CN1816501A - 液体速凝剂、喷浆材料以及使用其的喷浆施工方法 - Google Patents
液体速凝剂、喷浆材料以及使用其的喷浆施工方法 Download PDFInfo
- Publication number
- CN1816501A CN1816501A CNA2004800191728A CN200480019172A CN1816501A CN 1816501 A CN1816501 A CN 1816501A CN A2004800191728 A CNA2004800191728 A CN A2004800191728A CN 200480019172 A CN200480019172 A CN 200480019172A CN 1816501 A CN1816501 A CN 1816501A
- Authority
- CN
- China
- Prior art keywords
- parts
- liquid accelerator
- further characterized
- elemental composition
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
提供了具有可促凝性优良的喷浆施工的,可提高液体速凝剂的保存性等效果的液体速凝剂、喷浆材料以及使用其的喷浆施工方法。该液体速凝剂是含有硫、铝以及碱金属的元素成分和络合物形成剂的液体速凝剂,相对于换算成SO3的硫的元素成分100份,该液体速凝剂较好含有换算为Al2O3的25~110份的铝的元素成分、换算为R2O(R表示碱金属原子)的2.5~50份的碱金属的元素成分以及2.5~75份的络合物形成剂。
Description
技术领域
本发明涉及,在道路、铁道以及引水路等的隧道或坡面中所露出的天然地基上喷射速凝性水泥混凝土时,使用的液体速凝剂、喷浆材料以及使用其的喷浆施工方法。
背景技术
目前,为了防止在隧道开凿作业等中露出的天然地基的崩落,采用例如在铝酸钙中混合碱金属的铝酸盐或碳酸盐等制成粉体的速凝剂,再喷射由在混凝土中混合该速凝剂而得的速凝性混凝土的施工方法(参考专利文献1~2)。
但是,需要开发出与在铝酸钙中混合碱金属的铝酸盐或碳酸盐等而制得的粉体的速凝剂相比pH更低的,呈弱碱性~酸性,较好为中性或弱酸性的速凝剂。
为了解决该问题,作为液体速凝剂,使用以碱性铝盐或有机羧酸为主要成分的物质(参考专利文献3),以硫酸铝或烷醇胺为主要成分的物质(参考专利文献4),以及以铝的碱性水溶液、硅酸锂和铝酸锂为主要成分的物质(参考专利文献5)。
但是,这种液体速凝剂很难表现出初期强度,与目前的粉体系速凝剂相比较,存在在隧道坑内厚喷射时不易厚喷射的问题。
作为提高速凝性的酸性液体速凝剂,有使用在硫酸铝中含有氟的物质的专利公开(参考专利文献6、专利文献7、专利文献8)。
但是,在实用化时要求进一步提高速凝性,进一步提高在涌水处的粘着性。
近年来,希望开发出与目前的碱性速凝剂相比,对人体影响小的,初期强度表现性优良的液体速凝剂。
专利文献1:日本专利特公昭60-004149号公报
专利文献2:日本专利特开平09-019910号公报
专利文献3:日本专利特表2001-509124
专利文献4:日本专利特开平10-087358号公报
专利文献5:日本专利特开2001-130935号公报
专利文献6:日本专利特开2002-080250号公报
专利文献7:日本专利特开2002-047048号公报
专利文献8:日本专利特开2004-035387号公报
发明的揭示
发明要解决的课题
这样,希望开发出与粉体的速凝剂相比pH更低的,弱碱性~酸性,较好为中性或弱酸性的,在短时间内即可保证达到必要的安全强度的,而且长期使用后制品的性能和安全性等均无损的速凝剂。
解决课题的方法
本发明者,考虑上述状况,进行了解决上述课题的各种研究,结果发现通过特定的液体速凝剂,可提高液体的稳定性,从而可充分发挥速凝剂的能力,由此完成了本发明。
即,本发明是以下述要旨为特征的发明。
(1)液体速凝剂,其特征在于,含有硫、铝以及碱金属的元素成分和络合物形成剂。
(2)如(1)所述的液体速凝剂,其特征还在于,该液体速凝剂中相对于换算成SO3的硫的元素成分100份,含有换算为Al2O3的25~110份的铝的元素成分、换算为R2O(R表示碱金属原子)的2.5~50份的碱金属的元素成分以及2.5~75份的络合物形成剂。
(3)如(1)或(2)所述的液体速凝剂,其特征还在于,还含有氟。
(4)如(1)~(3)中任一项所述的液体速凝剂,其特征还在于,相对于换算成SO3的硫的元素成分100份,该液体速凝剂中含有2.5~50份的氟。
(5)如(1)~(4)中任一项所述的液体速凝剂,其特征还在于,还含有烷醇胺。
(6)如(1)~(5)中任一项所述的液体速凝剂,其特征还在于,相对于换算成SO3的硫的元素成分100份,该液体速凝剂中含有2.5~50份的烷醇胺。
(7)如(1)~(6)中任一项所述的液体速凝剂,其特征还在于,碱金属的元素成分是钠或者钾。
(8)如(1)~(7)中任一项所述的液体速凝剂,其特征还在于,络合物形成剂含有1~3个羧基。
(9)如(1)~(8)中任一项所述的液体速凝剂,其特征还在于,络合物形成剂的配比是,相对于换算成SO3的硫的元素成分100份,含含2.5~75份。
(10)如(1)~(9)中任一项所述的液体速凝剂,其特征还在于,该液体速凝剂的pH在6以下。
(11)喷浆材料,其特征在于,含有(1)~(10)中任一项所述的液体速凝剂、水泥、水以及骨料。
(12)如(11)所述的喷浆材料,其特征还在于,相对于100份水泥,含有换算为固体成分,5~15份的液体速凝剂。
(13)如(11)或(12)所述的喷浆材料,其特征还在于,单位水泥量在350Kg/m3以上。
(14)如(11)~(13)中任一项所述的喷浆材料,其特征还在于,使用了在100份水泥中,C3A含量在5份以上的水泥。
(15)喷浆施工方法,其特征在于,喷射上述(11)~(14)中任一项所述的喷浆材料。
发明的效果
该速凝剂、喷浆材料以及使用其的喷浆施工方法,具有可速凝性优良的喷浆施工,提高液体速凝剂的保存性等效果。
实施发明的最佳方式
本发明中所述的水泥混凝土是水泥浆、砂浆、或者混凝土的总称。
另,本发明中的份或%,只要没有特殊的限定均以质量基准表示。
本发明的液体速凝剂(以下称为本速凝剂)是含有硫、铝、以及碱金属的元素成分和络合物形成剂的速凝剂。本速凝剂的状态是液态,也包括悬浊液。悬浊液中的悬浊粒子的大小虽没有特别的限定,但是从悬浊粒子的分散性的角度来看,其平均粒径较好为5μm以下。
本发明中,本速凝剂只要是含有硫、铝、以及碱金属的元素成分和络合物形成剂的物质即可,因此,含有各成分的原料化合物,在化学结构等的不同,由该差别引起的异构体、结晶体或非结晶体、有无结晶水或结晶水的数量,结晶结构不同引起的多晶型,由微量元素引起的固溶以及晶格缺陷等方面均没有特别的限定。
在本发明中使用的含有硫元素成分的原料化合物没有特别的限定。例如,除了硫黄或升华硫这样元素状态的硫之外,还可例举如硫化物、硫酸或者其盐、亚硫酸或者其盐、硫代硫酸或者其盐、以及有机硫化合物等硫化合物。
作为硫化物,可例举如硫化钠、硫化钾、硫化铁以及五硫化磷等。
作为硫酸盐,可例举如铵矾、钠矾以及钾矾等明矾类,硫酸铵、硫酸钠、硫酸镁、硫酸钙、硫酸钡、硫酸锰、硫酸铝以及硫酸苯胺等。
作为亚硫酸盐,可例举如亚硫酸钠、亚硫酸钾以及亚硫酸氢钠等。
作为硫代硫酸盐,可例举如硫代硫酸铵、硫代硫酸钠以及硫代硫酸钡等。
本发明中可使用一种或两种以上的这些硫化合物,其中,由于对水的溶解性高、成本低并且凝结性状优良,因此较好为硫酸或其盐。在硫酸盐中,最好为含有铝或碱金属的明矾类。
本发明中使用的含有铝的元素成分的物质没有特别的限定。可例举如,以明矾类为代表的铝的硫酸盐,铝的铝酸盐,非晶型、结晶型的铝的氢氧化物,其它无机铝化合物以及有机铝化合物等铝化合物。
作为铝的硫酸盐,可例举如铵矾、钠矾以及钾矾等明矾类,羟基硫酸铝以及硫酸铝等。
作为铝酸盐,可例举如铝酸锂、铝酸钠、铝酸钾以及铝酸镁等。
作为其它的无机铝化合物,有矾土、氧化铝、氢氧化铝、氯化铝、磷酸铝、硝酸铝、氟化铝、聚氯化铝、硅铝胶、硅酸铝、碱式碳酸铝以及合成铝碳酸镁等。
作为有机铝化合物,可例举如硬酯酸铝、草酸铝、异丙醇铝以及甲酸铝等。
可使用这些铝化合物中的一种或两种以上。
本发明中较好为也有硫的元素成分的硫酸盐,由于凝结性状优良,特好为各种明矾。
本发明中使用的含有碱金属的元素成分的物质没有特别的限定,只要是含有锂、钠或者钾等的水溶性的化合物即可。可使用含有硫或铝的,例如硅酸盐、氟硅酸盐以及明矾,除此之外还可使用含有碱金属的氧化物、氯化物、氢氧化物、硝酸盐、亚硝酸盐、磷酸盐、磷酸一氢盐、磷酸二氢盐、铝酸盐、硫酸盐、硫代硫酸盐、硫化盐、碳酸盐、重碳酸盐、草酸盐以及硼酸盐等化合物,可使用这些化合物中的一种或两种以上。其中较好为较易得到的锂、钠或者钾的化合物。
本发明的液体速凝剂较好为含有氟成分。含有该氟成分的原料化合物没有特别的限定,只要是含有氟,且溶于或分散于水的化合物即没有特别的限定。例如可使用氟化盐、氟硅酸盐、氟硼酸盐、有机氟化物、氢氟酸等氟化合物,可使用这些化合物中的一种或两种以上。
作为上述氟化盐,可例举如氟化锂、氟化钠、氟化钾、氟化钙、氟化铝以及冰晶石等。冰晶石既可使用天然物又可使用合成物。
作为氟硅酸盐,可例举如氟硅酸铵、氟硅酸钠、氟硅酸钾以及氟硅酸镁等。
作为氟硼酸盐,可例举如氟化硼、三氟化硼、三氟化硼合单乙胺络合物、三氟化硼合醋酸络合物以及三氟化硼三乙醇胺、氟硼酸铵、氟硼酸钠、氟硼酸钾以及氟硼酸亚铁等。
作为含有氟成分的原料化合物,由于稳定性高,成本低并且凝结性状优良,因此较好为氟化盐或氟硅酸盐。
在本发明的液体速凝剂中较好含有烷醇胺。烷醇胺是,含有N-R-OH结构作为结构式的有机化合物。在此,R是称为亚烷基或亚芳香基的原子团。例如亚甲基、亚乙基、以及n-亚丙基等直链型的亚烷基,或异亚丙基等具有分支结构的亚烷基,以及亚苯基或甲代亚苯基等具有芳香族环的亚芳香基。
另外,R可与氮原子在2个以上部位结合,也可以部分或全部为环结构。
R可与多个氢氧基结合,也可在烷基的一部分中含有碳或氢以外的元素,例如硫、氟、氯以及氧等。
作为这样的烷醇胺,可例举如,乙醇胺、二乙醇胺、三乙醇胺、N-甲基二乙醇胺、N,N-二甲基乙醇胺、N,N-二丁基乙醇胺、N-(2-氨乙基)乙醇胺、三氟化硼三乙醇胺以及它们的衍生物。在本发明中可使用它们中的一种或两种以上。其中,较好为二乙醇胺、N,N-二甲基乙胺或者它们的混合物,更好为二乙醇胺和N,N-二甲基乙醇胺的混合物。
本发明中使用的络合物形成剂是,在酸性的液体速凝剂中使金属离子稳定的物质,只要是符合该目的可使用的物质就没有特别的限定。例如具有至少1个,较好为1~3个,更好为2~3个羧基的有机酸。还可以使用具有1~3个氢氧基和/或1~3个氨基的物质。
作为这些络合物形成剂的具体例,可例举如(1)甲酸、醋酸以及丙酸等一元羧酸类、(2)草酸、丙二酸、琥珀酸、戊二酸、己二酸、庚二酸、马来酸、延胡索酸、邻苯二甲酸等二元羧酸类、(3)1,2,4-苯三酸或丙三酸等三元羧酸类、(4)羟基丁酸、乳酸以及水杨酸等羟基一元羧酸类、苹果酸等羟基二元羧酸类、(5)天冬氨酸、谷氨酸等氨基羧酸类、(6)乙二胺四乙酸(EDTA)或反式-1,2-环己二胺四醋酸(CyDTA)等氨基多元羧酸类、(7)乙二胺四(亚甲基膦酸)(ethylenediaminetetra(methylene phosphonic acid),EDTPO)、乙二胺二(亚甲基膦酸)(ethylenediamine di(methylene phosphonic acid),EDDPO)、次氮基三(亚甲基膦酸)(nitrilotris(methylene phosphonic acid),NTPO)、1-羟基亚乙基-1,1’-二膦酸(1-hydroxy ethylidene-1,1’-diphosphonic acid,HEDPO)等膦酸类、(8)磷酸、三聚磷酸以及六偏磷酸等缩合磷酸类、(9)乙酰丙酮或六氟乙酰丙酮等二酮类,本发明中可使用这些络合物形成剂中的一种或两种以上。
上述的物质中,较好为选自草酸、丙二酸、琥珀酸以及缩合磷酸类中的至少1种。
从凝结性状、悬浊性以及泵压送性等考虑,在本速凝剂中,硫、铝以及碱金属的元素成分的配比较好为,相对于换算成SO3的硫的元素成分100份,铝的元素成分换算成Al2O3为25~110份,碱金属的元素成分换算成R2O(R是碱金属)为2.5~50份。
在该混合中,不含硫时液体速凝剂的pH升高,有发生碱蚀伤的可能性,铝或碱金属的含有量未满上述配比时则有不能得到充分的凝结性状的情况发生,该三成分的含有量如果超过上述配比则液体的粘性上升,有泵压送性下降的情况发生。其中特好为铝的元素成分换算成Al2O3为40~80份、碱金属的元素成分换算成R2O(R是碱金属)为10~25份。
另外,相对于换算成SO3的硫的元素成分100份,本速凝剂中氟成分或烷醇胺的配比比均较好为2.5~50份,特好为5~25份。另外,氟成分的配比是换算成氟原子来算得的。
另,相对于换算成SO3的硫的元素成分100份,本速凝剂中所含络合物形成剂的混合比较好为2.5~75份,特好为5~50份。
本速凝剂较好为对人体影响小的弱碱性~酸性,较好为pH在6以下,特好为3~1.5。
在本速凝剂100份中,本速凝剂中换算成SO3的硫的元素成分、换算成Al2O3的铝的元素成分、换算成R2O的碱金属的元素成分以及根据需要添加的其他成分的原料化合物的合计量,较好为10~65份,更好为25~55份。上述合计量未满10份时有不能得到优良凝结性状的情况发生,如超过65份则液体的粘性上升有泵压送性低劣化的情况发生。
相对于水泥100份,本速凝剂的使用量较好为5~15份,特好为7~10份。该使用量如未满5份则有不能发挥优良凝结性状的情况发生,如超过15份则有长期强度表现性低劣化的情况发生。
本发明中,水泥混凝土的水的量用W/C(水/水泥)表示较好为25/100~70/100,特好为40/100~60/100。如该比例未满25/100则水分不足,会有不能拌制的情况发生,如超过70/100则变成所谓的“豆腐渣(シヤブコン)”,有不能获得充分强度的情况发生。
另外,本发明中使用的水泥混凝土的坍落扩展度等没有特别的限定,但是从泵压送性良好上出发,坍落度值(JISA-1101)较好在8cm以上,扩展值(JISA1150)较好在250mm以上。
本发明中使用的水泥没有特别的限制。可使用普通、早强、超早强、中热以及低热等等各种波特兰水泥或者在这些波特兰水泥中混合高炉渣、飞灰或者石灰石粉末而形成的各种混合水泥等中的任一种。
另外作为构成水泥的矿物之一的C3A(CaO·3Al2O3),其含量在100份水泥中较好为5份以上。如未满5份则有不能得到充分的速凝性的情况发生。
水泥的使用量(将制造1m3混凝土所使用的水泥量称为单位水泥量)没有特别的限定,但是从强度表现性优良上出发,较好为在350kg/m3以上,特好为350~5500kg/m3。
本发明中根据需要还可以在不实质损害本发明目的的范围内并用石膏、氢氧化钙、氢氧化铝、铝酸钙、硅铝酸钙、硫铝酸钙、pH调整剂、分散剂、防冻剂、水溶性促进剂、AE剂、减水剂、AE减水剂、缓凝剂、增粘剂、纤维、微粉等添加剂。
作为本发明的向坡面或隧道喷浆的施工法,可使用一般使用的干式喷浆施工方法和湿式喷浆施工方法中的任一种,较好为使用粉尘产生量较少的湿式喷浆施工方法。
作为将本速凝剂和水泥混凝土混合制成本发明的喷浆材料(以下,称为本喷浆材料)的方法,例如较好为使用分支管等在临喷浆之前混合。具体地讲,是在被压送来的水泥混凝土中添加本速凝剂,至本喷浆材料被喷出的时间较好控制在10秒之内,更好为2秒以内。
本速凝剂可通过加热至较好为40℃以上,特好为45~70℃混合在水泥混凝土中,来使速凝性上升。
本喷浆材料可向天然地基的坡面,直接或向其配设有钢筋类的部位场所喷浆。在此,钢筋类是由金属网或钢筋等形成的,较好是将其组合固定在壁面上形成框架骨架,再向该框架上喷射本发明的喷浆材料,形成含钢筋类的水泥混凝土框架。
实施例
实施例1
使用C/S(水泥/砂比)为1/2.5,W/C(水/水泥比)为45/100的配比,并使用减水剂调制将坍落度(SL)调整至18cm程度的砂浆。
向调制好的砂浆中,相对于水泥100份,混入表1所示组成的液体速凝剂10份后装入型箱中,在实验环境温度为20℃下,测定葡氏(proctor)贯入阻力。结果也示于表1。
<使用材料>
原料A:铝原料、氢氧化铝,试剂1级品
原料B:铝原料、八水硫酸铝,试剂1级品
原料C:硫原料、硫酸,试剂1级品
原料D:碱金属原料、碳酸钠,试剂1级品
原料E:碱金属原料、氢氧化钾,试剂1级品
原料F:氟原料、冰晶石,试剂1级品
原料G:氟原料、氟化硼,试剂1级品
原料H:氟原料、氟硅酸镁、试剂1级品
原料I:烷醇胺、二乙醇胺,工业品
原料J:烷醇胺、N,N-二甲基乙醇胺,工业品
络合物形成剂a:丙二酸,试剂1级品
液体速凝剂:按照表1所示的元素组成计算混合各原料,将所得的混合物50份和水50分用球磨机混合,在80℃搅拌1小时。
水泥:市售水泥(C3S=57%,C2S=19%,C4AF=10%,C3A=7%,另外C:CaO,S:SiO2,A:Al2O3,F:Fe2O3),密度3.15g/cm3
减水剂:多元羧酸系高性能AE减水剂,市售品
砂:新潟县姬川产,密度2.62g/cm3
水:自来水
<测定方法>
葡氏贯入阻力值:按照JSCE D-102-1999测定,材龄10分钟
实施例2
除了,通过使表1的实验No.1-3、1-10以及1-17的液体速凝剂中的络合物形成剂的种类和量按照表2所示变化考察速凝剂的贮藏稳定性之外,与实施例1进行同样的试验。结果示于表2。
<使用材料>
络合物形成剂b:草酸,一级试剂
络合物形成剂c:琥珀酸,一级试剂
络合物形成剂d:磷酸,一级试剂
<评价方法>
促进贮藏稳定性:在密闭的试样瓶中装入液体速凝剂300cc,在40℃环境下分别于自试验开始的第3日、第7日、第1个月以及第3个月观察有无析出物。用5种A的滤纸分离析出物,析出物未满2%时记为○,2%以上但未满4%时记为△,4%以上记为×。
实施例3
将单位水泥量为400kg/m3,W/C=50/100,s/a=65%的,并使用减水剂的,坍落度调整为18cm的混凝土,用混凝土活塞泵以10m3/h的速度压送,在至喷出口50cm处,与4m3/h的喷射空气以及相对于水泥为10份的实验No.2-16中的液体速凝剂混合喷射。另外,s/a是细骨料率(sand-coarse aggregate ratio),是以混凝土中的细骨料相对于全部骨料的绝对容积的百分率所表示的数值。
在规定材龄测定喷浆所得的固化体求得强度。结果示于表3。
<使用材料>
水泥:市售水泥(C3S=57%,C2S=19%,C4AF=10%,C3A=7%),密度3.15g/cm
减水剂:多元羧酸系高性能AE减水剂,市售品
砂:新潟县姬川产,密度2.62g/cm3
砂石:新潟县姬川产,密度2.64g/cm3
<测定方法>
材龄3小时、24小时:按照JSCE G-561测定。
材龄28日:自固化体块切出_5.5×11cm的试验体,测定压缩强度。
另外,将作为本申请优先权的基础的日本专利特许特愿2003-351094号(2003年10月20日向日本专利厅申请)的说明书中的全部内容在这里引用,作为本发明的说明书的公开。
[表1]
实验NO. | SO3 | Al2O3 | R2O | F | 烷醇胺 | 络合物形成剂a | 使用原料 | 贯入阻力值 | 备考 |
1-11-21-31-4 | 100100100100 | 02560110 | 15151515 | ---- | ---- | 15151515 | C,DB,C,DA,B,DA,B,D | 1.23.55.36.2 | 比较例实施例实施例实施例 |
1-51-61-7 | 100100100 | 606060 | 02.550 | --- | --- | 151515 | A,BA,B,DA,B,D | 2.84.17.1 | 比较例实施例实施例 |
1-81-91-101-111-12 | 100100100100100 | 6060606060 | 1515151515 | 2.515151550 | ----- | 1515151515 | A,B,D,GA,B,D,GA,B,D,FA,B,D,HA,B,D,H | 11.513.516.214.616.8 | 实施例实施例实施例实施例实施例 |
1-131-141-151-161-171-18 | 100100100100100100 | 606060606060 | 151515151515 | 15-15151515 | 2.51515151550 | 151515151515 | A,B,D,F,IA,B,D,IA,B,D,F,IA,B,D,F,JA,B,D,F,I,JA,B,D,F,I | 18.78.323.321.125.627.2 | 实施例实施例实施例实施例实施例实施例 |
1-19 | 0 | 60 | 15 | - | - | 15 | A,D | 2.0 | 比较例 |
SO3、Al2O3、R2O、F、烷醇胺以及络合物形成剂a是(份)
实验No.1-17是使用I和J的等量混合物15份。
除实验No.1-19外液体速凝剂的pH均在6以下。
[表2]
实验No. | SO3、Al2O3、R2O、F的组成 | 络合物形成剂 | 贯入阻力值(N/mm2) | 促进贮藏稳定性 | 备考 | |||
第3日 | 第7日 | 1个月 | 3个月 | |||||
2-12-21-32-32-4 | 1-31-31-31-31-3 | - 0.0a 2.5a 15a 75a 90 | 3.24.45.34.13.0 | ×○○○○ | ×○○○○ | ×○○○○ | ×△○○○ | 比较例实施例实施例实施例实施例 |
2-51-102-6 | 1-101-101-10 | a 2.5a 15a 75 | 14.316.215.4 | ○○○ | ○○○ | ○○○ | ○○○ | 实施例实施例实施例 |
2-71-172-8 | 1-171-171-17 | a 2.5a 15a 75 | 22.325.623.1 | ○○○ | ○○○ | ○○○ | ○○○ | 实施例实施例实施例 |
2-92-102-11 | 1-31-31-3 | b 2.5b 15b 75 | 4.15.04.3 | ○○○ | ○○○ | ○○○ | ○○○ | 实施例实施例实施例 |
2-122-132-14 | 1-101-101-10 | b 2.5b 15b 75 | 13.315.512.8 | ○○○ | ○○○ | ○○○ | ○○○ | 实施例实施例实施例 |
2-152-162-17 | 1-171-171-17 | b 2.5b 15b 75 | 20.923.321.1 | ○○○ | ○○○ | ○○○ | ○○○ | 实施例实施例实施例 |
2-182-192-20 | 1-31-31-3 | c 2.5c 15c 75 | 3.24.43.8 | ○○○ | ○○○ | ○○○ | ○○○ | 实施例实施例实施例 |
2-212-222-23 | 1-101-101-10 | c 2.5c 15c 75 | 11.314.012.5 | ○○○ | ○○○ | ○○○ | ○○○ | 实施例实施例实施例 |
2-242-252-26 | 1-171-171-17 | c 2.5c 15c 75 | 19.622.120.4 | ○○○ | ○○○ | ○○○ | ○○○ | 实施例实施例实施例 |
络合物形成剂的促进贮藏稳定性,相对于SO3100份,析出物未满2%时记为○,2%以上但未满4%时记为△,4%以上记为×。
液体速凝剂的pH均在6以下。
[表3]
实验No. | 强度值 | ||
3小时 | 24小时 | 28日 | |
3-1 | 2.2 | 15.2 | 36.7 |
(单位:N/mm2)
Claims (15)
1.液体速凝剂,其特征在于,含有硫、铝以及碱金属的元素成分和络合物形成剂。
2.如权利要求1所述的液体速凝剂,其特征还在于,相对于换算成SO3的硫的元素成分100份,该液体速凝剂含有换算为Al2O3的25~110份的铝的元素成分、换算为R2O的2.5~50份的碱金属的元素成分以及2.5~75份的络合物形成剂,上述R表示碱金属原子。
3.如权利要求1或2所述的液体速凝剂,其特征还在于,还含有氟。
4.如权利要求1~3中任一项所述的液体速凝剂,其特征还在于,相对于换算成SO3的硫的元素成分100份,该液体速凝剂含有2.5~50份的氟。
5.如权利要求1~4中任一项所述的液体速凝剂,其特征还在于,还含有烷醇胺。
6.如权利要求1~5中任一项所述的液体速凝剂,其特征还在于,相对于换算成SO3的硫的元素成分100份,该液体速凝剂含有2.5~50份的烷醇胺。
7.如权利要求1~6中任一项所述的液体速凝剂,其特征还在于,碱金属的元素成分是钠或者钾。
8.如权利要求1~7中任一项所述的液体速凝剂,其特征还在于,络合物形成剂是具有1~3个羧基的有机酸。
9.如权利要求1~8中任一项所述的液体速凝剂,其特征还在于,络合物形成剂的配比是,相对于换算成SO3的硫的元素成分100份,含2.5~75份。
10.如权利要求1~9中任一项所述的液体速凝剂,其特征还在于,该液体速凝剂的pH在6以下。
11.喷浆材料,其特征在于,含有权利要求1~10中任一项所述的液体速凝剂、水泥、水以及骨料。
12.如权利要求11所述的喷浆材料,其特征还在于,相对于100份水泥,含有5~15份的液体速凝剂。
13.如权利要求11或12所述的喷浆材料,其特征还在于,单位水泥量在350Kg/m3以上。
14.如权利要求11~13中任一项所述的喷浆材料,其特征还在于,使用了100份水泥中C3A含量在5份以上的水泥。
15.喷浆施工方法,其特征在于,喷射权利要求11~14中任一项所述的喷浆材料。