DE1546785B2 - Verfahren zur herstellung eines aluminiumtraegers fuer vorsensibilisierte flachdruckplatten - Google Patents
Verfahren zur herstellung eines aluminiumtraegers fuer vorsensibilisierte flachdruckplattenInfo
- Publication number
- DE1546785B2 DE1546785B2 DE19651546785 DE1546785A DE1546785B2 DE 1546785 B2 DE1546785 B2 DE 1546785B2 DE 19651546785 DE19651546785 DE 19651546785 DE 1546785 A DE1546785 A DE 1546785A DE 1546785 B2 DE1546785 B2 DE 1546785B2
- Authority
- DE
- Germany
- Prior art keywords
- boehmite
- aluminum
- layer
- presensitized
- manufacturing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
Gegenstand des Patentes 1 151 818 sind vorsensibilisierte
Flachdruckplatten, bestehend aus Aluminiumträger und darauf befindlicher Kopierschicht, die
dadurch gekennzeichnet sind, daß sich zwischen Kopierschicht und Aluminiumträger eine durch Einwirkung
von Wasser oder wäßrig-alkalischen Lösungen bei erhöhter Temperatur erzeugte Böhmitschicht befindet.
Aufgabe der vorliegenden Zusatzerfindung war es, gewisse sich bei der Erzeugung der Böhmitschicht auf
dem Aluminiumträger ergebende Ungleichmäßigkeiten der Schicht zu vermeiden und einen verbesserten
Aluminiumträger mit Böhmitschicht für die vorsensibilisierten Flachdruckplatten des Hauptpatents zu erhalten.
Die Erfindung geht aus von einem Verfahren zur Herstellung eines auf seiner Oberfläche mit einer
Böhmitschicht versehenen Aluminiumträgers für vorsensibilisierte Flachdruckplatten nach Patent
1 151818.
Das erfindungsgemäße Verfahren ist dadurch gekennzeichnet, daß die Erzeugung der Böhmitschicht
durch Einwirkung von Wasser bei erhöhter Temperatur unter Anlegung schwacher elektrischer Gleichoder
Wechselspannungen an das Behandlungsbad erfolgt.
Bei der bekannten Erzeugung von Böhmit durch Reaktion zwischen Aluminium und Wasser oder
Wasserdampf, besonders bei Temperaturen zwischen 70 und 100° C, wird zu Beginn der Reaktion zu- .
nächst die immer bei Aluminium vorhandene, ari der Luft gebildete Aluminiumoxidschicht durch Wasseraufnahme
in Böhmit umgewandelt. Dann erfolgt unter Wasserstoffentwicklung die eigentliche Reaktion
zwischen Wasser und Aluminium. Diese Gasentwicklung ist wichtig für die Ausbildung einer Grobstruktur
des Böhmits, die den Transport von Wasser durch die Schicht an die Metalloberfläche auch bei
wachsender Schichtdicke gestattet.
Die Bildung der Grobstruktur des Böhmits hängt auch von der Reaktonszeit ab. Je schneller die Reaktion
einsetzt und verläuft, desto gröber ist die Makrostruktur des gebildeten Böhmits, und je weniger
verschmutzt die Oberfläche des Aluminiums bzw. der Aluminiumoxidaußenschicht ist, desto schneller
setzt die Einwirkung des Wassers ein. Die Bildung einer gleichmäßigen Böhmitschicht auf stellenweise
verunreinigten Aluminiumoberflächen — z.B. sind die Oberflächen von Bändern aus Aluminium immer
verunreinigt — ist daher nicht möglich. Auch nach Anwendung zusätzlicher Reinigungsverfahren, ζ. Β
nach dem Walzen, kommt es häufig zu einer unterschiedlichen Böhmitbildung, da die gereinigten Aluminiumoberflächen
außerordentlich empfindlich sind und leicht Fette und Öle, auch aus der Gasphase, adsorbieren.
Störungen dieser Art während der Böhmitbildung können oft als graue Streifen oder Flecken
auf der Oberfläche des Aluminiums erkannt werden.
Zur Vermeidung dieser Fehler hat man dem Wasser gewöhnlich alkalisch reagierende Chemikalien
zugesetzt. Diese Zusätze erleichtern aber nicht nur die Beseitigung der Verunreinigungen während der
Böhmitbildung, sondern sie beeinträchtigen auch die Grobstruktur der Metalloberfläche und der Böhmitschicht
und sind nicht in allen Fällen anzuwenden. Mit steigendem pH-Wert wächts der Reinigungseffekt,
aber auch die Korrosion des Aluminiums wird größer. Während der Böhmitbildung werden daher
die korrodierenden Zusätze verbraucht. Sie müssen kontinuierlich ergänzt und die Korrosionsprodukte
aus der Reaktionslösung entfernt werden.
Die Erfindung schlägt zur Verbeserung der Böhmitschicht und zur Erhöung ihrer Gleichmäßigkeit
vor, den von Verunreinigungen ausgehenden reaktionshemmenden Einfluß auf elektrochemischem
Wege zu beseitigen oder zu vermindern.
Durch Einwirkung von geringen elektrischen Strömen während der Böhmitbildung wird ein gleichmäßiger
Reaktionsbeginn bewirkt. Die Stromdichte wird bei technisch normalerweise anzuwendenden Spannungen
durch die geringe elektrische Leitfähigkeit des destillierten Wassers nach oben begrenzt und ist
damit in der Größenordnung deutlich verschieden von den Stromdichten, die bei den bekannten Eloxalverfahren
auftreten.
Wie Messungen zeigten, ist es möglich und zum Teil erwünscht, durch geringe elektrische Ströme
während der Böhmitbildung zwar die Größe der Poren der Schichten zu beeinflussen, doch wird die
Dicke der Schicht eindeutig durch die chemische Reaktion bestimmt, im Gegensatz zur Bildung der bekannten
Eloxalschichten.
B eispiel1
Durch destilliertes Wasser von 95 bis 98° C wird ein mechanisch entfettetes Aluminiumband gezogen.
Im Abstand von 1 bis 2 cm von dem Band sind im Bad zwei Elektroden angebracht.
Beim Anlegen von 6VoIt Gleichspannung stellt
sich nach kurzer Zeit eine Stromdichte von etwa 0,1 mA/cm2 ein, die zur Bildung einer fehlerfreien
Böhmitschicht ausreicht. Das Band -kann., mit gleichem Erfolg als Anode oder Kathode geschaltet werden.
In der Zeichnung ist die Betriebsanordnung schematisch dargestellt. A ist das Aluminiumband, auf
dem die Böhmitschicht erfindungsgemäß erzeugt wird, B ist der Wasserbehälter, durch den das Aluminiumband
über die Führungsrollen F gezogen wird. E ist die Elektrode, S die Stromquelle. Aluminiumband
und Behälter sind geerdet.
Es wird wie im Beispiel 1 verfahren, doch wird an Stelle einer Gleichspannung eine Wechselspannung
benutzt. Bei 5 Volt wurde eine Stromdichte von etwa 0,5 mA/cm2 gemessen. Das Aussehen der Böhmitschicht
war befriedigend.
Aluminiumfolien von 15 μ Stärke werden in 95 bis
}8° C heißem, doppelt destilliertem Wasser mit und
3hne angelegter Wechselspannung (0,3 mA/cm2) belandelt,
und die Struktur der entstandenen Böhmitichichten wird mit Hilfe der BET-Methode untersucht.
Es zeigt sich, daß bei den ohne Anlegung einer Wechselspannung erzeugten Böhmitschichten Poren
mit Durchmessern von sehr unterschiedlicher Größe vorhanden sind, durch den Stromfluß aber die Häufigkeit
der Poren mit größerem Durchmesser verringert, die von Poren mit kleinerem Durchmesser, besonders
solchen von 20 A, vergrößert ist.
Hierzu 1 Blatt Zeichnungen
Claims (1)
- Patentanspruch:Verfahren zur Herstellung eines auf seiner Oberfläche mit einer Böhmitschicht versehenen Aluminiumträgers für vorsensibilisierte Flachdruckplatten nach Patent 1 151818, dadurch gekennzeichnet, daß die Erzeugung der Böhmitschicht durch Einwirkung von Wasser bei erhöhter Temperatur unter Anlegung schwacher elektrischer Gleich- oder Wechselspannungen an das Behandlungsbad erfolgt.