JP2009084560A - 液晶組成物および液晶表示素子 - Google Patents
液晶組成物および液晶表示素子 Download PDFInfo
- Publication number
- JP2009084560A JP2009084560A JP2008211776A JP2008211776A JP2009084560A JP 2009084560 A JP2009084560 A JP 2009084560A JP 2008211776 A JP2008211776 A JP 2008211776A JP 2008211776 A JP2008211776 A JP 2008211776A JP 2009084560 A JP2009084560 A JP 2009084560A
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystal
- component
- crystal composition
- carbons
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 第一成分として大きな光学異方性を有する特定の二環化合物、および第二成分として大きな誘電率異方性を有する特定の四環化合物を含有し、第三成分として特に小さな粘度を有する特定の二環から四環化合物を含有してもよく、そしてネマチック相を有する液晶組成物、およびこの組成物を含有する液晶表示素子である。
【選択図】 なし
Description
1. 第一成分として式(1)で表される化合物、および第二成分として式(2)で表される化合物の群から選択された少なくとも1つの化合物を含有し、そしてネマチック相を有する液晶組成物。
ここで、R1は炭素数1から12のアルキル、炭素数1から12のアルコキシ、炭素数2から12のアルケニル、または任意の水素がフッ素で置き換えられた炭素数2から12のアルケニルであり;X1、X2、X3およびX4は独立して、水素またはフッ素であり;Y1はフッ素、塩素、またはトリフルオロメトキシである。
ここで、R3は、炭素数1から12のアルキル、または炭素数2から12のアルケニルである。
ここで、R1およびR2は独立して、炭素数1から12のアルキル、炭素数1から12のアルコキシ、炭素数2から12のアルケニル、または任意の水素がフッ素で置き換えられた炭素数2から12のアルケニルであり;環B、環C、環D、環E、環Fおよび環Gは独立して、1,4−シクロへキシレン、1,4−フェニレン、2−フルオロ−1,4−フェニレン、または3−フルオロ−1,4−フェニレンである。
ここで、R1およびR2は独立して、炭素数1から12のアルキル、炭素数1から12のアルコキシ、炭素数2から12のアルケニル、または任意の水素がフッ素で置き換えられた炭素数2から12のアルケニルであり;R3は、炭素数1から12のアルキル、または炭素数2から12のアルケニルである。
ここで、R1は、炭素数1から12のアルキル、炭素数1から12のアルコキシ、炭素数2から12のアルケニル、または任意の水素がフッ素で置き換えられた炭素数2から12のアルケニルであり;環Aは独立して、1,4−シクロへキシレン、1,3−ジオキサン−2,5−ジイル、1,4−フェニレン、3−フルオロ−1,4−フェニレン、3,5−ジフルオロ−1,4−フェニレン、または2,5−ピリミジンであり;Z1は独立して、単結合、エチレン、カルボニルオキシ、またはジフルオロメチレンオキシであり;X1およびX2は独立して、水素またはフッ素であり;Y1はフッ素、塩素、またはトリフルオロメトキシであり;nは1または2である。
ここで、R3は、炭素数1から12のアルキル、または炭素数2から12のアルケニルである。
表3において、1,4−シクロヘキシレンに関する立体配置はトランスである。実施例において記号の後にあるかっこ内の番号は好ましい化合物の番号に対応する。(−)の記号はその他の液晶性化合物を意味する。液晶性化合物の含有割合(百分率)は、液晶組成物の全重量に基づいた重量百分率(重量%)であり、液晶組成物にはこの他に不純物が含有している。最後に、組成物の特性値をまとめた。
特開平10−81881に開示された組成物の中から実施例2を選んだ。根拠は、この組成物が化合物(1)、化合物(3−1−1−1)および化合物(4)を含有し、最も粘度が小さいからである。この組成物の成分および特性は下記のとおりである。
V2−BB−2V (1) 15%
3−HBTB−1 (−) 7%
3−HBTB(2CH3)−1 (−) 6%
3−HdB(F,F)TB(2CH3)−1 (−) 12%
3−HBTB(F,F)−F (−) 13%
3−HdB(F,F)TB(F)−F (−) 13%
3−B(F)BTB(F)−F (−) 10%
3−B(F)BTB(F,F)−F (−) 8%
V2−HH−3 (3−1−1−1) 8%
V2−HHB(F)−F (4) 8%
NI=102.7℃;Δn=0.229;Vth=2.08V;η=21.3mPa・s.
実施例1の組成物は、比較例1のそれと比較して、小さな粘度を有する。
V2−BB−2V (1) 9%
3−BB(F)B(F,F)XB(F,F)−F (2−1−1) 4%
4−BB(F)B(F,F)XB(F,F)−F (2−1−1) 5%
V−HH−3 (3−1−1−1) 47%
2−BB(F)B−3 (3−2−3−1) 6%
1−BB(F)B−2V (3−2−3−1) 5%
2−BB(F)B−2V (3−2−3−1) 8%
3−BB(F)B−2V (3−2−3−1) 13%
3−BB(F,F)XB(F,F)−F (4−11−1) 3%
NI=74.0℃;Tc≦−20℃;Δn=0.132;Δε=2.4;Vth=2.68V;η=11.9mPa・s;γ1=37.2mPa・s;τ=3.4ms;VHR−1=99.3%;VHR−2=98.4%;VHR−3=98.2%.
実施例2の組成物は、比較例1のそれと比較して、小さな粘度を有する。
V2−BB−2V (1) 10%
3−BB(F)B(F,F)XB(F,F)−F (2−1−1) 3%
4−BB(F)B(F,F)XB(F,F)−F (2−1−1) 7%
V−HH−3 (3−1−1−1) 44%
1−BB(F)B−2V (3−2−3−1) 8%
2−BB(F)B−2V (3−2−3−1) 8%
V−HHB−1 (3−2−1−1) 4%
3−HHB−CL (4−4−1) 3%
3−HHXB(F,F)−F (4−6−1) 5%
3−HBB−F (4−7−1) 3%
3−BB(F,F)XB(F,F)−F (4−11−1) 5%
NI=72.9℃;Tc≦−20℃;Δn=0.120;Δε=3.5;Vth=2.30V;η=14.2mPa・s;γ1=42.5mPa・s;τ=4.1ms;VHR−1=99.4%;VHR−2=98.5%;VHR−3=98.3%.
実施例3の組成物は、比較例1のそれと比較して、小さな粘度を有する。
V2−BB−2V (1) 5%
3−BB(F)B(F,F)XB(F,F)−F (2−1−1) 4%
4−BB(F)B(F,F)XB(F,F)−F (2−1−1) 4%
5−BB(F)B(F,F)XB(F,F)−F (2−1−1) 3%
3−BB(F)B(F,F)XB(F)−OCF3(2−3−1) 3%
V−HH−3 (3−1−1−1) 45%
1V−HH−3 (3−1−1−1) 10%
1−BB(F)B−2V (3−2−3−1) 8%
3−HHXB(F,F)−F (4−6−1) 15%
3−HHBB(F,F)−F (−) 3%
NI=75.4℃;Tc≦−20℃;Δn=0.100;Δε=3.2;Vth=2.30V;η=16.0mPa・s;γ1=46.3mPa・s;τ=4.8ms;VHR−1=99.1%;VHR−2=98.2%;VHR−3=98.0%.
V2−BB−2V (1) 7%
3−BB(F)B(F,F)XB(F,F)−F (2−1−1) 3%
3−BB(F,F)B(F,F)XB(F,F)−F (2−2−1) 7%
V−HH−3 (3−1−1−1) 40%
1V−HH−3 (3−1−1−1) 5%
1−BB(F)B−2V (3−2−3−1) 7%
2−BB(F)B−2V (3−2−3−1) 8%
3−BB(F)B−2V (3−2−3−1) 6%
5−HBB(F)B−2 (3−3−3−1) 5%
3−BB(F)B(F,F)−F (4−9−1) 7%
3−BB(F,F)XB(F,F)−F (4−11−1) 5%
NI=74.2℃;Tc≦−20℃;Δn=0.143;Δε=4.2;Vth=2.43V;η=18.2mPa・s;γ1=51.0mPa・s;τ=5.4ms;VHR−1=99.3%;VHR−2=98.4%;VHR−3=98.2%.
V2−BB−2V (1) 6%
3−BB(F)B(F,F)XB(F,F)−F (2−1−1) 3%
4−BB(F)B(F,F)XB(F,F)−F (2−1−1) 5%
3−BBB(F,F)XB(F,F)−F (2−8) 4%
V−HH−3 (3−1−1−1) 48%
V−HHB−1 (3−2−1−1) 4%
V2−HHB−1 (3−2−1−1) 4%
1−BB(F)B−2V (3−2−3−1) 5%
3−HHB−CL (4−4−1) 3%
3−HHXB(F,F)−F (4−6−1) 4%
3−HBB(F,F)−F (4−8−1) 5%
3−BB(F,F)XB(F,F)−F (4−11−1) 3%
3−HHBB(F,F)−F (−) 3%
3−HHEBH−3 (−) 3%
NI=80.8℃;Tc≦−20℃;Δn=0.104;Δε=3.0;Vth=2.46V;η=18.0mPa・s;γ1=52.2mPa・s;τ=5.2ms;VHR−1=99.3%;VHR−2=98.3%;VHR−3=98.2%.
V2−BB−2V (1) 13%
4−BB(F)B(F,F)XB(F,F)−F (2−1−1) 6%
3−BBB(F,F)XB(F,F)−F (2−8) 4%
1V−HH−3 (3−1−1−1) 7%
V−HH−5 (3−1−1−1) 20%
3−HH−VFF (3−1−1−2) 15%
V2−HHB−1 (3−2−1−1) 5%
V2−BB(F)B−1 (3−2−3−1) 5%
2−BB(F)B−3 (3−2−3−1) 5%
3−HHB(F,F)−F (4−5−1) 3%
3−HHXB(F,F)−F (4−6−1) 5%
3−PyBB−F (4−10−1) 4%
4−PyBB−F (4−10−1) 4%
5−PyBB−F (4−10−1) 4%
NI=81.4℃;Tc≦−20℃;Δn=0.131;Δε=4.0;Vth=2.24V;η=18.5mPa・s;γ1=53.8mPa・s;τ=5.4ms;VHR−1=99.0%;VHR−2=98.2%;VHR−3=98.0%.
V2−BB−2V (1) 5%
4−BB(F)B(F,F)XB(F,F)−F (2−1−1) 7%
3−BBB(F,F)XB(F)−CL (2−7) 3%
V−HH−3 (3−1−1−1) 54%
1V−HH−3 (3−1−1−1) 3%
1−BB(F)B−2V (3−2−3−1) 8%
2−BB(F)B−2V (3−2−3−1) 6%
3−BB(F,F)XB(F)−OCF3 (4−12−1) 5%
5−GHB(F,F)−F (4−19) 3%
3−HHBB(F,F)−F (−) 3%
4−HHBB(F,F)−F (−) 3%
NI=72.6℃;Tc≦−20℃;Δn=0.108;Δε=2.3;Vth=2.40V;η=15.0mPa・s;γ1=45.2mPa・s;τ=4.3ms;VHR−1=99.4%;VHR−2=98.4%;VHR−3=98.2%.
V2−BB−2V (1) 6%
3−BB(F)B(F,F)XB(F)−OCF3(2−3−1) 5%
V−HH−3 (3−1−1−1) 46%
3−HHB−1 (3−2−1−1) 4%
V2−BB(F)B−1 (3−2−3−1) 5%
V2−BB(F)B−2 (3−2−3−1) 4%
1−BB(F)B−2V (3−2−3−1) 5%
2−BB(F)B−2V (3−2−3−1) 4%
3−HB−CL (4−1−1) 4%
3−HHXB(F,F)−F (4−6−1) 8%
5−PyB(F)XB(F,F)−F (4−21) 3%
5−PyB(F,F)XB(F,F)−F (4−22) 3%
1O1−HBBH−5 (−) 3%
NI=74.3℃;Tc≦−20℃;Δn=0.114;Δε=3.2;Vth=2.33V;η=13.1mPa・s;γ1=41.9mPa・s;τ=3.8ms;VHR−1=99.0%;VHR−2=98.0%;VHR−3=97.8%.
V2−BB−2V (1) 10%
3−BB(F)B(F,F)XB(F,F)−F (2−1−1) 5%
2−HH−3 (3−1−1−1) 24%
3−HH−4 (3−1−1−1) 10%
V−HHB−1 (3−2−1−1) 3%
2−BB(F)B−3 (3−2−3−1) 10%
1−BB(F)B−2V (3−2−3−1) 8%
3−HB−CL (4−1−1) 8%
3−HHXB(F)−F (4−13) 6%
4−BB(F,F)XB(F)−F (4−15) 6%
3−GHXB(F,F)−F (4−20) 5%
3−HHEBH−3 (−) 5%
NI=72.2℃;Tc≦−20℃;Δn=0.141;Δε=2.9;Vth=2.49V;η=19.6mPa・s;γ1=57.5mPa・s;τ=6.2ms;VHR−1=99.0%;VHR−2=97.8%;VHR−3=97.7%.
V2−BB−2V (1) 5%
3−BB(F)B(F,F)XB(F,F)−F (2−1−1) 5%
4−BB(F)B(F,F)XB(F,F)−F (2−1−1) 5%
V−HH−3 (3−1−1−1) 49%
V2−BB(F)B−1 (3−2−3−1) 6%
1−BB(F)B−2V (3−2−3−1) 6%
2−BB(F)B−3 (3−2−3−1) 3%
5−HBB(F)B−2 (3−3−3−1) 3%
5−HBB(F)B−3 (3−3−3−1) 3%
3−HHXB(F,F)−F (4−6−1) 3%
3−HHEB(F,F)−F (4−16) 3%
3−HBEB(F,F)−F (4−17) 3%
3−HGB(F,F)−F (4−18) 3%
1O1−HBBH−5 (−) 3%
NI=85.9℃;Tc≦−20℃;Δn=0.120;Δε=2.6;Vth=2.65V;η=19.7mPa・s;γ1=57.1mPa・s;τ=5.7ms;VHR−1=99.3%;VHR−2=98.5%;VHR−3=98.2%.
V2−BB−2V (1) 5%
3−BB(F)B(F,F)XB(F)−F (2−4) 4%
4−BB(F)B(F,F)XB−OCF3 (2−5) 4%
3−BB(F,F)B(F,F)XB(F)−OCF3 (2−6) 4%
V−HH−3 (3−1−1−1) 30%
3−HH−VFF (3−1−1−2) 15%
7−HB−1 (3−1−2−1) 3%
3−HB−O2 (3−1−2−1) 3%
3−HBB−2 (3−2−2−1) 7%
1−BB(F)B−2V (3−2−3−1) 5%
2−BB(F)B−3 (3−2−3−1) 5%
1V2−BB−F (4−2−1) 3%
1V2−BB−CL (4−3−1) 3%
3−HHXB(F)−OCF3 (4−14) 3%
3−HHBB(F,F)−F (−) 3%
3−HHEBH−3 (−) 3%
NI=70.4℃;Tc≦−20℃;Δn=0.116;Δε=3.9;Vth=2.36V;η=15.1mPa・s;γ1=48.4mPa・s;τ=5.0ms;VHR−1=99.3%;VHR−2=98.1%;VHR−3=98.0%.
V2−BB−2V (1) 5%
3−BB(F)B(F,F)XB(F,F)−F (2−1−1) 3%
4−BB(F)B(F,F)XB(F,F)−F (2−1−1) 7%
V−HH−3 (3−1−1−1) 45%
1V−HH−3 (3−1−1−1) 6%
1−BB(F)B−2V (3−2−3−1) 8%
2−BB(F)B−2V (3−2−3−1) 6%
2−BBB(2F)−4 (3−2−4−1) 4%
5−HBBH−2 (3−3−1−1) 4%
5−HBB(2F)H−3 (3−3−2−1) 3%
5−GHB(F,F)−F (4−19) 3%
3−HHBB(F,F)−F (−) 3%
4−HHBB(F,F)−F (−) 3%
NI=90.2℃;Tc≦−20℃;Δn=0.130;Δε=2.2;Vth=2.70V;η=19.9mPa・s;γ1=57.0mPa・s;τ=6.3ms;VHR−1=99.3%;VHR−2=98.3%;VHR−3=98.3%.
Claims (22)
- 第二成分が式(2−1)で表される化合物の群から選択された少なくとも1つの化合物である請求項2に記載の液晶組成物。
- 液晶組成物の全重量に基づいて、第一成分の含有割合が5重量%から30重量%の範囲であり、そして第二成分の含有割合が5重量%から30重量%の範囲である請求項1から3のいずれか1項に記載の液晶組成物。
- 第三成分が、式(3−1−1)で表される化合物の群から選択された少なくとも1つの化合物である請求項6に記載の液晶組成物。
- 第三成分が、式(3−2−1)で表される化合物の群から選択された少なくとも1つの化合物である請求項6に記載の液晶組成物。
- 第三成分が、式(3−2−3)で表される化合物の群から選択された少なくとも1つの化合物である請求項6に記載の液晶組成物。
- 第三成分が、式(3−3−3)で表される化合物の群から選択された少なくとも1つの化合物である請求項6に記載の液晶組成物。
- 液晶組成物の全重量に基づいて、第三成分の含有割合が40重量%から95重量%の範囲である請求項5から10のいずれか1項に記載の液晶組成物。
- 第四成分として式(4)で表される化合物の群から選択された少なくとも1つの化合物をさらに含有する、請求項1から11のいずれか1項に記載の液晶組成物。
ここで、R1は、炭素数1から12のアルキル、炭素数1から12のアルコキシ、炭素数2から12のアルケニル、または任意の水素がフッ素で置き換えられた炭素数2から12のアルケニルであり;環Aは独立して、1,4−シクロへキシレン、1,3−ジオキサン−2,5−ジイル、1,4−フェニレン、3−フルオロ−1,4−フェニレン、3,5−ジフルオロ−1,4−フェニレン、または2,5−ピリミジンであり;Z1は独立して、単結合、エチレン、カルボニルオキシ、またはジフルオロメチレンオキシであり;X1およびX2は独立して、水素またはフッ素であり;Y1はフッ素、塩素、またはトリフルオロメトキシであり;nは1または2である。 - 第四成分が、式(4−6)で表される化合物の群から選択された少なくとも1つの化合物である請求項13に記載の液晶組成物。
- 第四成分が、式(4−8)で表される化合物の群から選択された少なくとも1つの化合物である請求項13に記載の液晶組成物。
- 第四成分が、式(4−10)で表される化合物の群から選択された少なくとも1つの化合物である請求項13に記載の液晶組成物。
- 第四成分が、式(4−11)で表される化合物の群から選択された少なくとも1つの化合物である請求項13に記載の液晶組成物。
- 第四成分が、式(4−6)で表される化合物の群から選択された少なくとも1つの化合物および式(4−11)で表される化合物の群から選択された少なくとも1つの化合物の混合物である請求項13に記載の液晶組成物。
- 液晶組成物の全重量に基づいて、第四成分の含有割合が5重量%から35重量%の範囲である請求項12から18のいずれか1項に記載の液晶組成物。
- ネマチック相の上限温度が70℃以上であり、波長589nmにおける光学異方性(25℃)が0.08以上であり、そして周波数1kHzにおける誘電率異方性(25℃)が2以上である請求項1から19のいずれか1項に記載の液晶組成物。
- 請求項1から20のいずれか1項に記載の液晶組成物を含有する液晶表示素子。
- 液晶表示素子の動作モードが、TNモード、OCBモード、IPSモード、またはPSAモードであり、液晶表示素子の駆動方式がアクティブマトリックス方式である請求項21に記載の液晶表示素子。