CN111268908A - 一种低温孔雀绿釉瓷器的制备方法 - Google Patents
一种低温孔雀绿釉瓷器的制备方法 Download PDFInfo
- Publication number
- CN111268908A CN111268908A CN202010135263.9A CN202010135263A CN111268908A CN 111268908 A CN111268908 A CN 111268908A CN 202010135263 A CN202010135263 A CN 202010135263A CN 111268908 A CN111268908 A CN 111268908A
- Authority
- CN
- China
- Prior art keywords
- glaze
- parts
- temperature
- peacock green
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种低温孔雀绿釉瓷器的制备方法，低温孔雀绿釉瓷器包括坯体、设置在坯体上的透明釉和设置在透明釉上的孔雀绿釉，坯体包括以下原料：钠长石、黏土、德化石英、德化方解石、白云母、蛤粉、氧化锌、氧化钙、氧化铝，通过限定孔雀绿釉的原料组成，以铜矿石和氧化铜为呈色剂，与其他组分配合，使烧成而成的瓷器釉色十分鲜嫩，青翠欲滴，犹如孔雀羽毛般艳丽；制备时通过在坯体上先附着一层透明釉料，然后在透明釉料上施孔雀绿釉，再送入窑炉中二次烧制，釉与釉之间易结合，有效防止孔雀绿釉从瓷器上脱落，提高产品的成品率，且透明釉不会影响孔雀绿釉最后的呈色。
Description
技术领域
本发明属于瓷器制备领域，具体涉及一种低温孔雀绿釉瓷器的制备方法。
背景技术
我们日常使用的陶瓷器，一般都穿着一身光润、平滑的衣裳，特别是日用陶瓷器，对“衣裳”更为讲究，有的洁白如玉，有的五彩缤纷，十分美观。陶瓷的这种衣裳，名叫“釉”。
釉的主要成份是硅酸盐，它可以增加陶瓷器的机械强度、热稳定性、介电强度并且可以阻止液体、气体侵蚀陶瓷器，且釉还具有增加瓷器美观性、便于洗拭瓷器、使瓷器不被尘土粘染等作用。
釉的颜色就称为釉色。瓷器的釉彩开始比较单一，随着瓷业的发展与科技进步，由开始的一种釉彩的素瓷发展到如今多种釉彩的彩瓷，给瓷器增色不少。烧成的瓷器釉色光亮鲜明，不易开裂，一方面取决于烧制过程工艺的把握，更重要的是与釉料的配方关系重大。因此对釉料进行开发研究，以丰富瓷器釉色，并提高瓷器的美观度，是现在瓷器制造的一个重要方向。
发明内容
本发明的目的是克服现有技术的缺点，提供一种低温孔雀绿釉瓷器的制备方法。
本发明采用如下技术方案：
一种低温孔雀绿釉瓷器的制备方法，所述低温孔雀绿釉瓷器包括坯体、设置在坯体上的透明釉和设置在透明釉上的孔雀绿釉，
坯体包括以下重量份的原料：钠长石20-25份、黏土28-32份、德化石英30-40份、德化方解石10-18份、白云母8-15份、蛤粉2-5份、氧化锌5-8份、氧化钙3-6份、氧化铝8-10份；
透明釉包括以下重量份的原料：德化石英30-35份、白云石20-22份、透明熔块1-3份、氧化铝5-8份、氧化锌10-12份；
孔雀绿釉包括以下重量份的原料：德化石英35-40份、锂辉石10-12份、硅灰石3-8份、德化紫木节土2-5份、铜矿石2-4份、氧化铜1-3份、碳酸钙1-3份、五氧化二钒0.5-1份；
其制备方法包括如下步骤：
步骤一，按坯体的原料组成分别称重、破碎、混合、湿球磨制得泥浆；
步骤二，按透明釉和孔雀绿釉的原料称重配料，原料分别破碎、混合、湿球磨制得透明釉浆和孔雀绿釉浆；
步骤三，将步骤二制得的透明釉浆经过磁选机多次除铁，至透明釉浆中的含铁量低于0.05％；
步骤四，将步骤一制得的泥浆制成坯体，待坯体干燥后再坯体表面施步骤三制得的透明釉浆；
步骤五，待坯体表面的透明釉浆干燥后，送入窑炉中在1020-1050℃下煅烧3-4h，冷却得素坯；
步骤六，在步骤五制得的素坯表面施孔雀绿釉浆，待孔雀绿釉浆干燥后送入窑炉中烧制成型，烧成温度为1080-1100℃。
进一步的，所述步骤六中烧成控制如下：
低温干燥阶段：窑炉由常温升至100-120℃，将素坯置于窑炉中随窑炉自然冷却至室温；
低温阶段：窑炉内由常温升重新至400-420℃，烧窑时间70-80min；
氧化阶段：窑炉内升温至1080-1100℃，烧窑时间3-4小时；
高火保温阶段：窑炉内温度控制在1080-1100℃，烧窑时间1.5-2小时；
自然冷却阶段：窑炉内冷却至室温，冷却时间延长至8小时以上。
进一步的，所述透明熔块的化学组成如下：SiO2：48-56％、Al2O3：10-15％、MgO：8-12％、Na2O：6-12％、CaO：5-10％、ZnO：4-6％、LiO2：2-3％、La2O3：1-2％。
进一步的，所述步骤一中，泥浆湿法球磨时，原料在球磨机中湿法研磨15-18小时，研磨介质为水，原料：球：水＝1:1.2-1.5:1-1.2。
进一步的，所述步骤二中，透明釉浆湿法球磨时，原料在球磨机中湿法研磨22-24小时，研磨介质为水，原料：球：水＝1:1.5-1.8:1.2-1.5。
进一步的，所述步骤二中，孔雀绿釉浆湿法球磨时，原料在球磨机中湿法研磨22-24小时，研磨介质为水，原料：球：水＝1:1.8-2:1.3-1.5。
进一步的，所述步骤三中，磁选机的强度为为19000-21000GS。
进一步的，所述步骤四中，坯体的成型方式为碾压成型或注浆成型。
进一步的，所述透明釉浆的施釉方式为淋釉或浸釉。
进一步的，所述孔雀绿釉浆的施釉方式为喷釉或淋釉。
由上述对本发明的描述可知，与现有技术相比，本发明的有益效果是：通过限定孔雀绿釉的原料组成，以铜矿石和氧化铜为呈色剂，与其他组分配合，使烧成而成的瓷器釉色十分鲜嫩，青翠欲滴，犹如孔雀羽毛般艳丽；制备时通过在坯体上先附着一层透明釉料，然后在透明釉料上施孔雀绿釉，再送入窑炉中二次烧制，釉与釉之间易结合，有效防止孔雀绿釉从瓷器上脱落，提高产品的成品率，且透明釉不会影响孔雀绿釉最后的呈色；
孔雀绿釉中含有少量五氧化二钒，可在高温时，促进铜矿石和氧化铜的呈色，碳酸钙可使最后形成孔雀绿釉面呈现闪光的釉面，保证烧制而成的瓷器釉色十分鲜嫩，青翠欲滴，犹如孔雀羽毛般艳丽；
孔雀绿釉中还含有锂辉石,釉料煅烧时，锂辉石可使石英不断熔解于熔体中,抑制残余石英向热膨胀系数比石英高得多的方石英转化，还可降低β-石英向α-石英的晶型转变温度,使低热膨胀系数的β—石英在更宽广的温度区域内稳定，以使孔雀绿釉浆的膨胀系数小于坯体的膨胀系数，防止形成的孔雀绿釉面产生裂纹，保证釉面的美观性；
孔雀绿釉中的德化紫木节土能大大增加孔雀绿釉的粘性、悬浮和流动性，保证最后制得瓷器的釉面的完整性和均匀性；
透明釉料中的透明熔块以二氧化硅为主原料，辅以氧化铝、氧化锌、氧化镁、氧化钙等氧化物，可以进一步增加釉料的稳定性、悬浮性和与坯体的黏着性，减少气泡，保证透明釉料的完整性和均匀性；
坯体施孔雀绿釉浆进窑炉进行二次烧制时，需先经过低温干燥阶段，随窑炉从100-120℃冷却至室温，进一步干燥孔雀绿釉浆中的水分，防止因窑炉升温时，坯体内部和表面温度相差过大，导致孔雀绿釉表面的水排除太急，孔雀绿釉面收缩过快，产生较大的内应力，而产生裂纹。
具体实施方式
以下通过具体实施方式对本发明作进一步的描述。
一种低温孔雀绿釉瓷器包括坯体、设置在坯体上的透明釉和设置在透明釉上的孔雀绿釉。
坯体包括以下重量份的原料：钠长石20-25份、黏土28-32份、德化石英30-40份、德化方解石10-18份、白云母8-15份、蛤粉2-5份、氧化锌5-8份、氧化钙3-6份、氧化铝8-10份。
透明釉包括以下重量份的原料：德化石英30-35份、白云石20-22份、透明熔块1-3份、氧化铝5-8份、氧化锌10-12份。
透明熔块的化学组成如下：SiO2：48-56％、Al2O3：10-15％、MgO：8-12％、Na2O：6-12％、CaO：5-10％、ZnO：4-6％、LiO2：2-3％、La2O3：1-2％。
孔雀绿釉包括以下重量份的原料：德化石英35-40份、锂辉石10-12份、硅灰石3-8份、德化紫木节土2-5份、铜矿石2-4份、氧化铜1-3份、碳酸钙1-3份、五氧化二钒0.5-1份。
其制备方法包括如下步骤：
步骤一，按坯体的原料组成分别称重、破碎、混合、湿球磨制得泥浆；
步骤二，按透明釉和孔雀绿釉的原料称重配料，原料分别破碎、混合、湿球磨制得透明釉浆和孔雀绿釉浆；
步骤三，将步骤二制得的透明釉浆经过磁选机多次除铁，至透明釉浆中的含铁量低于0.05％；
步骤四，将步骤一制得的泥浆制成坯体，待坯体干燥后再坯体表面施步骤三制得的透明釉浆；
步骤五，待坯体表面的透明釉浆干燥后，送入窑炉中在1020-1050℃下煅烧3-4h，冷却得素坯；
步骤六，在步骤五制得的素坯表面施孔雀绿釉浆，待孔雀绿釉浆干燥后送入窑炉中烧制成型，烧成温度为1080-1100℃，具体烧成控制如下：
低温干燥阶段：窑炉由常温升至100-120℃，将素坯置于窑炉中随窑炉自然冷却至室温；
低温阶段：窑炉内由常温升重新至400-420℃，烧窑时间70-80min；
氧化阶段：窑炉内升温至1080-1100℃，烧窑时间3-4小时；
高火保温阶段：窑炉内温度控制在1080-1100℃，烧窑时间1.5-2小时；
自然冷却阶段：窑炉内冷却至室温，冷却时间延长至8小时以上。
具体的，步骤一中，泥浆湿法球磨时，原料在球磨机中湿法研磨15-18小时，研磨介质为水，原料：球：水＝1:1.2-1.5:1-1.2。
步骤二中，透明釉浆湿法球磨时，原料在球磨机中湿法研磨22-24小时，研磨介质为水，原料：球：水＝1:1.5-1.8:1.2-1.5。
步骤二中，孔雀绿釉浆湿法球磨时，原料在球磨机中湿法研磨22-24小时，研磨介质为水，原料：球：水＝1:1.8-2:1.3-1.5。
步骤三中，磁选机的强度为为19000-21000GS。
步骤四中，坯体的成型方式为碾压成型或注浆成型。
步骤四中，透明釉浆的施釉方式为淋釉或浸釉。
步骤六中，孔雀绿釉浆的施釉方式为喷釉或淋釉。
实施例1
一种低温孔雀绿釉瓷器包括坯体、设置在坯体上的透明釉和设置在透明釉上的孔雀绿釉。
坯体包括以下重量份的原料：钠长石20份、黏土32份、德化石英30份、德化方解石18份、白云母8份、蛤粉2份、氧化锌5份、氧化钙6份、氧化铝10份。
透明釉包括以下重量份的原料：德化石英30份、白云石22份、透明熔块1份、氧化铝8份、氧化锌10份。
透明熔块的化学组成如下：SiO2：48％、Al2O3：15％、MgO：8％、Na2O：12％、CaO：10％、ZnO：4％、LiO2：2％、La2O3：1％。
孔雀绿釉包括以下重量份的原料：德化石英40份、锂辉石10份、硅灰石3份、德化紫木节土5份、铜矿石2份、氧化铜3份、碳酸钙1份、五氧化二钒0.5份。
其制备方法包括如下步骤：
步骤一，按坯体的原料组成分别称重、破碎、混合、湿球磨制得泥浆；
步骤二，按透明釉和孔雀绿釉的原料称重配料，原料分别破碎、混合、湿球磨制得透明釉浆和孔雀绿釉浆；
步骤三，将步骤二制得的透明釉浆经过磁选机多次除铁，至透明釉浆中的含铁量低于0.05％；
步骤四，将步骤一制得的泥浆制成坯体，待坯体干燥后再坯体表面施步骤三制得的透明釉浆；
步骤五，待坯体表面的透明釉浆干燥后，送入窑炉中在1020℃下煅烧4h，冷却得素坯；
步骤六，在步骤五制得的素坯表面施孔雀绿釉浆，待孔雀绿釉浆干燥后送入窑炉中烧制成型，烧成温度为1080℃，具体烧成控制如下：
低温干燥阶段：窑炉由常温升至120℃，将素坯置于窑炉中随窑炉自然冷却至室温；
低温阶段：窑炉内由常温升重新至400℃，烧窑时间70min；
氧化阶段：窑炉内升温至1080℃，烧窑时间4小时；
高火保温阶段：窑炉内温度控制在1080℃，烧窑时间2小时；
自然冷却阶段：窑炉内冷却至室温，冷却时间延长至8小时以上。
具体的，步骤一中，泥浆湿法球磨时，原料在球磨机中湿法研磨15小时，研磨介质为水，原料：球：水＝1:1.2:1。
步骤二中，透明釉浆湿法球磨时，原料在球磨机中湿法研磨24小时，研磨介质为水，原料：球：水＝1:1.8:1.2。
步骤二中，孔雀绿釉浆湿法球磨时，原料在球磨机中湿法研磨22小时，研磨介质为水，原料：球：水＝1:1.8:1.3。
步骤三中，磁选机的强度为为19000GS。
步骤四中，坯体的成型方式为注浆成型。
步骤四中，透明釉浆的施釉方式为浸釉。
步骤六中，孔雀绿釉浆的施釉方式为淋釉。
实施例2
一种低温孔雀绿釉瓷器包括坯体、设置在坯体上的透明釉和设置在透明釉上的孔雀绿釉。
坯体包括以下重量份的原料：钠长石25份、黏土28份、德化石英40份、德化方解石10份、白云母15份、蛤粉5份、氧化锌8份、氧化钙3份、氧化铝8份。
透明釉包括以下重量份的原料：德化石英35份、白云石20份、透明熔块3份、氧化铝5份、氧化锌12份。
透明熔块的化学组成如下：SiO2：56％、Al2O3：10％、MgO：12％、Na2O：6％、CaO：5％、ZnO：6％、LiO2：3％、La2O3：2％。
孔雀绿釉包括以下重量份的原料：德化石英35份、锂辉石12份、硅灰石8份、德化紫木节土2份、铜矿石4份、氧化铜1份、碳酸钙3份、五氧化二钒1份。
其制备方法包括如下步骤：
步骤一，按坯体的原料组成分别称重、破碎、混合、湿球磨制得泥浆；
步骤二，按透明釉和孔雀绿釉的原料称重配料，原料分别破碎、混合、湿球磨制得透明釉浆和孔雀绿釉浆；
步骤三，将步骤二制得的透明釉浆经过磁选机多次除铁，至透明釉浆中的含铁量低于0.05％；
步骤四，将步骤一制得的泥浆制成坯体，待坯体干燥后再坯体表面施步骤三制得的透明釉浆；
步骤五，待坯体表面的透明釉浆干燥后，送入窑炉中在1050℃下煅烧3h，冷却得素坯；
步骤六，在步骤五制得的素坯表面施孔雀绿釉浆，待孔雀绿釉浆干燥后送入窑炉中烧制成型，烧成温度为1100℃，具体烧成控制如下：
低温干燥阶段：窑炉由常温升至100℃，将素坯置于窑炉中随窑炉自然冷却至室温；
低温阶段：窑炉内由常温升重新至420℃，烧窑时间80min；
氧化阶段：窑炉内升温至1100℃，烧窑时间3小时；
高火保温阶段：窑炉内温度控制在1100℃，烧窑时间1.5小时；
自然冷却阶段：窑炉内冷却至室温，冷却时间延长至8小时以上。
具体的，步骤一中，泥浆湿法球磨时，原料在球磨机中湿法研磨18小时，研磨介质为水，原料：球：水＝1:1.5:1.2。
步骤二中，透明釉浆湿法球磨时，原料在球磨机中湿法研磨22小时，研磨介质为水，原料：球：水＝1:1.5:1.5。
步骤二中，孔雀绿釉浆湿法球磨时，原料在球磨机中湿法研磨24小时，研磨介质为水，原料：球：水＝1:2:1.5。
步骤三中，磁选机的强度为为21000GS。
步骤四中，坯体的成型方式为碾压成型。
步骤四中，透明釉浆的施釉方式为淋釉。
步骤六中，孔雀绿釉浆的施釉方式为喷釉。
实施例3
一种低温孔雀绿釉瓷器包括坯体、设置在坯体上的透明釉和设置在透明釉上的孔雀绿釉。
坯体包括以下重量份的原料：钠长石22份、黏土30份、德化石英35份、德化方解石16份、白云母12份、蛤粉4份、氧化锌6份、氧化钙5份、氧化铝9份。
透明釉包括以下重量份的原料：德化石英33份、白云石21份、透明熔块2份、氧化铝6份、氧化锌11份。
透明熔块的化学组成如下：SiO2：53％、Al2O3：12％、MgO：10％、Na2O：9％、CaO：7％、ZnO：5％、LiO2：2.5％、La2O3：1.5％。
孔雀绿釉包括以下重量份的原料：德化石英37份、锂辉石11份、硅灰石5份、德化紫木节土3份、铜矿石3份、氧化铜2份、碳酸钙2份、五氧化二钒0.8份。
其制备方法包括如下步骤：
步骤一，按坯体的原料组成分别称重、破碎、混合、湿球磨制得泥浆；
步骤二，按透明釉和孔雀绿釉的原料称重配料，原料分别破碎、混合、湿球磨制得透明釉浆和孔雀绿釉浆；
步骤三，将步骤二制得的透明釉浆经过磁选机多次除铁，至透明釉浆中的含铁量低于0.05％；
步骤四，将步骤一制得的泥浆制成坯体，待坯体干燥后再坯体表面施步骤三制得的透明釉浆；
步骤五，待坯体表面的透明釉浆干燥后，送入窑炉中在1035℃下煅烧3.5h，冷却得素坯；
步骤六，在步骤五制得的素坯表面施孔雀绿釉浆，待孔雀绿釉浆干燥后送入窑炉中烧制成型，烧成温度为1090℃，具体烧成控制如下：
低温干燥阶段：窑炉由常温升至110℃，将素坯置于窑炉中随窑炉自然冷却至室温；
低温阶段：窑炉内由常温升重新至410℃，烧窑时间75min；
氧化阶段：窑炉内升温至1090℃，烧窑时间3.5小时；
高火保温阶段：窑炉内温度控制在1090℃，烧窑时间1.8小时；
自然冷却阶段：窑炉内冷却至室温，冷却时间延长至8小时以上。
具体的，步骤一中，泥浆湿法球磨时，原料在球磨机中湿法研磨16小时，研磨介质为水，原料：球：水＝1:1.3:1.1。
步骤二中，透明釉浆湿法球磨时，原料在球磨机中湿法研磨23小时，研磨介质为水，原料：球：水＝1:1.7:1.4。
步骤二中，孔雀绿釉浆湿法球磨时，原料在球磨机中湿法研磨23小时，研磨介质为水，原料：球：水＝1:1.9:1.4。
步骤三中，磁选机的强度为为20000GS。
步骤四中，坯体的成型方式为碾压成型。
步骤四中，透明釉浆的施釉方式为淋釉。
步骤六中，孔雀绿釉浆的施釉方式为淋釉。
本发明通过限定孔雀绿釉的原料组成，以铜矿石和氧化铜为呈色剂，与其他组分配合，使烧成而成的瓷器釉色十分鲜嫩，青翠欲滴，犹如孔雀羽毛般艳丽；制备时通过在坯体上先附着一层透明釉料，然后在透明釉料上施孔雀绿釉，再送入窑炉中二次烧制，釉与釉之间易结合，有效防止孔雀绿釉从瓷器上脱落，提高产品的成品率，且透明釉不会影响孔雀绿釉最后的呈色；孔雀绿釉中含有少量五氧化二钒，可在高温时，促进铜矿石和氧化铜的呈色，碳酸钙可使最后形成孔雀绿釉面呈现闪光的釉面，保证烧制而成的瓷器釉色十分鲜嫩，青翠欲滴，犹如孔雀羽毛般艳丽；孔雀绿釉中还含有锂辉石,釉料煅烧时，锂辉石可使石英不断熔解于熔体中,抑制残余石英向热膨胀系数比石英高得多的方石英转化，还可降低β-石英向α-石英的晶型转变温度,使低热膨胀系数的β—石英在更宽广的温度区域内稳定，以使孔雀绿釉浆的膨胀系数小于坯体的膨胀系数，防止形成的孔雀绿釉面产生裂纹，保证釉面的美观性；孔雀绿釉中的德化紫木节土能大大增加孔雀绿釉的粘性、悬浮和流动性，保证最后制得瓷器的釉面的完整性和均匀性。
透明釉料中的透明熔块以二氧化硅为主原料，辅以氧化铝、氧化锌、氧化镁、氧化钙等氧化物，可以进一步增加釉料的稳定性、悬浮性和与坯体的黏着性，减少气泡，保证透明釉料的完整性和均匀性。
坯体施孔雀绿釉浆进窑炉进行二次烧制时，需先经过低温干燥阶段，随窑炉从100-120℃冷却至室温，进一步干燥孔雀绿釉浆中的水分，防止因窑炉升温时，坯体内部和表面温度相差过大，导致孔雀绿釉表面的水排除太急，孔雀绿釉面收缩过快，产生较大的内应力，而产生裂纹。
以上所述，仅为本发明的较佳实施例而已，故不能以此限定本发明实施的范围，即依本发明申请专利范围及说明书内容所作的等效变化与修饰，皆应仍属本发明专利涵盖的范围内。
Claims (10)
1.一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述低温孔雀绿釉瓷器包括坯体、设置在坯体上的透明釉和设置在透明釉上的孔雀绿釉，
坯体包括以下重量份的原料：钠长石20-25份、黏土28-32份、德化石英30-40份、德化方解石10-18份、白云母8-15份、蛤粉2-5份、氧化锌5-8份、氧化钙3-6份、氧化铝8-10份；
透明釉包括以下重量份的原料：德化石英30-35份、白云石20-22份、透明熔块1-3份、氧化铝5-8份、氧化锌10-12份；
孔雀绿釉包括以下重量份的原料：德化石英35-40份、锂辉石10-12份、硅灰石3-8份、德化紫木节土2-5份、铜矿石2-4份、氧化铜1-3份、碳酸钙1-3份、五氧化二钒0.5-1份；
其制备方法包括如下步骤：
步骤一，按坯体的原料组成分别称重、破碎、混合、湿球磨制得泥浆；
步骤二，按透明釉和孔雀绿釉的原料称重配料，原料分别破碎、混合、湿球磨制得透明釉浆和孔雀绿釉浆；
步骤三，将步骤二制得的透明釉浆经过磁选机多次除铁，至透明釉浆中的含铁量低于0.05％；
步骤四，将步骤一制得的泥浆制成坯体，待坯体干燥后再坯体表面施步骤三制得的透明釉浆；
步骤五，待坯体表面的透明釉浆干燥后，送入窑炉中在1020-1050℃下煅烧3-4h，冷却得素坯；
步骤六，在步骤五制得的素坯表面施孔雀绿釉浆，待孔雀绿釉浆干燥后送入窑炉中烧制成型，烧成温度为1080-1100℃。
2.根据权利要求1所述的一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述步骤六中烧成控制如下：
低温干燥阶段：窑炉由常温升至100-120℃，将素坯置于窑炉中随窑炉自然冷却至室温；
低温阶段：窑炉内由常温升重新至400-420℃，烧窑时间70-80min；
氧化阶段：窑炉内升温至1080-1100℃，烧窑时间3-4小时；
高火保温阶段：窑炉内温度控制在1080-1100℃，烧窑时间1.5-2小时；
自然冷却阶段：窑炉内冷却至室温，冷却时间延长至8小时以上。
3.根据权利要求1所述的一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述透明熔块的化学组成如下：SiO2：48-56％、Al2O3：10-15％、MgO：8-12％、Na2O：6-12％、CaO：5-10％、ZnO：4-6％、LiO2：2-3％、La2O3：1-2％。
4.根据权利要求1或2或3所述的一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述步骤一中，泥浆湿法球磨时，原料在球磨机中湿法研磨15-18小时，研磨介质为水，原料：球：水＝1:1.2-1.5:1-1.2。
5.根据权利要求1或2或3所述的一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述步骤二中，透明釉浆湿法球磨时，原料在球磨机中湿法研磨22-24小时，研磨介质为水，原料：球：水＝1:1.5-1.8:1.2-1.5。
6.根据权利要求1或2或3所述的一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述步骤二中，孔雀绿釉浆湿法球磨时，原料在球磨机中湿法研磨22-24小时，研磨介质为水，原料：球：水＝1:1.8-2:1.3-1.5。
7.根据权利要求1或2或3所述的一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述步骤三中，磁选机的强度为为19000-21000GS。
8.根据权利要求1或2或3所述的一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述步骤四中，坯体的成型方式为碾压成型或注浆成型。
9.根据权利要求1或2或3所述的一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述透明釉浆的施釉方式为淋釉或浸釉。
10.根据权利要求1或2或3所述的一种低温孔雀绿釉瓷器的制备方法，其特征在于：所述孔雀绿釉浆的施釉方式为喷釉或淋釉。