JP6087064B2 - 金属の防食処理方法 - Google Patents
金属の防食処理方法 Download PDFInfo
- Publication number
- JP6087064B2 JP6087064B2 JP2012117670A JP2012117670A JP6087064B2 JP 6087064 B2 JP6087064 B2 JP 6087064B2 JP 2012117670 A JP2012117670 A JP 2012117670A JP 2012117670 A JP2012117670 A JP 2012117670A JP 6087064 B2 JP6087064 B2 JP 6087064B2
- Authority
- JP
- Japan
- Prior art keywords
- base material
- metal base
- metal
- concentration
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
実施例1では、チタン合金からなる金属母材と炭素繊維強化樹脂とを接着剤で接合した接合体の金属母材に、金属母材のイオン化傾向よりも大きいイオン化傾向を有する金属であるマグネシウム合金製の板を犠牲金属部材として接着剤で取り付けて、野外暴露した。
実施例2では、実施例1における板状の犠牲金属部材をマグネシウム合金製のねじに代えて、同様に野外暴露した。実施例2においても、目視により接合体を観察したところ、犠牲金属となるマグネシウム合金製のねじに腐食は生じたが、2年経過しても金属母材には腐食が生じなかった。
実施例3では、マグネシウムからなる金属母材と炭素繊維強化樹脂とを接着剤で接合した接合体の金属母材に、市販のステンレス製のねじと、マグネシウム製のねじを離して絶縁した状態で取り付けた。実施例3では、金属母材にステンレス製のねじをねじ込むことによってねじの表面の被膜が破れてしまい、金属母材と導通し、ステンレス製のねじの周囲では金属母材の腐食が生じた。一方、マグネシウム製のねじは、目視により観察したところ、腐食が生じたが、1年経過してもマグネシウム製のネジの周囲では金属母材の腐食は生じなかった。
実施例4では、金属母材として鉄合金を用いた以外は実施例1と同様に接合体を野外暴露した。実施例4においても、目視により接合体を観察したところ、犠牲金属となるマグネシウム合金は少し緩やかな腐食ではあったが、1年経過しても鉄合金からなる金属母材には腐食が生じなかった。
実施例5では、鉄合金の金属母材に、犠牲金属として電気めっき法によりカルシウムめっき膜を形成した。そして、めっき膜を形成した金属母材と、炭素繊維強化樹脂とを接着剤で接合した接合体を野外暴露した。カルシウムめっき膜の膜厚は、5μmとした。
実施例6では、金属母材にチタン合金を用いたこと以外は実施例5と同様にして接合体を作製し、接合体を野外暴露した。カルシウムめっき膜の膜厚は、5μmであり、めっき液及びめっき条件も実施例5と同様である。実施例6においても、1年経過しても接合体の金属母材に腐食は見られなかった。
実施例7では、金属母材に犠牲金属のバリウムめっき膜を形成したこと以外は実施例5と同様に接合体を作製し、接合体を野外暴露した。
実施例8では、金属母材にチタン合金を用いたこと以外は実施例7と同様に接合体を作製し、接合体を野外暴露した。実施例8では、1年経過しても接合体の金属母材に腐食は見られなかった。
実施例9では、金属母材にアルミニウム合金を用い、この金属母材に実施例7と同様にしてバリウムめっき膜を形成し、続けてバリウムめっき膜上に、実施例5と同様にしてカルシウムめっき膜を形成し、炭素繊維強化樹脂と接着剤で接合した接合体を作製し、接合体を野外暴露した。実施例9においても、金属母材に腐食は見られなかった。
Claims (2)
- 炭素繊維強化樹脂と接合される金属母材の腐食を防止する金属の防食処理方法であって、
上記金属母材よりもイオン化傾向が大きいカルシウムのめっき膜を上記金属母材に成膜し、
上記カルシウムのめっき膜を成膜する際のめっき液は、塩化カルシウムの濃度が200〜800g/L、メチルアルコール及びジエチレングリコールの濃度がそれぞれ100〜800mL/L、トリメチルアミン塩酸塩又はm−フェニレンジアミン硫酸塩の濃度が0.5〜5g/L、クエン酸ナトリウム、クエン酸カリウム、酒石酸ナトリウム、酒石酸カリウムのいずれかの濃度が5〜10g/Lとなるように調整した水溶液に、pHが10〜14となるように炭酸カルシウム又はカセイソーダを添加した水溶液であることを特徴とする金属の防食処理方法。 - 炭素繊維強化樹脂と接合される金属母材の腐食を防止する金属の防食処理方法であって、
上記金属母材よりもイオン化傾向が大きいバリウムのめっき膜を上記金属母材に成膜し、
上記バリウムのめっき膜を成膜する際のめっき液は、塩化バリウムの濃度が150〜800g/L、イソプロピルアルコールの濃度が12〜60mL/L、エチルアルコールの濃度が20〜80mL/L、トリメチルアミン塩酸塩又はm−フェニレンジアミン硫酸塩の濃度が0.5〜5g/L、クエン酸ナトリウム、クエン酸カリウム、酒石酸ナトリウム、酒石酸カリウムのいずれかの濃度が5〜10g/Lとなるように調整した水溶液に、pHが10〜14となるように炭酸カルシウム又はカセイソーダを添加した水溶液であることを特徴とする金属の防食処理方法。