JP2006036953A - 改質ポリエステル組成物及びその製造方法 - Google Patents
改質ポリエステル組成物及びその製造方法 Download PDFInfo
- Publication number
- JP2006036953A JP2006036953A JP2004219927A JP2004219927A JP2006036953A JP 2006036953 A JP2006036953 A JP 2006036953A JP 2004219927 A JP2004219927 A JP 2004219927A JP 2004219927 A JP2004219927 A JP 2004219927A JP 2006036953 A JP2006036953 A JP 2006036953A
- Authority
- JP
- Japan
- Prior art keywords
- modified polyester
- mol
- group
- sulfonic acid
- phosphonium salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】特定の化学構造式で表わされるスルホン酸ホスホニウム塩が共重合された改質ポリエステルを含む組成物であって、
(A)該スルホン酸ホスホニウム塩の共重合量が改質ポリエステルを構成する酸成分に対して0.1〜10モル%であり、
(B)安息香酸及び/又は安息香酸誘導体を該スルホン酸ホスホニウム塩に対して0.1モル%以上20モル%以下となる量含有し、
(C)上記一般式(I)成分1単位とアルキレンテレフタレート2単位から構成される環状3量体を改質ポリエステル組成物の全重量に対して0.1〜1重量%含有する改質ポリエステル組成物、及びベント付き押出機を用いるその改質ポリエステル組成物の製造方法。
【選択図】なし
Description
で表わされるスルホン酸ホスホニウム塩が共重合された改質ポリエステルを含む組成物であって、
(A)該スルホン酸ホスホニウム塩の共重合量が改質ポリエステルを構成する酸成分に対して0.1〜10モル%であり、
(B)安息香酸及び/又は安息香酸誘導体を該スルホン酸ホスホニウム塩に対して0.1モル%以上20モル%以下となる量含有し、
(C)上記一般式(I)成分1単位とアルキレンテレフタレート2単位から構成される環状3量体を改質ポリエステル組成物の全重量に対して0.1〜1重量%含有する改質ポリエステル組成物、
及び(A)上記一般式(I)で表わされるスルホン酸ホスホニウム塩が全繰返し単位当たり0.1〜20モル%共重合された改質ポリエステルと
(B)安息香酸及び/又はパラヒドロキシ安息香酸の合計量を、上記改質ポリエステルに共重合されたスルホン酸ホスホニウム塩の共重合量に対して0.1〜10モル%以下となる量含有するポリエステル組成物とを、
得られる改質ポリエステル組成物が上記一般式(I)で表されるスルホン酸ホスホニウム塩がポリエステルの繰り返し単位当たり0.1〜10モル%含有するように、予め混合してから又は別々にベント付き押出機に投入し、該ベント付き押出機中でエステル交換反応させる改質ポリエステル組成物の製造方法によって達成することができる。
本発明でいう改質ポリエステルは、産業上において通常用いられているものを主成分とするものであれば特に限定はないが、主成分がポリエチレンテレフタレート、ポリトリメチレンテレフタレート、ポリブチレンテレフタレートからなる群の少なくとも1種よりなるポリエステルであることが好ましい。具体的にはテレフタル酸又はその誘導体を主たる酸成分とし、少なくとも1種のグリコール、好ましくはエチレングリコール、トリメチレングリコール及びテトラメチレングリコールよりなる群から選ばれる少なくとも1種のアルキレングリコールをグリコール成分として製造されたポリエステルを主たる対象とする。ここで主成分及び主たる対象とは、ポリエステルの全繰り返し単位中70モル%以上であることを表し、また主たる酸成分とは、ポリエステルを構成するジカルボン酸成分若しくはジカルボン酸誘導体成分のうち、70モル%以上であることを表している。
で表わされる。上記一般式中、Aは芳香族基又は脂肪族基を示し、好ましくは炭素数6〜14の芳香族基又は炭素数1〜14の脂肪族基である。なかでも炭素数6〜14の芳香族基がより好ましい。X1はエステル形成性官能基を示し、具体例として以下のような官能基群等を挙げることができる。
このうちa,dは1以上10以下の整数であり、bは2以上10以下の整数であることが好ましい。更に好ましくはa,dが1以上6以下の整数であり、bが2以上6以下の整数であることである。
X2はX1と同一若しくは異なるエステル形成性官能基又は水素原子を示し、なかでもエステル形成性官能基であることが好ましい。R1、R2、R3及びR4は脂肪族基及び芳香族基よりなる群から選ばれた同一又は異なる基を示す。より好ましくは炭素数1〜10の脂肪族基又は炭素数6〜10の芳香族基である。nは正の整数であり、好ましくは6以下の正の整数である。
アルキレンテレフタレート2単位から構成される環状3量体を改質ポリエステル組成物の全重量に対して0.1〜1重量%含有することが必要である。環状3量体の含有量が0.1重量%より少ないと、染料浸透部が少なくなるためか染色性に劣るようになり、1重量%より多いと紡糸他成形時に口金異物の発生が多くなり、断糸が多発するようになる。
上記一般式(I)で表されるスルホン酸ホスホニウム塩化合物を共重合したポリエステル(以下マスターポリマーと称することがある。)は任意の方法によって製造することができる。例えばポリエチレンテレフタレートについて詳細に説明すれば、以下に述べるような2段階の反応によって製造することができる。まず第1段階の反応はテレフタル酸とエチレングリコールとを直接反応させる、又はテレフタル酸ジメチルのような低級アルキルエステルと反応させて、テレフタル酸のグリコールエステル及び/又はその低重合体を生成させる。次いで第1段階の反応生成物を重合触媒存在下減圧加熱して所望の重合度になるまで重縮合反応させる第2段階の反応によって製造される。この場合、共重合成分であるイソフタル酸成分や添加剤は第1段階の反応の前、後ないし第2段階の反応の前、後半等の任意の段階で添加することができ、一度にあるいは数回に分けて系内へ添加してもよい。
・スルホン酸ホスホニウム塩含有マスターポリマーの製造:
テレフタル酸ジメチル100部、エチレングリコール60部、酢酸マンガン4水塩0.03部(テレフタル酸ジメチルに対して0.024モル%)、整色剤として酢酸コバルト4水塩0.009部(テレフタル酸ジメチルに対して0.007モル%)、カチオン染料可染化剤としてテレフタル酸ジメチルに対して10モル%となる量の3,5−ジカルボメトキシベンゼンスルホン酸テトラ−n−ブチルホスホニウム塩(一般式(I)においてX1及びX2が共にカルボメトキシ基の化合物に対応している。)及び安定剤としてテレフタル酸ジメチルに対して0.050モル%の量のテトラエチルアンモニウムハイドロオキサイドをエステル交換反応器に仕込んだ。次に窒素ガス雰囲気下3時間かけて140℃から220℃まで昇温して生成するメタノールを系外に留去しながらエステル交換反応させた。続いて得られた生成物にエステル交換触媒失活剤として正リン酸の56%水溶液0.03部(テレフタル酸ジメチルに対して0.033モル%)及び消泡剤としてジメチルポリシロキサン0.03部を添加し、同時に過剰のエチレングリコールの昇温追出しを開始した。10分後重縮合触媒として三酸化アンチモン0.04部(テレフタル酸ジメチルに対して0.027モル%)を添加した。内温が240℃に達した時点でエチレングリコールの追出しを終了し、反応生成物を重合反応器に移した。
連続重合装置において、テレフタル酸ジメチル100部/h、エチレングリコール60部/h、酢酸マンガン4水塩0.03部/h(テレフタル酸ジメチルに対して0.024モル%)、整色剤として酢酸コバルト4水塩0.009部/h(テレフタル酸ジメチルに対して0.007モル%)、窒素ガス雰囲気下3時間かけて140℃から220℃まで昇温して生成するメタノールを系外に留去しながらエステル交換反応させた。続いて得られた生成物に安息香酸0.06部/h(0.10ミリモル%、スルホン酸ホスホニウム塩に対して1モル%)、エステル交換触媒失活剤として正リン酸の56%水溶液0.03部/h(テレフタル酸ジメチルに対して0.033モル%)を添加し、同時に過剰のエチレングリコールの昇温追出しを開始し、さらに重縮合触媒として三酸化アンチモン0.04部/h(テレフタル酸ジメチルに対して0.027モル%)を添加した。内温が240℃に達した時点でエチレングリコールの追出しを終了し、反応生成物を重合反応器に移送し、昇温しながら内温が260℃に到達するまで常圧反応させた後、常圧から133Paまで減圧し、同時に130分かけて内温を280℃まで昇温した。133Pa以下の減圧下、重合温度280℃で時点で溶融粘度を測定することによって重合反応を終了し、ポリマー配管を通じてポリマーを送出した。得られたポリマーの固有粘度[η]は表1に記載のとおりであった。
重量フィーダーを備え、チップ投入口から下流へ向けてオープンベントを2箇所、ベント孔を2箇所備え、かつL/D換算で5のニーディングディスクと、L/D換算で5のローターディスクを有する同方向回転型二軸ベント付き押出機に、溶融状態にある上述の安息香酸類含有ベースポリマーを供給した。別に予め製造しておいた上述のスルホン酸ホスホニウム塩含有マスターポリマー重量フィーダーで計量しつつ供給し、265℃で溶融させた。
Claims (4)
- 下記一般式(I)
で表わされるスルホン酸ホスホニウム塩が共重合された改質ポリエステルを含む組成物であって、
(A)該スルホン酸ホスホニウム塩の共重合量が改質ポリエステルを構成する酸成分に対して0.1〜10モル%であり、
(B)安息香酸及び/又は安息香酸誘導体の合計量を該スルホン酸ホスホニウム塩に対して0.1モル%以上20モル%以下となる量含有し、
(C)上記一般式(I)成分1単位とアルキレンテレフタレート2単位から構成される環状3量体を改質ポリエステル組成物の全重量に対して0.1〜1重量%含有する改質ポリエステル組成物。 - 改質ポリエステルの主成分がポリエチレンテレフタレート、ポリトリメチレンテレフタレート、ポリブチレンテレフタレートからなる群の少なくとも1種よりなる請求項1記載の改質ポリエステル組成物。
- (A)下記一般式(I)
で表わされるスルホン酸ホスホニウム塩が全繰返し単位当たり0.1〜20モル%共重合された改質ポリエステルと
(B)安息香酸及び/又はパラヒドロキシ安息香酸の合計量を、上記改質ポリエステルに共重合されたスルホン酸ホスホニウム塩の共重合量に対して0.1〜10モル%となる量含有するポリエステル組成物とを、
得られる改質ポリエステル組成物において上記一般式(I)で表されるスルホン酸ホスホニウム塩がポリエステルの繰り返し単位当たり0.1〜10モル%含有するように、予め混合してから又は別々にベント付き押出機に投入し、該ベント付き押出機中でエステル交換反応させる改質ポリエステル組成物の製造方法。 - 上記一般式(I)で表されるスルホン酸ホスホニウム塩0.1〜20モル%が共重合された改質ポリエステルにおいて、官能基X1及びX2の合計量の20〜100モル%がカルボキシル基又はその誘導体であるスルホン酸ホスホニウム塩が共重合されている改質ポリエステルを使用することを特徴とする請求項3記載の改質ポリエステル組成物の製造方法。