JP5259940B2 - 粘着剤組成物、粘着シートおよび表面保護フィルム - Google Patents
粘着剤組成物、粘着シートおよび表面保護フィルム Download PDFInfo
- Publication number
- JP5259940B2 JP5259940B2 JP2006237851A JP2006237851A JP5259940B2 JP 5259940 B2 JP5259940 B2 JP 5259940B2 JP 2006237851 A JP2006237851 A JP 2006237851A JP 2006237851 A JP2006237851 A JP 2006237851A JP 5259940 B2 JP5259940 B2 JP 5259940B2
- Authority
- JP
- Japan
- Prior art keywords
- weight
- sensitive adhesive
- pressure
- meth
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
酸価は、自動滴定装置(平沼産業社製、COM−550)を用いて測定を行い、下記式より求めた。
A={(Y−X)×f×5.611}/M
・A:酸価
・Y:サンプル溶液の滴定量(ml)
・X:混合溶媒50gのみの溶液の滴定量(ml)
・f:滴定溶液のファクター
・M:ポリマーサンプルの重量(g)。
・サンプル溶液:ポリマーサンプル約0.5gを混合溶媒(トルエン/2−プロパノール/蒸留水=50/49.5/0.5、重量比)50gに溶解してサンプル溶液とした。
・滴定溶液:0.1N、2−プロパノール性水酸化カリウム溶液(和光純薬工業社製、石油製品中和価試験用)
・電極:ガラス電極;GE−101、比較電極;RE−201
・測定モード:石油製品中和価試験1。
重量平均分子量は、GPC装置(東ソー社製、HLC−8220GPC)を用いて測定を行った。測定条件は下記の通りである。
・サンプル濃度:0.2重量%(THF溶液)
・サンプル注入量:10μl
・溶離液:THF
・流速:0.6ml/min
・測定温度:40℃
・カラム:
サンプルカラム;TSKguardcolumn SuperHZ−H(1本)+TSKgel SuperHZM−H(2本)
リファレンスカラム;TSKgel SuperH−RC(1本)
・検出器:示差屈折計(RI)
なお、重量平均分子量はポリスチレン換算値にて求めた。
ガラス転移温度(Tg)(℃)は、動的粘弾性測定装置(レオメトリックス社製、ARES)を用いて、下記の方法により求めた。
・測定:せん断モード
・温度範囲:−70℃〜150℃
・昇温速度:5℃/min
・周波数:1Hz。
〔アクリル系ポリマー(A)〕
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート199.4重量部、(メタ)アクリル酸アルキレンオキシド付加物(日本油脂社製、ブレンマーPME−1000、オキシアルキレン単位平均付加モル数:23)0.6重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル386.3重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(A)溶液(35重量%)を調製した。上記アクリル系ポリマー(A)の重量平均分子量は49万、ガラス転移温度(Tg)は−55℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート199重量部、アルキレンオキシド基含有反応性界面活性剤(花王社製、ラムテルPD−430、オキシアルキレン単位平均付加モル数:3〜40)1重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル386.3重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(B)溶液(35重量%)を調製した。上記アクリル系ポリマー(B)の重量平均分子量は55万、ガラス転移温度(Tg)は−53℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート199重量部、アルキレンオキシド基含有反応性界面活性剤(旭電化工業社製、アデカリアソープER−10、オキシアルキレン単位平均付加モル数:10)1重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル386.3重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(C)溶液(35重量%)を調製した。上記アクリル系ポリマー(C)の重量平均分子量は50万、ガラス転移温度(Tg)は−53℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート199重量部、(メタ)アクリル酸アルキレンオキシド付加物(日本油脂社製、ブレンマー50POEP−800B、オキシアルキレン単位平均付加モル数:8)1重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル386.3重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(D)溶液(35重量%)を調製した。上記アクリル系ポリマー(D)の重量平均分子量は53万、ガラス転移温度(Tg)は−54℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート199重量部、アルキレンオキシド基含有反応性界面活性剤(花王社製、ラテムルPD−420、オキシアルキレン単位平均付加モル数:3〜40)1重量部、2−ヒドロキシブチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル312重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(E)溶液(40重量%)を調製した。上記アクリル系ポリマー(E)の重量平均分子量は56万、ガラス転移温度(Tg)は−53℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート200重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル312重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(F)溶液(40重量%)を調製した。上記アクリル系ポリマー(F)の重量平均分子量は55万、ガラス転移温度(Tg)は−55℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート199.9重量部、(メタ)アクリル酸アルキレンオキシド付加物(日本油脂社製、ブレンマーPME−1000、オキシアルキレン単位平均付加モル数:23)0.1重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル386.3重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(G)溶液を調製した。上記アクリル系ポリマー(G)(35重量%)の重量平均分子量は52万、ガラス転移温度(Tg)は−55℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート199.4重量部、(メタ)アクリル酸アルキレンオキシド付加物(日本油脂社製、ブレンマーPME−4000、オキシアルキレン単位平均付加モル数:90)0.6重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル386.3重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(H)溶液(35重量%)を調製した。上記アクリル系ポリマー(H)の重量平均分子量は43万、ガラス転移温度(Tg)は−54℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート199重量部、(メタ)アクリル酸アルキレンオキシド付加物(花王社製、ラテムルPD−420、オキシアルキレン単位平均付加モル数:3〜40)1重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル386.3重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(I)溶液(35重量%)を調製した。上記アクリル系ポリマー(I)の重量平均分子量は58万、ガラス転移温度(Tg)は−53℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート199.78重量部、(メタ)アクリル酸アルキレンオキシド付加物(花王社製、ラテムルPD−430、オキシアルキレン単位平均付加モル数:3〜40)0.22重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル325重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(J)溶液(39重量%)を調製した。上記アクリル系ポリマー(J)の重量平均分子量は55万、ガラス転移温度(Tg)は−53℃、酸価は0.0であった。
攪拌羽根、温度計、窒素ガス導入管、冷却器を備えた四つ口フラスコに、2−エチルヘキシルアクリレート194重量部、(メタ)アクリル酸アルキレンオキシド付加物(旭電化工業社製、アデカリアソープER−10、オキシアルキレン単位平均付加モル数:10)6重量部、2−ヒドロキシエチルアクリレート8重量部、重合開始剤として2,2’−アゾビスイソブチロニトリル0.4重量部、酢酸エチル325重量部を仕込み、緩やかに攪拌しながら窒素ガスを導入し、フラスコ内の液温を60℃付近に保って5時間重合反応を行い、アクリル系ポリマー(K)溶液(39重量%)を調製した。上記アクリル系ポリマー(K)の重量平均分子量は49万、ガラス転移温度(Tg)は−53℃、酸価は0.0であった。
〔帯電防止剤溶液(a)〕
攪拌羽根、温度計、冷却器を備えた四つ口フラスコに、ヨウ化リチウム5重量部、酢酸エチル20重量部を仕込み、フラスコ内の液温を25℃付近に保って2時間混合撹拌を行い、帯電防止剤溶液(a)(20重量%)を調製した。
攪拌羽根、温度計、冷却器を備えた四つ口フラスコに、リチウムビス(ペンタフルオロエタンスルホニル)イミド5重量部、酢酸エチル20重量部を仕込み、フラスコ内の液温を25℃付近に保って2時間混合撹拌を行い、帯電防止剤溶液(b)(20重量%)を調製した。
攪拌羽根、温度計、冷却器を備えた四つ口フラスコに、ヨウ化リチウム0.1重量部、ポリプロピレングリコール(ジオール型、数平均分子量:2000)7.9重量部、酢酸エチル32重量部を仕込み、フラスコ内の液温を80℃付近に保って2時間混合撹拌を行い、帯電防止剤溶液(c)(20重量%)を調製した。
帯電防止剤(ソルベックス社製、マイクロソルバーRMd−142、酸化スズとポリエステル樹脂を主成分とする)10重量部を、水30重量部とメタノール70重量部からなる混合溶媒で希釈することにより帯電防止剤溶液を調製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(A)溶液(35重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)1重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(1)を調製した。
上記アクリル系粘着剤溶液(1)を上記の帯電防止処理フィルムの帯電防止処理面とは反対の面に塗布し、130℃で2分間加熱して、厚さ20μmの粘着剤層を形成した。次いで、上記粘着剤層の表面に、片面にシリコーン処理を施した厚さ25μmのポリエチレンテレフタレートフィルムのシリコーン処理面を貼り合わせた後、50℃で2日間養生し、粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(B)溶液(35重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)1重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(2)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(2)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(C)溶液(35重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)1重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(3)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(3)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(D)溶液(35重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(b)(20重量%)2重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(4)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(4)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(E)溶液(40重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)1重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(5)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(5)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(F)溶液(40重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)1重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(6)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(6)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(G)溶液(35重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)1重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(7)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(7)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(H)溶液(35重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)1重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(8)の調製を試みたが、上記アクリル系粘着剤溶液(8)では溶液のゲル化が起きてしまった。
上記アクリル系粘着剤溶液(8)ではゲル化が起きたため、粘着シートを作製することができなかった。
(粘着剤溶液の調製)
上記アクリル系ポリマー(F)溶液(40重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、アニオン系界面活性剤であるジアルキルスルホコハク酸エステルソーダ塩(第一工業製薬社製、ネオコールSW、29重量%溶液の溶媒を除去して100重量%としたもの)2.0重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(9)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(9)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(F)溶液(40重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(c)(20重量%)8重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(10)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(10)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(I)溶液(35重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)0.5重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(11)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(11)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(I)溶液(35重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(b)(20重量%)2重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(12)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(12)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(J)溶液(39重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)0.4重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(13)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(13)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(K)溶液(39重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)1重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(14)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(14)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
(粘着剤溶液の調製)
上記アクリル系ポリマー(F)溶液(40重量%)を酢酸エチルで20重量%に希釈し、この溶液100重量部に、上記帯電防止剤溶液(a)(20重量%)0.4重量部、架橋剤としてヘキサメチレンジイソシアネートのイソシアヌレート体(日本ポリウレタン工業社製、コロネートHX)0.3重量部、架橋触媒としてジラウリン酸ジブチルスズ(1重量%酢酸エチル溶液)0.4重量部を加えて、常温(25℃)下で約1分間混合撹拌し、アクリル系粘着剤溶液(15)を調製した。
上記アクリル系粘着剤溶液(1)に代えて、上記アクリル系粘着剤溶液(15)を用いた以外は、実施例1と同様の方法により粘着シートを作製した。
粘着シートを幅70mm、長さ130mmのサイズにカットし、セパレーターを剥離した後、あらかじめ除電しておいたアクリル板(三菱レイヨン社製、アクリライト、厚み:1mm、幅:70mm、長さ:100mm)に貼り合わせた偏光板(日東電工社製、SEG1425WVAGS2B、幅:70mm、長さ:100mm)表面に片方の端部が30mmはみ出すようにハンドローラーにて圧着した。
作製した粘着シートを、幅50mm、長さ80mmのサイズにカットし、セパレーターを剥離した後、偏光板(日東電工社製、SEG1425WVAGS2B、幅:70mm、長さ:100mm)に気泡を入れながらハンドローラーにて圧着し、評価サンプルを作製した。
・汚染が認められなかった場合:○
・汚染が認められた場合:×。
作製した粘着シートを、幅25mm、長さ100mmのサイズにカットし、セパレーターを剥離した後、偏光板(日東電工社製、SEG1425DU、幅:70mm、長さ:100mm)に0.25MPaの圧力でラミネートし、評価サンプルを作製した。
Claims (7)
- オキシアルキレン単位の平均付加モル数が3〜40であるアルキレンオキシド基含有反応性モノマー0.1〜4.9重量%を単量体成分とする(メタ)アクリル系ポリマー(ただし、単量体成分が、ウレタンアクリレートを含まない)、架橋剤、ならびにアルカリ金属塩を含有してなる表面保護フィルム用粘着剤組成物であって、
前記架橋剤が、イソシアネート化合物、エポキシ化合物、および、メラミン系樹脂からなる群より選択される少なくとも1種であり、
前記アルカリ金属塩が、LiBr、LiI、LiBF 4 、LiPF 6 、LiSCN、LiCF 3 SO 3 、Li(CF 3 SO 2 ) 2 N、Li(C 2 F 5 SO 2 ) 2 N、Li(CF 3 SO 2 ) 3 Cからなる群より選択される少なくとも1種であり、
前記(メタ)アクリル系ポリマー100重量部に対して、前記架橋剤0.01〜10重量部、および前記アルカリ金属塩0.01〜2重量部含有することを特徴とする表面保護フィルム用粘着剤組成物。 - 前記アルカリ金属塩がリチウム塩である請求項1に記載の表面保護フィルム用粘着剤組成物。
- 前記アルキレンオキシド基含有反応性モノマーがエチレンオキシド基を有する反応性モノマーである請求項1〜2のいずれかに記載の表面保護フィルム用粘着剤組成物。
- 請求項1〜3のいずれかに記載の粘着剤組成物を架橋してなる表面保護フィルム用粘着剤層。
- 請求項1〜3のいずれかに記載の粘着剤組成物を架橋してなる粘着剤層を、支持体の片面または両面に形成してなることを特徴とする粘着シート。
- 請求項5に記載の粘着シートを用いてなることを特徴とする表面保護フィルム。
- 前記支持体が、帯電防止処理したプラスチック基材であることを特徴とする請求項6に記載の表面保護フィルム。