CN1305914C - 用吗啉－2,3－二酮化合物交联水凝胶的方法 - Google Patents

用吗啉－2,3－二酮化合物交联水凝胶的方法 Download PDF

Info

Publication number
CN1305914C
CN1305914C CNB028194098A CN02819409A CN1305914C CN 1305914 C CN1305914 C CN 1305914C CN B028194098 A CNB028194098 A CN B028194098A CN 02819409 A CN02819409 A CN 02819409A CN 1305914 C CN1305914 C CN 1305914C
Authority
CN
China
Prior art keywords
weight
linking agent
hydrogel
matter
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB028194098A
Other languages
English (en)
Other versions
CN1561348A (zh
Inventor
T·丹尼尔
K·M·埃克斯纳
K·马松内
U·里格尔
M·魏泽曼塔尔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BASF SE
Original Assignee
BASF SE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BASF SE filed Critical BASF SE
Publication of CN1561348A publication Critical patent/CN1561348A/zh
Application granted granted Critical
Publication of CN1305914C publication Critical patent/CN1305914C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及吸水性水凝胶使用吗啉-2，3-二酮类化合物进行胶凝后交联或表面后交联的方法，以及后交联的水凝胶和它们的用途。

Description

用吗啉-2，3-二酮化合物交联水凝胶的方法
本发明涉及吸水性水凝胶使用吗啉-2，3-二酮化合物进行胶凝或表面后交联的方法，以及该后交联水凝胶和它们的用途。
称为超吸收性聚合物或SAP的溶胀性水凝胶形成加成聚合物在现有技术中是已知的。它们是柔性亲水加成聚合物的网络结构，可以是离子和非离子性质的。它们可以通过形成水凝胶而吸收和结合含水流体，因此首选用于制造棉塞，尿布，卫生棉，失禁制品，小孩用训练裤，鞋垫和用于吸收体液的其它卫生制品。超吸收剂也用于其中吸收流体、尤其水或水溶液的其它技术领域。这些领域包括例如贮存，包装，运输(水敏性制品的包装材料，例如鲜花运输，减震)；食品部门(鱼、鲜肉的运输；在鲜鱼/肉包装中的水、血的吸收)；医药(创伤膏药，烧伤敷料或其它渗出性伤口的吸水性材料)；化妆品(药物和药剂的载体材料，风湿病膏药，超声用凝胶，冷却凝胶，化妆品增稠剂，防晒剂)；水包油或油包水乳液的增稠剂；纺织品(手套，运动装，纺织品的水分调节，鞋垫)；化学方法工业应用(有机反应的催化剂，大官能团分子(酶)的固定，附聚用粘合剂，储热介质，助滤剂，聚合物层压材料的亲水组分，分散剂，液化剂)；房屋建造，安装设施(喷粉模塑，粘土基打底料，减震介质，与在富水地基下打隧道有关的助剂，电缆包皮)；水处理，废物处理，除水(防冻剂，可再用沙袋)；清洁；农业(灌溉，融水和露水沉淀物的保留，堆肥添加剂，保护森林不受真菌和害虫侵害，活性成分延迟释放到植物中)；防火(飞溅火花)(用SPA凝胶覆盖房屋或房屋墙壁，因为水具有非常高的热容，可以防止燃烧；在着火例如森林着火的情况下喷雾SAP凝胶)；在热塑性聚合物(多层的亲水化)薄膜中的共挤出剂；生产能吸水的薄膜和热塑性模制品(例如可以储存雨水和露水的农用薄膜；用于保养可以用湿膜包装的新鲜水果和蔬菜的含SAP的薄膜；SAP储存由水果和蔬菜释放的水，不会形成冷凝液滴，并且部分让水重新散发到水果和蔬菜中，使得既不会发出秽臭，也不会枯萎；例如用于食品包装如肉、鱼、家禽、水果和蔬菜的SAP-聚苯乙烯共挤出物)；活性成分制剂(药物，作物保护)中的载体物质。在卫生制品中，超吸收剂一般位于吸收性芯内，除了SAP以外，还含有其它材料，包括纤维(纤维素纤维)，它们用作一种液体缓冲剂，以在中间储存自发施加的液体侵入物和用来确保将吸收性芯内的体液有效疏通到超吸收剂中。
尿布设计的目前趋势是向具有减少的纤维素纤维含量和增加的水凝胶含量的更薄结构的方向发展。朝向更薄尿布结构的趋势已显著改变了近年来的水溶胀性亲水聚合物的所需性能分布。而在开发高吸收性水凝胶的开始，最初人们的兴趣仅仅集中在非常高的溶胀性，随后确定，超吸收剂传输和分布流体的能力也具有决定性作用。已经确定，普通超吸收剂在用液体润湿时在表面显著溶胀，使得液体输送到颗粒内部显著受阻或完全被阻止。超吸收剂的这种特性被称为凝胶阻断。在卫生制品中单位面积的聚合物的量较高不一定引起溶胀的聚合物形成后续流体的阻隔层。具有良好输送性能的产品确保了整个卫生制品的最佳利用。这防止了凝胶阻断现象，而该现象在极端情况下将会引起卫生制品渗漏。流体传输和分布因此对于体液的初始吸收具有决定性作用。
例如在溶胀状态具有高凝胶强度的水凝胶具有良好的输送性能。强度不足的凝胶在施加的压力(由于体重产生的压力)下易变形和堵塞SAP/纤维素纤维吸收剂中的孔，所以阻止了流体的继续吸收。提高的凝胶强度一般通过高交联度来获得，虽然这减低了保留性能。提高凝胶强度的较佳方式是表面后交联。在该方法中，具有平均交联密度的干燥超吸收剂进行另外的交联步骤。表面后交联增加了超吸收剂颗粒外壳的交联密度，从而在载荷下的吸收性升高到较高水平。虽然在超吸收剂颗粒外壳中的吸收能力降低，但芯具有改进的吸附能力(与外壳相比)，由于存在活动聚合物链，使得外壳结构确保了改进的流体传输，不会发生凝胶阻断效应。非常希望超吸收剂的总能力没有被立即占用，而是具有时间延迟。因为卫生制品通常反复被尿侵入，所以超吸收剂的吸收能力应该明显地在第一次处置之后没有被耗尽。
亲水超吸收性水凝胶尤其是聚合(共聚)亲水单体的聚合物，一种或多种亲水单体在适合的接枝基体上的接枝共聚物，交联纤维素或淀粉醚，交联羧甲基纤维素，部分交联聚氧化烯或在含水液体中可溶胀的天然产物，例如瓜尔胶衍生物。这类水凝胶在生产尿布、棉塞、卫生棉和其它卫生制品中用作吸收水溶液的产品，以及在商品蔬菜栽培中用作保水剂。
为了改进使用性能如尿布再润湿性和AUL，例如，亲水超吸收性水凝胶一般进行表面或凝胶后交联。该后交联对于本领域的技术人员来说是已知的，并且优选在凝胶水相中进行或作为研磨和筛分的聚合物颗粒的表面后交联来进行。
可用于该目的的交联剂包括含有至少两个能与亲水聚合物的羧基形成共价键的基团的化合物。有用的化合物例如包括二缩水甘油基和多缩水甘油基化合物，如膦酸二缩水甘油酯，烷氧基甲硅烷基化合物，聚氮丙啶，多胺或聚酰胺型胺类，这些化合物还可以以彼此的混合物使用(参看例如EP-A0 083 022，EP-A-0 543 303和EP-A-0 530 438)。聚酰胺型胺交联剂尤其在EP-A-0 349 935中有描述。
这些交联剂的主要缺点是它们的高反应性，因为这使得在工业操作中必须采用特殊的安全预防措施，以便可以避免不希望有的副作用。同样，上述交联剂具有皮肤刺激性能，这使它们在卫生制品中的应用出现了问题。
已知的交联剂此外包括多官能醇。例如EP-A-0 372 981、US-4 666 983和US-5 385 983分别教导了亲水多元醇的用途和多羟基表面活性剂的用途。在这些参考文献中的反应在120-250℃的高温下进行。该方法的缺点是交联酯化本身在这些温度下仅缓慢地进行。
已经描述了的其它适合的交联剂，包括在WO 99/42494中的2-唑烷酮及其衍生物，在WO 00/31153中的2-氧代四氢-1，3-嗪及其衍生物，在WO 00/31152中的N-酰基-2-唑烷酮类和在WO 99/43720中的双-和聚-2-唑烷二酮类。确实，它们满足了关于在卫生制品中使用的要求，但不能作为化合物商购，并且相当难以制备出纯的化合物。
已经描述的交联剂此外包括在US 6239230中的β-羟基烷基酰胺。它们也适合用于卫生制品。这些化合物的缺点是相对高的所需用量和相关的成本。
本发明的目的是提供可以在非常短的反应时间内和在非常低的反应温度下使用的用于超吸收剂的其它交联物质。
我们已经令人惊奇地发现，当使用吗啉-2，3-二酮作为交联剂时，达到了该目的。
吗啉-2，3-二酮本身是已知的，在文献EP 371640中作为制备某些草氨酸衍生物的起始原料。
本发明因而提供了交联用于制备能吸收含水流体的水凝胶形成聚合物的起始聚合物的方法，该方法包括使用通式1的交联剂：
Figure C0281940900071
其中R1是氢，C1-C4-烷基，C1-C4-羟烷基或结构式2的基团：
Figure C0281940900072
其中R2、R3、R4和R5各自独立地是C1-C4烷基，C1-C4羟烷基或氢。交联不仅包括凝胶交联(线性或轻度交联聚合物的交联)，而且包括表面后交联。表面后交联是获得芯壳结构的起始聚合物的表面更强交联。所谓起始聚合物是指在交联之前的聚合物。能吸收含水流体的水凝胶形成聚合物优选是吸收至少其本身重量和优选其本身重量10倍的蒸馏水(优选甚至在0.7psi的压力下)的那些。
表面后交联是优选的。起始聚合物优选含有羧基。
在上述交联方法中，用交联剂处理起始聚合物，以及优选通过在处理过程中或之后升高温度来进行后交联和干燥，交联剂优选存在于惰性溶剂中。惰性溶剂是基本不与起始聚合物或交联剂反应的溶剂。优选的是以超过90％、优选超过95％、尤其优选超过99％的程度、特别是超过99.5％的程度不与起始聚合物或交联剂发生化学反应的这些溶剂。
上述方法中的特别优选的交联剂是N-2-羟乙基吗啉-2，3-二酮(式3)：
它的制备特别简单且成本低。
后交联和干燥优选在30-250℃，尤其50-200℃和最优选100-180℃下进行。表面后交联溶液优选通过在适合的喷雾混合器内喷雾聚合物来施加。在喷雾之后，热法干燥聚合物粉料，以及交联反应不仅可以在干燥操作之前而且可以在干燥操作期间进行。优选在反应混合器或混合和干燥系统，如Ldige混合器、BEPEX混合器、NAUTA混合器、SHUGGI混合器或PROCESSALL中喷雾交联剂的溶液。此外还可以使用流化床干燥器。
干燥操作可以通过夹套加热或通过吹入热空气而在混合器本身中进行。还适合的是下游干燥器如柜式干燥器，旋转管式炉，或可加热螺杆。但还可以使用例如共沸蒸馏作为干燥技术。在反应混合器或干燥器中在该温度下的停留时间优选少于60分钟和更优选少于30分钟。
优选的是其中起始聚合物是聚合丙烯酸或聚丙烯酸酯、尤其通过使用多官能烯属不饱和自由基交联剂进行自由基聚合获得的聚合丙烯酸或聚丙烯酸酯的以上方法。
本发明还提供了包括式1的交联剂或优选交联剂和溶剂的物质组合物，所述溶剂选自水、水与在水中具有无限溶解度的一种或多种有机溶剂的混合物，以及水与一种或多种一元醇或多元醇例如甲醇和甘油的混合物。醇优选携带1、2或3个OH基团和优选具有1-10和尤其至多4个碳原子。优选的是伯醇和仲醇。
在物质组合物中，溶剂优选是具有10-90重量％、优选30-70重量％、更优选15-65重量％和尤其40-60重量％的醇含量的醇-水混合物，以该溶液为基准计。
优选的醇是甲醇，乙醇，异丙醇，乙二醇，1，2-丙二醇或1，3-丙二醇。
优选的物质组合物包括0.1-20重量％、尤其0.5-10重量％和尤其至多3重量％的交联剂。
以上方法优选使用上述物质组合物。
优选的是利用包括0.1-20重量％和尤其0.5-10重量％比率的交联剂和溶剂的物质组合物的那些方法，以起始聚合物的质量为基准计。
优选的是以0.01-5.0重量％、优选0.02-3.0重量％、更优选0.03-1.0重量％和尤其0.05-0.1重量％的剂量使用交联剂的那些方法，以起始聚合物为基准计。
本发明还提供了通过上述方法之一制备的聚合物和它们在卫生制品、包装材料和无纺织物中的用途，以及上述物质组合物用于生产交联聚合物或能通过加热来交联的聚合物的用途，尤其在涂料和油漆中的应用。
在本发明方法中使用的亲水超吸收性水凝胶(起始聚合物)尤其是聚合(共聚)亲水单体的聚合物，一种或多种亲水单体在适合的接枝基体上的接枝聚合物(共聚物)，交联纤维素或淀粉醚或在含水流体中可溶胀的天然产物，例如瓜尔胶衍生物。这些水凝胶对本领域的技术人员来说是已知的，例如描述在US-4 286 082，DE-C-27 06 135，US-4 340 706，DE-C-3713 601，DE-C-28 40 010，DE-A-43 44 548，DE-A-40 20 780，DE-A-40 15085，DE-A-39 17 846，DE-A-38 07 289，DE-A-35 33 337，DE-A-35 03 458，DE-A-42 44 548，DE-A-42 19 607，DE-A-40 21 847，DE-A-38 31 261，DE-A-35 11 086，DE-A-31 18 172，DE-A-30 28 043，DE-A-44 18 881，EP-A-0 801 483，EP-A-0 455 985，EP-A-0 467 073，EP-A-0 312 952，EP-A-0205 874，EP-A-0 499 774，DE-A 26 12 846，DE-A-40 20 780，EP-A-0 205674，US-5 145 906，EP-A-0 530 438，EP-A-0 670 073，US-4 057 521，US-4 062 817，US-4 525 527，US-4 295 987，US-5 011 892，US-4 076 663或US-4 931 497。还特别适合的是由在WO 01/38402中所述的生产方法获得的超吸收性水凝胶以及如在DE 198 54 575中所述的无机-有机混杂超吸收性水凝胶。上述专利文件的内容，尤其通过所述方法生产的水凝胶特地引入到本文中供参考。
适于制备这些亲水超吸收性水凝胶的亲水单体的实例是能聚合的酸，如丙烯酸，甲基丙烯酸，乙烯基磺酸，乙烯基膦酸，马来酸，包括其酸酐，富马酸，衣康酸，2-丙烯酰胺基-2-甲基丙磺酸，2-丙烯酰胺基-2-甲基丙烷膦酸以及它们的酰胺、羟烷基酯和含氨基或铵基的酯和酰胺，还有，水溶性N-乙烯基酰胺或氯化二烯丙基二甲基铵。优选的亲水单体是式4的化合物：
其中
R1是氢，甲基或乙基，
R2是-COOR4，磺酰基或膦酰基，(C1-C4)链烷醇酯化的膦酰基或式5的基团：
Figure C0281940900102
R3是氢，甲基，乙基，或羧基，
R1是氢，氨基，或羟基-(C1-C4)烷基，和
R5是磺酰基，膦酰基或羧基。
(C1-C4)链烷醇的实例是甲醇，乙醇，正丙醇或正丁醇。
尤其优选的亲水单体是丙烯酸和甲基丙烯酸。
对可通过烯属不饱和酸的接枝共聚获得的亲水水凝胶适合的接枝基体可以是天然或合成来源的。实例是淀粉，纤维素或纤维素衍生物以及其它多糖和寡糖，聚氧化烯，尤其聚环氧乙烷和聚环氧丙烷，以及亲水聚酯。
吸水性聚合物可通过丙烯酸或丙烯酸酯在水溶性聚合物基质上的自由基接枝共聚来获得。适合的水溶性聚合物基质非排他性地包括例如藻酸盐，聚乙烯醇和多糖如淀粉。用于本发明的目的的接枝共聚利用多官能烯属不饱和自由基交联剂。
吸水性聚合物可以是由聚合丙烯酸或聚丙烯酸酯和硅酸盐、铝酸盐或铝硅酸盐形成的有机-无机混杂聚合物。更尤其，可以使用这样的聚合丙烯酸或聚丙烯酸酯，其通过自由基聚合获得，和其中使用多官能烯属不饱和自由基交联剂，和其生产方法使用水溶性硅酸盐或可溶性铝酸盐或它们的混合物。
适合的聚氧化烯例如具有式6：
Figure C0281940900111
其中
R6和R7各自独立是氢，烷基，链烯基或芳基，
X是氢或甲基，和
n是1-10000。
R6和R7各自优选是氢，(C1-C4)烷基，(C2-C6)链烯基或苯基。
优选的水凝胶尤其是聚丙烯酸酯，聚甲基丙烯酸酯以及在US-4 931497、US-5 011 892和US-5 041 496中所述的接枝聚合物。更尤其优选的水凝胶是在WO 01 38402中所述的捏合聚合物和在DE 198 545 75中所述的以聚丙烯酸酯为基础的混杂有机-无机水凝胶。
亲水超吸收性水凝胶优选为交联形式，即它们含有已共聚到聚合物网络中的具有至少两个双键的化合物。适合的交联剂尤其是亚甲基双丙烯酰胺和亚甲基双甲基丙烯酰胺，不饱和单或多羧酸与多元醇形成的酯，如二丙烯酸酯或三丙烯酸酯，实例是丁二醇与乙二醇形成的二丙烯酸酯和二甲基丙烯酸酯，以及三羟甲基丙烷三丙烯酸酯和烯丙基化合物如(甲基)丙烯酸烯丙酯，氰脲酸三烯丙酯，马来酸二烯丙酯，多烯丙酯，四烯丙基氧基乙烷，三烯丙基胺，四烯丙基乙二胺，磷酸的烯丙酯和乙烯基膦酸衍生物，如在EP-A-0 343 427中所述。然而，本发明的方法尤其优选利用使用多烯丙基醚作为交联剂和通过丙烯酸的酸性均聚制备的水凝胶。适合的交联剂是季戊四醇三烯丙基醚，季戊四醇四烯丙基醚，聚乙二醇二烯丙基醚，单乙二醇二烯丙基醚，甘油二烯丙醚、甘油三烯丙基醚，以山梨醇为基础的多烯丙基醚以及它们的乙氧基化变型。还尤其优选的是属于聚乙二醇二丙烯酸酯、三羟甲基丙烷三丙烯酸酯的乙氧基化衍生物如Sartomer SR9035、以及甘油二丙烯酸酯和甘油三丙烯酸酯的乙氧基化衍生物的交联剂。应该认识到，也可以使用以上交联剂的混合物。
吸水性聚合物优选是聚合丙烯酸或聚丙烯酸酯。该吸水性聚合物可以通过从文献中获悉的方法来制备。优选的是含有交联共聚单体(0.001-10mol％)的聚合物，但最优选的是通过自由基聚合获得且其中使用多官能烯属不饱和自由基交联剂的聚合物。
亲水超吸收性水凝胶可以通过普通聚合方法来制备。优选的是通过凝胶聚合的方法在水溶液中的加聚。在该方法中，一种或多种亲水单体和任选的合适接枝基体的15-50重量％水溶液在自由基引发剂的存在下利用特罗姆斯多夫-诺利什效应聚合，优选不用机械混合(Makromol.Chem.1，169(1947))。聚合反应可以在0-150℃，优选10-100℃的温度范围，在大气压或者升压或减压下进行。通常，加聚还可以在保护气体氛围中，优选在氮气下进行。加聚可以使用热能电磁辐射或常用化学聚合引发剂来引发，例如有机过氧化物，如过氧化苯甲酰，氢过氧化叔丁基，过氧化甲基乙基酮，氢过氧化枯烯，偶氮化合物如偶氮二异丁腈以及无机过氧化合物如(NH4)2S2O8·K2S2O8或H2O2。
视需要而定，它们可以与还原剂结合使用，如抗坏血酸，亚硫酸氢钠，亚硫酸铁(II)，或氧化还原体系，其中还原组分是脂族或芳族亚磺酸如苯亚磺酸和甲苯亚磺酸或它们的衍生物，例如如在DE-C-1 301 566中所述的亚磺酸类，醛和氨基化合物的曼尼希加合物。加成聚合物的质量特性可以通过将聚合物凝胶在50-130℃和优选70-100℃的温度范围补充加热数小时来进一步改进。
将所得凝胶中和到0-100mol％，优选25-100mol％和尤其优选50-85mol％的程度，按所用单体计，为此，可以使用常规中和剂，优选碱金属氢氧化物、碱金属氧化物或相应的碱金属碳酸盐，尤其优选氢氧化钠、碳酸钠和碳酸氢钠。
中和通常通过混入水溶液或优选固体形式的中和剂来达到。将凝胶机械粉碎，例如利用绞肉机，以及喷雾、散播或倾倒中和剂，然后仔细混合。中和的凝胶材料然后可以反复切碎以便均化。中和的凝胶材料然后用带式干燥机或干燥鼓干燥，直到残留水分含量优选低于10重量％和尤其优选低于5重量％为止。
然而，加聚还可以通过在文献中描述的任何其它方法来进行。更尤其，丙烯酸的中和还可以在加聚之前进行。聚合然后可以在本领域技术人员已知的带式反应器或在捏合反应器内连续或间歇进行。当聚合在带式反应器内进行时，尤其优选利用电磁辐射、优选利用UV辐射或作为替代使用氧化还原引发剂体系来引发。还更尤其优选的是两种引发方法的组合：电磁辐射和化学氧化还原引发剂体系同时使用。
然后将干燥的水凝胶研磨和筛分，研磨通常可以使用辊磨机、销式磨机(pin mill)或振动磨来进行。筛出水凝胶的粒度优选为45-1000μm，更优选45-850μm，尤其优选200-850μm，最优选300-850μm。这些范围优选包括了80重量％的颗粒和尤其90重量％的颗粒。粒度分布可以使用常规的激光方法来测定。
根据本发明的水凝胶形成聚合物的CRC值[g/g]可以通过在实验部分所述的方法来测定，并且优选在15以上，尤其16、18、20、22、24，或更高，尤其优选25，特别是26、27、28、29，特别优选30、31、32、33、34、35、36、37或更高。
根据本发明的水凝胶形成聚合物的AUL-0.7psi值[g/g]可以通过在实验部分所述的方法来测定，并且优选为8以上，尤其9、10、11、12、13、14或更高，更优选15，特别是16、17、18、19或更高，特别优选高于20，更尤其21、22、23、24、25、26、27、28或更高。
根据本发明的水凝胶形成聚合物的AUL-0.5psi值[g/g]可以通过在实验部分所述的方法来测定，并且优选为8以上，尤其9、10、11、12、13、14或更高，更优选15，特别是16、17、18、19或更高，特别优选高于20，更尤其21、22、23、24、25、26、27、28或更高。
主题水凝胶形成聚合物的开发和应用
本发明进一步提供了上述水凝胶形成聚合物在卫生制品中的应用，该制品包括：
(A)液体可透性顶面片，
(B)液体不透性背片，
(C)位于(A)和(B)之间的芯，包括10-100重量％的根据本发明的水凝胶形成聚合物和0-90重量％的亲水纤维材料，优选20-100重量％的根据本发明的水凝胶形成聚合物和0-80重量％的亲水纤维材料，更优选30-100重量％的根据本发明的水凝胶形成聚合物和0-70重量％的亲水纤维材料，还更优选40-100重量％的根据本发明的水凝胶形成聚合物和0-60重量％的亲水纤维材料，进一步更优选50-100重量％的根据本发明的水凝胶形成聚合物和0-50重量％的亲水纤维材料，尤其优选60-100重量％的根据本发明的水凝胶形成聚合物和0-40重量％的亲水纤维材料，特别优选70-100重量％的根据本发明的水凝胶形成聚合物和0-30重量％的亲水纤维材料，极优选80-100重量％的根据本发明的水凝胶形成聚合物和0-20重量％的亲水纤维材料，最优选90-100重量％的根据本发明的水凝胶形成聚合物和0-10重量％的亲水纤维材料，
(D)任选的直接位于所述芯(C)上面和下面的薄织物层，和
(E)任选的位于(A)和(C)之间的截获层(acquisition layer)。
百分率应该这样来理解，在10-100重量％的情况下，11、12、13、14、15、16、17、18、19至100重量％的根据本发明的水凝胶形成聚合物和在各百分率之间的所有百分率(例如12.2重量％)是可行的，对于相应的亲水纤维材料，0至分别89、88、87、86、85、83、82、81重量％和位于其间的百分率(例如87.8重量％)是可行的。如果在芯中存在其它材料，聚合物和纤维的百分率相应地降低。同样的情况适用于优选的范围，例如，在极优选的情况下，根据本发明的水凝胶形成聚合物可以以81、82、83、84、85、86、87、88、89重量％存在，以及纤维材料相应为19、18、17、16、15、14、13、12、11重量％。所以，优选的范围含有20、21、22、23、24、25、26、27、28、29至100重量％的根据本发明的水凝胶形成聚合物，更优选的范围含有30、31、32、33、34、35、36、37、38、39至100重量％的根据本发明的水凝胶形成聚合物，还更优选的范围含有40、41、42、43、44、45、46、47、48、49至100重量％的根据本发明的水凝胶形成聚合物，进一步更优选的范围含有50、51、52、53、54、55、56、57、58、59至100重量％的根据本发明的水凝胶形成聚合物，尤其优选的范围含有60、61、62、63、64、65、66、67、68、69至100重量％的根据本发明的水凝胶形成聚合物，特别优选的范围含有70、71、72、73、74、75、76、77、78、79至100重量％的根据本发明的水凝胶形成聚合物，和最优选的范围含有90、91、92、93、94、95、96、97、98、99或100重量％的根据本发明的水凝胶形成聚合物。
用于本发明的目的的卫生制品不仅包括成人用的失禁床垫和失禁短裤，而且包括婴儿用尿布。
液体可透性顶面片(A)是与穿用者的皮肤直接接触的层。它的材料包括通常的聚酯、聚烯烃、人造丝或天然纤维如棉花的合成或制造纤维或薄膜。在无纺材料的情况下，纤维一般透过粘结剂如聚丙烯酸酯连接在一起。优选的材料是聚酯，人造丝或它们的共混物，聚乙烯和聚丙烯。液体可透过层的实例描述在WO 99/57355A1、EP 102 388 3A2中。
液体不透层(B)一般是聚乙烯或聚丙烯片材。
芯(C)不仅包括本发明的水凝胶形成聚合物，而且包括亲水纤维材料。所谓亲水是指含水流体在该纤维上快速散布。纤维材料通常是纤维素，改性纤维素，人造丝，聚酯如聚对苯二甲酸乙二醇酯。尤其优选的是纤维素纤维如纸浆。该纤维一般具有1-200μm、优选10-100μm的直径，以及具有1mm的最低长度。
尿布结构和形状是普通知识，例如描述在WO 95/26209，66页34行至69页11行，DE 196 04 601A1，EP-A-0 316 518和EP-A-0 202 127中。在WO 00/65084，尤其6-15页，WO 00/65348，尤其4-17页，WO00/35502，尤其3-9页，DE 19737434，WO 98/8439中也概括地描述了尿布和其它卫生制品。女性卫生用的卫生制品描述在以下参考文献中。在那些地方可以使用能吸收含水流体的本发明水凝胶形成聚合物。女性护理品(Femcare)参考文献：WO 95/24173：用于控制气味的吸收制品，WO91/11977：体液气味控制，EP 389023：吸收性卫生制品，WO 94/25077：气味控制材料，WO 97/01317：吸收性卫生制品，WO 99/18905，EP 834297，US 5,762,644，US 5,895,381，WO 98/57609，WO 2000/065083，WO2000/069485，WO 2000/069484，WO 2000/069481，US 6,123,693，EP1104666，WO 2001/024755，WO 2001/000115，EP 105373，WO2001/041692，EP 1074233。棉塞描述在以下参考文献中：WO 98/48753，WO 98/41179，WO 97/09022，WO 98/46182，WO 98/46181，WO2001/043679，WO 2001/043680，WO 2000/061052，EP 1108408，WO2001/033962，DE 20020662，WO 2001/001910，WO 2001/001908，WO2001/001909，WO 2001/001906，WO 2001/001905，WO 2001/24729。失禁制品描述在以下参考文献中：失禁者用一次性吸收性制品：EP 311344说明书3-9页；一次性吸收性制品：EP 850623；吸收性制品：WO 95/26207；吸收性制品：EP 894502；干法成网纤维结构：EP 850 616；WO 98/22063；WO 97/49365；EP 903134；EP 887060；EP 887059；EP 887058；EP 887057；EP 887056；EP 931530；WO 99/25284；WO 98/48753。女性护理品和失禁制品描述在以下参考文献中：月经用具：WO 93/22998说明书26-33页；体液用吸收性元件：WO 95/26209说明书36-39页；一次性吸收性制品：WO 98/20916说明书13-24页；改进的复合吸收性结构：EP 306262说明书3-14页；人体废物吸收制品：WO 99/45973。这些参考文献和在它们中的参考文献由此特地在本发明的公开物中引入。
根据本发明的水凝胶形成聚合物作为水和含水流体的吸收剂是非常有效的，使得它们可以有利地用作商品蔬菜栽培的保水剂、助滤剂和尤其卫生制品如尿布、棉塞或卫生棉中的吸收性组分。
根据本发明的高度可溶胀性水凝胶的引入和固定
除了上述高度可溶胀性水凝胶以外，本发明的吸收性组合物还包括能容纳高溶胀性水凝胶或固定这些水凝胶的结构。能容纳高溶胀性水凝胶且能并入到吸收层中的任何结构都是适合的。许多的这种组合物是已知的，并且详细描述在文献中。用于安装高溶胀性水凝胶的结构例如可以是由纤维素纤维混合物(气流法织网，湿法成网的织网)或合成聚合物纤维(熔体吹塑织网，纺粘型织物)或纤维素纤维和合成纤维的纤维混合物组成的纤维基质。可行的纤维材料详细描述在以下的章节中。气流成网法例如描述在WO 98/28478中。此外，开孔泡沫或类似物可以用来安装高溶胀性水凝胶。
另外，这种结构可以是熔合两个独立的层、从而形成包含高溶胀性水凝胶的一个或最好多个室的结果。这种室体系详细描述在EP 0 615 736A1，第7页第26行及以下中。
在这种情况下，这两层中的至少一层应该是可透水的。第二层可以是透水或不透水的。所用的层材料可以是薄纱或其它织物，闭孔或开孔泡沫，多孔薄膜，弹性体或由纤维材料组成的织物。当吸收性组合物由层结构组成时，层材料应该具有其孔尺寸足够小至保留高溶胀性水凝胶颗粒的孔结构。以上吸收性组合物的结构的实例还包括在其间安装和固定高溶胀性水凝胶的至少两层组成的层压件。
通常，可以将水凝胶颗粒固定在吸收性芯内，以改进干湿完整性。干湿完整性描述了将高溶胀性水凝胶安装到吸收性组合物内以使得它们不仅在湿状态而且在干燥状态也耐受外力且高溶胀性聚合物不易位或溢出的能力。所提到的力尤其是在穿用卫生制品时在移动的过程中发生的机械应力或在尤其失禁的情况下在卫生制品上的重量压力。至于固定，本领域的技术人员知道多种可行方法。在WO 95/26 209第37页第36行至第41页第14行描述了实例如用热处理固定，添加粘合剂、热塑性塑料、粘结剂材料。该引用的段落因此成为了本发明的一部分。提高强度的方法还可以在WO2000/36216A1中找到。
此外，吸收性组合物可以包括基底材料，例如在其上固定高溶胀性水凝胶颗粒的聚合物薄膜。该固定可以不仅在一个面而且可以在两个面进行。基底材料可以是透水或不透水的。
以上吸收性组合物的结构以10-100重量％，优选20-100重量％，更优选30-100重量％，还更优选40-100重量％，进一步更优选50-100重量％，尤其优选60-100重量％，特别优选70-100重量％，极优选80-100重量％和最优选90-100重量％的重量百分率引入高溶胀性水凝胶，以该结构和高溶胀性水凝胶的总重量为基准计。
吸收性组合物的纤维材料
根据本发明的吸收性组合物的结构可以以各种纤维材料为基础，它们用作纤维网络或基质。本发明不仅包括天然来源(改性或未改性)的纤维，而且包括合成纤维。
在WO 95/26 209的第28页第9行至第36页第8行中给出了可以在本发明中使用的纤维的实例的详细概述。所引用的段落因此为本发明的一部分。
纤维素纤维的实例包括在吸收产品中常用的纤维素纤维，如短纤浆和棉类的纤维素。材料(软或硬木)，生产方法如化学纸浆，半化学纸浆，化学热-机械纸浆(CTMP)和漂白方法不是特别限制的。例如，使用天然纤维素纤维如棉花，亚麻，蚕丝，羊毛，黄麻，乙基纤维素和乙酸纤维素。
适合的合成纤维由聚氯乙烯，聚氟乙烯，聚四氟乙烯，聚偏二氯乙烯，聚丙烯酸类化合物如ORLON，聚乙酸乙烯酯，聚乙酸乙基乙烯酯，可溶性或不溶性聚乙烯醇生产。合成纤维的实例包括热塑性聚烯烃纤维，如聚乙烯纤维(PULPEX)，聚丙烯纤维和聚乙烯-聚丙烯双组分纤维，聚酯纤维，如聚对苯二甲酸乙二醇酯纤维(DACRON或KODEL)，共聚酯，聚乙酸乙烯酯，聚乙酸乙基乙烯酯，聚氯乙烯，聚偏二氯乙烯，聚丙烯酸类，聚酰胺类，共聚酰胺类，聚苯乙烯，和上述聚合物的共聚物，以及由聚对苯二甲酸乙二醇酯-聚间苯二甲酸乙二醇酯共聚物、聚乙酸乙基乙烯酯/聚丙烯、聚乙烯/聚酯、聚丙烯/聚酯、共聚酯/聚酯组成的双组分纤维，聚酰胺纤维(尼龙)，聚氨酯纤维，聚苯乙烯纤维和聚丙烯腈纤维。优选的是聚烯烃纤维，聚酯纤维和它们的双组分纤维。此外优选的是由芯-壳型和并列型的聚烯烃组成的热粘合双组分纤维，这是由于它们在流体吸收之后具有优异的尺寸稳定性。
所述合成纤维优选与热塑性纤维结合使用。在热处理的情况下，后者一定程度上迁移到所存在的纤维材料的基质内，所以在冷却时构成了粘接部位和更新的硬挺元件。另外，添加热塑性纤维意味着，在热处理之后孔尺寸有增加。这使得有可能通过在吸收性芯的形成过程中连续添加热塑性纤维而在顶面片的方向中连续增加热塑性纤维的重量百分率，这导致了孔径的类似连续增加。热塑性纤维可以由具有低于190℃、优选75-175℃的熔点的多种热塑性聚合物形成。这些温度由于太低而不可能造成对纤维素纤维的损伤。
上述合成纤维的长度和直径不是特别限制的，一般可以优选使用1-200mm长度和0.1-100旦尼尔(g/9000m)直径的任何纤维。优选的热塑性纤维具有3-50mm的长度，尤其优选的热塑性纤维具有6-12mm的长度。热塑性纤维的优选直径为1.4-10分特，以及1.7-3.3分特的范围(g/10000m)是特别优选的。纤维的形式可以不同；实例包括织造型，窄圆截面型，断损/短切纱型，短纤维型和连续长丝纤维型。
在本发明的吸收性组合物中的纤维可以是亲水型、疏水型或它们的组合。根据Robert F.Gould在the 1964 American Chemical Societypublication“Contact angle，wettability and adhesion”中的定义，当液体和纤维(或纤维表面)之间的接触角小于90°时或当液体倾向于在所述表面上自发展开时，纤维被称为亲水型纤维。这两种过程一般是同时共存的。相反，当形成了大于90°的接触角和没有发现展开时，纤维被称为疏水型纤维。
优选使用亲水纤维材料。尤其优选使用在躯体侧弱亲水和在高溶胀性水凝胶周围区域最亲水的纤维材料。在生产方法中，使用具有不同亲水性的层来产生将侵入流体引导到水凝胶内的梯度，在那里该流体最终被吸收。
适用于本发明的吸收性组合物的亲水纤维例如包括纤维素纤维，改性纤维素纤维，人造丝，聚酯纤维，例如聚对苯二甲酸乙二醇酯(DACRON)，和亲水尼龙(HYDROFIL)。适合的亲水纤维还可以通过使疏水纤维亲水化，例如由聚烯烃(例如聚乙烯或聚丙烯)、聚酰胺、聚苯乙烯、聚氨酯等获得的热塑性纤维用表面活性剂或二氧化硅处理来获得。然而，因为成本和易获得性的原因，纤维素纤维是优选的。
将高溶胀性水凝胶颗粒植入到所述纤维素材料中。这可以通过各种方法来进行，例如通过共同使用水凝胶材料和纤维以形成基质形式的吸收层，或通过将高溶胀性水凝胶引入到纤维混合物层中，在那里它们通过粘合剂或各层的层压而被最终固定。
流体截获和分布纤维基质可以包括合成纤维、或纤维素纤维、或合成纤维和纤维素纤维的混合物，在这种情况下，混合比可以是(100-0)合成纤维：(0-100)纤维素纤维。所使用的纤维素纤维另外可以进行化学硬挺整理，以增加卫生制品的尺寸稳定性。
纤维素纤维的化学硬挺整理可以用不同方法来提供。提供纤维硬挺性的第一种方式是通过将适合的涂料加入到纤维材料中。这种添加剂例如包括聚酰胺-表氯醇涂料(Kymene557H，Hercoles，Inc.Wilmington，Delaware)，聚丙烯酰胺涂料(描述在US-A-3,556,932中或作为购自American Cyanamid Co.，Stamford，CT的Parez631NC商购产物)，蜜胺-甲醛涂料和聚乙烯亚胺涂料。
纤维素纤维还可以通过化学反应来进行化学硬挺整理。例如，可以添加适合的交联剂物质，以便在纤维内发生交联。适合的交联剂物质是用于交联单体的典型物质，包括、但不限于C2-C8二醛，具有酸官能团的C2-C8单醛和尤其C2-C9多羧酸。来自该系列的具体物质例如是戊二醛，乙二醛，乙醛酸，甲醛和柠檬酸。这些物质与在任何一条纤维素链内或在任何一种纤维素纤维中的两条相邻纤维素链之间的至少2个羟基反应。该交联引起了纤维的硬挺，作为该处理的结果，赋予了该纤维以更高的尺寸稳定性。除了它们的亲水特性以外，这些纤维表现了硬挺性和弹性的均衡组合。这种物理性能使得可以即使在同时接触流体和压缩力的情况下也保持毛细管结构和防止过早塌陷。
化学交联的纤维素纤维是已知的，并且描述在WO91/11162，US3,224,926，US3,440,135，US3,932,209，US4,035,147，US4,822,453，US4,888,093，US4,898,642和US5,137,537中。该化学交联赋予了纤维材料以硬挺性，这最终反映为卫生制品的尺寸稳定性得到总体改进。各层通过本领域技术人员已知的方法连接在一起，例如用热处理进行层间熔化，添加热熔型粘合剂、胶乳粘结剂等。
制备吸收性组合物的方法
吸收性组合物由能容纳高溶胀性水凝胶的结构和存在于所述结构中或固定于其上的高溶胀性水凝胶组成。
获得包括例如高溶胀性水凝胶固定于其一侧或两侧的基底材料的吸收性组合物的方法的实例是已知的，本发明包括、但不限于这些方法。
获得例如包括在高溶胀性水凝胶(c)中植入的合成纤维(a)和纤维素纤维(b)的纤维材料共混物(共混比为(100-0)合成纤维：(0-100)纤维素纤维)的吸收性组合物的方法的实例包括：(1)其中将(a)、(b)和(c)一起同时混合的方法，(2)其中将(a)和(b)的混合物混入到(c)中的方法，(3)其中将(b)和(c)的混合物与(a)混合的方法，(4)其中将(a)和(c)的混合物混入到(b)中的方法，(5)其中将(b)和(c)混合和连续计量加入(a)的方法，(6)其中将(a)和(c)混合和连续计量加入(b)的方法，以及(7)其中将(b)和(c)单独混入到(a)中的方法。在这些实例中，方法(1)和(5)是优选的。在该方法中所用的装置不是特别限制的，可以使用本领域技术人员已知的任何常用装置。
以这种方式获得的吸收性组合物任选可以进行热处理，以便获得在湿状态下具有优异尺寸稳定性的吸收层。热处理方法不是特别限制的。实例包括通过加入热空气或红外辐照射进行的热处理。热处理的温度为60-230℃，优选100-200℃，尤其优选100-180℃。
热处理的持续时间取决于合成纤维的类型、它的用量和卫生制品生产速率。通常，热处理的持续时间为0.5秒钟至3分钟，优选1秒钟至1分钟。
吸收性组合物一般例如配备了液体可透性顶面片和液体不透性背片。此外，接上分支袖带(leg cuffs)和粘合接头片，以制成卫生制品。可透性顶面片和不透性背片以及分支袖带和粘合接头片的材料和类型是本领域技术人员已知的，并且不是特别限制的。它们的实例可以在WO 95/26 209中找到。
实验部分
表面交联的质量可以通过干燥的水凝胶用以下试验方法试验来测定。
试验方法
a)离心保留能力(CRC)
本方法测定了水凝胶在茶叶袋中的自由溶胀性。将0.2000±0.0050g的干燥水凝胶(粒度级分106-850μm)称量到尺寸为60×85mm茶叶袋内，随后密封。将茶叶袋在过量的0.9重量％氯化钠溶液(至少0.83L的氯化钠溶液/1g的聚合物粉料)中放置30分钟。然后将茶叶袋在250g下离心3分钟。通过重新称量离心茶叶袋来测定液体的量。
b)在负荷下的吸收性(AUL)(0.7psi)
测定AUL 0.7psi的测量池是内径60mm和高度50mm的有机玻璃圆筒。粘接于其底面的是具有36μm的筛孔尺寸的不锈钢筛底板。测量池进一步包括具有59mm直径的塑料板和可以与该塑料板一起放入到测量池内的砝码。塑料板和砝码总共重1345g。AUL 0.7psi通过测定空有机玻璃圆筒和塑料板的重量并记录其为W0来测定。然后将0.900±0.005g的水凝胶形成聚合物(粒度分布150-800μm)称量到有机玻璃圆筒内，并非常均匀地分布在不锈钢筛底板上。然后小心地将塑料板放置在有机玻璃圆筒内，称量整个装置，该重量被记录为Wa。然后将砝码放置在有机玻璃圆筒内的塑料板上。然后将直径120mm且孔隙率为0的陶瓷滤板放置在直径200mm和高度30mm的陪替氏培养皿的中间，再引入足够的0.9重量％氯化钠溶液，使液体的表面与滤板表面平齐，滤板的表面没有被润湿。随后将直径90mm和孔径＜20μm的圆滤纸(购自Schleicher & Schull的S&S 589Schwarzband)放置在陶瓷板上。然后将含有水凝胶形成聚合物与塑料板和砝码的有机玻璃圆筒放置在滤纸的上面，并静置60分钟。在该时间的最后，从滤纸和陪替氏培养皿上移走整个装置，随后从有机玻璃圆筒中取出砝码。含有溶胀水凝胶的有机玻璃圆筒与塑料板一起称重，该重量被记录为Wb。
AUL通过以下等式来计算：
AUL 0.7psi[g/g]＝[Wb-Wa]/[Wa-W0]
AUL-0.5psi使用相应的较低压力来测定。
c)盐水导流能力(SFC)
测定SFC的试验方法描述在U.S.5 599 335中。
实施例
N-2-羟乙基吗啉-2，3-二酮的制备实施例
首先将657.6g(4.5mmol)的草酸二乙酯加入到装有回流冷凝器、温度计、KPG搅拌器和滴液漏斗的2L四颈烧瓶内，再加热到80℃。
在2小时的过程中滴加473.1g(4.5mmol)的二乙醇胺。在80℃下另外搅拌2小时之后，在减压下除去释放的乙醇，获得了大约749.4g的几乎无色的残留物，它还含有痕量的乙醇。
为了进一步纯化，在煮沸热量下将717.4g的粗产物溶解在1.8L乙醇中。在冷却到室温之后，在布氏漏斗上通过抽吸过滤出晶体，再每次用200ml的冰冷乙醇洗涤两次。在减压下干燥，获得了502.4g(3.15mmol)的无色、分析纯物质。
熔点：86.5℃(EtOH)
IR：3400，1757，1682，1148，1055cm-1
元素分析：理论值：C：45.31，H：5.7，N：8.8，O：40.2
          实测值：C：45.1，H：5.7，N：8.8，O：40.0
其属性通过1H和13C NMR以及质谱法确定。
可以类似方式或利用文献公开的方法制备其它吗啉-2，3-二酮衍生物。
水凝胶制备实施例1：
在40L塑料桶中，6.9kg的冰丙烯酸用其中溶解了213g淀粉(购自AVEBE-Netherlands的Paselli SA2)的23kg水稀释。在搅拌下将45g的季戊四醇三烯丙基醚加入到该溶液中，以及通过通入氮气使密封的桶惰性化。然后通过添加大约400mg的过氧化氢和200mg的抗坏血酸来引发聚合。在反应结束之后，将凝胶机械粉碎，再与足够的氢氧化钠水溶液混合，获得75mol％的中和度，以所使用的丙烯酸为基准计(192g的50％NaOH/kg的凝胶)。中和的凝胶然后用干燥鼓干燥，用销式磨机研磨，最后用300-800微米的筛目筛分。
水凝胶制备实施例2
具有大约30×40cm的底部面积且通过粘接于聚乙烯袋而惰性化的长方形塑料盘经管道系统接受在独立容器中制备的已用氮气惰性化的溶液。该溶液由以下组分组成：1466g的水，305g的丙烯酸，3204g的丙烯酸钠(37％水溶液)，11g的SARTOMER SR 9035(乙氧基化三羟甲基丙烷三丙烯酸酯，购自SARTOMER-US)，0.61g的2，2-偶氮双脒基丙烷二盐酸盐和3.1g的过硫酸钠。在引入单体溶液的同时，通过2个独立的管道系统添加另外2种引发剂溶液，并且使得与单体溶液均匀混合。这两种其它引发剂溶液分别是0.25g过氧化氢在5g水中的溶液和0.25g抗坏血酸在5g水中的溶液。聚合反应产生了大约4cm厚的凝胶块，用绞肉机进行机械粉碎，在循环空气干燥箱内在160℃下干燥，用超速离心磨研磨，随后用300-850μm的筛目筛分。
水凝胶制备实施例3：
重复水凝胶制备实施例2，只是单体溶液另外含有0.5g的N-2-羟乙基-吗啉-2，3-二酮。
本发明实施例1：
在Waring实验室混合机内，20g的水凝胶制备实施例1的基础聚合物用具有以下组成的交联剂溶液喷雾：1.5重量％的异丙醇，3.5重量％的水，0.08重量％的N-2-羟乙基-吗啉-2，3-二酮，各重量％以所使用的聚合物为基准。湿产物随后在循环空气干燥箱内在175℃下退火60分钟。干燥产物随后用850μm的筛目筛分，以除去团块。
对比实施例1：
在Waring实验室混合机内，20g的水凝胶制备实施例1的基础聚合物用具有以下组成的交联剂溶液喷雾：1.5重量％的异丙醇，3.5重量％的水，但不添加任何N-2-羟乙基-吗啉-2，3-二酮，各重量％以所使用的聚合物为基准。湿产物随后在循环空气干燥箱内在175℃下退火60分钟。干燥产物随后用850μm的筛目筛分，以除去团块。
本发明实施例2：
在Waring实验室混合机内，20g的水凝胶制备实施例2的基础聚合物用具有以下组成的交联剂溶液喷雾：1.5重量％的异丙醇，3.5重量％的水，0.08重量％的N-2-羟乙基-吗啉-2，3-二酮，各重量％以所使用的聚合物为基准。湿产物随后在循环空气干燥箱内在175℃下退火60分钟。干燥产物随后用850μm的筛目筛分，以除去团块。
本发明实施例3：
在Waring实验室混合机内，20g的水凝胶制备实施例2的基础聚合物用具有以下组成的交联剂溶液喷雾：1.5重量％的异丙醇，3.5重量％的水，0.08重量％的N-甲基吗啉-2，3-二酮，各重量％以所使用的聚合物为基准。湿产物随后在循环空气干燥箱内在175℃下退火60分钟。干燥产物随后用850μm的筛目筛分，以除去团块。
本发明实施例4：
在Waring实验室混合机内，20g的水凝胶制备实施例2的基础聚合物用具有以下组成的交联剂溶液喷雾：1.5重量％的异丙醇，3.5重量％的水，0.08重量％的N-叔丁基-吗啉-2，3-二酮，各重量％以所使用的聚合物为基准。湿产物随后在循环空气干燥箱内在175℃下退火60分钟。干燥产物随后用850μm的筛目筛分，以除去团块。
本发明实施例5：
在Waring实验室混合机内，20g的水凝胶制备实施例2的基础聚合物用具有以下组成的交联剂溶液喷雾：1.5重量％的异丙醇，3.5重量％的水，0.08重量％的N-乙基吗啉-2，3-二酮，各重量％以所使用的聚合物为基准。湿产物随后在循环空气干燥箱内在175℃下退火60分钟。干燥产物随后用850μm的筛目筛分，以除去团块。
对比实施例2：
在Waring实验室混合机内，20g的水凝胶制备实施例2的基础聚合物用具有以下组成的交联剂溶液喷雾：1.5重量％的异丙醇，3.5重量％的水，但不添加在本发明实施例2-5中使用的任何吗啉-2，3-二酮衍生物，各重量％以所使用的聚合物为基准。湿产物随后在循环空气干燥箱内在175℃下退火60分钟。干燥产物随后用850μm的筛目筛分，以除去团块。
本发明实施例6：
在Waring实验室混合机内，20g的水凝胶制备实施例3的基础聚合物用具有以下组成的交联剂溶液喷雾：1.5重量％的异丙醇，3.5重量％的水，0.08重量％的N-2-羟乙基吗啉-2，3-二酮，各重量％以所使用的聚合物为基准。湿产物随后在循环空气干燥箱内在175℃下退火60分钟。干燥产物随后用850μm的筛目筛分，以除去团块。
对比实施例3：
在Waring实验室混合机内，20g的水凝胶制备实施例3的基础聚合物用具有以下组成的交联剂溶液喷雾：1.5重量％的异丙醇，3.5重量％的水，但不添加如在本发明实施例6中使用的任何吗啉-2，3-二酮衍生物，各重量％以所使用的聚合物为基准。湿产物随后在循环空气干燥箱内在175℃下退火60分钟。干燥产物随后用850μm的筛目筛分，以除去团块。
表
实施例   根据水凝胶制备实施例的基础聚合物 交联剂 CRC(g/g) AUL0.5psi(g/g) AUL0.7psi(g/g)
  本发明实施例1 1   0.08％的N-2-羟乙基吗啉-2，3-二酮 34.2 26.8 23.9
  对比实施例1 1 - 38.3 9.4 8.4
  本发明实施例2 2   0.08重量％的N-2-羟乙基吗啉-2，3-二酮 35.6 25.2 19.5
  本发明实施例3 2   0.08％的N-甲基吗啉-2，3-二酮 37.4 13.7 9.7
  本发明实施例4 2   0.08％的N-叔丁基吗啉-2，3-二酮 37.2 13.2 8.9
  本发明实施例5 2   0.08％的N-乙基-吗啉-2，3-二酮 37.4 13.2 12.9
  对比实施例2 2 - 39.7 7.9 6.5
  本发明实施例6 3   0.08％的N-2-羟乙基吗啉-2，3-二酮 34.0 27.6 24.2
  对比实施例3 3 - 36.5 12.1 8.5

Claims (21)

1、一种交联用于制备能吸收含水流体的水凝胶形成聚合物的起始聚合物的方法，该方法包括使用通式1的交联剂：
其中R1是氢，C1-C4烷基，C1-C4羟烷基或式2的基团：
其中R2、R3、R4和R5各自独立地是C1-C4烷基，C1-C4羟烷基或氢。
2、一种含有羧基的起始聚合物的表面后交联方法，该方法包括使用如在权利要求1中所述的通式1的交联剂。
3、如权利要求1和2的任一项所要求的方法，其中用交联剂处理起始聚合物以及通过在处理期间或之后升高温度来进行后交联和干燥，该交联剂存在于惰性溶剂中。
4、如权利要求3所要求的方法，其中交联剂是N-羟乙基-2，3-吗啉二酮。
5、如权利要求1或2所要求的方法，其中起始聚合物是聚合丙烯酸或聚丙烯酸酯，尤其通过使用多官能烯属不饱和自由基交联剂进行自由基聚合获得的聚合丙烯酸或聚丙烯酸酯。
6、物质组合物，包含如权利要求1或权利要求4所述的通式1的交联剂和溶剂，所述溶剂选自水、水与在水中具有无限溶解度的一种或多种有机溶剂的混合物、以及水与一种或多种一元醇或多元醇的混合物。
7、如权利要求6所要求的物质组合物，其中溶剂是具有10-90重量％的醇含量的醇-水混合物，以该溶液为基准计。
8、如权利要求7所要求的物质组合物，其中溶剂是具有15-65重量％的醇含量的醇-水混合物，以该溶液为基准计。
9、如权利要求6-8的任一项所要求的物质组合物，其中醇是甲醇，乙醇，异丙醇，乙二醇，1，2-丙二醇或1，3-丙二醇。
10、如权利要求6-8的任一项所要求的物质组合物，其中交联剂占物质组合物的0.1-10重量％。
11、如权利要求10所要求的物质组合物，其中交联剂占物质组合物的0.5-3重量％。
12、如权利要求1或2所要求的方法，其中使用如权利要求6-11的任一项所要求的物质组合物。
13、如权利要求12所要求的方法，其中使用0.1-20重量％比率的包含交联剂和溶剂的物质组合物，以起始聚合物的质量为基准计。
14、如权利要求13所要求的方法，其中使用0.5-10重量％比率的包含交联剂和溶剂的物质组合物，以起始聚合物的质量为基准计。
15、如权利要求1或2所要求的方法，其中交联剂以0.01-5.0重量％的剂量使用，以起始聚合物为基准计。
16、如权利要求15所要求的方法，其中交联剂以0.02-3.0重量％的剂量使用，以起始聚合物为基准计。
17、如权利要求16所要求的方法，其中交联剂以0.03-1.0重量％的剂量使用，以起始聚合物为基准计。
18、如权利要求17所要求的方法，其中交联剂以0.05-0.1重量％的剂量使用，以起始聚合物为基准计。
19、通过如权利要求1-5或12-18的任一项所要求的方法获得的聚合物。
20、权利要求19的聚合物在卫生制品、包装材料和无纺织物中的用途。
21、如权利要求6-11的任一项所要求的物质组合物用于生产交联聚合物或能通过加热来交联的聚合物的用途。
CNB028194098A 2001-10-05 2002-09-27 用吗啉－2,3－二酮化合物交联水凝胶的方法 Expired - Fee Related CN1305914C (zh)