의 폴리아미드 수지, 페녹시 수지, 아크릴 수지, PET나 PBT 등의 포화 폴리에스테르 수지, 폴리아미드이미드 수지 또는 불소 수지 등을 들 수 있다. 이들의 열가소성 수지는 단독으로 또는 2종 이상을 병용해서 사용할 수 있다. 이들의 열가소성 수지 중, 이온성 불순물이 적고 내열성이 높으며, 반도체 소자의 신뢰성을 확보할 수 있는 아크릴 수지가 특히 바람직하다.
상기 아크릴 수지로는 특별히 한정되는 것은 아니며, 탄소수 30 이하, 특히 탄소수 4 내지 18의 직쇄 혹은 분지의 알킬기를 갖는 아크릴산 또는 메타크릴산의 에스테르의 1종 또는 2종 이상을 성분으로 하는 중합체(아크릴 공중합체) 등을 들 수 있다. 상기 알킬기로는, 예를 들어 메틸기, 에틸기, 프로필기, 이소프로필기, n-부틸기, t-부틸기, 이소부틸기, 아밀기, 이소아밀기, 헥실기, 헵틸기, 시클로헥실기, 2-에틸헥실기, 옥틸기, 이소옥틸기, 노닐기, 이소노닐기, 데실기, 이소데실기, 운데실기, 라우릴기, 트리데실기, 테트라데실기, 스테아릴기, 옥타데실기 또는 도데실기 등을 들 수 있다.
또한, 상기 중합체를 형성하는 다른 단량체로는 특별히 한정되는 것은 아니며, 예를 들어 글리시딜아크릴레이트, 글리시딜메타크릴레이트 등과 같은 글리시딜기 함유 단량체, 아크릴산, 메타크릴산, 카르복시에틸아크릴레이트, 카르복시펜틸아크릴레이트, 이타콘산, 말레산, 푸마르산 혹은 크로톤산 등과 같은 카르복실기 함유 단량체, 무수 말레산 혹은 무수 이타콘산 등과 같은 산 무수물 단량체, (메트)아크릴산 2-히드록시에틸, (메트)아크릴산 2-히드록시프로필, (메트)아크릴산 4-히드록시부틸, (메트)아크릴산 6-히드록시헥실, (메트)아크릴산 8-히드록시옥틸, (메트)아크릴산 10-히드록시데실, (메트)아크릴산 12-히드록시라우릴 혹은 (4-히드록시메틸시클로헥실)-메틸아크릴레이트 등과 같은 히드록실기 함유 단량체, 스티렌술폰산, 알릴술폰산, 2-(메트)아크릴아미드-2-메틸프로판술폰산, (메트)아크릴아미드프로판술폰산, 술포프로필(메트)아크릴레이트 혹은 (메트)아크릴로일옥시나프탈렌술폰산 등과 같은 술폰산기 함유 단량체, 2-히드록시에틸아크릴로일포스페이트 등과 같은 인산기 함유 단량체, 스티렌 단량체 또는 아크릴로니트릴을 들 수 있다.
또한, 다이본드 필름(3)에는, 그의 용도에 따라 충전제를 적절히 배합할 수 있다. 충전제의 배합은 도전성의 부여나 열전도성의 향상, 탄성률의 조절 등을 가능하게 한다. 상기 충전제로는 무기 충전제 및 유기 충전제를 들 수 있지만, 취급성의 향상, 열전도성의 향상, 용융 점도의 조정, 틱소트로피성 부여 등의 특성의 관점에서 무기 충전제가 바람직하다. 상기 무기 충전제로는 특별히 제한은 없고, 예를 들어 수산화알루미늄, 수산화마그네슘, 탄산칼슘, 탄산마그네슘, 규산칼슘, 규산마그네슘, 산화칼슘, 산화마그네슘, 산화알루미늄, 질화알루미늄, 붕산알루미늄위스커, 질화붕소, 결정질 실리카, 비정질 실리카 등을 들 수 있다. 이들은 단독으로 또는 2종 이상을 병용해서 사용할 수 있다. 열전도성 향상의 관점에서는, 산화알루미늄, 질화알루미늄, 질화붕소, 결정질 실리카, 비정질 실리카가 바람직하다. 또한, 상기 각 특성의 밸런스가 양호하다는 관점에서는, 결정질 실리카 또는 비정질 실리카가 바람직하다. 또한, 도전성의 부여, 열전도성의 향상 등의 목적으로, 무기 충전제로서 도전성 물질(도전 충전제)을 사용하는 것으로 해도 된다. 도전 충전제로는 은, 알루미늄, 금, 구리, 니켈, 도전성 합금 등을 구 형상, 바늘 형상, 플레이크 형상으로 한 금속분, 알루미나 등의 금속 산화물, 아몰퍼스 카본 블랙, 그래파이트 등을 들 수 있다. 상기 충전제의 평균 입경은 0.1 내지 80㎛로 할 수 있다. 또한, 충전제의 평균 입경은, 예를 들어 광도식의 입도 분포계(호리바(HORIBA)제, 장치명; LA-910)에 의해 구한 값이다.
상기 충전제 배합량은, 열경화성 수지 성분 및 열가소성 수지 성분 및 충전제의 합계 100중량부에 대하여 5중량부 이상인 것이 바람직하고, 100중량부 이상 500 중량부 이하인 것이 보다 바람직하며, 200중량부 이상 400중량부 이하인 것이 더욱 바람직하다.
또한, 다이본드 필름(3)에는, 상기 충전제 이외에, 필요에 따라서 다른 첨가제를 적절하게 배합할 수 있다. 다른 첨가제로는, 예를 들어 난연제, 실란 커플링제 또는 이온 트랩제 등을 들 수 있다. 상기 난연제로는, 예를 들어 삼산화안티몬, 오산화안티몬, 브롬화에폭시 수지 등을 들 수 있다. 이들은 단독으로 또는 2종 이상을 병용해서 사용할 수 있다. 상기 실란 커플링제로는, 예를 들어 β-(3,4-에폭시시클로헥실)에틸트리메톡시실란, γ-글리시독시프로필트리메톡시실란, γ-글리시독시프로필메틸디에톡시실란 등을 들 수 있다. 이들 화합물은 단독으로 또는 2종 이상을 병용해서 사용할 수 있다. 상기 이온 트랩제로는, 예를 들어 히드로탈사이트류, 수산화비스무트 등을 들 수 있다. 이들은 단독으로 또는 2종 이상을 병용해서 사용할 수 있다.
다이본드 필름(3)의 두께(적층체의 경우에는, 총 두께)는 특별히 한정되지 않지만, 예를 들어 1 내지 200㎛의 범위로부터 선택할 수 있고, 바람직하게는 5 내지 100㎛, 보다 바람직하게는 10 내지 80㎛이다.
보호 필름(14)은, 실용에 제공할 때까지 다이본드 필름(3)을 보호하는 보호재로서의 기능 등을 갖고 있다. 또한, 보호 필름(14)은, 추가로 점착제층(2)에 다이본드 필름(3)을 전사할 때의 지지 기재로서 사용할 수 있다. 보호 필름(14)은 다이본드 필름(3) 위에 워크를 부착할 때에 박리된다. 보호 필름(14)의 재질로는, 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌, 폴리프로필렌이나, 불소계 박리제, 장쇄 알킬아크릴레이트계 박리제 등의 박리제에 의해 표면 코팅된 플라스틱 필름이나 종이 등을 들 수 있다.
본 실시 형태에 따른 보호 필름이 부착된 다이싱 필름(10)은, 예를 들어 다음과 같이 제작된다.
우선, 기재(1)는 종래 공지된 제막 방법에 의해 제막할 수 있다. 당해 제막 방법으로는, 예를 들어 캘린더 제막법, 유기 용매 중에서의 캐스팅법, 밀폐계에서의 인플레이션 압출법, T 다이 압출법, 공압출법, 드라이 라미네이트법 등을 예시할 수 있다. 기재(1)를 착색할 경우에는, 상기 색재를 첨가한다.
이어서, 기재(1) 위에 점착제 조성물 용액을 도포해서 도포막을 형성한 후, 상기 도포막을 소정 조건하에서 건조시켜(필요에 따라 가열 가교시켜) 점착제층(2)을 형성한다. 도포 방법으로는 특별히 한정되지 않으며, 예를 들어 롤 도포 시공, 스크린 도포 시공, 그라비아 도포 시공 등을 들 수 있다. 또한, 건조 조건으로는, 예를 들어 건조 온도 80 내지 150℃, 건조 시간 0.5 내지 5분간의 범위 내에서 행해진다. 또한, 세퍼레이터 위에 점착제 조성물을 도포해서 도포막을 형성한 후, 상기 건조 조건으로 도포막을 건조시켜서 점착제층(2)을 형성해도 좋다. 점착제층(2)을 착색할 경우에는, 상기 색재를 상기 점착제 조성물 용액에 첨가한다. 그 후, 기재(1) 위에 점착제층(2)을 세퍼레이터와 함께 접합한다. 이에 따라, 다이싱 필름(11)이 제작된다.
다이본드 필름(3)은, 예를 들어 다음과 같이 제작된다.
우선, 다이본드 필름(3)의 형성 재료인 접착제 조성물 용액을 제작한다. 당해 접착제 조성물 용액에는, 상술한 바와 같이 상기 접착제 조성물이나 충전제, 기타 각종 첨가제 등이 배합되어 있다.
이어서, 접착제 조성물 용액을 기재 세퍼레이터 위에 소정 두께가 되도록 도포해서 도포막을 형성한 후, 상기 도포막을 소정 조건하에서 건조시켜 접착제층을 형성한다. 도포 방법으로는 특별히 한정되지 않고, 예를 들어 롤 도포 시공, 스크린 도포 시공, 그라비아 도포 시공 등을 들 수 있다. 또한, 건조 조건으로는, 예를 들어 건조 온도 70 내지 160℃, 건조 시간 1 내지 5분간의 범위 내에서 행해진다. 또한, 세퍼레이터 위에 점착제 조성물 용액을 도포해서 도포막을 형성한 후, 상기 건조 조건으로 도포막을 건조시켜서 접착제층을 형성해도 좋다. 그 후, 기재 세퍼레이터 위에 접착제층을 세퍼레이터와 함께 접합한다.
계속해서, 다이싱 필름(11) 및 다이본드 필름(3)으로부터 각각 세퍼레이터를 박리하고, 다이본드 필름(3)과 점착제층(2)이 접합면이 되도록 해서 양자를 접합한다. 접합하면, 예를 들어 압착에 의해 행할 수 있다. 이때, 라미네이트 온도는 특별히 한정되지 않고, 예를 들어 30 내지 50℃가 바람직하고, 35 내지 45℃가 보다 바람직하다. 또한, 선압은 특별히 한정되지 않고 예를 들어 0.1 내지 20kgf/cm가 바람직하고, 1 내지 10kgf/cm가 보다 바람직하다. 이어서, 다이본드 필름(3) 위의 기재 세퍼레이터를 박리하고, 보호 필름(14)과 접합하여, 본 실시 형태에 따른 보호 필름이 부착된 다이싱 필름(10)이 얻어진다. 본 실시 형태에서는, 보호 필름(14)에 긴 것을 사용하고, 복수의 다이싱 필름(11)(다이본드 필름(3)이 접합된 다이싱 필름(11))을 소정의 간격을 두고 보호 필름(14)에 접합한다.
도 3은, 다른 실시 형태에 따른 보호 필름이 부착된 다이싱 필름을 도시하는 단면 모식도이다.
기재(1)에는, 도 3에 도시하는 보호 필름이 부착된 다이싱 필름(20)과 같이, 기재(1)과 점착제층(2) 사이에 인쇄층(15)이 형성되어 있어도 좋다. 인쇄층(15)이 형성되어 있으면, 보호 필름(14)만의 투과율과, 다이싱 필름(11)을 포함하는 보호 필름이 부착된 다이싱 필름(20)의 투과율과의 차를 보다 확실하게 20％ 이상으로 할 수 있다.
인쇄층(15)은, 예를 들어 볼록판식 인쇄법, 평판식 인쇄법, 요판 인쇄법, 공판 인쇄법 등의 인쇄법에 의해 형성할 수 있다. 이 경우, 인쇄층(15)에 사용하는 색재(착색제)로는 상기와 마찬가지의 것을 사용할 수 있다.
(반도체 장치의 제조 방법)
이하에서는, 도 4의 (a), 도 4의 (b) 및 도 5를 참조하면서 보호 필름이 부착된 다이싱 필름(10)을 사용한 경우를 예로 들어 설명한다. 도 4의 (a) 및 도 4의 (b)는, 본 실시 형태에 따른 반도체 장치의 제조 방법을 설명하기 위한 단면 모식도이다. 도 5는, 도 1 및 도 2에 도시한 보호 필름이 부착된 다이싱 필름에 있어서의 접착제층을 개재시켜 반도체 칩을 실장한 예를 도시하는 단면 모식도이다.
도 4의 (a)에 도시한 바와 같이, 보호 필름이 부착된 다이싱 필름(10)은, 일정 방향(도 4의 (a)에서는 좌측 방향)으로 풀어지게 되어, 보호 필름(14)의 폭 방향 중앙 부분에는 필름 검출용 광 L이 조사되어 있다. 도 4의 (a)에서는, 광 L은 보호 필름(14)만을 투과하고 있어, 투과한 광 L은 도시하지 않은 센서에 의해 검출되며, 투과율이 산출된다. 이때의 투과율은 투과율 T1이 된다.
그 후, 보호 필름이 부착된 다이싱 필름(10)이 더욱 풀어지게 되면, 도 4의 (b)에 도시한 바와 같이, 광 L은 보호 필름(14)과 다이싱 필름(11)과의 적층 부분을 투과하게 된다. 투과한 광 L은 도시하지 않은 센서에 의해 검출되며, 투과율이 산출된다. 이때의 투과율은 투과율 T2가 된다.
필름 검출용 광은 파장 600nm 내지 700nm이며, 파장 620nm 내지 680nm인 것이 바람직하고, 파장 640nm 내지 660nm인 것이 보다 바람직하다.
센서는 투과율이 20％ 이상 변화하였을 때, 즉 투과율이 투과율 T1로부터 투과율 T2로 변화하였을 때, 보호 필름(14) 위의 다이싱 필름(11)을 검출하였다고 판단한다. 그리고, 웨이퍼 마운트 장치는, 이 검출 결과를 기초로 다이싱 필름(11)의 위치를 인식하고, 다이싱 필름(11)을 보호 필름(14)으로부터 박리해서 반도체 웨이퍼(4)를 압착한다(부착 공정). 본 공정은 압착 롤 등의 가압 수단에 의해 가압하면서 행한다. 마운트시의 부착 온도는 특별히 한정되지 않으며, 예를 들어 20 내지 80℃의 범위 내인 것이 바람직하다. 본 실시 형태에서는, 투과율 T1과 투과율 T2와의 차가 20％ 이상이기 때문에, 센서는 보호 필름(14)만의 투과율 T1로부터 보호 필름(14)과 다이싱 필름(11)과의 적층 부분의 투과율 T2로 변화한 것을 확실하게 인식할 수 있다. 그 결과, 검출 불가능한 다이싱 필름이 이송되어버려 사용되지 않는 것 등을 방지할 수 있고, 그 사이의 다운 타임을 삭감할 수 있다. 또한, 다이싱 필름을 반도체 웨이퍼에 위치 어긋남을 일으키지 않고 부착하는 것이 가능해진다.
이어서, 반도체 웨이퍼(4)의 다이싱을 행한다. 이에 따라, 반도체 웨이퍼(4)를 소정의 크기로 절단해서 개편화하고, 반도체 칩(5)을 제조한다(도 5 참조). 다이싱은, 예를 들어 반도체 웨이퍼(4)의 회로면측으로부터 통상법에 따라 행해진다. 또한, 본 공정에서는, 예를 들어 다이본드 필름(3)까지 깊게 절단하는 풀컷팅이라 불리는 절단 방식 등을 채용할 수 있다. 본 공정에서 사용하는 다이싱 장치로는 특별히 한정되지 않고 종래 공지된 것을 사용할 수 있다. 또한, 반도체 웨이퍼(4)는, 다이본드 필름(3)이 부착된 다이싱 필름(11)에 의해 접착 고정되어 있으므로, 칩 절결이나 칩 비산을 억제할 수 있을 뿐 아니라, 반도체 웨이퍼(4)의 파손도 억제할 수 있다.
다이본드 필름(3)이 부착된 다이싱 필름(11)에 접착 고정된 반도체 칩(5)을 박리하기 위해서, 반도체 칩(5)의 픽업을 행한다. 픽업의 방법으로는 특별히 한정되지 않고 종래 공지된 다양한 방법을 채용할 수 있다. 예를 들어, 각각의 반도체 칩(5)을 다이싱 필름(11)측으로부터 니들에 의해 밀어올리고, 밀어올려진 반도체 칩(5)에 픽업 장치에 의해 픽업하는 방법 등을 들 수 있다.
여기서 픽업은 점착제층(2)이 자외선 경화형일 경우, 상기 점착제층(2)에 자외선을 조사한 후에 행한다. 이에 따라, 점착제층(2)의 다이본드 필름(3)에 대한 점착력이 저하되고, 반도체 칩(5)의 박리가 용이해진다. 그 결과, 반도체 칩(5)을 손상시키지 않고 픽업이 가능해진다. 자외선 조사시의 조사 강도, 조사 시간 등의 조건은 특별히 한정되지 않으며, 적절히 필요에 따라 설정하면 좋다. 또한, 자외선 조사에 사용하는 광원으로는 상술한 것을 사용할 수 있다.
픽업한 반도체 칩(5)은, 다이본드 필름(3)을 개재시켜 피착체(6)에 접착 고정한다(다이본드). 피착체(6)로는 리드 프레임, TAB 필름, 기판 또는 별도 제작한 반도체 칩 등을 들 수 있다. 피착체(6)는, 예를 들어 용이하게 변형되는 변형형 피착체여도 좋고, 변형시키는 것이 곤란한 비변형형 피착체(반도체 웨이퍼 등)여도 좋다.
상기 기판으로는 종래 공지된 것을 사용할 수 있다. 또한, 상기 리드 프레임으로는, Cu 리드 프레임, 42 얼로이 리드 프레임 등의 금속 리드 프레임이나 유리 에폭시, BT(비스말레이미드-트리아진), 폴리이미드 등을 포함하는 유기 기판을 사용할 수 있다. 그러나, 본 발명은 이것으로 한정되는 것이 아니며, 반도체 소자를 마운트하고, 반도체 소자와 전기적으로 접속해서 사용 가능한 회로 기판도 포함된다.
다이본드 필름(3)이 열경화형인 경우, 가열 경화에 의해 반도체 칩(5)을 피착체(6)에 접착 고정하고, 내열 강도를 향상시킨다. 가열 온도는 80 내지 200℃, 바람직하게는 100 내지 175℃, 보다 바람직하게는 100 내지 140℃에서 행할 수 있다. 또한, 가열 시간은 0.1 내지 24시간, 바람직하게는 0.1 내지 3시간, 보다 바람직하게는 0.2 내지 1시간으로 행할 수 있다. 또한, 다이본드 필름(3)을 개재시켜 반도체 칩(5)이 기판 등에 접착 고정된 것은 리플로우 공정에 제공할 수 있다.
열경화 후 다이본드 필름(3)의 전단 접착력은, 피착체(6)에 대하여 0.2MPa 이상인 것이 바람직하고, 보다 바람직하게는 0.2 내지 10MPa이다. 다이본드 필름(3)의 전단 접착력이 적어도 0.2MPa 이상이면, 와이어 본딩 공정시에 당해 공정에 있어서의 초음파 진동이나 가열에 의해, 다이본드 필름(3)과 반도체 칩(5) 또는 피착체(6)와의 접착면에서 전단 변형을 일으키는 경우가 적다. 즉, 와이어 본딩시의 초음파 진동에 의해 반도체 소자가 움직이는 경우가 적고, 이에 따라 와이어 본딩의 성공률이 저하되는 것을 방지한다.
또한, 본 실시 형태에 따른 반도체 장치의 제조 방법은 다이본드 필름(3)의 가열 처리에 의한 열경화 공정을 거치지 않고 와이어 본딩을 행하고, 추가로 반도체 칩(5)을 밀봉 수지로 밀봉하여, 당해 밀봉 수지를 후경화해도 좋다. 이 경우, 다이본드 필름(3)의 가고착시의 전단 접착력은, 피착체(6)에 대하여 0.2MPa 이상인 것이 바람직하고, 보다 바람직하게는 0.2 내지 10MPa이다. 다이본드 필름(3)의 가고착시에 있어서의 전단 접착력이 적어도 0.2MPa 이상이면, 가열 공정을 거치지 않고 와이어 본딩 공정을 행해도, 당해 공정에 있어서의 초음파 진동이나 가열에 의해 다이본드 필름(3)과 반도체 칩(5) 또는 피착체(6)와의 접착면에서 전단 변형을 일으키는 경우가 적다. 즉, 와이어 본딩시의 초음파 진동에 의해 반도체 소자가 움직이는 경우가 적고, 이에 따라 와이어 본딩의 성공률이 저하되는 것을 방지한다.
상기한 와이어 본딩은, 피착체(6)의 단자부(이너 리드)의 선단과 반도체 칩(5) 위의 전극 패드(도시하지 않음)를 본딩 와이어(7)로 전기적으로 접속하는 공정이다. 상기 본딩 와이어(7)로는, 예를 들어 금선, 알루미늄선 또는 구리선 등이 사용된다. 와이어 본딩을 행할 때의 온도는 80 내지 250℃, 바람직하게는 80 내지 220℃의 범위 내에서 행해진다. 또한, 그의 가열 시간은 몇초 내지 몇분간 행해진다. 결선은, 상기 온도 범위 내가 되도록 가열된 상태에서, 초음파에 의한 진동 에너지와 인가 가압에 의한 압착 에너지의 병용에 의해 행해진다. 본 공정은 다이본드 필름(3)의 열경화를 행하지 않고 실행해도 좋다.
상기 밀봉 공정은, 밀봉 수지(8)에 의해 반도체 칩(5)을 밀봉하는 공정이다. 본 공정은 접착체(6)에 탑재된 반도체 칩(5)이나 본딩 와이어(7)를 보호하기 위해서 행해진다. 본 공정은 밀봉용 수지를 금형으로 성형함으로써 행한다. 밀봉 수지(8)로는, 예를 들어 에폭시계의 수지를 사용한다. 수지 밀봉시의 가열 온도는, 통상 175℃에서 60 내지 90초간 행해지지만, 본 발명이 이것으로 한정되지 않고, 예를 들어 165 내지 185℃에서 몇분간 경화할 수 있다. 이에 따라, 밀봉 수지를 경화시킴과 함께, 다이본드 필름(3)을 개재시켜 반도체 칩(5)과 피착체(6)를 고착시킨다. 즉, 본 발명에 있어서는, 후술하는 후경화 공정이 행해지지 않는 경우에도, 본 공정에 있어서 다이본드 필름(3)에 의한 고착이 가능하고, 제조 공정수의 감소 및 반도체 장치의 제조 기간의 단축에 기여할 수 있다.
상기 후경화 공정에 있어서는, 상기 밀봉 공정에서 경화 부족의 밀봉 수지(8)를 완전히 경화시킨다. 밀봉 공정에 있어서 다이본드 필름(3)이 완전히 열경화되지 않은 경우에도, 본 공정에 있어서 밀봉 수지(8)와 함께 다이본드 필름(3)의 완전한 열경화가 가능해진다. 본 공정에 있어서의 가열 온도는, 밀봉 수지의 종류에 따라 상이하지만, 예를 들어 165 내지 185℃의 범위 내이며, 가열 시간은 0.5 내지 8시간 정도이다.
상술한 실시 형태에서는, 다이본드 필름의 직경이 다이싱 필름의 직경보다도 작은 경우에 대해서 설명하였지만, 본 발명에 있어서는 이 예로 한정되지 않고, 다이본드 필름의 직경은 다이싱 필름과 동일하거나 그것보다 커도 좋다. 이 경우, 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분은, 다이싱 필름과 다이본드 필름이 적층되어 있게 된다. 즉, 이 경우, 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분에 있어서의 보호 필름이 부착된 다이싱 필름의 투과율은, 보호 필름과 다이싱 필름과 다이본드 필름과의 적층체의 투과율에 상당한다. 이때, 다이본드 필름의 파장 600 내지 700nm에 있어서의 투과율은 50 내지 80％인 것이 바람직하다. 또한, 다이본드 필름과 다이싱 필름과의 투과율의 차는 10％ 이상인 것이 바람직하다. 또한, 다이본드 필름과 보호 필름과의 투과율의 차는 10％ 이상인 것이 바람직하다.
상술한 실시 형태에서는, 다이싱 필름(11)의 전체가 착색되어 있는, 다이싱 필름(11)의 전체에 인쇄층(15)이 설치되어 있거나, 또는 다이싱 필름(11)의 기재(1)의 전체면이 엠보싱 처리되어 있고, 이에 따라 투과율 T1과 투과율 T2와의 차가 20％ 이상이 되어 있는 경우에 대해서 설명하였다. 그러나, 본 발명이 이 예에 한정되지 않으며, 상기 투과율의 차는 보호 필름의 투과율과, 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분에 있어서의 보호 필름이 부착된 다이싱 필름의 투과율과의 차가 20％ 이상이면 좋고, 예를 들어 보호 필름의 투과율과의 투과율의 차가 20％ 이상인 부분은, 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분(예를 들어, 도 1의 부분(17))으로부터, 필름의 반송 방향을 따라 소정 거리(예를 들어, 100㎛ 내지 5000㎛)의 부분만이어도 좋다. 이러한 구성으로 하는 경우, 예를 들어 상기 투과율의 차를 20％ 이상으로 하는 부분을 착색하면 좋다.
[실시예]
이하에, 본 발명의 적합한 실시예를 예시적으로 상세하게 설명한다. 단, 이 실시예에 기재되어 있는 재료나 배합량 등은, 특별히 한정적인 기재가 없는 한, 본 발명의 요지를 이들만으로 한정하는 취지인 것은 아니다. 또한, 이하에 있어서, 부라고 되어 있는 것은 중량부를 의미한다.
(다이싱 필름의 점착제층의 제작)
아크릴산 부틸 70부, 아크릴산에틸 30부, 아크릴산 5부를 아세트산에틸 중에서 통상법에 의해 공중합시키고, 중량 평균 분자량 80만의 아크릴계 중합체를 얻었다. 이어서, 이 아크릴계 중합체 100부에 가교제로서 다관능 에폭시 화합물(미쯔비시 가스 가가꾸(주)사제, 제품명 "TETRAD-C") 8부와, 광중합 개시제로서 1-히드록시시클로헥실페닐케톤 7부를 배합하고, 이들을 유기 용제로서의 톨루엔에 균일하게 용해시켜서, 농도 30중량％의 아크릴계 점착제 조성물 용액을 얻었다. 이 아크릴계 점착제 조성물 용액을 하기 표 1, 표 2에 나타내는 각 실시예, 각 비교예의 기재면 위에 두께가 10㎛가 되도록 도포하고, 120℃에서 3분간 건조를 행하였다. 그 후, 마스크를 개재시켜 반도체 웨이퍼가 부착되는 부분에만 자외선을 500mJ/cm2 조사하여, 반도체 웨이퍼가 부착되는 부분이 자외선 경화된 다이싱 필름을 얻었다. 또한, 실시예 1에 따른 기재(PP(폴리프로필렌))는 후따무라 가가꾸 가부시끼가이샤제, 제품명 "FVHK-LB#40 N100"이다. 실시예 2에 따른 기재(PP(폴리프로필렌))는 후따무라 가가꾸 가부시끼가이샤제, 제품명 "FBS-LB#40 S-400X"이다. 실시예 3에 따른 기재(PO(폴리올레핀))는 미쯔이 가가꾸 가부시끼가이샤제, 제품명 "TPX"이다. 실시예 4에 따른 기재(PVC(폴리염화비닐))는 닛토덴코 가부시키가이샤제, 제품명 "SPV-M4001"이다. 실시예 5에 따른 기재(PVC(폴리염화비닐))는 닛토덴코 가부시키가이샤제, 제품명 "SPV-320"이다. 비교예 1에 따른 기재(PET(폴리에틸렌테레프탈레이트)는 미쯔비시 주시 가부시끼가이샤제, 제품명 "MRA-38"이다. 비교예 2에 따른 기재(PET(폴리에틸렌테레프탈레이트))는 미쯔비시 주시 가부시끼가이샤제, 제품명 "MRF-150"이다.
(다이본드 필름의 제작)
하기 (a) 내지 (d)를 메틸에틸케톤에 용해시켜, 농도 23.6중량％의 접착제 조성물 용액을 얻었다.
(a) 에폭시 수지(JER(주)제, 에피코트 1001) 32중량부
(b) 페놀 수지(미쯔이 가가꾸(주)제, 미렉스 XLC-4L) 34중량부
(c) 아크릴산에틸-메틸메타크릴레이트를 주성분으로 하는 아크릴산에스테르계 중합체(나가세 켐텍스(주)제, SG-708-6) 100중량부
(d) 구 형상 실리카(애드마텍스(주)제, SO-25R) 110중량부
이 접착제 조성물 용액을 실리콘 이형 처리한 두께가 100㎛인 폴리에틸렌테레프탈레이트 필름으로 이루어지는 이형 처리 필름(박리 라이너) 위에 도포한 후, 120℃에서 3분간 건조시켰다. 이에 따라, 두께 10㎛의 다이본드 필름을 제작하였다.
(보호 필름이 부착된 다이싱 필름의 제작)
제작한 각 실시예, 각 비교예의 다이싱 필름을 각각 직경 370 mm가 되도록 원형으로 펀칭하였다. 이어서, 제작한 다이본드 필름을 직경 320 mm가 되도록 원형으로 펀칭하고, 각 다이싱 필름에 전사하였다. 전사는 다이싱 필름의 점착제층과 다이본드 필름이 대향하도록 행하였다. 그 후, 실리콘 이형 처리한 두께 35㎛의 폴리에틸렌테레프탈레이트 필름의 보호 필름을 다이본드 필름측에 접합하고, 본 실시예, 본 비교예의 보호 필름이 부착된 다이싱 필름을 얻었다.
(투과율의 측정)
투과율의 측정에는, 닛본 분꼬우사제의 분광 광도계(제품명 "V-670")를 사용하여, 측정 모드를 ％T(투과율 측정), 측정 파장 영역을 190 내지 800nm로서 행하였다. 그 때의 파장 650nm에서의 투과율을 측정값으로 하였다. 그 결과, 보호 필름의 파장 650nm에서의 투과율은 88.8％였다. 또한, 다이싱 필름의 파장 650nm에서의 투과율(％), 보호 필름과 다이싱 필름의 적층 부분의 투과율(％)은 표 1, 표 2에 나타내는 바와 같았다. 또한, 표 1, 표 2에는, 보호 필름과 다이싱 필름의 적층 부분의 투과율과, 보호 필름의 투과율과의 차도 나타내고 있다.
(센서 인식성)
보호 필름 위의 다이싱 필름을 검출하는 센서와, 검출된 다이싱 필름을 보호 필름으로부터 박리해서 반도체 웨이퍼를 부착하는 웨이퍼 마운트 장치를 사용하여 센서 인식성 시험을 행하였다. 센서가 다이싱 필름을 인식하여, 웨이퍼 마운트를 행할 수 있는 것을 ○, 다이싱 필름을 인식하지 않고 웨이퍼 마운트를 행할 수 없는 것을 ×로 하였다. 결과를 표 1, 표 2에 나타낸다.
<센서의 조건>
센서: 기엔스사제, LV-11SB
센서 헤드: 직선 광 회귀 반사형(형식: LV-S62)
검출 거리 50mm
<접합 조건>
웨이퍼 마운트 장치: 닛토 세이미쯔 기까이사제: MA-3000III
접합 속도: 10mm/초
풀어내기 속도: 10mm/초
(헤이즈값)
실시예 3의 기재에 대해서 헤이즈값을 측정하였다. 헤이즈값의 측정은, 구체적으로는 헤이즈 미터("NDH2000", 닛본 덴쇼꾸 고교(주)제)로 행하였다.
헤이즈(％)=Td/Tt×100
Td: 확산 투과율
Tt: 전체 광선 투과율
결과를 표 1에 나타낸다.
Figure 112012019205846-pat00001
Figure 112012019205846-pat00002
(결과)
표 1, 표 2의 결과로부터 알 수 있는 바와 같이, 보호 필름과 다이싱 필름의 적층 부분의 투과율과, 보호 필름의 투과율과의 차가 20％ 이상이면 센서에 의해 다이싱 필름을 인식할 수 있었다.
1 기재
2 점착제층
3 다이본드 필름
4 반도체 웨이퍼
5 반도체 칩
6 피착체
7 본딩 와이어
8 밀봉 수지
10, 20 보호 필름이 부착된 다이싱 필름
11 다이싱 필름
14 보호 필름
15 인쇄층

Claims (7)

  1. 다이싱 필름과 보호 필름이 적층된 보호 필름이 부착된 다이싱 필름이며,
    파장 600 내지 700nm에 있어서의 상기 보호 필름의 투과율과, 상기 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분에 있어서의 상기 보호 필름이 부착된 다이싱 필름의 투과율과의 차가 20％ 이상인 것을 특징으로 하는, 보호 필름이 부착된 다이싱 필름.
  2. 제1항에 있어서, 상기 다이싱 필름은 기재와 상기 기재 위에 적층된 점착제층을 갖고 있으며, 상기 기재에는 엠보싱 처리가 실시되어 있는 것을 특징으로 하는, 보호 필름이 부착된 다이싱 필름.
  3. 제1항에 있어서, 상기 다이싱 필름은 기재와 상기 기재 위에 적층된 점착제층을 갖고 있으며, 상기 기재가 착색되어 있는 것을 특징으로 하는, 보호 필름이 부착된 다이싱 필름.
  4. 제1항에 있어서, 상기 다이싱 필름의 필름 검출용 광이 최초로 투과하는 부분에 있어서의 상기 보호 필름이 부착된 다이싱 필름의 투과율은 0 내지 70％인 것을 특징으로 하는, 보호 필름이 부착된 다이싱 필름.
  5. 제1항에 있어서, 상기 보호 필름의 투과율은 75 내지 100％인 것을 특징으로 하는, 보호 필름이 부착된 다이싱 필름.
  6. 제2항 또는 제3항에 있어서, 상기 다이싱 필름의 상기 점착제층 위에 다이본드 필름이 적층되어 있는 것을 특징으로 하는, 보호 필름이 부착된 다이싱 필름.
  7. 제1항, 제4항 및 제5항 중 어느 한 항에 있어서,
    상기 다이싱 필름은 기재와 상기 기재 위에 적층된 점착제층을 갖고 있으며,
    상기 다이싱 필름의 상기 점착제층 위에 다이본드 필름이 적층되어 있는 것을 특징으로 하는, 보호 필름이 부착된 다이싱 필름.

KR1020120024293A 2011-03-11 2012-03-09 보호 필름이 부착된 다이싱 필름 KR101168562B1 (ko)