CN101560379B - 矿用速凝固化材料 - Google Patents
矿用速凝固化材料 Download PDFInfo
- Publication number
- CN101560379B CN101560379B CN 200910074622 CN200910074622A CN101560379B CN 101560379 B CN101560379 B CN 101560379B CN 200910074622 CN200910074622 CN 200910074622 CN 200910074622 A CN200910074622 A CN 200910074622A CN 101560379 B CN101560379 B CN 101560379B
- Authority
- CN
- China
- Prior art keywords
- portions
- parts
- rapid solidification
- mining
- solidification material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种矿用速凝固化材料,由下列重量配比的原料组成:铝矾土80份、硅酸盐10~15份、碱1~4份、氧化硅2~3份、氧化铝2~3份、石膏60份、石灰35~40份、聚安酯0.5~1份、多元醇0.3~2份、多元胺0.2~2份,粉煤灰100份。本发明解决了现有技术中存在的传统井下材料容易开裂、密闭不严、气密性能差、缺乏韧性和膨胀性,造成漏风问题;不能有效治理各类有害气体以及水、火等自然灾害;不能降低劳动强度、减少作业工序和提高功效等问题。
Description
技术领域
本发明属于一种固化材料,具体涉及一种矿用速凝固化材料。
背景技术
传统的矿业生产,通风质量差和水患频繁,是普遍存在的安全隐患问题。特别是煤矿,井下安全通风设施质量差,自燃发火频繁,有害气体泄漏,瓦斯爆炸事故不断发生,给国家财产和矿工人身安全造成了很大的损害。
目前,现有技术中使用的传统水泥、沙石构筑的各类密闭设施整体性差,漏风严重,施工工序多,劳动强度大。特别是井下施工环境大部分处于危险区,运料距离远,施工区巷道狭窄,作业难度增加,密闭质量无法提高,不能把采空区彻底密闭隔绝,影响了有效风量,并且不能有效的解决瓦斯、一氧化碳等有害气体灾害预防及治理问题。
发明内容
本发明就是针对上述现有技术中存在的缺陷,提供一种矿用速凝固化材料,解决上述现有技术中存在的传统井下材料容易开裂、密闭不严、气密性能差、缺乏韧性和膨胀性,造成漏风问题;不能有效治理各类有害气体以及水、火等自然灾害;不能降低劳动强度、减少作业工序和提高功效等问题。
本发明采用以下技术方案:一种矿用速凝固化材料,由下列重量配比的原料组成:铝矾土80份、硅酸盐10~15份、碱1~4份、氧化硅2~3份、氧化铝2~3份、石膏60份、石灰35~40份、聚安酯0.5~1份、多元醇0.3~2份、多元胺0.2~2份,粉煤灰100份。
本发明与现有技术相比具有以下有益效果:本发明的材料特性是无机材料,不污染环境,自身不燃烧,无毒、无害、无腐蚀性,材料性能具有在初凝时间上,在膨胀系数上,在抗压强度上都能够根据工作对象的要求进行调节,适应不同的环境条件,有效解决传统井下材料容易开裂、密闭不严、气密性能差、缺乏韧性和膨胀性,造成漏风问题;不能有效治理各类有害气体以及水、火等自然灾害;不能降低劳动强度、减少作业工序和提高功效等问题。
具体实施方式
实施例1
一种矿用速凝固化材料,将下列重量配比的原料:铝矾土80份、硅酸盐10份、碱4份、氧化硅3份、氧化铝3份,放入球磨机进行粉碎研磨均化后取100份,将下列重量配比的原料石膏60份、石灰35份、聚安酯1份、多元醇2份、多元胺2份放入球磨机进行粉碎研磨均化后取100份,粉煤灰100份,将上述材料加入到水为100份的搅拌容器中,充分搅拌、溶解,搅拌均匀后,通过泵送至充填体。
实施例2
一种矿用速凝固化材料,将下列重量配比的原料铝矾土80份、硅酸盐12.5份、碱2.5份、氧化硅2.5份、氧化铝2.5份,放入球磨机进行粉碎研磨均化后取100份,将下列重量配比的原料石膏60份、石灰37.5份、聚安酯0.5份、多元醇1份、多元胺1份,放入球磨机进行粉碎研磨均化后取100份,粉煤灰100份,将上述材料加入到水为100份的搅拌容器中,充分搅拌、溶解,搅拌均匀后,通过泵送至充填体。
实施例3
一种矿用速凝固化材料,将下列重量配比的原料铝矾土80份、硅酸盐15份、聚安酯1份、多元醇2份、多元胺2份,放入球磨机进行粉碎研磨均化后取100份,将下列重量配比的原料石膏60份、石灰40份、聚安酯0.5份、多元醇0.3份、多元胺0.2份放入球磨机进行粉碎研磨均化后取100份,粉煤灰100份,将上述材料加入到水为100份的搅拌容器中,充分搅拌、溶解,搅拌均匀后,通过泵送至充填体。
Claims (1)
1.一种矿用速凝固化材料,其特征在于:由下列重量配比的原料组成:铝矾土80份、硅酸盐10~15份、碱1~4份、氧化硅2~3份、氧化铝2~3份、石膏60份、石灰35~40份、聚氨酯0.5~1份、多元醇0.3~2份、多元胺0.2~2份,粉煤灰100份。