JP2023026489A - フィルム - Google Patents
フィルム Download PDFInfo
- Publication number
- JP2023026489A JP2023026489A JP2022200842A JP2022200842A JP2023026489A JP 2023026489 A JP2023026489 A JP 2023026489A JP 2022200842 A JP2022200842 A JP 2022200842A JP 2022200842 A JP2022200842 A JP 2022200842A JP 2023026489 A JP2023026489 A JP 2023026489A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- film
- less
- glossiness
- particles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明の課題は上記した従来技術の問題点を解消することにある。すなわち、転写フィルムとして用いた場合に、入射角度によらない均一な低光沢外観を転写可能であるフィルムを提供することにある。
(1)60°光沢度(G60)と、85°光沢度(G85)がいずれも27以下である低光沢層(A層)を有するフィルムであって、前記A層が少なくとも片側の表層にあり、前記60°光沢度(G60)と、前記85°光沢度(G85)が下記(I)式を満足し、前記A層の片側に基材層を有し、基材層、A層ともポリエステル樹脂を主成分とし、前記A層の厚みが3μmを超えて20μm以下であるフィルム。
0.1≦(G85)/(G60)≦3・・・(I)
(2)60°光沢度(G60)と、85°光沢度(G85)がいずれも27以下である低光沢層(A層)を有するフィルムであって、前記A層が少なくとも片側の表層にあり、前記60°光沢度(G60)と、前記85°光沢度(G85)が下記(I)式を満足し、前記A層の片側に基材層を有し、基材層、A層ともポリエステル樹脂を主成分とし、長手方向(MD)、幅方向(TD)の150℃での熱収縮率がいずれも2%以下であるフィルム。
0.1≦(G85)/(G60)≦3・・・(I)
(3)前記低光沢層(A層)の60°光沢度(G60)と、85°光沢度(G85)がいずれも10以下である(1)または(2)に記載のフィルム。
(4)フィルムの20cm×30cm範囲における引張破断強度のバラツキが20%以下である(1)~(3)のいずれかに記載のフィルム。
(5)前記A層が粒子を含んでおり、前記粒子の円形度が0.995以下である(1)~(4)のいずれかに記載のフィルム。
(6)前記粒子が無機粒子である(5)に記載のフィルム。
(7)前記粒子の嵩密度が0.5以上である(5)または(6)に記載のフィルム。
(8)二軸配向してなる(1)~(7)のいずれかに記載のフィルム。
(9)60°光沢度(G60)が6未満である(1)~(8)のいずれかに記載のフィルム。
(10)長手方向(MD)、幅方向(TD)の100℃から150℃の範囲での熱寸法変化率が、いずれも0.015%/℃以下である(1)~(9)のいずれかに記載のフィルム。
(11)前記A層表面の中心線平均粗さ(SRa)が1000nmを超えて3000nm以下である(1)~(10)のいずれかに記載のフィルム。
(12)下記方法により測定した150℃、10分間熱処理後のカール高さが0mm以上30mm以下である(1)~(11)のいずれかに記載のフィルム。
(測定方法) フィルムを任意の一方向に100mm、該方向に直交する方向に100mmの大きさに切り出し、サンプルとする。該サンプルを、150℃の熱風循環式オーブンで10分間放置して熱処理を行った後、ガラス板上に置き、ガラス板面から垂直方向での4隅の浮き上がり量を測定し、最大の高さをカール高さとする。
(13)前記A層表面の表面自由エネルギーが44mN/m以下である(1)~(12)のいずれかに記載のフィルム。
(14)転写用途に使用される(1)~(13)のいずれかに記載のフィルム。
(15)(1)~(14)のいずれかに記載のフィルムのA層の表面に離型層が積層されてなる積層体。
0.1≦(G85)/(G60)≦3・・・(I)
(I)式を満足するということは、60°光沢度(G60)と、85°光沢度(G85)の差が特定範囲で小さく制御されていることを示し、見る角度によらない均一な低光沢表面となる。均一低光沢表面の観点より、(II)式を満足すればより好ましく、(III)式を満足すれば最も好ましい。
0.1≦(G85)/(G60)≦2・・・(II)
0.1≦(G85)/(G60)≦1.5・・・(III)。
ポリエステル樹脂およびフィルムをヘキサフルオロイソプロパノール(HFIP)に溶解し、1H-NMRおよび13C-NMRを用いて各モノマー残基成分や副生ジエチレングリコールについて含有量を定量することができる。積層フィルムの場合は、積層厚みに応じて、フィルムの各層を削り取ることで、各層単体を構成する成分を採取し、評価することができる。なお、本発明のフィルムについては、フィルム製造時の混合比率から計算により、組成を算出した。
ポリエステル樹脂およびフィルムの固有粘度は、ポリエステルをオルトクロロフェノールに溶解し、オストワルド粘度計を用いて25℃にて測定した。積層フィルムの場合は、積層厚みに応じて、フィルムの各層を削り取ることで、各層単体の固有粘度を評価することができる。
ダイヤルゲージを用いて、フィルム厚みを測定した。
フィルムをエポキシ樹脂に包埋し、フィルム断面をミクロトームで切り出した。該断面を透過型電子顕微鏡(日立製作所製TEM H7100)で5000倍の倍率で観察し、
各層の厚みを求めた。
フィルムから、樹脂をプラズマ低温灰化処理法(ヤマト科学製PR-503型)で除去し粒子を露出させる。これを透過型電子顕微鏡(日立製作所製TEM H7100)で観察し、粒子の画像(粒子によってできる光の濃淡)をイメージアナライザー(ケンブリッジインストルメント製QTM900)に結び付け、観察箇所を変えて粒子数100個で次の数値処理を行ない、それによって求めた数平均径Dを平均粒子径とした。
D=ΣDi /N
ここでDi は粒子の円相当径、Nは粒子の個数である。
(5)と同様にして粒子の画像を観察した。また、円形度は、下記式より算出し、粒子数100個の平均値を本発明の円形度とした。
円形度=4π×面積/周囲長2
(7)粒子の形状・嵩高度
フィルム長手方向に平行かつフィルム厚み方向に垂直なフィルム断面、及び、フィルム幅方向に平行かつフィルム厚み方向に垂直なフィルム断面をミクロトームで切り出し、(5)に記載の方法にて観察を行った。断面における粒子で粒子の端と端が最も長くなる長さをL1、前記L1を求めるに際して粒子の端と端を繋いだ線分の垂直な方向で粒子の端と端が最も長くなる長さをL2とする(図1)。嵩高度は、フィルム長手方向に平行かつフィルム厚み方向に垂直なフィルム断面、及び、フィルム幅方向に平行かつフィルム厚み方向に垂直なフィルム断面それぞれにおいてL2/L1を求めてそれぞれ100個の平均として求めた。
ポリマー1gを1N-KOHメタノール溶液200mlに投入して加熱還流し、ポリマーを溶解した。溶解が終了した該溶液に200mlの水を加え、ついで該液体を遠心分離器にかけて粒子を沈降させ、上澄み液を取り除いた。粒子にはさらに水を加えて洗浄、遠心分離を2回繰り返した。このようにして得られた粒子を乾燥させ、その質量を量ることで粒子の含有量を算出した。
JIS-Z-8741(1997年)に規定された方法に従って、スガ試験機製デジタル変角光沢度計UGV-5Dを用いて、60°鏡面光沢度及び、85°鏡面光沢度をそれぞれN=3で測定し、平均値を本発明の60°光沢度(G60)、85°光沢度(G85)とした。
(10)MIT屈曲回数
ポリエステルフィルムを、幅15mm長さ100mmの短冊形に切り出しサンプルとした。 MIT耐折度試験機((株)マイズ試験機製)を用いて、フィルム長手方向および幅方向を各3回測定後平均値算出した。
・屈曲角度:左右135°
・屈曲速度:175往復/毎分
・荷重:9.8N
(11)中心線平均粗さSRa
長さ4.0cm×幅3.5cmの寸法に切り出したものをサンプルとし、触針法の高精細微細形状測定器(3次元表面粗さ計)を用いてJIS B0601-1994に準拠して、下記条件にてフィルムの表面形態を測定した。
・測定装置 :3次元微細形状測定器((株)小坂研究所製、ET-4000A型)
・解析機器 :3次元表面粗さ解析システム(TDA-31型)
・触針 :先端半径0.5μmR、径2μm、ダイヤモンド製
・針圧 :100μN
・測定方向 :フィルム長手方向、フィルム幅方向を各1回測定後平均
・X測定長さ:1.0mm
・X送り速さ:0.1mm/s(測定速度)
・Y送りピッチ:5μm(測定間隔)
・Yライン数:81本(測定本数)
・Z倍率 :20倍(縦倍率)
・低域カットオフ:0.20mm
・高域カットオフ:R+Wmm(粗さカットオフ値)R+Wとはカットオフしないことを意味する。
・フィルタ方式:ガウシアン空間型
・レベリング:あり(傾斜補正)
・基準面積 :1mm2。
上記条件にて測定を行い、その後解析システムを用いて中心線平均粗さSRaを算出した。
長手方向(MD)、幅方向(TD)がそれぞれ長さ方向になるように長さ50mm×幅4mmの矩形に切り出しサンプルとし、熱機械分析装置(セイコ-インスツルメンツ製、TMA EXSTAR6000)を使用して、下記条件下で昇温し、100℃から150℃における熱寸法変化率を測定した。
試長:15mm、荷重:19.6mN、昇温速度:10℃/分、
測定温度範囲:30~200℃
100℃から150℃の範囲での熱寸法変化率(%)=[{150℃でのフィルム長(mm)-100℃でのフィルム長(mm)}/100℃でのフィルム長(mm)]×100
なお、測定は各フィルムとも長手方向および幅方向に5サンプル実施して平均値で評価を行った。
長手方向(MD)、幅方向(TD)がそれぞれ長さ方向になるように長さ150mm×幅10mmの矩形に切り出しサンプルとした。サンプルに100mmの間隔で標線を描き、3gの錘を吊して150℃に加熱した熱風オーブン内に30分間設置し加熱処理を行った。熱処理後の標線間距離を測定し、加熱前後の標線間距離の変化から下記式により熱収縮率を算出した。測定は各フィルムとも長手方向および幅方向に5サンプル実施して平均値で評価を行った。
熱収縮率(%)={(加熱処理前の標線間距離)-(加熱処理後の標線間距離)}/(加熱処理前の標線間距離)×100。
フィルムを任意の一方向に100mm、該方向に直交する方向に100mmの大きさに切り出し、サンプルとする。該サンプルを150℃の熱風循環式オーブンで10分間放置して熱処理を行った後、ガラス板上に置き、ガラス板面から垂直方向での4隅の浮き上がり量を測定し、最大の高さをカール高さとした。
フィルムを任意の位置で幅20cm×長さ30cmの大きさに切り出したサンプルについて、長さ方向に15cmに2等分し、それぞれ15cm長のサンプルを幅方向に1cm幅に切り出し、長さ15cm×幅1cmの短冊状サンプル40本を作成する。該サンプルについて、引張試験機(オリエンテック製テンシロンUCT-100)を用いて、初期引張チャック間距離50mmとし、引張速度を300mm/分として引張試験を行い、フィルムが破断した際の強度(引張破断強度)を測定し、下記の通り、バラツキを求めた。
引張破断強度のバラツキ(%)={(最大値-最小値)/平均値}×100
(16)表面自由エネルギー
測定液としては、水、エチレングリコール、ホルムアミドおよびジヨードメタンの4種類を使用し、接触角計(協和界面科学(株)製CA-D型)を用いて各液体のフィルム表面に対する静的接触角を求めた。それぞれの液体について5回測定し、その平均接触角(θ)と測定液(j)の表面張力の各成分を下式にそれぞれ代入し、4つの式からなる連立方程式をγL、γ+、γ-について解いた。
(γLγjL)1/2+2(γ+γj-)1/2+2(γj+γ-)1/2
=(1+cosθ)[γjL+2(γj+γj-)1/2]/2
ただし、γ=γL+2(γ+γ-)1/2
γj=γjL+2(γj+γj-)1/2
ここで、γ、γL、γ+、γ-は、それぞれフィルム表面の表面自由エネルギー、長距離間力項、ルイス酸パラメーター、ルイス塩基パラメーターを、また、γj、γjL、γj+、γj-は、それぞれ用いた測定液の表面自由エネルギー、長距離間力項、ルイス酸パラメーター、ルイス塩基パラメーターを示す。また、ここで用いた各液体の表面張力は、Oss("fundamentals of Adhesion", L. H. Lee (Ed.), p153, Plenum ess, New York (1991).)によって提案された値を使用した。
フィルムを長さ100mm×幅100mmに切り出し用いた。下記のハードコート層形成用塗料組成物を、乾燥後の厚みが5μmになるように流量を制御してスロットダイコーターを用いて塗布し、100℃で1分間乾燥して溶剤を除去し、ハードコート層が積層された積層体を得た。
得られたフィルム/ハードコート層積層体を上金型温度、下金型温度ともに温度160℃に加熱したプレス機を使用し、厚さ0.2mmのアルミニウム板/厚さ0.125mmのポリイミドフィルム(東レデュポン製カプトン500H/V)/積層体/厚さ0.125mmのポリイミドフィルム(東レデュポン製カプトン500H/V)/厚さ0.2mmのアルミニウム板の構成体を1.5MPaの条件下で1時間加熱プレスを行った。加熱プレス後に、積層体を取り出し、高圧水銀灯を用いて300mJ/cm2の紫外線を積層体側から照射し、ハードコート層を硬化させサンプルを得る。このサンプルをフィルム、ハードコート層界面にて剥離テストを実施し、以下基準で剥離性の評価を行った。なお、フィルムに離型層が設けられている場合は、フィルム/離型層とハードコート層界面にて剥離テストを行った。剥離テストは5回行い、下記評価基準で評価を行った。
下記材料を混合し、メチルエチルケトンを用いて希釈し固形分濃度40質量%のハードコート層形成用塗料組成物を得た。
トルエン 30質量部
多官能ウレタンアクリレート 25質量部
(ダイセルオルネクス株式会社製 KRM8655)
ペンタエリスリトールトリアクリレート混合物 25質量部
(日本化薬株式会社製 PET30)
多官能シリコーンアクリレート 1質量部
(ダイセルオルネクス株式会社製 EBECRYL1360)
光重合開始剤 3質量部
(チバスペシャリティーケミカルズ社製 イルガキュア184)
(評価基準)
A:抵抗なく剥離可能であり、(5回の剥離テストにおいて、いずれも)フィルム破れは発生しなかった。
(17)と同様にして加熱プレスした後の積層体について、ガラス板上に置き、ガラス板面から垂直方向での4隅の浮き上がり量を測定し、最大の高さをカール高さとした。
B:カール高さが10mm以上20mm未満
C:カール高さが20mm以上30mm未満
D:カール高さが30mm以上。
(17)の方法にて得られたハードコート層の剥離面側について、光沢度を測定し、その平均値について以下の基準にて評価した。
(マット調外観の転写性)
A:60°光沢度(G60)と、85°光沢度(G85)いずれも10以下
B:60°光沢度(G60)と、85°光沢度(G85)の一方は10以下であったが、もう一方は10より大きく27以下であった
C:60°光沢度(G60)と、85°光沢度(G85)のいずれも10以上27以下であった
D:60°光沢度(G60)と、85°光沢度(G85)の少なくとも一方が27より大きかった。
A:0.1≦(G85)/(G60)≦1.5
B:1.5<(G85)/(G60)≦2
C:2.0<(G85)/(G60)≦3
D:0.1>(G85)/(G60)もしくは、(G85)/(G60)>3
(19)転写品位
(17)の方法にて得られたハードコート層の剥離面側について、外観を目視で観察し、以下の基準にて評価した。
A: シワが見られない
B:Aに該当せず、シワの発生が2本以下
C:A、Bに該当せず、シワの発生が5本以下
D:A,B、Cのいずれにも該当しない。
製膜に供したポリエステル樹脂は以下のように準備した。
ジカルボン酸成分としてテレフタル成分が100モル%、グリコール成分としてエチレングリコール成分が100モル%であるポリエチレンテレフタレート樹脂(固有粘度0.75)。
イソフタル酸がジカルボン酸成分に対して20モル%共重合された共重合ポリエチレンテレフタレート樹脂(固有粘度0.8)。
ジカルボン酸成分としてテレフタル成分が100モル%、グリコール成分として1,4-ブタンジオール成分が100モル%であるポリブチレンテレフタレート樹脂(固有粘度1.2)。
東レ-デュポン社製“ハイトレル(登録商標)”7247。
ポリエステルA中に平均粒子径6μm・六面体形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルA中に平均粒子径7.5μm・六面体形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルA中に平均粒子径10μm・六面体形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルA中に平均粒子径7.5μm・八面体形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルA中に平均粒子径5μm・球状形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルA中に平均粒子径7.5μm・球状形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルC中に平均粒子径6μm・六面体形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルC中に平均粒子径7.5μm・六面体形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルC中に平均粒子径10μm・六面体形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルC中に平均粒子径7.5μm・八面体形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルC中に平均粒子径5μm・球状形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルC中に平均粒子径7.5μm・球状形状の珪酸アルミ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
ポリエステルC中に平均粒子径6μm・平均厚み0.10μmのアルミナ粒子を粒子濃度30質量%で含有したポリエチレンテレフタレート粒子マスター(固有粘度0.7)。
以下に示す、架橋剤:バインダー樹脂:離型剤:粒子をそれぞれ、質量比60:23:17で混合し、固形分が1%の質量比となるように純水で希釈して調整した。
・架橋剤:メチル化メラミン/尿素共重合の架橋製樹脂((株)三和ケミカル製“ニカラック” (登録商標)「MW12LF」)
・バインダー樹脂I:アクリルモノマー共重合体(日本カーバイド製)
・離型剤: ガラス製反応容器中に、パーフルオロアルキル基含有アクリレートであるCF3(CF2)nCH2CH2OCOCH=CH2(n=5~11、nの平均=9)80.0g、アセトアセトキシエチルメタクリレート20.0g、ドデシルメルカプタン0.8g、脱酸素した純水354.7g、アセトン40.0g、C16H33N(CH3)3Cl1.0gおよびC8H17C6H4O(CH2CH2O)nH(n=8)3.0gを入れ、アゾビスイソブチルアミジン二塩酸塩0.5gを加え、窒素雰囲気下で攪拌しつつ60℃で10時間共重合反応させて得られた共重合体エマルション。
・粒子:平均粒子径170nmのシリカ粒子(日産化学工業(株)製“スノーテックス”(登録商標)MP2040)を固形分濃度が40質量%となるように純水で希釈して得られた水分散体。
組成、積層比が表の通りとなるように、原料をそれぞれ押出機に供給し、押出機シリンダー温度を270℃、短管温度を275℃、口金温度を280℃に設定し、樹脂温度280℃で、Tダイより25℃に温度制御した冷却ドラム上にシート状に吐出した。その際、直径0.1mmのワイヤー状電極を使用して静電印加し、冷却ドラムに密着させ、さらに冷却ドラムと反対面側に25℃に温度制御した冷却ニップロールを設けて未延伸シートを得た。次いで、長手方向に延伸温度85℃で3.1倍延伸し、その後、コロナ放電処理を施し、離型層形成用溶液(水分散体)をメタリングバーを用いてウェット厚みが13.5μmとなるように塗布し、次いでテンター式横延伸機にて、幅方向に延伸温度100℃で延伸倍率3.3倍延伸した。その後、テンター内にて、235℃で15秒間熱処理を行い、続いて、幅方向に3.5%弛緩しながら175℃で10秒間熱処理を行い、フィルム厚み50μmのフィルムを得た(低光沢層(A層)表面をA1面、基材層側表面をB面とした)。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとし、幅方向に延伸後に225℃で幅方向に1%弛緩しながら30秒熱処理した以外は、実施例2と同様にしてフィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとし、押出機より冷却ドラム上にシート押出する際、冷却ドラムと反対面側の冷却ニップロールを設けずに未延伸シートを得、手方向に延伸した後、コロナ放電処理、離型層塗布を実施しなかった以外は、実施例4と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとし、A層/基材層/A層の3層構成とした以外は、実施例5と同様にしてフィルム厚み50μmのフィルムを得た。
組成を表の通りとし、A層/基材層/A層の3層構成とした以外は、実施例5と同様にしてフィルム厚み50μmのフィルムを得た。
組成を表の通りとし、A層/基材層/A層の3層構成とした以外は、実施例5と同様にしてフィルム厚み38μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
長手方向延伸後に、コロナ放電処理、離型層塗布しなかった以外は実施例5と同様にしてフィルム厚み50μmのフィルムを得た。
組成を表の通りに変更し、横延伸温度を140℃とした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りに変更し、横延伸温度を140℃とした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りに変更した以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りに変更した以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りに変更し、幅方向への延伸後に幅方向への弛緩熱処理を235℃で2.0%、210℃にて1.5%の条件でそれぞれ5秒間ずつ行った以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りに変更し、幅方向への延伸後に幅方向への弛緩熱処理を235℃で1.5%、215℃にて1.0%、200℃にて1.0%の条件でそれぞれ5秒間ずつ行った以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りに変更し、幅方向への延伸後に幅方向への弛緩熱処理を240℃で3.5%、15秒間行った以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りに変更し、幅方向への延伸後に幅方向への弛緩熱処理を235℃で2.0%、210℃にて1.5%の条件でそれぞれ5秒間ずつ行った以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りに変更し、幅方向への延伸後に幅方向への弛緩熱処理を235℃で1.5%、215℃にて1.0%、200℃にて1.0%の条件でそれぞれ5秒間ずつ行った以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
(比較例2)
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとし、幅方向への延伸倍率を3.8倍とした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
組成を表の通りとした以外は実施例1と同様にして、フィルム厚み50μmのフィルムを得た。
Claims (15)
- 60°光沢度(G60)と、85°光沢度(G85)がいずれも27以下である低光沢層(A層)を有するフィルムであって、前記A層が少なくとも片側の表層にあり、前記60°光沢度(G60)と、前記85°光沢度(G85)が下記(I)式を満足し、前記A層の片側に基材層を有し、基材層、A層ともポリエステル樹脂を主成分とし、前記A層の厚みが3μmを超えて20μm以下であるフィルム。
0.1≦(G85)/(G60)≦3・・・(I) - 60°光沢度(G60)と、85°光沢度(G85)がいずれも27以下である低光沢層(A層)を有するフィルムであって、前記A層が少なくとも片側の表層にあり、前記60°光沢度(G60)と、前記85°光沢度(G85)が下記(I)式を満足し、前記A層の片側に基材層を有し、基材層、A層ともポリエステル樹脂を主成分とし、長手方向(MD)、幅方向(TD)の150℃での熱収縮率がいずれも2%以下であるフィルム。
0.1≦(G85)/(G60)≦3・・・(I) - 前記低光沢層(A層)の60°光沢度(G60)と、85°光沢度(G85)がいずれも10以下である請求項1または2に記載のフィルム。
- フィルムの20cm×30cm範囲における引張破断強度のバラツキが20%以下である請求項1~3のいずれかに記載のフィルム。
- 前記A層が粒子を含んでおり、前記粒子の円形度が0.995以下である請求項1~4のいずれかに記載のフィルム。
- 前記粒子が無機粒子である請求項5に記載のフィルム。
- 前記粒子の嵩密度が0.5以上である請求項5または6に記載のフィルム。
- 二軸配向してなる請求項1~7のいずれかに記載のフィルム。
- 60°光沢度(G60)が6未満である請求項1~8のいずれかに記載のフィルム。
- 長手方向(MD)、幅方向(TD)の100℃から150℃の範囲での熱寸法変化率が、いずれも0.015%/℃以下である請求項1~9のいずれかに記載のフィルム。
- 前記A層表面の中心線平均粗さ(SRa)が1000nmを超えて3000nm以下である請求項1~10のいずれかに記載のフィルム。
- 下記方法により測定した150℃、10分間熱処理後のカール高さが0mm以上30mm以下である請求項1~11のいずれかに記載のフィルム。
(測定方法) フィルムを任意の一方向に100mm、該方向に直交する方向に100mmの大きさに切り出し、サンプルとする。該サンプルを、150℃の熱風循環式オーブンで10分間放置して熱処理を行った後、ガラス板上に置き、ガラス板面から垂直方向での4隅の浮き上がり量を測定し、最大の高さをカール高さとする。 - 前記A層表面の表面自由エネルギーが44mN/m以下である請求項1~12のいずれかに記載のフィルム。
- 転写用途に使用される請求項1~13のいずれかに記載のフィルム。
- 請求項1~14のいずれかに記載のフィルムのA層の表面に離型層が積層されてなる積層体。