DE1577104A1 - Verfahren zur Herstellung von metallischen Verbundkoerpern - Google Patents
Verfahren zur Herstellung von metallischen VerbundkoerpernInfo
- Publication number
- DE1577104A1 DE1577104A1 DE19661577104 DE1577104A DE1577104A1 DE 1577104 A1 DE1577104 A1 DE 1577104A1 DE 19661577104 DE19661577104 DE 19661577104 DE 1577104 A DE1577104 A DE 1577104A DE 1577104 A1 DE1577104 A1 DE 1577104A1
- Authority
- DE
- Germany
- Prior art keywords
- base material
- cladding
- alloy
- copper
- base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K20/00—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating
- B23K20/04—Non-electric welding by applying impact or other pressure, with or without the application of heat, e.g. cladding or plating by means of a rolling mill
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12486—Laterally noncoextensive components [e.g., embedded, etc.]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/12—All metal or with adjacent metals
- Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
- Y10T428/12771—Transition metal-base component
- Y10T428/12861—Group VIII or IB metal-base component
- Y10T428/12903—Cu-base component
Landscapes
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Pressure Welding/Diffusion-Bonding (AREA)
Claims (9)
- P a t e n t a n s p r ü c h e 1. Verfahren zur Herstellung eines metallischen Verbundkörpers mit einem Grundwerkstoff aus Kupfer oder einer Kupferlegierung, der mit einem Werkstoff aus einem anderen Metall plattiert ist, d a d u r c h g e k e n n z e i c h n e t, daß man den Grundwerkstoff in einer Stärke von weniger als 12,7 mm und den Plattierwerkstoff in einer Stärke von weniger als 6,35 mm verwendet, den Grundwerkstoff auf eine Temperatur zwischen 149 und 538°C erhitzt, dann den Grundwerkstoff mit dem Plattierwerkatoff bei einer Geschwindigkeit von mindestens 30,5 m/min in einem Stichdurchgang und einer Verminderung der Ausgangsdicke von 40 bis 80 % zusammenwalzt, wobei der Grundwerkstoff mit dem Plattierwerkstoff erst am Eingriffspunkt der Walzen zusammenkommt, der Plattierwerkatoff die Walze vor der Berührung mit dem Grundwerkstoff berührt und der Einschlußwinkel zwischen Grundwerkstoff und Plattierwerkstoff beim Eintritt in die Walzen mindestens 5 0 beträgt.
- 2. Verfahren nach Anspruch 1, d a d u r c h g e k e n n z e i c h -n e t, daß als Plattierwerkstoff eine andere Kupferlegierung als das Grundwerkatoffmetall, eine Eisenlegierung, eine Bleilegierung, eine Silberlegierung, eine Nickellegierung, eine Zinklegierung, eine Zinnlegierung oder eine Aluminiumlegierung verwendet wird, und daß der Einschlußwinkel zwischen Grund-' werkatoff und Plattierwerkstoff beim Eintritt in die Walzen zwischen 5 und 22 ° beträgt.
- 3. Verfahren nach Anspruch 2, d a d u r c h g e k e n n z e i c h -n e t, daß der Einschlußwinkel mindestens 10o beträgt.
- 4. Verfahren nach Anspruch 2, d a d u r e h g e k e n n z e i c h -n e t, daß der Grundwerkstoff auf eine Temperatur zwischen 260 und 538°C erhitzt wird.
- 5. Verfahren nach Anspruch 2, d a d u r c h g e k e n n z e i c h -n e t, daß der Grundwerkstoff und der Plattierwerkatoff in einem Stichdurchgang unter Verminderung der Ausgangsdicke auf 50 bis 80 y6 zusammengesalzt werden.
- 6. Verfahren nach Anspruch 2, d a d u r c h g e k e n n z e i c h -n e t, daß die Oberflächen des Grundwerkstoffes und des Plattierwerkstoffes oder der Plattierwerkstoffe, die miteinander verbunden werden sollen, vor dem Walzen mechanisch aufgerauht werden.
- 7. Verfahren nach Anspruch 1 bis 6, d a d u r c h g e k e n n -z e i e h n e t, daß der Grundwerkstoff auf beiden Seiten plattiert wird. B.
- Verfahren nach Anspruch 1 bis 7, d a d u r c h g e k e n n -z e i c h n e t, daß sowohl der Grundwerkstoff als auch der Plattierwerkstoff bzw, die Plattierwerkstoffe vor dem Walzen gereinigt werden.
- 9. Verbundkörper aus einem Grundwerkstoff aus Kupfer oder einer Kupferlegierung, der mit einem Werkstoff aus einem anderen Metall plattiert ist, d a d u r c h g e k e n n z e i c h n e t, daß der Verbundkörper eine Stärke von weniger als 15,24 mm aufweist und wobei die Grenzfläche zwischen dem Grundwerkstoff und dem Plattierwerkstoff durch die Abwesenheit von atomarer Interdiffusion gekennzeichnet ist und diese Grenzfläche eine mindestens 20 % größere Kontaktoberfläche aufweist als die ebenen Bleche.