JP5894451B2 - 消臭機能付きシート - Google Patents
消臭機能付きシート Download PDFInfo
- Publication number
- JP5894451B2 JP5894451B2 JP2012022314A JP2012022314A JP5894451B2 JP 5894451 B2 JP5894451 B2 JP 5894451B2 JP 2012022314 A JP2012022314 A JP 2012022314A JP 2012022314 A JP2012022314 A JP 2012022314A JP 5894451 B2 JP5894451 B2 JP 5894451B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- fine particles
- deodorizing function
- particles
- tungsten oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
また、光触媒は、光を照射することにより有機物を分解する機能を有し、抗菌・抗ウイルス性といった効果が期待されている材料であり、酸化チタン光触媒が一部実用化されている。ただし、酸化チタンからなる光触媒は紫外線でしか励起されないため、紫外線が少ない屋内環境では十分な性能が得られない。その対策として、可視光でも性能を発揮する白金化合物を担持した酸化チタン、窒素や硫黄をドープした酸化チタン等の可視光応答型光触媒が開発されている。しかし、酸化チタンをベースにした可視光応答型光触媒は励起波長の範囲が狭く、一般的な屋内照明のように低い照度の下では十分な性能が得られていない。
本発明の目的は、上記問題を解決し、様々な臭いに対して、消臭機能を持つ実用的なシートを提供することにある。
一次粒子径が10μmを超える場合やBET比表面積が0.08m2/g未満の場合は、粒径が大きすぎ、均一な反応が得られず十分な消臭性能が得られない可能性がある。一方、酸化タングステン微粒子の平均一次粒径が1nm未満の場合やBET比表面積が820m2/gを超える場合には、粒子が小さくなりすぎて、塩基性物質との反応の際に反応点が多すぎ、粒子がすぐにイオン化してしまい、中和による消臭効果が消失しやすいことと、取扱い性(粉末としての取扱い性)が劣るため、実用性が低下する。
平均一次粒子径はSEMやTEM等の写真の画像解析から、n=50個以上の粒子の体積基準の積算径における平均一次粒子径(D50)に基づいて求めるものとする。平均一次粒子径(D50)は比表面積から換算した平均一次粒子径と一致していてもよい。
光触媒としての機能と固体酸としての機能をそれぞれ長期間発揮するためには、酸化タングステン系微粒子の一次粒子径のうち40nm以下の大きさである粒子が15質量%以上含まれ、かつ、100nm以上の大きさの粒子が15質量%以上含まれることが好ましい。
5cm×10cmのガラス試験片に上記粒子を0.2g付着させて、JIS−R−1701−1(2004)の窒素酸化物の除去性能(分解能力)評価に準じる流通式装置に試料を入れた状態で、初期濃度10ppmのアセトアルデヒドガスを140mL/minで流して測定したガス濃度において、光照射前のガス濃度をA、光照射から15分以上経過し、かつ安定したときのガス濃度をBとし、前記ガス濃度Aと前記ガス濃度Bから[式:(A−B)/A×100]に基づいて算出した値をガス分解率(%)としたとき、白色蛍光灯を使用し、紫外線カットフィルタを用い、波長が380nm以上のみの光で照度が6000lxあるいは1000lxの可視光を照射した際の前記ガス分解率を評価する。
消臭シートにおいて、酸化タングステン系微粒子の6000lxの光照射の時のガス分解率が10%以上の性能を有している粒子を具備することを特徴とする。さらに、より高い消臭効果を発揮させるためには、1000lxの光照射のときのガス分解率が2%以上の性能を有している微粒子を具備することが好ましい。
またこれら微粒子は光触媒としての機能を有し、臭い成分、細菌類、ウイルス類を分解することができる。
まず微粒子を水等の分散媒と混合し、超音波分散機、湿式ジェットミル、ビーズミル等により分散処理を行って分散液を作製する。得られた分散液をガラス板等の試験片に、滴下、スピンコート、ディップ、スプレー等の一般的な方法で塗布して試料を作製する。このような試料を用いてガス分解性能を評価する。酸化タングステン系微粒子が光触媒性能を有する場合、試験片の表面に塗布した状態で光触媒性能を発揮させるために、分散処理で粉末に歪を与えすぎないような条件を設定することが好ましい。
天然繊維としては、綿、麻、パルプ等のセルロース系繊維あるいは植物繊維、毛、絹などの動物繊維のいずれでも良いが、綿が好適である。
また、合繊繊維としては、ポリアミド系、ポリエステル系、ポリオレフィン系、ポリアクリロニトリル系、ポリウレタン系繊維等が上げられるが、ポリオレフィン系、ポリエス
テル系繊維が好適である。中でもポリプロピレン繊維、ポリエチレン繊維、ポリエチレン
テレフタレート繊維、ポリブチレンテレフタレート繊維が好ましい。
また、レーヨン、アセテート等の再生、半合成繊維などを使用できるが、レーヨンも好適である。
また、基材の形態は、織物でも不織布でも良い。不織布の場合の製法は、スパンポンド法、メルトブロー法、ポイントボイド法、乾式又は湿式法など任意に選定できる。
このようなシートの消臭性能を評価する場合には、当該シートから切り出した試験片を用いて評価試験を実施する。
酸化タングステン系微粒子を所定量固着させたシートを5cm×5cmに切り出し、このシートにアンモニア3%溶液(尿に含まれるアンモニア濃度の約10倍)を0.1cc(NH3:1.9×10−4mol)滴下し、直後のニオイを人間の官能試験により臭気強度で判定する。臭気強度の判定方法は、周囲には同様のニオイが発生しない場所で、アンモニア滴下後20秒以内に臭いを嗅ぎ、臭気強度を0〜5の間で、0.5刻みで判定する。判定者は6名以上とし、判定者中の最大と最小を除き、残りを平均する。平均した数値の小数点以下が0.25〜0.75の場合は0.5、0〜0.25、0.75〜1の場合は整数とする。このときに臭気強度が0〜1になるような性能を持つことが好ましい。さらに0〜0.5になることがより好ましい。本実施形態のシートは、臭気強度が0〜1、あるいは、0〜0.5という高い性能を有する。
ここで、消臭性能を有するシートに照射する光としては、上記した白色蛍光灯の光のみならず、太陽光、白色LED、電球、ハロゲンランプ、キセノンランプ等の一般照明、青色発光ダイオード、青色レーザ等を光源とする光であってもよい。さらに、消臭性能を有するシートは照度の高い可視光を照射することで、より高い消臭性能を発揮させることが可能となる。
ラズマ処理、アーク放電処理、レーザ処理、電子線処理、およびガスバーナー処理から選
ばれる少なくとも1種の処理が挙げられる。これらのうち、レーザ処理や電子線処理では
レーザまたは電子線を照射して昇華工程を行う。レーザや電子線は照射スポット径が小さ
いため、一度に大量の原料を処理するためには時間がかかるものの、原料粉の粒径や供給
量の安定性を厳しく制御する必要がないという長所がある。
間は10分〜16時間とすることが好ましく、さらに好ましくは30分〜7時間である。熱処理工程の温度および時間を上記範囲内にすることによって、三酸化タングステン以外の酸化タングステンから三酸化タングステンを形成しやすい。また、欠陥が少ない結晶性の良い粉末を得るためには、熱処理時の昇温や降温を緩やかに実施することが好ましい。熱処理時の急激な加熱や急冷は結晶性の低下を招くことになる。
粉末を三酸化タングステンにするための酸化効果を十分に得ることができない恐れがある。熱処理温度が1000℃を超えると酸化タングステン微粒子が急激に粒成長するため、酸化タングステン微粉末の粒径、比表面積のコントロールがしにくい。さらに、上記したような温度と時間で熱処理工程を行うことによって、三酸化タングステン微粉末の結晶構造や結晶性を調整することが可能となる。
次に、本発明の具体的な実施例およびその評価結果について述べる。粉末の製造方法と
して、タングステン酸アンモニウム塩を用いる、あるいは、昇華工程に誘導結合型プラズ
マ処理を適用しているが、本発明は、これに限定されるものではない。
平均一次粒子径はTEM写真の画像解析によって測定した。TEM観察には日立社製H−7100FAを使用し、拡大写真を画像解析にかけて粒子50個以上を抽出し、体積基準の積算径を求めてD50を算出した。また、40nm以下の大きさの粒子あるいは、100m以上の大きさの粒子の累積頻度から体積基準での含有比率を算出した。
BET比表面積の測定は、マウンテック社製比表面積測定装置Macsorb1201を用いて行った。前処理は窒素中にて200℃×20分の条件で実施した。
シートにおける酸化タングステン系微粒子の凝集体の平均粒径(D50)は、SEM等の写真の画像解析から、n=50個以上の粒子の体積基準の積算径における平均一次粒子径(D50)に基づいて求めた。
ニオイセンサー(新コスモス電機社製XP−329m)を用いて、滴下後30秒後のニオイセンサーによる強度測定を行った。測定時には周囲の環境のセンサー値も読み取り、環境の影響ではないことを確認している。
試験評価に用いた基材は、主にレーヨンの不織布である。酸化タングステン系微粒子の水分散液にSiO2バインダを含有させた液を用いて、含浸法によりシートを作製し、評価を行ったが、木綿布やポリエステル不織布を用いた場合でも同様の効果が得られており、基材や固着方法によらず、同様に消臭性能が得られることを確認した。このため、本発明は、これに限定されるものではない。
一方、固着量が少ない物は、充分なアンモニア消臭効果が確認できなかった。また、固着量が多いものは、消臭性能が高かったが、意匠性や触感が悪かった。
40nm以下の粒子が15質量%以上、かつ100nm以上の粒子が15質量%の含有した微粒子の場合、光触媒による分解性能もアンモニア消臭性能も非常に高く、かつ、繰り返し使用での高い効果が認められた。
タングステン複合材微粒子を含有させ、これらを塗布したところ、消臭効果を示すだけでなく、ウイルスの低減、菌やカビの発生を低減することができることが確認された。従って、このような消臭材料を適用することで、実用的な消臭、抗菌、抗ウイルス性能を長期間発揮するシートを提供することが可能となる。
Claims (10)
- 固体で酸性を示す固体酸である酸化タングステン微粒子あるいは酸化タングステン複合材微粒子から選ばれる少なくとも1種の粒子を具備するシートであって、前記微粒子の一次粒子径のうち、40nm以下の大きさである粒子が15質量%以上含まれ、かつ100nm以上の粒子が15質量%以上含まれていることを特徴とする消臭機能を有するシート。
- 請求項1記載の消臭機能を有するシートにおいて、前記微粒子の固着量が0.1〜50g/m2であることを特徴とする消臭機能を有するシート。
- 請求項1または2のいずれか1項記載の消臭機能を有するシートにおいて、前記微粒子の平均一次粒径(D50)が1nm以上10μm以下の範囲であることを特徴とする消臭機能を有するシート。
- 請求項1ないし3のいずれか1項記載の消臭機能を有するシートにおいて、前記微粒子のBET比表面積が0.08m2/g以上820m2/g以下の範囲の微粒子を含むことを特徴とする消臭機能を有するシート。
- 請求項1ないし4のいずれか1項記載の消臭機能を有するシートにおいて、前記微粒子が形成する凝集体の平均粒径(D50)が、0.05μm以上100μm以下の範囲であることを特徴とする消臭機能を有するシート。
- 請求項1ないし5のいずれか1項記載の消臭機能を有するシートにおいて、前記微粒子が可視光応答型光触媒粉末であって、JIS−R−1701−1(2004)の窒素酸化物の除去性能(分解能力)評価に準じる流通式装置に0.2gの試料を入れた状態で、初期濃度10ppmのアセトアルデヒドガスを140mL/minで流して測定したガス濃度において、光照射前のガス濃度をA、光照射から15分以上経過し、かつ安定したときのガス濃度をBとし、前記ガス濃度Aと前記ガス濃度Bから[式:(A−B)/A×100]に基づいて算出した値をガス分解率(%)としたとき、白色蛍光灯を使用し、紫外線カットフィルタを用い、波長が380nm以上のみの光で照度が6000lxの可視光を照射した際の前記ガス分解率が10%以上の性能を有する粉末を具備することを特徴とする消臭機能を有するシート。
- 請求項1ないし5のいずれか1項記載の消臭機能を有するシートにおいて、前記微粒子が可視光応答型光触媒粉末であって、JIS−R−1701−1(2004)の窒素酸化物の除去性能(分解能力)評価に準じる流通式装置に0.2gの試料を入れた状態で、初期濃度10ppmのアセトアルデヒドガスを140mL/minで流して測定したガス濃度において、光照射前のガス濃度をA、光照射から15分以上経過し、かつ安定したときのガス濃度をBとし、前記ガス濃度Aと前記ガス濃度Bから[式:(A−B)/A×100]に基づいて算出した値をガス分解率(%)としたとき、白色蛍光灯を使用し、紫外線カットフィルタを用い、波長が380nm以上のみの光で照度が1000lxの可視光を照射した際の前記ガス分解率が2%以上の性能を有する粉末を具備することを特徴とする消臭機能を有するシート。
- 請求項1ないし7のいずれか1項記載の消臭機能を有するシートにおいて、シート基材が木綿繊維、レーヨンなどのセルロース系繊維、あるいは、ポリプロピレン繊維から選ばれる少なくとも1種の繊維を含むことを特徴とする消臭機能を有するシート。
- 請求項8項記載の消臭機能を有するシートにおいて、シートの基材が不織布であることを特徴とする消臭機能を有するシート。
- 請求項1ないし9のいずれか1項記載の消臭機能を有するシートにおいて、基材が複数の繊維を積層する構造であり、前記微粒子が表面から2層目以上内部の層に具備されていることを特徴とする消臭機能を有するシート。