JP2015138904A - 高誘電率フィルム及びフィルムコンデンサ - Google Patents
高誘電率フィルム及びフィルムコンデンサ Download PDFInfo
- Publication number
- JP2015138904A JP2015138904A JP2014010307A JP2014010307A JP2015138904A JP 2015138904 A JP2015138904 A JP 2015138904A JP 2014010307 A JP2014010307 A JP 2014010307A JP 2014010307 A JP2014010307 A JP 2014010307A JP 2015138904 A JP2015138904 A JP 2015138904A
- Authority
- JP
- Japan
- Prior art keywords
- film
- inorganic filler
- dielectric constant
- cross
- high dielectric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(2)フィルム断面における無機フィラーの平均面積占有率の1.2倍以上の無機フィラーの面積占有率を有する格子が膜厚方向に連続している部分を少なくとも2か所有する、(1)の高誘電率フィルム。
ポリフッ化ビニリデン10重量部をN,N−ジメチルホルムアミド40重量部に溶融させた。チタン酸バリウム8.5重量部を炭酸プロピレン35重量部に分散させた。得られたポリフッ化ビニリデンの溶融液とチタン酸バリウムの分散液を混合し、超音波振動を与えることによってチタン酸バリウムを分散させて塗料を得た。得られた塗料を金属板にアプリケータで250μmのWet厚さで塗工した。塗料を塗工した金属板を170℃で5分間焼成し、その後、金属板を常温に冷却し、フィルムを剥離して、ポリフッ化ビニリデンに20体積%のチタン酸バリウムが分散したフィルムを得た。
焼成温度を200℃に変えた以外は実施例1と同様の方法でフィルムを得た。
得られたフィルムの断面写真の一部を図2に示す。このフィルムでは、チタン酸バリウムが実施例1のフィルムよりもさらに不均一に分散しており、格子中のチタン酸バリウムの面積占有率がフィルム断面におけるチタン酸バリウムの平均面積占有率(15.5%)の1.2倍以上である格子が膜厚方向に連続している部分が4か所あった(図2の太線で囲んだ部分)。
炭酸プロピレンを用いずに、チタン酸バリウムを、超音波振動に代えて機械的シェアをかけて分散させた以外は実施例2と同様の方法でフィルムを得た。
チタン酸バリウムを、超音波振動に代えて機械的シェアをかけて分散させた以外は実施例2と同様の方法でフィルムを得た。
Claims (2)
- 無機フィラーを含む高誘電率フィルムであって、膜厚の10倍の長さの任意のフィルム断面を選び、1辺が膜厚の1/2の長さの格子で区切って観察した際に、フィルム断面における無機フィラーの平均面積占有率の1.2倍以上の無機フィラーの面積占有率を有する格子を膜厚方向に連続して有する高誘電率フィルム。
- フィルム断面における無機フィラーの平均面積占有率の1.2倍以上の無機フィラーの面積占有率を有する格子が膜厚方向に連続している部分を少なくとも2か所有する、請求項1の高誘電率フィルム。