JP2021051246A - キャリア芯材並びにこれを用いた電子写真現像用キャリア及び電子写真用現像剤 - Google Patents
キャリア芯材並びにこれを用いた電子写真現像用キャリア及び電子写真用現像剤 Download PDFInfo
- Publication number
- JP2021051246A JP2021051246A JP2019175203A JP2019175203A JP2021051246A JP 2021051246 A JP2021051246 A JP 2021051246A JP 2019175203 A JP2019175203 A JP 2019175203A JP 2019175203 A JP2019175203 A JP 2019175203A JP 2021051246 A JP2021051246 A JP 2021051246A
- Authority
- JP
- Japan
- Prior art keywords
- core material
- carrier
- carrier core
- less
- mol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
測定装置:注入型画像解析粒度分布計 JASCO社製「IF−3200」
解析ソフトウエア:PIA−Pro 14.18
試料作製条件:試料0.07gをポリエチレングリコール400を9cm3投入したスクリュー管瓶(容量9cm3)中で分散させた後測定した。
測定条件:テレセントリックズームレンズ 倍率2倍
フロントレンズ 倍率2倍
キャリブレーション値 0.417μm/pixel
スペーサー厚 150μm
サンプリング 20%
解析タイプ 相対測定
測定量 0.95cm3
解析 ダーク検出
閾値 169(穴を埋める。)
O−Roughnessフィルター 0.5
測定時フィルター条件:
ISO Area Diametere:最小値5,最大値150,内側の範囲
解析フィルター条件:
ISO Area Diametere:最小値10,最大値55,内側の範囲
ISO Solidity :最小値0.9,最大値1,内側の範囲
O.Bluntness:粒子輪郭の滑らかさの指標
粒子画像における全ての内接円の半径のばらつき
ISO Roundness:粒子の丸み具合の指標
ISO Roundnessの計算式:
(4×Pixcel Count)/(π×ISO Max distance2)
キャリア芯材を下記方法で作製した。Feを11.1mol、Snを0.05mol、Srを0.04mol及びMn4.4molの比率となるようにFe2O3、SnO2、SrCO3及びMn3O4を水に分散し、分散剤としてポリカルボン酸アンモニウム系分散剤を0.600wt%、還元剤としてカーボンブラックを0.300wt%添加した。この混合物の固形分濃度は75wt%であった。
この混合物を湿式ボールミル(メディア径2mm)により粉砕処理し、混合スラリーを得た。この混合スラリーをスプレードライヤーにて約210℃の熱風中に噴霧し、粒径10〜75μmの乾燥造粒物を得た。この造粒物から、網目50×54μmの篩網を用いて粗粒を分離し、網目25×32μmの篩網を用いて微粒を分離した。
この造粒物を、電気炉に投入し1230℃まで5時間かけて昇温した。その後1230℃で3時間保持することにより焼成を行った。その後冷却速度2℃/分で500℃まで冷却した。昇温段階及び焼成温度の保持段階での電気炉内の酸素濃度は15000ppm、冷却段階での酸素濃度は4000ppmとなるよう、酸素と窒素とを混合したガスを炉内に供給した。
得られた焼成物をハンマーミルで解粒した後に振動篩を用いて分級し、平均粒径34.6μmの焼成物を得た。
次いで、得られた焼成物を大気雰囲気下410℃で1.5時間保持することにより酸化処理(高抵抗化処理)を行い、キャリア芯材を得た。
得られたキャリア芯材の組成、形状特性、粉体特性、磁気特性、電気特性などを後述の方法で測定した。測定結果を表1及び表2に示す。
焼成工程における電気炉温度を1275℃、昇温段階及び焼成温度の保持段階での電気炉内の酸素濃度を4000ppmに変更した以外は実施例1同様にして平均粒径34.8μmのキャリア芯材を作製した。
焼成工程における電気炉温度を1300℃に変更した以外は実施例1同様にして平均粒径34.5μmのキャリア芯材を作製した。
造粒時の篩網目を48μmの篩網を用いて粗粒を分離し、網目37μmの篩網を用いて微粒を分離した以外は、実施例3同様にして平均粒径35.0μmのキャリア芯材を作製した。
Feを10.0mol、Snを0.05mol、Srを0.04mol及びMn5.0molの比率となるようにFe2O3、SnO2、SrCO3及びMn3O4を水に分散したうえ、造粒時の篩網目を48μmの篩網を用いて粗粒を分離し、網目37μmの篩網を用いて微粒を分離し、焼成工程における電気炉温度を1315℃にした以外は、実施例1同様にして平均粒径36.6μmのキャリア芯材を作製した。
Sn及びSrを添加せず、焼成工程における電気炉温度を1200℃、昇温段階及び焼成温度の保持段階での電気炉内の酸素濃度は5000ppm、冷却段階での酸素濃度は10000ppmとなるようにした以外は実施例1同様にして平均粒径34.4μmのキャリア芯材を作製した。
Feを10.0mol%、Srを0.08mol%及びMn5.0%molとなるようにFe2O3、SrCO3及びMn3O4を水に分散し、分散剤としてポリカルボン酸アンモニウム系分散剤を0.600wt%、還元剤としてカーボンブラックを0.300wt%、36.5%の濃塩酸を0.177wt%添加した。この混合物の固形分濃度は75wt%であった。
この混合物を湿式ボールミル(メディア径2mm)により粉砕処理し、混合スラリーを得た。この混合スラリーをスプレードライヤーにて約210℃の熱風中に噴霧し、粒径10〜75μmの乾燥造粒物を得た。この造粒物から、網目50×54μmの篩網を用いて粗粒を分離し、網目33μmの篩網を用いて微粒を分離した。
この造粒物を、電気炉に投入し900℃まで3時間かけ昇温、その後900℃で5.5時間保持することにより焼成した。その際の電気炉内酸素濃度は210000ppmであった。その後出てきた焼成物を続けて電気炉に投入し1165℃まで5時間かけて昇温した。その後1165℃で3時間保持することにより焼成を行った。その後冷却速度2℃/分で500℃まで冷却した。昇温段階及び焼成温度の保持段階及び冷却段階での電気炉内の酸素濃度は7000ppm一定で、酸素と窒素とを混合したガスを炉内に供給した。
得られた焼成物をハンマーミルで解粒した後に振動篩を用いて分級し、平均粒径36.2μmのキャリア芯材を得た。
Feを10.0mol%、Mgを1.1mol%、Srを0.08mol%及びMn3.80mol%となるようにFe2O3、Mg(OH)2、SrCO3及びMn3O4を秤量し、乾式のメディアミル(振動ミル、1/8インチ径のステンレスビーズ)で10時間粉砕し、得られた粉砕物を電気炉で、1200℃で3時間加熱し、仮焼成を行った。次いで、乾式のメディアミル(振動ミル、1/8インチ径のステンレスビーズ)を用いて、10時間、平均粒径が約5μmまで粉砕した後、水を加え、さらに湿式ボールミル(メディア径2mm)を用いて10時間粉砕した。このスラリーの平均粒径が約2.3μmであった。このスラリーに分散剤を適量添加し、バインダーとしてPVA(10%溶液)を固形分に対して0.4質量%添加し、混合スラリーを得た。この混合スラリーをスプレードライヤーにて約210℃の熱風中に噴霧し、粒径10〜75μmの乾燥造粒物を得た。この造粒物から、網目50×54μmの篩網を用いて粗粒を分離し、網目33μmの篩網を用いて微粒を分離した。その後、ロータリー式電気炉を用い、大気雰囲気で、750℃で2時間加熱し、分散剤やバインダーといった有機成分の除去を行った。
この造粒物を、電気炉に投入し1300℃まで5時間かけて昇温した。その後1300℃で3時間保持することにより焼成を行った。その後冷却速度2℃/分で500℃まで冷却した。昇温段階及び焼成温度の保持段階及び冷却段階での電気炉内の酸素濃度は7000ppm一定で、酸素と窒素とを混合したガスを炉内に供給した。
得られた焼成物をハンマーミルで解粒した後に振動篩を用いて分級し、平均粒径36.9μmのキャリア芯材を得た。
焼成工程における電気炉温度を1275℃にした以外は、実施例5同様にして平均粒径36.6μmのキャリア芯材を作製した。
(Feの分析)
鉄元素を含むキャリア芯材を秤量し、塩酸と硝酸の混酸水に溶解させた。この溶液を蒸発乾固させた後、硫酸水を添加して再溶解し過剰な塩酸と硝酸とを揮発させる。この溶液に固体Alを添加して液中のFe3+を全てFe2+に還元する。続いて、この溶液中のFe2+イオンの量を過マンガン酸カリウム溶液で電位差滴定することにより定量分析し、Fe(Fe2+)の滴定量を求めた。
(Mnの分析)
キャリア芯材のMn含有量は、JIS G1311−1987記載のフェロマンガン分析方法(電位差滴定法)に準拠して定量分析を行った。本願発明に記載したキャリア芯材のMn含有量は、このフェロマンガン分析方法(電位差滴定法)で定量分析し得られたMn量である。
(Mgの分析)
キャリア芯材のMg含有量は、以下の方法で分析を行った。本願発明に係るキャリア芯材を酸溶液中で溶解し、ICPにて定量分析を行った。本願発明に記載したキャリア芯材のMg含有量は、このICPによる定量分析で得られたMg量である。
(Snの分析)
キャリア芯材のCa含有量は、Mgの分析同様にICPによる定量分析で行った。
(Srの分析)
キャリア芯材のSr含有量は、Mgの分析同様にICPによる定量分析で行った。
下記の測定装置及び測定条件で測定した。
測定装置:注入型画像解析粒度分布計 JASCO社製「IF−3200」
解析ソフトウエア:PIA−Pro 14.18
試料作製条件:試料0.07gをポリエチレングリコール400を9cm3投入したスクリュー管瓶(容量9cm3)中で分散させた後測定した。
測定条件:テレセントリックズームレンズ 倍率2倍
フロントレンズ 倍率2倍
キャリブレーション値 0.417μm/pixel
スペーサー厚 150μm
サンプリング 20%
解析タイプ 相対測定
測定量 0.95cm3
解析 ダーク検出
閾値 169(穴を埋める。)
O−Roughnessフィルター 0.5
測定時フィルター条件:
ISO Area Diametere:最小値5,最大値150,内側の範囲
解析フィルター条件:
ISO Area Diametere:最小値10,最大値55,内側の範囲
ISO Solidity :最小値0.9,最大値1,内側の範囲
O.Bluntness:粒子輪郭の滑らかさの指標
粒子画像における全ての内接円の半径のばらつき
ISO Roundness:粒子の丸み具合の指標
ISO Roundnessの計算式:
(4×Pixcel Count)/(π×ISO Max distance2)
キャリア芯材の見掛け密度はJIS Z 2504に準拠して測定した。
キャリア芯材の流動度はJIS Z 2502に準拠して測定した。
キャリア芯材の体積平均粒径D50及び粒径26μm以下の個数割合は、レーザー回折式粒度分布測定装置(日機装社製「マイクロトラックModel9320−X100」)を用いて測定した。
細孔容積の測定については、以下の通り行った。評価装置は、Quantachrome社製のPOREMASTER−60GTを使用した。具体的には、測定条件としては、Cell Stem Volume:0.5cm3、Headpressure:20PSIA、水銀の表面張力:485.00erg/cm2、水銀の接触角:130.00degrees、高圧測定モード:Fixed Rate、Moter Speed:1、高圧測定レンジ:20.00〜10000.00PSIとし、サンプル1.200gを秤量して0.5cm3のセルに充填して測定を行った。また、10000.00PSI時の容積B(cm3/g)から100PSI時の容積A(cm3/g)を差し引いた値を、細孔容積とした。
キャリア芯材を樹脂中に分散させ、真空脱泡処理を施すことでキャリア芯材内に樹脂を充填させた後、補助板に塗布し、温度200℃で20分間熱処理を行って樹脂を硬化させた。その後クロスセッションポリッシャー(SM−09010日本電子株式会社製)を用いてキャリア芯材をカットした。そしてキャリア芯材の断面を走査型電子顕微鏡(JSM−6510LA型日本電子株式会社製)で撮影した。
撮影した画像から画像解析ソフト(Image−Pro Plus、Media Cybernetics社製)を用いて、100粒子について空隙面積が20μm2以上の内部空隙の個数及び面積を測定して、面積20μm2以上の内部空隙の総空隙面積を算出し、これを100粒子の総粒子面積A(内部空隙を含む粒子断面積)で割って「空隙面積が20μm2以上の内部空隙の内部空隙率」を算出した。
室温専用振動試料型磁力計(VSM)(東英工業社製「VSM−P7」)を用いて、外部磁場を0〜79.58×104A/m(10000エルステッド)の範囲で1サイクル連続的に印加して、飽和磁化σS、磁化σ1k、残留磁化σrを測定した。
電極として表面を電解研磨した板厚2mmの真鍮板2枚を電極間距離が2mmとなるように配置し、2枚の電極板の間の空隙にキャリア芯材200mgを装入したのち、それぞれの電極板の背後に断面積240mm2の磁石を配置して電極間に被測定粉体のブリッジを形成させた状態で電極間に100V,500V、1000Vの直流電圧を印加し、キャリア芯材を流れる電流値を4端子法により測定し、キャリア芯材の電気抵抗を算出した。なお、表2中、「B.D.」はキャリア芯材が絶縁破壊を起こしたことを意味する。
得られたキャリア芯材の表面を樹脂で被覆してキャリアを作製した。具体的には、シリコーン樹脂450質量部と、(2−アミノエチル)アミノプロピルトリメトキシシラン9質量部とを、溶媒としてのトルエン450質量部に溶解してコート溶液を作製した。このコート溶液を、流動床型コーティング装置を用いてキャリア芯材50000質量部に塗布し、温度300℃の電気炉で加熱してキャリアを得た。以下、全ての実施例、比較例についても同様にしてキャリアを得た。
得られたキャリアと平均粒径5.0μm程度のトナーとを、ポットミルを用いて所定時間混合し、二成分系の電子写真現像剤を得た。この場合、キャリアとトナーとをトナーの質量/(トナーおよびキャリアの質量)=5/100となるように調整した。以下、全ての実施例、比較例についても同様にして現像剤を得た。得られた現像剤を、図1に示す構造の現像装置(現像スリーブの周速度Vs:406mm/sec,感光体ドラムの周速度Vp:205mm/sec,感光体ドラム−現像スリーブ間距離:0.3mm)に投入し、感光体ドラムの周方向にベタ画像部と非画像部とが隣り合い、その後は広い面積の中間調が続く画像を初期と20万枚画像形成後に取得し、現像ローラ2周目の現像ローラ1周目のベタ画像が現像された領域とそうでない領域との画像濃度を反射濃度計(東京電色社製の型番TC−6D)を用いて測定し、その差を求め下記基準で評価した。結果を表2に示す。
「◎」:0.003未満
「○」:0.003以上0.006未満
「△」:0.006以上0.020未満
「×」:0.020以上
図1に示す構造の現像装置(現像ローラの周速度Vs:406mm/sec,感光体ドラムの周速度Vp:205mm/sec,感光体ドラム−現像ローラ間距離:0.3mm)に、作製した二成分現像剤を投入してベタ画像を感光体ドラム表面に形成し、感光体ドラム表面のベタ画像をセロハンテープで剥がし取り、単位面積当たりのキャリア付着による白抜けの個数を下記基準で評価した。評価結果を表2に示す。
「◎」:キャリア付着が全く見られない。
「○」:僅かなキャリア付着が見られるが実使用上問題のない範囲である。
「△」:キャリア付着が見られ使用できない。
「×」:キャリア付着が強く見られ全く使用できない。
5 感光体ドラム
Claims (6)
- 注入型画像解析粒度分布計で測定されるO.Bluntnessの体積モーメント平均D[4,3]が65%以上80%以下で、
ISO Roundnessの体積モーメント平均D[4,3]が80%以上86%以下であることを特徴とするキャリア芯材。 - フェライト粒子から構成されるキャリア芯材であって、フェライト粒子の組成が、MnO:35mol%以上55mol%以下、Fe2O3:45mol%以上65mol%以下を含有し、その一部をSrO:0.1mol%以上1.0mol%以下、SnO:0.1mol%以上1.0mol%以下で置換したものである請求項1に記載のキャリア芯材。
- 飽和磁化σSが75Am2/kg以上88Am2/kg以下である請求項1又は2に記載のキャリア芯材。
- 細孔容積が0.01cm3/g以下である請求項1から請求項3のいずれかに記載のキャリア芯材。
- 請求項1から請求項4のいずれかに記載のキャリア芯材の表面を樹脂で被覆したことを特徴とする電子写真現像用キャリア。
- 請求項5記載の電子写真現像用キャリアとトナーとを含む電子写真用現像剤。