JP2015193521A - 紫外線透過ガラス及びその製造方法 - Google Patents
紫外線透過ガラス及びその製造方法 Download PDFInfo
- Publication number
- JP2015193521A JP2015193521A JP2014232546A JP2014232546A JP2015193521A JP 2015193521 A JP2015193521 A JP 2015193521A JP 2014232546 A JP2014232546 A JP 2014232546A JP 2014232546 A JP2014232546 A JP 2014232546A JP 2015193521 A JP2015193521 A JP 2015193521A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- ultraviolet
- less
- ppm
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明の紫外線透過ガラスは、厚み0.7mm、波長200nmにおける透過率が10%以上であることを特徴とする。
【選択図】図1
Description
Claims (20)
- 厚み0.7mm、波長200nmにおける透過率が10%以上であることを特徴とする紫外線透過ガラス。
- 厚み0.7mm、波長250nmにおける透過率をT250とし、厚み0.7mm、波長300nmにおける透過率をT300とした場合、T250/T300の値が0.3以上であることを特徴とする請求項1に記載の紫外線透過ガラス。
- 歪点が430℃以上であることを特徴とする請求項1又は2に記載の紫外線透過ガラス。
- 30〜380℃の温度範囲における平均線熱膨張係数が30×10−7〜100×10−7/℃であることを特徴とする請求項1〜3の何れかに記載の紫外線透過ガラス。
- 軟化点が1000℃以下であることを特徴とする請求項1〜4の何れかに記載の紫外線透過ガラス。
- ガラス組成として、質量%で、SiO2 50〜80%、Al2O3+B2O3 1〜45%、Li2O+Na2O+K2O 0〜25%、MgO+CaO+SrO+BaO 0〜25%を含有することを特徴とする請求項1〜5の何れかに記載の紫外線透過ガラス。
- ガラス組成として、質量%で、SiO2 50〜80%、Al2O3 1〜20%、B2O3 3〜25%、MgO 0〜10%、CaO 0〜15%、SrO 0〜7%、BaO 0〜7%、Na2O 0〜15%、K2O 0〜10%を含有することを特徴とする請求項1〜6の何れかに記載の紫外線透過ガラス。
- ガラス組成として、質量%で、SiO2 55〜70%、Al2O3 3〜15%、B2O3 5〜20%、MgO 0〜5%、CaO 0〜10%、SrO 0〜5%、BaO 0〜5%、Na2O 5〜15%、K2O 0〜10%を含有することを特徴とする請求項1〜7の何れかに記載の紫外線透過ガラス。
- Fe2O3+TiO2の含有量が100ppm以下であることを特徴とする請求項1〜8の何れかに記載の紫外線透過ガラス。
- Sb2O3の含有量が1000ppm以下であることを特徴とする請求項1〜9の何れかに記載の紫外線透過ガラス。
- SnO2の含有量が2000ppm以下であることを特徴とする請求項1〜10の何れかに記載の紫外線透過ガラス。
- F2+Cl2+SO3の含有量が10〜10000ppmであることを特徴とする請求項1〜11の何れかに記載の紫外線透過ガラス。
- 液相粘度が104.0dPa・s以上であることを特徴とする請求項1〜12の何れかに記載の紫外線透過ガラス。
- 平板形状であり、そのサイズが100mm×100mm以上であることを特徴とする請求項1〜13の何れかに記載の紫外線透過ガラス。
- 平板形状であり、その板厚が2.0mm以下であることを特徴とする請求項1〜14の何れかに記載の紫外線透過ガラス。
- 平板形状であり、その表面の表面粗さRaが10nm以下であることを特徴とする請求項1〜15の何れかに記載の紫外線透過ガラス。
- 請求項1〜16の何れかに記載の紫外線透過ガラスの製造方法であって、ガラス原料の一部に金属シリコンを用いることを特徴とする紫外線透過ガラスの製造方法。
- 請求項1〜16の何れかに記載の紫外線透過ガラスの製造方法であって、ガラス原料の一部にフッ化アルミニウムを用いることを特徴とする紫外線透過ガラスの製造方法。
- 請求項1〜16の何れかに記載の紫外線透過ガラスの製造方法であって、ガラス原料の一部に金属シリコン及びフッ化アルミニウムを用いることを特徴とする紫外線透過ガラスの製造方法。
- オーバーフローダウンドロー法で平板形状に成形することを特徴とする請求項17〜19の何れかに記載の紫外線透過ガラスの製造方法。