JP2009505807A - 光輝性複層塗膜の形成方法 - Google Patents
光輝性複層塗膜の形成方法 Download PDFInfo
- Publication number
- JP2009505807A JP2009505807A JP2008510345A JP2008510345A JP2009505807A JP 2009505807 A JP2009505807 A JP 2009505807A JP 2008510345 A JP2008510345 A JP 2008510345A JP 2008510345 A JP2008510345 A JP 2008510345A JP 2009505807 A JP2009505807 A JP 2009505807A
- Authority
- JP
- Japan
- Prior art keywords
- base coat
- pigment
- paint
- containing aqueous
- coat paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
分が10〜45質量%の水性第1ベースコート光輝性塗料を塗装して第1ベースコート塗膜を形成し、第2ステージにおいて、該第1ベースコート塗膜上に、塗膜塗料固形分が10〜40質量%の水性第2ベースコート光輝性塗料を塗装して第2ベースコート塗膜を形成することからなり、水性第1ベースコート光輝性塗料と水性第2ベースコート光輝性塗料との塗料固形分比率を1.1/1〜4/1である塗膜形成方法が開示されている。しかしながら、該塗膜形成方法では、第2ステージにおいて、第1ベースコート塗膜上に第2ベースコート塗膜を形成した際に、該塗膜界面において、両塗膜間の塗料固形分差に起因すると考えられる混層が生じ、該界面付近で光輝性顔料の配向が乱れ、光輝感が低下することがあるという問題がある。
(1) 被塗物上に、光輝性顔料含有水性ベースコート塗料(A1)を塗装して第1ベー
スコート塗膜を形成せしめ、
(2) 未硬化の第1ベースコート塗膜上に光輝性顔料含有水性ベースコート塗料(A2
)を塗装して第2ベースコート塗膜を形成せしめ、そして
(3) 両塗膜を加熱硬化させる
段階を含んでなる光輝性複層塗膜の形成方法であって、
(i) 光輝性顔料含有水性ベースコート塗料(A1)が、15質量%以上45質量%未
満の塗料固形分を有するものであり;
(ii) 光輝性顔料含有水性ベースコート塗料(A2)が、5質量%以上15質量%未満
の塗料固形分を有するものであり;
(iii)光輝性顔料含有水性ベースコート塗料(A1)が、平均一次粒子径が1μm以下
の無機微粒子を含有するものである
ことを特徴とする光輝性複層塗膜の形成方法を提供するものである。
囲内であることが好適であり、プレヒートの時間は約30秒間〜約10分間、特に約1〜約5分間の範囲内であることが好ましい。クリヤーコート塗料の塗装は、それ自体既知の手段により、例えば、回転霧化方式の静電塗装機、エアレススプレー塗装機、エアスプレー塗装機等の塗装機を用いて行うことができる。
硬化剤(b)との含有比率は、これら両成分の合計固形分量を基準にして、前者は50〜90質量%、特に60〜85質量%、そして後者は10〜50質量%、特に15〜40質量%の範囲内にあることが好ましい。
における光輝性顔料の配向の乱れが減少して、優れた光輝感を有する塗膜が形成されるものが考えられる。
光輝性顔料、染料等を含有させることができ、さらに、体質顔料、紫外線吸収剤、消泡剤、増粘剤、防錆剤、表面調整剤等を適宜含有せしめることもできる。
製造例1
温度計、サーモスタット、撹拌器、還流冷却器及び滴下装置を備えた反応容器に脱イオン水100部及びアクアロンKH−10(注1)0.5部を仕込み、窒素気流中で撹拌混合し、80℃に昇温した。次いで、下記のモノマー乳化物(1)のうちの全量の1%及び3%過硫酸アンモニウム水溶液10.3部を反応容器内に導入し、80℃で15分間保持した。その後、残りのモノマー乳化物(1)を3時間かけて反応容器内に滴下し、滴下終了後1時間熟成を行なった。その後、下記のモノマー乳化物(2)を2時間かけて滴下し、1時間熟成した後、2−(ジメチルアミノ)エタノール5%水溶液42部を反応容器に徐々に加えながら30℃まで冷却し、100メッシュのナイロンクロスで濾過しながら排出し、平均粒子径100nm(サブミクロン粒度分布測定装置「COULTER N4型」(ベックマン・コールター社製、商品名)を用いて、脱イオン水で希釈し20℃で測定した)、酸価32mgKOH/g、水酸基価48mgKOH/g及び固形分30%のアクリル樹脂エマルション(B1)を得た。
アンモニウム塩:第一工業製薬株式会社製、商品名、有効成分:97%。
温度計、サーモスタット、撹拌器、還流冷却器及び滴下装置を備えた反応容器に脱イオン水45部、アクアロンKH−10 0.5部を仕込み、窒素気流中で撹拌混合し、80℃に昇温した。次いで下記のモノマー乳化物(3)のうちの全量の1%及び3%過硫酸アンモニウム水溶液10.3部とを反応容器内に導入し80℃で15分間保持した。その後、残りのモノマー乳化物(3)を3時間かけて反応容器内に滴下し、滴下終了後1時間熟成を行なった。その後、下記のモノマー乳化物(4)を2時間かけて滴下し、1時間熟成した後、30℃まで冷却し、100メッシュのナイロンクロスで濾過しながら排出し、酸価32mgKOH/g、水酸基価48mgKOH/g及び固形分48%のアクリル樹脂エマルション(B2)を得た。
温度計、サーモスタット、撹拌器、還流冷却器及び滴下装置を備えた反応容器に脱イオン水55部、アクアロンKH−10 0.5部を仕込み、窒素気流中で撹拌混合し、80℃に昇温した。次いで下記のモノマー乳化物(5)のうちの全量の1%及び3%過硫酸アンモニウム水溶液10.3部とを反応容器内に導入し80℃で15分間保持した。その後、残りのモノマー乳化物(5)を3時間かけて反応容器内に滴下し、滴下終了後1時間熟成を行なった。その後、下記のモノマー乳化物(6)を2時間かけて滴下し、1時間熟成した後、30℃まで冷却し、100メッシュのナイロンクロスで濾過しながら排出し、酸価32mgKOH/g、水酸基価48mgKOH/g及び固形分43%のアクリル樹脂エマルション(B3)を得た。
製造例1におけるモノマー乳化物(1)を下記モノマー乳化物(7)に替え、モノマー乳化物(2)を下記モノマー乳化物(8)に替える以外は、製造例1と同様にして、酸価44mgKOH/g、水酸基価62mgKOH/g及び固形分30%のアクリル樹脂エマルション(B4)を得た。
製造例1におけるモノマー乳化物(1)を下記モノマー乳化物(9)に替え、モノマー乳化物(2)を下記モノマー乳化物(10)に替える以外は、製造例1と同様にして、酸
価19mgKOH/g、水酸基価24mgKOH/g及び固形分30%のアクリル樹脂エマルション(B5)を得た。
製造例6
温度計、サーモスタット、撹拌器、還流冷却器及び滴下装置を備えた反応容器にエチレングリコールモノブチルエーテル35部を仕込み、撹拌しながら100℃まで昇温した後、n−ブチルアクリレート30部、メチルメタクリレート17部、2−エチルヘキシルメタクリレート30部、スチレン5部、2−ヒドロキシエチルメタクリレート10部、メタクリル酸8部及びアゾビスイソブチロニトリル1部の混合物を、100℃に保ったまま、滴下ポンプを利用して4時間かけて一定速度で滴下した。滴下終了後100℃に1時間保ち、撹拌を続けた。その後、2,2’−アゾビス(2,4−ジメチルバレロニトリル)0.5部をエチレングリコールモノブチルエーテル10部に溶解させたものを1時間かけて一定速度で滴下し、さらに1時間115℃に保ちアクリル樹脂溶液を得た。反応終了後、2−(ジメチルアミノ)エタノールで当量中和し、さらに、エチレングリコールモノブチルエーテルを添加して固形分含有率が55%のアクリル樹脂溶液を得た。
製造例7
製造例6で得られたアクリル樹脂溶液180部、脱イオン水360部、サーフィノール104A(商品名、エアープロダクツ社製消泡剤、固形分:50%)6部及びネオライトSP−300(商品名、竹原化学工業社製、炭酸カルシウム粉末、平均一次粒子径:0.15μm)250部を、ペイントコンディショナー中でガラスビーズ媒体を加えて、室温で1時間混合分散し、無機微粒子分散液(C1)を得た。
製造例6で得られたアクリル樹脂溶液180部、脱イオン水360部、サーフィノール104A(商品名、エアープロダクツ社製消泡剤、固形分:50%)6部及びネオライトSP(商品名、竹原化学工業社製、炭酸カルシウム粉末、平均一次粒子径:0.08μm)250部を、ペイントコンディショナー中でガラスビーズ媒体を加えて、室温で1時間混合分散し、無機微粒子分散液(C2)を得た。
製造例6で得られたアクリル樹脂溶液100部、脱イオン水360部、サーフィノール104A(商品名、エアープロダクツ社製消泡剤、固形分:50%)6部及びAEROSIL200(商品名、日本アエロジル社製、シリカ粉末、平均一次粒子径:0.12μm)80部を、ペイントコンディショナー中でガラスビーズ媒体を加えて、室温で1時間混合分散し、無機微粒子分散液(C3)を得た。
製造例6で得られたアクリル樹脂溶液100部、脱イオン水360部、サーフィノール
104A(商品名、エアープロダクツ社製消泡剤、固形分:50%)6部及びAEROSIL380(商品名、日本アエロジル社製、シリカ粉末、平均一次粒子径:0.07μm)80部を、ペイントコンディショナー中でガラスビーズ媒体を加えて、室温で1時間混合分散し、無機微粒子分散液(C4)を得た。
製造例6で得られたアクリル樹脂溶液180部、脱イオン水360部、サーフィノール104A(商品名、エアープロダクツ社製消泡剤、固形分:50%)6部およびSPARWITE W−5HB(商品名、ウィルバーエリス社製、硫酸バリウム粉末、平均一次粒子径:1.6μm)250部を、ペイントコンディショナー中でガラスビーズ媒体を加えて、室温で1時間混合分散し、無機微粒子分散液(C5)を得た。
製造例6で得られたアクリル樹脂溶液180部、脱イオン水360部、サーフィノール104A(商品名、エアープロダクツ社製消泡剤、固形分:50%)6部及びSACHTLEBEN MICRO(商品名、ウィルバーエリス社製、硫酸バリウム粉末、平均一次粒子径:0.7μm)250部を、ペイントコンディショナー中でガラスビーズ媒体を加えて、室温で1時間混合分散し、無機微粒子分散液(C6)を得た。
製造例6で得られたアクリル樹脂溶液180部、脱イオン水360部、サーフィノール104A(商品名、エアープロダクツ社製消泡剤、固形分:50%)6部及びバリエースB−34(商品名、堺化学工業社製、硫酸バリウム粉末、平均一次粒子径:0.3μm)250部を、ペイントコンディショナー中でガラスビーズ媒体を加えて、室温で1時間混合分散し、無機微粒子分散液(C7)を得た。
製造例6で得られたアクリル樹脂溶液180部、脱イオン水360部、サーフィノール104A(商品名、エアープロダクツ社製消泡剤、固形分:50%)6部及びバリファインBF−1(商品名、堺化学工業社製、硫酸バリウム粉末、平均一次粒子径:0.05μm)250部を、ペイントコンディショナー中でガラスビーズ媒体を加えて、室温で1時間混合分散し、無機微粒子分散液(C8)を得た。
製造例6で得られたアクリル樹脂溶液180部、脱イオン水360部、サーフィノール104A(商品名、エアープロダクツ社製消泡剤、固形分50%)6部、バリファインBF−20(商品名、堺化学工業社製、硫酸バリウム粉末、平均粒子径0.03μm)250部を、ペイントコンディショナー中でガラスビーズ媒体を加えて、室温で1時間混合分散し、無機微粒子分散液(C9)を得た。
製造例16
攪拌混合容器にエチレングリコールモノブチルエーテル10部とオクタノール25部の混合溶剤を入れ、アルミニウム顔料ペースト「GX−180A」(商品名、旭化成メタルズ社製、金属含有量:74%)10部及びリン酸基含有樹脂溶液(注2)3部を添加し、攪拌混合してアルミニウム顔料ペースト濃厚液(D1)を得た。
下装置を備えた反応容器にメトキシプロパノール27.5部とイソブタノール2
7.5部の混合溶剤を入れ、110℃に加熱し、スチレン25部、n−ブチルメ
タクリレート27.5部、「イソステアリルアクリレート」(商品名、大阪有機
化学社製、分岐高級アルキルアクリレート)20部、4−ヒドロキシブチルアク
リレート7.5部、リン酸基含有重合性モノマー(注3)15部、2−メタクリ
ロイルオキシエチルアシッドホスフェート12.5部、イソブタノール10部及
びt−ブチルパーオキシオクタノエート4部からなる混合物121.5部を4時
間かけて上記の混合溶剤に加え、さらに、t−ブチルパーオキシオクタノエート
0.5部とイソプロパノール20部からなる混合物を1時間で滴下した。その後
、1時間攪拌熟成して固形分50%のリン酸基含有樹脂溶液を得た。本樹脂のリ
ン酸基による酸価は83mgKOH/g、4−ヒドロキシブチルアクリレートに
由来する水酸基価は29mgKOH/g、重量平均分子量は10000であった
。
及び滴下装置を備えた反応容器にモノブチルリン酸57.5部及びイソブタノー
ル41.1部を入れ、空気通気下でグリシジルメタクリレート42.5部を2時
間で滴下した後、さらに1時間攪拌熟成した。その後、イソプロパノ−ル59部
を加えて、固形分50%のリン酸基含有重合性モノマー溶液を得た。リン酸基に
よる酸価は285mgKOH/gであった。
攪拌混合容器にエチレングリコールモノブチルエーテル10部とオクタノール25部の混合溶剤を入れ、アルミニウム顔料ペースト「GX−180A」(旭化成メタルズ社製、金属含有量:74%)20部及びリン酸基含有樹脂溶液6部を添加し、攪拌混合してアルミニウム顔料ペースト濃厚液(D2)を得た。
攪拌混合容器にエチレングリコールモノブチルエーテル10部とオクタノール25部の混合溶剤を入れ、アルミニウム顔料ペースト「GX−180A」30部、リン酸基含有樹脂溶液9部を添加し、攪拌混合してアルミニウム顔料ペースト濃厚液(D3)を得た。
攪拌混合容器にエチレングリコールモノブチルエーテル10部とオクタノール25部の混合溶剤を入れ、アルミニウム顔料ペースト「GX−180A」40部、リン酸基含有樹脂溶液12部を添加し、攪拌混合してアルミニウム顔料ペースト濃厚液(D4)を得た。
攪拌混合容器にエチレングリコールモノブチルエーテル10部とオクタノール25部の混合溶剤を入れ、アルミニウム顔料ペースト「GX−180A」50部、リン酸基含有樹脂溶液15部を添加し、攪拌混合してアルミニウム顔料ペースト濃厚液(D5)を得た。
攪拌混合容器にエチレングリコールモノブチルエーテル10部とオクタノール25部の混合溶剤を入れ、アルミニウム顔料ペースト「GX−180A」60部、リン酸基含有樹脂溶液18部を添加し、攪拌混合してアルミニウム顔料ペースト濃厚液(D6)を得た。
製造例22
攪拌機、還流冷却器、水分離器及び温度計を備えた反応器に、トリメチロールプロパン109部、1,6−ヘキサンジオール141部、ヘキサヒドロ無水フタル酸126部及びアジピン酸120部を仕込み、160℃〜230℃の間を3時間かけて昇温させた後、2
30℃で4時間縮合反応させた。次いで、得られた縮合反応生成物にカルボキシル基を付加するために、さらに無水トリメリット酸38.3部を加え、170℃で30分間反応させた後、オクタノールで希釈し、酸価46mgKOH/g、水酸基価150mgKOH/g、重量平均分子量6,400及び固形分濃度70%のポリエステル樹脂溶液(PE)を得た。
製造例23
攪拌混合容器中に製造例16で得たアルミニウム顔料ペースト濃厚液(D1)48部を投入し、該アルミニウム顔料ペースト濃厚液(D1)を攪拌しながら、メラミン樹脂(E1)(メチル−ブチル混合エーテル化メラミン樹脂、重量平均分子量:2,000、メチル基とブチル基のモル数の和に対するブチル基のモル比:50mol%、固形分:70%)43部を添加した。さらに、攪拌を続けながら、製造例7で得た無機微粒子分散液(C1)32部及び製造例1で得たアクリル樹脂エマルション(B1)233部を添加して混合した。得られた混合物に2−(ジメチルアミノ)エタノール及び脱イオン水を添加しそして必要に応じて「SNシックナー660T」(商品名、サンノプコ社製、ウレタン会合型増粘剤)を加えて粘度を調節して、pH8.0、塗料固形分29%の光輝性顔料含有水性ベースコート塗料(A1−1)を得た。
下記表1に示す種類及び量のアクリル樹脂エマルション、無機微粒子分散液、アルミニウム顔料ペースト濃厚液及びメラミン樹脂を用い、製造例23と同様に操作して、下記表1に示す塗料固形分を有する各光輝性顔料含有水性ベースコート塗料(A1−2)〜(A1−27)を得た。
攪拌混合容器中に製造例16で得たアルミニウム顔料ペースト濃厚液(D1)48部を投入し、該アルミニウム顔料ペースト濃厚液(D1)を攪拌しながら、メラミン樹脂(E1)(メチル−ブチル混合エーテル化メラミン樹脂、重量平均分子量:2,000、メチル基とブチル基のモル数の和に対するブチル基のモル比:50mol%、固形分:70%)43部を添加した。さらに、攪拌を続けながら、製造例14で得た無機微粒子分散液(C8)43部、製造例1で得たアクリル樹脂エマルション(B1)117部及び製造例22で得たポリエステル樹脂溶液(PE)50部を添加して混合した。得られた混合物に2−(ジメチルアミノ)エタノール及び脱イオン水を添加して、pH8.0及び塗料固形分28%の光輝性顔料含有水性ベースコート塗料(A1−28)を得た。
下記表1に示す種類及び量のアクリル樹脂エマルション及びポリエステル樹脂溶液、無機微粒子分散液、アルミニウム顔料ペースト濃厚液及びメラミン樹脂を用い、製造例50と同様に操作して、下記表1に示す塗料固形分を有する各光輝性顔料含有水性ベースコート塗料(A1−29)〜(A1−33)を得た。
製造例56
攪拌混合容器中に、製造例20で得たアルミニウム顔料ペースト濃厚液(D5)100部を投入し、該アルミニウム顔料ペースト濃厚液(D5)を攪拌しながら、メラミン樹脂(E5)(メチルエーテル化メラミン樹脂、重量平均分子量:800、メチル基とブチル基のモル数の和に対するブチル基のモル比:0mol%、固形分:80%)を38部添加した。さらに攪拌を続けながら、製造例1で得たアクリル樹脂エマルション(B1)233部を添加して混合した。得られた混合物に「プライマルASE−60」(商品名、ロームアンドハース社製、ポリアクリル酸系増粘剤)、2−(ジメチルアミノ)エタノール及び脱イオン水を添加して、pH8.0、塗料固形分9%の光輝性顔料含有水性ベースコート塗料(A2−1)を得た。
下記表2に示す種類及び量のアクリル樹脂エマルション、無機微粒子分散液、アルミニウム顔料ペースト濃厚液及びメラミン樹脂を用い、製造例56と同様に操作して、下記表2に示す塗料固形分を有する各光輝性顔料含有水性ベースコート塗料(A2−2)〜(A2−14)を得た。
攪拌混合容器中に製造例20で得たアルミニウム顔料ペースト濃厚液(D5)100部を投入し、該アルミニウム顔料ペースト濃厚液(D5)を攪拌しながら、メラミン樹脂(E5)(メチルエーテル化メラミン樹脂、重量平均分子量:800、メチル基とブチル基のモル数の和に対するブチル基のモル比:0mol%、固形分:80%)38部を添加した。さらに、攪拌を続けながら、製造例1で得たアクリル樹脂エマルション(B1)117部及び製造例22で得たポリエステル樹脂溶液(PE)50部を添加して混合した。得られた混合物に、「プライマルASE−60」(商品名、ロームアンドハース社製、ポリアクリル酸系増粘剤)、2−(ジメチルアミノ)エタノール及び脱イオン水を添加して、pH8.0及び塗料固形分9%の光輝性顔料含有水性ベースコート塗料(A2−15)を得た。
下記表2に示す種類及び量のアクリル樹脂エマルション及びポリエステル樹脂溶液、無機微粒子分散液、アルミニウム顔料ペースト濃厚液及びメラミン樹脂を用い、製造例70と同様に操作して、下記表2に示す塗料固形分を有する各光輝性顔料含有水性ベースコート塗料(A2−16)〜(A2−18)を得た。
攪拌混合容器中に、製造例20で得たアルミニウム顔料ペースト濃厚液(D5)87部を投入し、該アルミニウム顔料ペースト濃厚液(D5)を攪拌しながら、上記メラミン樹脂(E5)を38部添加した。さらに攪拌を続けながら、製造例15で得た無機微粒子分散液(C9)64部及び製造例1で得たアクリル樹脂エマルション(B1)233部を添加して混合した。得られた混合物に上記「プライマルASE−60」、2−(ジメチルアミノ)エタノール及び脱イオン水を添加して、pH8.0、塗料固形分9%の光輝性顔料含有水性ベースコート塗料(A2−19)を得た。
製造例74において、無機微粒子分散液(C9)64部を無機微粒子分散液(C9)32部に替える以外は、製造例63と同様に操作して、pH8.0、塗料固形分9%の光輝性顔料含有水性ベースコート塗料(A2−20)を得た。
縦45cm×横30cm×厚さ0.8mmのりん酸亜鉛処理された冷延鋼板に「エレクロンGT−10」(商品名、関西ペイント社製、熱硬化エポキシ樹脂系カチオン電着塗料)を乾燥膜厚20μmになるように電着塗装し、170℃で30分加熱して硬化させてから、その上に中塗り塗料「アミラックTP−65−2」(商品名、関西ペイント社製、ポリエステル樹脂・アミノ樹脂系、有機溶剤型中塗り塗料)を乾燥膜厚40μmになるように塗装し、140℃で30分加熱して硬化させて試験用被塗物とした。
温度23℃及び湿度75%の塗装環境において、前記試験用被塗物上に、製造例23で得られた光輝性顔料含有水性ベースコート塗料(A1−1)を、回転霧化型のベル型塗装機「ABBカートリッジベル塗装機」(商品名、ABB社製)を用いて、表3に示す乾燥膜厚となるように塗装し、第1ベース塗膜を形成せしめた。1分間のインターバルをおいた後、前記試験用被塗物上に形成された第1ベース塗膜上に、製造例56で得られた光輝性顔料含有水性ベースコート塗料(A2−1)を、回転霧化型のベル型塗装機「ABBカートリッジベル塗装機」(商品名、ABB社製)を用いて、表3に示す乾燥膜厚となるように塗装し、第2ベース塗膜を形成せしめた。2分間のインターバルをおいた後、80℃で3分間プレヒートし、次いで、その未硬化のベースコート塗面上にマジクロンKINO−1200(商品名、関西ペイント社製、アクリル樹脂系溶剤型上塗りクリヤーコート塗料)を乾燥膜厚40μmとなるように塗装し、7分間放置した後、140℃で30分間加熱してこれらの塗膜を同時に硬化させることにより試験板を作製した。
表3に示す組み合わせ及び乾燥膜厚となるように、光輝性顔料含有水性ベースコート塗料(A1−2)〜(A1−33)を塗装して第1ベース塗膜を形成せしめた後、光輝性顔料含有水性ベースコート塗料(A2−1)〜(A2−20)を塗装して第2ベース塗膜を形成する以外は、実施例1と同様に操作して、実施例2〜42及び比較例1〜6の試験板を作製した。
上記実施例1〜42及び比較例1〜6で得られた各試験板についての塗膜性能試験結果を表3に示す。
FF値=受光角15度のL値/受光角110度のL値。
FF値が大きいほど、観察角度(受光角)によるL値(明度)の変化が大きく、フリップフロップ性に優れていることを示す。
◎:目視の角度によるメタリック感の変化が大きく、フリップフロップ性に優れ、メ
タリックムラもほとんど認められず、極めて優れた光輝感を有する。
○:メタリックムラがわずかに認められるが、目視の角度によるメタリック感の変化
が大きく、フリップフロップ性に優れ、良好な光輝感を有する。
△:目視の角度によるメタリック感の変化がやや小さく、フリップフロップ性がやや
劣り、光輝感はやや劣る。
×:目視の角度によるメタリック感の変化が小さく、フリップフロップ性が劣り、光
輝感は劣る。
◎:極めて優れた平滑性を有する。
○:優れた平滑性を有する。
△:平滑性がやや劣る。
×:平滑性が劣る。
0℃においてそのテープを急激に剥離した後のゴバン目塗膜の残存数を調べた。
◎:100個残存し、カッターによる切り込みの縁も滑らかである。
○:100個残存するが、カッターの切り込みの交差点において塗膜の小さなハガレ
が生じている。
△:99〜81個残存。
×:80個以下残存。
Claims (23)
- (1) 被塗物上に、光輝性顔料含有水性ベースコート塗料(A1)を塗装して第1ベー
スコート塗膜を形成せしめ、
(2) 未硬化の第1ベースコート塗膜上に光輝性顔料含有水性ベースコート塗料(A2
)を塗装して第2ベースコート塗膜を形成せしめ、そして
(3) 両塗膜を加熱硬化させる
段階を含んでなる光輝性複層塗膜の形成方法であって、
(i) 光輝性顔料含有水性ベースコート塗料(A1)が、15質量%以上45質量%未
満の塗料固形分を有するものであり;
(ii) 光輝性顔料含有水性ベースコート塗料(A2)が、5質量%以上15質量%未満
の塗料固形分を有するものであり;
(iii)光輝性顔料含有水性ベースコート塗料(A1)が、平均一次粒子径が1μm以下
の無機微粒子を含有するものである
ことを特徴とする光輝性複層塗膜の形成方法。 - 光輝性顔料含有水性ベースコート塗料(A1)が、20質量%以上40質量%未満の塗料固形分を有するものである請求項1に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A2)が、6質量%以上12質量%未満の塗料固形分を有するものである請求項1に記載の方法。
- 無機微粒子の顔料質量濃度が2〜30%の範囲内である請求項1に記載の方法。
- 無機微粒子が硫酸バリウム微粒子である請求項1に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)及び光輝性顔料含有水性ベースコート塗料(A2)が平均一次粒子径が1μm以下の硫酸バリウム微粒子を含有し、光輝性顔料含有水性ベースコート塗料(A1)に含まれる硫酸バリウム微粒子の顔料質量濃度(%)が、光輝性顔料含有水性ベースコート塗料(A2)に含まれる硫酸バリウム微粒子の顔料質量濃度(%)より5以上高い請求項1に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)及び光輝性顔料含有水性ベースコート塗料(A2)が、水溶性もしくは水分散性の基体樹脂(a)、硬化剤(b)及び光輝性顔料(c)を含んでなる水性塗料である請求項1に記載の方法。
- 基体樹脂(a)がカルボキシル基及び水酸基を有するアクリル樹脂又はポリエステル樹脂である請求項7に記載の方法。
- 光輝性顔料(c)を基体樹脂(a)と硬化剤(b)との合計固形分量100質量部あたり2〜50質量部の範囲内で含有する請求項8に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)が、光輝性顔料(c)を、1〜30%の顔料質量濃度で含有する請求項7に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A2)が、光輝性顔料(c)を、5〜40%の範囲内の顔料質量濃度で含有する請求項7に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)に含まれる光輝性顔料(c)の顔料質量濃度(PA1)と光輝性顔料含有水性ベースコート塗料(A2)に含まれる光輝性顔料(
c)の顔料質量濃度(PA2)の比PA1/PA2が1/5〜1/1.1の範囲内にある請求項7に記載の方法。 - 硬化剤(b)がアミノ樹脂、特にメラミン樹脂である請求項7に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)及び光輝性顔料含有水性ベースコート塗料(A2)がメラミン樹脂を含有し、光輝性顔料含有水性ベースコート塗料(A1)に含まれるメラミン樹脂の重量平均分子量(MA1)が800〜5,000の範囲内であり、光輝性顔料含有水性ベースコート塗料(A2)に含まれるメラミン樹脂の重量平均分子量(MA2)が400〜4,000の範囲内であり、且つ光輝性顔料含有水性ベースコート塗料(A1)に含まれるメラミン樹脂の重量平均分子量(MA1)が光輝性顔料含有水性ベースコート塗料(A2)に含まれるメラミン樹脂の重量平均分子量(MA2)よりも300〜4,000だけ大きい請求項1又は6に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)及び光輝性顔料含有水性ベースコート塗料(A2)が、メチルエーテル化メラミン樹脂、ブチルエーテル化メラミン樹脂、及びメチル−ブチル混合エーテル化メラミン樹脂からなる群より選ばれる少なくとも一種のアルキルエーテル化メラミン樹脂を含有し、光輝性顔料含有水性ベースコート塗料(A1)に含まれるアルキルエーテル化メラミン樹脂のメチル基とブチル基のモル数の和に対するブチル基のモル比(mol%)が、光輝性顔料含有水性ベースコート塗料(A2)に含まれるアルキルエーテル化メラミン樹脂のメチル基とブチル基のモル数の和に対するブチル基のモル比(mol%)より30以上大きい請求項1又は6に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)及び光輝性顔料含有水性ベースコート塗料(A2)がアルキルエーテル化メラミン樹脂を含有し、光輝性顔料含有水性ベースコート塗料(A1)に含まれるアルキルエーテル化メラミン樹脂がメチル−ブチル混合エーテル化メラミン樹脂及び/又はブチルエーテル化メラミン樹脂であり、そして光輝性顔料含有水性ベースコート塗料(A2)に含まれるアルキルエーテル化メラミン樹脂がメチルエーテル化メラミン樹脂である請求項1又は6に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)の塗料固形分(SA1)と光輝性顔料含有水性ベースコート塗料(A2)の塗料固形分(SA2)の比SA1/SA2が1.5/1〜5/1の範囲内にある請求項1に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)の塗料固形分(SA1)が20〜39質量%の範囲内であり、光輝性顔料含有水性ベースコート塗料(A2)の塗料固形分(SA2)が7〜9質量%であり、且つ光輝性顔料含有水性ベースコート塗料(A1)の塗料固形分(SA1)と光輝性顔料含有水性ベースコート塗料(A2)の塗料固形分(SA2)の比SA1/SA2が2.6/1〜4.5/1の範囲内にある請求項1、6、14、15又は16に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)によって形成される塗膜の乾燥膜厚(TA1)と、光輝性顔料含有水性ベースコート塗料(A2)によって形成される塗膜の乾燥膜厚(TA2)の比率TA1/TA2が1.5/1〜5/1の範囲内にある請求項1に記載の方法。
- 光輝性顔料含有水性ベースコート塗料(A1)によって形成される塗膜の乾燥膜厚が5〜15μmの範囲内にあり、そして光輝性顔料含有水性ベースコート塗料(A2)によって形成される塗膜の乾燥膜厚が1〜5μmの範囲内にある請求項19に記載の方法。
- 被塗物が、電着塗装及び中塗塗装が順次施されてなる自動車車体である請求項1に記載の方法。
- 形成される未硬化の第2ベースコート塗膜上にクリヤーコート塗料を塗装した後、加熱して第1ベースコート塗膜、第2ベースコート塗膜およびクリヤーコート塗膜を同時に硬化させる請求項1に記載の方法
- 請求項22に記載の方法により光輝性複層塗膜が形成された物品。