JP2004500299A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2004500299A5 JP2004500299A5 JP2001546594A JP2001546594A JP2004500299A5 JP 2004500299 A5 JP2004500299 A5 JP 2004500299A5 JP 2001546594 A JP2001546594 A JP 2001546594A JP 2001546594 A JP2001546594 A JP 2001546594A JP 2004500299 A5 JP2004500299 A5 JP 2004500299A5
- Authority
- JP
- Japan
- Prior art keywords
- sio
- granules
- primary particles
- specific surface
- surface area
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000008187 granular material Substances 0.000 claims description 29
- 229910004298 SiO 2 Inorganic materials 0.000 claims description 23
- 238000000034 method Methods 0.000 claims description 15
- 239000011164 primary particle Substances 0.000 claims description 14
- 239000002245 particle Substances 0.000 claims description 10
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims description 7
- 238000004017 vitrification Methods 0.000 claims description 6
- 238000005245 sintering Methods 0.000 claims description 3
- 238000010438 heat treatment Methods 0.000 claims 7
- 238000004519 manufacturing process Methods 0.000 claims 3
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims 2
- 229910052782 aluminium Inorganic materials 0.000 claims 2
- 238000009826 distribution Methods 0.000 claims 2
- QJGQUHMNIGDVPM-UHFFFAOYSA-N nitrogen group Chemical group [N] QJGQUHMNIGDVPM-UHFFFAOYSA-N 0.000 claims 2
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims 1
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims 1
- ZAMOUSCENKQFHK-UHFFFAOYSA-N Chlorine atom Chemical compound [Cl] ZAMOUSCENKQFHK-UHFFFAOYSA-N 0.000 claims 1
- 238000005054 agglomeration Methods 0.000 claims 1
- 230000002776 aggregation Effects 0.000 claims 1
- 229910052799 carbon Inorganic materials 0.000 claims 1
- 239000000460 chlorine Substances 0.000 claims 1
- 229910052801 chlorine Inorganic materials 0.000 claims 1
- 239000002019 doping agent Substances 0.000 claims 1
- 239000011796 hollow space material Substances 0.000 claims 1
- 238000000465 moulding Methods 0.000 claims 1
- 239000002105 nanoparticle Substances 0.000 claims 1
- 239000002344 surface layer Substances 0.000 claims 1
- 239000011148 porous material Substances 0.000 description 8
- 238000004438 BET method Methods 0.000 description 1
- 239000000654 additive Substances 0.000 description 1
- 230000015572 biosynthetic process Effects 0.000 description 1
- 239000000356 contaminant Substances 0.000 description 1
- 238000004031 devitrification Methods 0.000 description 1
- 230000002349 favourable effect Effects 0.000 description 1
- 230000007062 hydrolysis Effects 0.000 description 1
- 238000006460 hydrolysis reaction Methods 0.000 description 1
- 229910021331 inorganic silicon compound Inorganic materials 0.000 description 1
- 239000000463 material Substances 0.000 description 1
- 150000003961 organosilicon compounds Chemical class 0.000 description 1
- 230000003647 oxidation Effects 0.000 description 1
- 238000007254 oxidation reaction Methods 0.000 description 1
- LIVNPJMFVYWSIS-UHFFFAOYSA-N silicon monoxide Chemical compound [Si-]#[O+] LIVNPJMFVYWSIS-UHFFFAOYSA-N 0.000 description 1
- 238000003980 solgel method Methods 0.000 description 1
Applications Claiming Priority (2)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| DE19962451A DE19962451C1 (de) | 1999-12-22 | 1999-12-22 | Verfahren für die Herstellung von opakem Quarzglas und für die Durchführung des Verfahrens geeignetes Si0¶2¶-Granulat |
| PCT/EP2000/012687 WO2001046079A1 (de) | 1999-12-22 | 2000-12-14 | VERFAHREN FÜR DIE HERSTELLUNG VON OPAKEM QUARZGLAS, FÜR DIE DURCHFÜHRUNG DES VERFAHRENS GEEIGNETES SiO2-GRANULAT UND BAUTEIL AUS OPAKEM QUARZGLAS |
Publications (3)
| Publication Number | Publication Date |
|---|---|
| JP2004500299A JP2004500299A (ja) | 2004-01-08 |
| JP2004500299A5 true JP2004500299A5 (enExample) | 2005-02-24 |
| JP4681189B2 JP4681189B2 (ja) | 2011-05-11 |
Family
ID=7934123
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| JP2001546594A Expired - Lifetime JP4681189B2 (ja) | 1999-12-22 | 2000-12-14 | 不透明石英ガラスの製造方法、該方法に適したＳｉＯ２粒子および不透明石英ガラス物品 |
Country Status (9)
| Country | Link |
|---|---|
| US (1) | US6380110B1 (enExample) |
| EP (1) | EP1240114B1 (enExample) |
| JP (1) | JP4681189B2 (enExample) |
| KR (1) | KR100716485B1 (enExample) |
| CN (1) | CN1200896C (enExample) |
| CA (1) | CA2395501A1 (enExample) |
| DE (2) | DE19962451C1 (enExample) |
| TW (1) | TW548246B (enExample) |
| WO (1) | WO2001046079A1 (enExample) |
Families Citing this family (38)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| DE10019693B4 (de) * | 2000-04-20 | 2006-01-19 | Heraeus Quarzglas Gmbh & Co. Kg | Verfahren zur Herstellung eines Bauteils aus opakem, synthetischen Quarzglas, nach dem Verfahren hergestelltes Quarzglasrohr, sowie Verwendung desselben |
| DE10020955A1 (de) * | 2000-04-28 | 2001-11-22 | Fraunhofer Ges Forschung | Formkörper und Verfahren zur Herstellung |
| DE10055362C1 (de) * | 2000-11-08 | 2002-01-24 | Heraeus Quarzglas | Verfahren zur Herstellung eines SiO¶2¶-Rohlings und Vorrichtung zur Durchführung des Verfahrens |
| DE10055357C1 (de) * | 2000-11-08 | 2002-08-14 | Heraeus Quarzglas | Verfahren und Vorrichtung zur Herstellung eines SiO¶2¶-Rohlings |
| DE10159959A1 (de) * | 2001-12-06 | 2003-06-26 | Heraeus Quarzglas | Quarzglasrohling für ein optisches Bauteil und Verwendung desselben |
| DE10243953B4 (de) * | 2002-09-21 | 2005-11-17 | Heraeus Quarzglas Gmbh & Co. Kg | Verfahren für die Herstellung eines Bauteils aus opakem Quarzglas |
| EP1580170B1 (en) * | 2002-11-29 | 2019-01-16 | Heraeus Quarzglas GmbH & Co. KG | Method for producing synthetic quartz glass and synthetic quartz glass article |
| US7637126B2 (en) * | 2003-12-08 | 2009-12-29 | Heraeus Quarzglas Gmbh & Co. Kg | Method for the production of laser-active quartz glass and use thereof |
| DE102004038602B3 (de) * | 2004-08-07 | 2005-12-29 | Heraeus Quarzglas Gmbh & Co. Kg | Elektrogeschmolzenes, synthetisches Quarzglas, insbesondere für den Einsatz in der Lampen- und in der Halbleiterfertigung und Verfahren zur Herstellung desselben |
| DE102004052312A1 (de) * | 2004-08-23 | 2006-03-02 | Heraeus Quarzglas Gmbh & Co. Kg | Beschichtetes Bauteil aus Quarzglas sowie Verfahren zur Herstellung des Bauteils |
| DE102004051846B4 (de) * | 2004-08-23 | 2009-11-05 | Heraeus Quarzglas Gmbh & Co. Kg | Bauteil mit einer Reflektorschicht sowie Verfahren für seine Herstellung |
| US7563512B2 (en) * | 2004-08-23 | 2009-07-21 | Heraeus Quarzglas Gmbh & Co. Kg | Component with a reflector layer and method for producing the same |
| DE102006018711B4 (de) * | 2006-04-20 | 2008-09-25 | Heraeus Quarzglas Gmbh & Co. Kg | Werkstoff, insbesondere für ein optisches Bauteil zum Einsatz in der Mikrolithographie und Verfahren zur Herstellung eines Formkörpers aus dem Werkstoff |
| WO2008069194A1 (ja) * | 2006-12-05 | 2008-06-12 | Shin-Etsu Quartz Products Co., Ltd. | 合成不透明石英ガラス及びその製造方法 |
| DE102007017004A1 (de) * | 2007-02-27 | 2008-08-28 | Heraeus Quarzglas Gmbh & Co. Kg | Optisches Bauteil aus synthetischem Quarzglas mit erhöhter Strahlenbeständigkeit, sowie Verfahren zur Herstellung des Bauteils |
| JP5171098B2 (ja) * | 2007-04-24 | 2013-03-27 | 岩崎電気株式会社 | 石英ガラス製品の製造方法、それに用いるシリカ顆粒とその生成方法 |
| DE102009005446A1 (de) * | 2009-01-21 | 2010-07-22 | Schott Ag | Granulat, Verfahren zu dessen Herstellung sowie dessen Verwendung |
| KR101246157B1 (ko) * | 2010-12-09 | 2013-03-20 | 한국세라믹기술원 | 엔지니어드 스톤의 제조방법 |
| TWI652240B (zh) * | 2014-02-17 | 2019-03-01 | 日商東曹股份有限公司 | 不透明石英玻璃及其製造方法 |
| EP3000790B2 (de) | 2014-09-29 | 2023-07-26 | Heraeus Quarzglas GmbH & Co. KG | Verfahren für die Herstellung von Bauteilen aus synthetischem Quarzglas aus SiO2-Granulat |
| JP6558137B2 (ja) * | 2015-08-07 | 2019-08-14 | 東ソー株式会社 | 不透明シリカガラス製造用の高強度成形体 |
| CN108698895A (zh) * | 2015-12-18 | 2018-10-23 | 贺利氏石英玻璃有限两合公司 | 在悬挂式烧结坩埚中制备石英玻璃体 |
| CN109153593A (zh) | 2015-12-18 | 2019-01-04 | 贺利氏石英玻璃有限两合公司 | 合成石英玻璃粉粒的制备 |
| CN108698894A (zh) * | 2015-12-18 | 2018-10-23 | 贺利氏石英玻璃有限两合公司 | 在多腔式烘箱中制备石英玻璃体 |
| TWI733723B (zh) | 2015-12-18 | 2021-07-21 | 德商何瑞斯廓格拉斯公司 | 不透明石英玻璃體的製備 |
| CN108698883A (zh) * | 2015-12-18 | 2018-10-23 | 贺利氏石英玻璃有限两合公司 | 石英玻璃制备中的二氧化硅的喷雾造粒 |
| WO2017103131A1 (de) | 2015-12-18 | 2017-06-22 | Heraeus Quarzglas Gmbh & Co. Kg | Verringern des erdalkalimetallgehalts von siliziumdioxidgranulat durch behandlung von kohlenstoffdotiertem siliziumdioxidgranulat bei hoher temperatur |
| TW201731781A (zh) * | 2015-12-18 | 2017-09-16 | 何瑞斯廓格拉斯公司 | 於豎立式燒結坩堝中製備石英玻璃體 |
| KR20180095619A (ko) | 2015-12-18 | 2018-08-27 | 헤래우스 크바르츠글라스 게엠베하 ＆ 컴파니 케이지 | 실리카 유리 제조 동안 규소 함량의 증가 |
| JP2019506349A (ja) * | 2015-12-18 | 2019-03-07 | ヘレウス クワルツグラス ゲーエムベーハー ウント コンパニー カーゲー | 吊り下げ式金属シート坩堝内での石英ガラス体の調製 |
| KR20180094087A (ko) | 2015-12-18 | 2018-08-22 | 헤래우스 크바르츠글라스 게엠베하 ＆ 컴파니 케이지 | 실리카 과립으로부터 실리카 유리 제품의 제조 |
| WO2017103153A1 (de) | 2015-12-18 | 2017-06-22 | Heraeus Quarzglas Gmbh & Co. Kg | Glasfasern und vorformen aus quarzglas mit geringem oh-, cl- und al-gehalt |
| EP3390303B1 (de) | 2015-12-18 | 2024-02-07 | Heraeus Quarzglas GmbH & Co. KG | Herstellung von quarzglaskörpern mit taupunktkontrolle im schmelzofen |
| JP6940235B2 (ja) | 2015-12-18 | 2021-09-22 | ヘレウス クワルツグラス ゲーエムベーハー ウント コンパニー カーゲー | 高融点金属の溶融坩堝内での石英ガラス体の調製 |
| EP3185057A1 (de) * | 2015-12-22 | 2017-06-28 | Heraeus Quarzglas GmbH & Co. KG | Faseroptische streueinrichtung und herstellungsverfahren dafür |
| EP3248950B1 (de) * | 2016-05-24 | 2020-08-05 | Heraeus Quarzglas GmbH & Co. KG | Verfahren zur herstellung eines poren enthaltenden, opaken quarzglases |
| JP6878829B2 (ja) * | 2016-10-26 | 2021-06-02 | 東ソー株式会社 | シリカ粉末及び高流動性シリカ造粒粉末並びにその製造方法 |
| EP3476815B1 (en) | 2017-10-27 | 2023-11-29 | Heraeus Quarzglas GmbH & Co. KG | Production of a porous product including post-adapting a pore structure |
Family Cites Families (16)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| DE1567440B1 (de) | 1965-04-29 | 1971-02-25 | Degussa | Kugelfoermiges kieselsaeuregranulat |
| DE2557932A1 (de) * | 1975-12-22 | 1977-06-30 | Dynamit Nobel Ag | Verfahren zur herstellung von koernigem quarzglas |
| JPH02219814A (ja) * | 1989-02-21 | 1990-09-03 | Sumitomo Bakelite Co Ltd | エポキシ樹脂組成物 |
| JPH0326717A (ja) * | 1989-06-26 | 1991-02-05 | Sumitomo Bakelite Co Ltd | エポキシ樹脂組成物 |
| JPH07138015A (ja) * | 1993-06-15 | 1995-05-30 | Catalysts & Chem Ind Co Ltd | シリカ微小球状粒子およびその製造方法 |
| DE4338807C1 (de) * | 1993-11-12 | 1995-01-26 | Heraeus Quarzglas | Formkörper mit hohem Gehalt an Siliziumdioxid und Verfahren zur Herstellung solcher Formkörper |
| JP3368547B2 (ja) * | 1994-04-28 | 2003-01-20 | 信越石英株式会社 | 不透明石英ガラスおよびその製造方法 |
| DE4424044A1 (de) * | 1994-07-11 | 1996-01-18 | Heraeus Quarzglas | Verfahren zur Herstellung von Kieselsäuregranulat und Verwendung des so hergestellten Granulats |
| EP0725037B2 (de) * | 1995-02-04 | 2012-04-25 | Evonik Degussa GmbH | Granulate auf Basis von pyrogen hergestelltem Siliciumdioxid, Verfahren zu ihrer Herstellung und ihre Verwendung |
| JPH0912325A (ja) * | 1995-06-29 | 1997-01-14 | Nitto Chem Ind Co Ltd | 高純度不透明石英ガラス及びその製造方法並びにその用途 |
| JP3471514B2 (ja) * | 1996-02-01 | 2003-12-02 | 水澤化学工業株式会社 | 半導体封止用樹脂組成物及びそれに用いる吸湿性充填剤 |
| JP3647959B2 (ja) * | 1996-02-01 | 2005-05-18 | 水澤化学工業株式会社 | 非晶質シリカ系定形粒子の製造方法 |
| DE69716822T2 (de) * | 1996-07-04 | 2003-09-11 | Tosoh Corp., Shinnanyo | Opakes Quarzglas und Verfahren zu dessen Herstellung |
| GB2316414B (en) * | 1996-07-31 | 2000-10-11 | Tosoh Corp | Abrasive shaped article, abrasive disc and polishing method |
| DE19729505A1 (de) * | 1997-07-10 | 1999-01-14 | Heraeus Quarzglas | Verfahren zur Herstellung von Si0¶2¶-Granulat |
| FR2766170B1 (fr) * | 1997-07-17 | 1999-09-24 | Alsthom Cge Alcatel | Procede ameliore de fabrication d'une poudre de silice |
-
1999
- 1999-12-22 DE DE19962451A patent/DE19962451C1/de not_active Expired - Fee Related
-
2000
- 2000-01-14 US US09/484,113 patent/US6380110B1/en not_active Expired - Lifetime
- 2000-12-14 WO PCT/EP2000/012687 patent/WO2001046079A1/de not_active Ceased
- 2000-12-14 CA CA002395501A patent/CA2395501A1/en not_active Abandoned
- 2000-12-14 JP JP2001546594A patent/JP4681189B2/ja not_active Expired - Lifetime
- 2000-12-14 DE DE50011832T patent/DE50011832D1/de not_active Expired - Lifetime
- 2000-12-14 CN CNB008177104A patent/CN1200896C/zh not_active Expired - Lifetime
- 2000-12-14 EP EP00993506A patent/EP1240114B1/de not_active Expired - Lifetime
- 2000-12-14 KR KR1020027008182A patent/KR100716485B1/ko not_active Expired - Lifetime
- 2000-12-22 TW TW089127771A patent/TW548246B/zh not_active IP Right Cessation
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| JP2004500299A5 (enExample) | ||
| JP4681189B2 (ja) | 不透明石英ガラスの製造方法、該方法に適したＳｉＯ２粒子および不透明石英ガラス物品 | |
| US6672107B2 (en) | Quartz glass crucible and process for the production thereof | |
| JP6129263B2 (ja) | ＳｉＯ２造粒体の合成石英ガラスの製造方法及び該製造方法に適したＳｉＯ２造粒体 | |
| JP4157933B2 (ja) | ＳｉＯ２含有複合材料の製造方法及びその製造方法により得られる複合材料の使用 | |
| Elmer | Porous and reconstructed glasses | |
| US6684664B2 (en) | Process for manufacture of a component made of opaque synthetic quartz glass | |
| JP2004532176A5 (enExample) | ||
| EP2315727B1 (de) | Verfahren zur herstellung von mit stickstoff dotiertem quarzglas | |
| US9409810B2 (en) | Method for producing synthetic quartz glass granules | |
| JP5118007B2 (ja) | シリカ容器及びその製造方法 | |
| CN103153887B (zh) | 用于生产合成石英玻璃颗粒的方法 | |
| US9580348B2 (en) | Method for producing synthetic quartz glass granules | |
| JP6698585B2 (ja) | 細孔を含む不透明石英ガラスの製造方法 | |
| JP4700619B2 (ja) | レーザー活性石英ガラスの生産方法および使用 | |
| CA2283569C (en) | High-purity silica glass fabricating method using sol-gel process | |
| TW200304435A (en) | Dispersion comprising silicon/titanium mixed oxide powder, and green bodies and shaped glass articles produced therefrom | |
| JPH0558883B2 (enExample) | ||
| Assis et al. | Open pore microfiltration membranes produced from waste glass | |
| JPH05139768A (ja) | 偏光性石英ガラスの製造方法 | |
| Boiko et al. | Sol-gel synthesis of Fe-containing silica glasses | |
| JPH04198034A (ja) | 高粘度合成石英ガラス部材の製造方法 |