JP6378211B2 - 耐衝撃性または耐熱性に優れた高分子樹脂組成物 - Google Patents
耐衝撃性または耐熱性に優れた高分子樹脂組成物 Download PDFInfo
- Publication number
- JP6378211B2 JP6378211B2 JP2015555926A JP2015555926A JP6378211B2 JP 6378211 B2 JP6378211 B2 JP 6378211B2 JP 2015555926 A JP2015555926 A JP 2015555926A JP 2015555926 A JP2015555926 A JP 2015555926A JP 6378211 B2 JP6378211 B2 JP 6378211B2
- Authority
- JP
- Japan
- Prior art keywords
- copolymer
- aromatic vinyl
- resin composition
- weight
- polymer resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体、アルキルメタクリレート−ジエン系ゴム−芳香族ビニルグラフト共重合体、およびアルキルメタクリレート−シリコン/アルキルアクリレートグラフト共重合体からなる群より選択される1種以上の共重合体を含む高分子樹脂組成物を提供する。
不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体、アルキルメタクリレート−ジエン系ゴム−芳香族ビニルグラフト共重合体、およびアルキルメタクリレート−シリコン/アルキルアクリレートグラフト共重合体からなる群より選択される1種以上の共重合体を含む高分子樹脂組成物を提供する。
不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体、アルキルメタクリレート−ジエン系ゴム−芳香族ビニルグラフト共重合体、およびアルキルメタクリレート−シリコン/アルキルアクリレートグラフト共重合体からなる群より選択される1種以上の共重合体を含む高分子樹脂組成物を提供することができる。
不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体、アルキルメタクリレート−ジエン系ゴム−芳香族ビニルグラフト共重合体、およびアルキルメタクリレート−シリコン/アルキルアクリレートグラフト共重合体からなる群より選択される1種以上の共重合体で構成される基本樹脂全体対比10重量%以下で含むことができる。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:140℃、重量平均分子量:4万)70重量%、アクリロニトリル−ブタジエン−スチレングラフト共重合体10重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体5重量%、およびポリカーボネート15重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−グリシジルメタクリレート3重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:130℃、重量平均分子量:4万)70重量%、アクリロニトリル−ブタジエン−スチレングラフト共重合体10重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体5重量%、およびポリカーボネート15重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−グリシジルメタクリレート3重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:120℃、重量平均分子量:5万)70重量%、アクリロニトリル−ブタジエン−スチレングラフト共重合体5重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体10重量%、およびポリカーボネート15重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−グリシジルメタクリレート3重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:130℃、重量平均分子量:4万)70重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体15重量%、およびポリカーボネート15重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−グリシジルメタクリレート2重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:130℃、重量平均分子量:4万)70重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体15重量%、およびポリカーボネート15重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−無水マレイン酸3重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:130℃、重量平均分子量:4万)70重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体15重量%、およびポリカーボネート15重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−無水マレイン酸3重量%、カルボジイミド系耐加水分解剤0.5重量%、フェノール系1次酸化安定剤およびホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:130℃、重量平均分子量:4万)65重量%、アクリロニトリル−ブタジエン−スチレングラフト共重合体15重量%、およびポリカーボネート20重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−無水マレイン酸3重量%、カルボジイミド系耐加水分解剤0.5重量%、フェノール系1次酸化安定剤およびホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:140℃、重量平均分子量:4万)70重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体20重量%、およびアクリロニトリル−スチレン共重合体10重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−グリシジルメタクリレート2重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤2種類をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:120℃、重量平均分子量:5万)70重量%、メチルメタクリレート−シリコン/ブチルアクリレートグラフト共重合体15重量%、およびポリカーボネート15重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−グリシジルメタクリレート3重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:120℃、重量平均分子量:5万)70重量%、アクリロニトリル−ブタジエン−スチレングラフト共重合体10重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体5重量%、一般ポリカーボネート10重量%、および高分子ポリカーボネート5重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−グリシジルメタクリレート3重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:120℃、重量平均分子量:5万)60重量%、アクリロニトリル−ブタジエン−スチレングラフト共重合体10重量%、ポリカーボネート23重量%、およびスチレン−N−フェニルマレイミド−無水マレイン酸7重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−無水マレイン酸2重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:120℃、重量平均分子量:5万)60重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体10重量%、ポリカーボネート23重量%、およびスチレン−N−フェニルマレイミド−無水マレイン酸7重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−無水マレイン酸2重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:120℃、重量平均分子量:5万)60重量%、メチルメタクリレート−ブタジエン−スチレングラフト共重合体10重量%、ポリカーボネート23重量%、およびスチレン−アクリロニトリル−N−フェニルマレイミド7重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−無水マレイン酸2重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:95℃、重量平均分子量:5万)50重量%、アクリロニトリル−ブタジエン−スチレングラフト共重合体20重量%、およびアクリロニトリル−α−メチルスチレン30重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−グリシジルメタクリレート0.5重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、テレフタル酸−イソソルビド−1,4−シクロヘキサンジオール−エチレングリコール共重合体ポリエステル(Tg:110℃、重量平均分子量:5万)50重量%、アクリロニトリル−ブタジエン−スチレングラフト共重合体20重量%、およびアクリロニトリル−α−メチルスチレン30重量%からなる樹脂100重量%に対して、アクリロニトリル−スチレン−グリシジルメタクリレート0.5重量%、フェノール系1次酸化安定剤、ホスファイト系2次酸化安定剤をそれぞれ0.2重量%添加し、均一に混練押出を行ってペレットを製造した。
二軸混練押出機(Φ:40mm、L/D=40)を用いて、下記表4の組成で成分をそれぞれ添加した後、均一に混練押出を行ってペレットを製造した。
前記実施例1乃至15、および比較例1乃至5によって製造されたペレットを射出機を用いて射出温度250℃で同一に射出した後、射出された試験片を23±2℃、50±5%相対湿度条件下で状態調節を行い、下記のように機械的物性を測定した。測定結果を下記表1乃至4に示した。
ASTM D 256に基づいて、測定用試片を製作し、アイゾッド衝撃試験機(Impact Tester、Toyoseiki)を用いて衝撃強度値を測定した。
ASTM D 638に基づいて、測定用試片を製作し、万能材料試験機(Universal Testing Machine、Zwick Roell Z010)を用いて引張強度、伸び率を測定した。
ASTM D 790に基づいて、測定用試片を製作し、万能材料試験機(Universal Testing Machine、Zwick Roell Z010)を用いて屈曲強度、屈曲弾性率を測定した。
ASTM D 648に基づいて、測定用試片を製作し、耐熱度試験機(HDT Tester、Toyoseiki)を用いて耐熱性を測定した。
ASTM D1238に基づいて、測定用試片を製作し、溶融指数試験機(Melt Flow Indexer、Davenport)を用いて溶融指数を測定した。
−PLA:米国のNatureWorks LLC社のポリ乳酸樹脂3001D
−PLLA:米国のNatureWorks LLC社のL型ポリ乳酸樹脂Ingeo3251D
−PDLA:オランダのPurac社のポリ乳酸樹脂
−PP:湖南石油化学のポリプロピレンブロック共重合体
−PC:底粘度ポリカーボネート樹脂
−PEエラストマー:ポリオレフィン系エラストマー
−ABS:アクリロニトリル−ブタジエン−スチレン系グラフト共重合体
−SAN:スチレン−アクリロニトリル樹脂
−SMMA:メチルメタクリレート−アクリロニトリル−スチレン系共重合体
−PET:ポリエチレンテレフタレート樹脂
−MA系相溶化剤:無水マレイン酸グラフトエチレン−オクテン共重合体
−PLA−g−MA:無水マレイン酸グラフトポリ乳酸樹脂
−PE−GMA:米国のAldrich社のポリエチレン−グリシジルメタクリレート樹脂
−PP−g−MA:湖南石油化学社のポリプロピレン−無水マレイン酸グラフト共重合体
−Nano−Clay:米国のSouthern Clay Products社の有機化クレイCloisite20A
−トリアリールイソシアネート:日本の東京化学産業社のトリアリールイソシアネート
−Talc:Koch社のKC−3000
−MMA−Talc:メチルメタクリレートでコーティングされたTalc
−HI−WAX:日本のMitsui Chemicals社の低分子量ポリエチレン200P
−I−245:松原産業社のヒンダードフェノール系酸化防止剤Irganox245。
Claims (18)
- テレフタル酸を含むジカルボン酸成分の残基と、ジアンヒドロヘキシトールを含むジオール成分の残基を含むポリエステル共重合体;
不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体、アルキルメタクリレート−ジエン系ゴム−芳香族ビニルグラフト共重合体、およびアルキルメタクリレート−シリコン/アルキルアクリレートグラフト共重合体からなる群より選択される1種以上の共重合体;
ポリカーボネートを、前記ポリエステル共重合体、前記不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体、アルキルメタクリレート−ジエン系ゴム−芳香族ビニルグラフト共重合体、およびアルキルメタクリレート−シリコン/アルキルアクリレートグラフト共重合体からなる群より選択される1種以上の共重合体、および前記ポリカーボネートの合計量に対して5乃至90重量%;および
不飽和ニトリル−芳香族ビニル−グリシジルメタクリレート相溶化剤、および不飽和ニトリル−芳香族ビニル−無水マレイン酸相溶化剤からなる群から選択される1種以上を含み、
前記ポリエステル共重合体のガラス転移温度が130℃以下である、
高分子樹脂組成物。 - 前記ポリエステル共重合体5乃至90重量%、前記不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体、アルキルメタクリレート−ジエン系ゴム−芳香族ビニルグラフト共重合体、およびアルキルメタクリレート−シリコン/アルキルアクリレートグラフト共重合体からなる群より選択される1種以上の共重合体1乃至80重量%を含む請求項1に記載の高分子樹脂組成物。
- 芳香族ビニル−芳香族マレイミド−無水マレイン酸共重合体、芳香族ビニル−不飽和ニトリル−芳香族マレイミド共重合体、芳香族ビニル−α−メチル芳香族ビニル共重合体、および芳香族ビニル−不飽和ニトリル−α−メチル芳香族ビニル共重合体からなる群より選択される一つ以上をさらに含む請求項1に記載の高分子樹脂組成物。
- 前記ポリエステル共重合体は、重量平均分子量が10,000乃至100,000であり、ガラス転移温度が0乃至200℃である請求項1に記載の高分子樹脂組成物。
- 前記ポリエステル共重合体において、ジカルボン酸成分は、炭素数8乃至20の芳香族ジカルボン酸、および炭素数4乃至20の脂肪族ジカルボン酸からなる群より選択される1種以上をさらに含む請求項1に記載の高分子樹脂組成物。
- 前記ポリエステル共重合体において、ジアンヒドロヘキシトールは、イソソルビドである請求項1に記載の高分子樹脂組成物。
- 前記ポリエステル共重合体において、ジアンヒドロヘキシトールの含量は、全体ジオール成分の含量に対して5乃至60モル%である請求項1に記載の高分子樹脂組成物。
- 前記ポリエステル共重合体において、ジオール成分は、1,4−シクロヘキサンジオールおよびエチレングリコールをさらに含む請求項1に記載の高分子樹脂組成物。
- 前記不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体は、コア−シェルゴム(Core−Shell Rubber)形態で、平均粒子径が0.01乃至5μmであり、グラフト率が5乃至90%であり、コア(Core)のガラス転移温度が−20℃以下であり、シェル(Shell)のガラス転移温度が20℃以上である請求項1に記載の高分子樹脂組成物。
- 前記不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体において、不飽和ニトリルは、アクリロニトリル、メタクリロニトリル、エタクリロニトリル、フェニルアクリロニトリル、およびα−クロロアクリロニトリルからなる群より選択される1種以上である請求項1に記載の高分子樹脂組成物。
- 前記グラフト共重合体において、ジエン系ゴムは、ブタジエン系ゴムまたはイソプレン系ゴムである請求項1に記載の高分子樹脂組成物。
- 前記グラフト共重合体において、芳香族ビニルは、スチレン、α−メチルスチレンビニルトルエン、t−ブチルスチレン、ハロゲン置換スチレン、1,3−ジメチルスチレン、2,4−ジメチルスチレン、およびエチルスチレンからなる群より選択される1種以上である請求項1に記載の高分子樹脂組成物。
- 前記不飽和ニトリル−ジエン系ゴム−芳香族ビニルグラフト共重合体は、アクリロニトリル−ブタジエン−スチレングラフト共重合体である請求項1に記載の高分子樹脂組成物。
- 前記アルキルメタクリレート−ジエン系ゴム−芳香族ビニルグラフト共重合体は、メチルメタクリレート−ブタジエン−スチレングラフト共重合体である請求項1に記載の高分子樹脂組成物。
- 前記アルキルメタクリレート−シリコン/アルキルアクリレートグラフト共重合体は、メチルメタクリレート−シリコン/ブチルアクリレートグラフト共重合体である請求項1に記載の高分子樹脂組成物。
- 前記ポリカーボネートは、ガラス転移温度が50乃至200℃であり、重量平均分子量が10,000乃至200,000である請求項1に記載の高分子樹脂組成物。
- 酸化防止剤、滑剤、光安定剤、光吸収剤、トランスエステル化反応抑制剤、および耐加水分解剤からなる群より選択される1種以上の添加剤をさらに含む請求項1に記載の高分子樹脂組成物。