JP5607745B2 - 沈降炭酸マグネシウム - Google Patents
沈降炭酸マグネシウム Download PDFInfo
- Publication number
- JP5607745B2 JP5607745B2 JP2012537374A JP2012537374A JP5607745B2 JP 5607745 B2 JP5607745 B2 JP 5607745B2 JP 2012537374 A JP2012537374 A JP 2012537374A JP 2012537374 A JP2012537374 A JP 2012537374A JP 5607745 B2 JP5607745 B2 JP 5607745B2
- Authority
- JP
- Japan
- Prior art keywords
- magnesium oxide
- magnesium
- hydromagnesite
- carbonate
- suspension
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
Mg5(CO3)4(OH)2・4H2O
ハイドロマグネサイトは、炭酸マグネシウムの非常に特有の無機形であり、針状結晶または刃形結晶の小型針様結晶またはクラストとして自然に発生することが認識されるべきである。これに加えて、ハイドロマグネサイトは炭酸マグネシウムの特徴的で独自の形であり、炭酸マグネシウムの他の形とは化学的、物理的および構造的に異なることに注目すべきである。ハイドロマグネサイトは、他の炭酸マグネシウムからX線回折分析、熱重量分析または元素分析によって容易に区別することができる。ハイドロマグネサイトとして特に記載しない限り、他のすべての形の炭酸マグネシウム(例えばアルチナイト(Mg2(CO3)(OH)2・3H2O)、ダイピング石(Mg5(CO3)4(OH)2・5H2O)、ギオルギオサイト(Mg5(CO3)4(OH)2・5H2O)、ポクロブスカイト(Mg2(CO3)(OH)2・0.5H2O)、マグネサイト(MgCO3)、バリントナイト(MgCO3・2H2O)、ランスフォルダイト(MgCO3・5H2O)およびネスケホナイト(MgCO3・3H2O))は本発明の意味でのハイドロマグネサイトではなく、上記の式に化学的に一致しない。
a)少なくとも1つの酸化マグネシウム源を提供する段階;
b)ガス状CO2および/または炭酸塩を含むアニオンを提供する段階;
c)酸化マグネシウムを少なくとも部分的に水酸化マグネシウムに変換するための、段階a)の前記酸化マグネシウム源の消和段階;
d)水酸化マグネシウムを少なくとも部分的に沈降ネスケホナイトに変換するために、段階c)の得られた水酸化マグネシウムを段階b)の前記ガス状CO2および/または炭酸塩を含むアニオンと接触させる段階;および
e)段階d)で得られた沈降ネスケホナイトを加熱老化段階で処置する段階
を含む。
「ハイドロマグネサイト」、「塩基性炭酸マグネシウム」または「炭酸水酸化マグネシウム」は本発明の意味において、化学式Mg5(CO3)4(OH)2・4H2Oを有する、炭酸マグネシウムの合成的に調製された材料を定義する。
本発明の方法の段階a)により、少なくとも1つの酸化マグネシウム源が提供される。
酸化マグネシウム;および/または
酸化マグネシウムが自然に発生する材料;および/または
酸化マグネシウムに変換することができる少なくとも1つのマグネシウム化合物が発生する材料を指す。
本発明の方法の段階b)により、ガス状CO2および/または炭酸塩を含むアニオンが提供される。
本発明の方法の段階c)により、段階a)の前記少なくとも1つの酸化マグネシウム源は消和されて、酸化マグネシウムの少なくとも一部が水酸化マグネシウムに変換される。
本発明の方法の段階d)により、段階c)の前記得られた水酸化マグネシウムを段階b)の前記ガス状二酸化炭素および/または炭酸塩を含むアニオンと接触させて、少なくとも一部の水酸化マグネシウムを沈降ネスケホナイトに変換する。
本発明の方法の段階e)により、段階d)の前記得られた沈降ネスケホナイトを、ハイドロマグネサイトを得るために加熱老化によって処置する。
以下の測定方法は、実施例および請求項に与えるパラメータを評価するために使用される。
スラリーのBrookfield粘度は、LV−3スピンドルを装備したBrookfield粘度計RVT型によって、100rpmの速度および室温(20±3℃)にて決定した。
BET比表面積は、250℃にて30分の時間にわたって加熱することによる試料の調製後に、ISO4652によるBET法により測定した。このような測定の前に、試料を濾過して、すすぎ、乾燥器内で110℃にて少なくとも12時間乾燥させた。
微粒子材料の平均粒径および平均粒径質量分布は、レーザ回折、即ち懸濁物を通過するレーザからの光を介して決定され、および粒径分布は生じる回折パターンから計算される。測定はCILAS(フランス、オルレアン)の機器CILAS 920粒径分析装置を用いて行う。
水性懸濁物のpHは、標準pHメーターを使用しておよそ22℃にて測定する。
生成物の密度は、Micromeriticsによって販売されている標準密度分析装置Micromeritics AccuPyc(登録商標)を使用して測定する。
懸濁物固体含有率(「乾燥重量」としても公知)は、Mettler−Toledoによって販売されている水分分析装置HR73を以下の設定:温度120℃、自動スイッチオフ3、標準乾燥、懸濁物5から20gを使用して決定する。
以下の比較例は、従来技術の方法によるハイドロマグネサイトの調製を示す。前記方法は、苛性焼成マグネサイトを消和すること、および得られた水酸化マグネシウムをガス状CO2と接触させて得られた水酸化マグネシウムをハイドロマグネサイトに変換することによって行われ、炭酸化は約60℃の開始温度にて行われる。
本発明の以下の例証的な実施例は、苛性焼成マグネサイトを消和すること、および得られた水酸化マグネシウムをガス状CO2と接触させて得られた水酸化マグネシウムをハイドロマグネサイトに変換することによる、炭酸化が約20℃から25℃の開始温度によって行われるハイドロマグネサイトの調製、ならびに続いての加熱老化段階を包含する。
本発明の以下の例証的な実施例は、白色ドロマイト石を焼成および消和することならびに得られた水酸化マグネシウムをガス状CO2と接触させて得られた水酸化マグネシウムをハイドロマグネサイトに変換することによる、炭酸化が約12℃の開始温度によって行われるハイドロマグネサイトの調製、ならびに続いての加熱老化段階を包含する。
Claims (17)
- 水性環境においてハイドロマグネサイトを調製する方法であって:
a)ドロマイト、ハンタイト、およびこれらの混合物からなる群から選択される少なくとも1つの酸化マグネシウム源を提供する段階;
b)ガス状CO2 か、炭酸塩か、またはガス状CO 2 および炭酸塩かのいずれかを含むアニオンを、前記酸化マグネシウム源と混合する段階;
c)酸化マグネシウムを水と接触させて水和し、少なくとも部分的に水酸化マグネシウムに変換するための、段階a)の前記酸化マグネシウム源の消和段階;
d)水酸化マグネシウムを少なくとも部分的に沈降ネスケホナイトに変換するために、段階c)の得られた水酸化マグネシウムを段階b)の前記ガス状CO2 、炭酸塩、またはガス状CO 2 および炭酸塩を含むアニオンと接触させることで、沈降ネスケホナイトを、沈降炭酸カルシウムをさらに含む水性懸濁液の形態として得る段階;および
e)段階d)で得られた沈降ネスケホナイトおよび沈降炭酸カルシウムを加熱老化段階で処置する段階;
を含み、
得られたハイドロマグネサイトは、10μm未満の平均粒径d 50 を有する粒子であることを特徴とする、方法。 - 請求項1に記載の方法であって、ガス状CO2が外部CO2供給もしくはCO2の再循環または両方から得られる方法。
- 請求項1または2に記載の方法であって、炭酸塩を含むアニオンが炭酸ナトリウム、炭酸カリウム、炭酸水素ナトリウム、炭酸水素カリウムまたはこれらの混合物から成る群より選択される方法。
- 請求項1から3のいずれか一項に記載の方法であって、段階d)の開始温度が5℃と35℃の間の温度に調整される方法。
- 請求項1から4のいずれか一項に記載の方法であって、加熱老化段階e)が少なくとも90℃の温度にて行われる方法。
- 請求項5に記載の方法であって、加熱老化段階が20分から60分の時間にわたって行われる方法。
- 請求項1から6のいずれか一項に記載の方法であって、該方法によって得られたハイドロマグネサイトが10m2/gから150m2/gのBET比表面積を有する方法。
- 請求項1から7のいずれか一項に記載の方法であって、該方法によって得られたハイドロマグネサイトが少なくとも80%の白色度R457を有する方法。
- 請求項1から8のいずれか一項に記載の方法であって、該方法によって得られたハイドロマグネサイトが5μm未満の平均粒径d50を有する方法。
- 請求項1から9のいずれか一項に記載の方法であって、該方法によって得られたハイドロマグネサイトが脂肪酸によってさらに処置される方法。
- 前記脂肪酸が、ステアリン酸、パルミチン酸、ベヘン酸、モンタン酸、カプリン酸、ラウリン酸、ミリスチン酸、イソステアリン酸およびセロチン酸より選択される1つ以上の脂肪酸から成る群より選択される脂肪酸である、請求項10に記載の方法。
- 請求項1から11のいずれか一項に記載の方法によって得ることができるハイドロマグネサイト組成物。
- 請求項12に記載のハイドロマグネサイト組成物であって、ハイドロマグネサイトが2.26g/cm3と2.40g/cm3の間の密度を有するハイドロマグネサイト組成物。
- 紙コーティング用のまたは紙の無機充填剤としての請求項12または13に記載のハイドロマグネサイト組成物の使用。
- 請求項14に記載のハイドロマグネサイト組成物の使用であって、無機充填剤が喫煙用品の包装紙に使用されるハイドロマグネサイト組成物の使用。
- 難燃剤としての請求項12に記載のハイドロマグネサイト組成物の使用。
- 請求項16に記載のハイドロマグネサイト組成物の使用であって、難燃剤が電気および電子部品、建築材料、排水管、樋、自動車部品、テレビ、コンピュータおよび同様の機器のキャビネット、形材および取付具、ケーブル用取付具および電気スイッチ、シーラント、石膏、塗料またはこれらの混合物に使用されるハイドロマグネサイト組成物の使用。