JP6870848B2 - 合成樹脂用導電剤、導電性樹脂組成物及び導電性床材 - Google Patents
合成樹脂用導電剤、導電性樹脂組成物及び導電性床材 Download PDFInfo
- Publication number
- JP6870848B2 JP6870848B2 JP2017089279A JP2017089279A JP6870848B2 JP 6870848 B2 JP6870848 B2 JP 6870848B2 JP 2017089279 A JP2017089279 A JP 2017089279A JP 2017089279 A JP2017089279 A JP 2017089279A JP 6870848 B2 JP6870848 B2 JP 6870848B2
- Authority
- JP
- Japan
- Prior art keywords
- carbon atoms
- chemical formula
- conductive
- group
- quaternary ammonium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
R1:炭素数8〜16の脂肪族炭化水素基のうち本発明においては炭素数10〜16の脂肪族炭化水素基及び下記の化2で示される有機基から選ばれる基
R2,R3:炭素数1〜4の脂肪族炭化水素基
Y:分子中に1〜5個の炭素数2〜4のオキシアルキレン単位で構成された(ポリ)オキシアルキレン基を有する(ポリ)オキシアルキレングリコールからすべての水酸基を除いた残基
X−:塩素イオン基、過塩素酸イオン基及びアルキル基の炭素数が1〜4のアルキルスルホン酸イオン基から選ばれる基のうち本発明においては過塩素酸イオン基
R4:炭素数7〜15の脂肪族炭化水素基のうち本発明においては炭素数9〜13の脂肪族炭化水素基
R5:炭素数1〜5のアルキレン基
A:炭素数2〜4のアルキレン基
m:1〜10の整数
・実施例1
第四級アンモニウム塩(A−1)4.8部、第四級アンモニウム塩(B−1)4.8部及びジオール化合物(D−1)0.4部を混合して実施例1の導電剤(E−1)を調製した。
実施例1と同様にして、実施例2〜18,21、参考例19,20,22〜25及び比較例1〜7の導電剤(E−2)〜(E−25)及び(e−1)〜(e−7)を調製した。実施例1も含め、以上で調製した各例の導電剤の内容を表1及び表2にまとめて示した。
*1:(R1が炭素数8〜16の脂肪族炭化水素基である場合の化1で示される第四級アンモニウム塩)/(R1が化2で示される有機基である場合の化1で示される第四級アンモニウム塩)の質量比
A−1:2−ヒドロキシエチルジメチルドデシルアンモニウム過塩素酸塩
A−2:2−ヒドロキシエチルジメチルテトラデシルアンモニウム過塩素酸塩
A−3:2−ヒドロキシエチルジメチルデシルアンモニウム過塩素酸塩
A−4:2−ヒドロキシエチルジメチルヘキサデシルアンモニウム過塩素酸塩
A−5:2−ヒドロキシエチルジメチルオクチルアンモニウム過塩素酸塩
A−6:2−ヒドロキシエチルジメチルドデシルアンモニウムメチルスルホン酸塩
a−1:2−ヒドロキシエチルジメチルオクタデシルアンモニウム過塩素酸塩
B−1:2−ヒドロキシエチルジメチル−3−ドデカンアミドプロピルアンモニウム過塩素酸塩
B−2:2−ヒドロキシエチルジメチル−3−テトラデカンアミドプロピルアンモニウム過塩素酸塩
B−3:2−ヒドロキシエチルジメチル−3−デカンアミドプロピルアンモニウム過塩素酸塩
B−4:2−ヒドロキシエチルジメチル−3−ヘキサデカンアミドプロピルアンモニウム過塩素酸塩
B−5:2−ヒドロキシエチルジメチル−3−オクタンアミドプロピルアンモニウム過塩素酸塩
b−1:2−ヒドロキシエチルジメチル−3−オクタデカンアミドプロピルアンモニウム過塩素酸塩
b−2:ジメチル−3−ドデカンアミドプロピルアミンジエチル硫酸塩
D−2:ポリオキチエチレングリコール(m=5)
d−1:PEG−1000(三洋化成社製)
d−2:オレイルアルコールのエチレンエキサイド15モル付加物
d−3:テトラデシルアルコールのエチレンオキシド5モル付加物/オレイルアルコールのエチレンオキシド13モル付加物=50/50(質量比)
d−4:オレイン酸のエチレンオキシド13モル付加物
・実施例26
ポリ塩化ビニル系樹脂として塩化ビニル単独重合体(平均重合度800)(P−1)を100部、可塑剤としてフタル酸ジ−2−エチルヘキシル(K−1)を25部、炭酸カルシウムとしてステアリン酸表面処理炭酸カルシウム(M−1)/未処理炭酸カルシウム(N−1)=50/50(質量比)の混合物を160部及び試験区分1で調製した導電剤(E−1)を10部、以上を混練機に投入した後、更に安定剤としてバリウム−亜鉛系液体安定剤1.5部、バリウム−亜鉛系粉体安定剤0.5部、エポキシ化大豆油3部及びカラーリング剤としてGBG−2156(緑色、日本ピグメント社製の商品名)1部を加えて混練し、実施例26の導電性樹脂組成物(R−1)を調製した。
実施例26と同様にして、実施例27〜43,46、参考例44,45,47〜50及び比較例8〜19の導電性樹脂組成物(R−2)〜(R−25)及び(r−1)〜(r−12)を調製した。実施例26も含め、各例の導電性樹脂組成物の内容を表3及び表4にまとめて示した。
*2:(炭素数12〜22の飽和脂肪酸で表面処理された脂肪酸表面処理炭酸カルシウム)/(未処理の炭酸カルシウム)の質量比
P−1:塩化ビニル単独重合体(平均重合度800)
P−2:塩化ビニル単独重合体(平均重合度1050)
P−3:塩化ビニル−酢酸ビニル共重合体(平均重合度700)
P−4:塩化ビニル−酢酸ビニル共重合体(平均重合度900)
P−5:塩化ビニル−酢酸ビニル共重合体(平均重合度1100)
K−1:フタル酸ジ−2−エチルヘキシル
K−2:フタル酸ジイソノニル
K−3:フタル酸ジイソデシル
K−4:アジピン酸ジ−2−エチルヘキシル
K−5:トリメリット酸トリオクチル
M−2:ステアリン酸処理炭酸カルシウム(平均粒径2.2μm)
M−3:パルミチン酸処理炭酸カルシウム(平均粒径0.08μm)
M−4:ラウリン酸処理炭酸カルシウム(平均粒径0.08μm)
M−5:ベヘニン酸処理炭酸カルシウム(平均粒径2.2μm)
m−1:変性脂肪酸処理炭酸カルシウム(平均粒径1.8μm)
m−2:カーボンブラック
m−3:カーボン繊維(繊維径13μm、平均繊維長0.3〜0.4mm)
N−1:未処理炭カルシウム(製品名:ホワイトンB,白石カルシウム社製)
N−2:未処理炭酸カルシウム(製品名:ソフトン2200,白石カルシウム社製)
n−1:タルク(LMR、富士タルク工業社製)
E−1〜E−25,e−1〜e−7:表1及び表2に記載の導電剤
・実施例51
試験区分2で調製した導電性樹脂組成物(R−1)を用いて、カレンダー成形により厚さ2.0mmの導電性床材を成形した。
実施例51と同様にして、表5に記載の実施例52〜68,71、参考例69,70,72〜75及び比較例20〜31の導電性床材を成形した。実施例51も含め、成形した各例の導電性床材について次のようにカラーリング性、導電性及び非べたつき性を評価した。結果を表5にまとめて示した。
成形した導電性床材の色調を肉眼で観察し、下記の基準で評価した。
◎:くすみや変色がなく、鮮やかであり、カラーリング性に著しく優れる
○:くすみや変色が僅かにあるが、鮮やかであり、カラーリング性に優れる
△:くすみや変色があり、鮮やかさに欠け、カラーリング性に劣る
×:黒色であり、カラーリング性に著しく劣る
成形した導電性床材を、20℃で相対湿度55%の条件下に24時間調湿した後、同条件下で表面抵抗値(Ω)を電気抵抗値測定装置(日置電機社製の商品名SM−8220、SME−8310)を用いて測定した。
成形した導電性床材を、20℃で相対湿度55%の条件下に24時間調湿した後、表面の外観を肉眼で観察し、手で触って、下記の基準で評価した。
◎:導電剤のブリードアウトがなく、べたつきもない
○:導電剤のブリードアウトが僅かにあるが、べたつきはない
△:導電剤のブリードアウトがあり、べたつきがある
×:導電剤のブリードアウトが激しく、著しいべたつきがある
Claims (13)
- 下記の化1で示される第四級アンモニウム塩及びジオール化合物としてエチレングリコールを含有し、
前記第四級アンモニウム塩が、R 1 が炭素数10〜16の脂肪族炭化水素基である場合の化1で示される第四級アンモニウム塩と、R 1 が化2で示される有機基である場合の化1で示される第四級アンモニウム塩とを含むことを特徴とする合成樹脂用導電剤。
R1:炭素数10〜16の脂肪族炭化水素基及び下記の化2で示される有機基から選ばれる基
R2,R3:炭素数1〜4の脂肪族炭化水素基
Y:分子中に1〜5個の炭素数2〜4のオキシアルキレン単位で構成された(ポリ)オキシアルキレン基を有する(ポリ)オキシアルキレングリコールからすべての水酸基を除いた残基
X− :過塩素酸イオン基)
R4:炭素数9〜13の脂肪族炭化水素基
R5:炭素数1〜5のアルキレン基) - 下記の化3で示される第四級アンモニウム塩及びジオール化合物としてエチレングリコールを含有し、第四級アンモニウム塩としてR 1 が炭素数10〜16の脂肪族炭化水素基である場合の化3で示される第四級アンモニウム塩及びR 1 が化4で示される有機基である場合の化3で示される第四級アンモニウム塩から選ばれる少なくとも一種のみを含むことを特徴とする合成樹脂用導電剤。
R1:炭素数10〜16の脂肪族炭化水素基及び下記の化4で示される有機基から選ばれる基
R2,R3:炭素数1〜4の脂肪族炭化水素基
Y:分子中に1〜5個の炭素数2〜4のオキシアルキレン単位で構成された(ポリ)オキシアルキレン基を有する(ポリ)オキシアルキレングリコールからすべての水酸基を除いた残基
X− :過塩素酸イオン基)
R4:炭素数9〜13の脂肪族炭化水素基
R5:炭素数1〜5のアルキレン基) - 第四級アンモニウム塩/ジオール化合物=99.9/0.1〜80/20(質量比)の割合で含有する請求項1又は2記載の合成樹脂用導電剤。
- R1が炭素数12〜14の脂肪族炭化水素基であり、R4が炭素数11〜13の脂肪族炭化水素基である請求項1〜3のいずれか一つの項記載の合成樹脂用導電剤。
- 第四級アンモニウム塩が、(R1が炭素数10〜16の脂肪族炭化水素基である場合の化1で示される第四級アンモニウム塩)/(R1が化2で示される有機基である場合の化1で示される第四級アンモニウム塩)=80/20〜20/80(質量比)の混合物である請求項1記載の合成樹脂用導電剤。
- 第四級アンモニウム塩が、(R1が炭素数10〜16の脂肪族炭化水素基である場合の化3で示される第四級アンモニウム塩)/(R1が化4で示される有機基である場合の化3で示される第四級アンモニウム塩)=80/20〜20/80(質量比)の混合物である請求項2記載の合成樹脂用導電剤。
- ポリ塩化ビニル系樹脂用のものである請求項1〜6のいずれか一つの項記載の合成樹脂用導電剤。
- ポリ塩化ビニル系樹脂100質量部に対し、下記の可塑剤を15〜60質量部、炭酸カルシウムを50〜500質量部及び請求項1〜7のいずれか一つの項記載の合成樹脂用導電剤を5〜30質量部の割合で含有することを特徴とする導電性樹脂組成物。
可塑剤:フタル酸エステル系可塑剤、脂肪族ジカルボン酸エステル系可塑剤及びトリメリット酸エステル系可塑剤から選ばれる少なくとも一つ - 炭酸カルシウムが、炭素数12〜22の飽和脂肪酸で表面処理された脂肪酸表面処理炭酸カルシウムを含有するものである請求項8記載の導電性樹脂組成物。
- 炭酸カルシウムが、炭素数12〜22の飽和脂肪酸で表面処理された脂肪酸表面処理炭酸カルシウム/未処理の炭酸カルシウム=80/20〜20/80(質量比)の混合物である請求項9記載の導電性樹脂組成物。
- 表面処理炭酸カルシウムが、炭素数16〜18の飽和脂肪酸で表面処理されたものである請求項9又は10記載の導電性樹脂組成物。
- 請求項8〜11のいずれか一つの項記載の導電性樹脂組成物を用いて成形された厚さが1〜3mmの成形物であることを特徴とする導電性床材。
- 2層以上の積層導電性床材であって、表層を請求項8〜11のいずれか一つの項記載の導電性樹脂組成物を用いて成形された厚さが0.5〜1.5mmの導電性床材であることを特徴とする積層導電性床材。