JPWO2009145235A1 - 高分子組成物 - Google Patents
高分子組成物 Download PDFInfo
- Publication number
- JPWO2009145235A1 JPWO2009145235A1 JP2010514518A JP2010514518A JPWO2009145235A1 JP WO2009145235 A1 JPWO2009145235 A1 JP WO2009145235A1 JP 2010514518 A JP2010514518 A JP 2010514518A JP 2010514518 A JP2010514518 A JP 2010514518A JP WO2009145235 A1 JPWO2009145235 A1 JP WO2009145235A1
- Authority
- JP
- Japan
- Prior art keywords
- unsaturated carboxylic
- carboxylic acid
- mfr
- ethylene
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
<1> (A)エチレン・α,β−不飽和カルボン酸共重合体及びエチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体を含むアイオノマーと、(B)プロピレン系重合体と、を含有し、前記α,β−不飽和カルボン酸エステルに由来する構成単位の質量が、前記(A)アイオノマーの全質量の1〜4.5質量%である高分子組成物である。
前記<1>に記載の高分子組成物は、前記(A)アイオノマーの含有量が高分子組成物100質量部に対して85〜95質量部であり、かつ前記(B)プロピレン系重合体が高分子組成物100質量部に対して5〜15質量部であることが好ましい。
なお、本発明における「MFR」は、JIS K 7210−1999に準拠し、190℃又は230℃、荷重2160gにて測定される値である。以下、同様である。
前記<5>に記載の高分子組成物は、3元重合体を構成するα,β−不飽和カルボン酸エステルが、アクリル酸の炭素数4のアルキルエステルであることが好ましい。
本発明の高分子組成物は、(A)エチレン・α,β−不飽和カルボン酸共重合体及びエチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体を含むアイオノマー(好ましくは高分子組成物100質量部に対して85〜95質量部)と、(B)プロピレン系重合体(好ましくは高分子組成物100質量部に対して5〜15質量部)とを含有し、前記(A)におけるα,β−不飽和カルボン酸エステルに由来する構成単位の質量比をアイオノマーの全質量に対して1〜4.5質量%の範囲に調整して構成したものである。
本発明の高分子組成物は、エチレン・α,β−不飽和カルボン酸共重合体と、エチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体(以下、単に「本発明における3元共重合体」ともいう。)とを含むアイオノマーの少なくとも1種を含有する。本発明におけるアイオノマーは、少なくとも、エチレン・α,β−不飽和カルボン酸共重合体の1種又は2種以上と、本発明における3元共重合体の1種又は2種以上とが金属イオンで架橋されてなるものである。
中でも、アクリル酸、メタクリル酸、マレイン酸、無水マレイン酸、マレイン酸モノエステル、無水マレイン酸モノエステル、及びこれらの1価もしくは多価金属の塩が好ましく、アクリル酸又はメタクリル酸、及びこれらの1価もしくは多価金属の塩が特に好ましい。
具体的には、アクリル酸メチル、アクリル酸エチル、アクリル酸イソプロピル、アクリル酸イソブチル、アクリル酸n−ブチル、アクリル酸イソオクチル、メタクリル酸メチル、メタクリル酸イソブチル、マレイン酸ジメチル等のエステル化合物が挙げられる。中でも、アクリル酸メチル、アクリル酸エチル、アクリル酸イソプロピル、アクリル酸イソブチル、アクリル酸n−ブチル、メタクリル酸メチル、メタクリル酸イソブチルなどのアクリル酸又はメタクリル酸の低級アルキルエステル(炭素数2〜5)が好ましい。更には、アクリル酸又はメタクリル酸のn−ブチルエステルやイソブチルエステルが好ましく、中でも、アクリル酸の炭素数4のアルキルエステルが好ましく、特にイソブチルエステルが好ましい。
この場合、MFRの低い側の3元共重合体のMFR値(低MFR)は、1〜30g/10分の範囲が好ましい。
上記した2種の3元共重合体の組み合わせのうち、前記MFRの比(高MFR/低MFR)が3〜4の範囲であって、かつMFRの高い側の3元共重合体のMFR値(高MFR)が30〜40g/10分の範囲である場合が、ピールシール強度の向上の点で効果的である。
本発明の高分子組成物は、プロピレン系重合体の少なくとも1種を含有する。プロピレン系重合体を含むことにより、低温でのピーラブルシールが可能な温度領域が拡がる。
(1)前記(A)がエチレン・(メタ)アクリル酸共重合体及びエチレン・(メタ)アクリル酸・(メタ)アクリル酸エステル3元重合体からなるZnアイオノマーであって、前記(B)がプロピレン・エチレン共重合体である組み合わせ。
(2)前記(A)が、エチレン・(メタ)アクリル酸共重合体、30<MFR≦50のエチレン・(メタ)アクリル酸・(メタ)アクリル酸エステル3元重合体、及び1≦MFR≦30のエチレン・(メタ)アクリル酸・(メタ)アクリル酸エステル3元重合体からなり、MFR比(高MFR/低MFR)が2〜5であるZnアイオノマーであって、前記(B)がプロピレン・エチレン共重合体である組み合わせ。
(3)更には、上記(1)〜(2)において、ピールシール強度の点で、前記MFRの比(高MFR/低MFR)が3〜4あって、前記(B)のMFRが0.5〜100g/10分である場合が好ましい。
詳細には、アイオノマーの含有量が85質量部以上であるか又はプロピレン系重合体の含有量が15質量部以下である場合、シール強度(特に高温でのロックシール時のシール強度)が良好であり、ピーラブルシール部では易開封性とシール強度とのバランスがとれる。逆に、アイオノマーの含有量が95質量部以下であるか又は5質量部以上である場合、相対的にプロピレン系重合体の含有量が少なくなりすぎず、ピーラブルシール部での易開封性を保ち、ピーラブルシールが可能な温度領域が狭くなるのが回避される。
上記の中でも、アイオノマーの含有量を高分子組成物100質量部に対して90〜95質量部の範囲とし、プロピレン系重合体の含有量を高分子組成物100質量部に対して10〜5質量部の範囲とすることが好ましい。
(1)熱融着法
本発明の高分子組成物を予めフィルム状に成形し、この成形物を基材上に接着剤を介して載せて熱圧着することにより、あるいは基材又は成形物の少なくとも一方の表面に共押出法、押出被覆法等により予め接着剤を積層した後に熱圧着する方法である。
(2)サンドイッチラミネーション法
本発明の高分子組成物を予めフィルム状に成形し、この成形物と基材とをT−ダイ法等による接着剤の溶融膜を介して貼り合わせる方法である。
(3)共押出法
基材樹脂と本発明の高分子組成物を、あるいは基材樹脂と接着剤と本発明の高分子組成物とを共押出成形法により積層する方法である。
(4)接着剤を用いた圧着・接着法
本発明の高分子組成物を予めフィルム状の成形体とし、この成形体又は基材の一方又は双方に接着剤を塗布して圧着、接着する方法である。
−高分子組成物の調製−
下記組成の成分を用い、単軸押出機(40mmφ、先端ダルメージスクリュ)により、樹脂温度170℃、スクリュ回転数50rpmの条件にて溶融混練し、MFR4.8g/10分の高分子組成物を調製した。配合及び得られた高分子組成物の詳細を下記表1〜表2に示す。ただし、下記表2において、MAA量は、高分子組成物中のアイオノマー(高分子組成物からプロピレン共重合体を除いたもの)に対する割合である。IBA量は、高分子組成物中のアイオノマー(高分子組成物からプロピレン共重合体を除いたもの)に対する割合である。中和度は、高分子組成物中のアイオノマー(高分子組成物からプロピレン共重合体を除いたもの)中の酸基の中和度である。
・アイオノマー1
エチレン・メタクリル酸共重合体[メタクリル酸含量12%(質量比)]の亜鉛アイオノマー〔中和度36%、MFR(190℃、2160g荷重)1.5g/10分〕
・アイオノマー2
エチレン・メタクリル酸・アクリル酸イソブチル共重合体[メタクリル酸含量10%(質量比)、アクリル酸イソブチル含量10%(質量比)]の亜鉛アイオノマー〔中和度70%、MFR(190℃、2160g荷重)1.0g/10分〕
・EMAA1
エチレン・メタクリル酸・アクリル酸イソブチル共重合体〔メタクリル酸含量11%(質量比)、アクリル酸イソブチル含量8%(質量比)、MFR(190℃、2160g荷重)10.0g/10分〕
・EMAA2
エチレン・メタクリル酸・アクリル酸イソブチル共重合体〔メタクリル酸含量10%(質量比)、アクリル酸イソブチル含量10%(質量比)、MFR(190℃、2160g荷重)35.0g/10分〕
・EMAA3
エチレン・メタクリル酸共重合体〔メタクリル酸含量11%(質量比)、MFR(190℃、2160g荷重)8.0g/10分〕
・ EMAA4
エチレン・メタクリル酸共重合体〔メタクリル酸含量10%(質量比)、MFR(190℃、2160g荷重)35.0g/10分〕
・F219DA
プロピレン・エチレンランダム共重合体〔MFR(230℃、2160g荷重)8.0g/10分、密度910kg/m3、商品名:プライムポリプロF219DA、プライムポリマー(株)製〕
得られた高分子組成物を、樹脂温度170℃の条件にて50mmφインフレーション成形機を用いて厚み50μmのインフレフィルム(以下、インフレフィルム(50)と略記する。)を成形した。インフレフィルム(50)の片面には、コロナ放電処理を施した。
続いて、12μm厚のポリエチレンテレフタレート〔PET(12)〕/15μm厚のポリエチレン〔PE(15)〕の積層基材を用意し、そのPE(15)の上に前記インフレフィルムを別のPE(15)を介して載せ、65mmφラミネーター(温度315℃)でサンドラミネーション加工することにより、PET(12)/PE(30)/インフレフィルム(50)のサンプル1を得た。なお、PE(30)は、30μm厚のフィルム状ポリエチレンを表す。
実施例1において、「高分子組成物の調製」に用いた組成中の各成分を下記表1〜表2に示すように変更したこと以外は、実施例1と同様にして、厚み50μmインフレフィルムを成形し、ヒートシールを行なった後、実施例1と同様に測定した。測定結果を図1に示す。
実施例1において、「高分子組成物の調製」に用いた組成中の各成分を下記表1〜表2に示すように変更したこと以外は、実施例1と同様にして、厚み30μmのインフレフィルムを成形し、ヒートシールを行なった後、実施例1と同様に測定した。測定結果を図1に示す。
実施例1において、「高分子組成物の調製」に用いた組成中の各成分を下記表1〜表2に示すように変更したこと以外は、実施例1と同様にして、厚み50μmのインフレフィルムを成形し、ヒートシールを行なった後、実施例1と同様に測定した。測定結果を図1に示す。
実施例1において、「高分子組成物の調製」に用いた組成中の各成分を下記表1〜表2に示すように変更したこと以外は、実施例1と同様にして、厚み50μmのインフレフィルムを成形し、ヒートシールを行なった後、実施例1と同様に測定した。測定結果を図1に示す。
比較例1では、α,β−不飽和カルボン酸エステルに由来する構成単位の質量が多すぎるため、シール強度の高い部分と低い部分を有する階段状の二段階曲線を示すが、シール強度の低い部分でのシール強度が低くなりすぎ、イージーピール性が求められる用途が制限される。
なお、比較例2では、低温領域で実施例よりシール強度が高いものの、温度によるシール強度の変化が顕著で一定せず、安定したピーラブルシール部が得られなかった。即ち、シール強度の低い部分から高い部分まで温度とともに変化するため、所望のシール強度を得るためのヒートシール温度範囲が極めて狭く、生産性に劣っていた。また、実施例2及び比較例2の180〜190℃の範囲は、界面剥離せずにシール部破壊が生じやすかった。
比較例3では、シール強度の高い部分と低い部分を有する階段状の二段階曲線を示すが、高温領域でロックシールしたときのシール強度が低くなりすぎ、また低温領域でのシール強度も低いので、ロックシール性とイージーピール性が求められる用途が制限される。
本明細書に記載された全ての文献、特許出願、および技術規格は、個々の文献、特許出願、および技術規格が参照により取り込まれることが具体的かつ個々に記された場合と同程度に、本明細書中に参照により取り込まれる。
<1> (A)エチレン・α,β−不飽和カルボン酸共重合体及びメルトフローレート(MFR;190℃、荷重2.16Kg)の異なる少なくとも2種のエチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体を含み、前記3元重合体から選択された2種の3元重合体のMFRの比(高MFR/低MFR)が2〜5であるアイオノマーと、(B)プロピレン系重合体とを含有し、前記α,β−不飽和カルボン酸エステルに由来する構成単位の質量が、前記(A)アイオノマーの全質量の1〜4.5質量%である高分子組成物である。
前記<1>に記載の高分子組成物は、前記(A)アイオノマーの含有量が高分子組成物100質量部に対して85〜95質量部であり、かつ前記(B)プロピレン系重合体が高分子組成物100質量部に対して5〜15質量部であることが好ましい。
<6> 前記エチレン・α,β−不飽和カルボン酸共重合体及び前記3元重合体を構成するα,β−不飽和カルボン酸がアクリル酸及びメタクリル酸から選ばれ、前記3元重合体を構成するα,β−不飽和カルボン酸エステルが、アクリル酸の炭素数2〜5の低級アルキルエステル及びメタクリル酸の炭素数2〜5の低級アルキルエステルから選ばれる前記<4>又は前記<5>に記載の高分子組成物である。
前記<4>に記載の高分子組成物は、3元重合体を構成するα,β−不飽和カルボン酸エステルが、アクリル酸の炭素数4のアルキルエステルであることが好ましい。
本発明の高分子組成物は、(A)エチレン・α,β−不飽和カルボン酸共重合体及びメルトフローレート(MFR)の異なる少なくとも2種のエチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体を含み、前記3元重合体から選択された2種の3元重合体のMFRの比(高MFR/低MFR)が2〜5であるアイオノマー(好ましくは高分子組成物100質量部に対して85〜95質量部)と、(B)プロピレン系重合体(好ましくは高分子組成物100質量部に対して5〜15質量部)とを含有し、前記(A)におけるα,β−不飽和カルボン酸エステルに由来する構成単位の質量比をアイオノマーの全質量に対して1〜4.5質量%の範囲に調整して構成したものである。
本発明の高分子組成物は、エチレン・α,β−不飽和カルボン酸共重合体と、メルトフローレート(MFR)の異なる少なくとも2種のエチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体(以下、単に「本発明における3元共重合体」ともいう。)とを含むアイオノマーの少なくとも1種を含有する。アイオノマーにおいて、前記3元重合体から選択された2種の3元重合体のMFRの比(高MFR/低MFR)は2〜5である。本発明におけるアイオノマーは、少なくとも、エチレン・α,β−不飽和カルボン酸共重合体の1種又は2種以上と、本発明における3元共重合体の2種以上とが金属イオンで架橋されてなるものである。
実施例1において、「高分子組成物の調製」に用いた組成中の各成分を下記表1〜表2に示すように変更したこと以外は、実施例1と同様にして、厚み30μmのインフレフィルムを成形し、ヒートシールを行なった後、実施例1と同様に測定した。測定結果を図1に示す。
比較例1では、α,β−不飽和カルボン酸エステルに由来する構成単位の質量が多すぎるため、シール強度の高い部分と低い部分を有する階段状の二段階曲線を示すが、シール強度の低い部分でのシール強度が低くなりすぎ、イージーピール性が求められる用途が制限される。
なお、比較例2では、低温領域で実施例よりシール強度が高いものの、温度によるシール強度の変化が顕著で一定せず、安定したピーラブルシール部が得られなかった。即ち、シール強度の低い部分から高い部分まで温度とともに変化するため、所望のシール強度を得るためのヒートシール温度範囲が極めて狭く、生産性に劣っていた。また、参考例2及び比較例2の180〜190℃の範囲は、界面剥離せずにシール部破壊が生じやすかった。
比較例3では、シール強度の高い部分と低い部分を有する階段状の二段階曲線を示すが、高温領域でロックシールしたときのシール強度が低くなりすぎ、また低温領域でのシール強度も低いので、ロックシール性とイージーピール性が求められる用途が制限される。
<1> (A)エチレン・α,β−不飽和カルボン酸共重合体及びメルトフローレート(MFR)の異なる少なくとも2種のエチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体を含み、前記3元重合体から選択された2種の3元重合体のMFRの比(高MFR/低MFR)が2〜5であり、酸基の中和度が10〜40%であるアイオノマーと、(B)プロピレン系重合体と、を含有し、前記α,β−不飽和カルボン酸エステルに由来する構成単位の質量が、前記(A)アイオノマーの全質量の1〜4.5質量%であって、前記(A)アイオノマーの含有量が組成物100質量部に対して85〜95質量部であり、かつ前記(B)プロピレン系重合体の含有量が組成物100質量部に対して5〜15質量部である高分子組成物である。
前記<3>に記載の高分子組成物は、3元重合体を構成するα,β−不飽和カルボン酸エステルが、アクリル酸の炭素数4のアルキルエステルであることが好ましい。
本発明の高分子組成物は、(A)エチレン・α,β−不飽和カルボン酸共重合体及びメルトフローレート(MFR)の異なる少なくとも2種のエチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体を含み、前記3元重合体から選択された2種の3元重合体のMFRの比(高MFR/低MFR)が2〜5であり、酸基の中和度が10〜40%であるアイオノマー(高分子組成物100質量部に対して85〜95質量部)と、(B)プロピレン系重合体(高分子組成物100質量部に対して5〜15質量部)とを含有し、前記(A)におけるα,β−不飽和カルボン酸エステルに由来する構成単位の質量比をアイオノマーの全質量に対して1〜4.5質量%の範囲に調整して構成したものである。
Claims (11)
- (A)エチレン・α,β−不飽和カルボン酸共重合体及びエチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体を含むアイオノマーと、(B)プロピレン系重合体とを含有し、前記α,β−不飽和カルボン酸エステルに由来する構成単位の質量が、前記(A)アイオノマーの全質量の1〜4.5質量%である高分子組成物。
- 前記(A)アイオノマーの含有量が組成物100質量部に対して85〜95質量部であり、かつ前記(B)プロピレン系重合体の含有量が組成物100質量部に対して5〜15質量部である請求項1に記載の高分子組成物。
- 前記アイオノマー中の酸基の中和度が、10〜40%である請求項1に記載の高分子組成物。
- 前記エチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体のα,β−不飽和カルボン酸エステルが、α,β−不飽和カルボン酸の炭素数2〜5の低級アルキルエステルである請求項1に記載の高分子組成物。
- 前記エチレン・α,β−不飽和カルボン酸・α,β−不飽和カルボン酸エステル3元重合体として、メルトフローレート(MFR)の異なる少なくとも2種の3元重合体を含有し、前記3元重合体から選択された2種の3元重合体のMFRの比(高MFR/低MFR)が2〜5である請求項1に記載の高分子組成物。
- 前記2種の3元重合体のうち、MFRの高い一方の3元重合体のMFR値が20〜60である請求項5に記載の高分子組成物。
- 前記エチレン・α,β−不飽和カルボン酸共重合体及び前記3元重合体を構成するα,β−不飽和カルボン酸がアクリル酸及びメタクリル酸から選ばれ、前記3元重合体を構成するα,β−不飽和カルボン酸エステルが、アクリル酸の炭素数2〜5の低級アルキルエステル及びメタクリル酸の炭素数2〜5の低級アルキルエステルから選ばれる請求項6に記載の高分子組成物。
- 前記3元重合体を構成するα,β−不飽和カルボン酸エステルが、アクリル酸の炭素数4のアルキルエステルである請求項7に記載の高分子組成物。
- 前記α,β−不飽和カルボン酸エステルに由来する構成単位の質量が、前記(A)アイオノマーの全質量の2〜4質量%である請求項1に記載の高分子組成物。
- 前記(A)アイオノマーが、エチレン・(メタ)アクリル酸共重合体、メルトフローレート(MFR)が30超50以下のエチレン・(メタ)アクリル酸・(メタ)アクリル酸エステル3元重合体、及びMFRが1以上30以下のエチレン・(メタ)アクリル酸・(メタ)アクリル酸エステル3元重合体からなり、MFR比(高MFR/低MFR)が2〜5であるZnアイオノマーであって、前記(B)プロピレン系重合体がプロピレン・エチレン共重合体である請求項1に記載の高分子組成物。
- 前記MFR比(高MFR/低MFR)が3〜4あって、前記(B)プロピレン系重合体のMFRが0.5〜100g/10分である請求項10に記載の高分子組成物。