KR100410723B1 - 등속조인트용그리스조성물 - Google Patents

등속조인트용그리스조성물 Download PDF

Info

Publication number
KR100410723B1
KR100410723B1 KR1019960013506A KR19960013506A KR100410723B1 KR 100410723 B1 KR100410723 B1 KR 100410723B1 KR 1019960013506 A KR1019960013506 A KR 1019960013506A KR 19960013506 A KR19960013506 A KR 19960013506A KR 100410723 B1 KR100410723 B1 KR 100410723B1
Authority
KR
South Korea
Prior art keywords
metal salts
overbased
salt
salts
weight
Prior art date
Application number
KR1019960013506A
Other languages
English (en)
Other versions
KR970027278A (ko
Inventor
오니와 타까시
오사와 히사유끼
Original Assignee
교도유시 가부시끼가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP31053195A external-priority patent/JP3320598B2/ja
Application filed by 교도유시 가부시끼가이샤 filed Critical 교도유시 가부시끼가이샤
Publication of KR970027278A publication Critical patent/KR970027278A/ko
Application granted granted Critical
Publication of KR100410723B1 publication Critical patent/KR100410723B1/ko

Abstract

본 발명은 (a)기본오일; (b)우레아계 증감제; (c)몰리브데늄 디설파이드; 그리고 (d)산화왁스, 석유설폰산, 알킬아릴설폰산, 살리실산 및 페네이트의 금속염 또는 과염기금속염중에서 선택된 금속염 또는 과염기금속염을 필수성분으로 함유하는 등속조인트용 그리스 조성물에 관한 것이다. 또한 본 발명은 상기 (a) ∼ (d)를 필수성분으로 하고, 여기에 (e)금속을 함유하지 않은 황-인계 극압제 및 몰리브데늄 디티오포스페이트 중에서 선택된 극압제, 또는 (f)몰리브데늄 디티오카바메이트가 함유되어 있는 등속조인트용 그리스 조성물을 포함한다. 본 발명의 등속조인트용 그리스 조성물은 현저한 내마모 효과 및 현저한 피팅 억제효과를 갖고 있다.

Description

등속조인트용 그리스 조성물
본 발명은 등속조인트용 그리스 조성물에 관한 것으로서, 더욱 상세하게는 볼 타입(ball type)에 고정된 플런지 등속조인트에 유용한 그리스 조성물에 관한 것이다. 등속 조인트를 윤활시키기 위해서는 매우 높은 표면압을 가해야 하고, 조인트의 복잡한 롤링운동 및 슬라이딩 운동이 일어나며, 이로써 비이상적인 마모 및 금속 피로(fatigue)를 야기하고 그 결과 조인트 부분의 피팅(pitting)현상 등과 같은 스폴링 현상이 일어난다. 따라서 본 발명을 더욱 상세히 설명하면, 본 발명은 조인트 부분의 피팅(pitting)을 효율적으로 감소시키고 조인트의 마찰을 효율적으로 감소시켜 등속조인트를 효율적으로 윤활시킬 수 있는 그리스 조성물에 관한 것이다.
종래에는 등속조인트용 윤활그리스로서 몰리브데늄 디설파이드를 함유하고 있는 리튬 비누 현탁된 극압그리스, 그리고 몰리브데늄 디설파이드와 극압제 예를들면 황-인 또는 납 나프탈렌산염을 함유하고 있는 리튬비누 현탁된 극압그리스를 사용하였다. 그러나 상기의 등속 조인트용 그리스가 고성능 모터카에서와 같이 가혹 조건하에서 항상 만족스러운 것은 아니다.
연결 조인트로서 사용되는 비르필드 조인트는 물론이고 플런지 조인트로서 사용되는 이중 옵셋형 등속조인트와 크로스 그루브형 등속조인트는 토크(torques)가 6개의 볼(ball)을 통해 전해지는 구조를 갖는다. 이들 조인트들은 높은 접촉압력하에서 회전하는 동안에 복잡한 왕복운동 예를들면 복잡한 롤링운동과 슬라이딩운동을 하고, 응력(stresses)은 볼(ball) 그리고 볼과 접하고 있는 금속표면에 되풀이해서 작용하게 되며, 이로써 금속 피로(fatigue)에 의한 피팅현상이 발생한다. 최근 엔진의 힘을 개선시키기 위해 통상의 엔진에 비교하여 접촉압력을 증가시키는 연구가 진행되었다. 연료소비와 관련한 자동차 경량화 목적에 적합하도록 조인트의 크기를 줄이고 있고, 이로써 접촉압력을 감소시키는 효과를 얻고 있다. 그러나 통상의 그리스는 피틱현상을 효과적으로 감소시킬 수 없다. 따라서 통상의 그리스의 열저항은 개선되어야만 한다.
따라서 본 발명은 피팅현상 억제효과 및 열저항이 우수한 등속조인트용 신규 그리스 조성물을 제공하는데 그 목적이 있다.
본 발명자들은 비이상적인 마모 및 금속피로에 의한 피팅현상의 문제를 해결하고 열 저항을 개선하며 등속조인트의 마찰마모가 양호한 그리스 조성물을 개발하고자 연구노력하였다. 본 발명자들은 높은 접촉압력하에서 복잡한 왕복운동 즉, 복잡한 롤링운동과 슬라이딩운동을 수반하는 윤활조건에서 사용되는 그리스의 품질을 향상시키기 위해 노력하였고, 또한 다양한 종류의 극압제, 고체 윤활제 또는 첨가제의 첨가에 따른 윤활조건(예를들면, 마찰계수 및 마모)을 측정하기 위하여 진동마찰/마모 측정기로 잘 알려져 있는 SRV(Schwingung Reibung und Verschleiss)를사용하여 그리스의 특성을 평가하였다. 그 결과 본 발명자들은 기본오일; 우레아계 증감제; 몰리브데늄 디설파이드; 특정 화합물의 금속염 또는 과염기금속염이 특정 조성으로 이루어진 그리스, 또는 상기 특정 조성으로 이루어진 그리스에 극압제로서 금속이 함유되지 않은 황-인계 극압제 및 몰리브데늄 디티오포스페이트 중에서 선택된 극압제를 함유시킨 그리스, 또는 상기 특정 조성으로 이루어진 그리스에 윤활시 요구되는 양호한 마찰계수와 낮은 마모를 만족시킬 수 있는 몰리브데늄 디티오카바메이트 억제제가 함유된 그리스를 알게 되었고, 또한 이들 그리스의 내구성을 측정한 결과 통상의 등속 조인트용 그리스와는 다르게 어떠한 피팅현상의 발생을 방지할 수 있음을 알게됨으로써 본 발명을 완성하였다.
이하 본 발명을 상세히 설명하면 다음과 같다.
본 발명은 a)기본오일; b)우레아계 증감제;c)몰리브데늄 디설파이드; 그리고 d)산화왁스 금속염, 석유설폰산 금속염, 알킬아릴설폰산 금속염, 살리실산 금속염, 페네이트(phenates) 금속염, 산화왁스 과염기금속염, 석유설폰산 과염기금속염, 알킬아릴설폰산 과염기금속염, 살리실산 과염기금속염 및 페네이트(phenates) 과염기금속염 중에서 선택된 금속염 또는 과염기금속염으로 이루어진 등속조인트용 그리스 조성물에 관한 것이다.
또한, 본 발명은 상기 a) ∼ d)로 이루어진 그리스 조성물과 e)금속이 함유되지 않은 황-인계 극압제와 몰리브데늄 디티오포스페이트 중에서 선택된 극압제로 이루어진 등속조인트용 그리스 조성물에 관한 것이다.
또한, 본 발명은 상기 a) ∼ d)로 이루어진 그리스 조성물과 f)몰리브데늄디티오카바메이트로 이루어진 등속조인트용 그리스 조성물에 관한 것이다.
또한, 본 발명은 상기의 a) ∼ d)로 이루어진 그리스 조성물과 e)금속이 함유되지 않은 황-인계 극압제와 몰리브데늄 디티오포스페이트 중에서 선택된 극압제 그리고 f)몰리브데늄 디티오카바메이트가 첨가된 것으로서, 이때 d)성분의 금속염 또는 과염기금속염은 마그네슘염, 바륨염, 나트륨염, 칼륨염, 납염, 아연염 및 알루미늄염 중에서 선택된 금속염인 등속조인트용 그리스 조성물에 관한 것이다.
이와같은 본 발명을 더욱 상세히 설명하면 다음과 같다.
본 발명의 등속조인트용 그리스 조성물은 (a)성분으로 기본오일을 사용하는 바, 그 종류로는 광물유, 에스테르계 합성유, 에테르계 합성유, 탄화수소계 합성유 또는 이들의 혼합물을 사용함이 바람직하며, 본 발명이 이에 한정되는 것은 아니다.
본 발명의 등속조인트용 그리스 조성물은 (b)성분으로서 우레아계 증감제를 사용하는 바, 그 종류로는 디우레아 화합물 및 폴리우레아 화합물 중에서 선택된 것을 사용함이 바람직하며, 본 발명이 이에 한정되는 것은 아니다. 디우레아 화합물은 모노아민과 디이소시아네이트 화합물과의 반응에 의해 얻을 수 있다. 디이소시아네이트 화합물을 구체적으로 예시하면 페닐렌 디이소시아네이트, 디페닐 디이소시아네이트, 페닐 디이소시아네이트, 디페닐메탄 디이소시아네이트, 옥타데칸 디이소시아네이트, 데칸 디이소시아네이트 및 헥산 디이소시아네이트 중에서 선택된다. 모노아민 화합물을 구체적으로 예시하면 옥틸아민, 도데실아민, 헥사데실아민, 옥타데실아민, 올레일아민, 아닐린, p-톨루이딘 및 시클로헥실아민 중에서 선택된다. 폴리우레아 화합물은 디아민과 디이소시아네이트 화합물의 반응에 의해 얻을 수 있다. 디이소시아네이트 화합물은 상기 디우레아 화합물 제조시 사용된 것과 동일하다. 디아민 화합물을 구체적으로 예시하면 에틸렌디아민, 프로판디아민, 부탄디아민, 헥산디아민, 옥탄디아민, 페닐렌디아민, 토일렌디아민 및 자일렌디아민 중에서 선택된다. 바람직한 우레아계 증감제는 아닐린 또는 p-톨루이딘과 같은 아릴아민, 사이클로헥실아민, 또는 이들의 혼합물과 디이소시아네이트 화합물을 반응시켜 얻을 수 있다. 디우레아 화합물에 있어서 아릴기는 바람직하기로는 탄소원자수가 6 또는 7이고, 디우레아 화합물중의 아릴기와 사이클로헥실기의 총몰수에 대하여 디우레아 화합물중의 아릴기의 비율이 100 ∼ 0 몰%인 경우이다.
본 발명의 등속조인트용 그리스 조성물은 (c)성분으로서 몰리브데늄 디설파이드를 사용하는 바, 이는 극압제로서 광범위하게 사용되고 있다. 윤활 작용을 고려해볼 때, 몰리브데늄 디설파이드는 층격자 구조를 갖고 있어서 얇은 판 형성과정 동안에 내내 슬라이딩 운동을 하는 경우 쉽게 전단되며, 또한 마찰력을 감소시키고 조인트의 경련을 방지하는 효과를 갖는다. 다양한 입자크기를 갖는 몰리브데늄 디설파이드가 제품으로 시판되고 있으나, 피셔법(Fisher method; Fisher Sub-Sieve sizer 이용)으로서 알려져 있는 입자경 측정방법에 의해 측정한 평균 입자경이 0.25 ∼ 10 ㎛ 범위인 것이 바람직하고, 특히 바람직하기로는 평균 입자경이 0.55 ∼ 0.85 ㎛ 범위이다.
본 발명의 등속조인트용 그리스 조성물은 (d)성분으로서 금속염 또는 과염기금속염을 사용하는 바, 이는 엔진 오일과 같은 윤활제 제조시 사용되는 금속세척분산제 또는 녹방지제 예를들면 산화왁스 금속염; 윤활유 일부분으로 존재하는 방향족 탄화수소의 설폰화에 의해 제조한 석유설폰산 금속염; 디노닐나프탈렌설폰산 및 알킬벤젠설폰산과 같은 합성 설폰산 금속염; 살리실산 금속염; 페네이트(phenate) 금속염; 산화왁스 과염기금속염; 석유 설폰산 과염기금속염; 알킬아릴설폰산 과염기금속염; 살리실산 과염기금속염; 그리고 페네이트 과염기금속염 중에서 선택된 것이다. d)성분으로 사용되는 금속염 또는 과염기금속염에 있어서, 바람직하기로는 칼슘염, 마그네슘염, 바륨염, 나트륨염, 칼륨염, 납염, 아연염 및 알루미늄염 중에서 선택된 것이고, 특히 바람직하기로는 칼슘 및 나트륨 중에서 선택된 것이다.
본 발명의 등속조인트용 그리스 조성물은 (e)성분으로서 금속이 함유되지 않은 황-인계 극압제를 사용하는 바, 바람직하기로는 황 성분 15 ∼ 35 중량% 그리고 인 성분 0.5 ∼ 3 중량% 범위내에서 함유되는 경우 황과 인 성분이 적절히 균형을 이루어 마모 억제 및 조인트 경련 방지에 우수한 효과를 나타낸다. 다시말하면, 황 성분이 상기 함량 범위를 초과하면 조인트가 쉽게 부식되는 문제가 있고, 인 성분의 함량이 상기 범위를 초과하면 어떠한 마모 방지효과를 얻을 수 없다. 그리고 황과 인 성분 모두 상기 범위 미만 함유되면 본 발명에서 얻고자 하는 효과를 얻을 수 없다. 극압제 (e)성분으로서 몰리브데늄 디티오포스페이트가 사용될 수 있으며, 바람직하기로는 다음 구조식(1)로 표시되는 몰리브데늄 디티오포스페이트를 사용하는 것이다.
상기식에서, R1, R2, R3및 R4는 각각 서로 같거나 다른 것으로서, 탄소원자수 1 ∼ 24 바람직하기로는 탄소원자수 3 ∼ 20 의 일차 또는 이차 알킬기, 또는 탄소원자수 6 ∼ 30 바람직하기로는 탄소원자수 8 ∼ 18 의 아릴기이다.
본 발명의 등속조인트용 그리스 조성물은 (f)성분으로서 몰리브데늄 디티오카바메이트를 사용하는 바, 바람직하기로는 다음 구조식(2)로 표시되는 몰리브데늄 디티오카바메이트를 사용하는 것이다.
상기식에서, R5및 R6은 각각 서로 같거나 다른 것으로서, 탄소원자수 1 ∼ 24 바람직하기로는 탄소원자수 3 ∼ 18의 알킬기이고; m 은 0 ∼ 3 이고 n 은 4 ∼ 1이며, 단 m+n=4이다.
또한 본 발명의 그리스 조성물은 필요에 따라 산화방지제, 녹방지제 및 부식방지제 중에서 선택된 하나 또는 그 이상의 것을 상기의 필수성분에 첨가하여 사용할 수도 있다.
본 발명에서 첫번째로 구체화한 등속조인트용 그리스 조성물은 그리스 조성물 총량에 대하여 필수적으로 기본오일(a) 55.0 ∼ 98.0 중량%; 우레아계 증감제(b) 1 ∼ 25 중량%; 몰리브데늄 디설파이드(c) 0.5 ∼ 5.0 중량%; 그리고 금속염 또는 과염기금속염 0.5 ∼ 15 중량%가 함유된다.
본 발명에서 두번째로 구체화한 등속조인트용 그리스 조성물은 그리스 조성물 총량에 대하여 필수적으로 기본오일(a) 52.0 ∼ 97.9 중량%; 우레아계 증감제(b) 1 ∼ 25 중량%; 몰리브데늄 디설파이드(c) 0.5 ∼ 5.0 중량%; 금속염 또는 과염기금속염(d) 0.5 ∼ 15 중량%; 그리고 금속이 함유되지 않은 황-인계 극압제 및 몰리브데늄 디티오포스페이트 중에서 선택된 극압제(e) 0.1 ∼ 3 중량%가 함유된다.
본 발명에서 세번째로 구체화한 등속조인트용 그리스 조성물은 그리스 조성물 총량에 대하여 필수적으로 기본오일(a) 50.0 ∼ 97.9 중량%; 우레아계 증감제(b) 1 ∼ 25 중량%; 몰리브데늄 디설파이드(c) 0.5 ∼ 5.0 중량%; 금속염 또는 과염기금속염(d) 0.5 ∼ 15 중량%; 그리고 몰리브데늄 디티오카바메이트(f) 0.1 ∼ 5.0 중량%가 함유된다.
본 발명에서 네번째로 구체화한 등속조인트용 그리스 조성물은 그리스 조성물 총량에 대하여 필수적으로 기본오일(a) 63.0 ∼ 91.5 중량%; 우레아계 증감제(b) 5 ∼ 20 중량%; 몰리브데늄 디설파이드(c) 2 ∼ 4 중량%; 금속염 또는 과염기금속염(d) 1 ∼ 10 중량%; 그리고 몰리브데늄 디티오카바메이트(f) 0.5 ∼ 3.0 중량%가 함유된다.
본 발명에서 다섯번째로 구체화한 등속조인트용 그리스 조성물은 그리스 조성물 총량에 대하여 필수적으로 기본오일(a) 60.0 ∼ 91.4 중량%; 우레아계 증감제(b) 5 ∼ 20 중량%; 몰리브데늄 디설파이드(c) 2 ∼ 4 중량%; 금속염 또는과염기금속염(d) 1 ∼ 10 중량% 이때 금속염 또는 과염기금속염은 마그네슘염, 바륨염, 나트륨염, 칼륨염, 납염, 아연염, 및 알루미늄염 중에서 선택된 것이며; 금속이 함유되지 않은 황-인계 극압제 및 몰리브데늄 디티오포스페이트 중에서 선택된 극압제(e) 0.1 ∼ 3 중량%; 그리고 몰리브데늄 디티오카바메이트(f) 0.5 ∼ 3.0 중량%가 함유된다.
상기 그리스 조성물에 있어서, 우레아계 증감제(b)의 함량이 1 중량% 미만이면 증감제로서 작용할 수 없어 본 발명에서 목적으로 하는 그리스 조성물을 얻을 수 없으며, 25 중량%를 초과하면 너무 딱딱하여 그리스 조성물에 요구되는 효과를 얻을 수 없다. 몰리브데늄 디설파이드(c)의 함량 0.5 중량% 미만, 금속염 또는 과염기금속염(d)의 함량 0.5 중량% 미만, 극압제(e)의 함량 0.1 중량% 미만, 또는 몰리브데늄 디티오카바메이트(f)의 함량 0.1 중량% 미만이면 본 발명의 그리스 조성물에 요구되는 효과를 얻을 수 없다. 또한 몰리브데늄 디설파이드(c)의 함량 5 중량% 초과, 금속염 또는 과염기금속염(d)의 함량 15 중량% 초과, 극압제(e)의 함량 3 중량% 초과, 또는 몰리브데늄 디티오카바메이트(f)의 함량 5 중량%를 초과하면 더 이상의 개선된 효과를 얻을 수 없고, 오히려 피팅억제 효과는 저하된다.
이와같은 본 발명을 다음의 실시예와 비교예에 의거하여 더욱 상세히 설명하면 다음과 같은 바, 본 발명이 이에 한정되는 것은 아니다.
실시예 1 ∼ 11 및 비교예 1 ∼ 2
반응용기에 기본오일(4,100g)과 디페닐메탄-4,4' -디이소시아네이트(1,012g)을 투입하고, 이를 70 ∼ 80℃까지 가열하였다. 또다른 반응용기에 기본오일(4,100g), 사이클로헥실아민(563 g) 및 아닐린(225 g)을 투입하고, 이를 70 ∼ 80℃까지 가열한 다음, 이를 상기 반응용기에 투입하였다. 반응 혼합물은 30분동안 충분히 교반한 다음, 160℃까지 가열하고 다시 냉각하여 기본 우레아 그리스(a base urea grease)를 제조하였다. 그리고 나서 상기 기본 우레아 그리스에 다음 표1에 제시된 성분들 그리고 임의로 적당량의 기본 오일를 첨가하고, 쓰리-하이 롤 밀(three-high roll mill)에서 혼합하여 No. 1등급의 그리스 조성물을 제조하였다.
실시예 12 ∼ 13
반응용기에 기본오일(440 g)과 디페닐메탄-4,4' -디이소시아네이트(58.9 g)을 투입하고, 이를 70 ∼ 80℃까지 가열하였다. 또다른 반응용기에 기본오일(440 g)와 옥틸아민(61.1 g)을 투입하고, 이를 70 ∼ 80℃까지 가열한 다음, 이를 상기 반응용기에 투입하였다. 반응 혼합물은 30분동안 충분히 교반한 다음, 160℃까지 가열하고 다시 냉각하여 기본 지방족 아민 우레아 그리스(a base aliphatic amine urea grease)를 제조하였다. 그리고나서 상기 기본 지방족 아민 우레아 그리스에 다음 표1에 제시된 성분들 그리고 임의로 적당량의 기본오일를 첨가하고, 쓰리-하이 롤 밀(three-high roll mill)에서 혼합하여 No. 1등급의 그리스 조성물을 제조하였다.
상기 실시예와 비교예의 그리스 조성물 제조시 사용된 기본오일은 다음과 같은 특성을 갖는다.
점도(Viscosity) : 130 ㎟/s (40℃에서)
14 ㎟/s (100℃에서)
점도지수(Viscisity Index) : 106
또한, 비교예 3에서는 몰리브데늄 디설파이드, 황-인계 극압제 및 납 나프탈레이트를 함유하는 시판 리튬 그리스를 사용하였다.
다음의 측정방법에 의해 물리적 성질을 측정하였고, 그 결과는 다음 표1에 나타내었다.
[투시도(Penetration)] ISO 2137에 제시된 방법에 의함
[적하점(Dropping point)] ISO 2176에 제시된 방법에 의함
[SRV 시험]
시험편 : 볼(ball) 직경 10 mm (SUJ-2)
원통형판 직경 24 mm ×7.85 mm (SUJ-2)
측정조건 :
·하중 : 300 N
·주파수 : 15 Hz
·진폭 : 1,000 ㎛
·시간 : 10 분
·측정온도 : 150 ℃
측정항목 :
·최대마찰계수
·볼에서 관측한 마모자국의 평균반경(mm)
·플레이트에서 관측한 최대마모깊이(㎛)
[실제 조인트를 사용하여 작업대에서 내구성 측정시험]
다음과 같은 조건으로 실제 조인트를 사용하여 작업대에서 내구성을 측정함으로써 피팅 발생을 점검하였다.
측정조건 :
·회전수 : 200 rpm
·토크(torque) : 785 N ·m
·조인트 각도 : 7°
·측정시간 : 100 시간
·사용조인트의 형태 : 브리필드 조인트
크로스 그로브 조인트
측정항목 : 작동후 각 부분에서의 피팅 발생
표 1.
1) 모노아민으로서 사이클로헥실아민과 아닐린의 디우레아 화합물을 사용한 디우레아 그리스.
2) 모노아민으로서 옥틸아민의 디우레아 화합물을 사용한 디우레아 그리스.
3) 몰리브데늄 디설파이드(상품명: Molysulfide; Climax Molybdenum Company 제품; 평균입경 0.7 ㎛)
4) 산화왁스 칼슘염(상품명: Alox 165; Alox Corporation 제품)
5) 석유설폰산 칼슘염(상품명: Sulfol Ca-45; Matsumura Petroleum Laboratory Co., Ltd. 제품)
6) 살리실산 칼슘염(상품명: OSCA423; Osca Chemical Co., Ltd. 제품)
7) 칼슘 폐네이트(상품명: OLOA 218A: Oronite Japan Co., Ltd. 제품)
8) 황산 과염기칼슘염①(상품명: Lubrizol 5283; Lubrizol Japan 제품)
9) 황산 과염기칼슘염②(상품명: Bryton C-400C; Witco Corporation 제품)
10) 황-인계 극압제(상품명: Mobilad G-305; Mobil Chemical 제품)
11) 몰리브데늄 디티오포스페이트(상품명: Molyvan L; R.T.Vanderbilt 제품)
12) 몰리브데늄 디티오카바메이트①(상품명: Molyvan A; R.T.Vanderbilt 제품)
13) 몰리브데늄 디티오카바메이트②(상품명: Molyvan 822; R.T.Vanderbilt 제품)
14) ISO 2137에 의해 측정한 투시도
15) ISO 2176에 의해 측정한 적하점(℃)
16) 최대마찰계수
17) 볼(ball)에서 관측한 마모자국의 평균반경(mm)
18) 플레이트에서 관측한 최대마모깊이(㎛)
19) 실제 조인트(브리필드 조인트)를 사용하여 작업대에서 측정한 내구성
20) 실제 조인트(크로스 그로브 조인트)를 사용하여 작업대에서 측정한 내구성
내구성 측정에 있어서, ○ : 피팅이 관측되지 않음
× : 피팅이 관측됨
상기에서 설명된 바와 같이, 본 발명의 등속조인트용 그리스 조성물은 (a)기본오일; (b)우레아계 증감제; (c)몰리브데늄 디설파이드; (d)특정 금속염 또는 특정 과염기금속염; (e)금속이 함유되지 않은 황-인계 극압제와 몰리브데늄 디티오포스페이트 중에서 선택된 극압제; 또는 f)몰리브데늄 디티오카바메이트로 이루어져 있으며, 이는 실시예와 비교예의 실험결과로 부터 알 수 있듯이 우수한 내마모 효과 및 우수한 피팅 억제효과를 발휘한다.

Claims (8)

  1. (a) 기본오일 55.0∼98.0 중량%;
    (b) 우레아계 증감제 1∼25 중량;
    (c) 몰리브데늄 디설파이드 0.5∼5.0 중량% ; 그리고
    (d) 산화왁스 금속염, 석유설폰산 금속염, 알킬아릴설폰산 금속염, 살리실산 금속염, 페네이트(phenates) 금속염, 산화왁스 과염기금속염, 석유설폰산 과염기금속염, 알킬아릴설폰산 과염기금속염, 살리실산 과염기금속염 페네이트(phenates) 과염기금속염 중에서 선택된 금속염 또는 과염기금속염 0.5∼15 중량%가 함유되어 있는 것임을 특징으로 하는 등속조인트용 그리스 조성물.
  2. 제 1 항에 있어서,
    (a) 기본오일 52.0∼97.9 중량%;
    (b) 우레아계 증감제 1∼25 중량;
    (c) 몰리브데늄 디설파이드 0.5∼5.0 중량% ;
    (d) 산화왁스 금속염, 석유설폰산 금속염, 알킬아릴설폰산 금속염, 살리실산 금속염, 페네이트(phenates) 금속염, 산화왁스 과염기금속염, 석유설폰산 과염기금속염, 알킬아릴설폰산 과염기금속염, 살리실산 과염기금속염 페네이트(phenates) 과염기금속염 중에서 선택된 금속염 또는 과염기금속염 0.5∼15 중량% ; 그리고
    (e) 금속염이 함유되지 않은 황-인계 극압제와 몰리브데늄 디티오포스페이트중에서 선택되는 극압제 0.1∼3 중량%가
    함유되어 있는 것임을 특징으로 하는 등속조인트용 그리스 조성물.
  3. 제 1 항에 있어서,
    (a) 기본오일 50.0∼97.9 중량%;
    (b) 우레아계 증감제 1∼25 중량;
    (c) 몰리브데늄 디설파이드 0.5∼5.0 중량% ;
    (d) 산화왁스 금속염, 석유설폰산 금속염, 알킬아릴설폰산 금속염, 살리실산 금속염, 페네이트(phenates) 금속염, 산화왁스 과염기금속염, 석유설폰산 과염기금속염, 알킬아릴설폰산 과염기금속염, 살리실산 과염기금속염 페네이트(phenates) 과염기금속염 중에서 선택된 금속염 또는 과염기금속염 0.5∼15 중량% ; 그리고
    (f) 몰리브데늄 디티오카바메이트 0.1∼5 중량%가 함유되어 있는 것임을 특징으로 하는 등속조인트용 그리스 조성물.
  4. 제 1 항에 있어서, 상기 (d)금속염 또는 과염기금속염은 칼슘염, 마그네슘염, 바륨염, 나트륨염, 칼륨염, 납염, 아연염, 및 알루미늄 중에서 선택된 것임을 특징으로 하는 등속조인트용 그리스 조성물.
  5. 제 1 항에 있어서, 상기 (d)금속염 또는 과염기금속염은 칼슘염 또는 과염기칼슘염인 것임을 특징으로 하는 등속조인트용 그리스 조성물.
  6. 제 1 항에 있어서, 상기 (d)금속염 또는 과염기금속염은 나트륨염 또는 과염기나트륨염인 것임을 특징으로 하는 등속조인트용 그리스 조성물.
  7. 제 2 항에 있어서, 상기 황-인계 극압제는 황 성분 15∼35 중량%와 인 성분 0.5∼3 중량%가 함유되어 있는 것임을 특징으로 하는 등속조인트용 그리스 조성물.
  8. (a) 기본오일 60.0∼91.4 중량% ;
    (b) 우레아계 증감제 5∼20 중량 ;
    (c) 몰리브데늄 디설파이드 2∼4 중량%;
    (d) 산화왁스 금속염, 석유설폰산 금속염, 알칼아릴설폰산 금속염, 살리실산 금속염, 페네이트(phenates) 금속염, 산화왁스 과염기금속염, 석유설폰산 과염기금속염, 알킬아릴설폰산 과염기금속염, 살리실산 과염기금속염 및 페네이트(phenates) 과염기금속염 중에서 선택된 금속염 또는 과염기금속염; 마그네슘염, 바륨염, 나트륨염, 칼륨염, 납염, 아연염 및 알루미늄염 중에서 선택된 금속염 또는 과염기 금속염 1∼10 중량% ;
    (e) 금속이 함유되지 않은 황-인계 극압제와 몰리브데늄 디티오포스페이트 중에서 선택되는 극압제 0.1∼3 중량% ; 그리고
    (f) 몰리브데늄 디티오카바메이트 0.1∼5 중량%가
    필수성분으로 함유되어 있는 것임을 특징으로 하는 등속조인트용 그리스 조성물.
KR1019960013506A 1995-11-13 1996-04-29 등속조인트용그리스조성물 KR100410723B1 (ko)