CN1272858A - 有机硅低聚物及含该低聚物的可固化组合物 - Google Patents
有机硅低聚物及含该低聚物的可固化组合物 Download PDFInfo
- Publication number
- CN1272858A CN1272858A CN99800968A CN99800968A CN1272858A CN 1272858 A CN1272858 A CN 1272858A CN 99800968 A CN99800968 A CN 99800968A CN 99800968 A CN99800968 A CN 99800968A CN 1272858 A CN1272858 A CN 1272858A
- Authority
- CN
- China
- Prior art keywords
- group
- oligopolymer
- silane
- vinyl
- ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
表1 | ||||||||||
低聚物 | 无 | A-1751 | 实施例18 | 实施例19 | 实施例14 | 实施例17 | 实施例15 | 实施例16 | 实施例22 | |
在171℃下固化20分钟的物理性能 | ||||||||||
硬度,邵尔A | 84 | 84 | 87 | 87 | 86 | 88 | 87 | 88 | 86 | |
伸长,% | 520 | 420 | 370 | 400 | 350 | 340 | 350 | 310 | 380 | |
100%模量,psi | 620 | 850 | 780 | 790 | 830 | 810 | 850 | 840 | 780 | |
200%模量,psi | 750 | 1210 | 1260 | 1180 | 1340 | 1330 | 1370 | 1390 | 1270 | |
300%模量,psi | 870 | 1430 | 1470 | 1410 | 1660 | 1650 | 1680 | 1720 | 1550 | |
拉伸强度,psi | 2190 | 1750 | 1620 | 1600 | 1710 | 1740 | 1760 | 1750 | 1710 | |
在60HZ下的介电常数 | ||||||||||
当固化后 | 2.48 | 2.26 | 当固化后 | 2.56 | 2.45 | 2.54 | 2.41 | 2.43 | 2.31 | 2.55 |
3天在90℃水中 | 3.09 | 2.59 | ||||||||
14天在90℃水中 | 3.27 | 2.63 | 17天在90℃水中 | 2.62 | 2.43 | 2.58 | 2.44 | 2.44 | 2.31 | 2.57 |
28天在90℃水中 | 3.23 | 2.64 | 34天在90℃水中 | 2.65 | 2.48 | 2.60 | 2.45 | 2.46 | 2.28 | 2.58 |
55天在90℃水中 | 3.16 | 2.65 | 48天在90℃水中 | 2.64 | 2.47 | 2.60 | 2.44 | 2.46 | 2.27 | 2.58 |
83天在90℃水中 | 3.09 | 2.65 | 92天在90℃水中 | 2.64 | 2.47 | 2.61 | 2.45 | 2.47 | 2.50 | 2.60 |
在60HZ下的功率因子 | ||||||||||
当固化后 | 0.0022 | 0.0015 | 当固化后 | 0.0014 | 0.0014 | 0.0013 | 0.0011 | 0.0015 | 0.0015 | 0.0013 |
3天在90℃水中 | 0.045 | 0.0024 | ||||||||
14天在90℃水中 | 0.045 | 0.0024 | 17天在90℃水中 | 0.0061 | 0.0025 | 0.0031 | 0.0018 | 0.0021 | 0.0021 | 0.0032 |
28天在90℃水中 | 0.050 | 0.0028 | 34天在90℃水中 | 0.0066 | 0.0031 | 0.0033 | 0.0021 | 0.0025 | 0.0023 | 0.0034 |
55天在90℃水中 | 0.053 | 0.0033 | 48天在90℃水中 | 0.0056 | 0.0029 | 0.0029 | 0.0029 | 0.0023 | 0.0020 | 0.0029 |
83天在90℃水中 | 0.051 | 0.0051 | 92天在90℃水中 | 0.0055 | 0.0028 | 0.0032 | 0.0019 | 0.0022 | 0.0019 | 0.0032 |
Claims (20)