JP6614734B1 - 樹脂組成物およびそれより得られる成形体 - Google Patents
樹脂組成物およびそれより得られる成形体 Download PDFInfo
- Publication number
- JP6614734B1 JP6614734B1 JP2019084133A JP2019084133A JP6614734B1 JP 6614734 B1 JP6614734 B1 JP 6614734B1 JP 2019084133 A JP2019084133 A JP 2019084133A JP 2019084133 A JP2019084133 A JP 2019084133A JP 6614734 B1 JP6614734 B1 JP 6614734B1
- Authority
- JP
- Japan
- Prior art keywords
- resin composition
- resin
- group
- melt
- dipentaerythritol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
例えば、特許文献3には、溶融重合法で得られた芳香族ポリカーボネート樹脂を含む樹脂組成物を、耐薬品性および湿熱疲労性等の観点から、OA機器の内部部品等に用いる技術が開示されている。
また例えば、特許文献4には、溶融重合法で得られた芳香族ポリカーボネート樹脂を含む樹脂組成物を、色調、耐久性および安定性等の観点から、高密度光ディスク用の基板等に用いる技術が開示されている。
また例えば、特許文献5には、溶融重合法で得られたポリカーボネート樹脂を含む樹脂組成物を、ハイサイクル性および金型汚れの低減等の観点から、光学情報基板に用いる技術が開示されている。
<1> (A)ポリアリレート樹脂、(B)溶融重合ポリカーボネート樹脂、(C)下記一般式(I)および(II)で表されるホスファイト化合物からなる群から選択される1種以上の化合物、および(D)ジペンタエリスリトール脂肪酸エステルを含有する樹脂組成物であって、
(A)ポリアリレート樹脂と(B)溶融重合ポリカーボネート樹脂との質量比(A/B)が2/98〜98/2であり、
前記樹脂組成物のビカット軟化点が140℃以上である、樹脂組成物:
<2> 前記(C)ホスファイト化合物の含有量が、(A)ポリアリレート樹脂と(B)溶融重合ポリカーボネート樹脂との合計量100質量部に対し0.01〜0.5質量部である、<1>に記載の樹脂組成物。
<3> 前記(D)ジペンタエリスリトール脂肪酸エステルの含有量が、(A)ポリアリレート樹脂と(B)溶融重合ポリカーボネート樹脂との合計量100質量部に対し0.01〜1.0質量部である、<1>または<2>に記載の樹脂組成物。
<4> 前記(D)ジペンタエリスリトール脂肪酸エステルが、ジペンタエリスリトールヘキサラウレート、ジペンタエリスリトールヘキサミリステート、ジペンタエリスリトールヘキサパルミテート、ジペンタエリスリトールヘキサステアレート、ジペンタエリスリトールヘキサべヘネート、ジペンタエリスリトールアジピックステアレート、ジペンタエリスリトールアジピックステアレートオリゴマからなる群から選択される1種以上の化合物である、<1>〜<3>のいずれかに記載の樹脂組成物。
<5> 前記(A)ポリアリレート樹脂と前記(B)溶融重合ポリカーボネート樹脂との混合比率が質量比で30/70〜75/25であり、
前記(C)ホスファイト化合物が下記一般式(i−1)および前記一般式(II)で表されるホスファイト化合物からなる群から選択される1種以上の化合物である、<1>に記載の樹脂組成物:
<6> 前記(A)ポリアリレート樹脂と前記(B)溶融重合ポリカーボネート樹脂との混合比率が質量比で45/55〜75/25であり、
前記(C)ホスファイト化合物が前記一般式(i−1)で表されるホスファイト化合物からなる群から選択される1種以上の化合物であり、
前記(C)ホスファイト化合物の含有量が、(A)ポリアリレート樹脂と(B)溶融重合ポリカーボネート樹脂との合計量100質量部に対し0.01〜0.08質量部である、<5>に記載の樹脂組成物。
<7> 前記(A)ポリアリレート樹脂と前記(B)溶融重合ポリカーボネート樹脂との混合比率が質量比で65/35〜75/25である、<6>に記載の樹脂組成物。
<8> 前記樹脂組成物における単官能フェノール化合物の含有量が10,000ppm以下である、<1>〜<7>のいずれかに記載の樹脂組成物。
<9> 前記(B)溶融重合ポリカーボネート樹脂の対数粘度が0.30〜0.60dL/gである、<1>〜<8>のいずれかに記載の樹脂組成物。
<10> 前記(A)ポリアリレート樹脂の対数粘度が0.40〜0.75dL/gである、<1>〜<9>のいずれかに記載の樹脂組成物。
<11> 前記樹脂組成物の対数粘度が0.35〜0.65dL/gである、<1>〜<10>のいずれかに記載の樹脂組成物。
<12> 前記樹脂組成物が光反射体用基体を製造するための樹脂組成物である、<1>〜<11>のいずれかに記載の樹脂組成物。
<13> 前記樹脂組成物が車載用ランプの光反射体用基体を製造するための樹脂組成物である、<1>〜<12>のいずれかに記載の樹脂組成物。
<14> 前記樹脂組成物が射出成形に使用されるための樹脂組成物である、<1>〜<13>のいずれかに記載の樹脂組成物。
<15> <1>〜<14>のいずれかに記載の樹脂組成物を含む、成形体。
<16> <15>に記載の成形体を用いた光反射体用基体。
<17> <16>に記載の光反射体用基体を用いた車載用ランプ。
本発明の樹脂組成物は、金型汚れを十分に抑制できる。
本発明の樹脂組成物を用いると、表面外観特性および蒸着適性に十分に優れた成形体を製造することができる。
本発明の樹脂組成物を用いて製造された成形体は、熱エージング適性に十分に優れるため、当該成形体に蒸着層を形成して、より苛酷な高温雰囲気下にさらしても、蒸着層の光沢度および密着性の低下が十分に抑制される。
本発明の樹脂組成物は、(A)ポリアリレート樹脂および(B)溶融重合ポリカーボネート樹脂を含む。
溶融重合ポリカーボネート樹脂の対数粘度は、溶融重合ポリカーボネート樹脂を用いること以外、ポリアリレート樹脂の対数粘度と同様の方法により測定された値を用いている。
R21〜R30のうち、R21、R23、R28およびR30は、それぞれ独立して、炭素原子数1〜5、特に1〜4のアルキル基または炭素原子数7〜12、特に7〜10のアリールアルキル基であり、R25およびR26は、それぞれ独立して、水素原子、炭素原子数1〜5、特に1〜4のアルキル基または炭素原子数7〜12、特に7〜10のアリールアルキル基であり、残りの基は水素原子である;
R21〜R30のうち、R21、R23、R25、R26、R28およびR30は、それぞれ独立して、炭素原子数1〜5、特に1〜4のアルキル基または炭素原子数7〜12、特に7〜10のアリールアルキル基であり、残りの基は水素原子である;または
R21〜R30のうち、R22、R24、R27およびR29は、それぞれ独立して、炭素原子数1〜5、特に1〜4のアルキル基であり、残りの基は水素原子である。
ビス(2,4−ジ−tert−ブチルフェニル)ペンタエリスリトールジホスファイト;
ビス(2,6−ジ−tert−ブチル−4−メチルフェニル)ペンタエリスリトールジホスファイト;
ビス(2,4−ジメチル−6−tert−ブチルフェニル)ペンタエリスリトールジホスファイト;
ビス(2,4,6−トリ−tert−ブチルフェニル)ペンタエリスリトールジホスファイト;
ビス(2−メチル−4,6−ジ−tert−ブチルフェニル)ペンタエリスリトールジホスファイト;
ビス(3,5−ジ−tert−ブチルフェニル)ペンタエリスリトールジホスファイト;
ビス(ノニルフェニル)ペンタエリスリトールジホスファイト;
ビス(2,4−ジクミルフェニル)ペンタエリスリトールジホスファイト。
R31およびR32は、それぞれ独立して、炭素原子数10〜26、特に14〜22の直鎖状アルキル基である。
ジステアリルペンタエリスリトールジホスファイト。
R41〜R45のうち、R41およびR43は、それぞれ独立して、炭素原子数1〜5、特に1〜4のアルキル基であり、R45は水素原子または炭素原子数1〜5、特に1〜4のアルキル基であり、残りの基は水素原子である。
トリス(2,4−ジ−tert−ブチルフェニル)ホスファイト;
トリス(2,4,6−トリ−tert−ブチルフェニル)ホスファイト;
トリス(4−メチル−2,6−ジ−tert−ブチルフェニル)ホスファイト;
トリフェニルホスファイト;
トリノニルフェニルホスファイト。
また、ジペンタエリスリトール脂肪酸エステルとして、ジペンタエリスリトールとジカルボン酸の縮合反応によりオリゴマー化したポリオールと脂肪族、脂環族、芳香族のカルボン酸によりエステル化されたエステル化合物も用いることができる。例えば、脂肪族ジカルボン酸としてアジピン酸を用いた場合、すなわちペンタエリスリトールをアジピン酸でオリゴマー化しステアリン酸によりエステル化されたエステル化合物等も用いることができる。このようなエステル化合物の例として、ジペンタエリスリトールアジピックステアレートオリゴマ等が挙げられる。
成形体が灰色を有する場合、本発明の樹脂組成物は黒色顔料と白色顔料とを組み合わせて好適に含む。
白色顔料は白色を有する無機系顔料であり、例えば、酸化チタン、酸化亜鉛、硫化亜鉛、硫酸亜鉛、硫酸バリウム、炭酸カルシウム、酸化アルミナ等が挙げられる。白色顔料は単独また2種以上を組み合わせて用いることができる。
本発明の樹脂組成物を用いて、射出成形法、押出成形法、ブロー成形法、圧縮成形法、発泡成形法等のあらゆる成形法により、成形体を製造することができる。本発明の樹脂組成物を用いて射出成形法により製造された成形体は、射出成形法に特有のウェルドラインおよびその周辺において曇りに関する表面外観特性に優れるため、射出成形法により製造されることが好ましい。
(1)単官能フェノール化合物の総量
樹脂組成物ペレットを用い、下記の装置および条件にて、熱分解/ガスクロマトグラフ質量分析(Py/GC−MS)を行い、フェノール、p−tert−ブチルフェノールおよびp−クミルフェノールの3種のフェノール化合物の総量をデカン換算数値としてppm単位で表した。
1−1.Py装置:フロンティアラボ製PY2020D
ヘリウムガス雰囲気下で開始温度40℃から20℃/分で昇温、370℃到達で5分間ホールドし、上記条件にて採取された発生ガスを下記GC装置およびMS装置にて同定、定量した。
昇温条件:40℃で3分ホールド後、10℃/分で150℃まで昇温し、150℃から320℃までは20/分で昇温し、320℃で3分ホールドした。
カラム UltraALLOY−5(30m×0.25mm×0.25μm)
スプリット 50:1
マスレンジ:スキャン測定(massレンジ:29.0〜550.0)
トランスファーライン:320℃
1,1,2,2−テトラクロロエタンを溶媒として、温度25℃において測定し、dL/g単位で表した。
樹脂組成物ペレットを、120℃にて12時間以上熱風乾燥した後、射出成型機(東芝機械社製EC100N型)にて、樹脂温度320℃あるいは350℃、金型温度100℃、射出圧力150MPa、射出時間4秒、設定射出速度150mm/秒で成形した際の試験片の流動長を測定した。試験片の数は5点で、5点の平均値を各評価条件での流動長とした。
金型は厚み2mmおよび幅20mmのバーフロー試験金型を用いた。樹脂温度が同一条件下、流動長が長いほど流動性がよいことを示す。同一条件で測定した流動長を対比した場合5mm以上の差異があった場合、有意な差があると判断した。
樹脂温度350℃での流動長を以下のように評価した。
◎:420mm以上(最良)。
○:390mm以上、420mm未満(良)。
△:290mm以上、390mm未満(実用上問題なし)。
×:290mm未満(実用上問題あり)。
JIS K 7206に規定のB50法に準拠して測定した。ビカット軟化点は、HDT試験装置(ヒートディストーションテスター)(東洋精機製作所社製)で測定した。試験片として、厚さ4mmの成形体を用いて測定した。
ビカット軟化点を以下のように評価した。
◎◎:170℃以上(極上:extra quality)。
◎:160℃以上、170℃未満(最良)。
○:150℃以上、160℃未満(良)。
△:140℃以上、150℃未満(実用上問題なし)。
×:140℃未満(実用上問題あり)。
樹脂組成物ペレットを、120℃で8時間以上熱風乾燥した後、射出成形機(東芝機械社製EC100N型)に試験片金型を取り付けて、樹脂温度は各樹脂組成物ごとに最適な温度(表参照)に設定しつつ、金型温度は90℃に設定し、射出成形を行い、成形体(70mm×40mm)を得た。成形体は、厚みが1mm、2mmおよび3mmの三段階で変化した成形体であった。なお、金型の成形面は#8000のみがきをかけた鏡面仕様とし、溶融した樹脂組成物が金型内フル充填とならない、ショートショットの状態で連続50ショットの成形を行い、樹脂の流動先端近傍となる金型表面(可動型および固定型の成形面)を目視確認し、曇りの発生の有無を観察した。曇りの程度に応じて5段階(薄1<<3<<5濃)で評価をした。曇の程度の評価値が小さいほど、曇は少なく、良好である。
◎:評価値=1(最良)。
○:評価値=2(良)。
△:評価値=3(実用上問題なし)。
×:評価値=4(実用上問題あり)。
××:評価値=5(実用上問題あり)。
樹脂組成物ペレットを、120℃で8時間以上熱風乾燥した後、射出成形機(東芝機械社製EC100N型)に試験片金型を取り付けて、樹脂温度は各樹脂組成物ごとに最適な温度(表参照)に設定しつつ、金型温度は90℃に設定し、射出成形を行い、成形体(70×40mm、厚み2mmt)を得た。なお、金型の成形面は#8000のみがきをかけた鏡面仕様とした。また、金型は、短辺方向中央部に第一のゲートと、第一のゲートを有する短辺に対向する他方短辺に近接する長辺終端部に第二のゲートの2つのゲートを有するものであり、溶融樹脂は、2つのゲートより同時にキャビティ内に流入する。キャビティに流入した溶融樹脂は、キャビティ中央部で合流し樹脂冷却とともに合流部にウェルドを生成する。ウェルド部の成形体表面の外観を下記基準で評価した。
◎:ウェルドラインおよびその周辺に曇りは全く無い(最良)。
○:ウェルドラインおよび/またはその周辺に曇りが1カ所のみで部分的に生じた(良)。
△:ウェルドラインおよび/またはその周辺に曇りが2カ所以上で部分的に生じたが、実用上問題のない範囲であった。
×:ウェルドラインおよび/またはその周辺に沿って帯状の曇りが生じ、実用上問題があった。
(6)成形体の表面外観特性で使用した金型を用い、成形体(70×40mm、厚み2mmtを得た。なお、第一のゲートのみから溶融樹脂が金型内に流入するよう流路変更を行った以外は、(6)と同様の条件で行った。成形体の離型性を下記基準により判断した。◎のものは離型性が良好であり、×のものは離型性が不良である。
◎:得られた成形体を金型から離型する際、ビビリ音は発せず、抵抗なく取り出しができたため、成形体に突出ピンの跡が全く残らなかった。
×:得られた成形体を金型から離型する際、ビビリ音を発し、成形体に突出ピンの跡が残った。
樹脂組成物ペレットを、120℃で8時間以上熱風乾燥した後、射出成形機(東芝機械社製EC100N型)に試験片金型を取り付けて、樹脂温度は各樹脂組成物ごとに最適な温度(表参照)に設定しつつ、金型温度は90℃に設定し、射出成形を行い、成形体(70×10mm、厚み4mmt)を得た。得られた成形体につき、前記(2)対数粘度での条件に従い対数粘度を測定した。
一方、得られた試験片をプレッシャークッカー(平山製作所製、型式PC−242HSR2)に投入し、温度130℃、相対湿度75%RH、圧力0.2MPaの条件で、75時間処理をし、同様に成形体の対数粘度を測定し、処理前に対する処理後の対数粘度保持率を下記式により算出した。
成形体の対数粘度保持率56%以上であれば、耐加水分解性が「実用上問題なし」と判断した。
成形体の対数粘度保持率(%)=(処理後の成形体対数粘度/処理前の成形体対数粘度)×100
◎:保持率64%以上(最良)。
○:保持率60%以上64%未満(良)。
△:保持率56%以上60%未満(実用上問題なし)。
×:保持率56%未満(実用上問題あり)。
(6)で得た成形体の鏡面側に対し、アンダーコートすることなくベルジャー型真空蒸着装置(ULVAC社製)を用いアルミニウムを蒸着した。蒸着層の厚みはおよそ0.1μmであった。表面にアルミニウムの蒸着層が形成された成形体の初期外観について目視により下記の基準で判定した。
◎:蒸着層の全表面が鏡面であり、曇りが全く無く、成形体の外観が最良であった。
○:ウェルドラインおよびその周辺の蒸着層表面に曇りが1カ所のみで部分的に生じたが、成形体の外観が良好であった。
△:ウェルドラインおよびその周辺の蒸着層表面に曇りが2カ所以上で部分的に生じたが実用上問題なかった。
×:ウェルドラインおよびその周辺の蒸着層表面に曇りが全体的に生じ、成形体の外観は不良であった(実用上問題あり)。
(7)で得た蒸着層を有する成形体を各々高温炉中、135℃条件下、24時間熱エージング試験を行った。熱エージング試験とは、成形体を所定の温度で所定の時間だけ静置する処理のことである。熱エージング試験後の成形体について、(i)蒸着層表面の光沢度、(ii)蒸着層の密着性の評価をそれぞれ行った。
JIS Z8741に準拠し、光沢度計(日本電色工業社製、VG−2000型)を用い、各成形体における蒸着層表面の入射角20°における表面光沢度を測定し、下記の基準により4段階で評価した。なお(9)にて、蒸着層表面に曇りを生じたものは、特に曇り近傍の光沢度を測定した。N=5で測定を行い、その平均値を該成形体における光沢度とした。
◎:光沢度1500以上(最良)。
○:光沢度1000以上1500未満(良)。
△:光沢度750以上1000未満(実用上問題なし)。
×:光沢度750未満(実用上問題あり)。
JIS K5400で規定されているXカットテープ法に準拠し、各成形体の蒸着層に対し、カッターナイフにてクロスカット(Xカット)を入れ、セロハンテープを貼付後、剥離し、下記基準で測定した。N=5で測定を行い、その平均値を該成形体における蒸着層の密着性評価とした。
◎:蒸着層の剥がれが全くない(最良)。
○:Xカット部にわずかの剥がれがある(良)。
△:Xカット部の交点いずれかの方向に、3.0mm以内の剥がれがある(実用上問題なし)。
×:Xカット部より大きく剥がれる(実用上問題あり)。
流動性、耐熱性、金型成形面の耐曇り性、ならびに成形体の表面外観特性、蒸着適性および熱エージング適性の評価結果に基づいて、総合的に評価した。
◎◎:全ての評価結果うち、最も低い評価結果が◎であり、かつ耐熱性が◎◎であった。
◎:全ての評価結果が◎であった。
○:全ての評価結果うち、最も低い評価結果が○であった。
△:全ての評価結果うち、最も低い評価結果が△であった。
×:全ての評価結果うち、最も低い評価結果が×または××であった。
(1)ポリアリレート:U−パウダー Lタイプ(ユニチカ社製)(対数粘度0.54)
・ポリカーボネートb1:溶融重合ポリカーボネート:ジフェニルカーボネートおよびビスフェノールAから重合されたポリカーボネート
WONDERLITE PC−175(奇美実業社製)(対数粘度0.39)
・ポリカーボネートb2:界面重合ポリカーボネート:ホスゲンおよびビスフェノールAから重合されたポリカーボネート
SDポリカ200−80(住化ポリカーボネート社製)(対数粘度0.39)
・ホスファイト化合物c1:ビス(2,6−ジ−tert−ブチル−4−メチルフェニル)ペンタエリスリトールジホスファイト(ADEKA社製アデカスタブPEP−36)
・ホスファイト化合物c2:トリス(2,4−ジ−tert−ブチルフェニル)ホスファイト(ADEKA社製アデカスタブ2112)
・ホスファイト化合物c3:ジステアリルペンタエリスリトールジホスファイト(ADEKA社アデカスタブPEP−8)
・非ホスファイト化合物c4(ホスホナイト系化合物):テトラキス(2,4−ジ−t−ブチルフェニル)[1,1−ビフェニル]−4,4'−ジイルビスホスホナイト(BASF製IRGAFOS P−EPQ)
・ヒンダードフェノール系化合物:イルガノックス1010(ペンタエリスリチル−テトラキス[3−(3,5−ジ−t−ブチル−4−ヒドロキシフェニル)プロピオネート]、(BASF社製Irganox 1010)
・脂肪酸エステルd1:ジペンタエリスリトール脂肪酸エステル:ジペンタエリスリトールヘキサステアレート(エメリーオレオケミカルズ社製VPG−2571、末端水酸基0〜10.0mgKOH)
・脂肪酸エステルd2:ペンタエリスリトール脂肪酸エステル:ペンタエリスリトールテトラステアレート(エメリーオレオケミカル社製VPG−861、末端水酸基20〜37mgKOH)
・非脂肪酸エステルd3:脂肪酸エステル以外の化合物:パラフィンワックス(日本精蝋社製ルバックス1266)
・カーボンブラック(UP−D 701;大日精化工業社製)
所定のポリアリレートとポリカーボネートを、熱風循環式乾燥機を用いて120℃で8時間以上乾燥を行い、ホスファイト化合物(または非ホスファイト化合物)および脂肪酸エステル(または非脂肪酸エステル)とともに、表1〜表3に示した配合割合で均一混練をした。詳しくは、ポリアリレートとポリカーボネートとの合計量100質量部に対し、ホスファイト化合物(または非ホスファイト化合物)および脂肪酸エステル(または非脂肪酸エステル)をそれぞれ所定量、ならびに着色剤0.05質量部を、クボタ社製連続定量供給装置を用いて、同方向2軸押出機(東芝機械社製TEM−37BS)の主供給口に供給した。そして、所定の樹脂温度および吐出量10kg/時で溶融混練を行い、ノズルからストランド状に引き取った樹脂組成物を水浴にくぐらせて冷却固化し、ペレタイザーでカッティングした後、120℃で8時間熱風乾燥することによって樹脂組成物のペレットを得た。所定の樹脂温度とは表1〜表3に記載の成形温度のことである。さらに得られた樹脂組成物ペレットを、上記した評価方法に記載の方法に従って、射出成形し、成形体を得た。
得られた樹脂組成物ペレットもしくは成形体を用い、各種評価を行った。その結果を表1〜表3に示す。
なお、参考例1〜2においては、ポリカーボネート樹脂単独での前記評価(流動性、耐加水分解性および熱エージング適性の評価は未実施)を行った。
Claims (17)
- (A)ポリアリレート樹脂、(B)溶融重合ポリカーボネート樹脂、(C)下記一般式(I)および(II)で表されるホスファイト化合物からなる群から選択される1種以上の化合物、および(D)ジペンタエリスリトール脂肪酸エステルを含有する樹脂組成物であって、
(A)ポリアリレート樹脂と(B)溶融重合ポリカーボネート樹脂との質量比(A/B)が2/98〜98/2であり、
前記樹脂組成物のビカット軟化点が140℃以上である、樹脂組成物:
- 前記(C)ホスファイト化合物の含有量が、(A)ポリアリレート樹脂と(B)溶融重合ポリカーボネート樹脂との合計量100質量部に対し0.01〜0.5質量部である、請求項1に記載の樹脂組成物。
- 前記(D)ジペンタエリスリトール脂肪酸エステルの含有量が、(A)ポリアリレート樹脂と(B)溶融重合ポリカーボネート樹脂との合計量100質量部に対し0.01〜1.0質量部である、請求項1または2に記載の樹脂組成物。
- 前記(D)ジペンタエリスリトール脂肪酸エステルが、ジペンタエリスリトールヘキサラウレート、ジペンタエリスリトールヘキサミリステート、ジペンタエリスリトールヘキサパルミテート、ジペンタエリスリトールヘキサステアレート、ジペンタエリスリトールヘキサべヘネート、ジペンタエリスリトールアジピックステアレート、ジペンタエリスリトールアジピックステアレートオリゴマからなる群から選択される1種以上の化合物である、請求項1〜3のいずれかに記載の樹脂組成物。
- 前記(A)ポリアリレート樹脂と前記(B)溶融重合ポリカーボネート樹脂との混合比率が質量比で45/55〜75/25であり、
前記(C)ホスファイト化合物が前記一般式(i−1)で表されるホスファイト化合物からなる群から選択される1種以上の化合物であり、
前記(C)ホスファイト化合物の含有量が、(A)ポリアリレート樹脂と(B)溶融重合ポリカーボネート樹脂との合計量100質量部に対し0.01〜0.08質量部である、請求項5に記載の樹脂組成物。 - 前記(A)ポリアリレート樹脂と前記(B)溶融重合ポリカーボネート樹脂との混合比率が質量比で65/35〜75/25である、請求項6に記載の樹脂組成物。
- 前記樹脂組成物における単官能フェノール化合物の含有量が10,000ppm以下である、請求項1〜7のいずれかに記載の樹脂組成物。
- 前記(B)溶融重合ポリカーボネート樹脂の対数粘度が0.30〜0.60dL/gである、請求項1〜8のいずれかに記載の樹脂組成物。
- 前記(A)ポリアリレート樹脂の対数粘度が0.40〜0.75dL/gである、請求項1〜9のいずれかに記載の樹脂組成物。
- 前記樹脂組成物の対数粘度が0.35〜0.65dL/gである、請求項1〜10のいずれかに記載の樹脂組成物。
- 前記樹脂組成物が光反射体用基体を製造するための樹脂組成物である、請求項1〜11のいずれかに記載の樹脂組成物。
- 前記樹脂組成物が車載用ランプの光反射体用基体を製造するための樹脂組成物である、請求項1〜12のいずれかに記載の樹脂組成物。
- 前記樹脂組成物が射出成形に使用されるための樹脂組成物である、請求項1〜13のいずれかに記載の樹脂組成物。
- 請求項1〜14のいずれかに記載の樹脂組成物を含む、成形体。
- 請求項15に記載の成形体を用いた光反射体用基体。
- 請求項16に記載の光反射体用基体を用いた車載用ランプ。