JP5642384B2 - 造粒シリカ粒子、複合粉体およびこれらの製造方法並びにこれらを含有する化粧料 - Google Patents
造粒シリカ粒子、複合粉体およびこれらの製造方法並びにこれらを含有する化粧料 Download PDFInfo
- Publication number
- JP5642384B2 JP5642384B2 JP2009509131A JP2009509131A JP5642384B2 JP 5642384 B2 JP5642384 B2 JP 5642384B2 JP 2009509131 A JP2009509131 A JP 2009509131A JP 2009509131 A JP2009509131 A JP 2009509131A JP 5642384 B2 JP5642384 B2 JP 5642384B2
- Authority
- JP
- Japan
- Prior art keywords
- composite powder
- water
- skin
- powder
- silica
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
造粒シリカ粒子の製造
シラノール基密度が60μmol/m2である鱗片状シリカの15%濃度水性溶媒コロイド懸濁物(サンラブリー−LFS−C;旭硝子エスアイテック社製)を原料スラリーとした。このものを、噴霧装置としてディスク式アトマイザーを持つスプレードライヤー(L−8型;大川原化工機社製)を用い、アトマイザー回転数30000rpm、流量50ml/min、入口温度設定200℃、出口温度設定130〜140℃の条件で噴霧乾燥した。
シラノール基密度が8.0μmol/m2、平均粒子径が12μmである球状シリカを精製水に分散した15%濃度のスラリーを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用い、実施例1と同様の条件で噴霧乾燥した。乾燥物を走査型電子顕微鏡で観察した結果、12μmの球状粒子は、一部が凝集する集合体として存在するのみで、造粒粒子は得られなかった。
シラノール基密度が7.0μmol/m2、平均粒子径が25μmである鱗片状シリカを精製水に分散した15%濃度のスラリーを、噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用い、実施例1と同様の条件で噴霧乾燥した。乾燥物を走査型電子顕微鏡で観察した結果、上記鱗片状シリカは、一部が凝集する集合体として存在するのみで、造粒粒子は得られなかった。
固形粉末状ファンデーション(乾使用専用):
実施例1で得た造粒シリカ及び比較例1〜2で得た乾燥物を用い、表1に示す組成および下記製法で固形粉末状ファンデーションを調製した。
A.成分1〜12をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分13〜16を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状ファンデーション(乾使用専用)を得た。
化粧品評価専門パネル20名に、各固形粉末状ファンデーションを使用してもらい、「滑らかな伸び広がり」および「均一な化粧膜の形成」の項目について各自が以下の評価基準に従って各サンプルを7段階評価した。サンプル毎に付された評点について、全パネルの評点の平均点を求め、以下の判定基準に従って判定した。
( 評価 ) ( 内 容 )
6 : 非常に良い
5 : 良い
4 : やや良い
3 : 普通
2 : やや悪い。
1 : 悪い。
0 : 非常に悪い。
判定基準:
( 評点の平均点 ) ( 評 価 )
5.0以上 : ◎(非常に良好)
3.5以上5.0未満 : ○(良好)
1.0以上3.5未満 : △(普通)
1.0未満 : ×(不良)
固形粉末状フェイスカラー
下記成分および製造方法により、固形粉末状フェイスカラーを調製した。
A.成分1〜8をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分9、10を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状フェイスカラーを得た。
固形粉末状アイシャドウ
下記成分および製造方法により、固形粉末状アイシャドウを調製した。
1.ジメチルポリシロキサン処理合成金マイカ 10.0
2.ジメチルポリシロキサン処理タルク 残量
3.酸化チタン被覆雲母 30.0
4.窒化ホウ素 5.0
5.ポリエチレンテレフタレート・アルミニウム・エポキシ積層末 5.0
6.実施例1の造粒シリカ粒子 20.0
7.群青 2.0
8.黄色401号 0.5
9.架橋型シリコーン・網状シリコーン共重合体 1.0
10.パラオキシ安息香酸メチル 0.2
11.流動パラフィン 2.0
12.ワセリン 1.0
13.ジメチルポリシロキサン 3.0
14.香料 適量
A.成分1〜10をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分11〜14を加熱し、均一分散する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状アイシャドウを得た。
固形粉末状ファンデーション(水使用専用)
下記成分および製造方法により、固形粉末状ファンデーションを調製した。
A.成分1〜10をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分11〜15を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状ファンデーション(水使用専用)
を得た。
オイルクレンジング
下記成分および製造方法により、オイルクレンジングを調製した。
A.成分1〜10を均一に混合する。
B.Aに11を徐々に添加し、均一に混合することで、オイルクレンジングを得た。
油中水型日焼け止めクリーム
下記成分および製造方法により、油中水型日焼け止めクリームを調製した。
注2:KF−6028(信越化学工業社製)
注3:KF96A−2cs(信越化学工業社製)
注4:KF−7312J(信越化学工業社製)
注5:レオパールISK(千葉製粉社製)
A:成分1〜3をビーズミル処理して均一に分散する。
B:成分4〜10を70℃で加温溶解し、Aを添加して均一に混合溶解する。
C:成分11〜14及び成分17を混合溶解する。
D:BにCを添加しながら乳化後、冷却する。
E:Dに成分15、16を添加して均一に混合して、油中水型日焼け止めクリームを得た。
二層ローション
下記成分および製造方法により、二層ローションを調製した。
A.成分5〜7を均一に混合する。
B.成分1〜4を混合し、Aに均一分散する。
C.成分8〜13を混合後、Bに均一に混合し、二層ローションを得た。
液状洗浄料
下記成分および製造方法により、液状洗浄料を調製した。
A.成分6〜8を70℃で均一に混合した後、12の一部を添加し、乳化する。その
後、室温まで冷却する。
B.成分1〜5および12の残部を均一に混合する。
C.BにAを加え、均一に混合する。
D.Cに成分9、10を加え、均一に混合する。
E.Dに11、13を添加し、均一に混合し、液状洗顔料を得た。
水中油型乳化ファンデーション
下記成分および製造方法により、水中油型乳化ファンデーションを調製した。
A:成分1〜3及び成分5、6を加えて75℃にて均一に加熱混合する。
B:成分4、8、9に成分15〜19を混合し、3本のローラーにて均一分散する。
C:Bに成分10〜14を加え、75℃にて均一に加熱混合する。
D:CにAを添加して、乳化する。
E:Dを冷却後、成分7を添加し、水中油型乳化ファンデーションを得た。
非水系マスカラ
下記成分および製造方法により、非水系マスカラを調製した。
A:成分1〜8を110℃にて均一に加熱溶解する。
B:成分9〜11を均一分散し、油性ゲルを得る。
C:AにBを加え、均一混合する。
D:Cに成分12、13を加え、均一混合する。
E:Dを3本ローラーにて処理する。
F:Eに成分14を加え、均一に混合する。
G:Fを容器に充填して、非水系マスカラを得た。
グリセリン内包複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカの15%濃度水性溶媒コロイド懸濁物(サンラブリー−LFS−C;旭硝子エスアイテック社製)95質量部に、グリセリン5.0質量部をデスパーミルにて均一に分散させ、スラリーとした。このものを噴霧装置としてディスク式アトマイザーを持つスプレードライヤー(L−8型;大川原化工機社製)を用い、アトマイザー回転数30000rpm、流量50ml/min、入口温度設定200℃、出口温度設定130〜140℃の条件で噴霧乾燥した。
1,3−ブチレングリコール内包複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカを精製水に分散した15%濃度のコロイド分散物94.5質量部に、1,3−ブチレングリコール5.4質量部とこれに溶解したアスコルビン酸0.1質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例12の条件にて噴霧乾燥した。
グリセリン内包複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカを精製水に分散した15%濃度のコロイド分散物90質量部に、グリセリン9.9質量部とこれに溶解した水溶性吸収剤であるフェニルベンズイミダゾールスルホン酸0.1質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例12の条件にて噴霧乾燥し、複合粉体を得た。
ジグリセリン内包複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカを精製水に分散した15%濃度のコロイド分散物90質量部に、ジグリセリン9.9質量部とこれに溶解したグリチルリチン酸ジカリウム0.1質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例12の条件にて噴霧乾燥し、複合粉体を得た。
比較複合粉体の製造:
シラノール基密度が8.0μmol/m2、粒子径が12μmである球状シリカを精製水に分散した15%濃度のコロイド分散物95質量部に、グリセリン5.0質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用い、実施例12の条件にて噴霧乾燥して複合粉体を得た。
比較複合粉体の製造:
シラノール基密度が7.0μmol/m2、粒子径が25μmである鱗片状シリカを精製水に分散した15%コロイド分散物95質量部に、グリセリン5.0質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用い、実施例12の条件にて噴霧乾燥して複合粉体を得た。
固形粉末状ファンデーション(乾使用専用):
表2に示す組成および下記製造方法により、固形粉末状ファンデーション(乾使用専用)を調製した。この固形粉末状ファンデーションについて、その「滑らかな伸び広がり」、「肌への密着性」、「肌への保湿感」について、以下に示す評価方法及び判断基準により評価した。この結果を併せて表2に示した。
A.成分1〜14をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分15〜19を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状ファンデーション(乾使用専用)
を得た。
化粧料評価専門パネル20名に前記の本発明品及び比較品の固形粉末状ファンデーション(乾使用専用)を使用してもらい、「滑らかな伸び広がり」「肌への密着性」「戸田への保湿感」について各自が以下の評価基準に従って、サンプル毎に7段階評価し評点を付した。更に全パネルの評点の平均点を求め、以下の判定基準に従って判定した。尚、「肌への保湿感」については、各専門パネルの、塗布直後の保湿感および塗布後3時間通常の生活を行った後の保湿感との総合評価とした。
(評 価) ( 内 容 )
6 : 非常に良い
5 : 良い
4 : やや良い
3 : 普通
2 : やや悪い。
1 : 悪い。
0 : 非常に悪い。
( 評点の平均点 ) ( 評 価 )
5.0以上 : ◎(非常に良好)
3.5以上5.0未満 : ○(良好)
1.0以上3.5未満 : △(普通)
1.0未満 : ×(不良)
固形粉末状フェイスカラー:
下記成分および製造方法により、固形粉末状フェイスカラーを調製した。
A.成分1〜8をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分9、10を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状フェイスカラーを得た。
固形粉末状アイシャドウ:
下記成分および製造方法により、固形粉末状アイシャドウを調製した。
A.成分1〜10をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分11〜14を加熱し、均一分散する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状アイシャドウを得た。
固形粉末状ファンデーション(水使用専用):
下記成分および製造方法により、固形粉末状ファンデーション(水使用専用)を調製した。
A.成分1〜10をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分11〜15を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状ファンデーション(水使用専用)を
得た。
オイルクレンジング
下記成分および製造方法により、オイルクレンジングを調製した。
A.成分1〜10を均一に混合する。
B.Aに11を徐々に添加し、均一に混合することで、オイルクレンジングを得た。
油中水型日焼け止めクリーム
下記成分および製造方法により、油中水型日焼け止めクリームを調製した。
注2:KF−6028(信越化学工業社製)
注3:KF96A−2cs(信越化学工業社製)
注4:KF−7312J(信越化学工業社製)
注5:レオパールISK(千葉製粉社製)
A:成分1〜3をビーズミル処理して均一に分散する。
B:成分4〜10を70℃で加温溶解し、Aを添加して均一に混合溶解する。
C:成分11〜14及び成分17を混合溶解する。
D:BにCを添加しながら乳化後、冷却する。
E:Dに成分15、16を添加して均一に混合して、油中水型日焼け止めクリームを得た。
二層ローション
下記成分および製造方法により、二層ローションを調製した。
A.成分5〜7を均一に混合する。
B.成分1〜4を混合し、Aに均一分散する。
C.成分8〜13を混合後、Bに均一に混合し、二層ローションを得た。
液状洗浄料
下記成分および製造方法により、液状洗浄料を調製した。
A.成分6〜8を70℃で均一に混合した後、12の一部を添加し、乳化する。その後、室温まで冷却する。
B.成分1〜5および12の残部を均一に混合する。
C.BにAを加え、均一に混合する。
D.Cに成分9、10を加え、均一に混合する。
E.Dに11、13を添加し、均一に混合し、液状洗顔料を得た。
水中油型乳化ファンデーション
下記成分および製造方法により、水中油型乳化ファンデーションを調製した。
A:成分1〜3及び成分5、6を加えて75℃にて均一に加熱混合する。
B:成分4、8、9に成分15〜19を混合し、3本のローラーにて均一分散する。
C:Bに成分10〜14を加え、75℃にて均一に加熱混合する。
D:CにAを添加して、乳化する。
E:Dを冷却後、成分7を添加し、水中油型乳化ファンデーションを得た。
非水系マスカラ
下記成分および製造方法により、非水系マスカラを調製した。
A:成分1〜8を110℃にて均一に加熱溶解する。
B:成分9〜11を均一分散し、油性ゲルを得る。
C:AにBを加え、均一混合する。
D:Cに成分12、13を加え、均一混合する。
E:Dを3本ローラーにて処理する。
F:Eに成分14を加え、均一に混合する。
G:Fを容器に充填して、非水系マスカラを得た。
スクワラン内包複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカの15%濃度水性溶媒コロイド懸濁物(サンラブリー−LFS−C;旭硝子エスアイテック社製)70質量部に、スクワラン30質量部をデスパーミルにて分散させ、スラリーとした。このものを噴霧装置としてディスク式アトマイザーを持つスプレードライヤー(L−8型;大川原化工機社製)を用い、アトマイザー回転数30000rpm、流量50ml/min、入口温度設定200℃、出口温度設定135〜140℃の条件で噴霧乾燥した。
2−エチルヘキサン酸グリセリル内包複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカを精製水に分散した15%濃度のコロイド分散物70質量部に、2−エチルヘキサン酸グリセリル29.8質量部と、これに溶解された天然ビタミンE0.1重量部およびグリチルリチン酸ステアリル0.1重量部をデスパーミルにて分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例26記載の条件にて噴霧乾燥した。
N−ラウロイル−L−グルタミン酸ジ(フィトステリル 2−オクチルドデシル)内包複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカを精製水に分散した15%濃度のコロイド分散物80質量部に、保湿剤であるN−ラウロイル−L−グルタミン酸ジ(フィトステリル 2−オクチルドデシル)20質量部をデスパーミルにて分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例25記載の条件にて噴霧乾燥し、複合粉体を得た。
パラメトキシケイ皮酸2−エチルヘキシル内包複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカを精製水に分散した15%濃度のコロイド分散物90質量部に、油溶性の紫外線吸収剤であるパラメトキシケイ皮酸2−エチルヘキシル10質量部をデスパーミルにて分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例26記載の条件にて噴霧乾燥し、複合粉体を得た。
比較複合粉体の製造:
シラノール基密度が8.0μmol/m2、粒子径が12μmである球状シリカを精製水に分散した15%濃度のコロイド分散物95質量部に、スクワラン5.0質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用い、実施例26記載の条件にて噴霧乾燥して複合粉体を得た。
比較複合粉体の製造:
シラノール基密度が7.0μmol/m2、粒子径が25μmである鱗片状シリカを精製水に分散した15%コロイド分散物95質量部に、スクワラン5.0質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例26記載の条件にて噴霧乾燥した。
固形粉末状ファンデーション(乾使用専用):
表3に示す組成および下記製造方法により、固形粉末状ファンデーション(乾使用専用)を調製した。この固形粉末状ファンデーションについて、その「滑らかな伸び広がり」、「肌への密着性」、「肌へのエモリエント感」、「ケーキングの防止効果」について、以下に示す評価方法及び判断基準により評価した。この結果を併せて表3に示した。
A.成分1〜15をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分16〜19を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状ファンデーション(乾使用専用)を得た。
「滑らかな伸び広がり」「肌への密着性」「肌へのエモリエント感」については、化粧料評価専門パネル20名に前記の本発明品及び比較品の固形粉末状ファンデーション(乾使用専用)を使用してもらい、各項目について各自が以下の評価基準に従ってサンプル毎に7段階評価し、評点を付した。更に全パネルの評点の平均点を求め、以下の判定基準に従って判定した。尚、「肌へのエモリエント感」については、各専門パネルの、塗布直後のエモリエント感および塗布後3時間通常の生活を行った後のエモリエント感との総合評価とした。
(評 価) ( 内 容 )
6 : 非常に良い
5 : 良い
4 : やや良い
3 : 普通
2 : やや悪い。
1 : 悪い。
0 : 非常に悪い。
( 評点の平均点 ) ( 評 価 )
5.0以上 : ◎(非常に良好)
3.5以上5.0未満 : ○(良好)
1.0以上3.5未満 : △(普通)
1.0未満 : ×(不良)
(評 価) ( 内 容 )
3 : 変化なし。
2 : 表面のてかりがあるが、使用性に問題なし。
1 : 顕著な表面のてかりがあり、使用性に問題あり。
( 評点の平均点 ) ( 評 価 )
2.5以上 : ◎
2.0以上〜2.5未満 : ○
1.5以上〜2.0未満 : △
1.5未満 : ×
固形粉末状フェイスカラー:
下記成分および製造方法により、固形粉末状フェイスカラーを調製した。
A.成分1〜8をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分9、10を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状フェイスカラーを得た。
固形粉末状アイシャドウ:
下記成分および製造方法により、固形粉末状アイシャドウを調製した。
A.成分1〜10をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分11〜14を加熱し、均一分散する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状アイシャドウを得た。
固形粉末状ファンデーション(水使用専用):
下記成分および製造方法により、固形粉末状ファンデーション(水使用専用)を調製した。
A.成分1〜10をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分11〜15を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状ファンデーション(水使用専用)を得た。
乳化組成物の製造:
下記成分、製造方法により乳化組成物を製造した。
A.成分1〜3を70℃にてデスパーで均一に分散する。
B.Aに70℃にて成分4を加え、均一に混合する。
C.75℃にてBに成分5を徐徐に加え、デスパーにて乳化し、乳化組成物を得た。
乳化組成物の製造:
下記成分、製造方法により乳化組成物を製造した。
A.成分1〜3を70℃にてデスパーで均一に分散する。
B.成分4〜8を70℃にて均一に分散する。
C.75℃にてAにBを徐徐に加え、デスパーにて乳化し、乳化組成物を得た。
乳化組成物の製造:
下記成分、製造方法により乳化組成物を製造した。
B.成分6〜9を70℃にて均一に分散する。
C.75℃にて、AにBを徐徐に加え、デスパーにて乳化し、乳化組成物を得た。
複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカを精製水に分散した15%コロイド分散物40質量部に、参考例1で得た乳化組成物60質量部を加え、デスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例26記載の条件にて噴霧乾燥した。
複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカを精製水に分散した15%コロイド分散物50質量部に、参考例2で得た乳化組成物50質量部をデスパーミルにてに分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例26記載の条件にて噴霧乾燥した。
複合粉体の製造:
シラノール基密度が60μmol/m2である鱗片状シリカを精製水に分散した15%コロイド分散物60質量部に、参考例3で得た乳化組成物40質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例26記載の条件にて噴霧乾燥した。
比較複合粉体の製造:
シラノール基密度が8.0μmol/m2、粒子径が12μmである球状シリカを精製水に分散した15%濃度のコロイド分散物90質量部に、参考例1の乳化組成物10質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例26記載の条件にて噴霧乾燥した。
比較複合粉体の製造:
シラノール基密度が7.0μmol/m2、粒子径が25μmである鱗片状シリカを精製水に分散した15%コロイド分散物90質量部に、参考例1の乳化組成物10質量部をデスパーミルにて均一に分散させる。これを噴霧装置としてディスク式アトマイザーを持つスプレードライヤーを用いて、実施例26記載の条件にて噴霧乾燥した。
固形粉末状ファンデーション(乾使用専用):
表4に示す組成および下記製造方法により、固形粉末状ファンデーション(乾使用専用)を調製した。この固形粉末状ファンデーションについて、その「滑らかな伸び広がり」、「肌への密着性」、「肌へのエモリエント感」および「ケーキング防止効果」について、以下に示す評価方法及び判断基準により評価した。この結果を併せて表4に示した。
A.成分1〜15をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分16〜23を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状ファンデーション(乾使用専用)を得た。
実施例30と同様にして、本発明品および比較品の固形粉末状ファンデーション(乾使用専用)を使用してもらい、「滑らかな伸び広がり」、「肌への密着性」、「肌へのエモリエント感」および「ケーキング防止効果」について評価した。
固形粉末状フェイスカラー:
下記成分および製造方法により、固形粉末状フェイスカラーを調製した。
A.成分1〜8をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分9、10を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状フェイスカラーを得た。
固形粉末状アイシャドウ:
下記成分および製造方法により、固形粉末状アイシャドウを調製した。
A.成分1〜10をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分11〜14を加熱し、均一分散する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状アイシャドウを得た。
固形粉末状ファンデーション(水使用専用):
下記成分および製造方法により、固形粉末状ファンデーション(水使用専用)を調製した。
A.成分1〜10をヘンシェルミキサー(三井三池社製)で均一に分散する。
B.成分11〜15を均一に混合する。
C.Aをヘンシェルミキサーで攪拌しながら、Bを添加し、均一分散する。
D.Cをパルベライザーで粉砕する。
E.Dを金皿に充填し、圧縮成形し、固形粉末状ファンデーション(水使用専用)を得た。
オイルクレンジング
下記成分および製造方法により、オイルクレンジングを調製した。
A.成分1〜10を均一に混合する。
B.Aに11を徐々に添加し、均一に混合することで、オイルクレンジングを得た。
油中水型日焼け止めクリーム
下記成分および製造方法により、油中水型日焼け止めクリームを調製した。
注2:KF−6028(信越化学工業社製)
注3:KF96A−2cs(信越化学工業社製)
注4:KF−7312J(信越化学工業社製)
注5:レオパールISK(千葉製粉社製)
A:成分1〜3をビーズミル処理して均一に分散する。
B:成分4〜10を70℃で加温溶解し、Aを添加して均一に混合溶解する。
C:成分11〜14及び成分17を混合溶解する。
D:BにCを添加しながら乳化後、冷却する。
E:Dに成分15、16を添加して均一に混合して、油中水型日焼け止めクリームを得た。
二層ローション
下記成分および製造方法により、二層ローションを調製した。
A.成分5〜7を均一に混合する。
B.成分1〜4を混合し、Aに均一分散する。
C.成分8〜13を混合後、Bに均一に混合し、二層ローションを得た。
液状洗浄料
下記成分および製造方法により、液状洗浄料を調製した。
A.成分6〜8を70℃で均一に混合した後、12の一部を添加し、乳化する。その後、室温まで冷却する。
B.成分1〜5および12の残部を均一に混合する。
C.BにAを加え、均一に混合する。
D.Cに成分9、10を加え、均一に混合する。
E.Dに11、13を添加し、均一に混合し、液状洗顔料を得た。
水中油型乳化ファンデーション
下記成分および製造方法により、水中油型乳化ファンデーションを調製した。
A:成分1〜3及び成分5、6を加えて75℃にて均一に加熱混合する。
B:成分4、8、9に成分15〜19を混合し、3本のローラーにて均一分散する。
C:Bに成分10〜14を加え、75℃にて均一に加熱混合する。
D:CにAを添加して、乳化する。
E:Dを冷却後、成分7を添加し、水中油型乳化ファンデーションを得た。
非水系マスカラ
下記成分および製造方法により、非水系マスカラを調製した。
A:成分1〜8を110℃にて均一に加熱溶解する。
B:成分9〜11を均一分散し、油性ゲルを得る。
C:AにBを加え、均一混合する。
D:Cに成分12、13を加え、均一混合する。
E:Dを3本ローラーにて処理する。
F:Eに成分14を加え、均一に混合する。
G:Fを容器に充填して、非水系マスカラを得た。
Claims (5)
- 一次粒子の厚みが0.001〜0.1μm、比表面積当たりのシラノール基(SiOH)が20〜70μmol/m2、平均二次粒子径が0.05〜5μm、厚さと最長粒子径とのアスペクト比が10以上である鱗片状シリカを構成要素として形成され、当該鱗片状シリカを、濃度7〜20質量%で水性溶媒中に分散してスラリー化し、これをスプレードライヤーにて噴霧乾燥することにより得られる平均粒子径が1〜50μmであり、圧縮強度が1〜4MPaである球状の造粒シリカ粒子を含有する化粧料。
- 一次粒子の厚みが0.001〜0.1μm、比表面積当たりのシラノール基(SiOH)が20〜70μmol/m2、平均二次粒子径が0.05〜5μm、厚さと最長粒子径とのアスペクト比が10以上である鱗片状シリカを構成要素として形成され、当該鱗片状シリカを、濃度7〜20質量%で水性溶媒中に分散してスラリー化し、これをスプレードライヤーにて噴霧乾燥することにより得られる平均粒子径が1〜50μmであり、圧縮強度が0.1〜3MPaである球状の造粒シリカ粒子中に水不溶性成分(但し、シリコン系化合物を除く)を内包せしめたことを特徴とする複合粉体。
- 複合粉体中に、水不溶性成分を5〜75%で含有する請求項2記載の複合粉体。
- 一次粒子の厚みが0.001〜0.1μm、比表面積当たりのシラノール基(SiOH)が20〜70μmol/m2、平均二次粒子径が0.05〜5μm、厚さと最長粒子径とのアスペクト比が10以上である鱗片状シリカを、水不溶性成分を乳化組成物として分散する水性溶媒中に加えてスラリー化した後、これをスプレードライヤーにて噴霧乾燥することにより得られる請求項2または3記載の複合粉体。
- 請求項2ないし4の何れかの項記載の複合粉体を含有する化粧料。